WO2024080805A1 - 복합 고체 전해질 및 이의 제조방법 - Google Patents
복합 고체 전해질 및 이의 제조방법 Download PDFInfo
- Publication number
- WO2024080805A1 WO2024080805A1 PCT/KR2023/015786 KR2023015786W WO2024080805A1 WO 2024080805 A1 WO2024080805 A1 WO 2024080805A1 KR 2023015786 W KR2023015786 W KR 2023015786W WO 2024080805 A1 WO2024080805 A1 WO 2024080805A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- solid electrolyte
- group
- composite solid
- polymer
- cross
- Prior art date
Abstract
본 발명은 복합 고체 전해질 및 이의 제조방법에 관한 것이다. 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머를 포함하는 고분자; 세라믹 화합물; 및 극성 화합물을 포함하고, 상기 가교 결합성 작용기의 적어도 일부는 서로 가교 결합을 형성하여, 상기 고분자가 3차원 네트워크 구조를 형성하고 있고, 상기 극성 화합물은 기체 상태로 상기 3차원 네트워크 구조 내에 포함되거나, 상기 고분자 사슬 상에 결합되어 있는 것이다.
Description
관련 출원(들)과의 상호 인용
본 출원은 2022년 10월 14일자 한국 특허 출원 제 10-2022-0132765호 및 2023년 10월 12일자 한국 특허 출원 제10-2023-0136066호에 기초한 우선권의 이익을 주장하며, 해당 한국 특허 출원의 문헌에 개시된 모든 내용은 본 명세서의 일부로서 포함된다.
본 발명은 복합 고체 전해질 및 이의 제조방법에 관한 것이다.
액체 전해질을 사용하는 리튬 이온전지는 분리막에 의해 음극과 양극이 구획되는 구조여서 변형이나 외부 충격으로 분리막이 훼손되면 단락이 발생할 수 있으며 이로 인해 과열 또는 폭발 등의 위험으로 이어질 수 있다. 따라서 리튬 이온 이차전지 분야에서 안전성을 확보할 수 있는 고체 전해질의 개발은 매우 중요 한 과제라고 할 수 있다.
고체 전해질을 이용한 리튬 이차전지는 전지의 안전성이 증대되며, 전해액의 누출을 방지할 수 있어 전지의 신뢰성이 향상되며, 박형의 전지 제작이 용이하다는 장점이 있다. 또한, 음극으로 리튬 금속을 사용할 수 있어 에너지 밀도를 향상시킬 수 있으며 이에 따라 소형 이차전지와 더불어 전기 자동차용의 고용량 이차전지 등에 응용이 기대되어 차세대 전지로 각광받고 있다.
고체 전해질 중에서도 고분자 고체 전해질은 이온 전도성 재질의 고분자 재료를 사용할 수 있으며, 이러한 고분자 재료와 함께 무기 재료를 혼합한 복합 고체 전해질의 형태로 사용할 수 있다.
이와 같은 종래 하이브리드형(복합) 고체 전해질은 고분자 매트릭스에 산화물계 세라믹 등의 무기물 파우더를 분산시켜 제조한 것으로, 기존의 액체 전해질에 비해 높은 발화 및 연소 안정성을 가지고, 고분자 고체 전해질에 비해 높은 이온전도도를 가진다는 장점이 있으나, 고분자 매트릭스 내의 산화물계 세라믹 입자의 분산성 향상 및 사용되는 고분자 매트릭스의 물성 최적화 등 기본적인 전제 조건이 충족되어야 한다는 어려움이 있었다. 특히, 폴리에틸렌옥사이드(PEO)와 같이 결정성이 높은 고분자를 매트릭스로 사용할 경우, 이온전도도가 향상된 복합 고체 전해질을 제조하기 어렵다는 문제가 있었다. 즉, PEO 고분자의 높은 결정화도로 인하여 고분자의 사슬의 이동도(chain mobility)가 저해되고, 고분자 고체 전해질 내부의 리튬 이온이 이동하는데 제약이 있기 때문에, 고분자 고체 전해질의 이온전도도를 향상시키는데 한계가 있었던 것이다.
이러한 종래 복합 고체 전해질의 한계를 극복하기 위하여, 결정성 고분자의 구조를 변형하거나 또는 상기 고분자에 별도의 가소제(plasticizer)를 첨가하여 고분자 사슬의 이동도를 개선시켜 복합 고체 전해질의 이온전도도를 향상시키려는 노력이 있었으나, 이러한 고분자의 구조 변형이나 가소제 첨가 방식만으로는 복합 고체 전해질의 이온전도도를 향상시키는데 어려움이 있었다.
이에, 고분자의 구조 변형이나 가소제 첨가가 아닌 방식으로 복합 고체 전해질의 이온전도도를 향상시킬 수 있는 기술개발이 요구되고 있다.
[선행기술문헌]
[특허문헌]
(특허문헌 0001) 일본 공개 특허 제1994-124713호
본 발명은 복합 고체 전해질에 극미량의 극성 화합물(예를 들어, 극성 용매 화합물)이 비액체 상태로 부가되더라도, 이온 전도도의 개선이 가능한 복합 고체 전해질 및 이의 제조방법을 제공하는 것이다.
또, 본 발명은 상기 복합 고체 전해질을 포함하여, 향상된 이온 전도도 등을 나타내는 전고체 전지를 제공하는 것이다.
발명의 일 구현예에 따르면, 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머를 포함하는 고분자; 세라믹 화합물 및 극성 화합물을 포함하며, 상기 가교 결합성 작용기의 적어도 일부는 서로 가교 결합을 형성하여, 상기 고분자가 3차원 네트워크 구조를 형성하고 있고, 상기 극성 화합물은 기체 상태로 상기 3차원 네트워크 구조 내에 포함되거나, 상기 고분자 사슬 상에 결합되어 있는 복합 고체 전해질이 제공된다.
이러한 복합 고체 전해질에서, 상기 기체 상태의 극성 화합물은 상기 3차원 네트워크 구조를 형성한 고분자 사슬 사이에 분산되어 있거나, 상기 고분자 사슬의 표면 또는 내부에 흡착 또는 결합될 수 있다.
또, 상기 복합 고체 전해질은 가교제를 더 포함할 수 있고, 이 경우, 상기 가교 결합성 작용기의 적어도 일부는 상기 가교제를 매개로 서로 가교 결합을 형성할 수 있다.
상기 복합 고체 전해질에서, 상기 PEO계 코폴리머는 1종 이상, 혹은 2종 이상의 가교 결합성 작용기를 포함할 수 있고, 상기 가교 결합성 작용기는 상기 PEO계 코폴리머에 탄소수 0 내지 10의 알킬렌 링커 또는 알킬렌 옥사이드 링커(단, 탄소수 0인 알킬렌 링커는 단일 결합을 나타낸다)를 매개로 고분자 사슬에 결합되어 있고, 히드록시기(hydroxyl group), 카복실기(carboxyl group), 이소시아네이트기(isocyanate group), 니트로기(nitro group), 시아노기 (cyano group), 아민기(amine group), 아미드기(amide group), 에폭시기(epoxy group) 및 알릴기(allyl group)로 이루어진 군에서 선택되는 작용기로 될 수 있다.
또한, 상기 복합 고체 전해질은 상기 리튬염을 더 포함할 수 있으며, 이러한 리튬염은 이 중 적어도 일부가 해리된 양이온 및 음이온 상태로 포함될 수 있다. 상기 양이온 및/또는 음이온은 상기 고분자 상에 결합된 상태로 존재할 수 있고, 전지의 충/방전시 이동할 수 있다.
