CN100355925C - 生产钢绞线用82b盘条的微合金化方法 - Google Patents
生产钢绞线用82b盘条的微合金化方法 Download PDFInfo
- Publication number
- CN100355925C CN100355925C CNB2004101554523A CN200410155452A CN100355925C CN 100355925 C CN100355925 C CN 100355925C CN B2004101554523 A CNB2004101554523 A CN B2004101554523A CN 200410155452 A CN200410155452 A CN 200410155452A CN 100355925 C CN100355925 C CN 100355925C
- Authority
- CN
- China
- Prior art keywords
- wire rods
- percent
- wire rod
- temperature
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种用连铸小方坯生产钢绞线用82B盘条的微合金化方法，包括钢包脱氧合金化、LF炉精炼，其特征在于：出钢前20分加入高碳铬铁，并在LF炉中进行微调，出钢1/3时加入钒铁，微合金加入量具体如下：Cr：0.30-0.43%，V：0.02-0.08%，C：0.77-0.81%，Mn：0.80-0.90%。本发明改写了用连铸小方坯在标准斯太尔摩控冷线不能生产1860-2000MPa钢绞线用盘条的历史。所生产的盘条组织性能稳定，平均片层间距为0.18μm，平均珠光体球团直径为8.4μm，用于拔制1860MPa钢绞线的φ12.5mm盘条的抗拉强度1160-1220MPa，面缩率30-36%，用于拔制2000MPa钢绞线的φ13.0mm盘条的抗拉强度1200-1260MPa，面缩率29-34%。
Description
所属领域
本发明属于钢铁材料领域，主要适用于生产φ15.24mm 1860-2000MPa钢绞线用φ11-14mm SWRH82B，以下简称82B盘条。
背景技术
φ15.24mm1860-2000MPa钢绞线是目前建筑材料中强度级别最高、技术含量最高的线材制品，在大型高速铁路、公路、桥梁、屋架、吊车梁和高层建筑等重大工程中得到广泛应用。近年来，随着我国国民经济的快速发展，市场前景非常广阔。1860-2000MPa钢绞线采用φ11mm～φ14.0mm82B盘条作原料，盘条初始抗拉强度要求≥1150MPa，面缩率≥28％。经过8-9道拉拔成φ5.05、5.25mm的钢丝，然后合股，捻制成钢绞线，绞线抗拉强度级别分为1860MPa和2000MPa。
生产82B盘条的主要难点之一是：在一定的控冷条件下，选用合适的化学成分，得到适合冷变形量达80％以上的索氏体组织。目前国内外生产该产品采用高端设备，轧后斯太尔摩控冷线的风机的风量为15.4-18万m3/h，冷却速度可以达到12-15℃/s。其生产82B所采用的化学成分为：0.82-0.84％C，0.70-0.80％Mn，0.17-0.23％Cr。本发明是针对普通生产装置：连铸机只有结晶器电磁搅拌，130mm连铸小方坯，标准斯太尔摩控冷线，其风机风量仅为8.3万m3/h，冷却速度为5-8℃/S，这种设备条件被认为是不能生产82B盘条。根据82B盘条使用特点，发明了达到其使用性能的一种新的化学成分及相关生产工艺，能够用普通生产设备生产，重点是Cr、V微合金化方法，其化学成分的选择遵循以下原则：(1)通过微合金化降低相变温度，细化片层间距到0.10-0.20μm；(2)盘条在最大冷速、最上限成分的条件下，不能出现贝氏体、马氏体等组织；(3)盘条的抗拉强度≥1150MPa，面缩率≥28％。
发明内容
本发明的目的在于提供一种用连铸小方坯生产1860～2000 MPa钢绞线用82B盘条的微合金化方法，在普通生产装置上生产高附加值产品。通过加入合适的Cr、V量，减小珠光体球团直径，降低相变点，得到适合拉拔的珠光体片层间距，提高盘条的抗拉强度，改善盘条的塑性和拉拔性能。
本发明涉及一种生产钢绞线用82B盘条的微合金化方法，其中钢的化学成份(重量百分比)为：C：0.77-0.81％、Mn：0.80-0.90％、P：0.009-0.018％、S：0.004-0.011％、Si：0.19-0.29％、其余为Fe，微合金化包括钢包脱氧合金化、LF炉精炼，出钢前20分加入高碳铬铁，并在LF炉中进行微调，出钢1/3时加入钒铁，微合金加入量具体如下：Cr：0.30-0.43％，V：0.02-0.08％，C：0.77-0.81％，Mn：0.80-0.90％；开轧温度为1000℃以上，保证Cr、V元素固溶，终轧温度为1000-1040℃，轧后的两阶段水冷要均匀冷却，第一段水冷后温度为880-920℃，吐丝温度为810-850℃，风冷速度为5-8℃/s，风冷终冷温度为600-570℃，之后缓慢冷却。
