CA2243254A1 - Thermoplastic polymer propellant compositions - Google Patents
Thermoplastic polymer propellant compositions Download PDFInfo
- Publication number
- CA2243254A1 CA2243254A1 CA 2243254 CA2243254A CA2243254A1 CA 2243254 A1 CA2243254 A1 CA 2243254A1 CA 2243254 CA2243254 CA 2243254 CA 2243254 A CA2243254 A CA 2243254A CA 2243254 A1 CA2243254 A1 CA 2243254A1
- Authority
- CA
- Canada
- Prior art keywords
- propellant
- propellant composition
- composition
- polymer
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A propellant is disclosed, comprising, as binder, an ethylene copolymer especially ethylene/vinyl acetate copolymer. The binder may be silane-grafted and moisture curable. The propellant is particularly useful as a rocket propellant. A method of manufacture is disclosed.
Description
CA 022432~4 1998-07-1 TITLE
THERMOPLASTIC POLYMER PROPELLANT COMPOSITIONS
Field Of The Invention The present application relates to propellant compositions e.g. rocket propellant or gas generator compositions, that are based on thermoplastic ethylene co-polymers, especially ethylene/vinyl acetate copolymers(EVA) and other related polyolefins. In embodiments, the binder is a cross-linkable ethylene/vinyl acetate copolymer, or related cross-linkable copolymer. In particular, such polymers form the binder of the propellant composition. An example of a cross-linkable polymer is silane-grafted EVA.
Background To The Invention The original black powder rocket propellants were replaced in the early 1900's with propellants based on nitrocellulose and nitroglycerine. Subsequently propellants were developed that were based on a fuel oil, a binder e.g. asphalt, and an oxidizer e.g. potassium perchlorate. Polysulphide fuel binders that could be cast and cured at cool temperatures, mixtures of ammonium perchlorate, polyester and styrene cured by cumene hydroperoxide and compositions based on polyvinyl chloride plastisols were also developed.
A number of polybutadiene materials, including in particular polybutadiene acrylonitrile, carboxy terminated polybutadiene and hydroxy-terminated polybutadiene have also been developed and undergone commercial use. In particular, propellant compositions using polybutadiene acrylonitrile (PBAN) as binder have been developed and are used in a number of rocket systems, including the solid rocket boosters for the Space Shuttle. Propellant compositions using hydroxy-terminated polybutadiene (HTPB) are also known and in use. It is understood that systems utilizing thermoset polymers such as PBAN and HTPB exhibit relatively long CA 022432~4 1998-07-1~
curing times (several days) unless promoted through heat and/or catalysis, and that pot-life suffers accordingly, and may be as short as about 20 minutes.
In most cases, propellant compositions using the above binder systems and related systems require the use of toxic chemicals such as epoxides, diisocyanates or aziridines as curing agents. In addition, plasticizers e.g. ethyl hexyl acrylate or di-octyl adipate may be used, which are also known to exhibit toxicological properties. In addition to safety considerations during manufacture of the propellants, the cost of many of these constituents is relatively high.
The shelf life of some of these constituents, such as epoxides and diisocyanates, tends to be short.
Special handling e.g. freezing or refrigeration and/or inert gas blanketing, is required to extend their useful life, which further increases the overall cost of the propellants.
Of greater concern is the potential for allergic reactions and the consequent need for special handling in order to protect persons handling the compositions.
Propellant compositions offering greater flexibility, less stringent handling requirements and less lead time in fabrication would be useful.
Summary Of The Invention Propellants formed from thermoplastic polymers, and methods for the manufacture thereof, have now been found.
Accordingly, an aspect of the present invention provides a solid propellant composition comprising, as binder, a thermoplastic ethylene co-polymer, especially ethylene/vinyl acetate copolymer.
In embodiments of the compositions, the binder is a silane-grafted ethylene/vinyl acetate copolymer.
Another aspect of the invention provides a propellant comprising an ethylene co-polymer, especially ethylene/vinyl acetate copolymer, and at least 40% by weight of an oxidizer. In particular, the propellant CA 022432~4 1998-07-1~
contains at least 60% by weight of oxidizer.
In preferred embodiments of the propellant of the present invention, the propellant is a rocket propellant or gas generator.
In another embodiment the propellant contains at least one of the following: fuel additives, energetic compounds, ballistic modifiers, rheology modifiers, bonding agents, opacifiers, stabilizers, metal de-activators, anti-oxidants, and other agents known to the trade to modify processing, performance, mechanical properties, storage stability or shelf life.
A further aspect of the present invention provides a pre-propellant composition comprising ethylene/vinyl acetate copolymer and at least one of an energetic and a ballistic modifier.
Brief Description of the Drawings The present invention is illustrated by the embodiments shown in the drawings, in which:
Figure 1 is a photograph of a control sample of propellanti Figure 2 is a photograph of a second control sample of propellant; and Figure 3 is a photograph of a propellant of the invention.
Detailed Description Of The Invention The following acronyms are used in this application:
PETN pentaerythritol tetranitrate TMETN trimethanolethane trinitrate BTTN butanetriol trinitrate GAP glycidyl azide polymer HMX cyclotetramethylenetetranitramine RDX cyclotrimethylenetrinitramine PGN propylglycidyl nitrate BAMO/AMMO bis-azidomethyloxetane/azidomethyl-methyloxetane copolymer CA 022432~4 1998-07-1~
BAMO/NMMO bis-azidomethyloxetane/nitramethyl-methyloxetane copolymer PBAN polybutadiene acrylonitrile HTPB hydroxy-terminated polybutadiene AP ammonium perchlorate The propellants of the present invention are particularly intended for use in rockets, missiles, gas generating devices or similar devices. The propellant comprises, as a binder, an ethylene co-polymer, especially an ethylene/vinyl acetate co-polymer.
The polymers that are used in the present invention are ethylene co-polymers. Such polymers include co-polymers of ethylene and a vinyl alkanoate, especially ethylene/vinyl acetate co-polymers (EVA). Alternatively, the polymer may be a co-polymer of ethylene and an acrylate ester, examples of which are ethylene/ethyl acrylate co-polymers, ethylene/methyl acrylate co-polymers and ethylene/butyl acrylate co-polymers. The polymer may also be a co-polymer of ethylene with acrylic acid or methylacrylic acid or the related ionomers viz.
co-polymers having the acid groups thereof partially neutralized by metals especially sodium, zinc or aluminum. The polymers may have other copolymerized monomers e.g. carbon monoxide.
Compositions formed from EVA tend to exhibit physical properties equivalent to, or superior to for instance PBAN, and functional at temperatures of up to about 50~C.
The preferred binder is ethylene/vinyl acetate co-polymer. It has good overall mechanical properties, which may be further improved especially at elevated temperatures, through cross-linking. Propellant compositions may be manufactured for use at temperatures in the range of -65~C to 130~C. In addition, it has good adhesive properties, which has the potential to eliminate the need for bonding agents as are often required in other systems to improve mechanical adhesion of the binder to the oxidizer particles. These same adhesive CA 022432~4 1998-07-1~
properties also potentially eliminate the need for tie-coats or other enhancements of the propellant. These adhesive properties may be enhanced through cross-linking.
The ethylene/vinyl acetate co-polymer may have a wide range of melt index. Melt index is measured by the procedures of ASTM D1238. For example, melt indices of from about 0.4 dg/min which is a high viscosity ethylene/vinyl acetate co-polymer, up to at least 2500 dg/min are known, and may be selected according to the use. In embodiments the melt index is in the range of 400-2500 dg/min. Small amounts of plasticizers e.g.
polybutene, may be added to either the binder or formulated propellant system to enhance processability and/or mechanical properties.
