CN100357379C - 一种含铬有机硅耐高温涂料 - Google Patents
一种含铬有机硅耐高温涂料 Download PDFInfo
- Publication number
- CN100357379C CN100357379C CNB200310119266XA CN200310119266A CN100357379C CN 100357379 C CN100357379 C CN 100357379C CN B200310119266X A CNB200310119266X A CN B200310119266XA CN 200310119266 A CN200310119266 A CN 200310119266A CN 100357379 C CN100357379 C CN 100357379C
- Authority
- CN
- China
- Prior art keywords
- paint
- high temperature
- temperature resistant
- organic silicon
- silicone resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种含铬有机硅耐高温涂料，以有机硅树脂，加入适宜的稀释剂、固化剂为成膜剂，其特征在于：以三氧化二铬为物理改性材料，以有机硅树脂含固量计，三氧化二铬粉的加入量为1.0-400%重量。根据使用条件的不同，也可以添加一些硅、镁、铝、镍等金属氧化物或天然矿物中的一种或多种。该涂料涂在不锈钢薄片上，固化后经900℃，三小时的高温处理后，外观平整、牢固、无裂纹，是一种较为理想的耐高温涂料，同时也可以作为耐高温粘合剂和封装密封材料使用。
Description
技术领域：
本发明涉及涂料技术，特别提供了一种含铬的有机硅耐高温涂料。
背景技术：
能在较低的温度下固化、成膜性好、耐腐蚀性好、又能耐高温的涂料一直是人们探索的课题。有机硅树脂，由于其自身的结构特点，因而具有极优异的特性，越来越受到人们的重视。有机硅树脂以硅氧键为其主链，Si-O键的极性大，对所连烃基基团起到了屏蔽作用，提高了其氧化稳定性，受热后有机硅表面生成了-Si-O-Si-链的保护层，减轻了对高聚物内部的影响。使得有机硅具有了优异的耐热性和耐候性，因而被广泛地应用于建筑、电子、汽车、医疗等行业，显示出极好的应用前景。有机硅耐热涂料就是其中的一个范例。随着近代科学技术的飞速发展，在航空，航天，电子，机械等高科技领域中，对涂层的耐热性提出了越来越高的要求。国内的一些科研院所，也对其进行了大量的研究，使有机硅耐热涂料的使用温度已达到了500℃和600℃。如：西北工业大学，北方涂料工业研究设计院。专利CN 1295102A有机硅耐高温涂料。
发明内容：
本发明的目的在于提供一种耐温在800-900℃甚至更高的有机硅耐热涂料以满足科研实验的需要。
本发明提供了一种含铬有机硅耐高温涂料，以有机硅树脂，加入适宜的稀释剂、固化剂为成膜剂，其特征在于：以三氧化二铬为物理改性材料，以有机硅树脂计，三氧化二铬粉的加入量为1.0-400％重量。
本发明含铬有机硅耐高温涂料中，所述三氧化二铬粉的加入量最好为50-200％重量。
本发明含铬有机硅耐高温涂料中，还可以另外加入三氧化二铝、二氧化硅、氧化镁、氧化锆、二氧化钛、氧化镍金属氧化物或者滑石粉、云母粉天然矿物中的一种或多种，加入量分别为1％-100％重量。
本发明含铬有机硅耐高温涂料中，所述的稀释剂、固化剂为常规的有机硅树脂稀释剂、固化剂。如有机硅树脂可以为甲基硅氧烷；固化剂可以为单独或组合使用的三乙醇胺、三乙烯四胺、邻苯二甲酸二丁酯、辛酸亚锡、二丁基二月桂酸锡等有机金属盐；稀释剂可以为甲苯、苯、汽油等。
