CA2641029A1 - High-performance friction stir welding tools - Google Patents

High-performance friction stir welding tools Download PDF

Info

Publication number
CA2641029A1
CA2641029A1 CA002641029A CA2641029A CA2641029A1 CA 2641029 A1 CA2641029 A1 CA 2641029A1 CA 002641029 A CA002641029 A CA 002641029A CA 2641029 A CA2641029 A CA 2641029A CA 2641029 A1 CA2641029 A1 CA 2641029A1
Authority
CA
Canada
Prior art keywords
total weight
above item
hard particles
tic
head
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
CA002641029A
Other languages
French (fr)
Inventor
Shaiw-Rong Scott Liu
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Worldwide Strategy Holdings Ltd
Original Assignee
Genius Metal, Inc.
Shaiw-Rong Scott Liu
Worldwide Strategy Holdings Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US11/507,928 external-priority patent/US20070034048A1/en
Priority claimed from PCT/US2006/032654 external-priority patent/WO2007022514A2/en
Application filed by Genius Metal, Inc., Shaiw-Rong Scott Liu, Worldwide Strategy Holdings Limited filed Critical Genius Metal, Inc.
Publication of CA2641029A1 publication Critical patent/CA2641029A1/en
Abandoned legal-status Critical Current

Abstract

Friction stir welding tools made of a hardmetal including hard particles having a first material and a binder matrix having a second, different material.

Description

HIGH-PERFORMANCE FRICTION STIR WELDING TOOLS
[0001] This application claims the benefit of U.S.
Provisional Application No. 60/764,003 entitled "HIGH-PERFORMANCE FRICTION STIR WELDING TOOLS" and filed January 31, 2006.
[0002] This application further claims the benefits of and is a continuation-in-part of the following Patent Applications:
[0003] No. 11/507,928 entitled "Hardmetal Materials for High-Temperature Applications" and filed August 21, 2006, which claims the benefit of U.S. Provisional Application No.
60/710,016 entitled "HARDMETAL MATERIALS FOR HIGH-TEMPERATURE
APPLICATIONS" and filed on August 19, 2005;
[0004] No. PCT/US2006/032654 entitled "Hardmetal Materials for High-Temperature Applications" and filed August 21, 2006;
and [0005] No. 11/081,928 entitled "High-Performance Hardmetal Materials" and filed March 15, 2005, which is published as U.S. Publicatoin No. US 2005-0191482-Al.
[0006] The disclosures of the above patent applications and patent publications are incorporated by reference as part of the specification of this application.
Background [0007] This application relates to hardmetal compositions, their fabrication techniques, and associated applications.
[0008] Hardmetals include various composite materials and are specially designed to be hard and refractory, and exhibit strong resistance to wear. Examples of widely-used hardmetals include sintered or cemented carbides or carbonitrides, or a combination of such materials. Some hardm.etals, called cermets, have compositions that may include processed ceramic particles (e.g., TiC) bonded with binder metal particles.

Certain compositions of hardmetals have been documented in the technical literature. For example, a comprehensive compilation of hardmetal compositions is published in Brookes' World Dictionary and Handbook of Hardmetals, sixth edition, International Carbide Data, United Kingdom (1996).
[00091 Hardmetals may be used in a variety of applications.
Exemplary applications include cutting tools for cutting metals, stones, and other hard materials, wire-drawing dies, knives, minirng tools for cutting coals and various ores and =10 rocks, and drilling tools for oil and other drilling applications. In addition, such hardmetals also may be used to construct housing and exterior surfaces or layers for various devices to meet specific needs of the operations of the devices or the environmental conditions under which the devices operate.
[00103 Many hardmetals may be formed by first dispersing hard, refractory particles of carbides or carbonitrides in a binder matrix and then pressing and sintering the mixture. The sintering process allows the binder matrix to bind the particles and to condense the mixture to form the resulting hardmetals. The hard particles primarily contribute to the hard and refractory properties of the resulting hardmetals.
Stumtaty [00111 This application describes designs of friction stir welding (FSW) heads and associated FSW systems that use such heads. In various implementations, a FSW head can include a pin and a shoulder to which the pin is engaged. The head is engaged to a shank which is in turn fixed to a rotor. The rotor rotates the shank which spins the head during welding.
In operation, the spinning head is pressed to the interface of two metal pieces to be welded together and is moved along the interface. The pin and the shoulder are in direct contact with the two pieces to weld them together. In some imple,mentations, the pin and the shoulder are made of a hardmetal material described in this application. In other implementations, the surfaces of the pin and shoulder may be made of a material described in this application while the inner parts of the pin and shoulder may be made of a different material. Various materials described here exhibit high hardness and toughness under a high temoperature experienced by the pin and shoulder during the friction stir welding and thus can be used for constructing the head.
[00121 For example, a friction stir welding tool head described in this application includes a shoulder and a pin engaged to the shoulder. At least one.part of each of the shoulder and the pin includes a material described in this application. This material can include, at least, (1) a first material which includes at least one of or a combination of at least one carbide, at least one nitride, at least one boride, and at least one silicide, and (2) a second material that binds the first material and includes rhenium, a mixture of rhenium and cobalt, a nickel-based superalloy, a mixture of a nickel-based superalloy and rhenium, or a mixture of a nickel-based superalloy, rhenium and cobalt. The second material may also include Mo, W, Ta, or Cr. In implementating the above examples, the first material may include at least at least one carbide selected from at least one of TaC, HfC, NbC, ZrC, TiC, WC, VC, A14C3, ThC2, Mo2C, SiC and B4C, or at least one nitride =25 selected from at least one of HfN, TaN, BN, ZrN, and TiN, or at least one boride selected from at least one of HfB2, ZrB2, TaB2, TiB2, NbB2, and WB.
[00137 The hardmetal materials described below include materials comprising hard particles having a first material, .30 and a binder matrix having a second, different-material. The hard particles are spatially dispersed in the binder matrix in a substantially uniform manner. The first material for the hard particles may include, for example, materials based on tungsten carbide, materials based on titanium carbide, materials based on a mixture of tungsten carbide and titanium carbide, other carbides, nitrides, borides, silicides, and combinations of these materials. The second material for the binder matrix may include, among others, rhenium, a mixture of rhenium and cobalt, a nickel-based superalloy, a mixture of a nickel-based superalloy and rhenium, a mixture of a nickel-based superalloy, rhenium and cobalt, and these materials mixed with other materials. Tungsten may also be used as a binder matrix material in hardmetal materials. The nickel-based superalloy may be in the y-y' metallurgic phase.
[0014] In various implementations, for example, the volume of the second material may be from about 3% to about 40% of a total volume of the material. For some applications, the binder matrix may comprise rhenium in an amount at or greater than 25% of a total weight of the binder matrix of the final material. For other applications, the second material may include a Ni-based superalloy. The Ni-based superalloy may include Ni and other elements such as Re for certain applications.
[0015] Fabrication of the hardmetal materials of this application may be carried out by, according to one implementation, sintering the material mixture under a vacuum condition and performing a solid-phase sintering under a pressure applied through a gas medium. Such hardmetals may also be coated on surfaces using thermal spray methods to form either hardmetal coatings and hardmetal structures.
[0016] Advantages arising from various implementations of the described hardmetal materials may include one or more of the following: superior hardness in general, enhanced hardness at high temperatures, and improved resistance to corrosion and oxidation.

_4_.

[0017] Various specific implementations described in this application are summarized as follows. The first group of 265 specific implementations is as follows.
1. A material comprising:
hard particles having a first material; and a binder matrix having a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium in an amount greater than 25% of a total weight of the material, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
2. The material as in the above item no. 1 or below item no. 14, wherein said first material includes a carbide comprising tungsten.
3. The material as in the above item no. 2, wherein said carbide comprises mono tungsten carbide (WC).
4. The material as in the above item no. 2, wherein said first material further includes another carbide having a metal element different from tungsten.
5. The material as in the above item no. 4, wherein said metal element is titanium (Ti).
6. The material as in the above item no. 4, wherein said metal element is tantalum (Ta).
7. The material as in the above item no. 4-, wherein said metal element is niobium (Nb).
8. The material as in the above item no. 4, wherein said metal element is vanadium (V).
9. The material as in the above item no. 4, wherein said metal element is chromium (Cr).
10. The material as in the above item no. 4, wherein said metal element is hafnium (Hf).
11. The material as in the above item no. 4, wherein said metal element is molybdenum (Mo).
12. The material as in the above item no. 2, wherein said first material further includes a nitride.
13. The material as in the above item no. 2 or 12, wherein said nitride includes TiN, ZrN, VN, NbN, TaN or HfN.
14. A material, comprising:
hard particles comprising a first material which comprises a nitride; and a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner .
15. The material as in the above item no. 14, wherein said nitride includes TiN, ZrN, VN, NbN, TaN or HfN.
16. The material as in the above item no. 1, wherein said binder matrix further includes cobalt (Co).
17. A material comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and nickel (Ni), wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
18. A material comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and molybdenum (Mo), wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

_6-19. A material comprising:
hard parti-cles comprising a first material; and a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and iron (Fe), wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
20. A material comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and chromium (Cr), wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
21. A material comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and a Ni-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
22. The material as in the above item no. 21, wherein said binder material further includes cobalt.
23. A material comprising:
hard particles having a first material having a mixture selected from at least one from a group consisting of (1) a mixture of WC, TiC, and TaC, (2) a mixture of WC, TiC, and NbC, (3) a mixture of WC, TiC, and at least one of TaC and NbC, and (4) a mixture of WC, TiC, and at least one of HfC and NbC; and a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40%
of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
24. A material comprising:
hard particles having a first material comprising a material selected from at least one from a group consisting of (1) WC, TiC, and TaC, (2) WC, TiC, and NbC, (3) WC, TiC, and at least one of TaC and NbC, and (4) WC, TiC, and at least one of HfC and NbC; and a binder matrix comprising a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and a Ni-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
25. A material comprising:
hard particles having a first material having a mixture of Mo2C and T.iC; and a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40%
of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
26. A material, comprising:
30. hard particles comprising a'first material which comprises TiN, M02C and TiC; and a binder matrix comprising a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
27. A material, comprising:
-hard particles comprising a first material comprising M02C and TiC; and a binder matrix comprising a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and a Ni-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
28. A method comprising:
forming a grade power by mixing a powder of hard particles with a binder matrix material comprising rhenium;
processing the grade powder to use the binder matrix material to bind the hard particles to produce a solid hardmetal material, wherein the processing includes (1) sintering the grade powder in a solid phase under a vacuum condition, and (2) sintering the grade power in a solid phase under a pressure in an inert gas medium.
29. The method as in the above item no. 28, wherein the binder matrix material further includes a Ni-based superalloy.
30. The method as in the above item no. 29, wherein the binder matrix material further includes cobalt.
31. The method as in the above item no. 28, wherein the binder matrix material further includes cobalt.
32. The method as in the above item no_ 28, wherein each sintering is performed a temperature below an eutectic temperature of the hard particles and the binder matrix material.
33. A material comprising:
hard particles having a first material; and a binder matrix having a second, different material comprising a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
34. The material as in the above item no. 33 or 47, wherein said first material includes a carbide comprising tungsten.
35. The material as in the above item no. 34, wherein said carbide comprises mono tungsten carbide (WC).
36. The material as in the above item no. 34, wherein said first material further includes another carbide having a metal element different from tungsten.
37. The material as in the above item no. 36, wherein said metal element is titanium (Ti).
38. The material as in the above item no. 36, wherein said metal element is tantalum (Ta).
39. The material as in the above item no. 36, wherein .20 said metal element is niobium (Nb).
40. The material as in the above item no. 36, wherein said metal element is vanadium (V).
41. The material as in the above item no. 36, wherein said metal element is chromium (Cr).
42. The material as in the above item no. 36, wherein said metal element is hafnium (Hf).
43. The material as in the above item no. 36, wherein said metal element is molybdenum (Mo).
44. The material as in the above item no. 34, wherein said first material further includes a nitride.
45. The material as in the above item no. 34 or 44, wherein said nitride includes at least one of ZrN, HfN, VN, NbN, TaN and TiN.
46. The material as in the above item no. 34 or 44, wherein said first material includes a carbide.
47. A material, comprising:
hard particles comprising a first material which 5- comprises a nitride; and a binder matrix comprising a second, different material comprising a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
10. 48. The material as in the above item no. 47, wherein said nitride includes at least one.of ZrN, VN, NbN, TaN TiN
and HfN.
49. The material as in the above item no. 33 or 47, wherein said nickel-based superalloy comprises primarily 15 nickel and also comprises other elements.
50. The material as in the above item no. 49, wherein said other elements include Co, Cr, Al, Ti, Mo, Nb, W, and Zr.
51. A material, comprising:
hard particles comprising a first material; and 20 a binder matrix comprising a second, different material which comprises a nickel-based superalloy and a second, different nickel-based superalloy, , wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
25 52. The material as in the above item no. 51, wherein said binder matrix further comprises rhenium.
53. The material as in the above item no. 52, wherein said binder matrix further comprises cobalt.
54. The material as in the above item no. 33, wherein 30 said binder matrix further comprises rhenium.

_11_ 55. A material, comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy, rhenium and cobalt, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
56. A material comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy and cobalt, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
57. A material, comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy and nickel, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
58. A material, comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy and iron, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
59. A material, comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy molybdenum, wherein said hard particles are spatially dispersed in said binder 30= matrix in a substantially uniform manner.

60. A material, comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy and chromium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
61. The material as in the above item no. 33, wherein said binder matrix further comprises another alloy that is not a nickel-based alloy.
62. A material, comprising:
hard particles having a first material comprising TiC and Ti.N; and a binder matrix having a second, different material comprising at least one of Ni, Mo, and Mo2C, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
63. A material, comprising:
hard particles comprising a first material which comprises TiC and TiN; and a binder matrix comprising a second, different material which comprises Re and at least one of Ni, Mo, and M02C, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
64. The material as in the above item no. 63, wherein said binder matrix further includes Co.
65. The material as in the above item no. 64, wherein said binder matrix further includes a Ni-based superalloy.
66. The material as in the above item no. 63, wherein said binder matrix further includes a Ni-based superalloy.

67. A material, comprising:
hard particles comprising a first material comprising TiC
and TiN; and a binder matrix comprising a second, different material which comprises a Ni-based superalloy, and at least one of Ni, Mo, and M02C, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
68. A method comprising:
forming a grade powder by mixing a powder of hard particles with a binder matrix material comprising a nickel-based superalloy;
processing the grade powder to produce a solid hardmetal material by using the binder matrix material to bind the hard particles.
69. The method as in the above item no. 68, wherein said processing includes sequentially performing a pressing operation, a first sintering operation, a shaping operation, and a second sintering operation.
70. (The method as in the above item no. 68, further comprising: prior to the mixing, preparing the binder matrix material to further include rhenium.
71. The method as in the above item no. 68, further comprising: prior to the mixing, preparing the binder matrix material to further include cobalt.
72. The method as in the above item no. 68, wherein the processing includes a solid phase sintering in a hot isostatic pressing process.
73. The method as in the above item no. 68, wherein the processing includes (1) sintering the grade powder in a solid phase under a vacuum condition, and (2) sintering the grade power in a solid phase under a pressure in an inert gas medium.

74. The method as in the above item no. 68, further comprising: prior to the mixing, preparing the hard particles with a particle dimension less than 0.5 micron to reduce a temperature of the sintering operations.
5= 75. A device, comprising a wear part that removes material from an object, said wear part having a material which comprises:
hard particles having a first material; and a binder matrix having a second, different material 10= comprising rhenium and a Ni-based super alloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
76. The device as in the above item no. 75, wherein said binder matrix further includes a cobalt.
15 77. A device, comprising a wear part having a material which comprises:
hard particles having a first material; and a binder matrix of a second, different material comprising a nickel-based superalloy, wherein said hard 20 particles are spatially dispersed in said binder matrix in a substantially uniform manner.
78. A material comprising:
hard particles having a first material selected from at least one from a group consisting of (1) a solid solution of 25 WC, TiC, and TaC, (2) a solid solution of WC, TiC, and NbC, (3) a solid solution of WC, TiC, and at least one of TaC and NbC, and (4) a solid solution of WC, TiC, and at least one of HfC and NbC; and a binder matrix having a second, different material, a 30 volume of said binder matrix being from about 3% to about 40%
of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

79. The material as in the above item no. 78 or 87, wherein the hard particles comprise WC, Ti.C, and TaC, and the binder matrix is formed of pure Re.
80. The material as in the above item no. 79, wherein the hard particles are about 72% of and the Re is about 28% of the total weight of the material.
81. The material as in the above item no. 79, wherein the hard particles are about 85% of and the Re is about 15% of the total weight of the material.
82. The material as in the above item no. 79, wherein Ti.C
and TaC are approximately equal in quantity and have a total quantity less than a quantity of the WC.
83. The material as in the above item no. 24, wherein the hard particles comprise WC, TIC, and TaC.
84. The material as in the above item no. 83, wherein each of TiC and TaC is from about 3% to less than about 6% in a total weight of the material, and WC is above 78% and below 89% in the total weight of the material.
85. The material as in the above item no. 83, wherein the binder matrix further includes Co.
86. The material as in the above item no. 83, wherein the Ni-based superalloy comprises mainly Ni and other elements including Co, Cr, Al, Ti, Mo, Nb, W, Zr, B, C, and V.
87. A material, comprising:
hard particles comprising a first material selected from at least one from a group consisting of (1) WC, TiC, and TaC, (2) WC, TiC, and NbC, (3) WC, TiC, and at least one of TaC and NbC, and (4) WC, TiC, and at least one of HfC and NbC; and a binder matrix comprising a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed irl said binder matrix in a substantially uniform manner, wherein the binder matrix includes Re and a Ni-based superalloy which includes Re.
88. The material as in the above item no. 21, wherein said Ni-based superalloy includes Re.
89. The material as in the above item no. 24, wherein said Ni-based superalloy includes Re.
90. The material as in the above item no. 21 or 47, wherein said Ni-based superalloy includes Re.
91. A material comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner, wherein said Ni-based superalloy includes Re.
92. A material, comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner, wherein said Ni-based superalloy is in a y-y' phase.
93. A material, comprising:
hard particles comprising a first material; and a binder matrix comprising a second, different material which comprises a nickel-based superalloy which comprises nickel and other elements, said other elements comprising Co, Cr, Al, Ti, Mo, Nb, W, Zr, and Re, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
94. The material as in the above item no. 17, wherein said first material comprises a boride.

95. The material as in the above item no. 95, wherein said boride is one of TiB2, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B.
96. The material as in the above item no. 17, wherein said first material comprises a silicide.
97. The material as in the above item no. 96, wherein said silicide is one of TaSi2, Wsi2, NbSi2, and MoSi2.
98. The material as in the above item no. 17, wherein said first material comprises a carbide.
99. The material as in the above item no. 98, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
100. The material as in the above item no. 17, wherein said first material further comprises a nitri.de.
101. The material as in the above item no. 100, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
102. The material as in the above item no. 100, wherein said first material further comprises a carbide.
103. The material as in the above item no. 102, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
104. The material as in the above item no. 102, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
105. The material as in the above item no. 18, wherein said first material comprises a boride.
106. The material as in the above item no. 105, wherein said boride is one of TiB2, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B.
107. The material as in the above item no. 18, wherein said first material comprises a silicide.
108. The material as in the above item no. 107, wherein said si.licide is one of TaSi2, Wsi2, NbSi2, and MoSi2.

109. The material as in the above item no. 18, wherein said first material comprises a carbide.
110. The material as in the above item no. 109, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, MoaC, and WC.
111. The material as in the above item no. 18, wherein said first material further comprises a nitride.
112. The material as in the above item no. 111, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
113. The material as in the above item no. 111, wherein said first material further comprises a carbide.
114. The material as in the above item no. 113, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
115. The material as in the above item no. 113, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
116. The material as in the above item no. 19, wherein said first material comprises a carbide.
117. The material as in the above item no. 116, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, Mo2C, and WC.
118. The material as in the above item no. 19, wherein said first material comprises a boride.
119. The material as in the above item no. 118, wherein said boride is one of TiBa, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B.
120. The material as in the above item no. 19, wherein said first material comprises a silicide.
121. The material as in the above item no. 120, wherein said silicide is one of TaSi2, Wai2, NbSi2, and MoSi2.
122. The material as in the above item no. 19, wherein said first material further comprises a nitride.

123. The material as in the above item no. 122, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
124. The material as in the above item no. 122, wherein said first material further comprises a carbide.
125. The material as in the above item no. 124, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
126. The material as in the above item no. 125, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
127. The material as in the above item no. 20, wherein said first material comprises a boride.
128. The material as in the above item no. 127, wherein said boride is one of TiB2, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B.
129. The material as in the above item no. 20, wherein said first material comprises a silicide.
130. The material as in the above item no. 129, wherein said silicide is one of TaSi2, Wsi2, NbSi2, and MoSi2.
131. The material as in the above item no. 20, wherein said first material comprises a carbide.
132. The material as in the above item no. 131, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
133. The material as in the above item no. 20, wherein said first material further comprises a nitride.
134. The material as in the above item no. 133, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
135. The material as in the above item no. 133, wherein said first material further comprises a carbide.

136. The material as in the above item no. 135, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
137. The material as in the above item no. 135, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
138. The material as in the above item no. 21, wherein said first material comprises a carbide.
139. The material as in the above item no. 138, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
140. The material as in the above item no. 21, wherein said first material comprises a boride.
141. The material as in the above item no. 140, wherein said boride is one of TiB2, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and 142. The material as in the above item no. 21, wherein said first material comprises a silicide.
143. The material as in the above item no. 142, wherein said silicide is one of TaSi2, Wsi2, -NbSi2, and MoSiz.
144. The material as in the above item no. 21, wherein said first material comprises a nitride.
145. The material as in the above item no. 144, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
146. The material as in the above item no. 144, wherein said first material further comprises a carbide.
147. The material as in the above item no. 146, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
148. The material as in the above item no. 147, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN,V
and TaN.

149. The material as in the above item no. 22, wherein said first material comprises a boride.
150. The material as in the above item no. 149, wherein said boride is one of TiB2, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B.
151. The material as in the above item no. 22, wherein said first material comprises a silicide.
152. The material as in the above item no. 151, wherein said silicide is one of TaSi2, Wsi2i NbSi2, and MoSi2.
153. The material as in the above item no. 22, wherein said first material comprises a carbide.
154. The material as in the above item no. 153, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
155. The material as in the above item no. 22, wherein said first material further comprises a nitride.
156. The material as in the above item no. 155, wherein said nitride includes at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
157. The material as in the above item no. 155, wherein said first material further comprises a carbide.
158. The material as in the above item no. 157, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, Mo2C, and WC.
159. The material as in the above item no. 157, wherein said nitride comprises at least one=of TiN, ZrN, HfN, VN, NbN, and TaN.
160. The material as in the above item no. 24, wherein said first material further comprises a nitride.
161. The material as in the above item no. 160, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
162. The material as in the above item no. 24, wherein said binder matrix further comprises cobalt(Co).

163. The material as in the above item no. 24, wherein Re is from about 1.5% to about 24.4% of the total weight of the material, and said Ni-based superalloy is from about 0.86%
to about 4.88% of the total weight of the material, and wherein the first material comprises TiC which is from about 3% to about 14.7% of the total weight of the material, TaC which is from about 3% to about 6.2% of the total weight of the material, and WC which is above about 64% and below about 88% of the total weight of the material.
164. The material as in the above item no. 26, wherein said binder matrix further comprises a Ni-based superalloy.
165. The material as in the above item no. 164, wherein said binder matrix further comprises Co.
166. The material as in the above item no. 27, wherein =15 said binder matrix further comprises Co.
167. The material as in the above item no. 27, wherein said Re is from about 8.8% to about 23.8% of the total weight of the material, and said Ni-based superalloy is from about 3.0% to about 10.3% of the total weight of the material, and wherein said M02C is from about 13.8% to about 15.2% of the total weight of the material, and said TiC is from about 59_4%
to about 65.7% of the total weight of the material.
168. The material as in the above item no. 47, wherein said first material further comprises a carbide.
169. The material as in the above item no. 168, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, MoaC, and WC.
170. The material as in the above item no. 168, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
171. The material as in the above item no. 49, wherein said other elements comprise Cr, Co,- Fe, Al, Ti, Mo, W, Nb, Ta, Hf, Zr, B, C, Re.

172. The material as in the above item no. 51, wherein said first material comprises a carbide.
173. The material as in the above item no. 172, wherein said first material further comprises a nitride.
174. The material as in the above item no. 50, wherein said other elements further comprise Fe, Ta, Hf, C, and Re.
175. The material as in the above item no. 51, wherein said first material comprises a nitride.
176. The material as in the above item no. 55, wherein Re is from about 0.4% to about 1.8% of the total weight of the material, said Ni-based superalloy from about 2.7% to about 4.5% of the total weight of the material, and said cobalt from about 3% to about 4.8% of the total weight of the material, and wherein said first material comprises WC which is from about 90.4% to about 91.5% of the total weight of the material, and VC which is from about 0.3% to about 0.6% of the total weight of the material.
177. The material as in the above item no. 55, wherein said first material further comprises a nitride.
178. The material as in the above item no. 55, wherein said first material further comprises a carbide.
179. The material as in the above item no. 56, wherein said first material further comprises a nitride.
180. The material as in the above item no. 179, wherein said first material further comprises a carbide.
181. The material as in the above item no. 56, wherein said first material further comprises a carbide.
182. The material as in the above item no. 57, wherein said first material further comprises a nitride.
183. The material as in the above item no. 182, wherein said first material further comprises a carbide.
184. The material as in the above item no. 57, wherein said first material further comprises a carbide.

185. The material as in the above item no. 58, wherein said first material further comprises a nitride.
186. The material as in the above item no. 185, wherein said first material further comprises a carbide.
187. The material as in the above item no. 58, wherein said first material further comprises a carbide.
188. The material as in the above item no. 59, wherein said first material further comprises a nitride.
189. The material as in the above item no. 188, wherein said first material further comprises a carbide.
190. The material as in the above item no. 59, wherein said first material further comprises a carbide.
191. The material as in the above item no. 60, wherein said first material further comprises a nitride.
192. The material as in the above item no. 191, wherein said first material further comprises a carbide.
193. The material as in the above item no. 60, wherein said first material further comprises a carbide.
194. The device as in the above item no. 75, wherein said first material comprises a carbide.
195. The device as in the above item no. 194, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
196. The device as in the above item no. 75, wherein said first material further comprises a nitride.
197. The device as in the above item no. 196, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
198. The device as in the above item no. 196, wherein said first material further comprises a carbide.
199. The device as in the above item no. 198, wherein said first material comprises WC, TiC, TaC and Mo2C:

200. The device as in the above item no. 198, wherein said carbide comprises at least one of TIC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC .
201. The device as in the above item no. 198, wherZein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
202. The device as in the above item no. 75, wherein said first material further comprises a boride.
203. The device as in the above item no. 202, wherein said first material comprises at least one of TiBz, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B.
204. The device as in the above item no. 75, wherein said first material further comprises at least one boride and at least one carbide.
205. The device as in the above item no. 204, wherein said first material comprises WC, TiC, TaC, and B4C.
206. The device as in the above item no. 75, wherein said first material comprises a silicide.
207. the device as in the above item no. 75, wherein said first material comprises at least one of TaSi2, WSi2, NbSi2, and MoSi2.
208. The device as in the above item no. 75, wherein said Re is from about 9.04% to about 9.32% of the total weight of the material, and said Ni-based superalloy is from about 3.53% to about 3.64% of the total weight of the material, and wherein said first material comprises WC from about 67.24% to about 69.40% of the total weight of the material, Ti.C from about 6.35% to about 6.55% of the total weight of the material, TaC from about 6.24% to about 6.44% of, TiB2 from about 0.40% to about 7.39% of the total weight of the material, and B4C from about 0.22% to about 4.25% of the total weight of the material.

209. The device as in the above item no. 75, wherein said Re is from about 8.96% to about 9.37% of the total weight of the material, and said Ni-based superalloy is from about 3.50% to about 3.66% of the total weight of the material, and wherein said first material comprises WC from about 58.61% to about 66.67% of the total weight of the material, TiC from about 14.69% to about 15.37% of the total weight of the material, TaC from about 6.19% to about 6.47% of the'total weight of the material, and M02C from 0 to about 6.51% of the total weight of the material.
210. The device as in the above item no. 75, wherein said binder matrix further comprises Ni.
211. The device as in the above item no. 75, wherein said binder matrix further comprises Fe.
212. The device as in the above item no. 75, wherein said binder matrix further comprises Mo.
213. The device as in the above item no. 75, wherein said binder matrix further comprises Cr.
214. The material as in the above item no. 83, wherein the Ni-based superalloy comprises mainly Ni and other elements which comprise Cr, Co, Fe, Al, Ti, Mo, W, Nb, Ta, Hf, Zr, B, C, Re.
215. The material as in the above item no. 91, wherein said first material comprises a carbide.
216. The material as in the above item no. 215, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
217. The material as in the above item no. 91, wherein said first material further comprises a nitride.
218. The material as in the above item no. 217, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
219. The material as in the above item no. 217, wherein said first material further comprises a carbide.

220. The material as in the above item no. 219, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, Mo2C, and WC .
221. The material as in the above item no. 91, wherein said first material further comprises a boride.
222. The material as in the above item no. 221, wherein said first material comprises at least one of TiB2, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B.
223. The material as in the above item no. 91, wherein said first material further comprises at least one boride and at least one carbide.
224. The material as in the above item no. 223, wherein said first material comprises WC, TiC, TaC, and B4C.
225. The material as in the above item no. 91, wherein said first material comprises a silicide.
226. The material as in the above item no. 225, wherein said silicide comprises at least one of TaSi2, WSi2, NbSi2, and MoSi2 .
227. The material as in the above item no. 91, wherein said binder matrix further comprises Ni.
228. The material as in the above item no. 91, wherein said binder matrix further comprises Fe.
229. The material as in the above item no. 91, wherein said binder matrix further comprises Mo.
230. The material as in the above item no. 91, wherein said binder matrix further comprises=Cr.
231. The material as in the above item no. 92, wherein said first material comprises a carbide.
232. The material as in the above item no. 231, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
233. The material as in the above item no. 92, wherein said first material further comprises a nitride.

234. The material as in the above item no. 233, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
235. The material as in the above item no. 233, wherein said first material further comprises a carbide.
236. The material as in the above item no. 235, wherein said carbide comprises at least one of TIC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
237. The material as in the above item no. 235, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
238. The material as in the above item no. 92, wherein said first material further comprises a boride.
239. The material as in the above item no. 238, wherein said first material comprises at least one of TiB2, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B.
240. The material as in the above item no. 92, wherein said first material comprises a silicide.
241. The material as in the above item no. 92, wherein said first material comprises at least one of TaSi2, WSi2, NbSi2, and MoSi2.
242. The material as in the above item no. 92, wherein said second material further comprises at least one of Re, Ni, Co, Fe, Mo, and Cr.
243. The material as in the above item no. 92, wherein said second material further comprises at least another different Ni-based superalloy.
244. The material as in the above item no. 92, wherein said first material comprises WC from about 91.9% to about 30' 92.5% of the total weight of the material, and VC from about 0.3% to about 0.6% of the total weight of the material, and wherein said Ni-based superalloy is from about 7.2% to about 7.5% of the total weight of the material.

245. The material as in the above item no. 92, wherein said first material comprises Ti.C and MoaC which are about 69.44% and 16_09% of the total weight of the material, respectively, and wherein said Ni-based superalloy is about 14.47% of the total weight of the material.
246. The material as in the above item no. 93, wherein said first material comprises a carbide.
247. The material as in the above item no. 246, wherein said carbide comprises at least one of Ti.C, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
248. The material as in the above item no. 93, wherein said first material further comprises a nitride.
249. The material as in the above item no. 248, wwherein said nitride comprises at least one of Ti.N, ZrN, HfN, VN, NbN, and TaN.
250. The material as in the above item no. 249, wherein said first material further comprises a carbide.
251. The material as in the above item no. 250, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr2C3, M02C, and WC.
252. The material as in the above item no. 250, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.
253. The material as in the above item no_ 93, wherein said first material further comprises a boride.
254. The material as in the above item no. 253, wherein said first material comprises at least one of TiB2, ZrB2, HfBa, TaB2, VB2, MoB2, WB, and W2B.
255. The material as in the above item no. 93, wherein said first material comprises a silicide.
256. The material as in the above item no. 93, wherein said first material'comprises at least one of TaSi2, WSi2, NbSi2, and MoSi2.

257. The material as in the above item no. 93, wherein said second material further comprises at least one of Re, Ni, Co, Fe, Mo, and Cr.
258. The material as in the above item no. 93, wherein said second material further comprises at least another different Ni-based superalloy.
259. The material as in the above item no. 93, wherein said other elements in said nickel-based superalloy further comprise Fe, Ta, Hf, B, and C.
260. A method, comprising:
preparing a metal surface for a thermal spray process;
and performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface, wherein the hard metal layer comprises:
hard particles having a first material, and a binder matrix having a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium in an amount greater than 25% of a total weight of the material, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
261. A method, comprising:
.25 preparing a metal surface for a thermal spray process;
and performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface, wherein the hard metal layer comprises:
,30 hard particles having a first material having a mixture selected from at least one from a group consisting of (1) a mixture of WC, TiC, and TaC, (2) a mixture of WC, TiC, and NbC, (3) a mixture of WC, TiC, and at least one of TaC and NbC, and (4) a mixture of WC, TiC, and at least one of HfC and NbC; and a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40%
of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
262. A method, comprising:
lo preparing a metal surface for a thermal spray process;
and performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface, wherein the hard metal layer comprises:
hard particles having a first material having a mixture of Mo2C and TiC; and a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40%
of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
263. A method, comprising:
preparing a metal surface for a thermal spray process;
and performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface, wherein the hard metal layer comprises:
hard particles having a first material; and a binder matrix having a second, different material comprising a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

264. A method, comprising:
preparing a metal surface for a thermal spray process;
and performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface, wherein the hard metal layer comprises:
hard particles having a first material comprising TiC and TiN; and a binder matrix having a second, different material comprising at least one of Ni, Mo, and Mo2C, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.
265. A method, comprising:
preparing a metal surface for a thermal spray process;
and performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface, wherein the hard metal layer comprises:
hard particles having a first material selected from at least one from a group consisting of (1) a solid solution of WC, TiC, and TaC, (2) a solid solution of WC, TiC, and NbC, (3) a solid solution of WC, TiC, and at least one of TaC and NbC, and (4) a solid solution of WC, TiC, and at least one of HfC and NbC; and a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40%
of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

[00187 In addition, a second group of 288 specific implementations described in this application is as follows.
1. A material, comprising:
hard particles comprising at least one carbide selected from at least one of WC, TiC, and HfC; and a binder matrix that binds the hard particles and comprises rhenium, wherein the hard particles are less than 75% of a total weight of the material and rhenium is greater than 25% of the total weight of the material.
2. The material as in above item no. 1, wherein the at least one carbide is TiC which is greater than about 26% of the total weight of the material and the rhenium is less than about 74% of the total weight of the material.
3. The material as in above item no. 1, wherein the at least one carbide is WC which is greater than about 53% of the total weight of the material, and the rhenium is less than about 47% of the total weight of the material.
4. The material as in above item no. 1, wherein the at least one carbide is HfC which is greater than about 48% of the total weight of the material, and the rhenium is less than about 52% of the total weight of the material.
5. A material, comprising:
hard particles comprising at least one carbide selected from carbides that are formed from elements in IVb, Vb, and VIb columns of the periodic table of elements, exclusive of WC, TiC, and HfC; and a binder matrix that binds the hard particles and comprises rhenium, wherein the hard particles are less than 75% of a total weight of the material and rhenium is between 4% to 72% of the total weight of the material.