Examples of ethylene/vinyl acetate copolymers include ElvaxTM 210, Elvax 220 and Elvax 240 ethylene/vinyl acetate copolymers.
The propellant will normally be comprised of the binder i.e. ethylene copolymer, and at least 40% by weight of an oxidizer. In particular, the propellant contains at least 40% by weight of oxidizer, preferably at least 60% by weight and especially at least 70% by weight of oxidizer. The propellant may also contain an energetic, a ballistic modifier and other compounds.
A variety of oxidizers known to the trade may be used, including but not limited to ammonium perchlorate, potassium perchlorate, lithium perchlorate, sodium perchlorate, ammonium nitrate, potassium nitrate, sodium nitrate, strontium nitrate, guanidine nitrate, ammonium dinitramide. Nonetheless, it is understood that other oxidizers could be used.
In preferred embodiments, the propellant contains 75-90% by weight of oxidizer. Ammonium perchlorate (AP) is the preferred oxidizer for many applications because it is relatively non-hygroscopic, stable during normal storage and fabrication procedures and relatively low in cost, in addition to providing good performance.
CA 022432~4 1998-07-1~
As in other solid propellant systems, oxidizers may be incorporated in various particle sizes as necessitated by burn rate requirements, process rheology, solids loading, and commercial availability. Typically, propellant system utilize blends of particle sizes to improve packing density and thus achieve a high solids loading as is necessary for high performance. Typical coarse sizes of ammonium perchlorate, for example, would be 400-600 microns, medium sizes would be 50-200 microns, and fine AP e.g. ground onsite, commonly would be have a mean particle size of 5-15 microns. Ultrafine and other particle sizes may also be present e.g. particle sizes from submicron to 5 microns. A mixture of more than one particle size would normally be used.
In addition to the above, the propellant may contain one or more of the following: fuel additives, e.g. metal or non-metal powders or metal hydrides; energetic materials e.g. crystalline high explosives such as HMX or RDX, liquid high explosives such as TMETN or BTTN;
ballistic modifiers e.g. ferrocene or ferrocene derivatives, borohydrides, copper chromite, oxamide, oxides of iron, lead, chromium, copper, magnesium, and others; thermally-conductive burn rate modifiers such as silver wire staples or graphite whisker; coupling agents/rheology modifiers such as titanates, zirconates, aluminates; bonding agents; opacifiers, stabilizers, metal de-activators, anti-oxidants, or other agents known to the trade to modify processing, performance, mechanical properties, storage stability or shelf life.
Examples of stabilizers include zinc oxide, nickel oxide and triacetin. Examples of flame colorants include salts of strontium, barium sodium and lithium.
Examples of energetic materials are solid high explosives such as HMX, RDX, nitroguanidine, nitrocellulose, PETN, lead azide, sodium azide; liquid high explosives such as nitroglycerin, diethylene glycol dintrate, triethylene glycol dinitrate, TMETN, BTTN, energetic polymeric binders such as glycidyl azide CA 022432~4 1998-07-1~
polymer, BGN, BAMO/AMMO and BAMO/NMMO.
In order to obtain the propellant, according to one embodiment of the invention, the co-polymer in the form of pellets or powder may be mixed in a dry state with an oxidizer e.g. ammonium perchlorate.
Fuel additives, energetic materials and other modifiers may be added at this stage, or in many cases may be pre-blended into the polymer. As noted herein, a pre-propellant is an important feature of an aspect of the invention. The dry mixture is then heated e.g. to about 85-130~C, to form a mixture that is flowable. The resultant mixture may then be transferred to a mould and subjected to moderate pressure in order to form a fuel grain.
In preferred embodiments of the method of manufacture of propellant compositions, a pre-propellant composition is formed. In this method, the polymer is mixed with some or all of the additives and modifiers required in the final formulation, excluding oxidizer and energetic materials and any catalysts. The resultant composition is then pelletized or powdered in an extruder. To manufacture a propellant composition from this material, it is typically first pre-coated with a plasticizer, e.g. polybutene. The oxidizing and energetic materials and any other additives are then added, and the subsequent mixture is mixed at a typical temperature of about 85-130~C, to form a flowable, heterogenous propellant composition.
The composition is then formed into propellant grains. In a typical process, the propellant is pre-loaded into a ram extruder. The pre-loaded composition is then transferred to a press, in which the grain is formed under moderate pressure, conforming to the inner surface of the liner in the ram extruder, and to the mandrel in the extruder which defines the profile of the inner core of the propellant grain (if required). The mandrel and/or clamping blocks which retain the grains may be pre-heated to minimize surface freezing, then CA 022432~4 1998-07-1~
switched to a cold cycle during a pressing operation to speed the overall cure cycle. Small propellant grains have been formed by this method with a cycle time of 30-120 seconds, but it is anticipated that shorter cycle times may be achieved.
The resultant propellant grains have a uniform consistency, showing excellent distribution of the constituents, especially when compared to non de-gassed pour-cast propellant compositions, with an absence of significant bubbles. The propellant shows a high tensile strength and elongation at break. Such properties, in addition to good adhesive properties, are important for the finished propellant grain in order to minimize mechanical problems during storage and handling.
As noted herein, in more preferred embodiments of the method of manufacture of the propellant compositions, a pre-propellant composition is formed using EVA. The EVA is mixed with modifiers e.g. zirconates, aluminates or titanates, with energetics e.g. aluminum, magnesium, aluminum/magnesium powders, optionally with zinc powder or chlorinated hydrocarbons if tracing is required, and any ballistic modifiers to modify the burn rate e.g. iron oxide, copper oxide, chromium oxide or magnesium oxide, or calcium carbonate. The resultant composition is pelletized in an extruder. To add oxidizer to the pellets, the pellets may be coated with polybutene and then oxidizer e.g. ammonium perchlorate added. The ammonium perchlorate is typically a mixture of particle sizes which aids in formation of a uniform composition.
The resultant mixture of oxidizer and pellets is mixed to a dough-like consistency, which may be formed into a cylindrical preform for the forming of propellant grains.
Propellant grains are then formed in a ram extruder, under pressure, using a rapid hot/cold cycle. The use of a ram extruder permits the fabrication of propellant grains of complicated or sophisticated shapes without the need for post-forming operations. The requirement for vacuum de-gassing is believed to be reduced or CA 022432~4 1998-07-1~
eliminated. However, the process may easily be run under vacuum to effect removal of trapped and dissolved gases, traces of volatiles, etc.
It is understood that other fabrication techniques may be used.
Propellant grains formed in the ram extruder have a uniform consistency, even when viewed under a microscope as shown in the Figures herein, especially compared to PBAN, with an excellent distribution of constituents and an absence of significant bubbles. The propellant grains have high tensile strength and elongation. Such properties are important for the propellant grain in order to withstand acceleration during firing in a rocket without cracking. Cracking could have major adverse effects, on the rocket, including destruction.
Advantages of ethylene/vinyl acetate thermoplastic copolymer-based solid propellant binders over existing technologies include less critical limits on mix ratios of the component, easy processing of the pre-propellant, low to non-toxic properties of the binder constituents, the absence of shelf or pot-life problems, the potential absence of vacuum degassing requirements, the ability to recycle components and rapid cure times if required.
However, the most significant advantage is likely the lead time required for the production of propellants for rocket motors, because either the pre-mixed propellant or the individual ingredients can be stored indefinitely.