구체적인 실시예에서, 상기 복합 고체 전해질의 PEO(polyethylene oxide)계 코폴리머는 하기 화학식 1 내지 3의 반복 단위를 포함하는 공중합체로 될 수 있다:
[화학식 1]
[화학식 2]
[화학식 3]
상기 화학식 1 내지 3에서, R1은 -CH2-O-(CH2-CH2-O)k-R3 를 나타내며, k는 0 내지 20이고, R3는 탄소수 1 내지 5의 알킬기를 나타내고, R2는 히드록시기(hydroxyl group), 카복실기(carboxyl group), 이소시아네이트기(isocyanate group), 니트로기(nitro group), 시아노기(cyano group), 아민기(amine group), 아미드기(amide group), 에폭시기 (epoxy group) 및 알릴기(allyl group)로 이루어진 군에서 선택된 1종 이상의 가교 결합성 작용기가 탄소수 0 내지 10의 알킬렌 링커 또는 알킬렌 옥사이드 링커(단, 탄소수 0인 알킬렌 링커는 단일 결합을 나타낸다)를 매개로 고분자 사슬에 결합된 치환기를 나타내며, l, m 및 n은 반복 단위의 반복수로, l 및 n은 각각 독립적으로 1 내지 1000의 정수이고, m은 0 내지 1000의 정수이다.
한편, 이러한 복합 고체 전해질에서, 상기 극성 화합물의 함량은 복합 고체 전해질의 총 중량 기준으로, 0.1 중량% 이상 내지 10 중량% 미만으로 될 수 있다.
또, 상기 극성 화합물은 카보네이트계 화합물 및 설포닐계 화합물로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있고, 카보네이트계 용매 및 설포닐계 용매에서 유래하여 기체 상태로 포함된 극성 화합물로 될 수 있다. 보다 구체적으로, 상기 극성 화합물은 에틸메틸카보네이트(Ethyl Methyl carbonate, EMC), 디메틸카보네이트(Dimethyl Carbonate, DMC), 디에틸카보네이트(Diethyl Carbonate, DEC), 에틸렌카보네이트(Ethylene Carbonate, EC), 프로필렌카보네이트(Propylene Carbonate, PC), 비닐렌카보네이트(Vinylene Carbonate, VC) 및 술폴레인 (Sulfolane)으로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다.
또한, 상기 세라믹 화합물은 리튬 금속 산화물 또는 리튬 금속 인산화물의 산화물계 고체 전해질을 포함할 수 있고, 보다 구체적으로, 리튬-란타늄-지르코늄 산화물계(LLZO) 화합물, 리튬-실리콘티타늄 인산염계(LSTP) 화합물, 리튬-란타늄-티타늄 산화물계(LLTO) 화합물, 리튬-알루미늄-티타늄 인산염계(LATP) 화합물, 리튬-알루미늄-게르마늄 인산염계(LAGP) 화합물 및 리튬-란타늄-지르코늄-티타늄 산화물계(LLZTO) 화합물로 이루어진 군에서 선택되는 1종 이상의 산화물계 고체 전해질을 포함할 수 있다.
한편, 발명의 다른 구현예에 따르면, (S1) 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머와 세라믹 화합물을 혼합한 후, 상기 혼합물에 포함된 상기 PEO계 코폴리머에 대해 가교 결합 반응을 진행하는 단계; 및 (S2) 상기 (S1) 단계에서 가교된 고분자를 포함하는 혼합물에 극성 용매를 증기 증착 시키는 단계;를 포함하는 상기 일 구현예의 복합 고체 전해질의 제조방법이 제공된다.
이러한 제조방법에서, 상기 (S1)의 가교 결합 반응 단계는 가교제 및 개시제로 이루어진 군에서 선택되는 1종 이상의 추가 존재 하에 진행될 수 있다.
한편, 상기 제조방법에서, 상기 극성 용매는 상기 일 구현예의 극성 화합물에 대응하는 극성 용매로 될 수 있다.
또, 상기 제조방법에서, 상기 (S2) 단계에서는, 상기 극성 용매의 함량이 복합 고체 전해질의 총 중량 기준으로, 0.1 중량% 이상 내지 10 중량% 미만이 되도록, 상기 고분자에 상기 극성 용매의 증기를 증착시킬 수 있다.
발명의 또 다른 구현예에 따르면, 상술한 일 구현예의 복합 고체 전해질을 포함한 전해질층을 포함하는 전고체 전지가 제공된다.
발명의 일 구현예에 따른 복합 고체 전해질은 고분자 사슬의 변형이나 파괴없이 고분자 본연의 구조적 특성을 유지하면서, 고분자의 사슬의 이동도(mobility) 향상 및 복합 고체 전해질 내의 세라믹 입자를 균일하게 분포시킴으로써 복합 고체 전해질의 이온전도도를 향상시킬 수 있다.
또한, 상기 복합 고체 전해질은 극미량의 극성 화합물을 기체 상태로 포함함으로써, 고분자 고체 전해질의 이온 전도도 및 기계적 물성을 향상시킬 수 있다.
또한, 증기 증착에 의해 극성 용매를 복합 고체 전해질 내부에 포함되게 할 경우, 겔화(gelation)를 방지하고 내부 고분자 사슬의 완화 시간 (relaxation time)을 지연시켜 고분자 사슬의 이동도를 향상시킴으로써 기계적 물성 저하 없이 이온 전도도를 개선시킬 수 있다.
이하, 발명에 대한 이해를 돕기 위하여 발명의 구체적인 구현예들을 더욱 상세하게 설명한다.
본 명세서 및 청구범위에서 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.
본 명세서에서 사용된 용어 "결합", 즉, 극성 화합물이 고분자 사슬, 예를 들어, PEO계 코폴리머의 사슬에 "결합"된 형태와 관련하여, 상기 "결합"은 극성 용매가 증기 증착에 의해, 극성 용매 분자인 기체 상태의 극성 화합물이 고분자 사슬에 고정된 상태로 유지된 형태를 광범위하게 의미하는 것이다. 즉, 상기 "결합"은 특정 종류의 물리적 결합, 화학적 결합 등에 국한되는 의미는 아니며, 이들 물리적 결합, 화학적 결합 등을 비롯한 다양한 결합에 의해 고정된 상태, 또는 흡착 등과 같이 단순히 부착되어 고정된 상태, 또는 상기 고분자의 가교 결합에 의해 형성된 3차원 네트워크 구조 내에 포함되어 상기 고분자 사슬 또는 가교 결합 구조에 인접하게 위치하여 고정된 상태를 포함하는 의미이다.
본 명세서에서 사용된 용어 "3차원 네트워크 구조"란 3차원 입체 형상의 프레임(frame)과 상기 프레임에 의해 형성된 내부 공간을 포함하는 구조로서, 상기 프레임은 상기 가교 결합성 작용기에 의해 형성된 가교 결합, 예를 들어, 가교 결합성 작용기 간의 가교 결합 및/또는 가교 결합성 작용기와 가교제 간의 가교 결합을 포함하는 고분자 사슬을 포함하는 것일 수 있다. 상기 3차원 네트워크 구조는 가교 결합 구조라고도 할 수 있다.