6. The material as in above item no. 5, wherein the at least one carbide is ZrC which is greater than about 32% of the total weight of the material, and the rhenium is less than about 68% of the total weight of the material.
7. The material as in above item no. 5, wherein the at least one carbide is VC which is greater than about 28% of the total weight of the material, and the rhenium is less than about 72% of the total weight of the material.
8. The material as in above item no. 5, wherein the at least one carbide is NbC which is greater than about 36% of the total weight of the material, and the rhenium is less than about 64% of the total weight of the material.
9. The material as in above item no. 5, wherein the at least one carbide is TaC which is greater than about 51% of the total weight of the material, and the rhenium is less than about 49% of the total weight of the material.
10. The material as in above item no. 5, wherein the at least one carbide is Cr2C3 which is greater than about 32% of the total weight of the material, and the rhenium is less than about 68% of the total weight of the material.
11. The material as in above item no. 5, wherein the at least one carbide is M02C which is greater than about 39% of the total weight of the material, and the rhenium is less than about 61% of the total weight of the material.

=25 12. A material, comprising:
hard particles comprising at least one nitride from nitrides of IVB and Vb columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium, wherein the rhenium is between about 4% to about 72% of the total weight of the material.
13. The material as in above item no. 12, wherein the at least one nitride is TiN which is between about 28% to about 89% of the total weight of the material.

14. The material as in above item no. 12, wherein the at least one nitride is ZrN which is between about 34% to about 92% of the total weight of the material, and the rhenium is between about 8% to about 66% of the total weight of the material.
15. The material as in above item no. 12, wherein the at least one nitride is HfN which is between about 50% to about 96% of the total weight of the material, and the rhenium is between about 4% to about 50% of the total weight of the = material.
16. The material as in above item no. 12, wherein the at least one nitride is VN which is between about 30% to about 91% of the total weight of the material, and the rhenium is between about 9% to about 70% of the total weight of the material.
17. The material as in above item no. 12, wherein the at least one nitride is NbN which is between about 34% to about 92% of the total weight of the material, and the rhenium is between about 8% to about 66% of the total weight of the material.
18. The material as in above item no. 12, wherein the at least one nitride is TaN which is between about 51% to about 96% of the total weight of the material, and the rhenium is between about 4% to about 49% of the total weight of the material.
19. A material, comprising:
hard particles comprising at least one nitride from nitrides of IVB and Vb columns in the periodic table; and a binder matrix that binds the hard particles and comprises a Ni-based superalloy which is between about 1.7% to about 50% of a total weight of the material.
20. The material as in above item no. 19, wherein the at least one nitride is TiN between aboti.t 50% to about 96% of the total weight of the material and the Ni-based superalloy which is between about 4% to about 50% of =the total weight of the material.
21. The material as in above item no. 19, wherein the at least one nitride is ZrN between about 58% to about 97% of the total weight of the material and the Ni-based superalloy which is between about 3% to about 42% of the total weight of the material.
22. The material as in above item no. 19, wherein the at least one nitride is HfN between about 72% to about 98.2% of the total weight of the material and the Ni-based superalloy which is between about 1.8% to about 28% of the total weight of the material.
23. The material as in above item no. 19, wherein the at least one nitride is VN between about 53% to about 96% of the total weight of the material and the Ni-based superalloy which is between about 4% to about 47% of the total weight of the material.
24. The material as in above item no_ 19, wherein the at least one nitride is NbN between about 52% to about 97% of the total weight of the material and the Ni-based superalloy which is between about 3% to about 42% of the total weight of the material.
25. The material as in above item no. 19, wherein the at least one nitride is TaN between about 73% to about 98.3% of the total weight of the material and the Ni-based superalloy which is between about 1.7% to about 27% of the total weight of the material.
26. A material, comprising:
hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table;
and a binder matrix that binds the hard particles and comprises rhenium and a Ni-based superalloy, wherein the hard particles are between about 26.1 % to about 98.4% of a total weight of the material.
27. The material as in above item no. 26, wherein the at least one carbide is TiC between about 26.1% to about 95.1% of the total weight of the material, the rhenium is not greater than about 73.6% of the total weight of the material, and the Ni-based superalloy is not greater than about 51.1% of the total weight of the material.
28. The material as in above item no. 26, wherein the at least one carbide is ZrC between about 32% to about 96% of the total weight of the material, the rhenium is not greater than about 67.7% of the total weight of the material, and the Ni-based superalloy is not greater than about 44.1% of the total weight of the material.
29. The material as in above item no. 26, wherein the at least one carbide is HfC between about 47.7% to about 98.1% of the total weight of the material, the rhenium is not greater about 52.1% of the total weight of the material, and the Ni-based superalloy is not greater about 29.2% of the total weight of the material.
30. The material as in above item no. 26, wherein the at least one carbide is VC between about 28.3% to about 95.6% of the total weight of the material, the rhenium does not exceed about 71.5% of the total weight of the material, and the Ni-based superalloy does exceed about 48.4% of the total weight of the material.
31. The material as in above item no. 26, wherein the at least one carbide is NbC between about 36% to about 96.9% of the total weight of the material, the rhenium is equal to or less than about 63.8% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 39.9%
of the total weight of the material.

32. The material as in above item no. 26, wherein the at least one carbide is TaC between about 51% to about 98.3% of the total weight of the material, the rhenium is equal to or less than about 48.8% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 26.5%
of the total weight of the material.
33. The material as in above item no. 26, wherein the at least one carbide is Cr2C3 between about 32.4% to about 96.4%
of the total weight of the material, the rhenium is equal to or less than about 67.3% of the total weight of the material, and the Ni-based superalloy is equal*to or less than about 43.6% of the total weight of the material.
34. The material as in above item no. 26, wherein the at least one carbide is M02C between about 39.6% to about 97.3%
of the total weight of the material, the rhenium is equal to or less than about 60.2% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 36.3% of the total weight of the material.
35. The material as in above item no. 26, wherein the at least one carbide is WC between about 52.9% to about 98.4% of the total weight of the material, the rhenium is equal to or less than about 46.9% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 25% of the total weight of the material.
36. A material, comprising:
hard particles comprising at least one nitride from nitrides of IVb and Vb columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium and a Ni-based superalloy, .30 wherein the hard particles are between about 28% to about 98.3% of a total weight of the material.

37. The material as in above item no. 36, wherein the at least one nitride is TiN between about 28% to about 95.6% of the total weight of the material, the rhenium is equal to or less than about 71.7% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 48.7%
of the total weight of the material.
38. The material as in above item no. 36, wherein the at least one nitride is ZrN between about 34.5% to about 96.7% of the total weight of the material, the rhenium is equal to or less than about.65.30 of the total weight of the material, and the Ni-based superalloy is equal to or less than about 41.4%
of the total weight of the material.
39. The material as in above item no. 36,.wherein the at least one nitride is HfN between about 49.6% to about 98.2% of the total weight of the material, the rhenium is equal to or less than about 50% of the'total weight of the material, and the Ni-based superalloy is equal to or less than about 27.5%
of the total weight of the material.
40. The material as in above item no. 36, wherein the at least one nitride is VN between about 30% to about 96% of the total weight of the material, the rhenium is equal to or less than about 69_6% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 46.2% of the total weight of the material.
41. The material as in above item no. 36, wherein the at least one nitride is NbN between about 34.4% to about 96.7% of the total weight of the material, the rhenium is equal to or less than about 65.3% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 41.5%
of the total weight of the material.
42. The material as in above item no. 36, wherein the at least one nitride is TaN between about 50.7% to about 98.3% of the total weight of the material, the rhenium is equal to or less than about 49.1% of the total weight of the material, and the Ni-based superalloy is equaZ to.or less than about 26.8%
of the total weight of the material.
43. A material, comprising:
hard particles comprising at least one carbide from carbides of IVb, Vb, and Vib columns in the periodic table;
and a binder matrix that binds the hard particles and comprises rhenium and cobalt, wherein the hard particles are between about 26.1 % to about 98.2% of a total weight of the material.
44. The material as in above item no. 43, wherein the at least one carbide is TiC between about 26.1% to about 94.6% of the total weight of the material, the rhenium is equal to or less than about 73.6% of the total weight of the material, and the cobalt is equal to or less than about 54.1% of the total weight of the material.
45. The material as in above item no. 43, wherein the at least one carbide is ZrC between about 32% to about 96% of the total weight of the material, the rhenium is equal to or less than about 67.7% of the total weight of the material, and cobalt is equal to or less than about 47.1% of the total weight of the material.
46. The material as in above item no. 43, wherein the at least one carbide is HfC between about 47.6% to about 97.8% of the total weight of the material, the rhenium is equal to or less than about 52.1% of the total weight of the material, and the cobalt is equal to or less than about 31.8% of the total weight of the material.
47. The material as in above item no. 43, wherein the at least one carbide is VC between about 28.3% to about 95.1% of the total weight of the material, the rhenium is equal to or less than about 71.4% of the total weight of the material, and the cobalt is equal to or less than about 51.5% of the total weight of the material.

~41~
48. The material as in above item no. 43, wherein the at least one carbide is NbC between about 36% to about 96.5% of the total weight of the material, the rhenium is equal to or less than about 63.8% of the total weight of the material, and the cobalt is equal to or less than about 42.8% of the total weight of the material.
49. The material as in above item no. 43, wherein the at least one carbide is TaC between about 51% to about 98% of the total weight of the material, the rhenium is equal to or less .10 =than about 48.8% of the total weight of the material, and the cobalt is equal to or less than about 28.9% of the total weight of the material.
50. The material as in above item no. 43, wherein the at least one carbide is Cr2C3 between about 32.4% to about 96% of the total weight of the material, the rhenium is equal to or less than about 67.3% of the total weight of the material, and the cobalt is equal to or less than about 46.6% of the total weight of the material.
51. The material as in above item no. 43, wherein the at .20 least one carbide is M02C between about 39.6% to about 97% of the total weight of the material, the rhenium is equal to or less than about 60.2% of the total weight of the material, and the cobalt is equal to or less than about 39.2% of the total weight of the material.
52. The material as in above item no. 43, wherein the at least one carbide is WC between about 52.9% to about 98.2% of the total weight of the material, the rhenium is equal to or less than about 46.9% of the total weight of the material, and the cobalt is equal to or less than about 27.4% of the total weight of the material.
53. A material, comprising:
hard particles comprising at least one nitride from nitrides of IVb and Vb columns in the periodic table; and --42 =-a binder matrix that binds the hard particles and comprises rhenium and cobalt, wherein the hard particles are between about 28% to about 98% of a total weight of the material.
54. The material as in above item no. 53, wherein the at least one nitride is TiN between about 28% to about 95% of the total weight of the material, the rhenium is up to about 71.6%
of the total weight of the material, and the cobalt is up to about 51.7% of the total weight of the material.
55. The material as in above item no. 53, wherein the at least one nitride is ZrN between about 34.5% to about 96.3% of the total weight of the material, the rhenium is up to about 65.3% of the total weight of the material, and the cobalt is up to about 44.4% of the total weight of the material.
56. The material as in above item no. 53, wherein the at least one nitride is HfN between about 49.8% to about 98% of the total weight of the inaterial, the rhenium is up to about 50% of the total weight of the material, and the cobalt is up to about 30% of the total weight of the material.
57. The material as in above item no. 53, wherein the at least one nitride is VN between about 30% to about 95.5% of the total weight of the material, the rhenium is up to about 69.6% of the total weight of the material, and the cobalt is up to about 49.3% of the total weight of the material.
58. The material as in above item no. 53, wherein the at least one nitride is NbN between about 34.4% to about 96.3% of the total weight of the material, the rhenium is up to about 65.3% of the total weight of the material, and the cobalt is up to about 44.5% of the total weight of the material.
59_ The material as in above item no. 53, wherein the at least one nitride is TaN between about 50.7% to about 98% of the total weight of the material, the rhenium is up to d about 49.1% of the total weight of the material, and the cobalt is up to about 29.2% of the total weight of the material.

60. A material, comprising:
hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table;
and a binder matrix that binds the hard particles and comprises a Ni-based superalloy and cobalt, wherein the hard particles are between about 45 % to about 98% of a total weight of the material.
61. The material as in above item no. 60, wherein the at least one carbide is TiC between about 45% to about 95% of the total weight of the material, the Ni-based superalloy is up to about 51.5% of the total weight of the material, and the cobalt is up to about 54.5% of the total weight of the material.
62. The material as in above item no. 60, wherein the at least one carbide is ZrC between about 52% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 44.4% of the total weight of the material, and cobalt is up to about 47.4% of the total weight of the material.
63. The material as in above item no. 60, wherein the at least one carbide is HfC between about 68% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 29% of the total weight of the material, and the cobalt is up to about 32% of the total weight of the material.
64. The material as in above item no. 60, wherein the at least one carbide is VC between about 48% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 49% of the total weight of the material, and the cobalt is up to about 52% of the total weight of the material.
65. The material as in above item no. 60, wherein the at least one carbide is NbC between about 57% to about 97% of the total weight of the material, the Ni-based superalloy is up to about 40% of the total weight of the material, and the cobalt is up to about 43% of the total weight of the material.

66_ The material as in above item no. 60, wherein the at least one carbide is TaC between about 71% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 27% of the total weight of the material, and the cobalt is up to about 29% of the total weight of the material.
67. The material as in above item no. 60, wherein the at least one carbide is Cr2C3 between about 53% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 67.3% of the total weight of the material, and the cobalt'is up to about 44% of the total weight of the material.
68. The material as in above item no. 60, wherein the at least one carbide is Mo2C between about 60% to about 97% of the total weight of the material, the Ni-based superalloy is up to about 36.5% of the total weight of the material, and the cobalt is up to about 39% of the total weight of the material.
69. The material as in above item no. 60, wherein the at least one carbide is WC between about 72% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 46.9% of the total weight of the material, and the cobalt is up to about 27.5% of the total weight of the material.
70. A material, comprising:
hard particles comprising at least one nitride from nitrides of IVb and Vb columns in the periodic table; and a binder matrix that binds the hard particles and comprises a Ni-based superalloy and cobalt, wherein the hard particles are between about 47% to about 98% of a total weight of the material.
71. The material as in above item no. 70, wherein the at least one nitride is TiN between about 47% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 49% of the total weight of the material, and the cobalt is up to about 52% of the total weight of the material.

72. The material as in above item no. 70, wherein the at least one nitride is ZrN between about 55% to about 97% of the total weight of the material, the Ni-based superalloy is up to about 42% of the total weight of the material, and the cobalt is up to about 45% of the total weight of the material.
73. The material as in above item no. 70, wherein the at least one nitride is HfN between about 70% to about 98% of the total weight of the material, the Ni.-based superalloy is up to about 31% of the total weight of the material, and the cobalt =10 is up to about 27% of the total weight of the material.
74. The material as in above item no. 70, wherein the at least one nitride is VN between about 50% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 53% of the total weight of the material, and the cobalt is up to about 44% of the total weight of the material.
75. The material as in above item no. 70, wherein the at least one nitride is NbN between about 55% to about 97% of the total weight of the material, the Ni-based superalloy is up to about 47% of the total weight of the material, and the cobalt is up to about 40% of the total weight of the material.
76. The material as in above item no. 70, wherein the at least one nitride is TaN between about 70% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 30% of the total weight of the material, and the cobalt .25 is up to about 26% of the total weight of the material.
77. A material, comprising:
hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table;
and a binder matrix that binds the hard particles and comprises rhenium, a Ni-based superalloy and cobalt, wherein the hard particles are between about 26 % to about 98.3% of a total weight of the material.

78. The material as in above item no. 77, wherein the at least one carbide is TiC between about 26% to about 95% of the total weight of the material, the rhenium is up to about 73.6%
of the total weight of the material, the Ni-based superalloy is up to about 51.3% of the total weight of the material, and the cobalt is up to about 54.3% of the total weight of the material.
79. The material as in above item no. 77, wherein the at least one carbide is ZrC between about 32% to about 96% of the total weight of the material, the rhenium is up to about 67.7%
of the total weight of the material, the Ni-based superalloy is up to about 44.2% of the total weight of the material, and the cobalt is up to about 47.2% of the total weight of the material.
80. The material as in above item no. 77, wherein the at least one carbide is HfC between about 48% to about 98% of the total weight of the material, the rhenium is up to about 52.1%
of the total weight of the material,.the Ni-based superalloy is up to about 29.3% of the total weight of the material, and the cobalt is up to about 31.8% of the total weight of the material.
81. The material as in above item no. 77, wherein the at least one carbide is VC between about 28% to about 96% of the total weight of the material, the rhenium is up to about 71.5%
of the total weight of the material, the Ni-based superalloy is up to about 48.6% of the total weight of the material, and the cobalt is up to about 51.7% of the total weight of the material.
82. The material as in above item no. 77, wherein the at least one carbide is NbC between about 36% to about 97% of the total weight of the material, the rhenium is up to about 63.8%
of the total weight of the material, the Ni-based superalloy is up to about 40% of the total weight of the material, and the cobalt is up to about 43% of the total weight of the material.
83. The material as in above item no. 77, wherein the at least one carbide is TaC between about 51% to about 98.3% of the total weight of the material, the rhenium is up to about 48.8% of the total weight of the material, the Ni-based superalloy is up to about 26.6% of the total weight of the material, and the cobalt is up to about 29% of the total weight of the material.
84. The material as in above item no. 77, wherein the at least one carbide is Cr2C3 between about 32% to about 96% of the total weight of the material, the rhenium is up to about 67.3% of the total weight of the material, the Ni-based superalloy is up to about 43.8% of the total weight of the material, and the cobalt is up to about 46.8% of the total weight of the material.
85. The material as in above item no. 77, wherein the at least one carbide is M02C between about 39% to about 97% of the total weight of the material, the rhenium is up to about 60.2% of the total weight of the material, the Ni-based superalloy is up to about 36.4% of the total weight of the material, and the cobalt is up to about 39.3% of the total weight of the material.
86. The material as in above item no. 77, wherein the at least one carbide is WC between about 53% to about 98% of the total weight of the material, the rhenium is up to about 46.9%
of the total weight of the material, the Ni-based superalloy is up to about 25.1% of the total weight of the material, and the cobalt is up to about 27.5% of the total weight of the material.
87. A material, comprising:
hard particles comprising at least one nitride from nitrides of IVb and Vb columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium, a Ni-based superalloy, and cobalt, wherein the hard particles are between about 28% to about 98.3% of a total weight of the material.
88. The material as in above item no. 87, wherein the at least one nitride is TiN between about 28% to about 96% of the total weight of the material, the rhenium is up to about 71.6%
of the total weight of the material, the Ni-based superalloy is up to about 48.8% of the total weight of the material, and the cobalt is up to about 51.9% of the total weight of the material.
89. The material as in above item no. 87, wherein the at least one nitride is ZrN between about 34% to about 97% of the total weight of the material, the rhenium is up to about 65.3%
of the total weight of the material,. the Ni-based superalloy is up to about 41.6% of the total weight of the material, and the cobalt is up to about 44.6% of the total weight of the material.
90. The material as in above item no. 87, wherein the at least one nitride is HfN between about 50% to about 98% of the total weight of the material, the rhenium is up to about 50%
of the total weight of the material, the Ni-based superalloy is up to about 27.5% of the total weight of the material, and the cobalt is up to about 30% of the total weight of the material.
91. The material as in above item no. 87, wherein the at least one nitride is VN between about 30% to about 96% of the total weight of the material, the rhenium is up to about 60%
of the total weight of the material, the Ni-based superalloy is up to about 46.4% of the total weight of the material, and the cobalt is up to about 49% of the total weight of the material.

92. The material as in above item no. 87, wherein the at least one nitride is NbN between about 34% to about 97% of the total weight of the material, the rhenium is up to about 65%
of the total weight of the material, the Ni-based superalloy is up to about 42% of the total weight of the material, and the cobalt is up to about 45% of the total weight of the material.
93. The material as in above item no. 87, wherein the at least one nitride is TaN between about 51% to about 98.3% of =lo the total weight of the material, the rhenium is up to about 49% of the total weight of the material, the Ni-based superalloy is up to about 27% of the total weight of the material, and the cobalt is up to about 29% of the total weight of the material.
.15 94. A material, comprising:
hard particles comprising WC and TiC which are between about 40% to about 96% and between about 0.3% to about 21% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and 20 comprises rhenium which is between about 4 % to about 54% of the total weight of the material.
95. A material, comprising:
hard particles comprising WC between about 44% to about 96% and TaC up to about 21% of a total weight of the material, 25 respectively; and a binder matrix that binds the hard particles and comprises rhenium which is between about 4% to about 48% of.
the total weight of the material.
96. A material, comprising:
30 hard particles comprising WC, TiC and TaC which are between about 36% to about 95%, up to about 22%, and up to about 25% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium which is between about 4% to about 48% of a total weight of the material.
97_ A material, comprising:
hard particles comprising WC and TiC which are between about 60% to about 98%, and up to about 25% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a Nickel-based superalloy which is between about 1.5 % to about 31% of the total weight of the material.
98. A material, comprising:
hard particles comprising WC and TaC which are between about 63% to about 98%, and up to about 26% of a total weight of the material, respectively; and a binder matrix that binds the.hard particles and comprises a Nickel-based superalloy which is between about 1.5 % to about 26% of the total weight of the material.

99. A material, comprising:
hard particles comprising WC, Tic and TaC which are between about 51% to about 98%, up to about 23%, and up to about 26% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a Nickel-based superalloy which is between about 1.5 % to about 26% of the total weight of the material.

100. A material, comprising:
hard particles comprising WC and TiC which are between about 40% to about 98%, and up to about 24% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and a Nickel-based superalloy which are up to about 52% and 29% of the total weight of the material, respectively.

101. A material, comprising:
hard particles comprising WC and TaC which are between about 44% to about 98%, and up to about 24% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and a Nickel-based superalloy which are up to about 47% and about 25% of the total weight of the material, respectively.
102. A material, comprising:
hard particles comprising WC, TiC and TaC which are between about 40% to about 98%, up to about 23%, and up about 26% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and a Nickel-based superalloy which are up to about 53% and about 30% of the total weight of the material, respectively.
103. A material, comprising:
hard particles comprising WC and TiC which are between about 40% to about 98%, and up to about 23% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 53% and about 31% of the total weight of the material, respectively.

104. A material, comprising:
hard particles comprising WC and TaC which are between about 44% to about 98%, and up to about 24% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 47% and about 28% of the total weight of the material, respectively.
105. A material, comprising:
hard particles comprising WC, Tic and TaC which are between about 40% to about 98%, up to about 23%, and up to about 26% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 53% and about 33% of the total weight of the material, respectively.
106. A material, comprising:
hard particles comprising WC and TiC which are between about 58% to about 98%, and up to about 24% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises cobalt and a nickel-based superalloy which are up to about 33% and about 29% of the total weight of the material, respectively.
107. A material, comprising:
hard particles comprising WC and TaC which are between about 61% to about 98%, and up to about 24% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises cobalt and a nickel-based superalloy which are up to about 28% and about 25% of the total weight of the material, respectively.
108. A material, comprising:
hard particles comprising WC, TiC and TaC which are between about 57% to about 98%, up to about 23%, and up to about 26% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises cobalt and a nickel-based superalloy which are up to about 33% and about 30% of the total weight of the material, respectively.
109. A material, comprising:
hard particles comprising WC and TiC which are between about 40% to about 98%, and up to about 24% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises cobalt up to about 32% of the total weight of the material, rhenium and a nickel-based superalloy which are up to about 54% and about 29% of the total weight of the material, respectively.
110. A material, comprising:
hard particles comprising WC and TaC which are between about 45% to about 98%, and up to about 24% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises cobalt up to about 28% of the total weight of the material, rhenium and a nickel-based superalloy which are up .10 to about 47% and about 26% of the total weight of the material, respectively.
111. A material, comprising:
hard particles comprising WC, TiC and TaC which are between about 35% to about 93%, up to about 25%, and up to 'about 26% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises cobalt up to about 44% of the total weight of the material, rhenium and a nickel-based superalloy which are up to about 65% and about 41% of the total weight of the material, respectively.
112. A material, comprising:
hard particles comprising TiC between about 19% to about 88% of a total weight of the material and M02C up to about 38%
of the total weight of the material; and a binder matrix that binds the hard particles and comprises rhenium between about 9.5 % to about 65% of the total weight of the material.
113. A material, comprising:
hard particles comprising TiN between about 21% to about 89% of a total weight of the material and M02C up to about 36%
of the total weight of the material; and a binder matrix that binds the hard particles and comprises rhenium between about 9% to about 63% of the total weight of the material.

114. A material, comprising:
hard particles comprising Ti.C up to about 84% of a total weight of the material, T.iN up to about 85% of the total weight of the material, and M02C up to about 36% of the total weight of the material; and a binder matrix that binds the hard particles and comprises rhenium between about 9% to about 64% of the total weight of the material.
115. A material, comprising:
hard particles comprising TiC up to about 83% of a total weight of the material, TiN up to about 85% of the total weight of the material, MoaC up to about 25% of the total weight of the material, WC up to about 39% of the total weight of the material, TaC up to about 30% of the total weight of the material, VC up to about 11% of the total weight of the material, and Cr2C3 up to about 16% of the total weight of the material; and a binder matrix that binds the hard particles and comprises rhenium between about 6%.to about 65% of the total weight of the material.
116. A material, comprising:
hard particles comprising T.i.C and Mo2C which are between about 30% to about 90% and up to about 40% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a nickel based superalloy which is between about 4%
to about 41% of the total weight of the material.
117. A material, comprising:
hard particles comprising TiN and M02C which are up to about 91% and up to about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a nickel based superalloy which is between about 4%
to about 38% of the total weight of the material.

118. A material, comprising:
hard particles comprising TiC, TiN and MoaC which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a nickel based superalloy which is between about 4%
to about 40% of the total weight of the material.
119. A material, comprising:
hard particles comprising TiC, TiN, M02C, WC, and TaC
which are up to about 90%, about 90%, about 25%, about 42%, and about 36% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 14% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises a nickel based superalloy which is between about 2%
to about 40% of the total weight of the material.
120. A material, comprising:
hard particles comprising TiC, TiN and Mo2C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and a nickel based superalloy which are up to about 64% and about 40% of the total weight of the material, respectively.
121. A material, comprising:
hard particles comprising TiC, TiN, M02C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises rhenium and a nickel based superalloy which are up to about 64% and about 40% of the total weight of the material, respectively.
122. A material, comprising:
hard particles comprising TiC, TiN and M02C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and nickel which are up to about 64% and about 42% of the total weight of the material, respectively.
123. A material, comprising:
hard particles comprising TiC, TiN, M02C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises rhenium and nickel which are up to about 64% and about 42% of the total weight of the material, respectively.
124. A material, comprising:
hard particles comprising TiC, TiN and Mo2C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 64% and about 43% of the total weight of the material, respectively.
125. A material, comprising:
hard particles comprising TiC, TiN, Mo2C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 32% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 64% and about 43% of the total weight of the material, respectively.
126. A material, comprising:
hard particles comprising TiC, TiN and MozC which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a nickel-based superalloy and cobalt which are up to about 40% and about 43% of the total weight of the material, respectively.
127. A material, comprising:
hard particles comprising TiC, TiN, M02C, WC, and TaC
which are up to about 89%, about 90%, about 26%, between about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a nickel-based superalloy and cobalt which are up to about 40% and about 43% of the total weight of the material, respectively.
128. A material, comprising:
hard particles comprising TiC, TiN and M02C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a nickel-based superalloy and nickel which are up to about 40% and about 43% of the=total weight of the material, respectively.
129. A material, comprising:
hard particles comprising TiC, TiN, M02C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises a nickel-based superalloy and nickel which are up to about 40% and about 43% of the total weight of the material, respectively.
130. A material, comprising:
hard particles comprising TiC, TiN and Mo2C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and cobalt which are up to about 64%, about 40% and about 42% of the total weight of the material, respectively.
131. A material, comprising:
hard particles comprising TiC, TiN, M02C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and cobalt which are up to about 63%, about 39% and about 42% of the total weight of the material, respectively..
132. A material, comprising:
hard particles comprising TiC, TiN and M02C which are up to about 90%, about 91% and about 38% of a total weight of the .30 material, respectively; and a binder matrix that liinds the hard particles and comprises rhenium, a nickel-based superalloy and nickel which are up to about 63%, about 40% and about 42% of the total weight of the material, respectively.

133. A material, comprising:
hard particles comprising TiC, TiN, M02C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and nickel which are up to about 63%, about 39% and about 42% of the total weight of the material, respectively..
134. A material, comprising:
hard particles comprising TiC, TiN and Mo2C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium, nickel and cobalt which are up to about 63%, about 42% and about 42% of the total weight of the material, respectively.
135. A material, comprising:
hard particles comprising TiC, TiN, M02C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises rhenium, a nickel and cobalt which are up to about 63%, about 42% and about 42% of the total weight of the material, respectively...
136. A material, comprising:
hard particles comprising TiC, TiN and Mo2C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises a nickel-based superalloy, nickel and cobalt which are up to about 40%, about 42% and about 43% of the total weight of the material, respectively.
137. A material, comprising:
hard particles comprising TiC, Ti.N, M02C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises a nickel-based superalloy, nickel and cobalt which are up to about 40%, about 42% and about 42% of the total weight of the material, respectively.
138. A material, comprising:
hard particles comprising TiC, TiN and M02C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy, nickel and cobalt which are up to about 63%, about 39%, about 42% and about 42% of the total weight of the material, respectively.
139. A material, comprising:
hard particles comprising TiC, TiN, Mo2C, WC, and TaC
which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr2C3 up to about 16% and 18% of the total weight of the material, respectively;
and a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy, nickel and cobalt which are up to about 63%, about 39%, about 42% and about 42% of the total weight of the material, respectively.

140. A material, comprising:
hard particles comprising at least one boride from borides of IVB, VB and VIB columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium, wherein the rhenium is between about 4% to about 76% of the total weight of the material.
141. The material as in above item no. 140, wherein the at least one boride is TiB2 which is between about 24% to about 87.5% of the total weight of the material, and the rhenium is between about 12.5% to about 76% of the total weight of the material.
142. The material as in above item no. 140, wherein the at least one boride is ZrB2 which is between about 30% to about 90.5% of the total weight of the material, and the rhenium is between about 9.5% to about 70% of the total weight of the material.
143. The material as in above item no. 140, wherein the at least one boride is HfB2 which is between about 44.5% to about 94.5% of the total weight of the material, and the rhenium is between about 5.5% to about 55.5% of the total weight of the material.
144. The material as in above item no. 140, wherein the at least one boride is VB2 which is between about 27% to about 89% of the total weight of the material, and the rhenium is between about 11% to about 73% of the total weight of the material.
145. The material as in above item no. 140, wherein the at least one boride is NbB2 which is between about 34% to about 92% of the total weight of the material, and the rhenium 30- is between about 8% to about 66% of the total weight of the material.
146. The material as in above item no. 140, wherein the at least one boride is TaB2 which is between about 47% to about 95% of the total weight of the material, and the rhenium is between about 5% to about 53% of the total weight of the material.
147. The material as in above item no. 140, wherein the at least one boride is Cr3B2 which is between about 30.5% to about 90.5% of the total weight of the material, and the rhenium is between about 9.5% to about 69.5% of the total weight of the material.
148. The material as in above item no. 140, wherein the at least one boride is MOB2 which is between about 36% to about 92.5% of the total weight of the material, and the rhenium is between about 7.5% to about 64% of the total weight of the material.
149. The material as in above item no. 140, wherein the at least one boride is WB which is between about 53% to about 96% of the total weight of the material, and the rhenium is between about 4% to about 47% of the total weight of the material.
150. The material as in above item no. 140, wherein the at least one boride is W2B which is between about 53% to about 96% of the total weight of the material, and the rhenium is between about 4% to about 47% of the total weight of the material.
151. A material, comprising:
hard particles comprising at least one silicide from silicides of IVB, VB and VIB columns in the periodic table;
and a binder matrix that binds the hard particles and comprises rhenium, wherein the rhenium is between about 6% to about 77% of the total weight of the material.
-30 152. The material as in above item no. 151, wherein the at least one silicide is Ti5Si3 which is between about 23% to about 87% of the total weight of the material, and the rhenium is between about 13% to about 77% of the total weight of the material.

153. The material as in above item no. 151, wherein the at least one silicide is Zr6Si5 which is between about 28% to about 90% of the total weight of the material, and the rhenium is between about 10% to about 72% of the total weight of the material.
154. The material as in above item no. 151, wherein the at least one silicide is NbSi2 which is between about 31% to about 91% of the total weight of the material, and the rhenium is between about 9% to about 69% of the total weight of the material.
155. The material as in above item no. 151, wherein the at least one silicide is TaSi2 which is between about 38% to about 93% of the total weight of the material, and the rhenium is between about 7% to about 62% of the total weight of the material.
156. The material as in above item no. 151, wherein the at least one silicide is MoSia which is between about 31% to about 91% of the total weight of the material, and the rhenium is between about 9% to about 69% of the total weight of the material.
157. The material as in above item no. 151, wherein the at least one silicide is WSi2 which is between about 40% to about 94% of the total weight of the material, and the rhenium is between about 6% to about 60% of the total weight of the material.
158. A material, comprising:
hard particles; and a binder matrix that binds the hard particles and comprises tungsten.
159. The material as in above item no. 158, wherein the hard particles comprise at least one carbide from carbides of IVB, VB and VIB columns in the periodic table and the tungsten is between about 4% to about 72% of the total weight of the material.

160. The material as in above item no.159, wherein the at least one carbide is TiC which is between about 28% and about 89% of the total weight of the material, and the tungsten is between about 11% and about 72% of the total weight of the material.
161. The material as in above item no. 159, wherein the at least one carbide is ZrC which is between about 34% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 66% of the total weight of the material.
162. The material as in above item no. 159, wherein the at least one carbide is HfC which is between about 50% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 50% of the total weight of the material.
163. The material as in above item no. 159, wherein the at least one carbide is VC which is'between about 30% and about 90% of the total weight of the material, and the tungsten is between about 10% and about 70% of the total weight of the material.
164. The material as in above item no. 159, wherein the at least one carbide is NbC which is between about 38% and about 93% of the total weight of the material, and the tungsten is between about 7% and about 62% of the total weight of the material.
165. The material as in above item no. 159, wherein the at least one carbide is TaC which is between about 53% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 47% of the total weight of the material.
166. The material as in above item no. 159, wherein the at least one carbide is Cr2C3 which is between about 34% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 66% of the total weight of the material.
167. The material as in above item no. 159, wherein the at least one carbide is Mo2C which is between about 41% and about 94% of the total weight of the material, and the tungsten is between about 6% and about 59% of the total weight of the material.
168. The material as in above item no. 159, wherein the at least one carbide is WC which is between about 55% and =10 about 96% of the total weight of the material, and the tungsten is between about 4% and about 45% of the total weight of the material.
169. The material as in above item no. 158, wherein the hard particles comprise at least one nitride from nitrides of ,15 IVB and VB columns in the periodic table and the tungsten is between about 4% and about 72% of the total weight of the material.
170. The material as in above item no. 169, wherein the at least one nitride is TiN which is between about 28% and 20 about 89% of the total weight of the material, and the tungsten is between about 11% and about 72% of the total weight of the material.
171. The material as in above item no. 169, wherein the at least one nitride is ZrN which is between about 36% and 25 about 92% of the total weight of the material, and the tungsten is between about 8% and about 64% of the total weight of the material.
172. The material as in above item no. 169, wherein the at least one nitride is HfN which is between about 52% and 30 about 96% of the total weight of the material, and the tungsten is between about 4% and about 48% of the total weight of the material.

