BR102020007311A2 - composition to obtain water-based antiviral and antimicrobial coating film - Google Patents

Abstract

“COMPOSIÇÃO PARA OBTENÇÃO PELÍCULA DE REVESTIMENTO ANTIVIRAL E ANTIMICROBIANA, A BASE DE ÁGUA”. Compreendido por uma composição que detém: água de 50,00 a 70,00kg; espessante acrílico de 0,80 a 2,0kg; tensoativo não iônico de 0,05 a 0,30kg; antiespumante de 0,02 a 0,20kg; antioxidante de 0,05 a 0,20kg; nanoprata - solução aquosa estabilizada de 0,20 a 1,00kg; sílica de 0,00 a 0,50kg; copolímero acrílico - estirenado de 1,50 a 3,50kg; copolímero acrílico em dispersão 12,00 a 20,00kg; copolímero acrílico em dispersão de 8,00 a 15,00kg cera polietilenica de 1,00 a 3,00kg; alcalinizante de 0,05 a 1,00Kg.“COMPOSITION FOR OBTAINING ANTI-VIRAL AND ANTIMICROBIAL COATING FILM, THE WATER BASE”. Comprised of a composition that holds: water from 50.00 to 70.00kg; acrylic thickener from 0.80 to 2.0kg; non-ionic surfactant from 0.05 to 0.30 kg; antifoam from 0.02 to 0.20kg; antioxidant from 0.05 to 0.20kg; nano-silver - stabilized aqueous solution from 0.20 to 1.00 kg; silica from 0.00 to 0.50 kg; acrylic copolymer - styrene from 1.50 to 3.50 kg; acrylic copolymer in dispersion 12.00 to 20.00kg; acrylic copolymer in dispersion from 8.00 to 15.00kg polyethylene wax from 1.00 to 3.00kg; alkalinizing from 0.05 to 1.00Kg.

Description

001 A presente Patente de Invenção diz respeito a uma “COMPOSIÇÃO PARA OBTENÇÃO PELÍCULA DE REVESTIMENTO ANTIVIRAL E ANTIMICROBIANA, A BASE DE ÁGUA, foi desenvolvido para ser aplicado sobre um amplo espectro de superfícies, como fibrocimentos, sobre paredes pintadas com látex, tintas a óleo, papeis de paredes, quadros, metais, plásticos, tubulação e dutos de ar condicionado, madeira, têxteis, etc., constituído a partir de uma composição; polímeros acrílicos, aditivos, cera polietilenica, sílica e nanopartículas de prata estabilizada por uma superfície protetora. De forma inibir o crescimento e a permanência de bactérias e vírus em superfícies com alta solidez e persistência. tem como alvo os vírus, envelopados ou não, em envelopes lipídicos, como o caso do corona vírus.001 This Invention Patent refers to a “COMPOSITION FOR OBTAINING ANTI-VIRAL AND ANTIMICROBIAL COATING FILM, THE WATER BASE, was developed to be applied over a wide spectrum of surfaces, such as fiber cement, on walls painted with latex, oil paints , wall papers, pictures, metals, plastics, air conditioning pipes and ducts, wood, textiles, etc., made up of a composition; acrylic polymers, additives, polyethylene wax, silica and silver nanoparticles stabilized by a protective surface. In order to inhibit the growth and permanence of bacteria and viruses on surfaces with high solidity and persistence. it targets viruses, enveloped or not, in lipid envelopes, such as the case of the corona virus.

ESTADO DA TÉCNICATECHNICAL STATUS

002 A contaminação microbiana é uma preocupação essencial em nossa vida diária, quer com respeito aos moveis, corrimãos, assentos, áreas de superfície em banheiros, instrumentos cirúrgicos, paredes, pisos, brinquedos, quadros, metais, plásticos, tubulação e dutos de ar condicionado, madeira, têxteis ou tintas de parede. O uso de conservantes é um método comum para prevenir a contaminação microbiana. Entretanto, as tendências atuais mostram que os conservantes orgânicos não são bem examinados como tais por causa de questões reguladoras. Portanto, há uma real necessidade de novas substâncias antimicrobianas compatíveis e inofensivas.002 Microbial contamination is an essential concern in our daily life, whether with respect to furniture, handrails, seats, surface areas in bathrooms, surgical instruments, walls, floors, toys, pictures, metals, plastics, pipes and air conditioning ducts , wood, textiles or wall paints. The use of preservatives is a common method to prevent microbial contamination. However, current trends show that organic preservatives are not well examined as such because of regulatory issues. Therefore, there is a real need for new compatible and harmless antimicrobial substances.