按上述配方配制的含铬有机硅耐热涂料涂在经除锈去油脂的不锈钢片上，在80～120℃固化，放入箱式电阻炉中，加热至900℃，恒温3小时。取出后，涂层牢固平整、无裂纹，显示了极好的耐高温性能。
具体实施方式：
实施例1
精确称取市售有机硅树脂1份，与之配套销售的稀释剂、固化剂适量，三氧化二铬粉一份。先将有机硅树脂、稀释剂、三氧化二铬粉置入容器内，搅拌均匀后，加入固化剂，再搅拌均匀，即可使用。
比较例1
精确称取市售有机硅树脂1份，与之配套销售的稀释剂、固化剂适量，滑石粉0.2份、二氧化钛0.2份、云母粉0.15份、二氧化硅0.15份。先将有机硅树脂、稀释剂、滑石粉、二氧化钛、云母粉、二氧化硅置入容器内，搅拌均匀后，加入固化剂，再搅拌均匀，即可使用。
比较例2
精确称取市售有机硅树脂1份，与之配套销售的稀释剂、固化剂适量，滑石粉0.6份、氧化镍0.9份。先将有机硅树脂、稀释剂、滑石粉、氧化镍粉置入容器内，搅拌均匀后，加入固化剂，再搅拌均匀，即可使用。
实施例2
精确称取市售有机硅树脂1份，与之配套销售的稀释剂、固化剂适量，三氧化二铬1份，硅铝粉0.28份。先将有机硅树脂、稀释剂、三氧化二铬、硅铝粉置入容器内，搅拌均匀后，加入固化剂，再搅拌均匀，即可使用。
实施例3
精确称取市售有机硅树脂1份，与之配套销售的稀释剂、固化剂适量，三氧化二铬1份、云母粉0.3份、氧化镍0.2份、二氧化钛0.15份。先将有机硅树脂、稀释剂、三氧化二铬、云母粉、氧化镍、二氧化钛置入容器内，搅拌均匀后，加入固化剂，再搅拌均匀，即可使用。
实施例4
精确称取市售有机硅树脂1份，与之配套销售的稀释剂、固化剂适量，三氧化二铬1份、云母粉0.3份、氧化镍0.2份。先将有机硅树脂、稀释剂三氧化二铬、云母粉、氧化镍粉置入容器内，搅拌均匀后，加入固化剂，再搅拌均匀，即可使用。
比较例3
精确称取市售有机硅树脂1份，与之配套销售的稀释剂、固化剂适量，滑石粉0.3份、云母粉0.4份、氧化镍0.3份。先将有机硅树脂、稀释剂、滑石粉、云母粉、氧化镍粉置入容器内，搅拌均匀后，加入固化剂，再搅拌均匀，即可使用。
实施例5
精确称取市售有机硅树脂1份，与之配套销售的稀释剂、固化剂适量，三氧化二铬2份。先将有机硅树脂、稀释剂、三氧化二铬粉置入容器内，搅拌均匀后，加入固化剂，再搅拌均匀，即可使用。
实施例6
将上述实施例1～5及比较例1～3配制好的有机硅耐热涂料均匀地涂在经除锈去油脂的不锈钢薄片上，80-120℃固化后，放入箱式电阻炉中，分别进行了500℃，600℃，700℃，800℃，900℃的高温处理，恒温时间均为3小时。处理后的试片，于25倍显微镜下观察结果如表1所示。
表1
从表中结果可以看出，在有机硅树脂中添加滑石粉、云母粉、氧化镁、氧化镍等矿物或氧化物，都可以提高有机硅涂料的耐热温度，但都没有超过700℃，只有实施例2和实施例5，即有机硅树脂与三氧化二铬的比例为1∶1和1∶2时，其耐热性能均达到900℃，表面平整无裂纹。因此含铬有机硅耐温涂料是一种很具潜力的耐高温涂料。由于该涂料的工艺简单，使用方便，可操作性强，因而该涂料的应用与发展具有广阔的前景。
Claims (2)
1、一种含铬有机硅耐高温涂料，以有机硅树脂，加入适宜的稀释剂、固化剂为成膜剂，其特征在于：以三氧化二铬为物理改性材料，以有机硅树脂计，三氧化二铬粉的加入量为100-200％重量。
2、按照权利要求1所述含铬有机硅耐高温涂料，其特征在于：加入三氧化二铝、二氧化硅、氧化镁、氧化锆、二氧化钛、氧化镍、滑石粉、或者云母粉中的一种或多种，加入量分别为1％-100％重量。