CN100350589C - Shallow trench isolation method forming round corners by cleaning - Google Patents
Shallow trench isolation method forming round corners by cleaning Download PDFInfo
- Publication number
- CN100350589C CN100350589C CNB2005100018720A CN200510001872A CN100350589C CN 100350589 C CN100350589 C CN 100350589C CN B2005100018720 A CNB2005100018720 A CN B2005100018720A CN 200510001872 A CN200510001872 A CN 200510001872A CN 100350589 C CN100350589 C CN 100350589C
- Authority
- CN
- China
- Prior art keywords
- solution
- pad oxide
- etch
- ditches
- corner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to an isolation method for a shallow channel with round edge corners formed by cleaning. The present invention has the steps that a hard mask layer is deposited on a silicon substrate covered with a pad oxide layer; the hard mask layer and the pad oxide layer are decorated with patterns in order to form an opening, so the silicon substrate is exposed; the exposed silicon substrate is etched to form a channel; an inner liner is formed for the channel; an insulating material is filled in the channel; the insulating material is carried out for the back etching process; the hard mask layer and the pad oxide layer are removed in order to form a shallow channel isolation structure, wherein a silicon consumption solution is used in the cleaning process before the formation of the inner liner, so the edge corners of the channel become round in the cleaning process in order to solve the thinning problem of the edge corners of shallow channel isolation in a simple, rapid and low cost way.
Description
Technical field
The present invention is about a kind of semiconductor making method, particularly about a kind of shallow trench isolation (ShallowTrench Isolation; STI) manufacture method.
Background technology
In manufacture of semiconductor, the technology that is widely used in most the active region isolation traditionally is localized oxidation of silicon method (LOCOS), yet LOCOS can produce beak and invade active region, below the passage length micro to 0.25 of metal-oxide semiconductor (MOS) (MOS) element micron, LOCOS has been difficult to the demand of equivalence element insulation and integrated level.STI is a most general also most important isolation technology in the MOS processing procedure below 0.25 micron, and it in the sti trench canal, and applies cmp (ChemicalMechanical Polishing with the silicon dioxide backfill; CMP),, more can almost ignore the beak phenomenon, obtain maximum current densities simultaneously except planarization (globalplanarization) surface that can obtain wide area.
With reference to Fig. 1, a typical STI manufacture process is growth pad oxide 12 and a deposition pad nitration case 14 on silicon base 10, in pad nitration case 14 and pad oxide 12, form opening 16 to expose silicon base 10 to the open air through little shadow and etch process, again from opening 16 downward etching silicon substrates 10 to form irrigation canals and ditches 18, in irrigation canals and ditches 18, fill silicon dioxide, and, remove pad nitration case 14 and pad oxide 12 again and just finish sti structure with this silicon dioxide of CMP etch-back.Yet, as shown in Figure 2, when subsequent deposition grid oxic horizon 20, cause near the oxide layer thinning the STI corner 22 because of stress, cause the puncture voltage of the MOS element of finishing future to reduce and high leakage current, make the function deterioration of element.This problem is because corner 22 is close to the right angle, as shown in Figure 3, when deposition grid oxic horizon 20, the oxide 24 that is positioned on the silicon base 10 is pushed mutually with the oxide 26 that is positioned at the STI side, cause oxide 28 attenuation at 22 places, corner, and the corner thinning of STI can be reduced in slynessization corner 22.
Edge treated to STI is to suppress the corner effect and keep one of important topic of grid oxic horizon integrated level.People such as Bai Zhiyang propose a kind of STI processing procedure in No. the 6670279th, United States Patent (USP), on the sidewall of pad oxide and pad nitration case, forming spacer oxide (spaceroxide) earlier before the etching sti trench canal, utilize the some of this spacer oxide as shielding etching sti trench canal, the complete sti trench canal of etching again after removing this spacer oxide, thereby in follow-up interior coffin oxidation process, obtain slick and sly STI corner.Though the method can reduce the thinning of STI corner, increase the step and the time of STI processing procedure because of the utilization spacer oxide, make cost improve.Especially time-consuming longer in order to form used oxidate processing procedure of spacer oxide or polysilicon deposition and oxidation process, and make the etching of sti trench canal be forced to be divided into the discontinuous step of twice, the processing procedure time and the cost of increase are all a lot.Moreover, along with component size is dwindled gradually, except the difficulty raising of spacer oxide processing procedure, more limited the size and the density of element micro.