173. The material as in above item no. 169, wherein the at least one nitride is VN which is between about 32% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 68% of the total weight of the material.
174. The material as in above item no. 169, wherein the at least one nitride is NbN which is between about 36% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 64% of the total weight of the material.
175. The material as in above item no. 169, wherein the at least one nitride is TaN which is between about 53% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 47% of the total weight of the material.
176. The material as in above item no. 158, wherein the hard particles comprise at least one boride from borides of IVB, VB and VIB colu.mns in the periodic table and the tungsten is between about 3% and about 74% of the total weight of the material.
177. The material as in above item no. 176, wherein the at least one boride is TiB2 which is between about 26% and about 88% of the total weight of the material, and the tungsten is between about 12% and about 74% of the total weight of the material.
178. The material as in above item no. 176, wherein the at least one boride is ZrB2 which is between about 32% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 68% of the total weight of the material.
179. The material as in above item no. 176, wherein the at least one boride is HfBa which is between about 46% and about 95% of the total weight of the material, and the tungsten is between about 5% and about 54% of the total weight of the material.
180. The material as in above item no. 176, wherein the at least one boride is VB2 which is between about 28% and about 90% of the total weight of the material, and the tungsten is between about 10% and about 72% of the total weight of the material.
181. The material as in above item no. 176, wherein the at least one boride is NbB2 which is between about 36% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 64% of the total weight of the material.
182. The material as in above item no. 176, wherein the at least one boride is TaB2 which is between about 49% and about 95% of the total weight of the material, and the tungsten is between about 5% and about 51% of the total weight of the material.
183. The material as in above item no. 176, wherein the at least one boride is Cr3B2 which is between about 32% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 68% of the total weight of the material.
184. The material as in above i.tem no. 176, wherein the at least one boride is MoB2 which is between about 38% and about 93% of the total weight of the material, and the tungsten is between about 7% and about 62% of the total weight of the material.
185. The material as in above item no. 176, wherein the at least one boride is WB which is between about 55% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 45% of the total weight of the material.

186. The material as in above item no. 176, wherein the at least one boride is W2B which is between about 56% and about 97% of the total weight of the material, and the tungsten is between about 3% and about 44% of the total weight of the material.
187. The material as in above item no. 158, wherein the hard particles comprise at least one silicide from silicides of IVB, VB and VIB columns in the periodic table and the tungsten is between about 6% and about 75% of the total weight of the material.
188. The material as in above item no. 187, wherein the at least one silicide is Ti5Si3 which is between about 25% and about 88% of the total weight of the material, and the tungsten is between about 12% and about 75% of the total weight of the material.
189. The material as in above item no. 187, wherein the at least one silicide is Zr6Si5 which is between about 30% and about 90% of the total weight of the material, and the tungsten is between about 10% and about 70% of the total weight of the material.
190. The material as in above item no. 187, wherein the at least one silicide is NbSi2 which is between about 33% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 67% of the total weight of the material.
191. The material as in above item no. 187, wherein the at least one silicide is TaSi2 which is between about 40% and about 93% of the total weight of the material, and the tungsten is between about 7% and about 60% of the total weight of the material.
192. The material as in above item no. 187, wherein the at least one silicide is MoSi2 which is between about 31% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 67% of the total weight of the material.
193. The material as in above item no. 187, wherein the at least one silicide is WSi2 which is between about 42% and about 94% of the total weight of the material, and the tungsten is between about 6% and about 58% of the total weight of the material.
194. The material as in above item no. 158, wherein the binder matrix material further comprises rhenium in addition to tungsten.
195. The material as in above item no. 194, wherein the hard particles comprise at least one carbide from carbides of IVB, VB and VIB columns in the periodic table, and wherein the rhenium is less than about 73% and tungsten is less than about 72% of the total weight of the material.
196. The material as in above item no. 195, wherein the at least one carbide is TiC which is between about 26% and about 89% of the total weight of the material.
197. The material as in above item no. 195, wherein the at least one carbide is ZrC which is between about 32% and about 92% of the total weight of the material.
198. The material as in above item no. 195, wherein the at least one carbide is HfC which is between about 48% and about 95% of the total weight of the material.
.25 199. The material as in above item no. 195, wherein the at least one carbide is VC which is between about 28% and about 90% of the total weight of the material.
200. The material as in above item no. 195, wherein the at least one carbide is NbC which is between about 36% and about 93% of the total weight of the material.
201. The material as in above item no. 195, wherein the at least one carbide is TaC which is between about 51% and about 96% of the total weight of the material.

202. The material as in above item no. 195, wherein the at least one carbide is Cr2C3 which is between about 32% and about 92% of the total weight of the material.
203. The material as in above item no. 195, wherein the at least one carbide is M02C which is between about 39% and about 94% of the total weight of the material_ 204. The material as in.above item no. 195, wherein the at least one carbide is WC which is between about 53% and about 96% of the total weight of the material.
205. The material as in above item no. 194, wherein the hard particles comprise at least one nitride from nitrides of IVB and VB columns in the periodic table, and wherein the rhenium is less than about 71% and tungsten is less than about 70% of the total weight of the material.
206. The material as in above item no. 205, wherein the at least one nitride is TiN which is between about 28% and about 90% of the total weight of the material.
207. The material as in above item no. 205, wherein the at least one nitride is ZrN which is between about 34% and about 92% of the total weight of the material.
208. The.material as in above item no. 205, wherein the at least one nitride is HfN which is between about 50% and about 96% of the total weight of the material.
209. The material as in above item no. 205, wherein the at least one nitride is VN which is between about 30% and about 91% of the total weight of the material.
210. The material as in above item no. 205, wherein the at least one nitride is NbN which is between about 35% and about 92% of the total weight of the material.
211. The material as in above item no.205, wherein the at least one nitride is TaN which is between about 51% and about 96% of the total weight of the material.

-73._ 212. The material as in above item no.194, wherein the hard particles comprise at least one boride from borides of IVB, VB and VIB columns in the periodic table, and wherein the rhenium is less than about 75% and tungsten is less than about 73% of the total weight of the material.
213. The material as in above item no. 212, wherein the at least one boride is TiB2 which is between about 24% and about 88% of the total weight of the material.
214. The material as in above item no. 212, wherein the at least one boride is ZrB2 which is between about 30% and about 91% of the total weight of the material.
215. The material as in above item no. 212, wherein the at least one boride is HfB2 which is between about 44% and about 95% of the total weight of the material.
215A. The material as in above item no. 212, wherein the at least one boride is VB2 which is between about 27% and about 90% of the total weight of the.material.
216. The material as in above item no. 212, wherein the at least one boride is NbrB2 which is between about 34% and about 92% of the total weight of the material.
217. The material as in above item no. 212, wherein the at least one boride is TaB2 which is between about 47% and about 96% of the total.weight of the material.
218. The material as in above item no. 212, wherein the at least one boride is Cr3B2 which is between about 32% and about 91% of the total weight of the material.
219. The material as in above item no. 212, wherein the at least one boride is MoB2 which is between about 36% and about 93% of the total weight of the material.
220. The material as in above item no. 212, wherein the at least one boride is WB which is between about 53% and about 96% of the total weight of the material.

221. The material as in above item no. 212, wherein the at least one boride is W2B which is between about 54% and about 97% of the total weight of the material.
223. The material as in above item no. 194, wherein the hard particles comprise at least one silicide from silicides of IVB, VB and VIB columns in the periodic table, and wherein the rhenium is less than about 76% and tungsten is less than about 74% of the total weight of the material.
224. The material as in above item no. 223, wherein the .10 at least one silicide is Ti5Si3 which is between about 24% and about 88% of the total weight of the material.
225. The material as in above item no. 223, wherein the at least one silicide is Zr6Si5 which is between about 28% and about 90% of the total weight of the material.
226. The material as in above item no. 223, wherein the at least one silicide is NbSi2 which is between about 31% and about 91% of the total weight of the material.
227. The material as in above item no. 223, wherein the at least one silicide is TaSi.z which is between about 38% and about 93% of the total weight of the material.
228. The material as in above item no. 223, wherein the at least one silicide is MoSi2 which is between about 31% and about 91% of the total weight of the material.
229. The material as in above item no. 223, wherein the at least one silicide is WSiz which is between about 40% and about 94% of the total weight of the material.
230. A material, comprising:
hard particles comprising at least one nitride from nitrides=of IVB and VB columns in the periodic table; and a binder matrix that binds the'hard particles and comprises rhenium which is less than 71% of a total weight of the material and cobalt which is less than 52% of the total weight of the material.

231. The material as in above item no. 230, wherein the at least one nitride is TiN which is between about 28% and about 95% of the total weight of the material.
232. The material as in above item no. 230, wherein the at least one nitride is ZrN which is between about 34% and about 96% of the total weight of the material.
233. The material as in above item no. 230, wherein the at least one nitride is HfN which is between about 50% and about 98% of the total weight of the material.
234. The material as in above item no. 230, wherein the at least one nitride is VN which is between about 30% and about 96% of the total weight of the material.
235. The material as in above item no. 230, wherein the at least one nitride is NbN which is between about 3496 and about 96% of the total weight of the material.
236. The material as in above item no. 230, wherein the at least one nitride is TaN which is between about 51% and about 98% of the total weight of the material.
237. A material, comprising:
hard particles comprising at least one boride from borides of IVB, VB and VIB columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium which is less than 75% of a total weight of the material and cobalt which is less than 56% of the total weight of the material.
238. The material as in above item no. 237, wherein the at least one boride is TiB2 which is between about 24% and about 34% of the total weight of the material.
239. The material as in above item no. 237, wherein the at least one boride is ZrB2 which is between about 30% and about 96% of the total weight of the material.
240. The material as in above item no. 237, wherein the at least one boride is HfBz which is between about 45% and about 98% of the total weight of the material.

241. The material as in above item no. 237, wherein the at least one boride is VB2 which is between about 27% and about 95% of the total weight of the material.
242. The material as in above item no. 237, wherein the at least one boride is NbB2 which is between about 34% and about 96% of the total weight of the material.
243. The material as in above item no. 237, wherein the at least one boride is TaB2 which is between about 48% and about 98% of the total weight of the material.
244. The material as in above item no. 237, wherein the at least one-boride is Cr3B2 which is between about 30% and about 96% of the total weight of the material.
245. The material as in above item no. 237, wherein the at least one boride is MoB2 which is between about 36% and about 97% of the total weight of the material.
246. The material as in above item no. 237, wherein the at least one boride is WB which is between about 53% and about 98% of the total weight of the material.
247. The material as in above item no. 237, wherein the at least one boride is W2B which is between about 55% and about 98% of the total weight of the material.
248. A material, comprising:
hard particles comprising at least one silicide from silicides of IVB and VB columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium which is less than 76% of a total weight of the material and cobalt which is less than 57% of the total weight of the material.
249. The material as in above item no. 248, wherein the at least one silicide is Ti5Si3 which is between about 24% and about 94% of the total weight of the material.
250. The material as in above item no. 248, wherein the at least one silicide is Zr6Si3 which is between about 28% and about 95% of the total weight of the material.

251. The material as in'above item no_ 248, wherein the at least one silicide is NbSi2 which is between about 31% and about 96% of the total weight of the material.
252. The material as in above item no. 248, wherein the at least one silicide is TaSi2 which is between about 38% and about 97% of the total weight of the material.
253. The material as in above item no. 248, wherein the at least one silicide is MoSi2 which is between about 31% and about 96% of the total weight of the material.
254. The material as in above item no. 248, wherein the at least one silicide is WSi.2 which is between about 40% and about 97% of the total weight of the material.
255. A material, comprising:
hard particles comprising at least one carbide from carbides of IVB, VB and VIB columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium which is less than 74% of a total weight of the material and molybdenum which is less than 57% of the total weight of the material.
256. The material as in above item no. 255, wherein the at least one carbide is TiC which is between about 26% and about 94% of the total weight of the material.
257. The material as in above %tem no. 255, wherein the at least one carbide is ZrC which is between about 32% and about 95% of the total weight of the material.
258. The material as in above item no. 255, wherein the at least one carbide is HfC which is.between about 48% and about 98% of the total weight of the material.
259. The material as in above item no. 255, wherein the at least one carbide is VC which is between about 28% and about 95% of the total weight of the material.
260. The material as in above item no. 255, wherein the at least one carbide is NbC which is between about 36% and about 98% of the total weight of the material.

261. The material as in above item no. 255, wherein the at least one carbide is TaC which is between about 51% and about 98% of the total weight of the material.
262. The material as in above item no. 255, wherein the at least one carbide is Cr2C3 which is between about 32% and about 95% of the total weight of the=material.
263. The material as in above item'no. 255, wherein the at least one carbide is M02C which is between about 40% and about 97% of the total weight of the material.
264. The material as in above item no. 255, wherein the at least one carbide is WC which is between about 53% and about 98% of the total weight of the material.
265. A material, comprising:
hard particles comprising at least one carbide from .15 carbides of IVB, VB and VIB columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium which is less than 74% of a total weight of the material and nickel which is less than 54% of the total weight of the material.
266. The material as in above item no. 265, wherein the at least one carbide is TiC which is between about 26% and about 95% of the total weight of the material.
267. The material as in above item no. 265, wherein the at least one carbide is ZrC which is between about 32% and about 96% of the total weight of the material.
268. The material as in above item no. 265, wherein the at least one carbide is HfC which is between about 48% and about 98% of the total weight of the material.
269. The material as in above item no. 265, wherein the at least one carbide is VC which is between about 28% and about 95% of the total weight of the material.
270. The material as in above item no. 265, wherein the at least one carbide is NbC which is between about 36% and about 97% of the total weight of the material.

271. The material as in above item no. 265, wherein the at least one carbide is TaC which is between about 51% and about 98% of the total weight of the material.
272. The material as in above item no. 265, wherein the at least one carbide is Cr2C3 which is between about 32% and about 96% of the total weight of the material.
273. The material as in above item no. 265, wherein the at least one carbide is Mo2C which is between about 40% and about 97% of the total weight of the material.
274. The material as in above item no. 265, wherein the at least one carbide is WC which is between about 53% and about 98% of the total weight of the material.
275. A material, comprising:
hard particles comprising at least one carbide from carbides of IVB, VB and VIB columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium which is less than 74% of a total weight of the material and chromium which is less than 48% of the total weight of the material.
276. The material as in above item no. 275, wherein the at least one carbide is TiC which is between about 26% and about 96% of the total weight of the material.
277. The material as in above item no. 275, wherein the at least one carbide is ZrC which is between about 32% and about 97% of the total weight of the material.
278. The material as in above item no. 275, wherein the at least one carbide is HfC which is between about 48% and about 98% of the total weight of the material.
279. The material as in above item no. 275, wherein the at least one carbide is VC which is between about 28% and about 95% of the total weight of the material.
= 280. The material as in above item no. 275, wherein the at least one carbide is NbC which is between about 36% and about 97% of the total weight of the material.

--=7 8_.

281. The material as in above item no. 275, wherein the at least one carbide is TaC which is between about 51% and about 98% of the total weight of the material.
282. The material as in above item no. 275, wherein the at least one carbide is Cr2C3 which is between about 32% and about 97% of the total weight of the material.
283. The material as in above item no. 275, wherein the at least one carbide is M02C which is between about 40% and about 98% of the total weight of the material.
284. The material as in above item no. 275, wherein the at least one carbide is WC which is between about 53% and about 98.6% of the total weight of the material.
285. A method, comprising:
preparing a metal surface for a thermal spray process;
and performing the thermal spray process to deposit a hardmetal over the metal surface, wherein the hard metal comprises:
hard particles comprising at least a material made of a carbide, nitride, boride, or silicide; and a binder matrix to bind the hard particles and comprising at least rhenium.
286. A method, comprising:
preparing a metal surface for a thermal spray process;
- and performing the thermal spray process to deposit a hardmetal over the metal surface, wherein the hard metal comprises:
hard particles comprising at least a material made of a carbide, nitride, boride, or silicide; and a binder matrix to bind the hard particles and comprising at least a Ni-based superalloy.

287. A method, comprising:
preparing a metal surface for a thermal spray process;
and performing the thermal spray process to deposit a hardmetal over the metal surface, wherein the hard metal comprises:
hard particles comprising at least a material made of a carbide, nitride, boride, or silicide; and a binder matrix to bind the hard particles and comprising at least tungsten.
[0019] These and other features, implementations, and advantages are now described in details with respect to the drawings, the detailed description, and the claims.

Drawing Description [0020] FIG. 1 shows one exemplary fabrication flow in making a hardmetal according to one implementation.
[0021] FIG. 2 shows an exemplary two-step sintering process for processing hardmetals in a solid state.
[0022] FIGS. 3, 4, 5, 6, 7, and 8show various measured properties of selected exemplary hardmetals.
[0023] FIGS. 9 and 10 illustrate examples of the thermal spray methods.
[0024] FIG. 11 shows one example of a friction stir welding tool system with a friction stir welding head that uses a material described in this application.

Detailed Description [0025] Friction stir welding is a solid-state welding process to join metal components without melting and to avoid various adverse effects associated with traditional welding techniques that melt the metal pieces. Notably, the friction stir welding can be used to produce large welds in a variety of geometric configurations, where a rotating cylindrical tool head is plunged into a rigidly clamped workpiece, and then traversed along the joint between two metal piences to be welded. The tool is specially designed to provide a combination of frictional heat and thermo-mechanical working to the workpiece material as the tool traverses along the joint. A strong, solid-state bond is formed in the wake of the tool.
[0026] FIG. 11 illustrates one example of a FSW system_ A FSW
head 102 is engaged to a shank 108 which is in turn fixed to a rotor can include a pin and a shoulder to which the pin is engaged. A chuck may be used to hold the shank so that the rotor rotates the shank 108 which spins the head 102 during welding. In operation, the spinning head is pressed to the 20- interface of two metal pieces 1 and 2 to be welded together and is moved along the joint interface. The head 102 includes a shoulder 104 that is engaged to the shank 108 and a pin 106 that is engaged to the shoulder 104. The pin 106 and the shoulder 104 are in direct contact with the two pieces to weld them together. In some implementations, the pin 106 and the shoulder 104 are made of a hardmetal material described in this application. In other implementations, the surfaces of the pin and shoulder may be made of a material described in this application while the inner parts of the pin and shoulder may be made of a different material. Various materials described here exhibit high hardness and toughness under a high temoperature experienced by the pin and shoulder during the friction stir welding and thus can be used for constructing the head.

[0027] Examples of the FSW head designs are also described in U.S. Patent No. 6, 648,206 entitled "Frication stir welding using a superabrasive tool" and U.S. Patent Publication No.
US2004/0238599(Al) entitled "Apparatus and method for friction stir welding of high strength materials and articles made thereform." The above two U.S. patent documents are incorporated by reference as part of the specification of this application.
[0028] In some implementations, the whole FSW tool or pin and shoulder of the FSW tool may be made from a material such as a cermet described in this application. For example, a cermet may a metal bound ceramic particles from at least one ccerameic material. Examples of the ceramics include Carbides, Nitrides, Borides, and Silicides. Carbide may include at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr3C2, MOC, MoaC, WC, W2C. The nitride may include at least one of TiN, ZrN, HfN, VN, NbN. The boride may include at least one of TiB2, ZrB2, HfB2, VB2, NbB2, TaB2, Cr3C2, CrB2, Mo2C, MoB, MoB2, W2C, WB. The silicide may include at least one of Ti5Si3, Zr6Si5, Zr3Si2, Zr4Si3, ZrSi, HfSi2, NbSia, TaSi2, Mo3Si2, MoSi2, W3Si2, WSiz . At least one or more metal binder matesrials may be used to bind the pargicles, e.g., Re, a Ni based superalloy, Re-Ni based superalloy, Re-Co, Re-Ni, Re-Fe, Re-Cr, Re-Mo,, Ni based superalloy-Fe, Ni based superalloy-Ni, Ni based superalloy-Co, Ni based superalloy-Cr, Ni based superalloy-Mo, Ni based superalloy-Ni based superalloy, Re-Ni based superalloy-Ni, Re-Ni based superalloy-Co, Re-Ni based superalloy-Fe, Re-Ni based superalloy-Cr, and Re-Ni based superalloy-Mo.
[0029] More examples of the materials for the shoulder and the pin are described below.
[0030] Compositions of hardmetals are important in that they directly affect the technical performance of the hardmetals in their intended applications, and processing conditions and equipment used during fabrication of such hardmetals. The hardmetal compositions also can directly affect the cost of the raw materials for the hardmetals, and the costs associated with the fabrication processes. For these and other reasons, extensive efforts have been made in the hardmetal industry to develop technically superior and economically feasible compositions for hardmetals. This application describes, among other features, material compositions for hardmetals with selected binder matrix materials that, together, provide performance advantages.
[0031] Material compositions for hardmetals of interest include various hard particles and various binder matrix materials. In general, the hard particles may be formed from carbides of the metals in columns IVB (e.g., TiC, ZrC, HfC), = 15 VB (e. g. , VC, NbC, TaC), and VIB (e. g. , Cr3C2, M02C, WC) in the Periodic Table of Elements. In addition, nitrides formed by metals elements in columns IVB (e.g., TiN, ZrN, HfN) and VB
(e.g., VN, NbN, and TaN) in the Periodic Table of Elements may also be used. For example, one material composition for hard .20 particles that is widely used for many hardmetals is a tungsten carbide, e.g., the mono tungsten carbide (WC).
Various nitrides may be mixed with carbides to form the hard particles. Two or more of the above and other carbides and nitrides may be combined to form WC-based hardmetals or WC-25 free hardmetals. Examples of mixtures of different carbides include but are not limited to a mixture of WC and TiC, and a mixture of WC, TiC, and TaC. In addition to various carbides, nitrides, carbonitrides, borides, and silicides may also be used as hard particles for hardmetals. Examples of various 30 suitable hard particles are described in this application.
[00321 The material composition of the binder matrix, in addition to providing a matrix for bonding the hard particles together, can significantly affect the hard and refractory properties of the resulting hardmetals. In general, the binder matrix may include one or more transition metals in the eighth column of the Periodic Table.of Elements, such as cobalt (Co), nickel (Ni), and iron (Fe), and the metals in the 6B column such as molybdenum (Mo) and chromium (Cr). Two or more of such and other binder metals may be mixed together to form desired binder matrices for bonding suitable hard particles. Some binder matrices, for example, use combinations of Co, Ni, and Mo with different relative weights.
[0033] The hardmetal compositions described here were developed in part based on a recognition that the material composition of the binder matrix may be specially configured and tailored to provide high-performance hardmetals to meet specific needs of various applications. In particular, the material composition of the binder matrix has significant effects on other material properties of the resulting hardmetals, such as the elasticity, the rigidity, and the strength parameters (including the transverse rupture strength, the tensile strength, and the impact strength).
Hence, the inventor recognized that it was desirable to provide the proper material composition for the binder matrix to better match the material composition of the hard particles and other components of the hardmetals in order to enhance the material properties and the performance of the resulting hardmetals.
[0034] More specifically, these hardznetal compositions use binder matrices that include rhenium, a nickel-based superalloy or a combination of at least one nickel-based superalloy and other binder materials. Other suitable binder materials may include, among others, rhenium (Re) or cobalt.
A Ni-based superalloy exhibits a high material strength at a relatively high temperature. The resulting hardmetal formed with such a binder material can benefit from the high material strength at high temperatures of rhenium and Ni-superalloy and exhibit enhanced performance at high temperatures. In addition, a Ni-based superalloy also exhibits superior resistance to corrosion and oxidation, and thus, when used as a binder material, can improve the corresponding resistance of the hardmetals.
C00357 The compositions of the hardmetals described in this application may include the binder matrix material from about 3% to about 40% by volume of the total materials in the hardmetals so that the corresponding volume percentage of the hard particles is about from 97% to about 60%, respectively.
Within the above volume percentage range, the binder matrix material in certain implementations may be from about 4% to about 35% by volume out of the volume of the total hardmetal materials. More preferably, some compositions of the hardmetals may have from about 5% to about 30% of the binder matrix material by volume out of the volume of the total hardmetal materials. The weight percentage of the binder matrix material in the total weight of the resulting hardmetals may be derived from the specific compositions of the hardmetals.
C00361 In various implementations, the binder matrices may be formed primarily by a nickel-based superalloy, and by various combinations of the nickel-based superalloy with other elements such as Re, Co, Ni, Fe, Mo, and Cr. A Ni-based superalloy of interest may comprise, in addition to Ni, elements Co, Cr, Al, Ti, Mo, W, and other elements such as Ta, Nb, B, Zr and C. For example, Ni-based superalloys may include the following constituent metals in weight percentage of the total weight of the superalloy: Ni from about 30% to about 70%, Cr from about 10% to about 30%, Co from about 0% to about 25%, a total of Al and Ti from about 4% to about 12%, Mo from about 0% to about 10%, W from about 0% to about 10%, Ta from about 0% to about 10%, Nb from about 0% to about 5%, and Hf from about 0% to about 5%. Ni-based superalloys may also include either or both of Re and Hf, e.g., Re from 0% to about 10%, and Hf from 0% to about 5%. Ni-based superalloy with Re may be used in applications under high temperatures. A Ni-based super alloy may further include other elements, such as B, Zr, and C, in small amounts.
[0037] Compounds TaC and NbC have similar properties to a certain extent and may be used to partially or completely substitute or replace each other in hardmetal compositions in some implementations. Either one or both of HfC and NbC also may be used to substitute or replace a part or all of TaC in hardmetal designs. Compounds WC, TiC, TaC may be produced individually and then mixed to form a mixture or may be produced in a form of a solid solution. When a mixture is used, the mixture may be selected from at least one from a group consisting of (1) a mixture of WC, TiC, and TaC, (2) a mixture of WC, TiC, and NbC, (3) a mixture of WC, TiC, and at least one of TaC and NbC, and (4) a mixture of WC, TiC, and at least one of HfC and NbC. A solid solution of multiple carbides may exhibit better properties and performances than a mixture of several carbides. Hence, hard particles may be selected from at least one from a group consisting of (1) a solid solution of WC, TiC, and TaC, (2) a solid solution of WC, TiC, and NbC, (3) a solid solution of WC, TiC, and at least one of TaC and NbC, and (4) a solid solution of WC, TiC, and at least one of HfC and NbC.
[0038] The nickel-based superalloy as a binder material may be in a y-y' phase where the y' phase with a FCC structure mixes with the y phase. The strength increases with temperature within a certain extent. Another desirable property of such a Ni-based superalloy is its high resistance to oxidation and corrosion. The nickel-based superalloy may be used to either partially or entirely replace Co in various Co-based binder compositions. As demonstrated by examples disclosed in this application, the inclusion of both of rhenium and a nickel-based superalloy in a binder matrix of a hardmetal can significantly improve the performance of the resulting hardmetal by benefiting from the superior performance at high temperatures from presence of Re while utilizing the relatively low-sintering temperature of the Ni-based superalloy to maintain a reasonably low sintering temperature for ease of fabrication. In addition, the relatively low content of Re in such binder compositions allows for reduced cost of the binder materials so that such materials be economically feasible.
[0039] Such a nickel-based superalloy may have a percentage weight from several percent to 100% with respect to the total weight of all material components in the binder matrix based on the specific composition of the binder matrix. A typical nickel-based superalloy may primarily comprise nickel and other metal components in a y-y' phase strengthened state so that it exhibits an enhanced strength which increases as temperature rises.
[0040] Various nickel-based superalloys may have a melting point lower than the common binder material cobalt, such as alloys under the trade names Rene-95, Udimet-700, Udimet-720 from Special Metals which comprise primarily Ni in combination with Co, Cr, Al, Ti, Mo, Nb, W, B', and Zr. Hence, using such a nickel-based superalloy alone as a binder material may not increase the melting point of the resulting hardmetals in comparison with hardmetals using binders with Co.
[0041] However, in one implementation, the nickel-based superalloy can be used in the binder to provide a high material strength and to improve the material hardness of the =30 resulting hardmetals, at high temperatures near or above 500 C. Tests of some fabricated samples have demonstrated that the material hardness and strength for hardmetals with a Ni-based superalloy in the binder can improve significantly, e.g., by at least 10%, at low operating temperatures in comparison with similar material compositions without Ni-based superalloy in the binder. The following table show measured hardness parameters of samples P65 and P46A with Ni-based superalloy in the binder in comparison with samples P49 and P47A with pure Co as the binder, where the compositions of the samples are listed in Table 4.

Effects of Ni-based Superalloy (NS) in Binder Samp1e Co or NS Binder Iiv at Room Ksc at room Comparisoxx Code Temperature temperature Name (Kff1xs¾ne) (x106 Pa=m.liz) P49 Co: 10 volume% 2186 6.5 P65 NS: 10 volume% 2532 6.7 Hv is about 16%
greater than that of P49 P47A Co: 15 volume% 2160 6.4 P46A NS: 15 volume% 2364 6.4 Hv is about 10%
greater than that of P47A

[0042] Notably, at high operating temperatures above 500 C, hardmetal samples with Ni-based superalloy in the binder can exhibit a material hardness that is significantly higher than that of similar hardmetal samples without having a Ni-based superalloy in the binder. In addition, Ni-based superalloy as a binder material can also improve the resistance to corrosion of the resulting hardmetals or cermets in comparison with hardmetals or cermets using the conventional cobalt as the binder.
[0043] A nickel-based superalloy may be used alone or in combination with other elements to form a desired binder matrix. Other elements that may be combined with the nickel-based superalloy to form a binder matrix include but are not limited to, another nickel-based superalloy, other non-nickel-based alloys, Re, Co, Ni, Fe, Mo, and Cr.

[0044] Rhenium as a binder material may be used to provide strong bonding of hard particles and in particular can produce a high melting point for the resulting hardmetal material.
The melting point of rhenium is about 31800 C, much higher than the melting point of 1495 C of the commonly-used cobalt as a binder material. This feature of rhenium partially-contributes to the enhanced performance of hardmetals with binders using Re, e.g., the enhanced hardness and strength of the resulting hardmetals at high temperatures. Re also has other desired properties as a binder'material. For example, the hardness, the transverse rapture strength, the fracture toughness, and the melting point of the hardmetals with Re in their binder matrices can be increased significantly in comparison with similar hardmetals without Re in the binder matrices. A hardness Hv over 2600 Kg/mm2 has been achieved in exemplary WC-based hardmetals with Re in the binder matrices.
The melting point of some exemplary WC-based hardmetals, i.e., the sintering temperature, has shown to be greater than 2200 C. In comparison, the sintering temperature for WC-based hardmetals with Co in the binders in Table 2.1 in the cited Brookes is below 15000 C. A hardmetal with a high sintering temperature allows the material to operate at a high temperature below the sintering temperature. For example, tools based on such Re-containing hardmetal materials may operate at high speeds to reduce the processing time and the overall throughput of the processing.
[0045] The use of Re as a binder material in hardmetals, however, may present limitations in practice. For example, the desirable high-temperature property of Re generally leads to a high sintering temperature for fabrication. Thus, the oven or furnace for the conventional sintering process needs to operate at or above the high sintering temperature. Ovens or furnaces capable of operating at such high temperatures, e.g., above 2200 C, can be expensive and may not be widely available for commercial use. U. S. Patent No. 5,476,531 discloses a use of a rapid omnidirectional compaction (ROC) method to reduce the processing temperature in manufacturing WC-based hardmetals with pure Re as the binder material from 6% to 18% of the total weight of each hardmetal. This ROC
process, however, is still expensive and is generally not suitable for commercial fabrication.
[0046] One potential advantage of the hardmetal compositions and the composition methods described here is that they may provide or allow for a more practical fabrication process for fabricating hardmetals with either Re or mixtures of Re with other binder materials in the binder matrices. In particular, this two-step process makes it possible to fabricate hardmetals where Re is at or more than 25% of the total weight of the binder matrix of the resulting hardmetal. Such hardmetals with Re at or more than 25% may be used to achieve a high hardness and a high material strength at high temperatures.
[0047] Another limitation of using pure Re as a binder material for hardmetals is that Re oxidizes severely in air at or above about 3504C. This poor oxidation resistance may dramatically reduce the use of pure Re as binder for any application above about 300¾C. Since Ni-based superalloy has exceptionally strength and oxidation resistance under 10002C, a mixture of a Ni-based superalloy and Re where Re is the dominant material in the binder may be used to improve the strength and oxidation resistance of the resulting hardmetal using such a mixture as the binder. On the other hand, the addition of Re into a binder primarily comprised of a Ni-based superalloy can increase the melting range of the resulting hardmetal, and improve the high temperature strength and creep resistance of the Ni-based superalloy binder.

~91~

[0048] In general, the percentage weight of the rhenium in the binder matrix should be between a several percent to essentially 100% of the total weight of the binder matrix in a hardmetal. Preferably, the percentage weight of rhenium in the binder matrix should be at or above 5%. In particular, the percentage weight of rhenium in=the binder matrix may be at or above 10% of the binder matrix. In some implementations, the percentage weight of rhenium in the binder matrix may be at or above 25% of the total weight of the binder matrix of the resulting hardmetal. Hardmetals with such a high concentration of Re may be fabricated at relatively low temperatures with a two-step process described in this application.
[0049] Since rhenium is generally more expensive than other materials used in hardmetals, cost should be considered in designing binder matrices that include rhenium. Some of the examples given below reflect this consideration. In general, according to one implementation, a hardmetal composition includes dispersed hard particles having a first material, and a binder matrix having a second, different material that includes rhenium, where the hard particles are spatially dispersed in the binder matrix in a substantially uniform manner. The binder matrix may be a mixture of Re and other binder materials to reduce the total content of Re to in part reduce the overall cost of the raw materials and in part to explore the presence of other binder materials to enhance the performance of the binder matrix. Examples of binder matrices having mixtures of Re and other binder materials include, mixtures of Re and at least one Ni-based superalloy, mixtures of Re, Co and at least one Ni-based superalloy, mixtures of Re and Co, and others.

