CH622534A5 - Binder component for PUR binders, process for the preparation thereof, and the use of this component - Google Patents

Description

622534 622534

2 2nd

PATENTANSPRÜCHE PATENT CLAIMS

1. Bindemittelkomponente für PUR-Bindemittel, bestehend aus einer kolloidalen Lösung eines oder mehrerer, im Reinzustand mischbarer oder nichtmischbarer Polyole in einem flüssigen Medium. 1. Binder component for PUR binders, consisting of a colloidal solution of one or more, in the pure state miscible or immiscible polyols in a liquid medium.

2. Bindemittelkomponente für PUR-Bindemittel nach Anspruch 1, bestehend aus einer kolloidalen Lösung eines oder mehrerer, im Reinzustand mischbarer oder nichtmischbarer Polyole in einem Netzmittel und/oder Stabilisatoren enthaltenden flüssigen Medium. 2. Binder component for PUR binders according to claim 1, consisting of a colloidal solution of one or more, in the pure state miscible or immiscible polyols in a wetting agent and / or stabilizer-containing liquid medium.

3. Bindemittelkomponente nach Anspruch 1 oder 2, gekennzeichnet durch Wasser als flüssiges Medium. 3. Binder component according to claim 1 or 2, characterized by water as the liquid medium.

4. Bindemittelkomponente nach einem der Ansprüche 1 bis 3, gekennzeichnet durch 5 bis 45, vorzugsweise 10 bis 30 Gew.-% Polyol und 0,02 bis 2,5% oberflächenaktive Substanz, wobei der Rest aus dem flüssigen Medium besteht. 4. Binder component according to one of claims 1 to 3, characterized by 5 to 45, preferably 10 to 30 wt .-% polyol and 0.02 to 2.5% surface-active substance, the rest consisting of the liquid medium.

5. Bindemittelkomponente nach einem der vorhergehenden Ansprüche, gekennzeichnet durch einen Polyester oder einen Polyäther als Polyol. 5. Binder component according to one of the preceding claims, characterized by a polyester or a polyether as a polyol.

6. Verfahren zur Herstellung der Bindemittelkomponente nach Anspruch 1, dadurch gekennzeichnet, dass man ein Polyolkolloidal in einem flüssigen Medium löst. 6. A process for the preparation of the binder component according to claim 1, characterized in that a polyol colloidal is dissolved in a liquid medium.

7. Verfahren nach Anspruch 6, dadurch gekennzeichnet, dass man ein Polyol in Gegenwart von Netzmitteln und/oder Stabilisatoren kolloidal in einem flüssigen Medium löst. 7. The method according to claim 6, characterized in that a polyol is colloidally dissolved in a liquid medium in the presence of wetting agents and / or stabilizers.

8. Verwendung der Bindemittelkomponente nach Anspruch 1 zum Verbinden von teilchenförmigen Stoffen, dadurch gekennzeichnet, dass man die Bindemittelkomponente mit einem Polyisocyanat und danach mit dem teilchenförmigen Stoff mischt und aushärtet oder die Bindemittelkomponente mit dem teilchenförmigen Stoff mischt und danach ein Polyisocyanat zumischt und aushärtet. 8. Use of the binder component according to claim 1 for joining particulate substances, characterized in that the binder component is mixed and cured with a polyisocyanate and then with the particulate substance or the binder component is mixed with the particulate substance and then a polyisocyanate is mixed in and cured.

Es ist bekannt, zum Binden pulver-, faser-, span- oder granulatförmiger Stoffe nach Press- bzw. Heisspressverfahren Bindemittel wie Harnstoff-Formaldehyd, Phenol-Formaldehyd oder Melaminharze zu verwenden. Auch wurde schon vorgeschlagen, Epoxidharze und Polyol-Polyisocyanatsysteme zu verwenden. Die Verwendung von PUR-Systemen (Polyurethan-Systemen) als Bindemittel war bisher in vielen Fällen unwirtschaftlich, weil grosse Mengen Polyol und Isocyanat benötigt wurden, um solche Festigkeiten der damit gebundenen Materialien zu erreichen, wie mit anderen Bindemitteln. It is known to use binders such as urea-formaldehyde, phenol-formaldehyde or melamine resins for binding powder, fiber, chip or granular materials by pressing or hot pressing processes. It has also been proposed to use epoxy resins and polyol polyisocyanate systems. In many cases, the use of PUR systems as a binder has been uneconomical because large amounts of polyol and isocyanate were required to achieve the strength of the materials bound to them, as with other binders.