Therefore, a kind ofly forming the STI processing procedure of slick and sly corner with less step, short period and lower cost, is to be the institute Ji.
Summary of the invention
One of purpose of the present invention, be to propose a kind of with simple, fast and low cost method solve the problem of the corner thinning of STI.
More specifically, one of purpose of the present invention is to propose a kind of STI processing procedure with slick and sly corner.
In a kind of STI processing procedure, comprise that the hard screen of deposition is being coated with on the silicon base of pad oxide, this hard screen of patterning and pad oxide expose this silicon base to the open air to form opening, this silicon base that exposes to the open air of etching is to form irrigation canals and ditches, for these irrigation canals and ditches form liner, fill insulant in these irrigation canals and ditches, this insulant of etch-back, remove this hard screen and pad oxide to form sti structure, according to the present invention, use in the cleaning process when the formation liner and can consume the solution of silicon, thereby make corner while quilt slynessization in cleaning process of these irrigation canals and ditches, and then obtain to have the sti structure of slick and sly corner.
Owing to utilize the corner of the solution slynessization irrigation canals and ditches of the meeting of use consume silicon when cleaning, therefore do not increase the step of STI processing procedure, do not need to expend long handling procedure, and cost is very low.
Description of drawings
Fig. 1 is used for illustrating a typical STI processing procedure;
Fig. 2 is the schematic diagram of STI corner thinning;
Fig. 3 is that amplify the part of the STI corner of Fig. 2;
Fig. 4 is the schematic diagram behind the pad oxide of growing up on the silicon base, the hard screen of deposition and coating photoresistance;
Fig. 5 is the schematic diagram behind hard screen of etching and the pad oxide;
Fig. 6 is the schematic diagram after the trench etched;
Fig. 7 is the schematic diagram that retracts behind hard screen and the pad oxide edge;
Fig. 8 is the schematic diagram after cleaning;
Fig. 9 is the schematic diagram behind the coffin in growing up;
Figure 10 is the schematic diagram behind the deposition insulant;
Figure 11 is the schematic diagram behind the etch-back insulant;
Figure 12 is the schematic diagram behind the hard screen of removal;
Figure 13 is the schematic diagram behind the removal pad oxide;
Figure 14 is the schematic diagram of another embodiment that retracts the edge of pad oxide; And
Figure 15 is the schematic diagram of another embodiment of cleaning procedure.
Component symbol
10 silicon base, 12 pad oxides, 14 pad nitration cases
16 openings, 18 irrigation canals and ditches, 20 grid oxic horizons
Oxide on 24 silicon base 10 of 22 STI corners
The thinning oxide at 22 places, oxide 28 corners of 26 STI sides
30 silicon base, 32 pad oxides, 34 hard screens
36 photoresistances, 38 openings, 40 irrigation canals and ditches
Coffins in the corner 46 of 42 sharp-pointed corner 44 slynesses
48 insulants, 50 insulants, 52 sti structures
STI corner 56 coverings of 54 slynesses
Embodiment
Fig. 4 to 13 is one embodiment of the present of invention.When carrying out the STI processing procedure; earlier wafer is put into rinse bath; utilize grit or the Impurity removal of the method for chemistry or physics, for example use RCA to clean or its improvement processing procedure, to prevent that these grits or impurity from impacting follow-up processing procedure and to make that element can't operate as normal with crystal column surface.
After wafer cleans, as shown in Figure 4, growth pad oxide 32, the hard screen 34 of formation and coating photoresistance 36 on silicon base 30.The formation of pad oxide 32 can utilize the silicon dioxide of thermal oxidation method growth 100-300 in the hot environment that contains oxygen or aqueous vapor, to use the resilient coating between silicon base 30 and the hard screen 34 as.Hard screen 34 can use nitride or silicon nitride, for example under 650-800 ℃ with Low Pressure Chemical Vapor Deposition (Liquid Phase Chemical VaporDeposition; LPCVD) or under 250-400 ℃ promote chemical vapour deposition technique (PlasmaEnhanced Chemical Vapor Deposition with ion; PECVD) silicon nitride of deposition 800-2500 .