003 Um grande esforço tem sido feito para desenvolver uma variedade ampla de materiais que, em vários graus, sejam eficazes em retardar ou prevenir o crescimento e destruição subsequente causada por microrganismos em uma variedade de circunstâncias. Tais materiais antimicrobianos incluíram compostos halogenados, compostos organometálicos, compostos de amônio quaternário, fenólicos, sais metálicos, aminas heterocíclicas, adutos formaldeído, compostos organosulfúricos e semelhantes.003 A great effort has been made to develop a wide variety of materials that, to varying degrees, are effective in retarding or preventing the growth and subsequent destruction caused by microorganisms in a variety of circumstances. Such antimicrobial materials included halogenated compounds, organometallic compounds, quaternary ammonium compounds, phenolics, metal salts, heterocyclic amines, formaldehyde adducts, organosulfuric compounds and the like.

004 Nenhum composto antimicrobiano orgânico simples é capaz de prover proteção contra todos os microrganismos ou é apropriado para todas aplicações. Além de tais limitações concernentes à eficácia, outras limitações podem restringir a utilidade de determinados antimicrobianos.004 No single organic antimicrobial compound is capable of providing protection against all microorganisms or is suitable for all applications. In addition to such limitations regarding efficacy, other limitations may restrict the usefulness of certain antimicrobials.

005 Por exemplo a estabilidade, propriedades físicas, perfil toxicológico, considerações reguladoras, considerações econômicas ou aspectos ambientais podem tornar um ingrediente específico inadequado para um uso específico. Portanto, existe a necessidade de desenvolver-se constantemente novas combinações que oferecerão proteção de amplo espectro para uma variedade de necessidades.005 For example stability, physical properties, toxicological profile, regulatory considerations, economic considerations or environmental aspects can make a specific ingredient unsuitable for a specific use. Therefore, there is a need to constantly develop new combinations that will offer broad spectrum protection for a variety of needs.

006 Atualmente aproveitando os avanços feitos no campo de recobrimentos inteligentes, diversos fabricantes de tinta estão trazendo ao mercado uma nova qualidade de tinta antibacteriana, higiênica e/ou hospitalar contendo sais de prata ou prata metálica, entretanto, para o mercado de tintas. É indicada para pintura de superfícies externas e internas de clínicas e centros hospitalares, cirúrgicos, salas de espera, enfermaria, U.T.I, áreas de circulação e cozinhas industriais, onde a redução da proliferação de fungos e bactérias é requerida. No mercado de embalagens, as embalagens ativas como são conhecidas, possuem interação com o produto, desta forma, com o objetivo de preservar sua qualidade e garantir sua segurança, corrigindo desta forma, limitações das embalagens convencionais, aumentando assim, o tempo de vida, segurança e qualidade dos alimentos. O uso de filmes plásticos com agentes antimicrobianos tem como vantagem sobre a incorporação do agente antimicrobiano.006 Currently taking advantage of the advances made in the field of intelligent coatings, several paint manufacturers are bringing to the market a new quality of antibacterial, hygienic and / or hospital paint containing silver or metallic silver salts, however, for the paint market. It is indicated for painting external and internal surfaces of clinics and hospitals, surgical centers, waiting rooms, infirmary, U.T.I, circulation areas and industrial kitchens, where the reduction of the proliferation of fungi and bacteria is required. In the packaging market, active packaging as it is known, has interaction with the product, in this way, with the objective of preserving its quality and guaranteeing its safety, thus correcting limitations of conventional packaging, thus increasing the life span, food safety and quality. The use of plastic films with antimicrobial agents has the advantage over the incorporation of the antimicrobial agent.