[0050] TABLE 1 lists some examples of hardmetal compositions of interest. In this table, WC-based compositions are referred to as "hardmetals" and the TiC-based compositions are referred to as "cermets." Traditionally, TiC particles bound by a mixture of Ni and Mo or a mixture of Ni and Mo2C are cermets. Cermets as described here further include hard particles formed by mixtures of TiC and TiN, of TiC, TiN, WC, TaC, and NbC with the binder matrices formed by the mixture of Ni and Mo or the mixture of Ni and Mo2C. For each hardmetal composition, three different weight percentage ranges for the given binder material in the are listed. As an example, the binder may be a mixture of a Ni-based superalloy and cobalt, and the hard particles may a mixture of WC, TiC, TaC, and NbC.
In this composition, the binder may be from about 2% to about =15 40% of the total weight of the hardmetal. This range may be set to from about 3% to about 35% in some applications and may be further limited to a smaller range from about 4% to about 30% in other applications.

(NS: Ni-based superalloy) Binder Composition for i8 Binder 2 Binder 3" Binder Consposition Hard Particles Wt.96 Range Wt.% Range Wt.96 Range Wc 4 to 40 5 to 35 6 to 30 Re WC-TiC-TaC-NbC 4 to 40 5 to 35 6 to 30 WC 2 to 30 3 to 25 4 to 20 NS
WC-TiC-TaC-NbC 2 to 30 3 to 25 4 to 20 wc 2 to 40 3 to 35 4 to 30 Hardmetals NS-Re WC-TiC-TaC-NbC 2 to 40 3 to 35 4 to 30 WC 2 to 40 3 to 35 4 to 30 Re-Co WC-TiC-TaC-N'bC 2 to 40 3 to 35 4 to 30 WC 2 to 40 3 to 35 4 to 30 NS-Re-Co WC-TiC-TaC-NbC 2 to 40 3 to 35 4 to 30 M02C-TiC 5 to 40 6 to 35 8 to 40 NS M02C-TiC-TiN-WC-to 40 6 to 35 8 to 40 TaC-NbC
M02C-T1C 10 to 55 12 to 50 15 to 45 Cermets Re MozC-TiC-TiN-WC-to 55 12 to 50 15 to 45 TaC-NbC
MozC-TiC 5 to 55 6 to 50 8 to 45 NS-Re Mo2C-TiC-TiN-WC-5 to 55 6 to 50 8 to 45 TaC-NbC

[0051] Fabrication of- hardmetals with Re or a nickel-based 5 superalloy in binder matrices may be carried out as follows.
First, a powder with desired hard particles such as one or more carbides or carbonitrides is prepared. This powder may include a mixture of different carbides or a mixture of carbides and nitrides. The powder is mixed with a suitable 10 binder matrix material that includes Re or a nickel-based superalloy. In addition, a pressing lubricant, e.g., a wax, may be added to the mixture.
[0052] The mixture of the hard particles, the binder matrix material, and the lubricant is mixed through a milling or attriting process by milling or attriting over a desired period, e.g., hours, to fully mix the materials so that each hard particle is coated with the binder matrix material to facilitate the binding of the hard particles in the subsequent processes. The hard particles should also be coated with the lubricant material to lubricate the materials to facilitate the mixing process and to reduce or eliminate oxidation of the hard particles. Next, pressing, pre-sintering, shaping, and final sintering are subsequently performed to the milled mixture to form the resulting hardmetal. The sintering process is a process for converting a powder material into a continuous mass by heating to a temperature that is below the melting temperature of the hard particles and may be performed after preliminary compacting by pressure. During this process, the binder material is densified to form a continuous binder matrix to bind hard particles=therein. One or more additional coatings may be further formed on a surface of the resulting hardmetal to enhance the performance of the hardmetal. FIG. 1 is a flowchart for this implementation of the fabrication process.
[0053] In one implementation, the manufacture process for cemented carbides includes wet milling in solvent, vacuum drying, pressing, and liquid-phase sintering in vacuum. The temperature of the liquid-phase sintering is between melting point of the binder material (e.g., Co at 1495 C) and the eutectic temperature of the mixture of hardmetal (e.g., WC-Co at 1320 C). in general, the sintering temperature of cemented carbide is in a range of 1360 to 1480 C. For new materials with low concentration of Re or a Ni-based superalloy in binder alloy, manufacture process is same as conventional cemented carbide process. The principle of liquid phase sintering in vacuum is applied in here. The sintering temperature is slightly higher than the eutectic temperature 30, of binder alloy and carbide. For example, the sintering condition of P17 ( 25% of Re in binder alloy, by weight ) is at 1700 C for one hour in vacuum.

[0054] FIG. 2 shows a two-step fabrication process based on a solid-state phase sintering for fabricating various hardmetals described in this application. Examples of hardmetals that can be fabricated with this two-step sintering method include hardmetals with a high concentration of Re in the binder matrix that would otherwise require the liquid-phase sintering at high temperatures. This two-step process may be implemented at relatively low temperatures, e.g., under 22000 C, to utilize commercially feasible ovens and to produce the hardmetals at reasonably low costs. The liquid phase sintering is eliminated in this two-step process because the liquid phase sintering may not be practical due to the generally high eutectic temperatures of the binder alloy and carbide. As discussed above, sintering at such high temperatures requires ovens operating at high temperatures which may not be commercially feasible.
[0055] The first step of this two-step process is a vacuum sintering where the mixture materials for the binder matrix and the hard particles are sintered in vacuum. The mixture is initially processed by, e.g., wet milling, drying, and pressing, as performed in conventional processes for fabricating cemented carbides. This first step of sintering is performed at a temperature below the eutectic temperature of the binder alloy and the hard particle materials to remove or eliminate the interconnected porosity. The second step is a solid phase sintering at a temperature below the eutectic temperature and under a pressured condition to remove and eliminate the remaining porosities and voids left in the sintered mixture after the first step. A hot isostatic pressing (HIP) process may be used as this second step sintering. Both heat and pressure are applied.to the material during the sintering to reduce the processing temperature which would otherwise be higher in absence of the pressure. A
gas medium such as an inert gas may be used to apply and transmit the pressure to the sintered mixture. The pressure may be at or over 1000 bar. Application of pressure in the HIP process lowers the required processing temperature and allows for use of conventional ovens or furnaces. The temperatures of solid phase sintering and HIPping for achieving fully condensed materials are generally significantly lower than the temperatures for liquid phase sintering. For example, the sample P62 which uses pure Re as the binder may be fully densified by vacuum sintering at 2200 C for one to two hours and then HIPping at about 2000 C
under a pressure of 30,000 PSI in the inert gas such as Ar for about one hour. Notably, the use of ultra fine hard particles with a particulate dimension less than 0.5 micron can reduce the sintering temperature for fully densifying the hardmetals (fine particles are several microns in size). For example, in making the samples P62 and P63, the use of such ultra fine WC
allows for sintering temperatures to be low, e.g., around 2000 C. This two-step process is less expensive than the ROC
method and may be used to commercial production.
.20 [0056] The following sections describe exemplary hardmetal compositions and their properties based on various binder matrix materials that include at least rhenium or a nickel-based superalloy.
[0057] TABLE 2 provides a list of code names (lot numbers) for some of the constituent materials used to form the exemplary hardmetals, where H1 represents rhenium, and L1, L2, and L3 represent three exemplary commercial nickel-based superalloys.
TABLE 3 further lists compositions of the above three exemplary nickel-based superalloys, Udimet720(U720), Rene'95(R-95), and Udimet700(U700), respectively. TABLE 4 lists compositions of exemplary hardmetals, both with and without rhenium or a nickel-based superalloy in the binder matrices. For example, the material composition for Lot P17 primarily includes 88 grams of T32 (WC), 3 grams of 132 (TiC), 3 grams of A31 (TaC), 1.5 grams of H1 (Re) and 4.5 grams of L2 (R-95) as binder, and 2 grams of a wax as lubricant. Lot P58 represents a hardmetal with a nickel-based superalloy L2 as the only binder material without Re. These hardmetals were fabricated and tested to illustrate the effects of either or both of rhenium and a nickel-based superalloy as binder materials on various properties of the resulting hardmetals.
TABLES 5-8 further provide summary information of compositions and properties of different sample lots as defined above.
[00581 FIGS. 3 through 8 show measurements of selected hardmetal samples of this application. FIGS. 3 and 4 show measured toughness and hardness parameters of some exemplary hardmetals for the steel cutting grades. FIGS. 5 and 6 show measured toughness and hardness parameters of some exemplary hardmetals for the non-ferrous cutting grades. Measurements were performed before and after the solid-phase sintering HIP
process and the data suggests that the HIP process significantly improves both the toughness and the hardness of the materials. FIG. 7 shows measurements of the hardness as a function of temperature for some samples. As a comparison, FIGS. 7 and 8 also show measurements of commercial C2 and C6 carbides under the same testing conditions, where FIG. 7 shows the measured hardness and FIG. 8 shows measured change in hardness from the value at the room temperature (RT).
Clearly, the hardmetal samples based on the compositions described here outperform the commercial grade materials in terms of the hardness at high temperatures. These results demonstrate that the superior performance of binder matrices with either or both of Re and a nickel-based superalloy as binder materials in comparison with Co-based binder matrix materials.

Powder Code Note Composition T32 WC Particle size 1.5 }un, from Alldyne T35 WC Particle size 15 m, from Alldyne Y20 Mo Particle size 1.7-2.2 pm, from Alldyne L3 U-700 -325 Mesh, special metal Udimet 700 L1 U-720 -325 Mesh, Special Metal, Udimet 720 L2 Re-95 -325 Mesh, Special Metal, Rene 95 H1 Re -325 Mesh, Rhenium Alloy Inc.
132 TiC from AEE, Ti-302 121 TiB2 from AEE, Ti-201, 1-5 Eun A31 TaC from AEE, TA-301 Y31 M02C from AEE, MO-301 D31 VC from AEE, VA-301 B1 Co from AEE, CO-101 Ki Ni from AEE, Ni-101 K2 Ni from AEE, Ni-102 113 TiN from Cerac, T-1153 C21 ZrB2 from Cerac, Z-1031 Y6 Mo from AEE Mo+100, 1-2 m L6 Al from AEE Al-100, 1-5 Eun R31 BaC from AEE Bo-301, 3 pm T3.8 WC Particle size 0.8 m, Alldyne T3.4 WC Particle size 0.4 m, OMG
T3.2 WC Particle size 0.2 in, OMG

Ni Co Cr Al Ti Mo Nb W Zr B C V
R95 61.982 8.04 13.16 3.54 2.53 3.55 3.55 3.54 0.049 0.059 U700 54.331 17.34 15.35 4.04 3.65 5.17 .028 .008 .04 .019 .019 .005 U720 56.334 15.32 16.38 3.06 5.04 3.06 0.01 1.30 .035 .015 .012 .004 Lot No Composition (units in grams) P17 H1=1.5, L2=4.5, 132=3, A31=3, T32=88, Wax=2 P18 H1=3, L2=3, 132=3, A31=3, T32=88, Wax=2 P19 H1=1.5, L3=4.5, 132=3, A31=3, T32=88, Wax=2 P20 H1=3, L3=3, 132=3, A31=3, T32=88, Wax=2 P25 H1=3.75, L2=2.25, I32=3, A31=3, T32=88, Wax=2 P25A H1=3.75, L2=2.25, 132=3, A31=3, T32=88, Wax=2 P31 31=3.44, 81=4.4, T32=92.16, Wax=2 P32 H1=6.75, 31=2.88, T32=90.37, Wax=2 P33 H1=9.93, B1=1.41, T32=88.66, Wax=2 P34 L2=14_47, 132=69.44, Y31=16.09 P35 31=8.77, L2=10.27, 132=65.73, Y31=15.23 P36 H1=16.66, L2=6.50, I32=62.4, Y31=14.56 P37 111=23.80, L2=3.09, I32=59.38, Y31=13.76 P38 K1=15.51, 132=68.60, Y31=15.89 P39 K2=15.51, I32=68.60, Y31=15.89 P40 H1=7_57, L2=2_96, I32=5.32, A31=5.23, T32=78.92, Wax=2 P40A H1=7.57, L2=2.96, I32=5.32, A31=5.23, T32=78.92, Wax=2 P41 H1=11.1, L2=1.45, I32=5.20, A31=5.11, T32=77.14, Wax=2 P41A H1=11.1, L2=1.45, I32=5.20, A31=5.11, T32=77.14, Wax=2 P42 31=9.32, L2=3.64, 132=6.55, A31=6.44, I21=0.40, R31=4.25, T32=69.40, Wax P43 H1=9.04, L2=3.53, I32=6.35, A31=6.24, I21=7.39, R31=0.22, T32=67.24, Wax P44 H1=8.96, L2=3.50, I32=14.69, A31=6.19, T32=66_67, Wax=2 P45 111=9.37, L2=3.66, 132=15.37, A31=6.47, Y31=6.51, T32=58.61, Wax=2 P46 111=11.40, L2=4_45, I32=5_34, A31=5.25, T32=73_55, Wax=2 P46A H1=11.40, L2=4.45, I32=5.34, A31=5.25, T32=73.55, Wax=2 P47 111=11.35, 31=4.88, 132=5.32, A31=5.23, T32=73.22, Wax=2 P47A H1=11.35, 31=4.88, I32=5.32, A31=5.23, T32=73.22, Wax=2 P48 H1=3.75, L2=2.25, I32=5, A31=5, T32=84, Wax=2 P49 111=7.55, 31=3.25, I32=5.31, A31=5.21, T32=78.68, Wax=2 P50 31=4.83, L2=1.89, I32=5.31, A31=5.22, T32=82.75, Wax=2 P51 H1=7.15, L2=0.93, I32=5.23, A31=5.14, T32=81.55, Wax=2 P52 B1=8, D31=0.6, T3.8=91.4, Wax=2 P53 B1=8, D31=0.6, T3.4=91.4, Wax=2 P54 B1=8, D31=0.6, T3.2=91.4, Wax=2 P55 H1=1.8, B1=7.2, D31=0.6, T3.4=90.4, Wax=2 P56 H1=1.8, B1=7.2, D31=0.6, T3.2=90.4, Wax=2 P56A H1=1.8, B1=7.2, D31=0.6, T3.2=90.4, Wax=2 P57 H1=1.8, B1=7.2, T3.2=91, Wax=2 .__.
6, T3.2=91_9, Wax=2 L2=4.5, D31=0.6, T3.2=91_5, Wax=25.09, A31=5.00, T3.2=75.43, Wax=2 5.09, A31=5.00, T3.2=75.43, Wax=2 P63 H1=12_47, L2=0.86, I32=5.16, A31=5.07, T3.2=76.45, Wax=2 P65 H1=7.57, L2=2_96, I32=5.32, A31=5.23, T3.2=78.92, Wax=2 P65A H1=7.57, L2=2.96, I32=5.32, A31=5.23, T3.2=78.92, Wax=2 P66 H1=27_92, I32=4.91, A31=4.82, T3.2=62.35, Wax=2 P67 H1=24.37, L3=1.62, I32=5.04, A31=4.95, T32=32.01, T33=32.01, Wax=2 P69 L2=7.5, D31=0.4, T3.2=92.1, Wax=2 P70 L1=7.4, D31=0.3, T3.2=92.3, Wax=2 P71 L3=7.2, D31=0.3, T3.2=92.5, Wax=2 P72 H1=1.8, B1=7.2, D31=0.3, T3.2=90.7, Wax=2 P73 H1=1.8, B1=4.8, L2=2.7, D31=0.3, T3.2=90.4, Wax=2 P74 H1=1.8, B1=3, L2=4.5, D31=0.3, T3.2=90.4, Wax=2 P75 H1=0.8, B1=3, L2=4.5, D31=0.3, T3.2=91.4, Wax=2 P76 H1=0.8, B1=3, L1=4.5, D31=0.3, T3.2=91.4, Wax=2 P77 H1=0.8, B1=3, L3=4.5, D31=0.3, T3.2=91.4, Wax=2 P78 H1=0.8, 131=4.5, L1=3, D31=0.3, T3.2=91.4, Wax=2 P79 H1=0.8, B1=4.5, L3=3.1, D31=0.3, T3.2=91.3, Wax=2 [0059] Several exemplary categories of hardmetal compositions are described below to illustrate the above general designs of the various hardmetal compositions to include either of Re and Nickel-based superalloy, or both. The exemplary categories of hardmetal compositions are defined based on the compositions of the binder matrices for the resulting hardmetals or cermets. The first category uses a binder matrix having pure Re, the second category uses a binder matrix having a Re-Co alloy, the third category uses a binder matrix having a Ni-based superalloy, and the fourth category uses a binder matrix having an alloy having a Ni-based superalloy in combination with of Re with or without Co.
[00601 In general, hard and refractory particles used in hardmetals of interest may include, but are not limited to, carbides, nitrides, carbonitrides, borides, and silicides.
Some examples of Carbides include WC, TiC, TaC, HfC, NbC, Mo2C, Cr2C3, VC, ZrC, B4C1 and SiC. Examples of Nitrides include TiN, ZrN, HfN, VN, NbN, TaN, and BN. Examples of Carbonitrides include Ti(C,N), Ta(C,N), Nb(C,N), Hf(C,N), Zr(C,N), and V(C,N). Examples of Borides include TiB2, ZrB2, HfB2, TaB2, VB2, MoB2, WB, and W2B. In addition, examples of Silicides are TaSi2, WsiZ, NbSi2, and MoSi.2. The above-identified four categories of hardmetals or cermets can also use these and other hard and refractory particles.
[0061] In the first category of hardmetals based on the pure Re alloy binder matrix, the Re may be approximately'from 5% to 40% by volume of all material compositions used in a hardmetal or cermet. For example, the sample'with a lot No. P62 in TABLE 4 has 10% of pure Re, 70%of WC, 15% of TiC, and 5% of TaC by volume. This composition approximately corresponds to 1o. 14.48% of Re, 75.43% of WC, 5.09% of TiC and 5.0% of TaC by weight. In fabrication, the Specimen P62-4 was vacuum sintered at 2100 C for about one hour and 2158 C for about one hour.
The density of this material is about 14.51g/cc, where the calculated density is 14.50 g/cc. The average hardness Hv is 2627 35 Kg/mm2for 10 measurements taken at the room temperature under a load of 10 Kg. The measured surface fracture toughness KS is about 7.4 x106 Pa = ml/2 estimated by Palmvist crack length at a load of 10 Kg.
[0062] Another example under this category is P66 in TABLE 4.
This sample has about 20% of Re, 60% of WC, 15% of TiC, and 5%
of TaC by volume in composition. In the weight percentage, this sample has about 27.92% of Re, 62.35% of WC, 4.91% of TiC, and 4.82% of TaC. The Specimen P66-4 was first processed with a vacuum sintering process at about 2200 C for one hour and was then sintered in the solid-phase with a HIP process to remove porosities and voids. The density of the resulting hardmetal is about 14.40g/cc compared to the calculated density of 15.04g/cc. The average hardness Hv is about 2402 44 Kg/mm2 for 7 different measurements taken at the room temperature under a load of 10 Kg. The surface fracture toughness KS, is about 8.1 x106 Pa=m1/2. The sample P66 and other compositions described here with a high concentration of Re with a weight percentage greater than 25%, as the sole binder material or one of two or more different binder materials in the binder, may be used for various applications at high operating temperatures and may be manufactured by using the two-step process based on solid-phase sintering.
[0063] The microstructures and properties of Re bound multiples types of hard refractory particles, such as carbides, nitrides, carbon nitrides, silicides, and borides, may provide advantages over Re-bound WC material. For example, Re bound WC-TiC-TaC may have better crater resistance in steel cutting than Re bound WC material. Another example is materials formed by refractory particles of M02C and TiC
bound in a Re binder.
[0064] For the second category with a Re-Co alloy as the binder matrix, the Re-Co alloy may be about from 5 to 40 Vol%
of all material compositions used in the composition. In some implementations, the Re-to-Co ratio in the binder may vary from 0.01 to 0.99 approximately. Inclusion of Re can improve the mechanical properties of the resulting hardmetals, such as hardness, strength and toughness special at high temperature compared to Co bounded hardmetal. The higher Re content is the better high temperature properties are for most materials using such a binder matrix.
[0065] The sample P31 in TABLE 4 is one example within this category with 2.5% of Re, 7.5% of Co, and 90% of WC by volume, and 3.44% of Re, 4.40% of Co and 92.12% of WC by weight. In fabrication, the Specimen P31-1 was vacuum sintered at 1725C
for about one hour. slight under sintering with some porosities and voids. The density of the resulting hardmetal is about 15.16 g/cc (calculated density at 15.27 g/cc). The average hardness Hv is about 1889 18 Kg/mm2 at the room temperature under 10 Kg and the surface facture toughness Ks, is about 7.7 x106 Pa=m1/2. In addition, the Specimen P31-1 was treated with a hot isostatic press (HIP) process at about 1600C / 15Ksi for about one hour after sintering. The HIP
reduces or substantially eliminates the porosities and voids in the compound to increase the material density. After HIP, the measured density is about 15.25g/cc (calculated density at 15.27 g/cc). The measured hardness Hv is about 1887 12 Kg/mm2 at the room temperature under 10 Kg. The surface fracture toughness KS,: is about 7.6 x106 Pa =m112 .
[0066] Another example in this category is P32 in TABLE 4 with 5.0% of Re, 5.0% of Co, and 90% of WC in volume (6.75% of Re, 2.88% of Co and 90.38% of WC in weight). The Specimen P32-4 was vacuum sintered at 1800C for about one hour. The measured density is about 15.58 g/cc in comparison with the calculated density at 15.57 g/cc. The measured hardness Hv is about 2065 Kg/mm2 at the room temperature under 10 Kg. The surface fracture toughness KS, is about 5.9 x106 Pa-m112. The Specimen P32-4 was also HIP at 1600C / 15Ksi for about one hour after Sintering. The measured density is about 15.57g/cc (calculated density at 15.57 g/cc). The average hardness Hv is about 2010f12 Kg/mm2 at the room temperature under 10 Kg.
The surface fracture toughness Ksc is about 5.8 x106 Pa=m1i2.
[0067] The third example is P33 in TABLE 4 which has 7.5% of Re, 2.5% of Co, and 90% of WC by volume and 9.93% of Re, 1.41%
of Co and 88.66% of WC by weight. In fabrication, the Specimen P33-7 was vacuum sintered at 1950C for about one hour and was under sintering with porosities and voids. The measured density is about 15.38 g/cc (calculated density at 15.87 g/cc). The measured hardness Hv is about 2081 Kg/mm2 at the room temperature under a force of 10 Kg. The surface fracture toughness Ksc is about 5.6 x106 Pa=m1/2. The Specimen P33-7 was HIP at 1600C / 15Ksi for about one hour after Sintering. The measured density is about 15.82g/cc (calculated density=15.87 g/cc). The average hardness Hv is measured at about 2039-!-18 Kg/mm2 at the room temperature under 10 Kg. The surface fracture toughness Ksc is about 6.5 x106 Pa=m1ia.

TABLE 5 Re-Co alloy bound hardmetals Temperature Density Hv Ksc Grain C g/cc si.ze Sinter HIP Calculated Measured Kg/mnn x10 Pa-m P55-1 1350 1300 14.77 14.79 2047 8.6 Ultra-fine P56-5 1360 1300 14.77 14.72 2133 8.6 Ultra-fine P56A-4 1350 1300 14.77 14.71 2108 8.5 Ultra-fine P57-1 1350 1300 14.91 14.93 1747 12.3 Fine [0068] The samples P55, P56, P56A, and P57 in TABLE 4 are also examples for the category with a Re-Co alloy as the binder matrix. These samples have about 1.8% of Re, 7.2% of Co, 0.6%
of VC except that P57 has no VC, and finally WC in balance.
These different compositions are made to study the effects of hardmetal grain size on Hv and Ksc.. TABLE 5 lists the results.

TABLE 6 Properties of Ni-based superalloys, Ni, Re, and Co Test Temp. R-95 U-700 T3720 Nickel Rhenium Cobalt C
Density 21 8.2 7.9 8.1 8.9 21 8.9 (g/c.c.) Melting Point ( C) Elastic Modulus 21 30.3 32.4 32.2 207 460 211 (GPa) Ultimate Tensile Strength (Mpa) 0.296 Yield Strength (MPa) Tensile 21 15 17 13 30 >15 Elongation 760 15 20 9 Oxidation Excellent Excellent Excellent Good Poor Good Resistance [0069] The third category is based on binder matrices with Ni-based superalloys from 5 to 40% in volume of all materials in the resulting hardmetal. Ni-based superalloys'are a family of high temperature alloys with y' strengthening. Three different strength alloys, Rene'95, Udimet 720, and Udimet 700 are used as examples to demonstrate the effects of the binder strength on mechanical properties of the final hardm.etals.
The Ni-based superalloys have a high strength specially at elevated temperatures. Also, these alloys have good environmental resistance such as resistance to corrosion and oxidation at elevated temperature.' Therefore, Ni-based superalloys can be used to increase the hardness of Ni-based superalloy bound hardmetals when compared to Cobalt bound hardmetals. Notably, the tensile strengths of the Ni-based superalloys are much stronger than the common binder material cobalt as shown by TABLE 6. This further shows that Ni-based superalloys are good binder materials for hardmetals.
[00701 One example for this category is P58 in TABLE 4 which has 7.5% of Rene'95, 0.6% of VC, and 91.9% of WC in weight and compares to cobalt bound P54 in TABLE 4 (8% of Co, 0.6% of VC, and 91.4% of WC). The hardness of P58 is significant higher than P54 as shown in TABLE 7.

TABLE 7 Comparison of P54 and P58 Ksc Sintering HIP Iiv, Kg/ncrn' x106 Pa =ml/' P54-1 1350C / lhr 2094 8.8 P54-2 1380C / lhr 2071 7.8 P54-3 1420C / lhr 1305 C 2107 8.5 P58-1 1350, 1380, 1400, 1420, 15KSI under Ar 1450, 1475 for 1 hour at 1 hour 2322 7.0 each temperature P58-3 1450C / lhr 2272 7.4 P58-5 1500C / lhr 2259 7.2 P58-7 1550C / lhr 2246 7.3 [00711 The fourth category is Ni-based superalloy plus Re as binder, e.g., approximately from 5% to 40 % by volume of all materials in the resulting hardmetal or cermet. Because addition of Re increases the melting point of binder alloy of Ni-based superalloy plus Re, the processing temperature of hardmetal with Ni-based superalloy plus Re binder increases as the Re content increases. Several hardmetals with different Re concentrations are listed in TABLE 8. TABLE 9 further shows the measured properties of the hardmetals in TABLE 8.

TABLE 8 Hardmetal with a binder comprising Ni-based superalloy and Re Comnpoeition, aseight ~ Sintering Re to Binder Q_ C_ Tenverature Re Rene95 WC TiC TaC Ratio P17 1.5 4.5 88 3 3 25% 1600-1750 P18 3 3.0 88 3 3 50% 1600-1775 P25 3.75 2.25 88 3 3 62.5% 1650-1825 P48 3.75 2.25 84 5 .5 62.5% 1650-1825 P50 4.83 1.89 82.75 5.31 5.22 71.9% 1675-1850 P40 7.57 2.96 78.92 5.32 5.23 71.9% 1675-1850 P46 11.40 4.45 73.55 5.34 5.24 71.9$ 1675-1850 P51 7.15 0.93 81.55 5.23 5.14 88.5% 1700-1900 P41 11.10 1.45 77.14 5.20 5.11 88.5% 1700-1900 P63 12.47 0.86 76.45 5.16 5.07 93.6% 1850-2100 P19 1.5 4.5 88 3 3 25% 1600-1750 P20 3 3 88 3 3 50% 1600-1775 P67 24_37 1.62 64.02 5.04 4.95 93.6$ 1950-2300 TABLE 9 Properties of hardmetals bound by Ni-based superalloy and Re Temperature, C Density, g/cc Hv Ksc Sinter HIP Calculated Measured Kg/mm? x106Pa-ml12 P17 1700 14.15 14.18 2120 6.8 P17 1700 1600 14.15 14.21 2092 7.2 P18 1700 14.38 14.47 2168 5.9 P18 1700 1600 14.38 14.42 2142 6.1 P25 1750 14.49 14.41 2271 6.1 P25 1750 1600 14.49 14.48 2193 6.5 P48 1800 1600 13.91 13.99 2208 6.3 P50 1800 1600 13.9 13.78 2321 6.5 P40 1800 13.86 13.82 2343 P40 1800 1600 13.86 13.86 2321 6.3 P46 1800 13.81 13.88 2282 7.1 P46 1800 1725 13.81 13.82 2326 6.7 P51 1800 1600 14.11 13.97 2309 6.6 P41 1800 1600 14.18 14.63 2321 6.5 P63 2000 14.31 14.37 2557 7.9 P19 1700 14.11 14.11 2059 7.6 P19 1700 1600 14.11 2012 8.0 P20 1725 14.35 14.52 2221 6.4 P20 1725 1600 14.35 14.35 2151 7.0 P67 2200 14.65 14.21 2113 8.1 P67 2200 1725 14.65 14.34 2210 7.1 [0072] Another example under the fourth category uses a Ni-based superalloy plus Re and Co as binder which is also about 5% to 40% by volume. Exemplary compositions of hardmetals bound by Ni-based superalloy plus Re and Co are list in TABLE
10.

TABLE 10 Composition of hardmetals bound by Ni-based superalloy plus Re and Co Composition, weight 9s Re Co Rene95 U-720 U-700 WC VC
P73 1.8 4.8 2.7 90.4 0.3 P74 1.8 3 4.5 90.4 0.3 P75 0.8 3 4_5 91.4 0.3 P76 0.8 3 4.5 91.4 0.3 P77 0.8 3 4.5 91.4 0.3 P78 0.8 4.5 3 91.4 0.3 P79 0.8 4.5 3.1 91.3 0.3 [0073] Measurements on selected samples have been performed to study properties of the binder matrices with Ni-based superalloys. in general, Ni-based superalloys not only exhibit excellent strengths at elevated temperatures but also possess outstanding resistances to oxidation and corrosion at high temperatures. Ni-based superalloys have complex microstructures and strengthening mechanisms. In general, the strengthening of Ni-based superalloys is primarily due to precipitation strengthening of y-y' and solid-solution strengthening. The measurements the selected samples demonstrate that Ni-based superalloys can be used as a high-performance binder materials for hardmetals.

[0074] TABLE 11 lists compositions of selected samples by their weight percentages of the total weight of the hardmetals. The WC particles in the samples are 0.2 pm in size. TABLE 12 lists the conditions for the two-step process performed and measured densities, hardness parameters, and toughness parameters of the samples. The Palmqvist fracture toughness Ksc is calculated from the total crack length of Palmqvist crack which is produced by the Vicker Indentor:
Ksc=0.087*(Hv*W)112. See, e.g., Warren and H. Matzke, Proceedings Of the International Conference On the Science of Hard Materials, Jackson, Wyoming, Aug 23-28, 1981. Hardness Hv and Crack Length are measured at a load of 10 Kg for 15 seconds. During each measurement, eight indentations were made on each specimen and the average value was used in computation of the listed data.

Weight 96 Vol %
Re in Re Co R-95 WC VC 8inder Binder P54 0 8 0 91.4 0.6 0 13.13 P58 0 0 7.5 91.9 0.6 0 13.25 P56 1_8 7.2 0 90.4 0.6 20 13.20 P72 1.8 7.2 0 90.7 0.3 20 13.18 P73 1_8 4.8 2.7 90_4 0.3 20 14.00 P74 1_8 3 4.5 90.4 0.3 20 14.24 Palmgvist Cal. Measu.
Sample Sinter HIP Hardness,Hv Tougxsness Code Condition Condition Density Density Kg/mm' Rsc, g/c.c. g/c.c.
x106Pa=mliz 1360 C/1hr 14.58 2062t35 8.9t0.2 P54-5 14.63 1360 C/1hr 13050C/15KSI/1hr 14.55 2090t22 8.5t0.2 1550 C/1hr 14.40 2064 12 7.9t0.2 P58-7 14.50 1550 C/Zhr 13050C/15KSI/1hr 14.49 2246t23 7.3t0.1 1360 C/lhr 14.71 2064t23 8.2t0.1 P56-5 14.77 1360 C/1hr 13050C/15KSI/1hr 14.72 2133 34 8.6 0.2 1475 C/1hr 14.77 .2036t34 8.5t0.6 P72-6 14.83 1475 C/lhr 1305 C/15KSI/1hr 14.91 2041t30 9.1t0.4 1475 C/1hr 14.70 2195t23 7.7f0.1 P73-6 14.73 1475 C/lhr 1305 C/151(SI/1hr 14.72 2217t25 8.1t0.2 1500 C/1hr 14.69 2173t30 7.4t0.3 and 1520 C/1hr P74-5 14.69 1500 C/1hr 1305 C/15KSI/1hr 14.74 2223t34 7_7t0.1 and 1520 C/lhr [0075] Among the tested samples, the sample P54 uses the conventional binder consisting of Co. The Ni-superalloy R-95 is used in the sample P58 to replace Co as the binder in the sample P54. As a result, the Hv increases from 2090 of P54 to 2246 of P58. In the sample P56, the mixture of Re and Co is used to replace Co as binder and the corresponding Hv increases from 2090 of P54 to 2133 of P56. The samples P72, P73, P74 have the same Re content but different amounts of Co and R95. The mixtures of Re, Co, and R95 are used in samples P73 and P74 to replace the binder having a mixture of Re and Co as the binder in the sample 72. The hardness Hv increases from 2041(P72) to 2217 (P73) and 2223(P74).

Weight 9s Vol. 96 WC WC Re in Re R-95 Co TiC TaC Binder (2 m) (0.2 m) Binder P17 1.5 4.5 0 3 3 88 0 25 8.78 P18 3 3 0 3 3 88 0 50 7.31 P25 3.75 2.25 0 3 3 88 0 62.5 6.57 P48 3.75 2.25 0 5 5 84 0 62.5 6.3 P50 4.83 1.89 0 5.31 5.22 82.75 0 71.9 6.4 251 7.15 0.93 0 5.23 5.14 81.55 0 88.5 6.4 P49 7.55 0 3.25 5.31 5.21 78.68 0 69.9 10 P40A 7.57 2.96 0 5.32 5.23 78.92 0 71.9 10 P63 12.47 0.86 0 5.16 5.07 0 76.45 93.6 10 P62A 14.48 0 0 5.09 5.00 0 75.43 100 10 P66 27.92 0 0 4.91 4.82 0 62.35 100 20 ~111-[0076] Measurements on selected samples have also been performed to further study properties of the binder matrices with Re in the binder matrices. TABLE 13 lists the tested samples. The WC particles with two different particle sizes of 2 m and 0.2 m were used. TABLE 14 lists the conditions for the two-step process performed and the measured densities, hardness parameters, and toughness parameters of the selected samples.