PUR-Systeme haben jedoch ganz spezielle Vorteile, da die Isocyanatkomponente durch ihre hohe Reaktionsfähigkeit mit aktiven Gruppen an vielen Oberflächen chemische Bindungen eingeht und dadurch hervorragende Klebefugen schafft. PUR-Systeme lassen sich daher bekanntlich zum Verbinden der verschiedensten Materialien verwenden. Ausser dem relativ hohen Preis standen aber bisher noch zwei rein technische Hindernisse einer breiteren Verwendung von PUR-Systemen als Bindemittel entgegen. However, PUR systems have very special advantages because the isocyanate component forms chemical bonds on many surfaces due to its high reactivity with active groups, thereby creating excellent adhesive joints. It is well known that PUR systems can be used to connect a wide variety of materials. In addition to the relatively high price, there were previously two purely technical obstacles to the broader use of PUR systems as binders.

Es ist Stand der Technik, dass z. B. bei der Spanplattenfertigung der eingesetzte Leim (meistens ein Harnstoff-Formaldehyd- oder Phenolharz) optimal fein verdüst werden muss, um hohe Festigkeiten zu erreichen. Es ist aus der Fachliteratur bekannt, dass die Festigkeit von Spanplatten eine Funktion der Tröpfchengrösse des zugedüsten Leimes ist («Technologie der Spanplatte», Deppe & Ernst, Holz-Zentralbiatt Verlags GmbH, Stuttgart, Seite 128). Das deutlich erkennbare Maximum liegt laut dieser Darstellung bei einer Tröpfchengrösse von 10 |.im und darunter. Die Tröpfchengrösse ist einer experimentellen Überprüfung leicht zugänglich, da die Tröpfchen auf Glasplatten aufgefangen und unter dem Mikroskop vermessen werden können. In der technischen Praxis werden jedoch Tröpfchengrössen von unter 100 um nur selten erreicht. It is state of the art that, for. B. in chipboard production, the glue used (usually a urea-formaldehyde or phenolic resin) must be optimally atomized in order to achieve high strengths. It is known from the specialist literature that the strength of chipboard is a function of the droplet size of the glue sprayed in (“Chipboard Technology”, Deppe & Ernst, Holz-Zentralbiatt Verlags GmbH, Stuttgart, page 128). According to this illustration, the clearly recognizable maximum is a droplet size of 10 | .im and below. The droplet size is easily accessible for experimental verification, since the droplets can be collected on glass plates and measured under the microscope. In technical practice, however, droplet sizes of less than 100 µm are rarely achieved.

Beim Einsatz von höhermolekularen Polyhydroxylverbin-dungen ergibt sich, dass diese Verbindungen aufgrund der vielen Wasserstoffbrückenbindungen dickflüssig, ja sogar zähflüssig sind und sich auch durch Temperaturerhöhung nur unwesentlich dünnflüssiger machen lassen. Es ist also nicht möglich, diese höherviskosen Flüssigkeiten direkt fein genug zu verdüsen. Dies ist jedoch eine unabdingbare Notwendigkeit für einen wirtschaftlich sinnvollen Einsatz. An sich im Einzelfall verwendbare organische Lösungsmittel, wie Aceton, sind aus Gründen des Brandschutzes, der Kosten und des Umweltschutzes für die technische Praxis nicht sinnvoll. When using higher molecular weight polyhydroxyl compounds, it turns out that due to the many hydrogen bonds, these compounds are viscous, even viscous, and can only be made slightly less viscous by increasing the temperature. It is therefore not possible to atomize these highly viscous liquids directly enough. However, this is an essential requirement for an economically sensible use. Organic solvents that can be used in individual cases, such as acetone, are not useful for technical practice for reasons of fire protection, costs and environmental protection.