007 Os agentes antimicrobianos podem ser incorporados diretamente ao material plástico, em rótulos/etiquetas ou estar contidos em sachês. De acordo com BRODY et.al. (2001), dentre os agentes antimicrobianos, os de maior potencial parecem ser aqueles contendo sais de prata, capazes de liberar íons do metal. Na indústria farmacêutica, algumas empresas utilizam a prata em curativos para o tratamento de feridas. A tecnologia do curativo consiste em recobrir diferentes tipos de fios com uma camada de prata metálica. Isso garante uma liberação sustentada de prata ao longo do produto. Pode ser utilizado em contato direto com a ferida em ambos os lados, onde desenvolve uma potente ação antimicrobiana, sendo capaz de combater os micro-organismos presentes no leito da ferida, assim como prevenir que uma ferida limpa fique infectada. A prata metálica permite também o beneficiamento de tecidos, com características antimofo e antiodor. A substância é incorporada nas fibras dos tecidos e proporciona uma atividade antimicrobiana extremamente efetiva, mesmo após inúmeras lavagens a úmido.007 Antimicrobial agents can be incorporated directly into the plastic material, in labels / tags or be contained in sachets. According to BRODY et.al. (2001), among the antimicrobial agents, those with the greatest potential appear to be those containing silver salts, capable of releasing metal ions. In the pharmaceutical industry, some companies use silver in dressings to treat wounds. The dressing technology consists of covering different types of threads with a layer of metallic silver. This ensures a sustained release of silver throughout the product. It can be used in direct contact with the wound on both sides, where it develops a potent antimicrobial action, being able to combat microorganisms present in the wound bed, as well as preventing a clean wound from becoming infected. Metallic silver also allows for the improvement of fabrics, with anti-mold and anti-odor characteristics. The substance is incorporated into the fibers of the tissues and provides an extremely effective antimicrobial activity, even after numerous wet washes.

008 Biocidas tipo mercúrio tem sido largamente usados como ambos conservantes e nigelicidas em tintas. Eles têm excelente performance em ambas funções em muitas situações. Eles oferecem rápido tempo de morte e podem controlar altos níveis de contaminação bacteriana. Infelizmente, eles são perigosos para manusear e podem apresentar problemas ambientais.008 Mercury-type biocides have been widely used as both preservatives and nigelicides in paints. They perform excellently in both roles in many situations. They offer fast time to death and can control high levels of bacterial contamination. Unfortunately, they are dangerous to handle and can present environmental problems.

009 Assim, seu uso pode ser limitado a certas aplicações. Vários nigelicidas e conservantes sem mercúrio e têm sido grandemente considerados como substitutos para compostos de mercúrio.009 Thus, its use may be limited to certain applications. Various mercury-free nigelicides and preservatives have been widely considered as substitutes for mercury compounds.

010 A patente PI9807254-4 trata de uma composição de revestimento aquoso compreendendo: (a) água, (b) uma base média, (c) um sal de piritiona, em uma quantidade de 0,01% a 2,0% baseada no peso da composição, e (d) composto de óxido de zinco selecionado das muitas graduações adequadas para manufatura de tinta, a uma concentração de 0,001% a 10%, baseada no peso da composição de revestimento. Também foi divulgada uma composição de revestimento antimicrobiana, caracterizada pela eficácia anti-mofo e proteção contra descoloração atribuível à presença de piritiona nela, referida composição sendo selecionada do grupo consistido de tintas de base em água, adesivos, vedantes selantes, e combinações destes, a referida composição compreendendo água, um asl ou ácido de piritiona, uma base orgânica média e um composto de zinco, o referido íon zinco estando presente na referida composição em uma quantidade de 0,001% a 10%, baseada no peso da composição de revestimento.010 Patent PI9807254-4 deals with an aqueous coating composition comprising: (a) water, (b) a medium base, (c) a pyrithione salt, in an amount of 0.01% to 2.0% based on weight of the composition, and (d) zinc oxide compound selected from the many grades suitable for paint manufacture, at a concentration of 0.001% to 10%, based on the weight of the coating composition. An antimicrobial coating composition was also disclosed, characterized by the anti-mold efficacy and protection against discoloration attributable to the presence of pyrithione in it, said composition being selected from the group consisting of water-based paints, adhesives, sealants, and combinations thereof, a said composition comprising water, an asl or pyrithione acid, a medium organic base and a zinc compound, said zinc ion being present in said composition in an amount of 0.001% to 10%, based on the weight of the coating composition.