Thus rocket motors, or other propellant-using systems, could be produced on a just-in-time basis for rapid deployment in the field of use. In addition, components may be safely stored near a location where the propellant is to be used, and manufactured as needed in apparatus that is easy to operate.
The manufacture of the pre-propellant i.e.
propellant without oxidizer, is a rapid continuous process utilizing apparatus known in the plastics industry. Similarly, the mixing of pre-propellant and oxidizer, and the forming of fuel grains may also be CA 022432~4 1998-07-1 operated on a continuous basis. In both instances, recycle of materials may be used, but the amount of recycle material should be minimal. Nonetheless, the ability to recycle components is an important characteristic of the present invention as it improves economics of the process and reduces or eliminates the need to dispose of components of the propellant by, for example, burning. This is environmentally advantageous.
It is understood that recycling would normally not be carried out with cross-linked compositions. However, cross-linkable compositions may be recycled. For instance, the pre-propellant would normally be prepared without the cross-linking catalyst, which would permit recycling for a period of time.
In embodiments of the invention, especially where higher temperatures are involved in deployment and service, especially ambient or storage temperatures that might exceed about 40~C., the propellant compositions may be formed with a crosslinked copolymer. Cross-linked polymer may also be used at other temperatures including low ambient temperatures, but generally is not necessary.
Cross-linking will improve physical properties, especially at elevated temperatures. It will further reduce the likelihood of cracking, slumping, de-bonding or other mechanical problems of the propellant compositions. In these embodiments, the propellant compositions is formed using a polymer that has a moisture-crosslinkable monomer copolymerized into the polymer or grafted onto the polymer. Examples of moisture-crosslinkable monomers are vinyl silanes, particularly vinyl trialkoxysilanes, examples of which are vinyl trimethoxysilane and vinyl triethoxysilane.
Such silanes are available commercially. In addition, compositions containing vinyl silane, grafting catalyst and crosslinking catalyst are also available commercially.
Polymers containing vinyl silanes must be maintained in a moisture-free environment at all times prior to the CA 022432~4 1998-07-1~
desired time of crosslinking. Crosslinking may be effecting by exposure to moisture, especially by merely exposing the article to atmospheric conditions. Curing by contacting with water, especially steam, is not preferred in view of effects of water on the propellants.
Crosslinking may take place over a period of a few days in the presence of atmospheric moisture, it being understood that the shape and thickness of the fuel grain is a factor in the cross-linking rate, as the crosslinking reaction is believed to be controlled by the rate of diffusion of water into the fuel grain.
Crosslinking catalysts are normally incorporated into the composition. Techniques for the manufacture of moisture-crosslinkable polymers, and for the curing of such polymers are known.
An advantage of the use of ethylene/vinyl acetate copolymers as the binder in propellants is the increased safety that may be achieved during the manufacturing process. Energetic materials such as aluminium powder must be handled carefully during traditional fuel-grain manufacturing processes, as air-borne metallic powders can be extremely volatile under certain conditions.
According to the present invention, the energetic materials may be compounded with the thermoplastic polymer in compounding extruders. In such a method, the energetic materials would be inhibited and would no longer pose a hazard during shipping or the manufacture of fuel-grains. It is understood that such powders are frequently compounded with thermoplastic polymers as colorants or dyes for such polymers.
Shelf life of the components, including in particular the compounds of the pre-propellant that is formed, is generally indefinite. Thus, pot-life is not a consideration. However, if crosslinked compositions are prepared, steps must be taken to protect the vinyl compounds from moisture, as discussed above.
The present invention provides a fuel grain with uniform properties, and a method of manufacture that is CA 022432~4 1998-07-1~
versatile and easy to operate. Components may be recycled.
The propellant compositions may be used in a variety of end uses, including as rocket propellants or in gas generators. The latter use a propellant composition to produce gas for mechanical work such as start a turbine engine, drive a piston, or inflate an airbag, in contrast to a rocket motor which exhausts the gas through a nozzle to generate a reaction force.
One of the most desirable features of the present invention is that unlike most conventional propellant systems and processes this invention provides a propellant system and process which exhibits the combination of a very long or nearly indefinite pot-life, with a very short casting and curing time.
The present invention is illustrated by the following examples.
Example I
A control sample (Sample #1) of a first typical AP/Al/HTPB propellant composition was prepared. This composition employed a tri-modal blend of 400, 200 and 90 micron AP, 3 micron spherical aluminum, and HTPB binder, in addition to HX-878 bonding agent and carbon black opacifier in minor percentages. This sample was processed under atmospheric pressure, to show the severe porosity of propellants processed in this manner.
The total time required for preparation, including weighing, mixing and cast cycle time was 6 hours. The cure time was 2 days.
Figure 1 shows a photograph of a cross-section of the propellant. The dark pockets are voids of approximately 250-340 micron in diameter. Porosity of this magnitude would at least result in erratic performance and low density of the propellant, and likely result in catastrophic motor failure from pressure fluctuations or adiabatic compression. In addition, the AP particles show weak bonding in the binder matrix as CA 022432~4 1998-07-1~
evidenced by the crescent shaped air pockets created during sample preparation.
A second propellant composition (Sample #2) nearly identical to the first sample was prepared, with the major exception that the process was run under high vacuum for 1.5 hour mix cycle. In addition, this composition employed state of the art bonding agents to enhance adhesion of the binder to the AP particles.
The total time required for preparation, including weighing, mixing and cast cycle time was 6 hours. The cure time was 6 days.
Figure 2 shows a photograph of a cross-section of the propellant. The surface shows clean cleavage of the AP particles and lack of de-bonding under the shear force of cutting, in addition to an excellent surface distribution profile. Some tearing and pocketing is evident at the perimeter of the sample, as expected during sample preparation. The measured density of this sample is 0.0589 pounds per cubic inch (1.630 g/cc).
A sample (Sample #3) of propellant of the invention was prepared, with identical solids composition to the second sample except that ethylene/vinyl acetate co-polymer was used as binder. The propellant was formed from pre-propellant, using the ram extruder, as described. The total mix cycle for this batch was 20 minutes, under atmospheric pressure (no vacuum).
The total time required for preparation, including weighing, mixing and mix cycle time was 1.5 hours. The time for extrusion, pressing, cooling and curing in non-continuous prototype equipment was 4 minutes/grain.
Figure 3 shows a photograph of a cross-section of the propellant. This sample exhibits the same excellent surface distribution as the second sample above, as well as aggressive bonding of the AP particles to the binder matrix. No voids are visible other than at the periphery of the sample. The measured density of this sample is 0.05962 pounds per cubic inch (1.650 g/cc), an increase of 1.2% over the second sample.
CA 022432~4 l998-07-l~
Example II
Propellant compositions were prepared by the following procedure. A mixing bowl was heated to 210-215~F (99-102~C). Fine to medium particulate ammonlum perchlorate (AP) was fed to the bowl, together with any burn rate catalysts, and mixed for two minutes. All remaining AP was added, and dry mixed for 3-5 minutes at high speed.
A mixture of ethylene/vinyl acetate copolymer, polybutene or other plasticizer, rheology modifiers (if present) was prepared. This mixture was added to the mixer. Mixing was continued until the polymer had melted, and then for a further 10 minutes. The resultant mixture was then extruded into propellant grains in the ram extruder.
Example III
The procedure used for preparing pre-propellant blends was as follows. Using a Ross LDM-4 double planetary mixture, the temperature was set at 265~ F
(129~ C), when the ethylene-vinyl acetate copolymer was ElvaxTX 205 or 210 polymer. All fine dry materials of the composition were added to the mixing bowl, with any dust being allowed to settle. The mixing head was then wiped to remove settled material. The Elvax ethylene-vinyl acetate copolymer and all other medium to coarse materials were added, including fluid ingredients if any.