As shown in Figure 5, to photoresistance 36 exposure and develop to define the pattern of sti trench canal, the photoresistance 36 with patterning serves as that shielding hard screen 34 of etching and pad oxide 32 expose silicon base 30 to form opening 38 again.The patterning of hard screen 34 and pad oxide 32 can use the dry-etching method to stop at the surface of silicon base 30.
As shown in Figure 6, from opening 38 downward etching silicon substrates 30 to form irrigation canals and ditches 40.If the use ion(ic) etching, the etching of Fig. 5 and Fig. 6 can be finished in same reative cell, serves as the hard screen 34 of shielding etching, pad oxide 32 and silicon base 30 with photoresistance 36 for example, up to finishing irrigation canals and ditches 40.
As shown in Figure 7, burn (ozone ashing) and sulfuric acid with ozone and brew and remove photoresistance 36, utilize etching to retract the edge of hard screen 34 and pad oxide 32 again, with the corner 42 of exposing irrigation canals and ditches 40 to the open air; Or soak high temperature phosphoric acid to divest photoresistance 36, while is also etched with the edge of the hard screen 34 that silicon nitride is made, soak the edge of hydrofluoric acid with etching pad oxide 32 again, corner 42 is because the edge of hard screen 34 and pad oxide 32 is pulled and exposes to the open air out.
Also can use dry ecthing method to retract the edge of hard screen 34 and pad oxide 32 and become structure shown in Figure 7, for example the STI that proposes in No. the 6828248th, United States Patent (USP) with reference to people such as Tao Hongyuan retreats processing procedure.
As shown in Figure 8, in the cleaning process of interior coffin processing procedure, use can consume silicon solution, for example temperature is greater than 65 ℃ standard cleaning one (Standard Clean 1; SC1) solution, ammonia concn be higher than SC1 solution, ozone and the hydrofluoric acid of concentration of hydrogen peroxide mixed solution (FPM), contain can the corrosion acid of silicon or other can corrode the solution of silicon, the solution that for example contains potassium hydroxide (KOH), these solution that can consume silicon make corner 42 while in cleaning process become slick and sly corner 44 also by slynessization.
As shown in Figure 9, the silicon dioxide of growth 150-700 also can and then deposit one deck nitride as interior coffin 46 on this silicon dioxide 46 in the high-temperature oxydation boiler tube.
As shown in figure 10, deposition insulant 48 is to fill irrigation canals and ditches 40.For example use high density ion vapor deposited method (HDP CVD), silica deposit extremely is full of irrigation canals and ditches 40 and opening 38 fully.
As shown in figure 11, use for example CMP etch-back insulant 48, this etch-back stops at hard screen 34, obtains the surface of planarization, and stays the surface of insulant 50 to hard screen 34.
As shown in figure 12, remove hard screen 34.For example, when hard screen 34 is silicon nitride, using 180 ℃ the hot phosphoric acid solution or mixed solution (HPO) etching of silicon nitride of use phosphoric acid and hydrogen peroxide, is the barrier layer with silicon dioxide 32 and 50.
As shown in figure 13, remove pad oxide 32, for example use the diluent hydrofluoric acid solution etching, also can add ammonium fluoride as buffer.In the sti structure of finishing 52, previous interior coffin 46 and HDP oxide 50 have combined, and have slick and sly corner 54.The preferably passes through one rapid thermal treatment (RTP) again, makes oxide 52 finer and close.
Change ground, Figure 14 retracts another embodiment at the edge of pad oxide 32, covers the silicon base 30 that exposes to the open air with covering 56 earlier, re-uses dry ecthing or wet etching the edge of pad oxide 32 is retreated, dismantle and carry out cleaning procedure after 56, make corner 42 slynessizationes simultaneously.
Change ground, another embodiment of Figure 15 cleaning procedure, after finishing the step of Fig. 4 to 6, use is cleaned greater than the solution to the rate of etch of silicon the rate of etch of silicon dioxide, for example the mixed solution of nitric acid and hydrofluoric acid also can add acetic acid as buffer, in this process, pad oxide 32 is etched than silicon base more than 30, therefore obtains slick and sly corner 44 simultaneously.Also can use hydrofluoric acid that the edge of pad oxide 32 is retreated earlier, to expose corner 42 to the open air, re-use temperature and make corner 42 slynesses turn to corner 44 greater than 65 ℃ SC1 solution, SC1 solution, FPM solution or other solution of understanding loss silicon that ammonia concn is higher than concentration of hydrogen peroxide.