Ein weiterer Punkt ist die bekannte Tatsache, dass man die Eigenschaften von durchgehärteten Zweikomponentensystemen durch sachkundige Auswahl der einzelnen Komponenten in einem weiten Bereich variieren kann. Es ist dazu notwendig, etwa bei PUR-Systemen die Isocyanatkomponente aus mehreren verschiedenen Isocyanaten zu mischen oder auch für die Polyolkomponente nicht ein einheitliches Polyol, sondern eine Mischung aus mehreren Polyolen zu verwenden. Je nach Kettenlänge und/oder Verzweigungen der einzelnen Polyole lassen sich bekanntlich die mechanischen Eigenschaften des ausgehärteten und durchreagierten Systems in weiten Bereichen einstellen. Another point is the well-known fact that the properties of through-hardened two-component systems can be varied within a wide range by the expert selection of the individual components. It is necessary to mix the isocyanate component from several different isocyanates, for example in PUR systems, or to use a mixture of several polyols rather than a uniform polyol for the polyol component. Depending on the chain length and / or branching of the individual polyols, it is known that the mechanical properties of the cured and fully reacted system can be adjusted over a wide range.

Diese an sich bekannte und viel benutzte Variationsmöglichkeit stösst aber auf dem PUR-Gebiet auf die Schwierigkeit, dass sich nur wenige Polyole untereinander mischen lassen. In dem Kunststoffhandbuch «BAYER Kunststoffe», 3. Ausgabe, Leverkusen 1963, Seite 60, ist diese Tatsache in einem besonderen Absatz hervorgehoben. However, this well-known and widely used variation option encounters the difficulty in the PUR field that only a few polyols can be mixed with one another. This fact is highlighted in a special paragraph in the plastics manual “BAYER Kunststoffe”, 3rd edition, Leverkusen 1963, page 60.

Es wurde nun gefunden, dass sich die beiden oben skizzierten grundsätzlichen Schwierigkeiten, die einer Verwendung von PUR-Systemen als Bindemittel für pulver-, faser, span-oder granulatförmige Stoffe bisher zum Teil entgegenstanden, dadurch überraschenderweise vermieden werden können, dass man die Polyolkomponente kolloidal in einem flüssigen Medium löst, z. B. in Wasser oder einem chlorierten Kohlenwasserstoff. It has now been found that the two basic difficulties outlined above, which have hitherto partially opposed the use of PUR systems as binders for powder, fiber, chip or granular substances, can surprisingly be avoided by colloidally isolating the polyol component dissolves in a liquid medium, e.g. B. in water or a chlorinated hydrocarbon.

Entgegen der Erwartung des Fachmannes wurde gefunden, dass ein Wasseranteil in der Polyolkomponente die Reaktion des Polyols mit dem Isocyanat nicht stört. Ferner ist bekannt, dass z. B. Holzsspäne oder Holzstaub eine sehr eng tolerierte Feuchtigkeit besitzen sollen, um zu qualitativ befriedigenden Teilen verpresst werden zu können. Das erfindungsgemässe System, dessen Wassergehalt sich jedoch in einem weiten Bereich mühelos verändern lässt, gestattet es mm, durch eben diesen einstellbaren Wassergehalt die Gesamtfeuchtigkeit im beleimten Pressgut genau einzuhalten. Die Messung der Feuchte im Pressgut vor der Beleimung ist etwa über ein Dekameter (eine Messung der Dielektrizitätskonstante des Materials) schnell und einfach möglich. Contrary to the expectation of the person skilled in the art, it was found that a proportion of water in the polyol component does not interfere with the reaction of the polyol with the isocyanate. It is also known that, for. B. wood shavings or wood dust should have a very tightly tolerated moisture in order to be pressed into qualitatively satisfactory parts. The system according to the invention, the water content of which can be changed effortlessly over a wide range, allows mm to precisely maintain the total moisture in the glued pressed material by means of this adjustable water content. The moisture in the pressed material can be measured quickly and easily using a decameter (a measurement of the dielectric constant of the material).