本发明的有益效果是：与先进的轧后强力风冷工艺12-14℃/s仅加0.20％Cr生产82B不同，本发明在5-8℃/s的冷速下，加入0.37％的左右Cr使平均相变温度由633.5℃降到了618.5℃，平均片层间距由0.24μm降到了0.15μm。在标准斯太尔摩冷却和冬季条件下，Cr含量达到0.43％时，不出现M组织。
加入V的作用如下：(1)通过析出强化，提高了盘条的强度，每0.01％的V提高强度10-15MPa：(2)固定钢中氮25-30ppm，降低了钢中的游离氮含量；(3)细小的V析出物形成了氢陷阱，改善了盘条的抗迟延断裂性。
本发明改写了用连铸小方坯在标准斯太尔摩控冷线不能生产1860MPa钢绞线用盘条的历史和成功研制出更高强度级别枛2000MPa钢绞线用盘条。
具体实施方式
本发明可在钢铁联合企业实施，下面是首钢第三炼钢厂-高速线材厂生产82B盘条
工艺路线为：铁水脱硫扒渣→三炼钢80t转炉冶炼→挡渣出钢→钢包脱氧合金化→钢包渣改质→LF钢包精炼→喂Si-Ca线→钢包底吹氩软吹→130mm2方坯铸机→铸坯表面质量检查→高速线材轧机轧制∮12～14mm盘条→轧后标准斯太尔摩控冷线冷却→成品包装。
出钢前20分加入高碳铬铁，并在LF炉中进行微调，出钢1/3时加入钒铁，微合金加入量具体如下：Cr：0.30-0.43％，V：0.02-0.08％，C：0.77-0.81％，Mn：0.80-0.90％。开轧温度为1000℃以上，保证Cr、V元素固溶。终轧温度为1000-1040℃，轧后的两阶段水冷要均匀冷却，第一段水冷后温度为880-920℃，吐丝温度为810-850℃。风冷速度为5-8℃/s，风冷终冷温度为600-570℃，之后缓慢冷却。所生产的盘条组织性能稳定，平均片层间距为0.18μm，平均珠光体球团直径为8.4μm，φ12-12.5mm盘条的抗拉强度为1160-1220MPa，面缩率为30-36％，优于用户要求抗拉强度≥1150MPa，面缩率≥28％，用于拔制1860MPa钢绞线。φ13.0？4.0mm盘条的抗拉强度为1200-1260MPa，面缩率为29-44％，用于拔制2000MPa钢绞线，满足了用户要求。
由于季节变化，盘条的冷却速度也发生了变化，为此制订了不同月份的Cr含量控制范围，如下表所示。
不同月份的Cr含量，％
| 月份 | 1、2、3、11、12 | 其余月份 |
| 1860MPa用82B盘条 | 0.30-0.37 | 0.34-0.41 |
| 2000MPa用82B盘条 | 0.34-0.41 | 0.37-0.43 |
下表为首钢生产φ13mm82B盘条的实物质量。
| 月份 | 批号 | 炉号 | 化学成分，％ | 抗拉强度MPa | 面缩率％ | |||||||||||||||
| C | Si | Mn | P | S | Cr | V | ||||||||||||||
| 7月 | 7-1130 | 3D63043D63053F66023F66033F66043F66073F66063F66063F6605 | 0.780.790.780.790.800.790.810.810.78 | 0.210.200.210.190.210.230.230.230.21 | 0.800.830.820.780.820.820.830.830.83 | 0.0130.0180.0120.0140.0130.0090.0100.0100.011 | 0.0070.0060.0040.0110.0050.0090.0060.0060.008 | 0.380.370.400.370.370.390.380.380.39 | 0.0800.0650.0690.0690.0700.0670.0680.0680.070 | 124012501260125012601260126012601260 | 30 | |||||||||
| 7-1131 | 29 | |||||||||||||||||||
| 7-1132 | 31 | |||||||||||||||||||
| 7-1133 | 32 | |||||||||||||||||||
| 7-1134 | 30 | |||||||||||||||||||
| 7-1135 | 34 | |||||||||||||||||||
| 7-1136 | 30 | |||||||||||||||||||
| 7-1202 | 30 | |||||||||||||||||||
| 7-1203 | 31 | |||||||||||||||||||
| 平均值 | 0.7920.810.78 | 0.2130.230.19 | 0.8180.830.78 | 0.0120.0180.009 | 0.0690.0110.004 | 0.3810.40.37 | 0.06960.080.065 | 125612601240 | 30.8 | |||||||||||
| 最大值 | 34 | |||||||||||||||||||
| 最小值 | 29 | |||||||||||||||||||
下表为首钢生产φ12.5mm82B盘条的实物质量。
| 月份 | 批号 | 炉号 | 化学成分，％ | 抗拉强度 | 面缩率％ | |||||||||||
| C | Si | Mn | P | S | Cr | MPa | ||||||||||