A vacuum was then applied to the mixture.
The dry mixing cycle was commenced, at low speed mixing. The mixing speed was increased when the temperature passed the melting point of the composition, typically about 100~ C, and mixing was continued for 20 minutes. The mixing bowl was scraped down once after about 10 minutes.
The mixing head was then lifted, leaving the blades at the surface of the composition for 1-2 minutes to CA 022432~4 1998-07-1 allow adhered material to flow into the bowl with minimal trapped air. The contents of the bowl were then discharged. A similar procedure may be used with different types of mixer, including mixes that do not operate under vacuum.
Example IV
A composition was prepared in a K-5 air mixer. The mixing bowl temperature was set at 99-102~ C, and all fine to medium sized particulate ammonium perchlorate and any burn rate catalyst was added to the mix bowl. The mixture was then mixed at high speed for 2 minutes. Any remaining ammonium perchlorate was added and the resultant mixture was preheated for 3-5 minutes under high speed mixing. A mixture of Elvax ethylene/vinyl acetate copolymer with any polybutene or other plasticizer, rheology modifiers or other ingredients was then added, and mixed at a moderate mixing speed. After the mixture had reached the melting point, the mixture was mixed for a further 10 minutes. The mixture was subsequently extruded into grains.
Using this procedure a composition was prepared as follows:
Material: Weight Charged (g) AP-400* 500.5 AP-200* 115.5 AP-90* 153.5 Pre-blend** 215.5 Polybutene 6 (Soltex) 10 NZ-33 neo-alkoxy 5 zirconate***
Batch total 1000 grams * Ammonium perchlorate, with 400, 200 or 90 micron particulate size.
** Pre-blend of Example VII, below.
*** Kenrich Petrochemicals, Inc.
Processing was difficult in that the composition CA 022432~4 1998-07-1 exhibited high initial tack, requiring more frequent scraping.
The procedure was repeated, using a pre-blend of binder PB-6 and NZ-33. All ammonium perchlorate was added at the same time. The mixture dispersed easily as it heated, and suddenly transitioned into a crumbly, mobile blend. Extrusion in the ram extruder was good.
Example V
The procedure of Example IV was repeated, using the following composition:
Material: Weight Charged (g) AP-400 479.45 AP-200 122.1 AP-90 212.3 Pre-blend* 66.3 ElvaxTM 210 EVA 103.85 Polybutene-6 10 NZ-33 neo-alkoxy zirconate 5 Iron oxide Batch Total 1000 grams * Pre-blend of Example VII, below.
This formulation has reduced aluminum content (2%), an increased amount of 90 micron AP (from 25 to 30~ by weight), and iron oxide, with a proportional reduction in ammonium perchlorate of 400 micron size. These changes were intended to reduce nozzle erosion and increase ignition response.
CA 022432~4 1998-07-1 Example VI
A pre-blend batch was prepared with the following composition:
Material:Weight Charged (g) Elvax 210 EVA 719.28 Polybutene 6 0.00 Carbon Black 2.40 Zinc, (Purity Zinc Metals 1678.32 UP-6) Batch Total 2400 grams No problems were experienced in the mixing cycle, the extrusion cycle or pelletising of the pre-blend.
The pre-blend was then formulated into a propellant grain using 50.05% by weight of the pre-blend and 49.95%
by weight of 200 micron particulate ammonium perchlorate.
Example VII
A pre-blend was formed of the following composition:
Material:Weight Charged (g) Elvax 210 EVA 2088.17 Polybutene 6 0.00 Carbon Black 6.96 Aluminum, spherical904.87 Iron oxide 0.00 Batch Total 3000 grams The pre-blend was blended with ammonium perchlorate, to form propellant grain, with the resultant composition containing 21.55% by weight of the pre-blend.
No problems were encountered in the processing of the composition.
Example VIII
Samples similar to Sample #2 and #3 of Example I
were subjected to Martin-Marietta PEPcode analysis to determine characteristics of the compositions as propellants. Sample #2 is a HTPB control sample and CA 022432~4 l998-07-l~
Sample #3 iS an EVA composition of the invention.
The results obtained were as follows:
Sample #2 Sample #3 Density lb/in3O. 05946 0.06017 g/cm3 1. 6457 1.6654 Specific Impulse Frozen Flow 233.9 233.3 Shifting Flow236.3 236.6 Density Impulse Fro~en Flow 384.9 388.5 Shifting Flow388.8 394.0 The composition of the invention showed a small increase in density impulse indicating that the composition is at least equivalent to a HTPB composition, and possibly superior for some uses.
THERMOPLASTIC POLYMER PROPELLANT COMPOSITIONS
Field Of The Invention The present application relates to propellant compositions e.g. rocket propellant or gas generator compositions, that are based on thermoplastic ethylene co-polymers, especially ethylene/vinyl acetate copolymers(EVA) and other related polyolefins. In embodiments, the binder is a cross-linkable ethylene/vinyl acetate copolymer, or related cross-linkable copolymer. In particular, such polymers form the binder of the propellant composition. An example of a cross-linkable polymer is silane-grafted EVA.
Background To The Invention The original black powder rocket propellants were replaced in the early 1900's with propellants based on nitrocellulose and nitroglycerine. Subsequently propellants were developed that were based on a fuel oil, a binder e.g. asphalt, and an oxidizer e.g. potassium perchlorate. Polysulphide fuel binders that could be cast and cured at cool temperatures, mixtures of ammonium perchlorate, polyester and styrene cured by cumene hydroperoxide and compositions based on polyvinyl chloride plastisols were also developed.
A number of polybutadiene materials, including in particular polybutadiene acrylonitrile, carboxy terminated polybutadiene and hydroxy-terminated polybutadiene have also been developed and undergone commercial use. In particular, propellant compositions using polybutadiene acrylonitrile (PBAN) as binder have been developed and are used in a number of rocket systems, including the solid rocket boosters for the Space Shuttle. Propellant compositions using hydroxy-terminated polybutadiene (HTPB) are also known and in use. It is understood that systems utilizing thermoset polymers such as PBAN and HTPB exhibit relatively long CA 022432~4 1998-07-1~
curing times (several days) unless promoted through heat and/or catalysis, and that pot-life suffers accordingly, and may be as short as about 20 minutes.
In most cases, propellant compositions using the above binder systems and related systems require the use of toxic chemicals such as epoxides, diisocyanates or aziridines as curing agents. In addition, plasticizers e.g. ethyl hexyl acrylate or di-octyl adipate may be used, which are also known to exhibit toxicological properties. In addition to safety considerations during manufacture of the propellants, the cost of many of these constituents is relatively high.
The shelf life of some of these constituents, such as epoxides and diisocyanates, tends to be short.
Special handling e.g. freezing or refrigeration and/or inert gas blanketing, is required to extend their useful life, which further increases the overall cost of the propellants.
Of greater concern is the potential for allergic reactions and the consequent need for special handling in order to protect persons handling the compositions.
Propellant compositions offering greater flexibility, less stringent handling requirements and less lead time in fabrication would be useful.
Summary Of The Invention Propellants formed from thermoplastic polymers, and methods for the manufacture thereof, have now been found.
Accordingly, an aspect of the present invention provides a solid propellant composition comprising, as binder, a thermoplastic ethylene co-polymer, especially ethylene/vinyl acetate copolymer.
