BR112012013190A2 - aço estanhado a quente e método para produzir o mesmo - Google Patents
aço estanhado a quente e método para produzir o mesmoInfo
- Publication number
- BR112012013190A2 BR112012013190A2 BR112012013190A BR112012013190A BR112012013190A2 BR 112012013190 A2 BR112012013190 A2 BR 112012013190A2 BR 112012013190 A BR112012013190 A BR 112012013190A BR 112012013190 A BR112012013190 A BR 112012013190A BR 112012013190 A2 BR112012013190 A2 BR 112012013190A2
- Authority
- BR
- Brazil
- Prior art keywords
- produce
- same
- tinned steel
- hot tinned
- hot
- Prior art date
Links
- 229910000831 Steel Inorganic materials 0.000 title 1
- 239000010959 steel Substances 0.000 title 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05D1/00—Processes for applying liquids or other fluent materials
- B05D1/18—Processes for applying liquids or other fluent materials performed by dipping
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/12—Aluminium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/14—Removing excess of molten coatings; Controlling or regulating the coating thickness
- C23C2/16—Removing excess of molten coatings; Controlling or regulating the coating thickness using fluids under pressure, e.g. air knives
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/50—Controlling or regulating the coating processes
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
- C23C28/021—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material including at least one metal alloy layer
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
- C23C28/023—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
- C23C30/005—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process on hard metal substrates
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12736—Al-base component
- Y10T428/1275—Next to Group VIII or IB metal-base component
- Y10T428/12757—Fe
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12736—Al-base component
- Y10T428/12764—Next to Al-base component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12785—Group IIB metal-base component
- Y10T428/12792—Zn-base component
- Y10T428/12799—Next to Fe-base component [e.g., galvanized]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12861—Group VIII or IB metal-base component
- Y10T428/12903—Cu-base component
- Y10T428/12917—Next to Fe-base component
- Y10T428/12924—Fe-base has 0.01-1.7% carbon [i.e., steel]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12861—Group VIII or IB metal-base component
- Y10T428/12951—Fe-base component
- Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12861—Group VIII or IB metal-base component
- Y10T428/12951—Fe-base component
- Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
- Y10T428/12979—Containing more than 10% nonferrous elements [e.g., high alloy, stainless]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12993—Surface feature [e.g., rough, mirror]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
- Y10T428/263—Coating layer not in excess of 5 mils thick or equivalent
- Y10T428/264—Up to 3 mils
- Y10T428/265—1 mil or less
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Coating With Molten Metal (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2010033502 | 2010-02-18 | ||
PCT/JP2011/053426 WO2011102434A1 (ja) | 2010-02-18 | 2011-02-17 | 溶融めっき鋼材及びその製造方法 |
Publications (2)
Publication Number | Publication Date |
---|---|
BR112012013190A2 true BR112012013190A2 (pt) | 2016-03-01 |
BR112012013190B1 BR112012013190B1 (pt) | 2020-04-07 |