본 명세서에서 복합 고체 전해질 내의 극성 화합물(극성 용매)이 “기체 상태”로 존재 또는 포함된다 함은, 상기 극성 용매 또는 이를 포함한 전해질이 액체 상태로 주입되는 경우와 구별되게, 상기 극성 화합물이 증기 상태로 증착되어 상기 복합 고체 전해질의 제조 직후 내지 이를 포함하는 전고체 이차전지의 충, 방전 과정에서, 상기 극성 화합물이 액상 주입된 전해액과 구별되는 상태로 존재함을 나타내는 것이다. 다만, 상기 복합 고체 전해질 및/또는 이차전지의 보관 또는 구동 조건 등에 따라, 상기 증기 증착된 극성 화합물이 국부적 또는 한시적으로 액화된 상태를 가질 수 있다. 이러한 경우에도, 상기 증기 증착된 극성 화합물은 상기 액체 상태로 주입된 극성 용매 등에 비해 높은 이동도를 나타내어 액체 상태의 극성 용매와는 상이한 상태를 나타내므로, 이 또한 상기 “기체 상태”로 존재 또는 포함되는 것으로 볼 수 있다.
한편, 기존에는 고체 전해질의 이온전도도를 개선하기 위해, 고분자 매트릭스에 산화물과 같은 세라믹 화합물을 분산시킨 복합 고체 전해질을 제조하였으나, 이러한 복합 고체 전해질은 고분자 매트릭스 내의 산화물계 세라믹 입자가 불균일하게 분포되거나, 상기 고분자로 폴리에틸렌 옥사이드와 같은 결정성이 높은 고분자를 사용하는 경우, 이온전도도가 저하되는 문제점이 있었다.
또한, 기존에는 고체 전해질의 이온 전도도를 개선하기 위해, 고체 전해질을 액체 전해질 또는 액체 상태의 용매에 침지 또는 담지시키거나, 고체 전해질에 액체 전해질 또는 용매를 액체 상태로 직접 주입하였다. 이와 같이 고체 전해질에 액체 전해질 또는 용매를 직접 추가할 경우, 고체 전해질의 이온 전도도가 개선되는 효과는 있으나, 이는 액체 자체가 갖는 높은 이온 전도도에 기반한 고체 전해질의 이온 전도도 상승 효과에 불과하였고, 그 개선의 정도 또한 충분치 않아 상당량의 액체 전해질 등의 주입이 필요하였다. 즉, 리튬이온의 전도는 고체 전해질 고유의 물성보다 상기 고 체 전해질에 추가된 액체 전해질에 의해서 이루어지기 때문에, 고체 전해질 자체의 물성 개선과는 거리가 멀다. 또한, 고체 전해질에 액체 전해질 또는 용매를 액체 상태로 직접 추가 또는 주입할 경우, 고분자와 액상 사이의 원하지 않는 부반응(unexpected side reaction)에 의해 고분자 사슬이 손상되거나 고분자 내 결합이 끊어지는 등 고체 전해질의 구조가 붕괴되거나 이로 인해 이온 전도도가 감소하는 문제점이 있었다.
또한, 고체 전해질에 용매 또는 액체 전해질을 직접 주입할 경우, 상기 고체 전해질 내에 액상 분자가 급격하게 확산됨으로써 고분자 사슬의 완화 현 상이 급속하게 일어나, 표면에서 겔화(gelation)가 촉진되고 이로 인한 기계적 물성 저하 현상이 나타날 수 있으며, 액체 전해질의 누액 등의 문제가 완전히 해결되지 못할 수 있다.
또한, 종래기술인 일본 공개특허 제1994-124713호의 경우에는, 일반적인 PEO(polyethylene oxide) 고분자에 용매를 증기 증착시키는 기술이 있었으나, 이 경우에는 고분자의 내부 구조가 붕괴되어 이온 전도도가 확보되지 않는 문제점이 있었다.
이에 본 발명자는 가교 결합성 작용기로 개질된 PEO(polyethylene oxide)계 코폴리머를 가교 결합한 고분자 및 세라믹 화합물을 포함하는 복합 고체 전해질에 극성 용매에서 유래한 극성 화합물을 증기 증착하는 방법을 적용하였다. 이렇게 제조된 일 구현예의 복합 고체 전해질은 가교 결합성 작용기를 포함하는 PEO계 코폴리머를 포함하는 고분자; 세라믹 화합물 및 극성 화합물을 포함하며, 상기 가교 결합성 작용기의 적어도 일부는 서로 가교 결합을 형성하여 상기 고분자가 3차원 네트워크 구조를 형성하고 있고, 상기 극성 화합물은 기체 상태로 상기 3차원 네트워크 구조 내에 포함되거나, 상기 고분자 사슬 상에 결합된 구조를 나타낼 수 있다.
이러한 복합 고체 전해질은 미량의 극성 용매에서 유래한 극성 화합물을 기체 상태로 포함하면서도, 향상된 이온 전도도를 나타냄이 확인되었다. 이는 기체 상태의 극성 화합물이 PEO계 코폴리머의 결정성 등 물성에 영향을 미쳐 고분자 사슬의 이동도(chain mobility)를 증가시키고, 이를 통해 복합 고체 전해질에 포함된 리튬 이온의 전도도를 향상시킬 수 있기 때문으로 예측된다.
더 나아가, 상기 복합 고체 전해질은 상기 3차원 네트워크 구조 내에 균일하게 분산된 세라믹 화합물로 인해 더욱 우수한 이온 전도도를 나타낼 수 있다.
따라서, 일 구현예의 복합 고체 전해질은 액체 상태의 극성 용매 또는 전해액을 실질적으로 포함하지 않으면서도, 향상된 이온 전도도를 나타내어, 우수한 물성을 갖는 전고체 전지의 개발에 크게 기여할 수 있다.
이하에서는, 발명의 일 구현예에 따른 복합 고체 전해질에 대해 구체적으로 설명한다.
복합 고체 전해질
상술한 바와 같이, 일 구현예의 복합 고체 전해질은 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머를 포함하는 고분자; 세라믹 화합물 및 극성 화합물을 포함하며, 상기 코폴리머의 가교 결합성 작용기의 적어도 일부는 서로 가교 결합을 형성하여, 상기 고분자가 3차원 네트워크 구조를 형성하고 있고, 상기 극성 화합물은 기체 상태로 3차원 네트워크 구조 내에 포함되거나, 상기 고분자 사슬 상에 결합되어 있다.
구체적인 일 예에서, 상기 기체 상태의 극성 화합물은 상기 3차원 네트워크 구조를 형성한 고분자 사슬 사이에 분산되어 있거나, 상기 고분자 사슬의 표면 또는 내부에 흡착 또는 결합된 형태를 가질 수 있다.
이러한 복합 고체 전해질은 실질적으로 액체 상태의 용매 또는 전해액을 포함하지 않으며, 후술하는 증기 증착에 의해 미량의 기체 상태로 포함 또는 결합된 극성 화합물을 포함한다. 이러한 복합 고체 전해질은, 예를 들어, 이를 포함하는 전해질층을 전고체 전지 등으로부터 분리한 후, 육안 또는 전자 현미경 등으로 관찰하였을 때, 상기 전해질층 표면에서 액상의 성분이 관찰되지 않는 것으로부터 확인될 수 있다. 이와 달리, 복합 고체 전해질에 액체 상태의 극성 용매 또는 전해액이 주입된 경우, 전해질층 표면에서 액상의 성분 또는 젖음성을 나타내는 성분이 관찰될 수 있다. 또한, 상기 극성 화합물이 증기 증착되어 기체 상태로 포함된 일 구현예의 복합 고체 전해질은 후술하는 실시예를 통해서도 확인되는 바와 같이, 액체 상태의 극성 용매 또는 전해액이 주입된 경우에 비해, 크게 높은 이온 전도도를 나타낸다. 이러한 이온 전도도의 비교 등을 통해서도 상기 극성 화합물이 증기 증착되어 기체 상태로 포함되는 복합 고체 전해질이 확인될 수 있다.