Im Zuge von Versuchen, deren Ziel es war, die Bindemittelmengen herabzusetzen und die Wasserempfindlichkeit von PUR-Bindemitteln kennenzulernen, wurde gefunden, dass sich Polyole in Wasser kolloidal lösen lassen. Diese Lösung ist leicht opalisierend, zeigt den Tyndalleffekt und hat besonders bei höherem Wasseranteil eine sehr niedrige Viskosität. Sie besteht zu etwa 5 bis 45%, insbesondere 10 bis 30% aus Polyol und zu etwa 0,02 bis 2,5 % aus Netzmittel, wobei der Rest Wasser ist. Diese kolloidale Lösung des an sich wasserunlöslichen Polyols lässt sich nun durch die niedrige Viskosität sehr einfach verdüsen und z. B. mit pulver-, faser-, span- oder granulatförmigem Mahlgut gleichmässig vermischen. Die passende Menge an Polyisocyanat kann der kolloidalen Polyol-lösung vor, während oder vorzugsweise nach dem Vermischen mit zu verbindendem Mahlgut zugegeben werden, z. B. ebenfalls durch Verdüsen. Danach kann in an sich bekannter Weise s In the course of experiments, the aim of which was to reduce the amounts of binders and to learn about the water sensitivity of PUR binders, it was found that polyols can be colloidally dissolved in water. This solution is slightly opalescent, shows the Tyndall effect and has a very low viscosity, especially with a higher water content. It consists of approximately 5 to 45%, in particular 10 to 30%, polyol and approximately 0.02 to 2.5% wetting agent, the rest being water. This colloidal solution of the water-insoluble polyol can now be atomized very easily by the low viscosity and z. B. mix evenly with powder, fiber, chip or granular regrind. The appropriate amount of polyisocyanate can be added to the colloidal polyol solution before, during or preferably after mixing with the regrind to be joined, e.g. B. also by atomizing. Then s

10 10th

15 15

20 20th

25 25th

30 30th

35 35

40 40

45 45

50 50

55 55

60 60

65 65

unter erhöhter Temperatur und Druck zu beliebigen Formteilen verpresst werden. can be pressed to any shape under elevated temperature and pressure.

Die vorstehenden Ausführungen gelten sinngemäss auch für andere flüssige Medien als Wasser, z. B. chlorierte Kohlenwasserstoffe. The above statements apply mutatis mutandis to liquid media other than water, eg. B. chlorinated hydrocarbons.

Beim Heisspressen können keine brennbaren Dämpfe entstehen, weil keine brennbaren Lösungsmittel verwendet werden. Der Wassergehalt des Bindemittels schliesst Staubexplosionen weitgehend aus. Das mit der Polyollösung behandelte staub-, faser-, span- oder granulatförmige Gut ist längere Zeit lagerbeständig. Flammable vapors cannot be produced during hot pressing because flammable solvents are not used. The water content of the binder largely excludes dust explosions. The dust, fiber, chip or granular material treated with the polyol solution has a long shelf life.

Es hat sich sogar als günstig erwiesen, die wässerige Polyollösung einige Zeit auf das zu bindende Material einwirken zu lassen, weil dabei der Wasseranteil der Lösung in die Staub-, Faser-, Span- bzw. Granulatteilchen diffundiert. Das führt dazu, dass an der Oberfläche dieser Teilchen das höhermolekulare Polyol praktisch wasserfrei zurückbleibt und mit dem hinzukommenden Polyisocyanat reagieren kann. It has even proven to be advantageous to let the aqueous polyol solution act on the material to be bound for some time because the water content of the solution diffuses into the dust, fiber, chip or granulate particles. This means that the higher molecular weight polyol remains practically anhydrous on the surface of these particles and can react with the added polyisocyanate.