Family
ID=44483020
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112012013190A BR112012013190B1 (pt) | 2010-02-18 | 2011-02-17 | aço por imersão a quente e método para produzir o mesmo |
Country Status (13)
Country | Link |
---|---|
US (1) | US9080231B2 (pt) |
EP (1) | EP2537954B1 (pt) |
JP (1) | JP5118782B2 (pt) |
KR (3) | KR20120112450A (pt) |
CN (1) | CN102762759B (pt) |
AU (1) | AU2011216352B2 (pt) |
BR (1) | BR112012013190B1 (pt) |
CA (1) | CA2780445C (pt) |
ES (1) | ES2657614T3 (pt) |
MX (1) | MX2012005996A (pt) |
MY (1) | MY180909A (pt) |
TW (1) | TWI438302B (pt) |
WO (1) | WO2011102434A1 (pt) |
Families Citing this family (31)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101349612B1 (ko) * | 2012-03-22 | 2014-01-09 | 포스코강판 주식회사 | 용융도금욕, 도금강재 및 도금강재의 제조방법 |
WO2013160566A1 (fr) | 2012-04-25 | 2013-10-31 | Arcelormittal Investigacion Y Desarrollo, S.L. | Procédé de réalisation d'une tôle à revêtements znalmg huilés et tôle correspondante. |
KR101535073B1 (ko) * | 2012-08-01 | 2015-07-10 | 동국제강주식회사 | 가공성 및 내식성이 우수한 아연-알루미늄계 합금도금강판의 제조방법 |
US9863029B2 (en) | 2012-08-01 | 2018-01-09 | Dongkuk Steel Mill Co., Ltd. | Apparatus for forming nitrogen cloud to produce hot dip coated steel sheet |
AU2013209303B2 (en) * | 2012-08-01 | 2015-05-07 | Dongkuk Coated Metal Co., Ltd. | Method and apparatus for producing zinc-aluminum alloy-coated steel sheet with superior workability and corrosion resistance |
US20160168658A1 (en) | 2012-10-17 | 2016-06-16 | Bluescope Steel Limited | Method of producing metal-coated steel strip |
AU2013332256B2 (en) * | 2012-10-18 | 2018-03-22 | Bluescope Steel Limited | Method of producing metal coated steel strip |
WO2014125173A1 (fr) * | 2013-02-18 | 2014-08-21 | Arcelormittal Investigacion Y Desarrollo, S.L. | Procédé de préparation d'une tôle à revêtement znmg ou znaimg comprenant l'application d'une solution basique d'un agent complexant les ions magnésium et tôle obtenue |
KR101748978B1 (ko) * | 2013-03-25 | 2017-06-19 | 제이에프이 스틸 가부시키가이샤 | Al-Zn 계 도금 강판 |
KR101758529B1 (ko) * | 2014-12-24 | 2017-07-17 | 주식회사 포스코 | 인산염 처리성과 스폿 용접성이 우수한 아연합금도금강판 및 그 제조방법 |
TWI592499B (zh) | 2015-03-02 | 2017-07-21 | Jfe Galvanizing & Coating Co | Melted Al-Zn-Mg-Si plated steel sheet and manufacturing method thereof |
KR101629260B1 (ko) * | 2015-09-25 | 2016-06-10 | 포스코강판 주식회사 | 용융도금욕 조성물 |
CN105671469B (zh) * | 2016-03-22 | 2018-08-21 | 首钢集团有限公司 | 一种热浸镀钢及其制造方法 |
JP6696274B2 (ja) * | 2016-04-11 | 2020-05-20 | 日本製鉄株式会社 | 合金化溶融亜鉛めっき鋼板の製造方法 |
JP6087461B1 (ja) * | 2016-04-26 | 2017-03-01 | 日本ペイント・インダストリアルコ−ティングス株式会社 | 表面処理鋼材 |
KR101758717B1 (ko) | 2016-05-17 | 2017-07-18 | 동국제강주식회사 | 표면 품질이 우수한 용융도금강판을 제조하기 위한 질소구름을 형성하기 위한 장치 및 이를 이용한 아연-알루미늄합금도금강판을 제조하는 방법 |
KR20210068627A (ko) * | 2016-09-05 | 2021-06-09 | 제이에프이 스틸 가부시키가이샤 | 용융 Al-Zn계 도금 강판 |
CN111051558B (zh) * | 2017-09-08 | 2022-05-31 | 日本制铁株式会社 | Zn-Al-Mg系镀覆钢板 |
CN108914033B (zh) * | 2018-08-08 | 2020-02-14 | 湖南恒力通电气设备科技有限公司 | 一种钢板镀锌生产线及该生产线的镀锌工艺 |
JP7335960B2 (ja) | 2018-12-18 | 2023-08-30 | ポスコ カンパニー リミテッド | 合金コーティング鋼板およびその製造方法 |
JP7475162B2 (ja) * | 2019-03-01 | 2024-04-26 | Jfe鋼板株式会社 | 塗装鋼板及び塗装鋼板の製造方法 |
JP2020143370A (ja) * | 2019-03-01 | 2020-09-10 | Jfe鋼板株式会社 | 溶融Al−Zn−Mg−Si系めっき鋼板及びその製造方法、並びに、塗装鋼板及びその製造方法 |
JP2020139224A (ja) * | 2019-03-01 | 2020-09-03 | Jfe鋼板株式会社 | 溶融Al−Zn−Mg−Si系めっき鋼板の製造方法及び塗装鋼板の製造方法 |
JP2020164986A (ja) * | 2019-03-26 | 2020-10-08 | Jfe鋼板株式会社 | 溶融Al−Zn−Mg−Si系めっき鋼板及びその製造方法、並びに、塗装鋼板及びその製造方法 |
JP7136342B2 (ja) * | 2019-04-19 | 2022-09-13 | 日本製鉄株式会社 | めっき鋼板 |