011 A patente PI0303682-0 trata de uma tinta em pó do tipo híbrido, esta é caracterizada pelo fato de apresentar uma composição que compreende 35-70% de resina poliéster com grupos COOH, 15-50% de resina epóxi, 0,12,0% de agente endurecedor, 0,1-5,0% de aditivos contendo o agente animicrobiano, 0-35% de pigmento inorgânico, 0-5% de pigmento orgânico e 0-45% de carga, sendo que o agente bactericida tem como princípio ativo o poli(he-xametilenobiguanida)-PHMB. O método também objeto desta Privilégio de Invenção é caracterizado pelo fato de partir compreender uma primeira etapa de pré-mistura, onde os componentes básicos da tinta que são resinas, agentes de cura, pigmentos, aditivos e cargas são submetidos a um prémisturador (1) sendo que após passar pelo pré-misturador (1); uma segunda que compreende a extrusão do material, etapa que ocorre após o volume de material processado no pré-misturador (1) ser direcionado para um alimentador-dosador (2), o qual opera em conjunto com uma extrusora (3), sendo que o material processado pela extrusora (3) sai de sua saída (4) e é imediatamente alimentado em um conjunto de rolos laminadores (5); uma terceira etapa que compreende o resfriamento do material, etapa que ocorre pela deposição do material processado pelo conjunto de rolos laminadores (5) por sobre uma esteira resfriadora (6), dito material é então alimentado em um triturador (7); uma quarta etapa onde ocorre a micronização do material processado e em um micronizador (8), equipamento que processa o material em escamas recebido do triturador (7); e uma etapa de classificação, onde o material micronizado é enviado ao filtro de mangas (9), que opera com fluxo de ar gerado pelo ventilador de sucção (10).011 The patent PI0303682-0 deals with a hybrid type powder paint, this is characterized by the fact that it has a composition comprising 35-70% polyester resin with COOH groups, 15-50% epoxy resin, 0.12, 0% hardening agent, 0.1-5.0% additives containing the animicrobial agent, 0-35% inorganic pigment, 0-5% organic pigment and 0-45% filler, the bactericidal agent having the active ingredient is poly (he-xamethylenebiguanide) -PHMB. The method also object of this Invention Privilege is characterized by the fact that it comprises a first pre-mixing step, where the basic components of the paint, which are resins, curing agents, pigments, additives and fillers, are subjected to a premixer (1) being that after going through the pre-mixer (1); a second which comprises the extrusion of the material, a step that occurs after the volume of material processed in the pre-mixer (1) is directed to a feeder-doser (2), which operates in conjunction with an extruder (3), the material processed by the extruder (3) leaves its outlet (4) and is immediately fed into a set of rolling rolls (5); a third step that comprises the cooling of the material, a step that occurs by depositing the material processed by the set of laminating rollers (5) on a cooling belt (6), said material is then fed into a crusher (7); a fourth step where the micronization of the processed material takes place and in a micronizer (8), equipment that processes the scaled material received from the crusher (7); and a classification step, where the micronized material is sent to the bag filter (9), which operates with air flow generated by the suction fan (10).

012 Já a patente EP O 251 783 descreve uma composição antimicrobiana compreendendo um composto de prata antimicrobiano, tal como cloreto de prata ou fosfato de prata, depositado em um material de suporte sintético fisiologicamente inerte, tal como óxidos de titânio, alumínio ou silício na forma particulada. A área de superfície dos materiais de suporte adequados deve ser prolongada. A composição antimicrobiana resultante pode ser dispersa em um material polimérico para prevenir uma contaminação antimicrobiana.012 EP patent 251 783 describes an antimicrobial composition comprising an antimicrobial silver compound, such as silver chloride or silver phosphate, deposited on a physiologically inert synthetic support material, such as titanium, aluminum or silicon oxides in the form particulate. The surface area of suitable support materials should be extended. The resulting antimicrobial composition can be dispersed in a polymeric material to prevent antimicrobial contamination.