상기 일 구현예의 복합 고체 전해질에서, 상기 가교 결합성 작용기는 상기 PEO계 코폴리머의 주쇄 등에 직접 결합될 수도 있지만, 알킬렌 또는 알킬렌 옥사이드 링커를 매개로 결합될 수 있다. 이에 상기 가교 결합성 작용기는 탄소수 0 내지 10의 알킬렌 링커 또는 알킬렌 옥사이드 링커(단, 탄소수 0인 알킬렌 링커는 단일 결합을 나타낸다)를 매개로 결합될 수 있고, 히드록시기 (hydroxyl group), 카복실기(carboxyl group), 이소시아네이트기(isocyanate group), 니트로기(nitro group), 시아노기(cyano group), 아민기(amine group), 아미드기(amide group), 에폭시기(epoxy group) 및 알릴기(allyl group)로 이루어진 군에서 선택되는 1종 이상으로 될 수 있다.
발명의 일 실시예에서, 상기 가교 결합성 작용기는 2종 이상일 수 있다. 상기 가교 결합성 작용기는 서로 동일 또는 상이할 수 있으며, 바람직하게는 상이한 것일 수 있다. 상기 가교 결합성 작용기가 상이할 경우, 이들 작용기를 각각 포함하는 복수 종의 반복 단위가 포함될 수 있다. 또한, 복수 종의 가교 결합성 작용기가 포함된 경우, 고분자 사슬의 이동도 및 이온 전도도의 제어가 보다 용이하게 될 수도 있다.
상기 가교 결합성 작용기는 가교 결합성 작용기 간의 가교 결합을 형성하거나, 및/또는 가교제를 매개로 서로 가교 결합을 형성할 수 있는 작용기(functional group)를 의미하는 것으로, 고분자 사슬의 주쇄에 측쇄(side chain) 형태로 결합될 수 있다.
보다 구체적인 일 실시예에서, 상기 가교 결합성 작용기를 포함하는 PEO 계 코폴리머는 하기 화학식 1 내지 3의 반복 단위를 포함하는 공중합체로 될 수 있다:
[화학식 1]
[화학식 2]
[화학식 3]
상기 화학식 1 내지 3에서, R1은 -CH2-O-(CH2-CH2-O)k-R3 를 나타내며, k는 0 내지 20이고, R3는 탄소수 1 내지 5의 알킬기를 나타내고,
R2는 히드록시기(hydroxyl group), 카복실기(carboxyl group), 이소시아네이트기(isocyanate group), 니트로기(nitro group), 시아노기(cyano group), 아민기(amine group), 아미드기(amide group), 에폭시기 (epoxy group) 및 알릴기(allyl group)로 이루어진 군에서 선택된 1종 이상의 가교 결합성 작용기가 탄소수 0 내지 10의 알킬렌 링커 또는 알킬렌 옥사이드 링커(단, 탄소수 0인 알킬렌 링커는 단일 결합을 나타낸다)를 매개로 고분자 사슬에 결합된 치환기를 나타내며,
l, m 및 n은 반복 단위의 반복수로, l 및 n은 각각 독립적으로 1 내지 1000의 정수이고, m은 0 내지 1000의 정수이다.
예를 들어, 상기 R2의 가교 결합성 작용기는 상기 가교 결합에 의해 형성된 3차원 네트워크 구조의 매트릭스 형태를 가지는 고분자를 형성할 수 있다. 상기 가교 결합에 의한 3차원 네트워크 구조가 형성됨으로써, 상기 복합 고체 전해질의 기계적 물성이 향상될 수 있으며, 이러한 3차원 네트워크 구조 내에 상기 기체 상태의 극성 화합물이 포함 또는 결합되어 이온 전도도가 보다 향상된 일 구현예의 복합 고체 전해질이 제공될 수 있다.
또한, 상기 PEO계 코폴리머는 상기 R2가 서로 다른 가교 결합성 작용기로 되는 2종 이상의 화학식 3의 반복 단위를 포함할 수도 있고, 화학식 2의 반복 단위 역시 1종 이상으로 포함될 수 있음은 자명하다.
상기 l, m 및 n이 각각 1 미만인 경우, 고분자를 형성하기에는 분자량이 작아 어려움이 있고, 상기 l, m 및 n이 각각 1000 초과인 경우, 점도 증가로 인해 고분자 용액 제조시 용해도가 감소되고 복합 고체 전해질 제조를 위한 성형이 어려워질 수 있다. 특히, l, m 및 n 중 가교 결합성 작용기가 포함된 반복 단위의 반복수가 1000을 초과할 경우, 가교도가 지나치게 증가되어 고분자 사슬의 이 동도가 저하되어 이온 전도도가 감소될 수 있다.
본 명세서에 있어서, “히드록시기”는 -OH기를 지칭한다.
본 명세서에 있어서, "카복실기"는 -COOH기를 지칭한다.
본 명세서에 있어서, "이소시아네이트기"는 -N=C=O기를 지칭한다.
본 명세서에 있어서, "니트로기"는 -NO2기를 지칭한다.
본 명세서에 있어서, "시아노기"는 -CN기를 지칭한다.
본 명세서에 있어서, “아미드기”는 -C(=O)NR’R”을 지칭하며, 여 기서 R’ 및 R”은 각각 독립적으로 수소 또는 C1 내지 C5의 알킬기일 수 있거나, R’ 및 R”은 이들이 부착된 N원자와 함께 고리 구조 내에서 C4 내지 C8의 원자를 갖는 헤테로고리를 형성할 수 있다.
본 명세서에 있어서, "아민기"는 모노알킬아민기; 모노아릴아민기; 모노헤테로아릴아민기; 디알킬아민기; 디아릴아민기; 디헤테로아릴아민기; 알킬아릴아민기; 알킬헤테로아릴아민기; 및 아릴헤테로아릴아민기로 이루어진 군으로부터 선택될 수 있으며, 탄소수는 특별히 한정되지 않으나, 1 내지 30인 것이 바람직하 다. 상기 아민기의 구체적인 예로는 메틸아민기, 디메틸아민기, 에틸아민기, 디에 틸아민기, 페닐아민기, 나프틸아민기, 비페닐아민기, 디비페닐아민기, 안트라세닐 아민기, 9-메틸-안트라세닐아민기, 디페닐아민기, 페닐나프틸아민기, 디톨릴아민기, 페닐톨릴아민기, 트리페닐아민기, 비페닐나프틸아민기, 페닐비페닐 아민기, 비페닐플루오레닐아민기, 페닐트리페닐레닐아민기, 비페닐트리페닐레닐 아민기 등이 있으나, 이들에만 한정되는 것은 아니다. 또한, “아미노기”는 -NH2를 지칭한다.
본 명세서에 있어서, "알릴기"는 -CH2-CH=CH2기를 지칭한다.
상기 화학식 1 내지 3을 포함하는 코폴리머의 중량평균분자량(Mw)은 100,000 g/mol 내지 2,000,000 g/mol 일 수 있으며, 구체적으로, 100,000 g/mol 이 상, 200,000 g/mol 이상 또는 300,000 g/mol 이상일 수 있고, 1,600,000 g/mol 이 하, 1,800,000 g/mol 이하 또는 2,000,000 g/mol 이하일 수 있다. 상기 코폴리머의 중량평균분자량(Mw)이 100,000 g/mol 미만이면 제조되는 복합 고체 전해질의 기계적 물성을 충족시키지 못할 수 있다. 상기 코폴리머의 중량평균분자량(Mw)이 2,000,000 g/mol 초과이면, 점도 증가로 인해 고분자 용액 제조시 용해도가 감소되고 복합 고체 전해질 제조를 위한 성형이 어려워질 수 있다. 또한, 상기 복합 고체 전해질 내부의 결정성 증가 및 사슬 이동도의 감소로 인해 복합 고체 전해질의 이온 전도도가 감소할 수 있다.