Cal. Measu. Palmqvist Sample Sinter HIP Hardness,Hv Code Condition Condition Density Density Kg/mmz Toughness**
g/C.c. g/c.C. Ksc, MPamo.5 P17-5 1800 C/lthr 1600 C/15KS1/Zhr 14.15 14.21 2092 3 7.2t0.1 P18-3 1800 C/1hr 1600 C/15KSI/1hr 14.38 14.59 2028 88 6.8 0.3 P25-3 1750 C/lhr 1600 C/15KSI/lhr 14.49 14.48 2193f8 6.5t0.1 P48-1 1800 C/1hr 1600 C/15KSI/lhr 13.91 13.99 2208t12 6.3 0.4 P50-4 1800 C/1hr 1600 C/15K51/lhr 13.9 13.8 2294t20 6.3t0.1 P51-1 1800 C/lhr 1600 C/15KSI/1hr 14.11 13.97 2309f6 6.6t0.1 P40A-1 1800 C/lhr 1600 C/15KSI/1hr 13.86 13.86 2321t10 6.3t0.1 P49-1 1800 C/1hr 1600 C/15KSI/lhr 13.91 13.92 2186t29 6.5t0.2 P62A-6 2200 C/lhr 17250C/30KSI/1hr 14.5 14.41 2688t22 6.7 0.1 P63-5 2200 C/lhr 17250C/30KSI/lhr 14.31 14.37 2562 31 6.7 0.2 P66-4 2200 C/lhr 15.04 14.40 2402t44 8.2t0.4 P66-4 2200 C/1hr 1725 C/30KSI/1hr 15.04 14.52 1725 C/30KSI/ihr P66-4 2200 C/lhr 15.04 14.53 2438 47 6.9 0.2 +1950 C/30KSI/1hr P66-5 2200 C/lhr 15.04 14.33 2092t23 7.3 0.3 P66-5 2200 C/lhr 1725 C/30KSI/lhr 15.04 14.63 1725 C/30KSI/1hr P66-5 2200 C/lhr 15.04 14.66 2207t17 7.1t0.2 +1850 C/30KSI/1hr [0077] TABLE 15 further shows measured hardness parameters under various temperatures for the selected samples, where the Knoop hardness Hk were measured under a load of 1 Kg for 15 seconds on a Nikon QM hot hardness tester and R is a ratio of Hk at an elevated testing temperature over Hk at 25 C. The hot hardness specimens of C2 and C6 carbides were prepared from inserts SNU434 which were purchased from MSC Co.(Melville, NY).

(each measured value at a given temperature is an averaged value of 3 different measurements) Testing Temperature, C
Lot No. Tiv @25 25 400 500' 600 700 800 900 Hk, Kg/mm2 1880 1720 1653 1553 1527 2092 17 25 t29 t6 3 R, $ 100 91 88 83 81 Hk, Kg/mm2 R, $ 100 85 83 81 76 Hk, Kg/mm2 45 12 t0 5 8 R, % 100 92 87 81 Hk, Kg/mm2 R, $ 100 85 83 79 77 Hk, Kg/nmt2 R, ~ 100 84 80 77 = 72 Hk, Kg/mm2 P49-1 32 t0 6 17 29 R, % 100 87 81 79 Hk , Kg/mm2 2057 1857 1780 1713 1627 2294 R, $ 100 90 87 83 79 Hk, Kg/mm2 2050 1797 1743 1693 1607 2309 R, ~ 100 88 85 83 78 Hk, Kg/mmz 2228 2063 1960 1750 2688 P62A-6 29 25 76 t0 22 R, $ 100 93 88 79 Hk, Kg/mm2 1887 1707 1667 1633 1603 2562 R, % 100 Hk, Kg/mm2 1503 988 711 584 1685 C2 Carbide 38 9 t0 27 16 R, % 100 66 47 39 C6 Carbide Hk, Kg/mm2 1423 1127 1090 1033 928 1576 E

R, $ 100 79 77 73 65 [0078] Inclusion of Re in the binder matrices of the hardmetals increases the melting point of binder alloys that include Co-Re, Ni superalloy-Re, Ni superalloy-Re-Co. For example, the melting point of the sample P63 is much higher than the temperature of 2200 C used for the solid-phase sintering process. Hot hardness values of such hardmetals with Re in the binders (e.g., P17 to P63) are much higher than conventional Co bound hardmetals( C2 and C6 carbides). in particular, the above measurements reveal that an increase in the concentration of Re in the binder increases the hardness at high temperatures. Among the tested samples, the sample P62A with pure Re as the binder has the highest hardness. The sample P63 with a binder composition of 94% of Re and 6 % of the Ni-based superalloy R95 has the second highest hardness.
The samples P40A(71.9%Re-29.1%R95), P49(69.9%Re-30.1%R95), P51(88.5%Re-11.5%R95), and P50(71.9%Re-28.1%R95) are the next group in their hardness. The sample P48 with 62.5% of Re and 37.5% of R95 in its binder has the lowest hardness at high temperatures among the tested materials in part because its Re content is the lowest.
[0079] In yet another category, a hardmetal or cermet may include TiC and TiN bonded in a binder matrix having Ni and Mo or M02C. The binder Ni of cermet can be fully or partially replaced by Re, by Re plus Co, by Ni-based superalloy, by Re plus Ni-based superalloy, and by Re plus Co and Ni-based superalloy. Samples P38 and P39 are examples of Ni-bound cermets. The sample P34 is an example of Rene95-bound Cermet.
The P35, P36, P37, and P45 are Re plus Rene95 bound cermet.
Compositions of P34, 35, 36, 37, 38, 39, and 45 are listed in TABLE 16.

TABLE 16 Composition of P34 to P39 Weight =%
Re Rene95 Ni 1 Ni 2 TiC M02C WC TaC
P34 14.47 69.44 16.09 P35 8.77 10.27 65.37 15.23 P36 16.6 6.50 62.40 14.46 P37 23.8 3.09 59.38 13.76 P38 15.51 68.60 15.89 P39 15.51 68.60 15.89 P45 9.37 3.66 15.37 6.51 58.6 6.47 [0080] TABLES 17-29 list additional compositions with 3 exemplary composition ranges 1, 2, and 3 which may be used for different applications.

TABLE 17. Compositions that use pure Re as a binder for binding a carbide from carbides of IVb, Vb, & VIb colu.mns of the Periodic Table or a nitride from nitrides of IVb & Vb columns Composition Range Composition Range 2 Composition Range Estimated 1 3 Malting Point, Volume % Weight Volume % Weight % Volume Weight ~ c Re Re 7.25 to 5 to 74 7.25 to 25 to 70 7.25 to 25 to 65 3000 to 3200 Bound 40 35 30 TiC
TiC 60 to 26 to 65 to 30 to 75 70 to 35 to 75 92.75 75 92.75 92.75 Re Re 3 to 40 9 to 68 4 to 35 12 to 63 5 to 30 14 to 58 3000 to 3200 Bound ZrC 60 to 97 32 to 65 to 96 37 to 88 70 to 42 to 86 ZrC 93 95 Re Re 16.75 to 25 to 16.75 to 25 to 47 16.75 25 to 42 3000 to 3200 Bound 40 52 35 to 30 HfC HfC 60 to 48 to 65 to 53 to 75 70 to 58 to 75 83.25 75 83.25 83.25 Re Re 3 to 40 11 to 4 to 35 14 to 67 5 to 30 17 to 62 2700 to 3100 Bound 72 VC VC 60 to 97 28 to 65 to 96 33 to 86 70 to 38 to 83 Re Re 3 to 40 8 to 64 4 to 35 10 to 59 5 to 30 12 to 54 3000 to 3200 Bound NbC 60 to 97 36 to 65 to 96 41 to 90 70 to 46 to 88 NbC 92 95 Re Re 3 to 40 4 to 49 4 to 35 6 to 44 5 to 30 7 to 38 3000 to 3200 Bound TaC 60 to 97 51 to 65 to 96 56 to 94 70 to 62 to 93 TaC 96 95 Re Re 3 to 40 9 to 68 4 to 35 12 to 63 5 to 30 14 to 57 1700 to 1900 Bound CrZC3 60 to 97 32 to 65 to 96 37 to 88 70 to 43 to 86 Cr2C3 91 95 Re Re 3 to 40 7 to 61 4 to 35 9 to 55 5 to 30 11 to 50 2300 to 2600 Bound MozC 60 to 97 39'to 65 to 96 45 to 91 70 to 50 to 89 Re Re 20 to 40 25 to 20 to 35 25 to 42 20 to 25 to 37 2700 to 2900 Bound 47 30 WC WC 60 to 80 53 to 65 to 80 58 to 75 70 to 63 to 75 Re Re 3 to 40 11 to 4 to 35 14 to 68 5 to 30 17 to 62 2900 to 3100 Bound 72 TiN TiN 60 to 97 28 to 65 to 96 32 to 86 70 to 38 to 83 Re Re 3 to 40 8 to 66 4 to 35 11 to 61 5 to 30 13 to 55 2900 to 3100 Bound ZrN 60 to 97 34 to 65 to 96 39 to 89 70 to 45 to 87 ZrN 92 95 Re Re 3 to 40 4 to 50 4 to 35 6 to 45 5 to 30 7 to 39 3000 to 3200 Bound HfN 60 to 97 50 to 65 to 96 55 to 94 70 to 61 to 93 HfN 96 95 Re Re 3 to 40 9 to 70 4 to 35 13 to 65 5 to 30 16 to 62 2100 to 2300 Bound VN 60 to 97 30 to 65 to 96 35 to 87 70 to 38 to 84 Re Re 3 to 40 8 to 66 4 to 35 11 to 61 5 to 30 13 to 55 2300 to 2500 Bound NbN 60 to 97 34 to 65 to 96 39 to 89 70 to 45 to 87 NbN 92 95 Re Re 3 to 40 4 to 49 4 to 35 6 to 44 5 to 30 7 to 39 3000 to 3200 Bound F TaN 60 to 97 51 to 65 to 96 56 to 94 70 to 61 to 93 TaN 96 95 ^116--TABLE 18. Compositions that use Ni-based superalloy(NBSA) in a binder for binding a nitride from nitrides of IVb &Vb columns of the Periodic Table.
Composition Range 1 Composition Range 2 Composition Range Volume Weight % Volum.e Weight % Volume Weight=%

NBSA NBSA 3 to 40 4 to 50 4 to 35 6 to 44 5 to 30 7 to 39 TiN TiN 60 to 50 to 96 65 to 56 to 94 70 to 61 to NBSA NBSA 3 to 40 3 to 42 4 to 35 4 to 37 5 to 30 5 to 32 ZrN ZrN 60 to 58 to 97 65 to 63 to 96 70 to 68 to NBSA NBSA 3 to 40 1.8 to 28 4 to 35 2.4 to 24 5 to 30 3 to 19 HfN HfN 60 to 72 to 65 to 76 to 70 to 81 to 97 98.2 96 97.6 95 97 NBSA NBSA 3 to 40 4 to 47 4 to 35 5 to 42 5 to 30 7 to 36 VN VN 60 to 53 to 96 65 to 58 to 95 70 to 64 to NBSA NBSA 3 to 40 3 to 42 4 to 35 4 to 37 5 to 30 5 to 32 NbN NbN 60 to 52 to 97 65 to 33 to 96 70 to 68 to NBSA NBSA 3 to 40 1.7 to 27 4 to 35 2.3 to 23 5 to 30 3 to 19 TaN TaN 60 to 73 to 65 to 77 to 70 to 81 to 97 '98.3 96 97.7 95 97 TABLE 19. Compositions that use Re and Ni-based superalloy (Re+NBSA) in a binder for binding a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of the binder is from 1oRe + 99% superalloy to 99% Re + 1%
superalloy.

Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight %
(Re+NBSA) Re 0.03 to 0.13 to 0.04 to 0.17 to 0.05 to 0.21 to - 39.6 73_6 34.7 69.3 29.7 64.3 TiC NBSA 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 39.6 51.1 34.7 45.9 29.7 40.4 TiC 60 to 97 26.1 to 65 to 96 30.5 to 70 to 95 35.5 to 92 95.1 93.6 (Re+NBSA) Re 0.03 to 0.09 to 0.04 to 0.13 to 0.05 to 0.16 to - 39.6 67.7 34.7 62.9 29.7 57.5 ZrC NBSA 0.03 to 0.03 to 0.04 to 0.05 to 0.05 to 0.06 to 39.6 44.1 34.7 39.0 29.7 33.8 ZrC 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 42 to 94 (Re+NBSA) Re 0.03 to 0.05 to 0.04 to 0.07 to 0.05 to 0.08 to - 39.6 52.1 34.7 46.8 29.7 41.2 HfC NBSA 0.03 to 0.02 to 0.04 to 0.025 to 0.05 to 0.03 to 21 39.6 29.2 34.7 25 29.7 HfC 60 to 97 47.7 to 65 to 96 53 to 70 to 95 58.6 to 98.1 97.4 96.7 (Re+NBSA) Re 0.03 to 0.11 to 0.04 to 0.15 to 0.05 to 0.19 to - 39.6 71.5 34.7 67.0 29.7 61.8 VC NBSA 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 39.6 48.4 34.7 43.3 29.7 37.9 VC 60 to 97 28.3 to 65 to 96 32.8 to 70 to 95 38 to 92.8 95.6 94.2 (Re+NBSA) Re 0.03 to 0.08 to 0.04 to 0.1 to 0.05 to 0.13 to - 39.6 63.8 34.7 58.7 29.7 53.1 NbC NBSA 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 30 39.6 39.9 34.7 35 29.7 NbC 60 to 97 36 to 96.9 65 to 96 41 to 70 to 95 46.6 to 95.8 94.8 (Re+NBSA) Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 38 - 39.6 48.8 34.7 43.5 29.7 TaC NBSA 0.03 to 0.016 to 0.04 to 0.02 to 0.05 to 0.03 to 39.6 26.5 34.7 ' 22.6 29.7 18.9 TaC 60 to 97 51 to 98.3 65 to 96 56.3 to 70 to 95 61.8 to 97.7 97.1 (Re+NBSA) Re 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.16 to - 39.6 67.3 34.7 62.5 29.7 57.0 Cr2C3 NBSA 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 39.6 43.6 34.7 38.6 29.7 33.4 Cr2C3 60 to 97 32.4 to 65 to 96 37.3 to 70 to 95 42.8 to 96.4 95.2 94.0 (Re+NBSA) Re 0.03 to 0.07 to 0.04 to 0.1 to 55 0.05 to 0.12 to - 39.6 60.2 34.7 29.7 49.3 M02C NBSA 0.03 to 0.025 to 0.04 to 0.03 to 0.05 to 0.04 to 39.6 36.3 34.7 31.6 29.7 26.9 M02C 60 to 97 39.6 to 65 to 96 44.8 to 70 to 95 50.5 to 97.3 96.4 95.5 (Re+NBSA) Re 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to - 39.6 46.9 34.7 41.7 29.7 36.3 WC NBSA 0.03 to 0.015 to 25 0.04 to 0.02 to 0.05 to 0.025 to 39.6' 34.7 21.3 29.7 17.8 wC 60 to 97 52.9 to 65 to 96 58.2 to 70 to 95 63.6 to 98.4 97.9 97.3 (Re+NBSA) Re 0.03 to 0.1 to 71.7 0.04 to 0.15 to 0.05 to 0.19 to 62 - 39.6 34.7 67.2 29.7 TiN NBSA 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 38 39.6 48.7 34.7 43.5 29.7 ~118~

TiN 60 to 97 28 to 95.6 65 to 96 32.6 to 70 to 95 37.8 to 94.1 92.7 (Re+NBSA) Re 0.03 to 0.09 to 0.04 to 0.1 to 0.05 to 0.14 to - 39.6 65.3 34.7 . 60.3 29.7 54.8 ZrN NBSA 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 39.6 41.4 34.7 36.5 29.7 31.4 ZrN 60 to 97 34.5 to 65 to 96 39.4 to 70 to 95 45 to 94.5 96.7 95.6 (Re+NBSA) Re 0.03 to 0.05 to 50 0.04 to 0.06 to 0.05 to 0.08 to - 39.6 34.7 44.7 29.7 39.2 HfN NBSA 0.03 to 0.017 to 0.04 to 0.02 to 0.05 to 0.03 to 39.6 27.5 34.7 23.5 29.7 19.6 HfN 60 to 97 49.8 to 65 to 96 55.1 to 70 to 95 60.7 to 97 98.2 97.6 (Re+NBSA) Re 0.03 to 0.1 to 69.6 0.04 to 0.14 to 0.05 to 0.17 to - 39.6 34.7 65 29.7 59.6 VN NBSA 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 39.6 46.2 34.7 41.1 29.7 35.8 VN 60 to 97 30 to 96 65 to 96 35 to 70 to 95 40 to 93.3 94.7 (Re+NBSA) Re 0.03 to 0.09 to 0.04 to 0.1 to 0.05 to 0.14 to - 39.6 65.3 34.7 60.4 29.7 54.9 NbN = NBSA 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 39.6 41.5 34.7 36.5 29.7 31.5 NbN 60 to 97 34.4 to 65 to 96 39.4 to 70 to 95 45 to 94.5 96.7 95.6 (Re+NBSA) Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.08 to - 39.6 49.1 34.7 43.8 29.7 38.3 TaN NBSA 0.03 to 0.017 to 0.04 to 0.02 to 0.05 to 0.027 to 19 39.6 26.8 34.7 = 22.8 29.7 TaN 60 to 97 50.7 to 65 to 96 56 to 70 to 95 61.5 to 97 98.3 97.7 TABLE 20. Compositions that use Re and Co (Re+Co) in a binder for binding a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 1%Re +
99% Co to 99% Re + 1%Co.
Material Composition Range 1 Composition Range 2 Composition Range 3 Volume Weight % Volume % Weight ~ Volume ~ Weight %
(Re+Co) Re 0.03 to 0.13 to 0.04 to 0.17 to 0.05 to 0.20 to - 39.6 73.6 34.7 69.3 29.7 64.3 TiC Co 0.03 to 0.05 to 0.04 to 0.07 to 0,05 to 0.08 to 39.6 54.1 34.7 48.9 29.7 43.3 TiC 60 to 26.1 65 to 96 30.4 to 70 to 95 35.5 to 91 97 to94.6 92.8 (Re+Co) Re 0.03 to 0.09 to 0.04 to 0.13 to 0.05 to 0.16 to - 39.6 67.7 34.7 62.9 29.7 57.5 ZrC Co 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 39.6 47.1 34.7 42.0 29.7 36.6 ZrC 60 to 32 to 96 65 to 96 37 to 95 70 to 95 42 to 93 (Re+Co) Re 0.03 to 0.05 to 0.04 to 0.07 to 0.05 to 0.08 to - 39.6 52.1 34.7 46.8 29.7 41.2 HfC Co 0.03 to a.02 to 0.04 to 0.028 to 0.05 to 0.035 to 23 39.6 31.8 34.7 27 29.7 HfC 60 to 47.6 to 65 to 96 53 to 70 to 95 58.6 to 97 97_8 97.1 96.3 (Re+Co) Re 0.03 to 0.11 to 0.04 to 0.15 to 0.05 to 0.19 to 39.6 71.4 34.7 67.0 29.7 61.8 VC Co 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.07 to 39.6 51.5 34.7 46.3 29.7 40.8 VC 60 to 28.3 to 65 to 96 32.8 to 70 to 95 38 to 92 97 95.1 93.5 (Re+Co) Re 0.03 to 0.08 to 0.04 to 0.1 to 0.05 to 0.13 to - 39.6 63.8 34.7 58.7 29.7 53.1 NbC Co 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 39.6 42.8 34.7 37.8 29.7 32.6 NbC 60 to 36 to 65 to 96 41 to 70 to 95 46.6 to 97 96.5 95.4 94.2 (Re+Co) Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 38 - 39.6 48.8 34.7 43.5 29.7 TaC Co 0.03 to 0.018 to 0.04 to 0.024 to 0.05 to 0.03 to 39.6 28.9 34.7 24.8 29.7 20.8 TaC 60 to 51 to 98 65 to 96 56.3 to 70 to 95 61.8 to 97 97.4 96.8 (Re+Co) Re 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.15 to - 39.6 67.3 34.7 62.5 29.7 57.0 Cr2C3 Co 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 39.6 46.6 34.7 41.5 29.7 36.1 Cr2C3 60 to 32.4 to 65 to 96 37.3 to 70 to 95 42.7 to 97 96 94.6 93.3 (Re+Co) Re 0.03 to 0.07 to 0.04 to 0.1 to 55 0.05 to 0.12 to - 39.6 60.2 34.7 29.7 49.3 M02C Co 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 39.6 39.2 34.7 34.3 29.7 29.4 M02C 60 to 39.6 to 65 to 96 44.8 to 70 to 95 50_5 to 95 (Re+Co) Re 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to - 39.6 46.9 34.7 41.7 29.7 36.3 wC Co 0.03 to 0.017 to 0.04 to 0.023 to 0.05 to 0.028 to 39.6 27.4 34.7 23.4 29.7 19.6 WC 60 to 52.9 65 to 96 58.2 to 70 to 95 63.6 to 97 97 to98.2 97 (Re+Co) Re 0.03 to 0.1 to 0.04 to 0.15 to 0.05 to 0.19 to 62 - 39.6 71.6 34.7 67.1 29.7 TiN Co 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.07 to 41 39.6 51.7 34.7 46.5 2s=7 -120- .

TiN 60 to 28 to 95 65 to 96 32.6 to 70 to 95 37.8 to 92 97 93.4 (Re+Co) Re 0.03 to 0.09 to 0.04 to 0.11 to 0.05 to 0.14 to - 39.6 65.3 34.7 60.3 29.7 54.8 ZrN Co 0.03 to 0.035 to 0.04 to 0.046 to 0_05 to 0.056 to 34 39.6 44.4 34.7 39.3 29.7 ZrN 60 to 34.5 to 65 to 96 39.4 to 70 to 95 45 to 93.8 97 96.3 95 (Re+Co) Re 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.08 to - 39.6 50 34.7 44.7 29.7 39.2 HfN Co 0.03 to 0.02 to 0.04 to 0.026 to 0.05 to 0.03 to 39.6 30 34.7 25.7 29.7 21.6 HfN 60 to 49.8 to 65 to 96 55.1 to 70 to 95 60.7 to 97 98 97.3 96.6 (Re+Co) Re 0.03 to 0.1 to 0.04 to 0.14 to 0.05 to 0.17 to - 39.6 69.6 34.7 65 29.7 59.6 VN Co 0.03 to 0.04 to 0.04 to 0.055 to 0.05 to 0.067 to 39.6 49.3 34.7 44 29.7 38.6 VN 60 to 30 to 65 to 96 35 to 94 70 to 95 40 to 92.6 97 95.5 (Re+Co) Re 0.03 to 0.09 to 0.04 to 0.11 to 0.05 to 0.14 to - 39.6 65.3 34.7 60.4 29.7 54.8 NbN Co 0.03 to 0.035 to 0.04 to 0.046 to 0.05 to 0.057 to 39.6 44.5 34.7 39.4 29.7 34.1 NbN 60 to 34.4 to 65 to 96 39.4 to 70 to 95 45 to 93.8 97 96.3 95 (Re+Co) Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.075 to - 39.6 49.1 34.7 43.8 29.7 38.3 TaN Co 0.03 to 0.019 to 0.04 to 0.025 to 0.05 to 0.03 to 21 39.6 29.2 34.7 25 29.7 TaN 60 to 50.7 to 65 to 96 56 to 70 to 95 61.5 to 97 98 97.4 96.7 -121~

TABLE. 21. Compositions that use Ni-based superalloy (NBSA) and Co in a binder for binding a carbide from carbides of IV'b, Vb, &
VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 1%NBSA + 99% Co to 99%NBSA + 1%Co.
Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight ~
(NBSA+Co) NBSA 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 29.7 0.08 to - 39.6 51.5 34.7 46.2 40.6 TiC Co 0.03 to 0.05 to 0.04 to 0.07 to 0.05 to 29.7 0.09 to 39.6 54.5 34.7 49.2 43.6 TiC 60 to 97 45 to 95 65 to 96 50 to 93.6 70 to 95 56 to 92 (NBSA+Co) NBSA 0.03 to 0.04to 0.04 to 0.05 to 0.05 to 29.7 0.06 to - 39.6 44.4 34.7 39.2 57.5 ZrC Co 0.03 to 0.04 to 0.04 to 0.05 to 42 0.05 to 29.7 0.07 to 39.6 47.4 34.7 34 ZrC 60 to 97 52 to 96 65 to 96 57 to 95 70 to 95 63 to 94 (NBSA+Co) NBSA 0.03 to 0.02 to 0.04 to 0.026 to 0.05 to 29.7 0.03 to - 39.6 29 34.7 25 21 HfC Co 0.03 to 0.02 to 0.04 to 0.03 to 0.05 to 29.7 0.036 to 39.6 32 34.7 27.5 23 HfC 60 to 97 68 to 98 65 to 96 72 to 97.4 70 to 95 77 to 96.8 (NBSA+Co) NBSA 0.03 to 0.04 to 0.04 to 0.06 to 44 0.05 to 29.7 0.07 to - 39.6 49 34.7 38 VC Co 0.03 to 0.05 to 0.04 to 0.06 to 47 0.05 to 29.7 0.08 to 39.6 52 34.7 41 VC 60 to 97 48 to 96 65 to 96 53 to 93.5 70 to 95 59 to 93 (NBSA+Co) NBSA 0.03 to 0.03 to 0.04 to 0.04 to 35 0.05 to 29.7 0.05 to - 39.6 40 34.7 30 NbC Co 0.03 to 0.035 to 0.04 to 0.046 to 0.05 to 29.7 0.06 to 39.6 43 34.7 38 33 NbC 60 to 97 57 to 97 65 to 96 62 to 96 70 to 95 67 to 95 (NBSA+Co) NBSA 0.03 to 0.017 to 0.04 to 0.022 to 0.05 to 29.7 0.03 to - 39.6 27 34.7 23 19 TaC Co 0.03 to 0.02 to 0.04 to 0.025 to 0.05 to 29.7 0.03 to 39.6 29 34.7 25 21 TaC 60 to 97 71 to 98 65 to 96 75 to 97.8 70 to 95 79 to 97 (NBSA+Co) NBSA 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 29.7 0.15 to - 39.6 67.3 34.7 62.5 57.0 Cr2C3 Co 0.03 to 0.04 to 0.04 to 0.05 to 39 0.05 to 29.7 0.06 to 39.6 44 34.7 34 Cr2C3 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 63 to 94 (NBSA+Co) NBSA 0.03 to 0.026 to 0.04 to 0.035 to 0.05 to 29.7 0.044.to - 39.6 36.5 34.7 32 27 M02C Co 0.03 to 0.03 to 0.04 to 0.04 to 34 0.05 to 29.7 0.05 to 39.6 39 34.7 30 Mo2C 60 to 97 60 to 97 65 to 96 65 to 96 70 to 95 70 to 95.6 (NBSA+Co) NBSA 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 29.7 0.07 to - 39.6 46.9 34.7 41.7 36.3 trTC Co 0.03 to 0.018 to 0.04 to 0.024 to 0.05 to 29.7 0.03 to 39.6 27.5 34.7 23.5 19.7 WC 60 to 97 72 to98 65 to 96 76 to 98 70 to 95 80 to 97 (NBSA+Co) NBSA 0.03 to 0.4 to 49 0.04 to 0.06 to 44 0.05 to 29.7 0.07 to - 39.6 34.7 38 TiN Co 0.03 to 0.05 to 0.04 to 0.065 to 0.05 to 29.7 0.08 to 39.6 52 34.7 47 41 TiN 60 to 97 47 to 96 65 to 96 53 to 94 70 to 95 58 to 93 (NBSA+Co) NBSA 0.03 to 0.03 to 0.04 to 0.04 to 37 0.05 to 29.7 0.05 to - 39.6 42 34.7 32 ZrN Co 0.03 to 0.04 to 0.04 to 0.05 to 40 0.05 to 29.7 0.06 to 39.6 45 34.7 34 ZrN 60 to 97 55 to 97 65 to 96 60 to 96 70 to 95 65 to 95 (NBSA+Co) NBSA 0.03 to 0.02 to 0.04 to 0.027 to 0.05 to 29.7 0.03 to - 39.6 31 34.7 27 22 HfN Co 0.03 to 0.02 to 0.04 to 0.024 to 0.05 to 29.7 0.03 to 39.6 27 34.7 23 20 HfN 60 to 97 70 to 98 65 to 96 74 to 97.6 70 to 95 78 to 97 (NBSA+Co) NBSA 0.03 to 0.045 to 0.04 to 0.06 to 47 0.05 to 29.7 0.07 to - 39.6 53 34.7 41 VN Co 0.03 to 0.04 to 0.04 to 0.055 to 0.05 to 29.7 0.066 to 39.6 44 34.7 40 34 VN 60 to 97 50 to 96 65 to 96 55 to 95 70 to 95 61 to 93 (NBSA+Co) NBSA 0.03 to 0.04 to 0.04 to 0.05 to 41 0.05 to 29.7 0.06 to - 39.6 47 34.7 36 NbN Co 0.03 to 0.03 to 0.04 to 0.04 to 35 0.05 to 29.7 0.05 to 39.6 40 34.7 30 NbN 60 to 97 55 to 97 65 to 96 60 to 96 70 to 95 65 to 95 (Re+Co) NBSA 0.03 to 0.02 to 0.04 to 0.026 to 0.05 to 29.7 0.032 to - 39.6 30 34.7 26 22 TaN Co 0.03 to 0.017 to 0.04 to 0.023 to 0.05 to 29.7 0.03 to 39.6 26 34.7 23 19 TaN 60 to 97 70 to 98 65 to 96 75 to 97.7 70 to 95 79 to 97 TABLE 22. Compositions that use Re, Ni-based superalloy (NBSA), and Co in a binder for binding a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 0.5%Re + 0.5% Co+ 99% superalloy to 99% Re + 0.5%
Co + 0.5% Superalloy to 0.5%Re + 99% Co+ 0.5% Superalloy Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight ~ Volume ~ Weight ~ Volume ~ Weight $
(Re+Co Re 0.015 to 0.06 to 0.02 to 0.08 to 0.025 to 0.1 to 64.3 39.6 73.6 34.65 69.3 29.7 +NBSA) NBSA 0.015 to 0.02 to 0.02 to 0.03 to 0.025 to 0.035 to 39.6 51.3 34.65 46.0 29.7 40.5 - Co 0.015 to 0.03 to 0.02 to 0.036 to 0.025 to 0.045 to 39.6 54.3 34.65 49.0 29.7 43.5 TiC TiC 60 to 97 26 to 95 65 to 96 30 to 94 70 to 95 35 to 92 (Re+Co Re 0.015 to 0.05 to 0.02 to 0.06 to 0.025 to 0.08 to +NBSA) 39.6 67.7 34.65 62.9 29.7 57.5 - NBSA 0.015 to 0.017 to 0.02 to 0.022 to 0.025 to 0.028 to ZrC 39.6 44.2 34.65 39.1 29.7 33.9 Co 0.015 to 0.02 to 0.02 to 0.027 to 0.025 to 0.034 to 39.6 47.2 34.65 42.0 29.7 36.7 2rC 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 43 to 94 (Re+Co Re 0.015 to 0.025 to 0.02 to 0.034 to 0.025 to 0.042 to +NBSA) 39.6 52.1 34.65 46.8 29.7 41.2 - NBSA 0.015 to 0.009 to 0.02 to 0.012 to 0.025 to 0.015 to 21 HfC 39.6 29.3 34.65 25.1 29.7 Co 0.015 to 0.01 to 0.02 to 0.014 to 0.025 to 0.018 to 39.6 31.8 34.65 27.4 29.7 23.1 HfC 60 to 97 48 to 98 65 to 96 53 to 70 to 95 59 to 96.8 97.4 (Re+Co Re 0.015 to 0.06 to 0.02 to 0.08 to 0.025 to 0.09 to +I4BSA) 39.6 71.5 34.65 67 29.7 61.8 - NBSA 0.015 to 0.02 to 0.02 to 0.026 to 0.025 to 0.032 to 38 VC 39.6 48.6 34.65 43.4 29.7 Co 0.015 to 0.024 to 0.02 to 0.032 to 0.025 to 0.04 to 39.6 51.7 34.65 46.4 29.7 40.9 VC 60 to 97 28 to 96 65 to 96 33 to 94 70 to 95 38 to 93 (Re+Co Re 0.015 to 0.04 to 0.02 to 0.05 to 0.025 to 0.07 to +NBSA) 39.6 63.8 34.65 58.7 29.7 53.1 - NBSA 0.015 to 0.015 to 0.02 to 0.02 to 0.025 to 0.024 to 30 NbC 39.6 40 34.65 35 29.7 Co 0.015 to 0.017 to 0.02 to = 0.023 to 0.025 to 0.03 to 39.6 43 34.65 37.9 29.7 32.7 Nbc 60 to 97 36 to 97 65 to 96 41 to 96 70 to 95 47 to 95 (Re+Co Re 0.015 to 0.02 to 0.02 to 0.03 to 0.025 to 0.04 to 38 +NBSA) 39.6 48.8 34.65 43.5 29.7 - NBSA 0.015 to 0.008 to 0.02 to 0.011 to 0.025 to 0.013 to TaC 39.6 26.6 34.65 22.6 29.7 18.9 Co 0.015 to 0.01 to 0.02 to 0.013 to 0.025 to 0.016 to 39.6 29 34.65 24.8 29.7 20.8 TaC 60 to 97 51 to 65 to 96 56 to 70 to 95 61.8 to 98.3 97.7 97.2 (Re+Co Re 0.015 to 0.05 to 0.02 to 0.06 to 0.025 to 0.08 to 57 +NBSA) 39.6 67.3 34.65 62.5 29.7 - NBSA 0.015 to 0.017 to 0.02 to 0.022 to 0.025 to 0.027 to Cr2C3 39.6 43.8 34.65 38.7 29.7 33.5 Co 0.015 to 0.02 to 0.02 to 0.027 to 0.025 to 0.033 to 39.6 46.8 34.65 41.6 29.7 36.2 Cr2C3 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 43 to94 (Re+Co Re 0.015 to 0.03 to 0.02 to 0.05 to 0.025 to 0.06 to 49 +NBSA) 39.6 60.2 34.65 55 29.7 - NBSA 0.015 to 0.013 to 0.02 to 0.017 to 0.025 to 0.02 to 27 MoZC 39.6 36.4 34.65 31.7 29.7 Co 0.015 to 0.015 to 0.02 to 0.02 to 0.025 to 0.025 to 29 39.6 39.3 34.65 34 29.7 MozC 60 to 97 39 to 97 65 to 96 45 to 96 70 to 95 50 to 95.6 (Re+Co Re 0.015 to 0.02 to 0.02 to 0.027 to 0.025 to 0.034 to +NBSA) 39.6 46.9 34.65 41.7 29.7 36.3 - NBSA 0.015 to 0.008 to 0.02 to 0.01 to 0.025 to 0.013 to WC 39.6 25.1 34.65 21.3 29.7 17.8 Co 0.015 to 0.009 to 0.02 to 0.012 to 0.025 to 0.015 to 39.6 27.5 34.65 23.5 29.7 19.6 1 65 to 96 58 to 70 to 95 64 to 97.4 WC 60 to 97 53 to 98 97.8 ' Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight ~ Volume % Weight %
(Re+Co Re 0.015 to 0.06 to 0.02 to 0.08 to 0.025 to 0.1 to 62 39.6 71.6 34.65 67.2 29.7 +NBSA) NBSA 0.015 to 0.02 to 0.02 to 0.027 to 0.025 to 0.032 to 39.6 48.8 34.65 43.6 29.7 38.2 - Co 0.015 to 0.025 to 0.02 to 0.03 to 0.025 to 0.04 to 39.6 51.9 34.65 46.6 29.7 41 TiN TiN 60 to 97 28 to 96 65. to 96 33 to 94 70 to 95 38 to 93 (Re+Co Re 0.015 to 0.04 to 0.02 to 0.06 to 0.025 to 0.07 to +NBSA) 39.6 65.3 34.65 60.3 29.7 54.8 - NBSA 0.015 to 0.016 to 0.02 to 0.02 to 0.025 to 0.025 to ZrN 39.6 41.6 34.65 36.6 29.7 31.5 Co 0.015 to 0.02 to 0.02 to 0.025 to 0.025 to 0.03 to 39.6 44.6 34.65 40 29.7 34 ZrN 60 to 97 34 to 97 65 to 96 39 to 96 70 to 95 45 to 95 Re+Co Re 0.015 to 0.02 to 0.02 to 0.03to 45 0.025 to 0.04 to +NBSA 39.6 50 34.65 29.7 39 - NBSA 0.015 to 0.009 to 0.02 to 0.011 to 0.025 to 0.014 to HfN 39.6 27.5 34.65 23.5 29.7 20 Co 0.015 to 0.01 to 0.02 to 0.013 to 0.025 to 0.017 to 39.6 30 34.65 25.8 29.7 22 HfN 60 to 97 50 to 98 65 to 96 55 to 97.6 70 to 95 61 to 97 Re+Co Re 0.015 to 0.05 to 0.02 to 0.07 to 65 0.025 to 0.09 to +NBSA 39.6 60 34.65 29.7 60 - NsSA 0.015 to 0.02 to 0.02 to 0.024to 0.025 to 0.03 to VN 39.6 46.4 34.65 41.2 29.7 36 Co 0.015 to 0.02 to 0.02 to 0.03 to 44 0.025 to 0.04 to 39.6 49 34.65 29.7 39 VN 60 to 97 30 to 96 65 to 96 35 to 95 70 to 95 40 to 93 Re+Co Re 0.015 to 0.04 to 0.02 to 0.06 to 60 0.025 to 0.07 to +NBSA 39.6 65 34.65 29.7 55 - NBSA 0.015 to 0.016to 0.02 to 0.02 to 37 0.025 to 0.025 to NbN 39.6 42 34.65 29.7 32 Co 0.015 to 0.02 to 0.02 to 0.025 to 0.025 to 0.03 to 39.6 45 34.65 39.5 29.7 34 NbN 60 to 97 34to 97 65 to 96 39 to 96 70 to 95 45 to 95 Re+Co Re 0.015 to 0.02 to 0.02 to 0.03 to 44 0.025 to 0.04 to +NBSA 39.6 49 34.65 29.7 38 - NBSA 0.015 to 0.008 to 0.02 to 0_011 to 0.025 to 0.014 to TaN 39.6 27 34.65 23 29.7 19 Co 0.015 to 0.01 to 0.02 to 0.013 to 0.025 to 0_016 to 39.6 29 34.65 25 29.7 21 TaN 60 to 97 51 to 65 to 96 56 to 97.7 70 to 95 61.5 to 98.3 97.1 --125~