According to principle of the present invention, in the cleaning process of interior coffin processing procedure, use the solution that can consume silicon, make the corner of irrigation canals and ditches in cleaning procedure also simultaneously by slynessization, therefore needn't increase other extra step again, reach in mode simply, fast and cheaply and solve the problem of STI corner thinning.
Claims (20)
1. one kind by cleaning the shallow trench isolation method form slick and sly corner, it is characterized in that, comprises the following steps:
Depositing hard screen is being coated with on the silicon base of pad oxide;
This hard screen of patterning and pad oxide expose this silicon base to the open air to form opening;
This silicon base that exposes to the open air of etching is to form irrigation canals and ditches;
The edge that retracts this pad oxide is to expose the corner of these irrigation canals and ditches to the open air; And
Bestow cleaning, make this corner of exposing to the open air simultaneously by slynessization.
2. the method for claim 1 more comprises the following steps:
For these irrigation canals and ditches form liner, comprise to cover on this slyness corner;
Fill insulant in these irrigation canals and ditches;
This insulant of etch-back; And
Remove this hard screen and pad oxide to form shallow slot isolation structure.
3. the method for claim 1 is characterized in that, this step that retracts the edge of this pad oxide comprises that use has the edge of this pad oxide of solution etching of high rate of etch to this pad oxide.
4. method as claimed in claim 3 is characterized in that this solution comprises hydrofluoric acid.
5. the method for claim 1 is characterized in that, this step that retracts the edge of this pad oxide comprises:
Cover the surface that this shallow trench is exposed to the open air; And
The edge of this pad oxide of etching.
6. the method for claim 1 is characterized in that, this step of bestowing cleaning comprises that use can consume the solution of silicon and clean.
7. method as claimed in claim 6 is characterized in that, this solution comprises that temperature is greater than 65 ℃ SC1 solution.
8. method as claimed in claim 6 is characterized in that, this solution comprises that ammonia concn is higher than the SC1 solution of concentration of hydrogen peroxide.
9. method as claimed in claim 6 is characterized in that this solution comprises the mixed solution of ozone and hydrofluoric acid.
10. method as claimed in claim 2 is characterized in that the step of this this insulant of etch-back comprises cmp.
11. one kind by cleaning the shallow trench isolation method form slick and sly corner, it is characterized in that, comprises the following steps:
Depositing hard screen is being coated with on the silicon base of pad oxide;
This hard screen of patterning and pad oxide expose this silicon base to the open air to form opening;
This silicon base that exposes to the open air of etching is to form irrigation canals and ditches; And
Bestow cleaning, make the corner slynessization of these irrigation canals and ditches.
12. method as claimed in claim 11 is characterized in that, more comprises the following steps:
For these irrigation canals and ditches form liner, comprise to cover on this slyness corner;
Fill insulant in these irrigation canals and ditches;
This insulant of etch-back; And
Remove this hard screen and pad oxide to form shallow slot isolation structure.
13. method as claimed in claim 11 is characterized in that, this step of bestowing cleaning comprises:
Use is cleaned first solution that this pad oxide has high rate of etch; And
Use second solution that can consume silicon to clean.
14. method as claimed in claim 13 is characterized in that, this first solution comprises hydrofluoric acid.
15. method as claimed in claim 13 is characterized in that, this second solution comprises that temperature is greater than 65 ℃ SC1 solution.
16. method as claimed in claim 13 is characterized in that, this second solution comprises that ammonia concn is higher than the SC1 solution of concentration of hydrogen peroxide.
17. method as claimed in claim 13 is characterized in that, this second solution comprises the mixed solution of ozone and hydrofluoric acid.
18. method as claimed in claim 11, it is characterized in that, this step of bestowing cleaning comprises edge and this irrigation canals and ditches that use solution to clean this pad oxide, this solution has first rate of etch to this pad oxide, this silicon base is had second rate of etch, and this first rate of etch is greater than this second rate of etch.
19. method as claimed in claim 18 is characterized in that, this solution comprises the mixed solution of nitric acid and hydrofluoric acid.
20. method as claimed in claim 12 is characterized in that, the step of this this insulant of etch-back comprises this insulant of cmp.