JP7417473B2 (ja) * | 2020-05-20 | 2024-01-18 | 日鉄鋼板株式会社 | 被覆めっき鋼板 |
CN111705286A (zh) * | 2020-06-12 | 2020-09-25 | 靖江新舟合金材料有限公司 | 一种含镁锶钛的铝锌硅钢板及其生产方法 |
CN111560607B (zh) * | 2020-06-24 | 2022-08-09 | 攀钢集团攀枝花钢铁研究院有限公司 | 热镀锌铝镁钢板表面处理液及热镀锌铝镁无铬钝化板的制备方法 |
CN117265445A (zh) * | 2022-06-13 | 2023-12-22 | 宝山钢铁股份有限公司 | 一种热浸镀锌铝镁钙合金镀层钢板及其制造方法 |
CN115558877A (zh) * | 2022-09-15 | 2023-01-03 | 首钢集团有限公司 | 一种锌铝镁镀层、锌铝镁镀层钢板 |
WO2024136361A1 (ko) * | 2022-12-19 | 2024-06-27 | 주식회사 포스코 | 내식성이 우수한 도금강판 및 이의 제조방법 |
Family Cites Families (16)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4897124A (en) * | 1987-07-02 | 1990-01-30 | Sky Aluminium Co., Ltd. | Aluminum-alloy rolled sheet for forming and production method therefor |
JP2996251B2 (ja) * | 1988-10-31 | 1999-12-27 | 本田技研工業株式会社 | 成形加工用アルミニウム合金圧延板およびその製造方法 |
JP3282501B2 (ja) * | 1996-05-22 | 2002-05-13 | 日本鋼管株式会社 | 耐エッジクリープ性に優れた塗装Al−Zn系合金めっき鋼板 |
JPH11279735A (ja) | 1998-03-27 | 1999-10-12 | Nisshin Steel Co Ltd | Al−Si−Mg−Zn系溶融Al基めっき鋼板 |
JP3983932B2 (ja) | 1999-05-19 | 2007-09-26 | 日新製鋼株式会社 | 表面外観の良好な高耐食性Mg含有溶融Zn−Al系合金めっき鋼板 |
US6465114B1 (en) * | 1999-05-24 | 2002-10-15 | Nippon Steel Corporation | -Zn coated steel material, ZN coated steel sheet and painted steel sheet excellent in corrosion resistance, and method of producing the same |
JP4136286B2 (ja) | 1999-08-09 | 2008-08-20 | 新日本製鐵株式会社 | 耐食性に優れたZn−Al−Mg−Si合金めっき鋼材およびその製造方法 |
KR100446789B1 (ko) * | 2000-02-29 | 2004-09-08 | 신닛뽄세이테쯔 카부시키카이샤 | 고내식성과 우수한 가공성의 도금 강재 및 이의 제조 방법 |
JP3718479B2 (ja) | 2001-03-30 | 2005-11-24 | 新日本製鐵株式会社 | 耐食性に優れる溶融Zn−Al−Cr合金めっき鋼材 |
JP2002322527A (ja) * | 2001-04-25 | 2002-11-08 | Nippon Steel Corp | Al−Zn−Mg系合金めっき鉄鋼製品 |
JP4174058B2 (ja) * | 2002-10-28 | 2008-10-29 | 新日本製鐵株式会社 | 表面平滑性と成形性に優れる高耐食性溶融めっき鋼材と溶融めっき鋼材の製造方法 |
TW201601494A (zh) | 2005-04-04 | 2016-01-01 | 內數位科技公司 | 無縣區域網路中改善交換圖框反應性方法及裝置 |
JP4470874B2 (ja) | 2005-11-30 | 2010-06-02 | Jfeスチール株式会社 | 表面処理亜鉛系めっき鋼板 |
JP4584179B2 (ja) | 2006-04-13 | 2010-11-17 | Jfe鋼板株式会社 | 耐食性および加工性に優れた溶融Zn−Al合金めっき鋼板の製造方法 |
US20090269611A1 (en) | 2006-08-29 | 2009-10-29 | Bluescope Steel Limited | Metal-coated steel strip |
US20110027613A1 (en) * | 2008-03-13 | 2011-02-03 | Bluescope Steel Limited | Metal-coated steel strip |
-
2011
- 2011-02-17 KR KR1020127014630A patent/KR20120112450A/ko not_active Application Discontinuation
- 2011-02-17 WO PCT/JP2011/053426 patent/WO2011102434A1/ja active Application Filing
- 2011-02-17 KR KR1020147030933A patent/KR101678538B1/ko active IP Right Grant
- 2011-02-17 MX MX2012005996A patent/MX2012005996A/es active IP Right Grant
- 2011-02-17 KR KR1020167031923A patent/KR101692684B1/ko active IP Right Grant
- 2011-02-17 MY MYPI2012002404A patent/MY180909A/en unknown
- 2011-02-17 BR BR112012013190A patent/BR112012013190B1/pt active IP Right Grant
- 2011-02-17 JP JP2012500648A patent/JP5118782B2/ja active Active
- 2011-02-17 CN CN201180004914.XA patent/CN102762759B/zh active Active
- 2011-02-17 EP EP11744720.1A patent/EP2537954B1/en active Active
- 2011-02-17 US US13/513,025 patent/US9080231B2/en active Active
- 2011-02-17 AU AU2011216352A patent/AU2011216352B2/en active Active
- 2011-02-17 ES ES11744720.1T patent/ES2657614T3/es active Active
- 2011-02-17 CA CA2780445A patent/CA2780445C/en active Active
- 2011-02-18 TW TW100105485A patent/TWI438302B/zh active
Also Published As
Publication number | Publication date |
---|---|
WO2011102434A1 (ja) | 2011-08-25 |
ES2657614T3 (es) | 2018-03-06 |
MX2012005996A (es) | 2012-08-08 |
MY180909A (en) | 2020-12-11 |