Die an Pressteilen ermittelten Werte, etwa der Biegefestigkeit, beweisen die Wirksamkeit des erfindungsgemässen Bindemittelsystems. Trotz der bekannten Streuung der Messwerte von Biegebruchversuchen lässt eine statistische Untersuchung durch ein Bestimmtheitsmass von r2 = 0.91 den Schluss zu, dass die Funktion Bindemittelanteil gegen Biegebruchlast einer logarithmischen Beziehung folgt (Bruchlast = a + b in Bindemittelgehalt ( %)). Die Konstante a hat etwa den Wert von ca. 2 bis 25 und die Konstante b erreicht etwa ca. 8 bis 25, (Biegebruch nach DIN 52 352, Proben 50 mm breit und 10 mm dick). The values determined on pressed parts, such as the bending strength, prove the effectiveness of the binder system according to the invention. Despite the known spread of the measured values of bending fracture tests, a statistical analysis using a coefficient of determination of r2 = 0.91 leads to the conclusion that the function of the proportion of the binding agent against the bending breaking load follows a logarithmic relationship (breaking load = a + b in the binding agent content (%)). The constant a has the value of approx. 2 to 25 and the constant b reaches approx. 8 to 25 (bending fracture according to DIN 52 352, samples 50 mm wide and 10 mm thick).

Die im Bereich von 2 bis 10 Gew. % PUR-Anteil gemessenen Festigkeiten zeigen, dass bereits bei einem PUR-Anteil von ca. 5 % die für Qualitätsspanplatten notwendigen Biegefestigkeiten erreicht werden können. The strengths measured in the range from 2 to 10% by weight of PUR show that the bending strengths required for quality chipboard can be achieved with a PU content of approx. 5%.

Die technologischen Eigenschaften der kolloidalen Lösung des Polyols gestatten es, eine überraschend grosse Gruppe der verschiedensten Materialien, solange sie pulver-, faser-, span-oder granulatförmig sind, unter- und miteinander zu binden. Hierbei können die Netzmittel und Schutzkolloide ebenfalls eine, allerdings bisher noch nicht näher untersuchte Funktion haben. Es gelingt z.B. den in der Spanplattenindustrie als Abfallstoff anfallenden feinkörnigen Schleifstaub homogen zu hochwertigen Platten zu verpressen. Auch landwirtschaftliche Abfallprodukte, z.B. zerkleinertes Stroh, Pressrückstände bei Olivenölgewinnung, sogar mit einem bestimmten Restfettanteil, Kakaobohnenschalen, Reiskleie, Holzrindenabfälle, lassen sich ohne Schwierigkeiten verbinden und z.B. durch Heisspressen nach an sich bekannten Technologien zu den verschiedensten Gegenständen, wie Platten, Profilen oder Formteilen, flach-, sträng- oder formpressen. Auch anorganische Materialien, z.B. Ziegelstaub oder Schlackenstaub, lassen sich gut verbinden, wobei anzunehmen ist, dass in diesem Fall die Isocyanatkomponente auch mit den Oxid- bzw. Hydroxyschichten der Oberfläche der anorganischen Teilchen reagiert. The technological properties of the colloidal solution of the polyol allow a surprisingly large group of the most diverse materials to be bound to and with one another as long as they are powder, fiber, chip or granular. The wetting agents and protective colloids can also have a function here, but have not yet been investigated. It succeeds e.g. to homogeneously compress the fine-grained sanding dust generated in the chipboard industry into high-quality boards. Agricultural waste products, e.g. crushed straw, pressed residues from olive oil production, even with a certain residual fat content, cocoa bean husks, rice bran, wood bark waste, can be combined without difficulty and e.g. by hot pressing according to known technologies to the most varied objects, such as plates, profiles or molded parts, flat, extrusion or molding. Also inorganic materials, e.g. Brick dust or slag dust can be easily combined, it being assumed that in this case the isocyanate component also reacts with the oxide or hydroxyl layers of the surface of the inorganic particles.