특히, l, m 및 n 중 가교 결합성 작용기가 포함된 화학식 3의 반복 단위의 반복수가 1000을 초과할 경우, 가교도가 지나치게 증가하여 고분자 사슬의 이동도가 저하되어 복합 고체 전해질의 이온 전도도가 감소될 수 있다.
또한, 상기 코폴리머는 랜덤 코폴리머(random copolymer) 또는 블록 코폴리머(block copolymer)일 수 있다.
발명의 구체적인 일 실시예에서, 상기 극성 화합물은 기체 상태로 상기 고분자 사슬의 표면 또는 내부에 포함 또는 결합된 것일 수 있다. 구체적으로, 상기 기체 상태의 극성 화합물은 상기 가교 결합에 의해 3차원 네트워크 구조를 형성한 고분자 사슬 사이에 확산 또는 분산되어 있거나, 상기 고분자 사슬의 표면 또는 내부에 흡착 또는 결합될 수 있다.
상기 극성 화합물은 증기 증착 공정에서 사용된 극성 용매의 기체 분자로서, 증기 증착시 상기 극성 용매의 기체 분자가 고분자에 흡착된 후, 고분자의 사슬 내 부로 확산하여, 상기 고분자 사슬에 결합되거나, 또는 고분자 사슬 사이의 내부 공 간에 분산 또는 확산된 형태로 포함될 수 있다. 상기 극성 화합물이 고분자 사슬에 결합되거나, 또는 고분자 사슬 사이의 내부 공간에 분산된 형태로 포함됨으로써, 최종 제조된 복합 고체 전해질의 이온 전도도를 향상시킬 수 있다.
구체적으로, 상기 고분자 사슬에 결합되거나, 고분자 사슬 사이에 포함된 극성 화합물은 가소제 역할을 하여, 상기 고분자를 가소화(plasticization)시킬 수 있다. 상기 가소화된 고분자는 내부에 무정형 영역(amorphous region)이 증가하여, 고분자 사슬의 이동도가 향상될 수 있다. 상기 고분자 사슬의 이동도가 향상됨에 따라, 상기 고분자 내부에서 이온 호핑(ion hopping) 효과가 증대되어, 복합 고체 전해질의 이온 전도도가 향상될 수 있다.
또한, 상기 극성 화합물은 이온 호핑을 통해 원활한 이온 전달을 위한 중간체(intermediate) 역할을 할 수 있다. 리튬 이온과 극성 화합물 간의 친화 도(affinity)는 리튬 이온과 PEO계 코폴리머의 에테르 산소(ether oxygen) 간의 친 화도보다 강하므로, 상기 극성 화합물이 흡착된 고분자의 내부에서 리튬 이온의 전 달이 보다 빠르고 용이할 수 있다. 즉, 상기 고분자 내부에 극성 화합물이 유입됨에 따라 리튬 이온의 양이온 용매화(cation solvation) 효과가 증대되므로, 이온 이동도가 향상되고, 이에 따라 복합 고체 전해질의 이온 전도도가 개선될 수 있다.
또한, 상기 극성 화합물은 카보네이트계 화합물 및 설포닐계 화합물로 이루어진 군에서 선택되는 1종 이상을 포함하는 것일 수 있다.
구체적으로, 상기 극성 화합물은 에틸메틸카보네이트(Ethyl Methyl carbonate, EMC), 디메틸카보네이트(Dimethyl Carbonate, DMC), 디에틸카보네이트 (Diethyl Carbonate, DEC), 에틸렌카보네이트(Ethylene Carbonate, EC), 프로필렌 카보네이트(Propylene Carbonate, PC), 비닐렌카보네이트(Vinylene Carbonate, VC) 및 술폴레인(Sulfolane)로 이루어진 군에서 선택되는 1종 이상을 포함하거나, 이들의 조합을 포함할 수 있다.
상기 극성 화합물의 함량은 상기 복합 고체 전해질의 총 중량 기 준으로, 0.1 중량% 이상 내지 10 중량% 미만을 포함할 수 있다. 예를 들어, 상기 극성 화합물의 함량은 0.1 중량% 이상, 1 중량% 이상, 2 중량% 이상이거나, 5 중량% 이하, 6 중량% 이하, 7 중량% 이하, 8 중량% 이하, 9 중량% 이하, 10 중량% 미만일 수 있다. 상기 극성 화합물의 함량이 0.1 중량 % 미만인 경우, 고분자 내부의 사슬의 형태(chain conformation) 변화를 유발하기 힘들어 상기 복합 고체 전해질의 이온 전도도가 향상되지 않고, 상기 극성 화합물의 함량이 10 중량% 이상인 경우, 상기 복합 고체 전해질에 액체의 함유량이 많아 반고체전지의 성질을 띠게 되고, 또한, 고분자의 겔화로 인해 복합 고체 전해질의 기계적 강도가 저하될 수 있다.
발명의 일 실시예에서, 상기 복합 고체 전해질은 가교 결합성 작용기 간의 가교 결합을 포함할 수 있다. 또한, 상기 복합 고체 전해질은 가교제를 더 포함하여, 상기 가교제와 가교 결합성 작용기 간의 가교 결합을 더 포함할 수 있다. 예를 들어, 상기 가교 결합성 작용기의 적어도 일부는 상기 가교제를 매개로 서로 가교 결합을 형성하여, 상술한 3차원 네트워크 구조를 형성할 수 있다.
상기 가교 결합은 우레탄 가교 결합(urethane bond), 에스테르 가교 결합(ester bond), 수소 결합(hydrogen bond), 알릴기(allyl group, -CH2-CH=CH2) 말단의 비닐기에 의한 라디칼 중합 반응으로 형성된 결합 등일 수 있으나, 이들의 예로만 한정되는 것은 아니다.
또한, 상기 복합 고체 전해질의 제조 공정에서 가교제를 첨가할 경우, 상기 가교제와 가교 결합성 작용기 간의 가교 결합이 형성될 수도 있으며, 상기 가교 결합은 수소결합, 루이스 산-염기 상호작용에 의한 결합, 이온결합, 배 위결합 또는 라디칼 중합에 의해 형성된 결합일 수 있다.