In embodiments of the compositions, the binder is a silane-grafted ethylene/vinyl acetate copolymer.
Another aspect of the invention provides a propellant comprising an ethylene co-polymer, especially ethylene/vinyl acetate copolymer, and at least 40% by weight of an oxidizer. In particular, the propellant CA 022432~4 1998-07-1~
contains at least 60% by weight of oxidizer.
In preferred embodiments of the propellant of the present invention, the propellant is a rocket propellant or gas generator.
In another embodiment the propellant contains at least one of the following: fuel additives, energetic compounds, ballistic modifiers, rheology modifiers, bonding agents, opacifiers, stabilizers, metal de-activators, anti-oxidants, and other agents known to the trade to modify processing, performance, mechanical properties, storage stability or shelf life.
A further aspect of the present invention provides a pre-propellant composition comprising ethylene/vinyl acetate copolymer and at least one of an energetic and a ballistic modifier.
Brief Description of the Drawings The present invention is illustrated by the embodiments shown in the drawings, in which:
Figure 1 is a photograph of a control sample of propellanti Figure 2 is a photograph of a second control sample of propellant; and Figure 3 is a photograph of a propellant of the invention.
Detailed Description Of The Invention The following acronyms are used in this application:
PETN pentaerythritol tetranitrate TMETN trimethanolethane trinitrate BTTN butanetriol trinitrate GAP glycidyl azide polymer HMX cyclotetramethylenetetranitramine RDX cyclotrimethylenetrinitramine PGN propylglycidyl nitrate BAMO/AMMO bis-azidomethyloxetane/azidomethyl-methyloxetane copolymer CA 022432~4 1998-07-1~
BAMO/NMMO bis-azidomethyloxetane/nitramethyl-methyloxetane copolymer PBAN polybutadiene acrylonitrile HTPB hydroxy-terminated polybutadiene AP ammonium perchlorate The propellants of the present invention are particularly intended for use in rockets, missiles, gas generating devices or similar devices. The propellant comprises, as a binder, an ethylene co-polymer, especially an ethylene/vinyl acetate co-polymer.
The polymers that are used in the present invention are ethylene co-polymers. Such polymers include co-polymers of ethylene and a vinyl alkanoate, especially ethylene/vinyl acetate co-polymers (EVA). Alternatively, the polymer may be a co-polymer of ethylene and an acrylate ester, examples of which are ethylene/ethyl acrylate co-polymers, ethylene/methyl acrylate co-polymers and ethylene/butyl acrylate co-polymers. The polymer may also be a co-polymer of ethylene with acrylic acid or methylacrylic acid or the related ionomers viz.
co-polymers having the acid groups thereof partially neutralized by metals especially sodium, zinc or aluminum. The polymers may have other copolymerized monomers e.g. carbon monoxide.
Compositions formed from EVA tend to exhibit physical properties equivalent to, or superior to for instance PBAN, and functional at temperatures of up to about 50~C.
The preferred binder is ethylene/vinyl acetate co-polymer. It has good overall mechanical properties, which may be further improved especially at elevated temperatures, through cross-linking. Propellant compositions may be manufactured for use at temperatures in the range of -65~C to 130~C. In addition, it has good adhesive properties, which has the potential to eliminate the need for bonding agents as are often required in other systems to improve mechanical adhesion of the binder to the oxidizer particles. These same adhesive CA 022432~4 1998-07-1~
properties also potentially eliminate the need for tie-coats or other enhancements of the propellant. These adhesive properties may be enhanced through cross-linking.
The ethylene/vinyl acetate co-polymer may have a wide range of melt index. Melt index is measured by the procedures of ASTM D1238. For example, melt indices of from about 0.4 dg/min which is a high viscosity ethylene/vinyl acetate co-polymer, up to at least 2500 dg/min are known, and may be selected according to the use. In embodiments the melt index is in the range of 400-2500 dg/min. Small amounts of plasticizers e.g.
polybutene, may be added to either the binder or formulated propellant system to enhance processability and/or mechanical properties.
Examples of ethylene/vinyl acetate copolymers include ElvaxTM 210, Elvax 220 and Elvax 240 ethylene/vinyl acetate copolymers.
The propellant will normally be comprised of the binder i.e. ethylene copolymer, and at least 40% by weight of an oxidizer. In particular, the propellant contains at least 40% by weight of oxidizer, preferably at least 60% by weight and especially at least 70% by weight of oxidizer. The propellant may also contain an energetic, a ballistic modifier and other compounds.
A variety of oxidizers known to the trade may be used, including but not limited to ammonium perchlorate, potassium perchlorate, lithium perchlorate, sodium perchlorate, ammonium nitrate, potassium nitrate, sodium nitrate, strontium nitrate, guanidine nitrate, ammonium dinitramide. Nonetheless, it is understood that other oxidizers could be used.
In preferred embodiments, the propellant contains 75-90% by weight of oxidizer. Ammonium perchlorate (AP) is the preferred oxidizer for many applications because it is relatively non-hygroscopic, stable during normal storage and fabrication procedures and relatively low in cost, in addition to providing good performance.
CA 022432~4 1998-07-1~
As in other solid propellant systems, oxidizers may be incorporated in various particle sizes as necessitated by burn rate requirements, process rheology, solids loading, and commercial availability. Typically, propellant system utilize blends of particle sizes to improve packing density and thus achieve a high solids loading as is necessary for high performance. Typical coarse sizes of ammonium perchlorate, for example, would be 400-600 microns, medium sizes would be 50-200 microns, and fine AP e.g. ground onsite, commonly would be have a mean particle size of 5-15 microns. Ultrafine and other particle sizes may also be present e.g. particle sizes from submicron to 5 microns. A mixture of more than one particle size would normally be used.
In addition to the above, the propellant may contain one or more of the following: fuel additives, e.g. metal or non-metal powders or metal hydrides; energetic materials e.g. crystalline high explosives such as HMX or RDX, liquid high explosives such as TMETN or BTTN;
ballistic modifiers e.g. ferrocene or ferrocene derivatives, borohydrides, copper chromite, oxamide, oxides of iron, lead, chromium, copper, magnesium, and others; thermally-conductive burn rate modifiers such as silver wire staples or graphite whisker; coupling agents/rheology modifiers such as titanates, zirconates, aluminates; bonding agents; opacifiers, stabilizers, metal de-activators, anti-oxidants, or other agents known to the trade to modify processing, performance, mechanical properties, storage stability or shelf life.
Examples of stabilizers include zinc oxide, nickel oxide and triacetin. Examples of flame colorants include salts of strontium, barium sodium and lithium.
Examples of energetic materials are solid high explosives such as HMX, RDX, nitroguanidine, nitrocellulose, PETN, lead azide, sodium azide; liquid high explosives such as nitroglycerin, diethylene glycol dintrate, triethylene glycol dinitrate, TMETN, BTTN, energetic polymeric binders such as glycidyl azide CA 022432~4 1998-07-1~
polymer, BGN, BAMO/AMMO and BAMO/NMMO.
In order to obtain the propellant, according to one embodiment of the invention, the co-polymer in the form of pellets or powder may be mixed in a dry state with an oxidizer e.g. ammonium perchlorate.
Fuel additives, energetic materials and other modifiers may be added at this stage, or in many cases may be pre-blended into the polymer. As noted herein, a pre-propellant is an important feature of an aspect of the invention. The dry mixture is then heated e.g. to about 85-130~C, to form a mixture that is flowable. The resultant mixture may then be transferred to a mould and subjected to moderate pressure in order to form a fuel grain.