TABLE 23. Compositions that use Re for binding WC+TiC or WC+TaC
or WC+TiC+TaC

Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight %
Re Re 3 to 40 4 to 54 4 to 35 5 to 49 5 to 30 7 to 43 - WC 40 to 96 40 to 96 43 to 94.5 44 to 94 45 to 93 48 to 93 WC+TiC TiC 1 to 48 0.3 to 21 1.5 to 43 0.5 to 19 2 to 45 0.6 to 18 Re Re 3 to 40 4 to 48 4 to 35 5 to 42 5 to 30 7 to 37 - WC 50 to 96.5 44 to 96 55 to 95 49 to 94 60 to 93.5 55 to 92 WC+TaC TaC 0.5 to 24 0.5 to 21 1 to 22 1 to 19 1.5 to 18 1.5 to18 Re Re 3 to 40 4 to 48 4 to 35 5 to 43 5 to 30 7 to 38 - WC 40 to 95.5 36 to 95 45 to 93 41 to 93 50 to 90 48 to 90 WC+TiC TiC l to 48 0.3 to 22 2 to 45 0.6 to 20 3 to 42 0.9 to 18 +TaC TaC 0.5 to 20 0.5 to 25 1 to 18 0.8 to 22 2 to 15 2 to 17 TABLE 24. Compositions that use Ni-based superalloy (NBSA) for binding WC+TiC or WC+TaC or WC+TiC+TaC

Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight ~ Volume % Weight % Volume % Weight %
NBSA NBSA 3 to 40 1.5 to 4 to 35 2 to 26 5 to 30 3 to 23 - WC 40 to 96 60 to 98 43 to 63 to 97 45 to 93 66 to 94.5 96.5 WC+TiC TiC 1 to 48 0.3 to 1.5 to 43 0.5 to 2 to 45 0.6 to 20 NBSA NBSA 3 to 40 1.5 to 4 to 35 2 to 22 5 to 30 3 to 18 - WC 50 to 63 to 98 55 to 95 67 to 97 60 to 71 to 96 96.5 93.5 WC+TaC TaC 0.5 to 24 0.5 to 1 to 22 1 to 23 1.5 to 18 1.5 to 21 NBSA NBSA 3 to 40 1.5 to 4 to 35 2 to 22 5 to 30 3 to 19 - WC 40 to 51 to 98 45 to 93 56 to 96 50 to 90 61 to 94 WC+TiC TiC 1 to 48 0.4 to 2 to 45 0.8 to 3 to 42 1 to 19 +TaC TaC 0.5 to 20 0.6 to 1 to 18 1 to 23 2 to 15 2 to 18 TABLE 25. Compositions that use Re and Ni-based superalloy (NBSA) in a binder for binding WC+TiC or WC+TaC or WC+TiC+TaC

Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight $
(Re+ Re 0.03 to 0.04 to 0.04 to 0.06 to 48 0.05 to 0.07 to 39.6 52 34.65 29.7 45 NSSA) NBSA 0.03 to 0.015 to 0.04 to 0.02 to 26 0.05 to 0.026 to 39.6 29 34.65 29.7 23 - WC 40 to 96 40 to 98 43 to 44 to 97 45 to 93 48 to 94.5 96.6 WC+TiC TiC 1 to 48 0.3 to 24 1.5 to 45 0.5 to 22 2 to 42 0.6 to 21 (Re+ Re 0.03 to 0.04 to 0.04 to 0.055 to 0.05 to 0.07 to 39.6 47 34.65 42 29.7 37 NBSA) NBSA 0.03 to 0.015 to 0.04 to 0.02 to 22 0.05 to 0.025 to 39.6 25 34.65 29.7 18 - WC 50 to 44 to 98 55 to 95 50 to 97 60 to 93 55 to 96.5 95.5 WC+TaC TaC 0.5 to 0.5 to 24 1 to 20 1 to 21.5 2 to 18 2 to 19 (Re+ Re 0.03 to 0.04 to 0.04 to 0.06 to 47 0.05 to 0.07 to 39.6 53 34.65 29.7 41 NBSA) NBSA 0.03 to 0.015 to 0.04 to 0.02 to 25 0.05 to 0.026 to - 39.6 30 34.65 29.7 21 WC+TiC WC 40 to 40 to 98 45 to 93 46 to 96 50 to 90 51 to 94 +TaC 95.5 TiC 1 to 48 0.3 to 23 2 to 45 0.6 to 21 3 to 42 0.9 to 19 TaC 0.5 to 0.4 to 26 1 to 18 0.8 to 23 2 to 15 2 to 18 ~128~

TABLE 26. Compositions that use Re and Co in a binder for binding WC+TiC or WC+TaC or WC+TiC+TaC

Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight %
(Re+ Re 0.03 to 0.04 to 0.04 to 0.055 to 0.05 to 0.07 to 39.6 53 34.65 48 29.7 43 Co) Co 0.03 to 0.017 to 0.04 to 0.023 to 0.05 to 0.03 to 39.6 31 34.65 28 29.7 26 - WC 40 to 96 40 to 98 43 to 94.5 44 to 97 45 to 93 48 to 96 WC+TiC TiC 1 to 48 0.3 to 23 1.5 to 45 0.5 to 22 2 to 42 0.6 to 21 (Re+ Re 0.03 to 0.04 to 0.04 to 0.055 to 0.05 to 0.07 to 39.6 47 34.65 42 29.7 37 Co) CO 0.03 to 0.017 to 0.04 to 0.023 to 0.05 to 0.03 to 39.6 28 34.65 24 29.7 20 - WC 50 to 44 to 98 55 to 95 50 to 97 60 to 93 55 to 95 96.5 WC+TaC TaC 0.5 to 0.5 to 24 1 to 20 1 to 21 2 to 18 2 to 19 (Re+ Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 39.6 53 34.65 47 29.7 41 Co) Co 0.03 to 0.017 to 0.04 to 0.023 to 0.05 to 0.03 to - 39.6 33 34.65 28 29.7 23 WC+TiC WC 40 to 40 to 98 45 to 93 46 to 96 50 to 90 51 to 94 +TaC 95.5 TiC 1 to 48 0.3 to 23 2 to 45 0.6 to 21 3 to 42 0.9 to 19 TaC 0.5 to 0.4 to 26 1 to 18 0.8 to 23 2 to 15 2 to 18 TABLE 27. Compositions that use Co and Ni-based superalloy (NBSA) in a binder for binding WC+TiC or WC+TaC or WC+TiC+TaC

Material Composition Range Composition Range 2 Composition Range 3 Volume Weight % Volume ~ Weight % Volume ~ Weight %
$
(Co+ Co 0.03 to 0.018 to 0.04 to 0.024 to 0.05 to 0.03 to 39.6 33 34.65 29 29.7 25 NBSA) NBSA 1 0.03 to 0.015 to 0.04 to 0.02 to 26 0.05 to 0.03 to 39.6 29 34.65 29.7 23 - WC 40 to 58 to 98 43 to 61 to 97 45 to 93 64 to 96 94.5 96.7 WC+TiC TiC 1 to 48 0.3 to 1.5 to 0.5 to 22 2 to 42 0.7 to 21 (Co+ Co 0.03 to 0.018 to 0.04 to 0.024 to 0.05 to 0.03 to 39.6 28 34.65 24 29.7 20 NBSA) NBSA 0.03 to 0.015 to 0.04 to 0.02 to 22 0.05 to 0.025 to 39.6 25 34.65 29.7 18 - WC 50 to 61 to 98 55 to 95 65 to 97 60 to 93 69 to 95 96.5 WC+TaC TaC 0.5 to 0.5 to 1 to 20 1 to 21.5 2 to 18 2 to 19 (Co+ Co 0.03 to 0.018 to 0.04 to 0.024 to 0.05 to 0.03 to 39.6 33 34.65 28 29.7 23 NBSA) NBSA 0.03 to 0.015 to 0.04 to 0.02 to 25 0.05 to 0.026 to 39.6 30 34.65 29.7 21 - WC 40 to 57 to 98 45 to 93 62 to 96 50 to 90 67 to 94 WC+TiC 95.5 +TaC TiC 1 to 48 0.4 to 2 to 45 0.7 to 21 3 to 42 1 to 19 TaC 0.5 to 0.6 to 1 to 18 1 to 23 2 to 15 2 to 18 TABLE 28. Compositions that use Re, Ni-based superalloy (NBSA), and Co in a binder for binding WC+TiC or WC+TaC or WC+TiC+TaC.
The range of Binder is from 0.5%Re + 99.5% superalloy to 99.5% Re + 0.5% Superalloy to 0.5%Re + 0.5% Superalloy+ 99% Co.
Material Composition Range 1 Composition Range 2 Composition Range 3 Volume Weight ~ Volume ~ Weight % Volume $ Weight %
$
(Re+Co Re 0.015 0.02 to 0.02 to 0.027 to 0.025 to 0.035 to NBSA) to 39.8 54 34.8 48 29.9 43 NBSA 0.015 0.008 to 0.02 to 0.01 to 0.025 to 0.13 to - to 39.8 29 34.8 26 29.9 24 WC+TiC Co 0 to 0 to 32 0 to 34.7 0 to 29 0 to 0 to 26 39.6 29.8 WC 40 to 40 to 98 43 to 44 to 97 45 to 93 48 to 96 96 94.5 TiC 1 to 48 0.3 to 24 1.5 to 45 0.5 to 22 2 to 42 0.6 to 21 (Re+Co Re 0.015 0.02 to 0.02 to 0.027 to 0.025 to 0.034 to +NBSA) to 39.8 47 34.8 42 29.9 37 - NBSA 0.015 0.008 to 0.02 to 0.01 to 0.025 to 0.13 to I to 39.8 26 34.8 22 29.9 18 WC+TaC Co 0 to 0 to 28 0 to 34.7 0 to 24 0 to 0 to 20 39.6 29.8 WC 50 to 45 to 98 55 to 95 50 to 97 60 to 93 55 to 95 96.5 TaC 0.5 to 0.5 to 24 1 to 20 0.9 to 21 2 to 18 1.8 to19 (Re+ Re 0.015 0.02 to 0.02 to 0.027 to 0.025 to 0.034 to NBSA to 39.8 65 34.8 58 29.9 51 NBSA 0.015 0.008 0.02 to 0.01 to 0.025 to 0.13 to to 39.8 to4l 34.8 34 29.9 28 +Co) Co 0 to 0 to 44 0 to 34.7 0 to 37 0 to 0 to 31 39.6 29.8 - WC 35 to 35 to 93 40 to 80 41 to 88 40 to 75 47 to83 WC+TiC 85 +TaC TiC 1 to 50 0.3 to 25 2 to 45 Ø6 to 22 3 to 40 0.9 to 18 TaC 0.5 to 0.4 to 26 1 to 22 0.8 to 24 2 to 20 1.6 to 21 TABLE 29. Additional Material Samples and Their Compositions Lot Coatposition in Weight o No.
Re R95 Co U700 U720 Ni WC TiC TaC VC Mo2C TiN
P80 0 0 14.28 74.15 5.835 5.733 P81 0.736 0 13.904 73.84 5.811 5.709 P82 0.707 6.026 7.3694 74.31 5.847 5.744 P83 0.679 12.82 0 74.83 5.889 5.785 P84 1.45 5.903 7.1237 73.98 5.822 5.719 P85 3.06 5.532 6.7027 73.27 5.766 5.665 P86 1.45 5.903 7.1237 36.99 5.822 5.719 P87 1.063 4.126 5.4174 78.14 5.676 5.576 P88 1.861 7.57 9.1372 69.59 5.974 5.869 P89 1.368 5.572 6.7242 80.31 3.004 3.023 P99 0 0 5.5 15 29 10 9.5 20 P100 4.8 4.65 14.5 28.1 9.7 9.5 19.4 P101 4.8 4.65 14.5 28.1 9.7 9.5 19.4 P102 4.8 10 14.5 28.1 9.7 9.5 19.4 P103 9.6 20 11.25 21.65 7.5 7.1 14.9 P104 7.2 15 12.8 25 8.6 8.1 17.3 P105 15 7.5 13.6 26.35 9.05 8.9 18.1 P106 14.49 0 0 74.415 5.092 6.003 P107 15.101 0 0 66.875 7.076 10.95 P108 11.796 0.7485 0.437 75.727 5.182 6.109 P109 12.303 0.7807 0.456 68.105 7.206 11.15 P110 9.5724 1.4017 0.761 76.812 5.256 6.196 P 111 9.9896 1.4628 0.794 69.124 7.314 11.32 P112 6.9929 2.1369 1.16 78.07 5.342 6.298 P113 14.131 4.3182 2.343 67.447 5.398 6.363 P114 21.418 6.545 3.552 56.602 5.454 6.43 P115 3.8745 3.0258 1.642 79.591 5.446 6.421 P116 7.988 6.2383 3.385 70.155 5.614 6.619 P117 12.363 9.6552 5.24 60.119 5.793 6.829 P118 1.8824 3.5833 1.961 80.561 5.513 6.499 P119 2.8849 5.4917 3.006 76.345 5.632 6.64 P120 5.0264 9.5681 5.237 67.339 5.888 6.941 P121 13.157 0.5708 0 75.078 5.138 6.057 P122 5.294 2.0672 0 81.057 5.316 6.266 Weight %
Re R95 Co U700 U720 Ni. WC TiC TaC VC Mo2C TiN
P123 19.908 5.9798 1.976 60.41 5.382 6.344 P124 20.68 9.9386 2.736 54.464 5.59 6.59 P125 1.5492 3.0246 0.833 82.731 5.444 6.418 P126 8.4621 13.217 3.639 61.723 5.948 7.011 P127 12.191 13.964 3.844 61.702 3.808 4.49 P128 11.906 0.5166 0 86.99 0.604 P129 1.6752 2.0169 1.9524 93.77 0.599 P130 11.97 8.0334 8.085 71.33 0.6 P131 1.4372 3.8162 3.7765 90.39 0.596 P132 6.6223 1.3705 1.3191 90.1 0.605 P133 5.505 1.7196 1.6331 90.55 0.609 P134 11.43 5.0212 4.8443 78.11 0.613 P135 1.644 2.3344 2.571 79.98 3.151 10.32 P136 3.6545 5.1371 5.657 73.439 0 12.11 P137 4.4642 6.3916 7.039 69.776 0 12.33 P138 4.899 6.5757 7.241 69.279 1.435 10.57 P139 6.5381 7.902 8.702 64.651 1.459 10.75 P140 3.0601 5.5324 6.703 73.274 5.766 5.665 P141 2.9261 5.2902 6.409 71.233 3.308 10.83 P142 5.0649 6.1371 7.419 67.113 3.337 10.93 A 13.853 0.2847 0.314 74.887 5.125 5.538 B 2.7327 5.0305 0 81.358 5.488 5.391 C 3.0601 5.5324 6.703 73.274 5.766 5.665 D 1.8803 3.5793 1.988 81.637 5.507 5.41 E 7.7737 9.4819 0 71.578 5.633 5.534 P144 0.6786 12.821 0 74.827 5.889 5.785 P145 0.6437 5.663 0 80.041 3.194 10.46 P146 1.8837 5.3941 0 81.786 5,517 5.42 P147 2.3479 5.1953 0 81.552 5.501 5.404 P148 1.5479 8.462 0 76.038 3.264 10.69 P 14 9 1.6376 15.347 0 68.255 3.453 11.31 J 25.75 2.5 14.5 24.1 8.5 8 16.65 K 11.671 0.4143 0.3935 0 0 86.92 0.605 L 2.6826 5.5683 0 0 0 91.32 0.43 M 3.5669 0 14.235 0 0 81.75 0.452 N 0 7.5039 0 0 0 92.06 0.44 0 12.515 0 0 0 0.2541 86.63 0.601 P 1.7969 0 0 6.9309 90.68 0.597 Q 0 0 0 7.4214 91.98 0.602 s 8.371 0 0 5.3814 85.67 0.579 T 1_6967 0 4.681 0 92.98 0.645 U 3.9002 0 0 3.8684 91.6 0.636 P 15 0 0 0 14.847 84.68 0.469 P151 0 3.2554 11.851 84.38 0.51 Weight %
Re R95 Co U700 U720 Ni WC TiC TaC VC M02C TiN
P152 1.5219 3.225 11.153 83.59 0.505 P153 12.451 1.2899 4.6957 81.09 0.478 P154 2.6486 2.9933 7.6052 54.464 0.509 P155 0 0 11.55 82.731 0.414 P156 1.1019 3.5804 6.2338 61.723 0.671 P157 0 3.761 6.5607 86.24 0.675 P158 0 0 9.9898 88.04 0.512 P 15 9 0.9437 3.0766 5.5161 88.41 0.502 P160 0 3.0946 5.9144 89 0.505 P161 0 0 8.7552 89.5 0.506 P162 2.967 5.6892 0.6379 0.654 89.817 0.2346 P163 0.581 8.1942 0.9297 0.8972 89.156 0.2413 P164 2.16 7.569 0.8669 0.8333 88.331 0.2391 P165 2.801 6.7279 1.976 2.026 86.226 0.2422 P166 2.797 8.3834 1.2603 1.2361 86.082 0.2418 P167 2.789 11.13 0 0 85.84 0.2411 [0081] The following TABLES 30-41 list exemplary cermet compositions with 3 exemplary composition ranges 1, 2, and 3 which may be used for different applications.

-1.34--TABLE 30. Compositions that use Re as a binder for binding TiC+
M02C, or TiN+ Mo2C, or TiC+TiN+ MoZC, or TiC+TiN+Mo2C+WC+TaC+VC+Cr2C3 Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight %
Re Re 3 to 30 9.5 to 65 4 to 27 13 to 60 5 to 25 15 to 58 - TiC 43 to 97 19 to 88 48 to 92 23 to 79 51 to 90 25 to 75 TiC+M02C M02C 0 to 27 0 to 38 0 to 26 0 to 36 0 to 24 0 to 33 Re Re 3 to 30 9 to 63 4 to 27 12 to 58 5 to 25 15 to 56 - TiN 43 to 97 21 to 89 48 to 92 25 to 81 51 to 90 27 to 76 TiN+MoZC MoZC 0 to 27 0 to 36 0 to 26 0 to 34 0 to 24 0 to 31 Re Re 3 to 30 9 to 64 4 to 27 12 to 60 5 to 25 15 to 58 - TiC 0.3 to 0.2 to 84 0.4 to 0.3 to 79 0.5 to 0.35 to TiC+TiN 93.7 91_6 89.5 74 +Mo2C TiN 0.3 to 0.3 to 85 0.4 to 0.4 to 80 0.5 to 0.5 to 76 93.7 91.6 89.5 MoyC 0 to 27 0 to 36 0 to 26 0 to 34 0 to 24 0 to 31 Re Re 3 to 30 6 to 65 4 to 27 9 to 61 5 to 25 11 to 65 TiC 0.3 to 0.1 to 83 0.4 to 0.2 to 78 0.5 to 0.3 to 74 - 93.5 91.3 89.1 TiN 0.3 to 0.15 to 0.4 to 0.2 to 80 0.5 to 0.3 to 76 TiC+TiN 93.5 85 91.3 89=1 +Mo2C MoZC 0 to 28 0 to 25 0 to 26 0 to 25 0 to 24 0 to 24 +WC+TaC wC 0.1 to 0.15 to 0.15 to 0.25 to 0.2 to 0.35 to +VC+Cr2C3 20 39 15 32 12 28 TaC 0.1 to 0.15 to 0_15 to 0.25 to 0.2 to 0.3 to 22 VC 0 to 15 0 to 11 0 to 12 0 to 10 0 to 10 0 to 9 CzZC3 0 to o 15 0 to 16 0 to 12 0 to 14 0 to 10 0 to12 TABLE 31. Compositions that use Ni-based superalloy (NBSA) as a binder for binding TiC+ M02C, or TiN+ MoZC, or TiC+TiN+ Mo2C, or TiC+TiN+MozC+WC+TaC+VC+CrZC3 Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight %
NBSA NBSA 3 to 30 4 to 41 4 to 27 5 to 37 5 to 25 6 to 34 - TiC 43 to 94 30 to 90 48 to 92 35 to 87 51 to 90 37 to 84 TiC+MozC Mo2C 3 to 27 4 to 40 4 to 26 6 to 39 5 to 24 8 to 36 NBSA NBSA 3 to 30 4 to 38 4 to 27 5 to 34 5 to 25 6 to 32 - TiN 43 to 94 32 to 91 48 to 92 37 to 88 51 to 90 40 to 85 TiN+MoZC MozC 3 to 27 4 to 38 4 to 26 6 to 37 5 to 24 7 to 34 NBSA NBSA 3 to 30 4 to 40 4 to 27 5 to 36 5 to 25 6 to 34 - TiC 0.3 to 0.2 to 0.4 to 0.3 to 0.5 to 0.4 to TiC+TiN 93.7 90 91.6 86 89.5 83 +MozC TiN 0.3 to 0.3 to 0.4 to 0.4 to 0.5 to 0.5 to 93.7 91 91.6 88 89.5 85 M02C 3 to 27 4 to 38 4 to 26 6 to 37 5 to 24 8 to 34 NBSA NHSA 3 to 30 2 to 40 4 to 27 4 to 36 5 to 25 5 to 34 TiC 0.3 to 0.15 to 0.4 to 0.2 to 0.5 to 0.3 to 93.3 90 91.3 86 89.3 83 TiN 0.3 to 0.25 to 0.4 to 0.35 to 0.5 to 0.45 to TiC+TiN 93.3 90 91.3 87 89.3 84 +Mo2C M02C 3 to 27 4 to 25 4 to 26 6 to 26 5 to 24 8 to +WC+TaC 25.5 +VC+CrZC3 WC 0.1 to 20 0.25 to 0.15 to 0.4 to 0.2 to 0.5 to TaC 0.1 to 15 0.25 to 0.15 to 0.4 to 0.2 to 0.5 to VC 0 to 15 0 to 14 0 to 12 0 to 12 0 to 10 0 to 10 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 tol3 --13 6 =-TABLE 32. Compositions that use Re and Ni-based superalloy (NBSA) in a binder for binding TiC+ Mo2C, or TiN+ Mo2C, or TiC+TiN+ M02C, or T iC+TiN+Mo2C+WC+TaC+VC+Cr2C3 Material Compositi-on Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight %
(Re+NBSA) Re 0.03 to 0.1 to 64 0.04 to 0.13 to 0.05 to 0.16 to - 29.7 26.73= 60 24.75 57 TiC+TiN NBSA 0.03 to 0.03 to 0.04 to 0.05 to 0.05 to 0.06 to +M02C 29.7 40 26.73 36 24.75 34 TiC 0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 84 TiN 0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 M02C 3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 (Re+NBSA) Re 0.03 to 0.06 to 0.04 to 0.1 to 60 0.05 to 0.12 to 29.7 64 26.73 24.75 57 TiC+TiN NBSA 0.03 to 0.02 to 0.04 to 0.03 to 0.05 to 0.04 to +M02C 29.7 40 26.73 36 24.75 34 +WC+TaC TiC 0.3 to 0.15 to .40 to 0.2 to 86 0.5 to 0.3 to 83 +VC+CrZC3 93.5 89 91.3 89.1 TiN 0.3 to 0.15 to .40 to 0.2 to 87 0.5 to 0.3 to 84 93.5 90 91.3 89.1 M02C 3 to 28 3 to 26 4 to 26 4 to 26 5 to 24 5 to 25.5 WC 0.1 to 0.15 to 0.15 to 0.25 to 0.2 to 0.35 to TaC 0.1 to 0.15 to 0.15 to 0.25 to 0.2 to 0.3 to 24 VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13 TABLE 33. Compositions that use Re and Ni in a binder for binding TiC+ MoZC, or TiN+ MoZC, or TiC+TiN+ MoaC, or T iC+TiN+Mo2C+WC+TaC+VC+Cr2C3 Material Composition Range Composition Range 2 Composition Range 3 Volume Weight % Volume % Weight % Volume % Weight ~
(Re+Ni) Re 0.03 to 0.1 to 64 0.04 to 0.13 to 60 0.05 to 0.16 to - 29.7 26.73 24.75 57 TiC+TiN Ni 0.03 to 0.04 to 0.04 to 0.05 to 38 0.05 to 0.06 to +M02C 29.7 42 26.73 24.75 36 TiC 0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 83 TiN 0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 M02C 3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 (Re+Ni) Re 0.03 to 0.06 to 0.04 to 0.1 to 60 0.05 to 0.12 to - 29.7 64 26.73 24.75 57 TiC+TiN Ni 0.03 to 0.03 to 0.04 to 0.04 to 39 0.05 to 0.05 to +M02C 29.7 42 26.73 24.75 36 +WC+TaC TiC 0.3 to 0.15 to .40 to 0.2 to 85 0.5 to 0.3 to +VC+Cr2C3 93.5 89 91.3 89.1 82 TiN 0.3 to 0.15 to .40 to 0.2 to 87 0.5 to 0.3 to 93.5 90 91.3 89.1 83 M02C 3 to 28 3 to 26 4 to 26 4 to 26 5 to 24 5 to 25.5 WC 0.1 to 0.15 to 0.15 to 0.25 to 35 0.2 to 12 0.35 to TaC 0.1 to 0.15 to 0.15 to 0.25 to 28 0.2 to 10 0.3 to VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to13 TABLE 34. Compositions that use Re and Co in a binder for binding TiC+ MoZC, or TiN+ MozC, or TiC+TiN+ M02C, or TiC+TiN+MozC+WC+TaC+VC+Cr2C3 Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight ~ Volume % Weight % Volume % Weight %
Re+Co Re 0.03 to 0.1 to 64 0.04 to 0.13 to 0.05 to 0.16 to 29.7 26.73 60 24.75 57 - Co 0.03 to 0.04 to 0.04 to. 0.05 to 0.05 to 0.06 to TiC+TiN 29.7 43 26.73 39 24.75 36 +M02C TiC 0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 83 TiN 0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 M02C 3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 Re+Co Re 1 0.03 to 0.06 to 0.04 to 0.1 to 0.05 to 0.12 to 29.7 64 26.73 60 24.75 57 Co 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 29.7 43 26.73 39 24.75 36 TiC+TiN TiC 0.3 to 0.15 to .40 to 0.2 to 0.5 to 0.3 to +M02C 93.5 89 91.3 85 89.1 82 +WC+TaC TiN 0.3 to 0.15 to .40 to 0.2 to 0.5 to 0.3 to +VC+Cr2C3 93.5 90 91.3 87 89.1 83 MoZC 3 to 28 3 to 26 4 to 26 4 to 26 5 to 24 S to 25.5 WC 0.1 to 0.15 to 0.15 to 0.25 to 0.2 to 12 0.35 to TaC 0.1 to 0.15 to 0.15 to 0.25 to 0.2 to 10 0.3 to VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to13 TABLE 35. Compositions that use Ni-based superalloy (NBSA) and Co in a binder for binding TiC+ Mo2C, or Ti.N+ MoZC, or TiC+TiN+ Mo2C, or TiC+TiN+Mo2C+WC+TaC+VC+Cr2C3 Material Composition Range 1 Composition Range 2 Composition Range Volume $ Weight % Volume % Weight % Volume $ Weight $
(NBSA+Co) NBSA 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to - 29.7 40 26.73 37 24.75 34 TiC+TiN Co 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to +M02C 29.7 43 26.73 39 24.75 37 TiC 0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 84 TiN 0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 86 M02C 3 to 27 4 to 38 4 to 26 6 to 37 5 to 24 7 to 34 (NBSA+Co) NBSA 0.03 to 0.02 to 0.04 to 0.03 to 0.05 to 0.05 to - 29.7 40 26.73 36 24.75 34 TiC+TiN Co 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to +M02C 29.7 43 26.73 39 24.75 36 +WC+TaC TiC 0.3 to 0.15 to .40 to 0.2 to 0.5 to 0.3 to +VC+Cr2C3 93.5 89 91.3 86 89.1 83 TiN 0.3 to 0.25 to .40 to 0.35 to 0.5 to 0.45 to 93.5 90 91.3 87 89.1 84 M02C 3 to 28 4 to 26 4 to 26 6 to 26 5 to 24 7 to 25.5 WC 0.1 to 20 0.25 to 0.15 to 0.38 to 0.2 to 12 0.5 to TaC 0.1 to 15 0.23 to 0.15 to 0.35 to 0.2 to 10 0.47 to VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to13 TABLE 36. Compositions that use Ni-based superalloy (NBSA) arid Ni in a binder for binding TiC+ M02C, or TiN+ Mo2C, or TiC+TiN+ Mo2C, or TiC+TiN+Mo2C+WC+TaC+VC+CrZC3 Material Composition Range 1 Composition Range Composition Range 3 Volume % Weight ~ Volume % Weight % Volume % Weight %
(NBSA+Ni) NBSA 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to - 29.7 40 26.73 37 24.75 34 TiC+TiN Ni 0.03 to 0.04 to 0.04 to 0.055 to 0.05 to 0.07 to +M02C 29.7 43 26.73 39 24.75 36 TiC 0 to 94 0 to 90 0 to 92 0 to 88 0 to 90 0 to 85 TiN 0 to 94 0 to 91 0 to 92 0 to 89 0 to 90 0 to 86 M02C 3 to 27 4 to 38 4 to 26 6 to 37 5 to 24 7 to 34 (NBSA+Ni) NBSA 0.03 to 0.02 to 0.04 to 0.035 to 0.05 to 0.05 to - 29.7 40 26.73 36 24.75 34 TiC+TiN Ni 0.03 to 0.03 to 0.04 to 0_04 to 0.05 to 0.05 to +M02C 29.7 43 26.73 39 24.75 36 +WC+TaC TiC 0_3 to 0.15 to .40 to 0.2 to 0.5 to 0.3 to +VC+Cr2C3 93.5 89 91.3 86 89.1 83 TiN 0.3 to 0.25 to .40 to 0.35 to 0.5 to 0.45 to 93.5 90 91.3 87 89.1 84 M02C 3 to 28 4 to 26 4 to 26 6 to 26 5 to 24 7 to 25.5 WC 0.1 to 0.25 to 0.15 to 0.38 to 0.2 to 12 0.5 to TaC 0.1 to 0.23 to 0.15 to 0.35 to 0.2 to 10 0.47 to VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to13 TABLE 37. Compositions that use Re, Co, and Ni-based superalloy (NBSA) in a binder for binding TiC and MoaC, or TiN and Mo2C, or TiC, TiN, and Mo2C, or TiC, TiN, Mo2C, WC, TaC, VC, and Cr2C3 Material Composition Range Composition Range 2 Composition Range 3 Volume Weight % Volume % Weight % Volume % Weight $
(Re+NBSA Re 0.03 to 0.1 to 0.04 to 0.13 to 60 0.05 to 0.16 to 57 +Co) 29.4 64 26.46 24.5 - NBSA 0.03 to 0.035 to 0.04 to 0.045 to 0.05 to 0.055 to TiC+TiN 29.4 40 26.46 36 24.5 34 +M02C Co 0.03 to 0.04 to 0.04 to 0.05 to 39 0.05 to 0.06 to 36 29.4 42 26.46 24.5 TiC 0 to 94 0 to 90 0 to 92 0 to 88 0 to 90 0 to 84 TiN 0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 Mo2C 3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 (Re+NBSA Re 0.03 to 0.06 to 0.04 to 0.1 to 60 0.05 to 0.13 to 57 +Co) 29.4 63 26.46 24.5 - NBSA 0.03 to 0.02 to 0.04 to 0.03 to 36 0.05 to 0.04 to 33 29.4 39 26.46 24.5 TiC+TiN Co 0.03 to 0.03 to 0.04 to 0.04 to 39 0.05 to 0.05 to 36 +M02C 29.4 42 26.46= 24.5 +WC+TaC TiC 0.3 to 0.15 to 0.4 to 0.2 to 86 0.5 to 0.3 to 83 +VC+Cr2C3 93.5 89 91.3 89.1 TiN 0.3 to 0.15 to 0.4 to 0.2 to 87 0.5 to 0.3 to 84 93.5 90 91.3 89.1 M02C 3 to 28 3 to 26 4 to 26 4 to 26 5 to 24 5 to 25.5 WC 0.1 to 0.15 to 0.15 to 0.25 to 35 0.2 to 12 0.35 to 29 TaC 0.1 to 0.15 to 0.15 to 0.25 to 28 0.2 to 10 0.3 to 24 VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13 TABLE 38. Compositions that use Re, Ni, and Ni-based superalloy (NBSA) in a binder for binding TiC+ Mo2C, or TiN+ M02C, or TiC+TiN+
MoZC, or TiC+TiN+MozC+WC+TaC+VC+Cr2C3 Material Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight 96 Volume % Weight % Volume % Weight %
(Re+NBSA Re 0.03 to 0.1 to 63 0.04 to 0.13 to 0.05 to 0.16 to +Ni) 29.4 26.46 60 24.5 57 - NBSA 0.03 to 0.035 to 0.04 to 0.045 to 0.05 to 0.055 to TiC+TiN 29.4 40 26.46 36 24.5 33 +MOZC Ni 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 29.4 42 26.46= 38 24.5 36 TiC 0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 84 TiN 0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 M02C 3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 (Re+NBSA Re 0.03 to 0.06 to 0.04 to 0.1 to 60 0.05 to 0.13 to +Ni) 29.4 63 26.46 24.5 57 - NBSA 0.03 to 0.02 to 0.04 to 0.03 to 0.05 to 0.04 to TiC+TiN 29.4 39 26.46 36 24.5 33 +M02C Ni 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to +WC+TaC 29.4 42 26.46 38 24.5 36 +VC+CrZC3 TiC 0.3 to 0.15 to 0.4 to 0.2 to 86 0.5 to 0.3 to 83 93.5 89 91.3 89.1 TiN 0.3 to 0.15 to 0.4 to 0.2 to 87 0.5 to 0.3 to 84 93.5 90 91.3 = 89.1 B Mo2C 3 to 28 3 to 26 4 to 26 4 to 26 5 to 24 5 to 25.5 WC 0.1 to 0.15 to 0.15 to 0.25 to 0.2 to 0.35 to TaC 0.1 to 0.15 to 0.15 to 0.25 to 0.2 to 0.3 to 24 VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13 TABLE 39. Compositions that use Re, Ni,'and Co in a binder for binding TiC+ Mo2C, or Ti.N+ MozC, or TiC+TiN+ Mo2C, or TiC+T iN+Mo2C+WC+TaC+VC+Cr2C3 Material Composition Range Composition Range 2 Composition Range 3 Volume Weight % Volume ~ Weight % Volume ~ Weight %
(Re+Ni Re 0.03 to 0.1 to 63 0.04 to 0.13 to 0.05 to 0.16 to +Co) 29.4 26.46 60 24.5 57 - Ni 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to TiC+TiN 29.4 42 26.46 38 24.5 36 +M02C Co 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 29.4 42 26.46 39 24.5 36 TiC 0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 83 TiN 0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 M02C 3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 (Re+Ni Re 0.03 to 0.06 to 0.04 to 0.1 to 0.05 to 0.13 to +Co) 29.4 63 26.46 60 24.5 57 - Ni 0.03 to 0.025 to 0.04 to 0.04 to 0.05 to 0.05 to 29.4 42 26.46 38 24.5 36 TiC+TiN Co 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to +M02C 29.4 42 26.46 39 24.5 36 +WC+TaC TiC 0.3 to 0.15 to 0.4 to 0.2 to 0.5 to 0.3 to 82 +VC+CrZCJ 93.5 89 91.3 85 89.1 TiN 0.3 to 0.15 to 0.4 to 0.2 to 0.5 to 0.3 to 83 93.5 90 91.3 87 89.1 M02C 3 to 28 3 to 26 4 to 26 4 to 26 5 to 24 5 to 25.5 WC 0.1 to 0_15 to 0.15 to 0.25 to 0.2 to 12 0.35 to TaC 0.1 to 0.15 to 0.15 to 0.25 to 0.2 to 10 0.3 to 24 VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13 TABLE 40. Compositions that use Co, Ni, and Ni-based superalloy (NBSA) in a binder for binding TiC+ MoZC, or TiN+ Mo2C, or TiC+TiN+
Mo2C, or TiC+TiN+Mo2C+WC+TaC+VC+CrZC3 Material Composition Range Composition Range 2 Composition Range 3 Volvme % Weight Volume $ weight % Volume ~ Weight %
$
(NBSA+Ni NBSA 0.03 to 0.04 to 0.04 to 0.5 to 36 0.05 to 0.06 to 34 +Co) 29.4 40 26.46 24.5 - Ni 0.03 to 0.04 to 0.04 to 0.055 to 0.05 to 0.07 to 37 TiC+TIN 29.4 42 26.46 39 24.5 +M02C Co 0.03 to 0.04 to 0.04 to 0.055 to 0.05 to 0.07 to 36 29.4 43 26.46 39 24.5 TiC 0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 84 TiN 0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 M02C 3 to 27 4 to 38 4 to 26 5 to 37 5 to 24 7 to 34 (NBSA+Ni NBSA 0.03 to 0.025 0.04 to 0.035 to 0.05 to 0.05 to 33 +Co) 29.4 to 40 26.46 36 24.5 - Ni 0.03 to 0.025 0.04 to 0.04 to 0.05 to 0.05 to 36 29.4 to 42 26.46 38 24.5 TiC+Ti.N Co 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 36 +M02C 29.4 42 26.46 39 24.5 +WC+TaC TiC 0.3 to 0.15 to 0.4 to 0.2 to 86 0.5 to 0.3 to 83 +VC+Cr2C3 93.5 89 91.3 89.1 TiN 0.3 to 0.25 to 0.4 to 0_35 to 0.5 to 0.45 to 84 93.5 90 91.3 87 89.1 Mo2C 3 to 28 4 to 26 4 to 26 6 to 26 5 to 24 7 to 25.5 wC 0.1 to 0.25 to 0.15 to 0.35 to 0.2 to 12 0. 5 to 29 TaC 0.1 to 0.25 to 0.15 to 0.35 to 0.2 to 10 0.45 to 24 VC 0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr2C3 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13 TABLE 41. Compositions that use Re, Ni, Co, and Ni-based superalloy (NBSA) in a binder for binding TiC+ Mo2C, or TiN+ MoZC, or TiC+TiN+
Mo2C, or TiC+TiN+Mo2C+WC+TaC+VC+Cr2C3 Material Cosnposition Composition Coniposition Range 1 Range 2 Range 3 Volume Weight Volume Weight Volume Weight (Re+NBSA+Ni Re 0.03 to 0.1 to 0.04 to 0.13 0.05 to 0.16 +Co) 29.1 63 26.19 to 59 24.25 to 57 - NBSA 0.03 to 0.035 0.04 to 0.45 0.05 to 0.055 TiC+TiN 29.1 to 39 26.19 to 36 24.25 to 33 +M02C Ni 0.03 to 0.04 0.04 to 0_05 0.05 to 0.06 29.1 to 42 26.19 to 38 24.25 to 36 Co 0.03 to 0.04 0.04 to 0.5 to 0.05 to 0.06 29.1 to 42 26.19 38 24.25 to 36 TiC 0 to 94 0 to 0 to 92 0 to 0 to 90 0 to TiN 0 to 94 0 to 0 to 92 0 to 0 to 90 0 to MozC 3 to 27 3 to 4 to 26 4 to 5 to 24 5 to (Re+NBSA+Ni Re 0.03 to 0.06 0.04 to 0.1 to 0.05 to 0.12 +Co) 29.1 to 63 26.19 59 24.25 to 56 - NBSA 0.03 to 0.02 0.04 to 0.03 0.05 to 0.04 29.1 to 39 26.19 to 35 24.25 to 33 TiC+TiN Ni 0.03 to 0.025 0.04=to 0.035 0.05 to 0.05 +M02C 29.1 to 42 26.19 to 38 24.25 to 35 +WC+TaC Co 0.03 to 0.025 0.04 to 0.03 0.05 to 0.05 +VC+Cr2C3 29.1 to 42 26.19 to 38 24_25 to 36 TiC 0.3 to 0.15 0.4 to 0.2 to 0.5 to 0.3 to 93.5 to 89 91.3 86 89.1 83 TiN 0.3 to 0.15 0.4 to 0.2 to 0.5 to 0.3 to 93.5 to 90 91.3 87 89.1 84 M02C 3 to 28 3 to 4 to 26 4 to 5 to 24 5 to 26 26 25.5 WC 0.1 to 0.15 0.15 to 0.25 0.2 to 0.3 to 20 to 42 15 to 35 12 29 TaC 0.1 to 0.15 0.15 to 0.2 to 0.2 to 0.3 to 15 to 33 12 28 10 24 VC 0 to 15 0 to 0 to 12 0 to 0 to 10 0 to CrZC3 0 to 15 0 to 0 to 12 0 to 0 to 10 0 to [0082] The following TABLES 42-51 list additional examples of various compositions with 3 exemplary composition ranges 1, 2, and 3 which may be used for different applications. Similar to some compositions described above, some compositions in TABLES 42-51 may be particularly useful for applications at high temperatures as indicated in the last row under "estimated melting points."
[0083] As described above, binder matrix materials with rhenium, a nickel-based superalloy or a combination of both can enhance material performance at high temperatures.
Tungsten is typically used as a constituent element in various hard particles such as carbides, nitrides, carbonitrides, borides, and silicides. When used as a binder matrix material, either alone or in combination with other metals, tungsten can significantly raise the melting point of the final hardmetal materials to the range of about 2500 to about 3500 C. Hence, hardmetals using W-based binder matrix materials can be used in applications at high temperatures that may not be possible with other materials. Notably, certain compositions that use a binder matrix based on tungsten (W) shown in TABLES 43-48 show expected high melting points around 3500 C.
[0084] For the compositions made of nitrides bound by rhenium and cobalt in TABLE 47, each nitride may be substituted by a combination of a nitride and carbide as the hard particle material. A material under this design includes hard particles comprising at least one nitride from nitrides of IVB
and VB columns in the periodic table and one carbide from carbides of IVB, VB and VIB columns in the periodic table, and a binder matrix that binds the hard particles and comprises rhenium and cobalt.