상기 가교제는 상기 가교 결합성 작용기와 가교 결합을 형성할 수 있는 다관능성 가교제라면 특별히 제한되는 것은 아니다. 예컨대, 상기 가교제는 트라이메틸올프로페인 트라이메타크릴레이트 (trimethylolpropane trimethacrylate), 폴리에틸렌글라이콜 다이아크릴레이트(poly(ethylene glycol) diacrylate), 폴리에틸렌글라이콜 다이메타크리레이트(poly(ethylene glycol) dimethacrylate), 에틸렌 글리콜 디메틸아클릴레이트(ethylene glycol dimethylacrylate, 이하 'EGDMA'), 1,3-다이아이소프로페닐벤젠(1,3-diisopropenylbenzene(DIP)), 1,4-다이아크릴로일 피페라진(1,4-diacryloyl piperazine), 2-(다이에틸아미노)에틸 메타크릴레이트(2(diethylamino)ethyl methacrylate), 2,6-비스아크릴로일아미도피리딘(2,6bisacryloylamidopyridine), 3-(아크릴록시)-2-하이드록시프로필 메타크릴레이트 (3-(acryloyloxy)-2-hydroxypropyl methacrylate), 3,5-비스(아크릴아마이도)벤조산(3,5-bis(acryloylamido)benzoic acid), 3-아미노프로필트라이에톡시실란(3aminopropyltriethoxysilane), 3-아이소시아나토프로필트라이에톡시실란(3isocyanatopropyltriethoxysilane), 3-메틸아크리록시프로필 트라이메톡시실란(3methylacryloxypropyl trimethoxysilane), 비스-(1-(tert-뷰틸퍼옥시)-1-메틸에틸)-벤젠(bis-(1-(tert-butylperoxy)-1-methylethyl)-benzene), 다이큐밀 퍼옥사이드(dicumyl peroxide), 다이메타크릴레이트(dimethacrylate), 다이비닐벤젠(Divinylbenzene), 에틸렌 글라이콜 말레익 로지네이트 아크릴레이트 (ethylene glycol maleic rosinate acrylate), 글라이시딜메타크릴레이트 (glycidilmethacrylate), 하이드록시 퀴놀린(hydroxyquinoline), 아이페닐다이에톡시실란(iphenyldiethoxysilane), 말레익 로진 글라이콜 아크릴레이트(maleic rosin glycol acrylate), 메틸렌 바이사크릴아마이드(methylene bisacrylamide), N,N'1,4-페닐렌다이아크릴아민(N,N'-1,4-phenylenediacrylamine), N,O-비스아크릴로일페닐알아니놀(N,O-bisacryloyl-phenylalaninol), N,O-비스메타크릴로일 에타놀아민 (N,O-bismethacryloyl ethanolamine), 펜타에리스리톨 트라이아크릴레이트 (pentaerythritol triacrylate), 페닐트라이메톡시 실란(phenyltrimethoxy silane), 테트라메톡시실란(tetramethoxysilane), 테트라메틸렌(tetramethylene), 테트라에톡시실란(tetraethoxysilane), 트라이알릴 아이소시아뉴레이트(triallyl isocyanurate)으로 이루어진 군에서 선택되는 1종 이상의 다관능성 가교제, 예를 들어, 2 관능 이상의 다가 화합물로 될 수 있다.
또한, 상기 가교제는 상기 가교 결합성 작용기를 포함하는 PEO계 코폴리머 100 중량부에 대하여 1 내지 30 중량부로 포함될 수 있다. 상기 가교제의 함량이 1 중량부 미만이면 가교 결합성 작용기와의 가교 결합이 충분히 이루어지지 않을 수 있고, 30 중량부 초과이면 가교 결합이 과도하게 이루어져 오히려 고분자 사슬의 이동도가 감소함으로써 이온 전도도가 저하될 수 있다.
발명의 일 실시예에서, 상기 복합 고체 전해질은 리튬염을 더 포함할 수 있다. 상기 리튬염은 상기 고분자 사슬 사이의 내부 공간에 해리된 이온 상태로 포함되어, 복합 고체 전해질의 이온 전도도를 향상시킬 수 있다. 상기 리튬염에서 해리된 양이온 및/또는 음이온의 적어도 일부는 상기 고분자 사슬에 결합된 상태로 존재하여, 전지의 충/방전시에 이동성을 나타낼 수 있다.
상기 리튬염은 (CF3SO2)2NLi(Lithium bis(trifluoromethanesulphonyl)imide, LiTFSI), (FSO2)2NLi(Lithium bis(fluorosulfonyl)imide, LiFSI), LiNO3, LiOH, LiCl, LiBr, LiI, LiClO4, LiBF4, LiB10Cl10, LiPF6, LiCF3SO3, LiCF3CO2, LiAsF6, LiSbF6, LiAlCl4, CH3SO3Li, CF3SO3Li, LiSCN, LiC(CF3SO2)3, 클로로보란 리튬, 저급 지방족 카르본산 리튬 및 테트라페닐 붕산 리튬으로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다.
또한, 상기 리튬염은 상기 가교 결합성 작용기를 포함하는 PEO계 코폴리머 100 중량부에 대하여 25 내지 45 중량부로 포함될 수 있으며, 구체적으로, 25 중량부 이상, 30 중량부 이상 또는 35 중량부 이상으로 포함되거나, 40 중량부 이하 또는 45 중량부 이하로 포함될 수 있다. 상기 리튬염의 함량이 25 중량부 미 만이면 복합 고체 전해질의 이온 전도도가 저하될 수 있고, 45 중량부 초과이면 기계적 강도가 저하될 수 있다.
상술한 복합 고체 전해질은 세라믹 화합물을 포함할 수 있다. 상기 세라믹 화합물은 리튬 이온의 전도성을 향상시키기 위한 리튬 이온 전달 능력을 갖는 것으로서, 바람직하게는 리튬 원자를 함유하되 리튬을 저장하지 아니하고 리튬 이온을 이동시키는 기능을 가질 수 있는 것으로, 복합 고체 전해질의 이온 전도도를 향상시킬 수 있다.
또한, 상기 세라믹 화합물은 가교 결합된 고분자 사슬 사이, 예를 들어, 상기 3차원 네트워크 구조 내에 균일하게 분산된 상태로 포함될 수 있다. 상기 세라믹 화합물은 가교 결합 공정에서 함께 첨가되어, 가교 결합에 의해 형성되는 고분자 사슬의 사이에 뭉침없이 균일하게 분산될 수 있다. 이와 같은 세라믹 화합물은 균일한 분산 형태로 인하여 복합 고체 전해질의 기계적 강도와 이온 전도도 향상에 유리할 수 있다.
또한, 상기 세라믹 화합물은 입자 형태일 수 있다. 입자라는 형태적인 특징으로 인하여, 복합 고체 전해질 내부에서 더욱 균일하게 분산된 상태로 포함될 수 있다. 상기 세라믹 화합물의 입자는 구형일 수 있으며, 그 직경은 100 nm 내지 1000 nm 일 수 있다. 상기 직경이 100 nm 미만이면 고분자의 결정성 감소를 통한 비결정화 효과가 미미할 수 있고, 1000 nm 초과이면 입자들 간의 응집 (aggregation) 증가로 인해 분산성이 저하되어 균일하게 분산되기 어려울 수 있다.
상기 세라믹 화학물은 산화물계 또는 인산염계 화합물일 수 있으며, 예를 들어, 리튬 금속 산화물 또는 리튬 금속 인산화물 형태의 산화물계 고체 전해질로 될 수 있다. 보다 구체적으로, 상기 세라믹 화합물은 가넷(Garnet)형 리튬-란타늄-지르코늄 산화물계(LLZO, Li7La3Zr2O12) 화합물, 페로브스카이트(perovskite)형 리튬-란타늄-티타늄 산화물계(LLTO, Li3xLa2/3-xTiO3) 화합물, 인산염(phosphate)계의 나시콘(NASICON)형 리튬-알루미늄-티타늄 인산염계(LATP, Li1+xAlxTi2-x(PO4)3) 화합물, 리튬-알루미늄-게르마늄 인산염계(LAGP, Li1.5Al0.5Ge1.5(PO4)3)계 화합물, 리튬-실리콘-티타늄 인산염계(LSTP, LiSiO2TiO2(PO4)3) 화합물 및 리튬-란타늄-지르코늄-티 타늄 산화물계(LLZTO) 화합물로 이루어진 군으로부터 1종 이상 선택될 수 있으며, 더욱 바람직하게는 리튬-란타늄-지르코늄 산화물(LLZO), 리튬-실리콘-티타늄 인산염(LSTP), 리튬-란타늄-티타늄 산화물(LLTO), 리튬-알루미늄-티타늄 인산염 (LATP), 리튬-알루미늄-게르마늄 인산염(LAGP) 및 리튬-란타늄-지르코늄-티타늄 산화물(LLZTO)로 이루어지는 군에서 선택되는 1종 이상의 산화물계 고체 전해질을 사용할 수 있다.