In preferred embodiments of the method of manufacture of propellant compositions, a pre-propellant composition is formed. In this method, the polymer is mixed with some or all of the additives and modifiers required in the final formulation, excluding oxidizer and energetic materials and any catalysts. The resultant composition is then pelletized or powdered in an extruder. To manufacture a propellant composition from this material, it is typically first pre-coated with a plasticizer, e.g. polybutene. The oxidizing and energetic materials and any other additives are then added, and the subsequent mixture is mixed at a typical temperature of about 85-130~C, to form a flowable, heterogenous propellant composition.
The composition is then formed into propellant grains. In a typical process, the propellant is pre-loaded into a ram extruder. The pre-loaded composition is then transferred to a press, in which the grain is formed under moderate pressure, conforming to the inner surface of the liner in the ram extruder, and to the mandrel in the extruder which defines the profile of the inner core of the propellant grain (if required). The mandrel and/or clamping blocks which retain the grains may be pre-heated to minimize surface freezing, then CA 022432~4 1998-07-1~
switched to a cold cycle during a pressing operation to speed the overall cure cycle. Small propellant grains have been formed by this method with a cycle time of 30-120 seconds, but it is anticipated that shorter cycle times may be achieved.
The resultant propellant grains have a uniform consistency, showing excellent distribution of the constituents, especially when compared to non de-gassed pour-cast propellant compositions, with an absence of significant bubbles. The propellant shows a high tensile strength and elongation at break. Such properties, in addition to good adhesive properties, are important for the finished propellant grain in order to minimize mechanical problems during storage and handling.
As noted herein, in more preferred embodiments of the method of manufacture of the propellant compositions, a pre-propellant composition is formed using EVA. The EVA is mixed with modifiers e.g. zirconates, aluminates or titanates, with energetics e.g. aluminum, magnesium, aluminum/magnesium powders, optionally with zinc powder or chlorinated hydrocarbons if tracing is required, and any ballistic modifiers to modify the burn rate e.g. iron oxide, copper oxide, chromium oxide or magnesium oxide, or calcium carbonate. The resultant composition is pelletized in an extruder. To add oxidizer to the pellets, the pellets may be coated with polybutene and then oxidizer e.g. ammonium perchlorate added. The ammonium perchlorate is typically a mixture of particle sizes which aids in formation of a uniform composition.
The resultant mixture of oxidizer and pellets is mixed to a dough-like consistency, which may be formed into a cylindrical preform for the forming of propellant grains.
Propellant grains are then formed in a ram extruder, under pressure, using a rapid hot/cold cycle. The use of a ram extruder permits the fabrication of propellant grains of complicated or sophisticated shapes without the need for post-forming operations. The requirement for vacuum de-gassing is believed to be reduced or CA 022432~4 1998-07-1~
eliminated. However, the process may easily be run under vacuum to effect removal of trapped and dissolved gases, traces of volatiles, etc.
It is understood that other fabrication techniques may be used.
Propellant grains formed in the ram extruder have a uniform consistency, even when viewed under a microscope as shown in the Figures herein, especially compared to PBAN, with an excellent distribution of constituents and an absence of significant bubbles. The propellant grains have high tensile strength and elongation. Such properties are important for the propellant grain in order to withstand acceleration during firing in a rocket without cracking. Cracking could have major adverse effects, on the rocket, including destruction.
Advantages of ethylene/vinyl acetate thermoplastic copolymer-based solid propellant binders over existing technologies include less critical limits on mix ratios of the component, easy processing of the pre-propellant, low to non-toxic properties of the binder constituents, the absence of shelf or pot-life problems, the potential absence of vacuum degassing requirements, the ability to recycle components and rapid cure times if required.
However, the most significant advantage is likely the lead time required for the production of propellants for rocket motors, because either the pre-mixed propellant or the individual ingredients can be stored indefinitely.
Thus rocket motors, or other propellant-using systems, could be produced on a just-in-time basis for rapid deployment in the field of use. In addition, components may be safely stored near a location where the propellant is to be used, and manufactured as needed in apparatus that is easy to operate.
The manufacture of the pre-propellant i.e.
propellant without oxidizer, is a rapid continuous process utilizing apparatus known in the plastics industry. Similarly, the mixing of pre-propellant and oxidizer, and the forming of fuel grains may also be CA 022432~4 1998-07-1 operated on a continuous basis. In both instances, recycle of materials may be used, but the amount of recycle material should be minimal. Nonetheless, the ability to recycle components is an important characteristic of the present invention as it improves economics of the process and reduces or eliminates the need to dispose of components of the propellant by, for example, burning. This is environmentally advantageous.
It is understood that recycling would normally not be carried out with cross-linked compositions. However, cross-linkable compositions may be recycled. For instance, the pre-propellant would normally be prepared without the cross-linking catalyst, which would permit recycling for a period of time.
In embodiments of the invention, especially where higher temperatures are involved in deployment and service, especially ambient or storage temperatures that might exceed about 40~C., the propellant compositions may be formed with a crosslinked copolymer. Cross-linked polymer may also be used at other temperatures including low ambient temperatures, but generally is not necessary.
Cross-linking will improve physical properties, especially at elevated temperatures. It will further reduce the likelihood of cracking, slumping, de-bonding or other mechanical problems of the propellant compositions. In these embodiments, the propellant compositions is formed using a polymer that has a moisture-crosslinkable monomer copolymerized into the polymer or grafted onto the polymer. Examples of moisture-crosslinkable monomers are vinyl silanes, particularly vinyl trialkoxysilanes, examples of which are vinyl trimethoxysilane and vinyl triethoxysilane.
Such silanes are available commercially. In addition, compositions containing vinyl silane, grafting catalyst and crosslinking catalyst are also available commercially.
Polymers containing vinyl silanes must be maintained in a moisture-free environment at all times prior to the CA 022432~4 1998-07-1~
desired time of crosslinking. Crosslinking may be effecting by exposure to moisture, especially by merely exposing the article to atmospheric conditions. Curing by contacting with water, especially steam, is not preferred in view of effects of water on the propellants.
Crosslinking may take place over a period of a few days in the presence of atmospheric moisture, it being understood that the shape and thickness of the fuel grain is a factor in the cross-linking rate, as the crosslinking reaction is believed to be controlled by the rate of diffusion of water into the fuel grain.
Crosslinking catalysts are normally incorporated into the composition. Techniques for the manufacture of moisture-crosslinkable polymers, and for the curing of such polymers are known.
An advantage of the use of ethylene/vinyl acetate copolymers as the binder in propellants is the increased safety that may be achieved during the manufacturing process. Energetic materials such as aluminium powder must be handled carefully during traditional fuel-grain manufacturing processes, as air-borne metallic powders can be extremely volatile under certain conditions.
According to the present invention, the energetic materials may be compounded with the thermoplastic polymer in compounding extruders. In such a method, the energetic materials would be inhibited and would no longer pose a hazard during shipping or the manufacture of fuel-grains. It is understood that such powders are frequently compounded with thermoplastic polymers as colorants or dyes for such polymers.
Shelf life of the components, including in particular the compounds of the pre-propellant that is formed, is generally indefinite. Thus, pot-life is not a consideration. However, if crosslinked compositions are prepared, steps must be taken to protect the vinyl compounds from moisture, as discussed above.
The present invention provides a fuel grain with uniform properties, and a method of manufacture that is CA 022432~4 1998-07-1~
versatile and easy to operate. Components may be recycled.
The propellant compositions may be used in a variety of end uses, including as rocket propellants or in gas generators. The latter use a propellant composition to produce gas for mechanical work such as start a turbine engine, drive a piston, or inflate an airbag, in contrast to a rocket motor which exhausts the gas through a nozzle to generate a reaction force.