013 A combinação, da atividade antimicrobiana e condutividade elétrica; é descrita em EP O 427 858. Uma partícula fina inorgânica, tal como óxido de mica, alumina ou titânio é revestida com um metal antibacteriano tal como, prata, cobre, zinco ou chumbo - e/ou composto de metal antibacteriano. As partículas resultantes podem ser introduzidas em polímeros sintéticos desse modo obtendo os polímeros eletricamente condutor e antibacterianos.013 The combination of antimicrobial activity and electrical conductivity; is described in EP O 427 858. A fine inorganic particle, such as mica oxide, alumina or titanium is coated with an antibacterial metal such as silver, copper, zinc or lead - and / or an antibacterial metal compound. The resulting particles can be introduced into synthetic polymers in this way obtaining the electrically conductive and antibacterial polymers.

014 Enquanto a patente EP O 677 989 divulga uma composição em pó antimicrobiana compreendendo partículas inorgânicas, tal como óxidos de titânio, alumínio ou zinco, mica ou sílica, tendo um revestimento de superfície primário de um metal ou composto de metal, tal como prata, cobre, óxido de prata, haletos de prata, óxido de cobre, silicato de zinco, óxido de zinco ou misturas destes, e um revestimento secundário fornecendo uma função protetora, tal como sílica e alumina. O revestimento secundário funciona como uma barreira entre a partícula antimicrobiana e uma matriz do polímero na qual ela possa ser incorporada. Além disso, a camada do revestimento secundário é acreditada influenciar a taxa na qual o componente antimicrobiano difunde de uma partícula dispersa no polímero.014 While EP 0 677 989 discloses an antimicrobial powder composition comprising inorganic particles, such as titanium, aluminum or zinc oxides, mica or silica, having a primary surface coating of a metal or metal compound, such as silver, copper, silver oxide, silver halides, copper oxide, zinc silicate, zinc oxide or mixtures thereof, and a secondary coating providing a protective function, such as silica and alumina. The secondary coating acts as a barrier between the antimicrobial particle and a polymer matrix in which it can be incorporated. In addition, the secondary coating layer is believed to influence the rate at which the antimicrobial component diffuses from a particle dispersed in the polymer.

015 É objetivo do presente pedido de patente prover uma composição para ser aplicada em diversas superfícies, de forma a impedir meios de propagação, hospedando vírus e bactérias prejudiciais a saúde e ao meio ambiente, bem como contribuir para reduzir o risco e a velocidade de contaminação e transmissão do corona vírus.015 The purpose of the present patent application is to provide a composition to be applied on various surfaces, in order to prevent means of propagation, hosting viruses and bacteria harmful to health and the environment, as well as to contribute to reduce the risk and speed of contamination. and transmission of the corona virus.

016 É ainda objetivo do presente pedido de patente prover uma composição para ser aplicada em diversas superfícies, cuja função é desativar o vírus no menor tempo possível, auxiliando na inibição e replicação de bactérias, as quais podem ser consideradas possíveis hospedeiras para o vírus, que é um parasita intracelular obrigatório.016 It is also the objective of the present patent application to provide a composition to be applied on several surfaces, whose function is to deactivate the virus in the shortest possible time, assisting in the inhibition and replication of bacteria, which can be considered possible hosts for the virus, which it is a mandatory intracellular parasite.

017 É ainda objetivo do presente pedido de patente prover uma composição em forme de um verniz leitoso a base de água, com uma forte ação de repelência a água e antimicrobiana, para ser aplicada em diversas superfícies.017 It is also the objective of the present patent application to provide a composition in the form of a water-based milky varnish, with a strong water-repellent and antimicrobial action, to be applied on various surfaces.

018 É ainda objetivo do presente pedido de patente prover uma composição, atóxico para ser aplicado sobre várias superfícies sem a necessidade de lixamento prévio para promover aderência, é necessário somente a limpeza e descontaminação da superfície.018 It is also the objective of the present patent application to provide a composition, non-toxic to be applied on various surfaces without the need for prior sanding to promote adhesion, it is only necessary to clean and decontaminate the surface.