Als Polyol kommen die grosse Zahl der in der PUR-Chemie für Klebstoffe eingesetzten Polyole in Frage, z.B. lineare oder verzweigte hydroxylgruppenhaltige Polyester oder auch lineare oder verzweigte hydroxylgruppenhaltige Polyäther. Besonders vorteilhaft sind Polyäther mit einem Anteil an endständigen, The large number of polyols used in PUR chemistry for adhesives are suitable as polyols, e.g. linear or branched hydroxyl-containing polyesters or linear or branched hydroxyl-containing polyethers. Polyethers with a proportion of terminal,

also primären OH-Gruppen, da diese primären OH-Gruppen mit Isocyanat schneller reagieren als Wasser. primary OH groups, since these primary OH groups react with isocyanate faster than water.

622534 622534

Als ein konkretes Beispiel eines linearen Polyesters sei Desmophen 2100 (Bayer, aus Adipinsäure und Diäthylen-glykol), als Beispiel eines schwach verzweigten Polyesters sei Desmophen 2300 (Bayer, aus Adipinsäure, Diäthylenglykol und Triol) und als Beispiel eines verzweigten Polyesters sei Desmophen 2400 (Bayer, aus Adipinsäure, Phthalsäure, Buty-lenglykol und Triol) zitiert. Desmophen 2100 (Bayer, from adipic acid and diethylene glycol) is a concrete example of a linear polyester, Desmophen 2300 (Bayer, from adipic acid, diethylene glycol and triol) is an example of a weakly branched polyester, and Desmophen 2400 is an example of a branched polyester ( Bayer, from adipic acid, phthalic acid, butylene glycol and triol).

Ein konkretes Beispiel für einen linearen Polyäther stellt Desmophen 3200 dar (Bayer, aus Propylenglykol und Propy-lenoxid), ein verzweigter Polyäther ist z. B. Desmophen 3300 (Bayer, aus Trimethylolpropan und Propylenoxid) oder Desmophen 3200 (Bayer, aus Amin und Propylenoxid). Beispiele für Polyäther mit primären OH-Gruppen, die entstehen, wenn gegen Ende der Polymerisationsreaktion anstelle des Propylen-oxids mit Äthylenoxid zur Reaktion gebracht wird, sind Desmophen 7100 (Bayer) oder Voranol CP 4711 (Dow). Desmophen 3200 (Bayer, made from propylene glycol and propylene oxide) is a concrete example of a linear polyether. B. Desmophen 3300 (Bayer, from trimethylolpropane and propylene oxide) or Desmophen 3200 (Bayer, from amine and propylene oxide). Desmophen 7100 (Bayer) or Voranol CP 4711 (Dow) are examples of polyethers with primary OH groups which are formed when, instead of the propylene oxide, reaction is carried out with ethylene oxide towards the end of the polymerization reaction.

Als Beispiel eines Polyäthers, der sich gut dazu eignet, gezielt die Vernetzungsdichte zu erhöhen, sei Voranol RA 800 genannt (Dow, ein mit Amin gestartetes Polyol). Voranol RA 800 (Dow, a polyol started with amine) is an example of a polyether that is well suited to specifically increase the crosslinking density.

Als Isocyanatkomponente eignen sich aliphatische oder aromatische Di- bzw. Polyisocyanate, wobei wie bei den Polyolen die Liste nicht vollständig sein kann; Beispiele sind Hexa-methylen-l,6-diisocyanat (Desmodur H, Bayer), Toluylen-2,4-bzw.-2,6-diisocyanat (Desmodur T, Bayer), Naphthalin-1,5-diisocyanat (Desmodur 15, Bayer), Diphenylmethan-4,4-di-isocyanat (Desmodur 44, Bayer) oder etwa Triphenylmethan-4,4', 4"-triisocyanat (Desmodur R, Bayer). Aliphatic or aromatic di- or polyisocyanates are suitable as the isocyanate component, but as with the polyols, the list cannot be exhaustive; Examples are hexa-methylene-1,6-diisocyanate (Desmodur H, Bayer), toluene-2,4-or 2,6-diisocyanate (Desmodur T, Bayer), naphthalene-1,5-diisocyanate (Desmodur 15, Bayer), diphenylmethane-4,4-di-isocyanate (Desmodur 44, Bayer) or about triphenylmethane-4,4 ', 4 "-triisocyanate (Desmodur R, Bayer).