| 2月 | 2-1327 | 3F17583E17213F17093D13063F18153F18143F18123D13493D13483E17593F17573D13443D13433E79553F80213D74883D74833F77933F77923D66033D66023E67563E67493F6858 | 0.770.80.80.770.780.790.810.790.80.810.770.790.80.790.770.790.790.800.800.790.780.810.770.78 | 0.210.20.20.240.220.210.210.210.210.220.220.220.230.210.190.220.230.230.230.220.200.210.220.29 | 0.840.820.810.830.820.790.810.80.810.810.840.810.810.810.790.830.870.840.840.860.850.830.800.85 | 0.0130.0100.0140.0130.0170.0140.0130.0130.0120.0140.0160.0150.0140.0130.0130.0180.0140.0100.0100.0180.0120.0150.0140.010 | 0.0090.0060.0060.0070.0070.0090.0100.0060.0070.0080.0080.0080.0070.0070.0070.0060.0070.0060.0060.0070.0060.0110.0080.006 | 0.320.310.320.330.310.30.310.300.300.300.330.330.340.360.350.370.370.370.370.360.380.360.380.36 | 119012001170116011701170118011901160116011901180119011851190121012001220119512001190118011801160 | 31 | ||||||
| 2-1328 | 32 | |||||||||||||||
| 2-1329 | 34 | |||||||||||||||
| 2-1330 | 34 | |||||||||||||||
| 2-1331 | 36 | |||||||||||||||
| 2-1332 | 36 | |||||||||||||||
| 2-1333 | 31 | |||||||||||||||
| 2-1334 | 30 | |||||||||||||||
| 2-1335 | 35 | |||||||||||||||
| 2-1336 | 35 | |||||||||||||||
| 2-1337 | 33 | |||||||||||||||
| 2-1338 | 32 | |||||||||||||||
| 2-1339 | 32 | |||||||||||||||
| 7、8、9月 | 9-147 | 32 | ||||||||||||||
| 9-148 | 32 | |||||||||||||||
| 8-1325 | 33 | |||||||||||||||
| 8-1326 | 32 | |||||||||||||||
| 8-1327 | 30 | |||||||||||||||
| 8-1328 | 32 | |||||||||||||||
| 7-1536 | 35 | |||||||||||||||
| 7-1537 | 30 | |||||||||||||||
| 7-1538 | 31 | |||||||||||||||
| 7-1540 | 34 | |||||||||||||||
| 7-1541 | 34 | |||||||||||||||
| 平均值 | 0.790.81 | 0.220.29 | 0.820.87 | 0.0140.18 | 0.0070.11 | 0.340.38 | 11841220 | 33 | ||||||||
| 最大值 | 36 | |||||||||||||||
| 最小值 | 0.77 | 0.19 | 0.79 | 0.1 | 0.06 | 0.30 | 1160 | 30 |
Claims (1)
1、一种生产钢绞线用82B盘条的微合金化方法，其中钢的化学成份重量百分比为：C：0.77-0.81％、Mn：0.80-0.90％、P：0.009-0.018％、S：0.004-0.011％、Si：0.19-0.29％、其余为Fe，微合金化包括钢包脱氧合金化、LF炉精炼，其特征在于：出钢前20分加入高碳铬铁，并在LF炉中进行微调，出钢1/3时加入钒铁，微合金加入量具体如下：Cr：0.30-0.43％，V：0.02-0.08％，C：0.77-0.81％，Mn：0.80-0.90％；开轧温度为1000℃以上，保证Cr、V元素固溶，终轧温度为1000-1040℃，轧后的两阶段水冷要均匀冷却，第一段水冷后温度为880-920℃，吐丝温度为810-850℃，风冷速度为5-8℃/s，风冷终冷温度为600-570℃，之后缓慢冷却。