019 É ainda objetivo do principal do presente pedido de patente uma “COMPOSIÇÃO PARA OBTENÇÃO PELÍCULA DE REVESTIMENTO ANTIVIRAL E ANTIMICROBIANA, A BASE DE ÁGUA” obtida por uma composição que detém: água de 50,00 a 70,00kg; espessante acrílico de 0,80 a 2,0kg; tensoativo não iônico de 0,05 a 0,30kg; antiespumante de 0,02 a 0,20kg; antioxidante de 0,05 a 0,20kg; nanoprata - solução aquosa estabilizada de 0,20 a 1,00kg; sílica de 0,00 a 0,50kg; copolímero acrílico - estirenado de 1,50 a 3,50kg; copolímero acrílico em dispersão 12,00 a 20,00kg; copolímero acrílico em dispersão de 8,00 a 15,00kg cera polietilenica de 1,00 a 3,00kg; alcalinizante de 0,05 a 1,00Kg.019 The main objective of the present patent application is also a “COMPOSITION TO OBTAIN ANTI-VIRAL AND ANTIMICROBIAL COATING FILM, THE WATER BASE” obtained by a composition that holds: water from 50.00 to 70.00kg; acrylic thickener from 0.80 to 2.0kg; non-ionic surfactant from 0.05 to 0.30kg; antifoam from 0.02 to 0.20kg; antioxidant from 0.05 to 0.20kg; nano-silver - stabilized aqueous solution from 0.20 to 1.00 kg; silica from 0.00 to 0.50 kg; acrylic copolymer - styrene from 1.50 to 3.50 kg; acrylic copolymer in dispersion 12.00 to 20.00kg; acrylic copolymer in dispersion from 8.00 to 15.00kg polyethylene wax from 1.00 to 3.00kg; alkalinizing from 0.05 to 1.00Kg.

020 Com base no descrito podemos dizer que a “COMPOSIÇÃO PARA OBTENÇÃO PELÍCULA DE REVESTIMENTO ANTIVIRAL E ANTIMICROBIANA, A BASE DE ÁGUA”, é um produto que traz enormes vantagens, pois sua função é desativar o vírus no menor tempo possível, auxiliando na inibição e replicação de bactérias, as quais podem ser consideradas possíveis hospedeiras para o vírus, que eh um parasita intracelular obrigatório.020 Based on what has been described, we can say that the “COMPOSITION FOR OBTAINING AN ANTIVIRAL AND ANTIMICROBIAL COATING FILM, THE WATER BASE”, is a product that brings enormous advantages, as its function is to deactivate the virus in the shortest possible time, helping in the inhibition and replication of bacteria, which can be considered possible hosts for the virus, which is a mandatory intracellular parasite.

021 Sua obtenção consiste em: - pesar os materiais pela ordem com agitação lenta e constante: água 50 a 70kg; espessante acrílico 0,80 a 2,20kg; umectante 0,20kg; tensoativo não iônico 0,05 a 2,0kg; antiespumante 0,02 a 0,20kg; antioxidante 0,05 a 0,20kg, em seguida após a homogeneização, adicionar pela ordem com agitação lenta: solução aquosa de nanoprata estabilizada 0,2 a 1,0kg. Após a dissolução total da dessa mistura, adicionar sílica 0,00 a 0,5kg, após a homogeneização da mistura adicionar resina acrílica metalizada 2,00kg; resina acrílica estirenada 29,00kg; cera polietilenica 2,00kg; por fim ajustar o PH alcalinizante.021 Its obtainment consists of: - weighing the materials in order with slow and constant agitation: water 50 to 70kg; acrylic thickener 0.80 to 2.20kg; humectant 0.20kg; non-ionic surfactant 0.05 to 2.0kg; antifoam 0.02 to 0.20kg; antioxidant 0.05 to 0.20kg, then after homogenization, add in order with slow stirring: aqueous solution of stabilized nano-silver 0.2 to 1.0kg. After the total dissolution of this mixture, add silica 0.00 to 0.5 kg, after homogenization of the mixture add 2.00 kg metallized acrylic resin; styrene acrylic resin 29.00kg; 2.00kg polyethylene wax; finally adjust the alkalizing PH.