TABLE 42. Re bound a Boride from Borides of TVb, Vb, & VIb or a Silicide from Silicides of IVb, Vb & VIb osition Range Estimated Coatposition Range Composition Range C7=, 1 2 3 Melting Weight po int, C
Volume $ Weight Volume % Weight V5 to 30 Re Re 3 to 40 12.5 to 4 to 35 16 to 20 to 2700 to Bound 76 71 67 3000 Ti.B2 TiBZ 60 to 97 24 to 65 to 96 29 to 70 to 95 33 to 87.5 84 80 Re Re 3 to 40 9.5 to 4 to 35 12.5 to 5 to 30 15 to 2800 to Bound 70 65 60 3000 ZrBZ ZrB2 60 to 97 30 to 65 to 96 35 to 70 to 95 40 to 90.5 87.5 85 Re Re 3 to 40 5.5 to 4 to 35 7 to 50 5 to 30 9 to 3000 to Bound 55.5 44.5 3200 HtB2 HfB2 60 to 97 44.5 to 65 to 96 50 to 70 to 95 55.5 to 94.5 93 91 Re Re 3 to 40 11 to 4 to 35 14.5 to 5 to 30 18 to 2000 to Bound 73 69 64 2500 VB2 VB2 60 to 97 27 to 65 to 96 31 to 70 to 95 36 to 89 85.5 82 Re Re 3 to 40 8 to 66 4 to 35 11 to 5 to 30 13 to 2800 to Bound 61 55.5 3100 NbB2 A7bB2 60 to 97 34 to 65 to 96 39 to 70 to 95 44.5 to Re Re 3 to 40 5 to 53 4 to 35 6.5 to 5 to 30 8 to 42 3000 to Bound 47 3200 TaB2 TaB2 60 to 97 47 to 65 to 96 53 to 70 to 95 58 to 95 93.5 92 Re Re 3 to 40 9.5 to 4 to 35 12.5 to 5 to 30 15 to 1800 to Bound 69.5 65 60 2200 Cr3BZ Cr3Bz 60 to 97 30.5 to 65 to 96 35 to 70 to 95 40 to 90.5 87.5 85 Re Re 3 to 40 7.5 to 4 to 35 10 to 5 to 30 12.5 to 2000 to Bound 64 59 54 2400 MoB2 MoB2 60'to 97 36 to 65 to 96 41 to 70 to 95 46 to 92.5 90 87_5 Re Re 3 to 40 4 to 47 4 to 35 5 to 41 5 to 30 6.5 to 2700 to Bound 36 3000 WB WB 60 to 97 53 to 65 to 96 59 to 70 to 95 64 to 96 95 93.5.
Re Re 3 to 40 4 to 47 4 to 35 5 to 41 5 to 30 6.5 to 2600 to Bound 36 2900 WZB WZB 60 to 97 53 to 65 to 96 59 to 70 to 95 64 to 96 95 93.5 Re Re 3 to 40 13 to 4 to 35 17 to 5 to 30 20 to 2000 to Bound 77 72 68 2400 Ti5Si3 Ti5Si3 60 to 97 23 to 65 to 96 28 to 70 to 95 32 to Re Re 3 to 40 10 to 4 to 35 14 to 5 to 30 17 to 2100 to Bound 72 67 62 2500 Zr6Si5 Zr6Si5 60 to 97 28 to 65 to 96 33 to 70 to 95 38 to Re Re 3 to 40 9 to 69 4 to 35 12 to 5 to 30 15 to 1800 to Bound 64 59 2200 NbSi2 NbSi2 60 to 97 31 to 65 to 96 36 to 70 to 95 41 to Re Re 3 to 40 7 to 62 4 to 35 9 to 57 5 to 30 12 to 2200 to Bound 51 2600 TaSi2 TaSi2 60 to 97 38 to 65 to 96 43 to 70 to 95 49 to Re Re 3 to 40 9 to 69 4 to 35 12 to 5 to 30 15 to 1800 to Bound 64 59 2200 -~148~

MoSi2 60 to 97 31 to 65 to 96 36 to 70 to 95 41 to Re Re 3 to 40 6 to 60 4 to 35 9 to 55 5 to 30 11 to 1800 to Bound 49 2200 WSi2 Wsi2 60 to 97 40 to 65 to 96 45 to 70 to 95 51 to TABLE 43_ W bound a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb.

Coniposition Range 1 Corroosition Range 2 Cornposition Range 3 Estimated VoZume $ Weight % Volume % Weight % Volume ~ Weight $ Melting Point, C
W W 3 to 40 11 to 72 4 to 35 25.02 to 5 to 30 25.02 to 3000 to Bound 70 65 3300 TiC TiC 60 to 97 28 to 89 65 to 96 30'to 70 to 95 35 to 74.98 74.98 W W 3 to 40 8 to 66 4 to 35 11 to 61 5 to 30 13 to 56 3200 to Bound ZrC 60 to 97 34 to 92 65 to 96 39 to 89 70 to 95 44 to 87 3500 ZrC
W W 3 to 40 4 to 50 4 to 35 6 to 45 5 to 30 7 to 40 3300 to Bound HfC 60 to 97 50 to 96 65 to 96 55 to 64 70 to 95 60 to 93 3500 HfC
W W 3 to 40 10 to 70 4 to 35 13 to 65 5 to 30 16 to 60 2700 to Bound VC 60 to 97 30 to 90 65 to 96 35 to 87 70 to 95 40 to 84 3300 VC
W W 3 to 40 7 to 62 4 to 35 9 to 57 5 to 30 11 to 51 3000 to Bound NbC 60 to 97 38 to 93 65 to 96 43 to 91 70 to 95 49 to 89 3500 NbC
W W 3 to 40 4 to 47 4 to 35 5 to 42 5 to 30 7 to 36 3300 to Bound TaC 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 64 to 93 3500 TaC
W W 3to 40 8 to 66 4 to 35 11 to 61 5 to 30 13 to 55 1700 to Bound Cr2C3 60 to 97 34 to 92 65 to 96 39 to 89 70 to 95 45 to 87 2100 Cr2C3 W W 3 to 40 6 to 59 4 to 35 8 to 53 5 to 30 10 to 48 2400 to Bound M02C 60 to 97 41 to 94 65 to 96 47 to 93 70 to 95 52 to 90 2600 w w 3 to 40 4 to 45 4 to 35 5 to 40 5 to 30 6 to 35 2800 to Bound WC 60 to 97 55 to 96 65 to 96 60 to 95 70 to 95 65 to 94 3000 WC
W D+i 3 to 40 11 to 72 4 to 35 14 to 68 5 to 30 16 to 60 2800 to Bound TiN 60 to 97 28 to 89 65 to 96 32 to 86 70 to 95 40 to 84 3300 TiN
W W 3 to 40 8 to 64 4 to 35 10 to 59 5 to 30 12 to 53 2900 to Bound ZrN 60 to 97 36 to 92 65 to 96 41 to 90 70 to 95 47 to 88 3300 ZrN
W W 3 to 40 4 to 48 4 to 35 6 to 43 5 to 30 7 to 37 3200 to Bound HfN 60 to 97 52 to 96 65 to 96 57 to 94 70 to 95 63 to 93 3500 HfN
W W 3 to 40 9 to 68 4 to 35 12 to 63 5 to 30 15 to 58 2000 to Bound VN 60 to 97 32 to 91 65 to 96 37 to 88 70 to 95 42 to 85 2400 VN
W W 3 to 40 8 to 64 4 to 35 10 to 59 5 to 30 12 to 53 2200 to Bound NbN 60 to 97 36 to 92 65 to 96 41 to 90 70 to 95 47 to 88 2600 = NbN
W W 3 to 40 4 to 47 4 to 35 5 to 42 5 to 30 7 to 37 3000 to Bound TaN 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 63 to 93 3500 TaN

TABLE 44_ W bound a Boride from Borides of 2Vb, Vb, & VIb or a Silicide from Silicides of IVb, Vb & Vib Composition Composition Range Composition Range Estimated Range 1 2 3 Melting Volume Weight Volume Weight VoJ.ume Weight Point, C
%_ __ % % % % %
w w 3 to 40 12 to 4 to 35 15 to 5 to 30 18 to 2700 to Bound 74 70 65 3000 TiB2 TiB2 60 to 26 to 65 to 30 to 70 to 35 to W W 3 to 40 9 to 68 4 to 35 12 to 5 to 30 14 to 2800 to Bound 63 58 3000 ZrB2 ZrB2 60 to 32 to 65 to 37 to 70 to 42 to W W 3 to 40 5 to 54 4 to 35 7 to 48 5 to 30 8 to 42 3000 to Bound HfB2 60 to 46 to 65 to 52 to 70 to 58 to 3400 HfB2 97 95 96 93 95 92 W W 3 to 40 10 to 4 to 35 14 to 5 to 30 17 to 2000 to Bound 72 67 62 2500 VBZ VBz 60 to 28 to 65 to 33 to 70 to 38 to W W 3 to 40 8 to 64 4 to 35 10 to 5 to 30 12 to 2900 to Bound 59 53 3400 NbBZ NbB2 60 to 36 to 65 to 41 to 70 to 47 to W W 3 to 40 5 to 51 4 to 35 6 to 45 5 to 30 7 to 40 3100 to Bound TaB2 60 to 49 to 65 to 55 to 70 to 60 to 3400 TaB2 97 95 96 94 95 93 w W 3 to 40 9 to 68 4 to 35 12 to 5 to 30 14 to 1800 to Bound 63 58 2200 Cr3B2 Cr3B2 60 to 32 to 65 to 37 to 70 to 42 to w W 3 to 40 7 to 62 4 to 35 9 to 57 5 to 30 12 to 2000 to Bound 52 2400 MoBZ MoB2 60 to 38 to 65 to 43 to 70 to 48 to w w 3 to 40 4 to 45 4 to 35 5 to 39 5 to 30 6 to 34 2700 to Bound WB 60 to 55 to 65 to 61 to 70 to 66 to 3000 W W 3 to 40 3 to 44 4 to 35 5 to 38 5 to 30 6 to 33 2600 to Bound W2B 60 to 56 to 65 to 62 to 70 to 67 to 2900 WzB 97 97 96 95 95 94 w W 3 to 40 12 to 4 to 35 16 to 5 to 30 19 to 2000 to Bound 75 71 66 2400 Ti5Si3 Ti5Si3 60 to 25 to 65 to 29 to 70 to 34 to w w 3 to 40 10 to 4 to 35 13 to 5 to 30 16 to 2100 to Bound 70 65 60 2500 Zr6Si5 Zr6Si5 60 to 30 to 65 to 35 to 70 to 40 to W W 3 to 40 9 to 67 4 to 35 11 to 5 to 30 14 to 1800 to Bound 62 57 2200 NbSi2 NbSiz 60 to 33 to 65 to 38 to 70 to 43 to W W 3 to 40 7 to 60 4 to 35 9 to 55 5 to 30 11 to 2200 to Bound 49 2600 TaSi2 TaSi2 60 to 40 to 65 to 45 to 70 to 51 to W W 3 to 40 9 to 67 4 to 35 11 to 5 to 30 14 to 1800 to Bound 62 57 2200 MoSi2 MoSi2 60 to 31 to 65 to 38 to 70 to 43 to w W 3 to 40 6 to 58 4 to 35 8 to 53 5 to 30 10 to 1800 to Bound 47 2200 WSi2 WSi2 60 to 42 to 65 to 47 to 70 to 43 to TABLE 45. Re and W (Re+W) bound a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 1%Re + 99% W to 99% Re + 1%W.

Coxnposition Range 1 Cosnposition Range 2 Conposition Range 3 Estimated Volume ~ Weight ~ Volume $ Weight % Volume % Weight $ Melting Point, C
Re +W Re 0.03 to 0.12 to 0.04 to 0.15 to 0.05 to 0.19 to 2900 Bound 39.6 73 34.7 69 29.7 64 to TiC W 0.03 to 0.1 to 72 0.04 to 0.14 to 0.05 to 0.17 to 3300 39.6 34.7 67 29.7 62 TiC 60 to 97 26 to 89 65 to 96 30 to 86 70 to 95 35 to 83 Re + Re 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.15 to 3000 w 39.6 67 34.7 63 29.7 57 to Bound W 0.03 to 0.08 to 0.04 to 0.11 to 0.05 to 0.13 to 3400 ZrC 39.6 66 34.7 61 29.7 55 ZrC 60 to 97 32 to 92 65 to 96 37 to 89 70 to 95 42 to 87 Re +W Re 0.03 to 0.05 to 0.04 to 0.07 to 0.05 to 0.08 to 3100 Bound 39.6 52 34.7 47 29.7 41 to HfC W 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.07 to 3500 39.6 50 34.7 45 29.7 39 HfC 60 to 97 48 to 95 65 to 96 53 to 94 70 to 95 58 to 93 Re +W Re 0.03 to 0.11 to 0.14 to 0.15 to 0.17 to 0.19 to 2700 Bound 39.6 71 67 67.0 62 61.8 to VC W 0.03 to 0.1 to 69 0.13 to 0.06 to 0.15 to 0.07 to 3000 39.6 65 46.3 60 40.8 VC 60 to 97 28 to 90 33 to 87 32.8 to 70 to 95 38 to 84 93.5 Re + Re 0.03 to 0.08 to 0.04 to 0.1 to 0.05 to 0.13 to 3200 W 39.6 64 34.7 59 29.7 53 to Bound W 0.03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.11 to 3500 NbC 39.6 56 34.7 56 29.7 51 NbC 60 to 97 36 to 93 65 to 96 41 to 91 70 to 95 ' 47 to 88 Re + Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 3100 w 39.6 49 34.7 43 29.7 38 to Bound W 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to 3500 TaC 39.6 47 34.7 41 29.7 36 TaC 60 to 97 51 to 96 65 to 96 56 to 95 70 to 95 62 to 93 Re + Re 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.14 to 1700 W 39.6 67 34.7 62 29.7 57 to Bound w 0.03 to 0.08 to 0.04 to 0.11 to 0.05 to 0.13 to 1900 39.6 65 34.7 60 29.7 55 Cr2C3 Cr2C3 60 to 97 32 to 92 65 to 96 37 to 89 70 to 95 43 to 87 Re + Re 0.03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.11 to 2400 W 39.6 60 34.7 55 29.7 49 to Bound W 0.03 to 0.06 to 0.04 to 0.08 to 0.05 to 0.1 to 47 2600 M02C 39.6 58 34.7 53 29.7 M02C 60 to 97 39 to 94 65 to 96 45 to 92 70 to 95 50 to 90 Re + Re 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to 2700 w 39.6 47 34.7 42 29.7 36 to Bound W 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 2900 WC 39.6 45 34.7 40 29.7 34 WC 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 63 to 94 Re + Re 0.03 to 0.1 to 71 0.04 to 0.14 to 0.05 to 0.17 to 2900 w 39.6 34_7 67 29.7 62 to Bound W 0.03 to 0.1 to 70 0.04 to 0.13 to 0.05 to 0.16 to 3200 TiN 39.6 34.7 65 29.7 60 TiN 60 to 97 28 to 90 65 to 96 32 to 87 70 to 95 38 to 84 Re + Re 0.03 to 0.08 to 0.04 to 0.11 to 0.05 to 0.13 to 2900 w 39.6 65 34.7 60 29.7 55 to Bound W 0.03 to 0.08 to 0.04 to 0.1 to 0.05 to 0.12 to 3200 ZrN 39.6 63 34.7 58 29.7 53 ZrN 60 to 97 34 to 92 65 to 96 39 to 90 70 to 95 45 to 88 Re + Re 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.08 to 3100 W 39.6 50 34.7 45 29.7 39 to "

Bound W 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 3400 HfN 39.6 48 34.7 43 29.7 37 HfN 60 to 97 50 to 96 65 to 96 55 to 95 70 to 95 61 to 93 Re + Re 0.03 to 0.1 to 69 0.04 to 0.13 to 0.05 to 0.16 to 2100 w 39.6 34.7 65 29.7 59 to Bound W 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.14 to 2300 VN 39.6 67 34.7 63 29.7 57 VN 60 to 97 30 to 91 65 to 96 35 to 88 70 to 95 40 to 86 Re + Re 0.03 to 0.08 to 0.04 to 0.11 to 0.05 to 0_13 to 2300 w 39.6 65 34.7 60 29.7 55 to Bound W 0.03 to 0.08 to 0.04 to 0.1 to 0.05 to 0.12 to 2500 NbN 39.6 63 34.7 58 29.7 53 NbN 60 to 97 35 to 92 65 to 96 39 to 90 70 to 95 45 to 88 Re + Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 2900 W 39.6 49 34.7 44 29.7 38 to Bound W 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to 3400 TaN 39.6 47 34.7 42 29.7 36 FTaN 60 to 97 51 to 96 65 to 96 56 to 95 70 to 95 61 to 93 TABLE 46. Re and W (Re+W) bound a boride from borides of IVb, Vb, & V2b or a silicide from silicides of IVb & Vb. The range of Binder is from 1%Re + 99% W to 99% Re + 1%W

Composition Range 1 Composition Range 2 CoxtVosition Range 3 Estintated Volume $ Weight $ Volume $ Weight ~ Volume ~ Weight % Melting Point, C
Re +W Re 0.03 to 0.13 to 0.04 to 0.16 to 0.05 to 0.2 to 2900 Bound 39.6 75 34.7 71 29.7 66 to TiB2 W 0.03 to 0.12 to 0.04 to 0.15 to 0.05 to 0.18 to 3100 39.6 73 34_7 69 29.7 64 TiB2 60 to 97 24 to 88 65 to 96 29 to 85 70 to 95 33 to 82 Re + W Re 0.03 to 0.1 to 69 0.04 to 0.13 to 0.05 to 0.16 to 2900 Bound 39.6 34.7 64 29.7 59 to ZrB2 W 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.14 to 3200 39.6 67 34.7 63 29.7 57 ZrB2 60 to 97 30 to 91 65 to 96 35=to 88 70 to 95 40 to 86 Re +W Re 0.03 to 0.05 to 0.04 to 0.07 to 0.05 to 0.09 to 3100 Bound 39.6 54 34.7 50 29.7 44 to HfBZ w 0.03 to 0.05 to 0.04 to 0.07to 0.05 to 0.OSto 3300 39.6 53 34.7 48 29.7 42 HfB2 60 to 97 44 to 95 65 to 96 50 o 93 70 to 95 55 to 92 Re +W Re 0.03 to 0.11 to 0.14 to 0.15 to 0.17 to 0.18 to 2000 Bound 39.6 73 67 68 62 63 to VBZ W 0.03 to 0.1 to 71 0.13 to 0.13 to 0.15 to 0.16 to 2200 39.6 65 66 60 61 VBz 60 to 97 27 to 90 33 to 87 31 to 70 to 95 36 to Re + W Re 0.03 to 0.08 to 0.04 to 0.1 to 0.05 to 0.13 to 2900 Bound 39.6 65 34.7 61 29.7 55 to NbBz W 0.03 to 0.08 to 0.04 to 0_1 to 0.05 to 0.12 to 3100 39.6 63 34.7 58 29.7 53 NbB2 60 to 97 34 to 92 65 to 96 39 to 90 70 to 95 44 to 88 Re + W Re 0_03 to 0.05 to 0.04 to 0.07 to 0.05 to 0.08 to 3100 Bound 39.6 52 34.7 47 29.7 41 to TaB2 W 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.07 to 3300 39.6 50 34.7 39 29.7 39 TaB2 60 to 97 47 to 96 65 to 96 53 to 94 70 to 95 58 to 93 Re + W Re 0.03 to 0.1 to 69 0.04 to 0.13 to 0.05 to 0.16 to 1900 Bound 39.6 34_7 64 29.7 59 to Cr3B2 W 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.14 to 2100 39.6 67 34.7 62 29.7 57 Cr3B 60 to 97 32 to 91 65 to 96 35=to 88 70 to 95 40 to 86 Re + W Re 0.03 to 0.08 to 0.04 to 0.1 to 0.05 to 0.13 to 2000 Bound 39.6 64 34.7 59 29.7 53 to MoB2 W 0.03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.11 to 2200 39.6 62 34.7 57 29.7 51 MoB2 60 to 97 36 to 93 65 to 96 41 to 91 70 to 95 46 to 88 Re + W Re 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to 2800 Bound 39.6 46 34.7 41 29.7 36 to WB W 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 2900 39.6 44 34.7 39 29.7 34 WB 60 to 97 53 to 96 65 to 96 57 to 95 70 to 95 64 to 94 Re + W Re 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 2700 Bound 39.6 45 34.7 40 29.7 35 to W2B W 0.03 to 0.03 to 0.04 to 0.05 to 0.05 to 0.06 to 2900 39.6 43 34.7 38 29.7 33 W2B 60 to 97 54 to 97 65 to 96 60 to 95 70 to 95 65 to 94 Re + W Re 0.03 to 0.13 to 0.04 to 0.17 to 0.05 to 0.21 to 2000 Bound 39.6 76 34.7 72 29.7 67 to T].5S].3 w 0.03 to 0.12 to 0.04 to 0.16 to 0.05 to 0.19 to 2200 39.6 74 34.7 70 29.7 65 Ti5S 60 to 97 24 to 88 65 to 96 28 to 84 70 to 95 32 to 81 1g Re + W Re 0_03 to 0.11 to 0.04 to 0.14 to 0.05 to 0.17 to 2100 Bound 39.6 71 34.7 67 29.7 61 to Zr6Sis W 0.03 to 0.1 to 69 0.04 to 0.13 to 0.05 to 0.15 to 2400 39.6 34.7 65 29.7 59 Zr6S 60 to 97 28 to 90 65 to 96 33=to 87 70 to 95 38 to 84 1s Re + W Re 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.15 to 1900 Bound 39.6 68 34.7 64 29.7 58 to NbSiz w 0.03 to 0.09 to 0.04 to 0.11 to 0.05 to 0.14 to 2100 39.6 66 34.7 62 29.7 56 NbSi 60 to 97 31 to 91 65 to 96 36 to 89 70 to 95 41 to 86 z Re + W Re 0.03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.12 to 2300 Bound 39.6 62 34.7 57 29.7 51 to TaSi2 w 0.03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.11 to 2500 39.6 60 34.7 54 29.7 49 TaSi 60 to 97 38 to 93 65 to 96 43 to 91 70 to 95 49 to 89 z Re + W Re 0.03 to 0.1 to 69 0.04 to 0.12 to 0.05 to 0.15 to 1900 Bound 39.6 34.7 64 29_7 58 to MoSiz W 0.03 to 0.09 to 0.04 to 0.11 to 0.05 to 0.14 to 2100 39.6 67 34.7 62 29.7 56 MoSi 60 to 97 31 to 91 65 to 96 36 to 89 70 to 95 41 to 86 Re + W Re 0_03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.11 to 1900 Bound 39.6 60 34.7 54 29.7 49 to WSi2 W 0.03 to 0.06 to 0.04 to 0.08 to 0.05 to 0.1 to 2100 39_6 58 34.7 52 29.7 47 wsi2 60 to 97 40 to 94 65 to 96 45 to 92 70 to 95 51 to 90 TABLE 47. Re and Co (Re+Co) bound a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 1%Re + 99% Co to 99% Re + 1%Co.