Als Isocyanatkomponente haben sich insbesondere folgende Di- bzw. Polyisocyanate bewährt, wobei wie bei den Polyolen die Aufzählung nicht vollständig ist: Hexamethylen-l,6-diiso-cyanat, Toluylen-2,4- und Toluylen-2,6-diisocyanat, Naphthalin-1,4-diisocyanat und Triphenylmethan-4,4', 4"-triisocyanat. The following di- or polyisocyanates have proven particularly useful as isocyanate components, although, as with the polyols, the list is not complete: hexamethylene-l, 6-diisocyanate, tolylene-2,4- and toluene-2,6-diisocyanate, naphthalene -1,4-diisocyanate and triphenylmethane-4,4 ', 4 "triisocyanate.

Auch die Liste der verwendbaren Netzmittel, die zur Herstellung einer kolloidalen Lösung geeignet sind, ist überaus gross. Sie enthält ausser ionischen und nichtionischen Netzmitteln bzw. Schutzkolloiden auch Substanzen, wie Lingning-sulfat, Dextrin und Methylcellulose. Allesamt sind sie bekannte Dispergierhilfen bzw. Stabilisatoren. The list of usable wetting agents that are suitable for the preparation of a colloidal solution is also extremely large. In addition to ionic and non-ionic wetting agents or protective colloids, it also contains substances such as Lingning sulfate, dextrin and methyl cellulose. All of them are known dispersion aids or stabilizers.

Im folgenden wird die Herstellung der kolloidalen Lösung des Polyols an einem Beispiel beschrieben. The preparation of the colloidal solution of the polyol is described below using an example.

Beispiel example

200 g Desmophen 1100 (BAYER, ein verzweigter hydroxyl-gruppenhaltiger Polyester aus Adipinsäure und Triol/Butylen-glykol 1:1) wird mit 6 g Lithiumstearylsulfonat unter kräftigem Dispergieren der beiden Flüssigkeiten mit einem Ultraturrax vermischt. Dieser Mischung werden wieder unter kräftigem Dispergieren (je nach dem Feuchtigkeitsgehalt des zu beleimenden Materials) zwischen 500 und 1000 g Wasser langsam beigefügt. Es resultiert eine dünnflüssige kolloidale Lösung, die sich leicht verdüsen und mit pulver-, faser-, span- oder granulat-förmigem, zu verpressendem Material homogen vermischen lässt. Diese kolloidale Lösung stellt ein Beispiel der erfindungsgemässen Polyolkomponente dar, während es im Hinblick auf die technischen Eigenschaften der Pressteile sinnvoll sein kann, Mischungen mehrerer kolloidal gelöster Polyole zu verwenden, die sich im Reinzustand nicht mischen lassen. 200 g Desmophen 1100 (BAYER, a branched hydroxyl-containing polyester made from adipic acid and triol / butylene glycol 1: 1) is mixed with 6 g lithium stearyl sulfonate with vigorous dispersion of the two liquids using an Ultraturrax. Again, with vigorous dispersion (depending on the moisture content of the material to be glued), between 500 and 1000 g of water are slowly added to this mixture. The result is a low-viscosity colloidal solution that can be easily atomized and mixed homogeneously with powder, fiber, chip or granular material to be pressed. This colloidal solution represents an example of the polyol component according to the invention, while in view of the technical properties of the pressed parts it can be useful to use mixtures of several colloidally dissolved polyols which cannot be mixed in the pure state.

3 3rd

s s

10 10th

15 15

20 20th

25 25th

30 30th

35 35

40 40

45 45

50 50

55 55

B B