022 O produto obtido deve ser aplicado sobre as superfícies através de spray, rolo, pincel e imersão a base de água em duas demãos, garantindo o revestimento em toda área da superfície, não é necessário lixamento prévio, apenas a limpeza e descontaminação.022 The product obtained must be applied to the surfaces by spray, roller, brush and water-based immersion in two coats, guaranteeing the coating on the entire surface area, prior sanding is not necessary, only cleaning and decontamination.

023 A secagem ao toque ocorre após a eliminação da água do filme, por volta de 4 horas, porém a cura total se dá em 72 horas, ela pode ser acelerada através de sopramento de ar quente, a película formada poderá ser brilhante, semibrilho acetinada ou fosca, sendo um produto leitoso que ao secar torna-se transparente, e repelente a água. Em dias úmidos ou frios o produto leva mais tempo para secar.023 Touch drying occurs after removing the water from the film, around 4 hours, but the total cure takes place in 72 hours, it can be accelerated by blowing hot air, the formed film can be shiny, satin semi-gloss or matte, being a milky product that on drying becomes transparent, and repels water. On damp or cold days the product takes longer to dry.

024 Estas misturas antimicrobianas fornecem um alto nível de atividade por um período de tempo prolongado, provendo as resistências dos ingredientes individuais, enquanto minimizando a fraqueza de cada um. É este tipo de atividade complemente que permite que se use a formulação cuja combinação obtém-se um efeito desejado em níveis que não podem ser obtidos com qualquer um dos ingredientes individuais.024 These antimicrobial mixtures provide a high level of activity for an extended period of time, providing the strengths of the individual ingredients, while minimizing the weakness of each. It is this type of complementary activity that allows the use of the formulation whose combination achieves a desired effect at levels that cannot be achieved with any of the individual ingredients.

025 Devemos salientar que o composto segue rigorosamente os testes que acordo com norma JIS Z 2801, que efetua a avaliação da eficácia de um produto antimicrobiano a serem aplicadas em materiais como plásticos e outros materiais poliméricos.025 We must point out that the compound strictly follows the tests according to JIS Z 2801, which evaluates the effectiveness of an antimicrobial product to be applied to materials such as plastics and other polymeric materials.

026 Por ser inovador e até então não compreendidas no estado da técnica que se enquadra perfeitamente dentro dos critérios que definem a patente de invenção. São as seguintes suas reivindicações.026 For being innovative and until then not understood in the state of the art that fits perfectly within the criteria that define the invention patent. The following are his claims.

Claims (1)

1 - “COMPOSIÇÃO PARA OBTENÇÃO PELÍCULA DE REVESTIMENTO ANTIVIRAL E ANTIMICROBIANA, A BASE DE ÁGUA” caracterizado por uma composição que detém: água de 50,00 a 70,00kg; espessante acrílico de 0,80 a 2,0kg; tensoativo não iônico de 0,05 a 0,30kg; antiespumante de 0,02 a 0,20kg; antioxidante de 0,05 a 0,20kg; nanoprata - solução aquosa estabilizada de 0,20 a 1,00kg; sílica de 0,00 a 0,50kg; copolímero acrílico - estirenado de 1,50 a 3,50kg; copolímero acrílico em dispersão 12,00 a 20,00kg; copolímero acrílico em dispersão de 8,00 a 15,00kg cera polietilenica de 1,00 a 3,00kg; alcalinizante de 0,05 a 1,00Kg.1 - “COMPOSITION FOR OBTAINING ANTI-VIRAL AND ANTIMICROBIAL COATING FILM, THE WATER BASE” characterized by a composition that holds: water from 50.00 to 70.00kg; acrylic thickener from 0.80 to 2.0kg; non-ionic surfactant from 0.05 to 0.30kg; antifoam from 0.02 to 0.20kg; antioxidant from 0.05 to 0.20kg; nano-silver - stabilized aqueous solution from 0.20 to 1.00 kg; silica from 0.00 to 0.50 kg; acrylic copolymer - styrene from 1.50 to 3.50 kg; acrylic copolymer in dispersion 12.00 to 20.00kg; acrylic copolymer in dispersion from 8.00 to 15.00kg polyethylene wax from 1.00 to 3.00kg; alkalinizing from 0.05 to 1.00Kg.