One of the most desirable features of the present invention is that unlike most conventional propellant systems and processes this invention provides a propellant system and process which exhibits the combination of a very long or nearly indefinite pot-life, with a very short casting and curing time.
The present invention is illustrated by the following examples.
Example I
A control sample (Sample #1) of a first typical AP/Al/HTPB propellant composition was prepared. This composition employed a tri-modal blend of 400, 200 and 90 micron AP, 3 micron spherical aluminum, and HTPB binder, in addition to HX-878 bonding agent and carbon black opacifier in minor percentages. This sample was processed under atmospheric pressure, to show the severe porosity of propellants processed in this manner.
The total time required for preparation, including weighing, mixing and cast cycle time was 6 hours. The cure time was 2 days.
Figure 1 shows a photograph of a cross-section of the propellant. The dark pockets are voids of approximately 250-340 micron in diameter. Porosity of this magnitude would at least result in erratic performance and low density of the propellant, and likely result in catastrophic motor failure from pressure fluctuations or adiabatic compression. In addition, the AP particles show weak bonding in the binder matrix as CA 022432~4 1998-07-1~
evidenced by the crescent shaped air pockets created during sample preparation.
A second propellant composition (Sample #2) nearly identical to the first sample was prepared, with the major exception that the process was run under high vacuum for 1.5 hour mix cycle. In addition, this composition employed state of the art bonding agents to enhance adhesion of the binder to the AP particles.
The total time required for preparation, including weighing, mixing and cast cycle time was 6 hours. The cure time was 6 days.
Figure 2 shows a photograph of a cross-section of the propellant. The surface shows clean cleavage of the AP particles and lack of de-bonding under the shear force of cutting, in addition to an excellent surface distribution profile. Some tearing and pocketing is evident at the perimeter of the sample, as expected during sample preparation. The measured density of this sample is 0.0589 pounds per cubic inch (1.630 g/cc).
A sample (Sample #3) of propellant of the invention was prepared, with identical solids composition to the second sample except that ethylene/vinyl acetate co-polymer was used as binder. The propellant was formed from pre-propellant, using the ram extruder, as described. The total mix cycle for this batch was 20 minutes, under atmospheric pressure (no vacuum).
The total time required for preparation, including weighing, mixing and mix cycle time was 1.5 hours. The time for extrusion, pressing, cooling and curing in non-continuous prototype equipment was 4 minutes/grain.
Figure 3 shows a photograph of a cross-section of the propellant. This sample exhibits the same excellent surface distribution as the second sample above, as well as aggressive bonding of the AP particles to the binder matrix. No voids are visible other than at the periphery of the sample. The measured density of this sample is 0.05962 pounds per cubic inch (1.650 g/cc), an increase of 1.2% over the second sample.
CA 022432~4 l998-07-l~
Example II
Propellant compositions were prepared by the following procedure. A mixing bowl was heated to 210-215~F (99-102~C). Fine to medium particulate ammonlum perchlorate (AP) was fed to the bowl, together with any burn rate catalysts, and mixed for two minutes. All remaining AP was added, and dry mixed for 3-5 minutes at high speed.
A mixture of ethylene/vinyl acetate copolymer, polybutene or other plasticizer, rheology modifiers (if present) was prepared. This mixture was added to the mixer. Mixing was continued until the polymer had melted, and then for a further 10 minutes. The resultant mixture was then extruded into propellant grains in the ram extruder.
Example III
The procedure used for preparing pre-propellant blends was as follows. Using a Ross LDM-4 double planetary mixture, the temperature was set at 265~ F
(129~ C), when the ethylene-vinyl acetate copolymer was ElvaxTX 205 or 210 polymer. All fine dry materials of the composition were added to the mixing bowl, with any dust being allowed to settle. The mixing head was then wiped to remove settled material. The Elvax ethylene-vinyl acetate copolymer and all other medium to coarse materials were added, including fluid ingredients if any.
A vacuum was then applied to the mixture.
The dry mixing cycle was commenced, at low speed mixing. The mixing speed was increased when the temperature passed the melting point of the composition, typically about 100~ C, and mixing was continued for 20 minutes. The mixing bowl was scraped down once after about 10 minutes.
The mixing head was then lifted, leaving the blades at the surface of the composition for 1-2 minutes to CA 022432~4 1998-07-1 allow adhered material to flow into the bowl with minimal trapped air. The contents of the bowl were then discharged. A similar procedure may be used with different types of mixer, including mixes that do not operate under vacuum.
Example IV
A composition was prepared in a K-5 air mixer. The mixing bowl temperature was set at 99-102~ C, and all fine to medium sized particulate ammonium perchlorate and any burn rate catalyst was added to the mix bowl. The mixture was then mixed at high speed for 2 minutes. Any remaining ammonium perchlorate was added and the resultant mixture was preheated for 3-5 minutes under high speed mixing. A mixture of Elvax ethylene/vinyl acetate copolymer with any polybutene or other plasticizer, rheology modifiers or other ingredients was then added, and mixed at a moderate mixing speed. After the mixture had reached the melting point, the mixture was mixed for a further 10 minutes. The mixture was subsequently extruded into grains.
Using this procedure a composition was prepared as follows:
Material: Weight Charged (g) AP-400* 500.5 AP-200* 115.5 AP-90* 153.5 Pre-blend** 215.5 Polybutene 6 (Soltex) 10 NZ-33 neo-alkoxy 5 zirconate***
Batch total 1000 grams * Ammonium perchlorate, with 400, 200 or 90 micron particulate size.
** Pre-blend of Example VII, below.
*** Kenrich Petrochemicals, Inc.
Processing was difficult in that the composition CA 022432~4 1998-07-1 exhibited high initial tack, requiring more frequent scraping.
The procedure was repeated, using a pre-blend of binder PB-6 and NZ-33. All ammonium perchlorate was added at the same time. The mixture dispersed easily as it heated, and suddenly transitioned into a crumbly, mobile blend. Extrusion in the ram extruder was good.
Example V
The procedure of Example IV was repeated, using the following composition:
Material: Weight Charged (g) AP-400 479.45 AP-200 122.1 AP-90 212.3 Pre-blend* 66.3 ElvaxTM 210 EVA 103.85 Polybutene-6 10 NZ-33 neo-alkoxy zirconate 5 Iron oxide Batch Total 1000 grams * Pre-blend of Example VII, below.
This formulation has reduced aluminum content (2%), an increased amount of 90 micron AP (from 25 to 30~ by weight), and iron oxide, with a proportional reduction in ammonium perchlorate of 400 micron size. These changes were intended to reduce nozzle erosion and increase ignition response.
CA 022432~4 1998-07-1 Example VI
A pre-blend batch was prepared with the following composition:
Material:Weight Charged (g) Elvax 210 EVA 719.28 Polybutene 6 0.00 Carbon Black 2.40 Zinc, (Purity Zinc Metals 1678.32 UP-6) Batch Total 2400 grams No problems were experienced in the mixing cycle, the extrusion cycle or pelletising of the pre-blend.
The pre-blend was then formulated into a propellant grain using 50.05% by weight of the pre-blend and 49.95%
by weight of 200 micron particulate ammonium perchlorate.
Example VII
A pre-blend was formed of the following composition:
Material:Weight Charged (g) Elvax 210 EVA 2088.17 Polybutene 6 0.00 Carbon Black 6.96 Aluminum, spherical904.87 Iron oxide 0.00 Batch Total 3000 grams The pre-blend was blended with ammonium perchlorate, to form propellant grain, with the resultant composition containing 21.55% by weight of the pre-blend.