CA2780445A1 (en) | 2011-08-25 |
KR20120112450A (ko) | 2012-10-11 |
KR101692684B1 (ko) | 2017-01-03 |
CA2780445C (en) | 2014-02-04 |
JPWO2011102434A1 (ja) | 2013-06-17 |
EP2537954A1 (en) | 2012-12-26 |
KR20160137650A (ko) | 2016-11-30 |
EP2537954B1 (en) | 2017-11-01 |
KR20140146167A (ko) | 2014-12-24 |
TW201144481A (en) | 2011-12-16 |
US20120282488A1 (en) | 2012-11-08 |
CN102762759A (zh) | 2012-10-31 |
US9080231B2 (en) | 2015-07-14 |
EP2537954A4 (en) | 2016-04-27 |
KR101678538B1 (ko) | 2016-11-22 |
BR112012013190B1 (pt) | 2020-04-07 |
AU2011216352A1 (en) | 2012-06-21 |
TWI438302B (zh) | 2014-05-21 |
CN102762759B (zh) | 2015-11-25 |
AU2011216352B2 (en) | 2013-06-20 |
JP5118782B2 (ja) | 2013-01-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112012013190A2 (pt) | aço estanhado a quente e método para produzir o mesmo | |
BR112012006216A2 (pt) | refrigerador e método para controlar o mesmo | |
ZA201402216B (en) | Galvanized steel sheet and method of manufacturing the same | |
DK2717999T3 (da) | Varme- og fugtveksler | |
BR112013031647A2 (pt) | polissacarídeo péctico e método para produzir o mesmo | |
PL2998414T3 (pl) | Walcowana na gorąco blacha stalowa cienka i sposób jej wytwarzania | |
PL3000905T3 (pl) | Blacha stalowa cienka walcowana na gorąco i sposób jej wytwarzania | |
EP2769071A4 (en) | SYSTEMS AND METHODS OF ENERGY CONSERVATION | |
BR112013009517A2 (pt) | chapa de aço e método para produção de chapa de aço | |
BR112013016299A2 (pt) | artigo abrasivo; e método para formar o mesmo | |
BR112013001592A2 (pt) | artigo e método | |
PL2530180T3 (pl) | Blacha stalowa cienka i sposób wytwarzania blachy stalowej cienkiej | |
BR112015010947A2 (pt) | composições e métodos para aumentar o metabolismo energético. | |
PT2663864T (pt) | Método de avaliação de imunodiversidade e seu uso | |
BR112013010847A2 (pt) | artigo e método | |
BR112013008317A2 (pt) | revestimento e método para produzir umrevestimento | |
BR112012027159A2 (pt) | estrutura e método | |
BR112014010450A2 (pt) | composição e método | |
EP2672279A4 (en) | MULTI-SOCKET AND CURRENT METHOD | |
BR112014005422A2 (pt) | suplemento de micronutriente, e, método para fazer o mesmo | |
BR112013016641A2 (pt) | artigo e método | |
BR112012022525A2 (pt) | método para produzir butanol | |
BR112014010860A2 (pt) | composição e método | |
BR112013031661A2 (pt) | método de colagem de folhas e ferramentas de colagem de folhas | |
BR112014013245A2 (pt) | método para melhorar as fotodepilação baseado em nano-complexos metálicos |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B25D | Requested change of name of applicant approved |
Owner name: NIPPON STEEL AND SUMIKIN COATED SHEET CORPORATION (JP) , NIPPON STEEL AND SUMITOMO METAL CORPORATION (JP) Owner name: NIPPON STEEL AND SUMIKIN COATED SHEET CORPORATION |
|
B06F | Objections, documents and/or translations needed after an examination request according [chapter 6.6 patent gazette] | ||
B06T | Formal requirements before examination [chapter 6.20 patent gazette] | ||
B25D | Requested change of name of applicant approved |
Owner name: NIPPON STEEL AND SUMIKIN COATED SHEET CORPORATION |
|
B25D | Requested change of name of applicant approved |
Owner name: NIPPON STEEL CORPORATION (JP) ; NIPPON STEEL COATE |
|
B09A | Decision: intention to grant [chapter 9.1 patent gazette] | ||
B16A | Patent or certificate of addition of invention granted [chapter 16.1 patent gazette] |
Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 17/02/2011, OBSERVADAS AS CONDICOES LEGAIS. |