Covposition Range 1 Conposition Range 2 Coniposition Range 3 Eatimated Volume ~ Weight ~ Volume % Weight % Volume % Weight % Melting Point, C
Re +Co Re 0.03 to 0.12 to 0.04 to 0.17 to 0.05 to 0.2 to 64 1400 Bound 39.6 74 34.7 69 29.7 to TiC Co 0.03 to 0.05 to 0.04 to 0.07 to 0.05 to 0.08 to 3200 39.6 54 34.7 49 29.7 43 Ti 60 to 97 26 to 95 65 to 96 30 to 93 70 to 95 35 to 91 C
Re +Co Re 0.03 to 0.09 to 0.04 to 0.13 to 0.05 to 0.16 to 1400 Bound 39.6 68 34.7 63 29.7 57 to ZrC Co 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 3200 39.6 47 34.7 42 29.7 37 Zr 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 42 to 93 C
Re +Co Re 0.03 to 0.05 to 0.04 to 0.07 to 0.05 to 0.08 to 1400 Bound 39.6 52 34_7 47 29_7 41 to HfC Co 0.03 to 0.02 to 0_04 to 0.03 to 0.05 to 0.04 to. 3200 39.6 32 34.7 27 29.7 23 Hf 60 to 97 48 to 98 65 to 96 53 to 97 70 to 95 59 to 96 C
Re -{-Co Re 0.03 to 0.11 to 0.14 to 0_15 to 0.17 to 0.19 to 1400 Bound 39.6 71 67 67.0 62 62 to VC Co 0.03 to 0.05 to 0.13 to 0.06 to 0.15 to 0.07 to 2900 39.6 51 65 46 60 41 VC 60 to 97 28 to 95 33 to 87 33 to 94 70 to 95 38 to 92 Re + Re 0.03 to 0.08 to 0.04 to 0.1 to 59 0.05 to 0.13 to 1400 Co 39.6 64 34.7 29.7 53 to Bound Co 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 3200 NbC 39.6 43 34.7 38 29.7 33 Nb 60 to 97 36 to 97 65 to 96 41 to 95 70 to 95 47 to 94 C
Re + Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 1400 Co 39.6 49 34.7 43 29.7 38 to Bound Co 0.03 to 0.02 to 0.04 to 0.024 to 0.05 to 0.03 to 3200 TaC 39.6 29 34.7 25 29.7 21 Ta 60 to 97 51 to 98 65 to 96 56 to 97 70 to 95 62 to 97 C
Re +Co Re 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.15 to 1400 Bound 39.6 67 34.7 62 29.7 57 to Cr2C3 Co 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 1900 39.6 47 34.7 41 29.7 36 Crz 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 43 to 93 Re + Re 0.03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.11 to 1400 Co 39.6 60 34.7 55 29.7 49 to Bound Co 0.03 to 0.03 to 0_04 to 0.04 to 0.05 to 0.05 to 2600 MozC 39.6 39 34.7 34 29.7 29 Moz 60 to 97 40 to 97 65 to 96 45 to 96 70 to 95 50 to 95 C
Re + Re 0.03 to 0.04 to 0_04 to 0.05 to 0.05 to 0.07 to 1400 Co 39.6 47 34_7 42 29.7 36 to Bound Co 0.03 to 0.017 to 0.04 to 0.023 to 0.05 to 0.028 to 2900 WC 39.6 27 34.7 23 29.7 20 WC 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 63 to 94 Re + Re 0.03 to 0.11 to 0.04 to 0.15 to 0.05 to 0.19 to 1400 Co 39.6 71 34.7 67 29.7 62 to Bound Co 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.07 to 3200 TiN 39.6 52 34.7 46 29.7 41 Ti 60 to 97 28 to 95 65 to 96 33 to 93 70 to 95 38 to 92 N

Re + Re 0.03 to 0.08 to 0.04 to 0.11 to 0.05 to 0.14 to 1400 Co 39.6 65 34.7 60 29.7 55 to Bound Co 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 3200 ZrN 39_6 44 34.7 39 29.7 34 Zr 60 to 97 34 to 96 65 to 96 39 to 95 70 to 95 45 to 94 N
Re + Re 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.08 to 1400 Co 39.6 50 34.7 45 29.7 39 to Bound Co 0.03 to 0.019 to 0.04 to 0.026 to 0.05 to 0.032 to 3200 HfN 39.6 30 34.7 26 29.7 22 Hf 60 to 97 50 to 98 65 to 96 55 to 97 70 to 95 61 to 97 N
Re + Re 0.03 to 0.1 to 70 0.04 to 0.14 to 0.05 to 0.17 to 1400 Co 39.6 34.7 65 29.7 - 60 to Bound Co 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to 2300 VN 39.6 49 34.7 44 29.7 39 VN 60 to 97 30 to 96 65 to 96 35 to 94 70 to 95 40 to 93 Re + Re 0.03 to 0.08 to 0.04 to 0.11 to 0.05 to 0.14 to 1400 Co 39.6 65 34.7 60 29.7 55 to Bound Co 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 2500 NbN 39.6 45 34.7 39 29.7 34 Nb 60 to 97 34 to 96 65 to 96 39 to 95 70 to 95 45 to 94 N
Re + Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 1400 Co 39.6 49 34.7 44 29.7 38 to Bound Co 0.03 to 0.02 to 0.04 to 0.025 to 0.05 to 0.03 to 3200 TaN 39.6 29 34.7 25 29.7 21 Ta 60 to 97 51 to 98 65 to 96 56 to 97 70 to 95 62 to 98 N

TABLE 48. Re and Co (Re+Co) bound a boride from borides of IVb, Vb, & VIb or a silicide from silicides of IVb & Vb. The range of Binder is from 1%Re + 99% Co to 99% Re + 1%Co.

Composition Range 1 Coxiposition Range 2 Cosqposition Ran983 Eati.ma.ted Volume % Weight ~ Volume $ Weight ~ Volume ~ Weight $ D2elting Point, C
Re Re 0.03 to 0.13 to 0.04 to 0.18 to 71 0.05 to 0.22 to 1400 +Co 39.6 75 34.7 29.7 66 to Bound Co 0.03 to 0.05 to 0.04 to 0.07 to 51 0.05 to 0.08 to 3100 TiB2 39_6 56 34.7 29.7 45 TiB2 60 to 97 24 to 34 65 to 96 29 to 92 70 to 95 34 to 90 Re + Re 0.03 to 0.1 to 69 0.04 to 0.13 to 64 0.05 to 0.17 to 1400 Co 39.6 34.7 29.7 59 to Bound Co 0.03 to 0.04 to 0.05 to 0.05 to 44 0.05 to 0.07 to 3100 ZrB2 39.6 49 34.7 29.7 38 ZrB2 60 to 97 30 to 96 65 to 96 35 to 94 70 to 95 40 to 93 Re Re 0.03 to 0.06 to 0.04 to 0.08 to 50 0.05 to 0.09 to 1400 +Co 39.6 55 34.7 29.7 44 to Bound Co 0.03 to 0.2 to 34 0.04 to 0.03 to 30 0.05 to 0.04 to 3200 HfB2 39.6 34.7 29.7 25 HfB2 60 to 97 45 to 98 65 to 96 50 o 97 70 to 95 56 to 96 Re Re 0.03 to 0.12 to 0.14 to 0.16 to 69 0.17 to 0.2 to 63 1400 +Co .6 73 67 62 to Bound Co 0.03 to 0.05 to 0.13 to 0_06 to 48 0.15 to 0.08 to 2200 VB2 39_6 53 65 60 42 VBZ 60 to 97 27 to 95 33 to 87 31 to 93 70 to 95 36 to 91 Re + Re 0.03 to 0.09 to 0.04 to 0.12 to 61 0.05 to 0.14 to 1400 Co 39.6 66 34.7 29_7 55 to Bound Co 0.03 to 0.04 to 0.04 to 0.05 to 40 0.05 to 0.06 to 3100 NbB2 39.6 45 34.7 29.7 34 NbB2 60 to 97 34 to 96 65 to 96 39 to 95 70 to 95 45 to 94 Re + Re 0.03 to 0.05 to 0.04 to 0.07 to 47 0.05 to 0.08 to 1400 ,Co 39.6 52 34.7 29.7 41 to Bound Co 0.03 to 0.02 to 0.04 to 0.03 to 27 0.05 to 0.035 to 3300 TaB2 39.6 32 34.7 29.7 23 TaB2 60 to 97 48 to 98 65 to 96 53 to 97 70 to 95 58 to 96 Re + Re 0.03 to 0.1 to 69 0.04 to 0.13 to 65 0.05 to 0.17 to 1400 Co 39.6 34.7 29.7 59 to Bound Co 0.03 to 0.04 to 0.04 to 0.05 to 44 0.05 to 0.07 to 2100 Cr3B2 39.6 49 34.7 29.7 38 Cr3B2 60 to 97 30 to 96 65 to 96 35 to 93 70 to 95 41 to 93 Re Re 0.03 to 0.08 to 0.04 to 0.1 to 59 0.05 to 0.13 to 1400 +Co 39.6 64 34.7 29.7 53 to Bound Co 0.03 to 0.03 to 0.04 to 0.04 to 38 0.05 to 0.05 to 2200 MoB2 39_6 43 34.7 29.7 33 MoB2 60 to 97 36 to 97 65 to 96 41 to 95 70 to 95 46 to 94 Re + Re 0.03 to 0.04 to 0.04 to 0.05 to 41 0.05 to 0.07 to 1400 Co 39.6 46 34.7 29.7 36 to Bound Co 0.03 to 0.017 to 0.04 to 0.022 to 23 0.05 to 0.028 to 2900 WB 39.6 27 34.7 29.7 19 WB 60 to 97 53 to 98 65 to 96 59 to 98 70 to 95 64 to 97 Re + Re 0.03 to 0.04 to 0.04 to 0.05 to 40 0.05 to 0.06 to 1400 Co 39.6 45 34.7 29.7 35 to Bound Co 0.03 to 0.016 to 0.04 to 0.021 to 22 0.05 to 0.027 to 2900 WZB 39.6 26 34.7 29.7 19 W2B 60 to 97 55 to 98 65 to 96 60 to 98 70 to 95 65 to 97 Re Re 0.03 to 0.14 to 0.04 to 0.18 to 72 0.05 to 0.23 to 1400 +Co 39.6 76 34.7 29.7 67 to Bound Co 0.03 to 0.06 to 0.04 to 0.07 to 52 0.05 to 0.09 to 2200 Ti5Si3 39.6 57 34.7 29.7 47 TiSSi 60 to 97 24 to 94 65 to 96 28 to 92 70 to 95 32 to 90 Re + Re 0.03 to 0.11 to 0_04 to 0.15 to 67 0.05 to 0.19 to 1400 =Co 39_6 71 34.7 29_7 62 to Bound Co 0.03 to 0.05 to 0.04 to 0.06 to 46 0.05 to 0.07 to 2400 Zr6Si5 39.6 51 34.7 29.7 41 ZrN 60 to 97 28 to 95 65 to 96 33 to 94 70 to 95 38 to 92 Re + Re 0.03 to 0.1 to 69 0.04 to 0.13 to 64 0.05 to 0.16 to 1400 Co 39.6 34.7 29.7 58 to Bound Co 0.03 to 0.04 to 0.04 to 0.05 to 43 0.05 to 0.06 to 2100 NbSiz 39.6 48 34.7 29.7 37 NbSiz 60 to 97 31 to 96 65 to 96 36 to 94 70 to 95 41 to 93 Re + Re 0.03 to 0.07 to 0.04 to 0.1 to 57 0.05 to 0.12 to 1400 Co 39.6 62 34.7 29.7 51 to Bound Co 0.03 to 0.03 to 0.04 to 0.04 to 36 0.05 to 0.05 to 2500 TaSiZ 39.6 41 34.7 29.7 31 TaSiz 60 to 97 38 to 97 65 to 96 43 to 96 70 to 95 49 to 95 Re + Re 0.03 to 0.1 to 69 0.04 to 0.13 to 64 0.05 to 0.16 to 1400 Co 39.6 34.7 29.7 59 to Bound Co 0.03 to 0.04 to 0.04 to 0.05 to 43 0.05 to 0.07 to 2100 MoSi2 39.6 48 34.7 29.7 38 MoSi2 60 to 97 31 to 96 65 to 96 36 to 94 70 to 95 41 to 93 Re Re 0.03 to 0.07 to 0.04 to 0.09 to 55 0.05 to 0.11 to 1400 +Co 39.6 60 34.7 29.7 49 to Bound Co 0.03 to 0.03 to 0.04 to 0.04 to 34 0.05 to 0.046 to 2100 WSiZ 39.6 39 34.7 29.7 29 WSia 60 to 97 40 to 97 65 to 96 45 to 96 70 to 95 51 to 95 TABLE 49. Re and Mo (Re+Mo) bound a carbide from carbides of IVb, Vb, & VIb. The range of Binder is from 1%Re + 99% Mo to 99% Re + 1%Mo.

Com osition Range 1 Compoaition Range 2 Composition Range 3 Eatimated Volume ~ Weight ~ Volume ~ Weight $ Volume $ Weight % Melting Point, C
Re +Mo Re 0.03 to 0.12 to 0.04 to 0.16 to 0.05 to 0.2 to 2600 Bound 39.6 74 34.7 69 29.7 64 to TiC Mo 0.03 to 0.06 to 0.04 to 0.07 to 0.05 to 0.09 to 3200 39.6 57 34.7 52 29.7 46 TiC 60 to 97 26 to 94 65 to 96 30 to 92 70 to 95 35 to 90 Re +Mo Re 0.03 to 0.09 to 0.04 to 0.13 to 0.05 to 0.16 to 2600 Bound 39.6 68 34.7 63 29.7 57 to ZrC Mo 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 3200 39.6 50 34.7 45 29.7 39 ZrC 60 to 97 32 to 95 65 to 96 37 to 94 70 to 95 42 to 92 Re +Mo Re 0.03 to 0.05 to 0.04 to 0:07 to 0.05 to 0.08 to 2600 Bound 39.6 52 34.7 47 29.7 41 to HfC Mo 0.03 to 0.02 to 0.04 to 0.03 to 0.05 to 0.04 to 3200 39.6 34 34.7 30 29.7 25 HfC 60 to 97 48 to 98 65 to 96 53 to 97 70 to 95 59 to 96 Re +Mo Re 0.03 to 0.11 to 0.14 to 67 0.15 to 0.17 to 0.18 to 2600 Bound 39.6 71 67.0 62 62 to VC Mo 0.03 to 0.05 to 0.13 to 65 0.07 to 0.15 to 0.08 to 2900 39.6 55 49 60 44 VC 60 to 97 28 to 95 33 to 87 33 to 93 70 to 95 38 to 91 Re + Re 0.03 to 0.08 to 0.04 to 0.1 to 59 0.05 to 0.13 to 2600 Mo 39.6 64 34.7 29.7 53 to Bound Mo 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 3200 N=bC 39.6 46 34.7 41 29.7 35 NbC 60 to 97 36 to 96 65 to 96 41 to 95 70 to 95 47 to 94 Re + Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 2600 Mo 39.6 49 34.7 43 29.7 38 to Bound Mo 0.03 to 0.02 to 0.04 to 0.028 to 0.05 to 0.03 to 3200 TaC 39.6 31 34.7 27 29.7 22 TaC 60 to 97 51 to 98 65 to 96 56 to 97 70 to 95 62 to 96 Re +Mo Re 0.03 to 0_09 to 0.04 to 0.12 to 0.05 to 0.15 to 1700 Bound 39.6 67 34.7 62 29.7 57 to Cr2C3 Mo 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 1900 39.6 50 34,7 45 29.7 39 Cr2C 60 to 97 32 to 95 65 to 96 37 to 94 70 to 95 43 to 92 Re + Re 0.03 to 0.07 to 0.04 to O.b9 to 0.05 to 0.11 to 2500 Mo 39.6 60 34.7 55 29.7 49 to Bound Mo 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 2600 M02C 39.6 42 34.7 37 29.7 32 M02C 60 to 97 40 to 97 65 to 96 45 to 96 70 to 95 50 to 95 Re + Re 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to 2600 Mo 39.6 47 34.7 42 29.7 36 to Bound Mo 0.03 to 0.019 to 0.04 to 0.026 to 0.05 to 0.032 to 2900 WC 39.6 30 34.7 26 29.7 22 WC 60 to 97 53 to 98 65 to 96 58 to 97 70 to 95 64 to 97 5=

TABLE 50. Re and Ni (Re+Ni) bound a carbide from carbides of IVb, Vb, & V2b. The range of Binder is from 1%Re + 99% Ni to 99% Re + 1%Ni.

ComBosition Range 1 composition Range 2 Composition Range 3 Estimated Volume % Weight ~ Volume $ Weight t Volume % Weight ~ Melting Point, C
Re +Ni Re 0.03 to 0.12 to 0.04 to 0.17 to 0.05 to 0.2 to 64 1400 Bound 39.6 74 34.7 69 29.7 to TiC Ni 0.03 to 0.05 to 0.04 to 0.06 to 0.05 to 0.08 to 3200 39.6 54 34.7 49 29.7 43 TiC 60 to 97 26 to 95 65 to 96 30 to 93 70 to 95 35 to 91 Re +Ni Re 0.03 to 0.09 to 0.04 to 0.13 to 0.05 to 0.16 to 1400 Bound 39.6 68 34.7 63 29.7 57 to ZrC Ni 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 3200 39.6 47 34.7 42 29.7 36 ZrC 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 42 to 93 Re +Ni Re 0.03 to 0_05 to 0.04 to 0.07 to 0.05 to 0.08 to 1400 Bound 39.6 52 34.7 47 29.7 41 to HfC Co 0.03 to 0.02 to 0.04 to 0.027 to 0.05 to 0.034 to 3200 39.6 31 34.7 27 29.7 23 HfC 60 to 97 48 to 98 65 to 96 53 to 97 70 to 95 59 to 96 Re +Ni Re 0.03 to 0.11 to 0.14 to 0.15 to 0.17 to 0.19 to 1400 Bound 39.6 71 67 67.0 62 62 to VC Ni 0.03 to 0.04 to 0.13 to 0.06 to 0.15 to 0.07 to 2900 39.6 51 65 46 60 40 VC 60 to 97 28 to 95 33 to 87 33 to 94 70 to 95 38 to 92 Re + Re 0.03 to 0_08 to 0.04 to 0.1 to 59 0.05 to 0.13 to 1400 Ni 39.6 64 34.7 29.7 53 to Bound Ni 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 3200 NbC 39_6 43 34.7 37 29.7 32 NbC 60 to 97 36 to 97 65 to 96 41 to 95 70 to 95 47 to 94 Re + Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 1400 Ni 39.6 49 34.7 43 29.7 38 to Bound Ni 0.03 to 0.018 to 0_04 to 0.024 to 0.05 to 0.03 to 3200 TaC 39.6 29 34.7 25 29.7 21 TaC 60 to 97 51 to 98 65 to 96 56 to 97 70 to 95 62 to 97 Re +Ni Re 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.15 to 1400 Bound 39.6 67 34.7 62 29.7 57 to Cr2C3 Ni 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 1900 39.6 46 34.7 41 29.7 36 CrZC 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 43 to 93 Re + Re 0.03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.11 to 1400 Ni 39.6 60 34.7 55 29.7 49 to Bound Ni 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 2600 M02C 39.6 39 34.7 34 29.7 29 M02C 60 to 97 40 to 97 65 to 96 45 to 96 70 to 95 50 to 95 Re + Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 1400 Ni 39.6 47 34.7 42 29.7 36 to Bound Ni 0.03 to 0.017 to 0.04 to 0.022 to 0_05 to 0.028 to 2900 WC 39.6 27 34.7 23 29.7 19 WC 60 to 97 53 to 98 65 to 96 58 to 98 70 to 95 64 to 97 TABLE 51. Re and Cr (Re+Cr) bound a carbide from carbides of IVb, Vb, & VIb. The range of Binder is from 1%Re + 99% Cr to 99% Re + 1%Cr.

Composition Range 1 composition Range 2 Composition Range 3 Estimated Volume ~ Weight $ Volume $ Weight $ Volume $ Weight ~ Melting Point, C
Re +Cr Re 0.03 to 0.13 to 0.04 to 0.17 to 0.05 to 0.2 to 64 1800 Bound 39.6 74 34.7 69 29.7 to TiC Cr 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.06 to 3200 39.6 48 34.7 43 29.7 39 TiC 60 to 97 26 to 96 65 to 96 30 to 94 70 to 95 36 to 93 Re +Cr Re 0.03 to 0.1 to 68 0.04 to 0.13 to 0.05 to 0.16 to 1800 Bound 39.6 34.7 63 29.7 57 to ZrC Cr 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 3200 39.6 41 34.7 36 29.7 32 ZrC 60 to 97 32 to 97 65 to 96 37 to 95 70 to 95 42 to 94 Re +Cr Re 0.03 to 0.05 to 0.04 to 0.07 to 0.05 to 0.09 to 1800 Bound 39.6 52 34.7 47 29.7 41 to HfC Cr 0.03 to 0.017 to 0.04 to 0.022 to 0.05 to 0.027 to 3200 39.6 27 34.7 23 29.7 19 HfC 60 to 97 48 to 98 65 to 96 53 to 98 70 to 95 59 to 97 Re +Cr Re 0.03 to 0.11 to 0.14 to 0.15 to 0.17 to 0.19 to 1800 Bound 39.6 71 67 67.0 62 62 to VC Cr 0.03 to 0.04 to 0.13 to 0.05 to 0.15 to 0.06 to 2900 39.6 46 65 41 60 35 VC 60 to 97 28 to 96 33 to 87 33 to 95 70 to 95 38 to 93 Re + Re 0.03 to 0.08 to 0.04 to 0.1 to 59 0.05 to 0.13 to 1800 Cr 39.6 64 34.7 29.7 53 to Bound Cr 0.03 to 0.026 to 0.04 to 0.034 to 0.05 to 0.04 to 3200 NbC 39.6 37 34.7 33 29.7 28 NbC 60 to 97 36 to 97 65 to 96 41 to 96 70 to 95 47 to 95 Re + Re 0.03 to 0.04 to 0.04 to 0.06 to 0.05 to 0.07 to 1800 Cr 39.6 49 34.7 43 29.7 38 to Bound Cr 0.03 to 0.015 to 0.04 to 0.019 to 0.05 to 0.024 to 3200 TaC 39.6 25 34.7 21 29.7 17 TaC 60 to 97 51 to 98 65 to 96 56 to 98 70 to 95 62 to 97 Re.+Cr Re 0.03 to 0.09 to 0.04 to 0.12 to 0.05 to 0.16 to 1800 Bound 39.6 67 34.7 62 29.7 57 to Cr2C3 Cr 0.03 to 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 1900 39.6 41 34.7 36 29.7 31 Cr2C 60 to 97 32 to 97 65 to 96 37 to 96 70 to 95 43 to 95 Re + Re 0.03 to 0.07 to 0.04 to 0.09 to 0.05 to 0.11 to 1800 Cr 39.6 60 34.7 55 29.7 49 to Bound Cr 0.03 to 0.023 to 0.04 to 0.03 to 0.05 to 0.037 to 2600 M02C 39.6 34 34.7 29 29.7 25 102C 60 to 97 40 to 98 65 to 96 45 to 97 70 to 95 50 to 96 Re + Re 0.03 to 0.04 to 0.04 to 0.05 to 0.05 to 0.07 to 1800 Cr 39.6 47 34.7 42 29.7 36 to Bound Cr 0.03 to 0.014 to 0.04 to 0.018 to 0.05 to 0.023 to 2900 WC 39.6 23 34.7 20 29.7 16 WC 60 to 97 53 to 65 to 96 58 to 98 70 to 95 64 to 98.6 97.6 [0085] The above compositions for hardmetals or cermets may be used for a variety of applications. For example, a material as described above may be used to form a wear part in a tool that cuts, grinds, or drills a target object by using the wear part to remove the material of the target object. Such a tool may include a support part made of a different material, such as a steel. The wear part is then engaged to the support part as an insert. The tool may be designed to include multiple inserts engaged to the support part. For example, some mining drills may include multiple button bits made of a hardmetal material. Examples of such a tool includes a drill, a cutter=
such as a knife, a saw, a grinder, and a drill.
Alternatively, hardmetals descried=here may be used to form the entire head of a tool as the wear part for cutting, drilling or other machining operations. The hardmetal particles may also be used to form abrasive grits for .polishing or grinding various materials. in addition, such hardmetals may also be used to construct housing and exterior surfaces or layers for various devices to meet specific needs of the operations of the devices or the environmental conditions under which the devices operate.
[0086] More specifically, the hardmetals described here may be used to manufacture cutting tools for machining metals, alloys, composite materials, plastic materials, wooden materials, and others. The cutting tools may include indexable inserts for turning, milling, boring and drilling, drills, end mills, reamers, taps, hobs and milling cutters.
Since the temperature of the cutting edge of such tools may be higher than 500 C during machining, the hardmetal compositions for high-temperature operating conditions described above may have special advantages when used in such cutting tools, e.g., extended tool life and improved productivity by such tools by increasing the cutting speed.
[0087] The hardmetals described here may be used to manufacture tools for wire drawing, extrusion, forging and cold heading. Also as mold and Punch for powder process. In addition, such hardmetals may be used as wear-resistant material for rock drilling and mining.
[0088] The hardmetal materials described in this application may be fabricated in bulk forms or as coatings on metal surfaces. Coatings with such new hardmetal materials may be advantageously used to form a hard layer on a metal surface to achieve desired hardness that would otherwise be difficult to achieve with the underlying metal material. Bulk hardmetal materials based on the compositions in this application may be expensive and hence the use of coatings on less expensive metals with lower hardness may be used to reduce the costs of various components or parts with high hardness.
[0089] A number of powder processes for producing commercial hardmetals may be used to manufacture the harc7metals of this application. As an example, a binder alloy with Re higher than 85% in weight may be fabricated by the process of solid phase sintering to eliminate open porosities then HIP replaces liquid phase sintering.
[0090] FIG. 9 shows a flowchart for several fabrication methods for materials or structures from the above hardmetal compositions. As illustrated, alloy powders for the binders and the hard particle powders may be mixed with a milling liquid in a wet mixing process with or without a lubricant (e.g., wax). The fabrication flows on the left hand side of FIG. 9 are for fabricating hardmetals with lubricated wet mixing. The mixture is first dried by vacuum drying or spray drying process to produce lubricated grade powder. Next, the lubricated grade power is shaped into a bulky material via pill pressing, extruding, or cold isostatic press (CIP) and shaping. The CIP is a process to consolidate powder by isostatic pressure. The bulky material is then heated to remove the lubricant and is sintered in a presintering process. Next, the material may be processed via several different processes. For example, the material may be processed via a liquid phase sintering in vacuum or hydrogen and then further processed by a HIP process to form the final hardmetal parts. Alternatively, the material after the presintering may go through a solid phase sintering to eliminate open porosity and then a HIP process to form the final hardmetal parts.
[0091] When alloy powders for the binders and the hard particle powders are mixed without the lubricant, the unlubricated grade power after the drying process may be processed in two different ways to form the final hardmetal parts. The first way as illustrated simply uses hot pressing to complete the fabrication. The second way uses a thermal spray forming process to form the grade powder on a metal substrate in vacuum. Next, the metal substrate is removed to leave the structure by the thermal spray forming as a free-standing material as the final hardmetal part. In addition, the free-standing material may be further processed by a HIP
process to reduce the porosities if needed.
[0092] In forming a hardmetal coating on a metal surface, a thermal spray process may be used under a vacuum condition to produce large parts coated with harcdmetal materials. For example, surfaces of steel parts and tools may be coated to improve their hardness and thus performance. FIG. 10 shows an exemplary flow chart of a thermal spray process.
[0093] Various thermal spray processes are known for coating metal surfaces. For example, the ASM Handbook Vol. 7 (P408, 1998) describes the thermal spray as a family of particulate/droplet consolidation processes capable of forming metals, ceramics, intermetallics, composites, and polymers into coatings or freestanding structures. During the process, powder, wire, or rods can be injected into combustion or arc-heated jets, where they are heated, melted or softened, accelerated, and directed toward the surface, or substrate, .30 being coated. On impact at the substrate, the particles or droplets rapidly solidify, cool, contract, and incrementally build up to form a deposit on a target surface. The thin "splats" may undergo high cooling rates, e.g., in excess of 106 K/s for metals.

-164~

[0094] A thermal spray process may use chemical (combustion) or electrical (plasma or arc) energy to heat feed materials injected into hot-gas jets to create a stream of molten droplets that are accelerated and directed toward the substrates being coated. Various thermal spray processes are shown in Figure 3 and 4 in ASM Handbook Vol. 7, pages 409-410.
[0095] Various details of thermal spray processes are described in "Spray Forming" by Lawley et al. and "Thermal Spray Forming of Materials" by Knight et al., which are published in ASM Handbook, Volume 7, Powder Metal Technologies and Application (1998), from pages 396 to 407, and pages 408 to 419, respectively.
[0096] In various applications, selected hardmetal compositions described here can be used to maintain high 15material strength and hardness at high temperatures at or above 1500 C. For example, certain high-power engines operate at such high temperatures such as various jet and rocket engines used in various flying devices and vehicles.
More specifically, jet and rocket nozzles, including non-erosive nozzle throats and low-erosive nozzle throats, in these and other engines may be partially or entirely made of the selected hardmetal materials described in this application.
[0097] For example, hardmetals based on one or more of (1) one or more carbides, (2) one or more nitrides, (3) one or more borides and (4) a combination of two or more of (1), (2) and (3) with a binder material which is either pure Re or a composite binder material with Re as one component. The melting points of various carbides, nitrides, and borides in this application are above 2400 C. Examples of suitable carbides for the present high-temperature hardmetal materials include TaC, HfC, NbC, ZrC, TiC, WC, VC, A14C3, ThC2, M02C, SiC
and B4C. Examples of suitable nitrides for the present high-temperature hardmetal materials include HfN, TaN, BN, ZrN, and TiN. Examples of suitable borides for the present high-temperature hardmetal materials include HfB2, ZrB2, TaB2, TiBz, NbB2, and WB. Two examples of the composite binder material with Re as one component are (1) W and Re and (2) Ta and Re.
[00981 In the binder material compositions described in this application, Rhenium can be used in a binder material to achieve cetain properties. For example, addition of Re into W
in a binder material can improve the mechanical properities, such as the ductility, of the W-Re alloy binder material over W without Re. As another example, addition of Re into Mo in a binder material can improvethe mechanical properities (e.g., ductility) of the Mo-Re alloy binder material over Mo without Re. As yet another example, addition of Re into Cr in a binder material can improve the mechanical properities (e.g., ductility) of the Cr-Re alloy binder material over Cr without Re.
[0099] Molybdenum can also be added-in a binder material to improve the properties of the binder material. Adding Mo into a Ni-bound TiC material forms a Ni-Mo-bound TiC material and can improve the ductility and toughness of the Ni-Mo-bound TiC
material over the Ni-bound TiC material. in hardmetals using Ni-based superalloy binder materials, Mo can be added to the Ni-based superalloy binder material. For example, Mo can be added to the Ni-based superalloy-bound TiC to improve the ductility and toughness of Ni-based superalloy-Mo-bound TiC
over Ni-based superalloy-bound TiC.
[00100] While this specification contains many specifics, these should not be construed as limitations on the scope of an invention or of what may be claimed, but rather as descriptions of features specific to particular embodiments of the invention. Certain features that are described in this specification in the context of separate embodiments can also be implemented in combination in a single embodiment.
Conversely, various features that are described in the context of a single embodiment can also be implemented in multiple embodiments separately or in any suitable subcombination.
Moreover, although features may be described above as acting in certain combinations and even initially claimed as such, one or more features from a claimed combination can in some cases be excised from the combination, and the claimed combination may be directed to a subcombination or a variation of a subcombination.
[00101] only a few implementations and examples are disclosed.
.10 However, it is understood that variations and enhancements may be made.

Claims (52)

1. A friction stir welding tool head, comprising:
a shoulder; and a pin engaged to the shoulder, wherein at least one part of each of the shoulder and the pin comprises:
a first material comprising at least one of or a combination of at least one carbide, at least one nitride, at least one boride, and at least one silicide, and a second material to bind the first material, the second material comprising at least rhenium.
2. The head as in claim 1, wherein the first material comprises at least one of tungsten carbide and titanium carbide.
3. The head as in claim 1, wherein the first material comprises:
hard particles comprising at least one of TaC, HfC, NbC, ZrC, TiC, WC, VC, Al4C3, ThC2, Mo2C, SiC, B4C and Cr2C3.
4. The head as in claim 3, wherein the hard particles are less than 75% of a total weight of the material and rhenium is greater than 25% of the total weight of the material.
5. The head as in claim 3, wherein the second material further comprises W.
6. The head as in claim 3, wherein the second material further comprises Ta.

~168~
7. The head as in claim 3, wherein the second material further comprises Mo.
8. The head as in claim 3, wherein the second material further comprises Cr.
9. The head as in claim 3, wherein the hard particles further comprise at least one of HfN, TaN, BN, ZrN, TiN, VN, SiN and NbN.
10. The head as in claim 9, wherein the second material further comprises W.
11. The head as in claim 9, wherein the second material further comprises Ta.
12. The head as in claim 3, wherein the hard particles further comprise at least one of VB2, Cr3B2, HfB2, ZrB2, TaB2, TiB2, NbB2, and WB.
13. The head as in claim 12, wherein the second material further comprises W.
14. The head as in claim 12, wherein the second material further comprises Ta.
15. The head as in claim 1, wherein the first material comprises:
hard particles comprising at least one of HfN, TaN, BN, ZrN, TiN, VN, SiN and NbN.
16. The head as in claim 15, wherein the second material further comprises W.

~169~
17. The head as in claim 15, wherein the second material further comprises Ta.
18. The head as in claim 15, wherein the hard particles further comprise at least one of VB2, Cr3B2, HfB2, ZrB2, TaB2, TiB2, NbB2, and WB.
19. The head as in claim 18, wherein the second mateiral further comprises W.
20. The head as in claim 18, wherein the second material further comprises Ta.
21. The head as in claim 1, wherein the second material further comprises Mo.
22. The head as in claim 1, wherein the second material further comprises Cr.
23. The head as in claim 1, wherein the second material further comprises cobalt.
24. The head as in claim 1, wherein the second material further comprises a nickel-based superalloy.
25. The head as in claim 24, wherein the second material further comprises cobalt.
26. The head as in claim 1, wherein the first material comprises at least one of Ti5Si3, Zr6Si5, Zr3Si2, Zr4Si3, ZrSi, HfSi2, NbSi2, TaSi2, Mo3Si2, MoSi2, W3Si2, and WSi2.

~170~
27. The head as in claim 1, wherein the first material comprises at least one of VB2, Cr3B2, HfB2, ZrB2, TaB2, TiB2, NbB2, and WB.
28. A friction stir welding tool head, comprising:
a shoulder; and a pin engaged to the shoulder, wherein at least one part of each of the shoulder and the pin comprises:
a first material comprising at least one of or a combination of at least one carbide, at least one nitride, at least one boride, and at least one silicide, and a second material to bind the first material, the second material comprising at least a Ni-based superalloy.
29. The head as in claim 28, wherein the first material comprises at least one of tungsten carbide and titanium carbide.
30. The head as in claim 28, wherein the first material comprises:
hard particles comprising at least one of TaC, HfC, NbC, ZrC, TiC, WC, VC, Al4C3, ThC2, Mo2C, SiC, B4C and Cr2C3.
31. The head as in claim 30, wherein the hard particles are less than 75% of a total weight of the material.
32. The head as in claim 30, wherein the second material further comprises W.
33. The head as in claim 30, wherein the second material further comprises Ta.

~171~
34. The head as in claim 30, wherein the second material further comprises Mo.
35. The head as in claim 30, wherein the second material further comprises Cr.
36. The head as in claim 30, wherein the hard particles further comprise at least one of HfN, TaN, BN, ZrN, TiN, VN, SiN and NbN.
37. The head as in claim 36, wherein the second material further comprises W.
38. The head as in claim 36, wherein the second material further comprises Ta.
39. The head as in claim 30, wherein the hard particles further comprise at least one of HfB2, ZrB2, TaB2, TiB2, NbB2, and WB.
40. The head as in claim 39, wherein the second material further comprises W.
41. The head as in claim 39, wherein the second material further comprises Ta.
42. The head as in claim 28, wherein the first material comprises :
hard particles comprising at least one of HfN, TaN, BN, ZrN, TiN, VN, SiN and NbN.
43. The head as in claim 42, wherein the second material further comprises W.

~172~
44. The head as in claim 42, wherein the second material further comprises Ta.
45. The head as in claim 42, wherein the hard particles further comprise at least one of VB2, Cr3B2, HfB2, ZrB2, TaB2, TiB2, NbB2, and WB.
46. The head as in claim 45, wherein the second mateiral further comprises W.
47. The head as in claim 45, wherein the second material further comprises Ta.
48. The head as in claim 28, wherein the second material further comprises Mo.
49. The head as in claim 28, wherein the second material further comprises Cr.
50. The head as in claim 28, wherein the second material further comprises cobalt.
51. The head as in claim 28, wherein the first material comprises at least one of Ti5Si3, Zr6Si5, Zr3Si2, Zr4Si3, ZrSi, HfSi2, NbSi2, TaSi2, Mo3Si2, MoSi2, W3Si2, and WSi2.
52. The head as in claim 28, wherein the first material comprises at least one of VB2, Cr3B2, HfB2, ZrB2, TaB2, TiB2, NbB2, and WB.

~173~
CA002641029A 2006-01-31 2007-01-31 High-performance friction stir welding tools Abandoned CA2641029A1 (en)