상기 산화물계 또는 인산염계 산화물계 고체 전해질은 일반적으로 상온에서 최대 10-4~10-3 S/cm의 이온전도도 값을 가지며, 고전압 영역에서 안정하고, 공기 중에서 안정해 합성 및 취급이 용이한 장점들이 있다.
따라서, 상술한 복합 고체 전해질이 상기 세라믹 화합물을 혼합하여 복합 고체 전해질을 더 포함하여 고분자계 고체 전해질이 갖는 단점들을 보완할 수 있다.
또한 상기 세라믹 화합물은 400 ℃ 이상의 고온 조건 하에서도 쉽게 연소되거나 발화현상을 일으키지 않으므로 고온 안정성이 높다. 따라서, 상기 복합 고체 전해질이 상기 세라믹 화합물을 포함하는 경우, 복합 고체 전해질의 기계적 강도는 물론, 고온 안정성 및 이온 전도도를 향상시킬 수 있다.
상기 세라믹 화합물은 상기 가교 결합성 작용기를 포함하는 PEO계 코폴리머 100 중량부에 대하여 10 중량부 내지 100 중량부, 혹은 10 중량부 내지 60 중량부로 포함될 수 있다.
상기 세라믹 화합물이 지나치게 작은 함량으로 포함되면, 세라믹 화합물에 의한 고분자 결정성 저하 및 무정형(amorphous)화 효과가 감소하여 복합 고체 전해질의 이온 전도도 증가 효과가 크지 않으며, 기계적 물성 또한 복합체(composite) 형성으로 인해 기대하는 수준에 미치지 못할 수 있다.
상기 세라믹 화합물이 지나치게 큰 함량으로 포함되면, 상기 세라믹 화합물이 상기 고분자 내에 균일하게 분산되지 않아, 세라믹 화합물 입자들이 서로 뭉쳐 응집되는 현상이 발생하고, 결과적으로 이온 전도도가 저하된 복합 고체 전해질이 제조될 수 있다.
복합 고체 전해질의 제조방법
발명의 다른 구현예에서, 상술한 복합 고체 전해질의 제조방법은 (S1) 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머와 세라믹 화합물을 혼합한 후, 상기 혼합물에 포함된 상기 PEO계 코폴리머에 대해 가교 결합 반응을 진행하는 단계; 및 (S2) 상기 (S1) 단계에서 가교된 고분자를 포함하는 혼합물에 극성 용매를 증기 증착 시키는 단계;를 포함할 수 있다.
상기 가교 결합성 작용기를 포함하는 PEO계 코폴리머에 대한 설명은 상기 기재된 바와 같다.
이하, 각 단계별로 보다 상세히 설명한다.
상기 (S1) 단계에서는, 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머와, 세라믹 화합물을 혼합한 후, 이러한 혼합물에 포함된 상기 PEO계 코폴리머에 대해 가교 결합 반응을 진행하여, 상술한 3차원 네트워크 구조를 형성한 고분자를 제조할 수 있다.
상기 (S1) 단계의 가교 결합 반응은 가교제 및 개시제로 이루어진 군에서 선택되는 1종 이상의 추가 존재 하에 진행할 수 있다.
또한, 복합 고체 전해질 형성을 위해 상기 (S1) 단계에서, 리튬염을 함께 첨가할 수도 있다.
또, 상기 세라믹 화합물은 앞서 설명한 복합 고체 전해질에서 사용한 것과 동일한 것을 사용할 수 있으며, 함량 역시 동일하게 사용할 수 있다.
상기 가교 결합 반응은 상기 PEO계 코폴리머 및 세라믹 화합물 등을 포함하는 용액을 기재 상에 도포하여 도포막을 형성한 후 건조하는 과정에서 형성될 수 있다.
구체적으로, 상기 혼합 용액은 상기 PEO계 코폴리머 및 세라믹 화합물을 용매에 혼합하여 제조될 수 있으며, 추가로, 가교제, 개시제 및/또는 리튬염을 함께 혼합하여 제조될 수 있다. 또, 상기 PEO계 코폴리머와 가교제, 개시제 및/또는 리튬염을 포함하는 용액을 먼저 제조한 다음, 세라믹 화합물을 추가한 혼 합 용액 또는 서스펜션(suspension)이 제조될 수도 있다.
상기 용매는 상기 PEO계 코폴리머, 가교제, 개시제 및/또는 리튬염을 혼합시킬 수 있고, 건조 공정에 의해 쉽게 제거될 수 있는 용매라면 특별히 제 한되는 것은 아니다. 예를 들어, 상기 용매는 아세토나이트릴(acetonitrile), 메탄 올(methanol), 에탄올(ethanol), 테트라히로퓨란(tetrahydrofuran), 물(water), 이 소프로필알코올, 디메틸설폭사이드(DMSO, Dimethyl sulfoxide), 메틸피롤리돈(NMP, N-Methyl-2-Pyrrolidone) 또는 디메틸포름아미드(DMF, N,N-Dimethyl formamide) 등일 수 있다. 이러한 용매는 가교 결합 형성을 위한 반응 매질로서의 용매로서, 액체 전해질 등에 포함되는 극성 용매 등과는 구분되며, 가교 결합 후 건조 등에 의해 완전히 제거되는 것이다.
상기 혼합 용액의 농도는 복합 고체 전해질 제조를 위한 성형 공정이 원활히 진행될 수 있을 정도를 감안하여 적절히 조절할 수 있다. 구체적으로, 상기 고분자 용액의 농도란, 상기 고분자 용액 내에서 고분자의 농도(w/w%)를 의미하는 것일 수 있다. 상기 고분자의 농도란 PEO계 코폴리머의 농도인 것일 수 있다. 예를 들어, 상기 고분자 용액의 농도는 5중량% 내지 20중량% 일 수 있으며, 구체적으로, 5중량% 이상, 7중량% 이상 또는 9중량% 이상일 수 있고, 13중량% 이하, 17중량% 이하 또는 20중량% 이하 일 수 있다. 상기 고분자 용액의 농도가 5중량% 미만이면, 농도가 지나치게 묽어 복합 고체 전해질의 기계적 강도가 저하되거나, 기재 상에 도포 시 흘러내릴 수 있고, 20중량% 초과이면 고분자 용액 내에 원하는 농도로 리튬염을 용해시키기 어렵고, 점도가 높아 용해도가 감소하거나 균일한 박막 형태로 도포하기 어려울 수 있다.
상기 기재는 상기 도포막에 대한 지지체 역할을 할 수 있는 것이라 면 특별히 제한되는 것은 아니다. 예를 들어, 상기 기재는 SUS(Stainless Use Steel), 폴리에틸렌테레프탈레이트 필름, 폴리테트라플로오로에틸렌 필름, 폴리에틸렌 필름, 폴리프로필렌 필름, 폴리부텐 필름, 폴리부타디엔 필름, 염화비닐 공중합체 필름, 폴리우레탄 필름, 에틸렌-비닐아세테이트 필름, 에틸렌-프로필렌 공중 합체 필름, 에틸렌-아크릴산 에틸 공중합체 필름, 에틸렌-아크릴산 메틸 공중합체 필름 또는 폴리이미드 필름일 수 있다.