No problems were encountered in the processing of the composition.
Example VIII
Samples similar to Sample #2 and #3 of Example I
were subjected to Martin-Marietta PEPcode analysis to determine characteristics of the compositions as propellants. Sample #2 is a HTPB control sample and CA 022432~4 l998-07-l~
Sample #3 iS an EVA composition of the invention.
The results obtained were as follows:
Sample #2 Sample #3 Density lb/in3O. 05946 0.06017 g/cm3 1. 6457 1.6654 Specific Impulse Frozen Flow 233.9 233.3 Shifting Flow236.3 236.6 Density Impulse Fro~en Flow 384.9 388.5 Shifting Flow388.8 394.0 The composition of the invention showed a small increase in density impulse indicating that the composition is at least equivalent to a HTPB composition, and possibly superior for some uses.
Claims (41)
1. A solid propellant composition comprising, as binder, a thermoplastic ethylene co-polymer.
2. The propellant composition of Claim 1 in which the co-polymer is a co-polymer of ethylene and a vinyl alkanoate.
3. The propellant composition of Claim 2 in which the co-polymer is ethylene/vinyl acetate copolymer.
4. The propellant composition of Claim 1 in which the copolymer is selected from an ethylene/ethyl acrylate co-polymer, ethylene/methyl acrylate co-polymer or ethylene/butyl acrylate co-polymer, a co-polymer of ethylene with acrylic acid or methylacrylic acid and an ionomer thereof.
5. The propellant composition of any one of Claims 1-4 in which the co-polymer has carbon monoxide as a copolymerized monomer.
6. The propellant composition of Claim 4 in which the co-polymer is a co-polymer of ethylene and an acrylate ester.
7. The propellant composition of Claim 1 in which the co-polymer of the binder has a moisture crosslinkable monomer.
8. The propellant composition of Claim 7 in which the moisture crosslinkable monomer is selected from vinyl trimethoxysilane and vinyltriethoxysilane.
9. The propellant composition of Claim 1 in which the binder is a silane-grafted ethylene/vinyl acetate copolymer.
10. The propellant composition of any one of Claims 1-9 comprising said binder and at least 40% by weight of an oxidizer.
11. The propellant composition of any one of Claims 1-9 comprising said binder and at least 60% by weight of an oxidizer.
12. The propellant composition of Claim 10 and Claim 11 in which the composition contains at least 70%
by weight of oxidizer.
by weight of oxidizer.
13. The propellant composition of Claim 12 in which the composition contains 75-90% by weight of oxidizer.
14. The propellant composition of any one of Claims 1-13 in which the propellant additionally contains at least one of an energetic and a ballistic modifier.
15. The propellant composition of any one of Claims 10-14 in which the oxidizer is selected from ammonium perchlorate, ammonium nitrate and potassium perchlorate.
16. The propellant composition of Claim 15 in which the oxidizer is ammonium perchlorate.
17. The propellant composition of any one of Claims 1-16 in which there is an energetic selected from the group consisting of aluminum, magnesium and aluminum/magnesium alloys.
18. The propellant composition of any one of Claims 1-17 in which there is a ballistic modifier selected from the group consisting of oxides of iron, copper, chromium and magnesium and calcium carbonate.
19. The propellant composition of any one of Claims 1-18 in which there is a modifier selected from the group consisting of a titanate, a zirconate and an aluminate.
20. The propellant composition of any one of Claims 1-19 in which there is at least one of an additive selected from opacifiers; stabilizers; metal de-activators;
anti-oxidants; flame colorants; or an agent that modifies the processing, performance, mechanical properties, storage stability or shelf life of solid propellant systems.
anti-oxidants; flame colorants; or an agent that modifies the processing, performance, mechanical properties, storage stability or shelf life of solid propellant systems.
21. The propellant composition of Claim 20 in which the stabilizer is selected from zinc oxide, nickel oxide and triacetin, and the flame colorant is selected from salts of strontium, barium, sodium and lithium.
22. The propellant composition of any one of Claims 15-21 in which the oxidizer is a mixture of particle sizes selected from coarse, medium, fine and ultrafine particles, said coarse particles being 400-600 micron, said medium particles being 50-200 micron, said fine particles being 5-15 micron and said ultrafine particles being submicron to 5 micron.
23. The propellant composition of any one of Claims 1-22 in which the composition is a gas generator propellant.
24. The propellant composition of any one of Claims 1-22 in which the propellant is a rocket propellant.
25. A method of manufacture of a propellant composition comprising:
(a) preparing a pre-propellant composition of ethylene co-polymer; and (b) admixing the pre-propellant composition with an oxidizer.
(a) preparing a pre-propellant composition of ethylene co-polymer; and (b) admixing the pre-propellant composition with an oxidizer.
26. The method of Claim 25 in which the propellant composition obtained in (b) is formed into propellant grains by an extrusion process.
27. The method of Claim 26 in which the grain is consolidated into final form under mechanical, pneumatic or hydraulic pressure or centrifugal force.
28. The method of Claim 26 or Claim 27 in which the extrusion process utilizes a cooling cycle to cool the propellant grain.
29. The method of Claim 25 in which the pre-propellant composition is prepared by melt blending.
30. The method of Claim 27 in which the propellant composition obtained in (b) is formed into fuel grains in a ram extruder.
31. The method of Claim 28 in which there is a cold cycle to cool the propellant grain so obtained.
32. The method of any one of Claims 25-31 in which the pre-propellant contains at least one of an energetic and ballistic modifier.
33. The method of Claim 32 in which the energetic is selected from the group consisting of aluminum, magnesium and aluminum/magnesium alloys.
34. The method of Claim 32 in which the ballistic modifier is selected from the group consisting of oxides of iron, copper, chromium and magnesium, and calcium carbonate.
35. The method of Claim 32 in which the pre-propellant contains at least one additive selected from opacifiers; stabilizers; metal de-activators; anti-oxidants;
flame colorants; or an agent that modifies the processing, performance, mechanical properties, storage stability or shelf life of solid propellant systems.
flame colorants; or an agent that modifies the processing, performance, mechanical properties, storage stability or shelf life of solid propellant systems.
36. The method of any one of Claims 25-35 in which the oxidizer of step (b) is selected from ammonium perchlorate, ammonium nitrate and potassium perchlorate.
37. The method of any one of Claims 25-36 in which the pre-propellant is admixed in step (b) with at least one of an energetic and a ballistic modifier.
38. The method of any one of Claims 25-37 in which the preparing of step (a) or the admixing of step (b) includes addition of at least one of opacifiers;
stabilizers; metal de-activators; anti-oxidants; flame colorants; or an agent that modifies the processing, performance, mechanical properties, storage stability or shelf life of solid propellant systems.
stabilizers; metal de-activators; anti-oxidants; flame colorants; or an agent that modifies the processing, performance, mechanical properties, storage stability or shelf life of solid propellant systems.
39. The method of any one of Claims 25-38 in which the oxidizer is a mixture of particle sizes selected from coarse, medium, fine and ultrafine particles, said coarse particles being 400-600 micron, said medium particles being 50-200 micron, said fine particles being 5-15 micron and said ultrafine particles being submicron to 5 micron.
40. The method of any one of Claims 25-39 in which the ethylene co-polymer is ethylene/vinyl acetate polymer.
41. A pre-propellant composition comprising ethylene/vinyl acetate copolymer and at least one of an energetic and a ballistic modifier.