또한, 상기 도포 방법 역시 상기 고분자 용액을 상기 기재 상에 도포하여 도포막을 형성할 수 있는 방법이라면 특별히 제한되는 것은 아니다. 예를 들어, 상기 도포 방법은 바코팅(bar coating), 롤코팅(roll coating), 스핀코팅 (spin coating), 슬릿코팅(slit coating), 다이코팅(die coating), 블레이드코팅 (blade coating), 콤마코팅(comma coating), 슬롯다이코팅(slot die coating), 립 코팅(lip coating), 스프레이코팅(spray coating) 또는 솔루션캐스팅(solution casting)일 수 있다.
상기와 같은 도포 방법 의해 기재 상에 형성된 도포막은 건조 공정을 통해 잔류 용매가 완전히 제거된 필름 형태의 고분자로 성형될 수 있다. 상기 건조는 용매의 급격한 증발로 인한 고분자의 수축을 방지하기 위해, 1차 건조 공정 및 2차 건조 공정으로 나누어 실시될 수 있다. 상기 1차 건조 공정은 상온 건조를 통해 용매의 일부를 제거할 수 있고, 상기 2차 건조 공정은 진공 고온 건조를 통해 용매를 완전히 제거할 수 있다. 상기 고온 건조는 80℃ 내지 130℃의 온도에서 실 시될 수 있으며, 고온 건조 온도가 80℃ 미만이면 잔류 용매가 완전히 제거될 수 없고, 130℃ 초과이면 고분자가 수축하여 균일한 전해질 막을 성형하기 어려울 수 있다.
또한, 상기 가교제는 상기 가교 결합성 작용기와 결합을 형성하는 것일 수 있다. 상기 가교제의 종류, 가교제의 함량 및 상기 가교 결합성 작용기와의 결합의 종류에 대한 설명은 상기 기재된 바와 같다.
또한, 상기 개시제는 상기 가교 결합성 작용기 간의 라디칼 중합 반응을 유도하여, 상기 가교 결합성 작용기 간의 가교 결합이 형성되도록 할 수 있다. 상기 라디칼 중합 반응을 가능하게 하는 작용기는 말단부에 비닐이 포함된 작용기일 수 있으며, 예를 들어, 알릴기일 수 있다.
상기 개시제는 상기 가교 결합성 작용기 간의 라디칼 중합 반응을 유도할 수 있는 개시제라면 특별히 제한되는 것은 아니다. 예컨대, 상기 개시제는 벤조일 퍼옥사이드 (benzoyl peroxide), 아조비스이소부티로니트릴 (azobisisobutyronitrile), 라우로일퍼옥사이드(lauroyl peroxide), 큐멘 하이드로 퍼옥사이드(cumene hydroperoxide), 디이소프로필페닐하이드로퍼옥사이드 (diisopropylphenyl-hydroperoxid), 3급 부틸하이드로퍼옥사이드(tert-butyl hydroperoxide), 파라메탄하이드로퍼옥사이드(p-메틸하이드로퍼옥사이드) 및 2,2'아조비스(2-메틸프로피오니트릴)(2,2'-azobis(2-methylpropionitrile))로 이루어진 군에서 선택된 1종 이상을 포함하는 것일 수 있다.
상기 개시제는 상기 가교 결합성 작용기를 포함하는 PEO계 코폴리머 100 중량부에 대하여 0.5 내지 2 중량부로 사용될 수 있으며, 상기 범위로 사용될 경우 가교 결합성 작용기 간의 라디칼 중합 반응을 유도하여 가교 결합을 효율적으로 형성하는 것을 가능하게 할 수 있다.
또한, 상기 리튬염의 함량 및 종류에 대한 설명은 상기 기재된 바와 같다.
상기 (S2) 단계에서는, 상기 (S1) 단계에서 제조된 가교된 고분자 함유 혼합물에 극성 용매를 증기 증착시켜, 상술한 일 구현예의 복합 고체 전해질을 제조할 수 있다. 이때, 상기 극성 용매의 기체 분자는 일 구현예에 포함된 극성 화합물일 수 있다.
상기 증기 증착은, 상기 극성 용매를 상온에서, 또는 가열하여 발생된 상기 극성 용매의 증기를 상기 고분자에 접촉시키고 내부로 침투시켜 실시될 수 있다. 이와 같이, 상온에 두거나, 또는 가열을 통한 증기 증착을 통하여, 상기 고분자 표면 및/또는 내부에 기체 상태의 극성 화합물이 균일하게 확산되어, 극성 화합물 기체 분자가 상기 고분자 사슬에 결합하거나, 고분자 사슬의 내부 공간에 균일하게 분산 또는 확산된 형태로 포함될 수 있다.
상기 증기 증착시, 극성 용매를 상온에서 두는 경우, 비점이 낮은 미량의 극성 용매를 상온에서 서서히 기화하면서 고분자 내부로 침투시켜, 상기 고분자 내에 가교 결합된 고분자 사슬의 형태(conformation) 변화를 효과적으로 유도할 수 있다.
또한, 상기 증기 증착시, 극성 용매를 가열하는 경우, 증기 증착 속도를 향상시킬 수 있다. 이때, 가열 온도는 극성 용매가 증기로 상 변화할 수 있는 온도라면 특별히 제한되는 것은 아니며, 예컨대 30℃ 내지 80℃ 일 수 있다. 일 반적인 PEO는 60℃에서 멜팅되나, 상기 가교 결합성 작용기로 개질된 PEO계 코폴리 머는 가교 구조를 형성할 경우 내열성이 향상되어 80℃까지 견딜 수 있으므로, 증 기 증착 속도를 더욱 빠르게 할 수 있다. 또한, 상기 가열 방법은 증기를 발생시키는 에너지를 공급할 수 있는 방법이면 어느 것이든 제한이 없다. 예를 들어, 버너 또는 풍로 등으로 직접 가열 방법, 히터 또는 스팀관 등으로 간접 가열 방법 등을 사용할 수 있으나, 이들의 예로만 한정되는 것은 아니다.
상기 가열 시, 온도가 지나치게 높은 고온으로 가열할 경우, 극성 용매의 비점 이상에서 용매가 끓거나, 용매의 구조 변화가 나타날 수 있고, 또는 고분자의 변형이 유발될 수 있고, 증기 증착시 극성 용매의 증발 속도를 제어하기 힘든 단점이 있으므로, 미량의 극성 용매로 증기 증착 시키기 위해서는 상기 규정된 바와 같은 적정 범위의 가열 온도에서 증기 증착을 실시하는 것이 바람직할 수 있다.
전고체 전지
발명의 추가적인 구현예는 또한, 상기 복합 고체 전해질을 포함하는 전고체 전지에 관한 것으로, 상기 전고체 전지는 음극, 양극 및 상기 음극과 양극 사이에 개재되는 복합 고체 전해질을 포함하며, 상기 복합 고체 전해질은 전술한 일 구현예에 따른 것이다.
구체적으로, 상기 복합 고체 전해질은 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머가 가교 결합된 고분자 및 기체 상태의 극성 화합물을 포함하며, 상기 기체 상태의 극성 화합물이 포함 또는 결합되어 있고, 세라믹 화합물이 균일하게 분산되어 이온 전도도가 향상되므로, 전고체 전지의 전해질로서 적합할 수 있다.
한편, 상기 전고체 전지에 포함된 양극은 양극 활물질층을 포함하며, 상기 양극 활물질층은 양극 집전체의 일 면에 형성될 것일 수 있다.
상기 양극 활물질층은 양극 활물질, 바인더 및 도전재를 포함한다.
또한, 상기 양극 활물질은, 리튬이온을 가역적으로 흡장 및 방출하 는 것이 가능한 물질이면 특별히 한정되지 않고, 예를 들면, 리튬 코발트 산화물, 리튬 니켈 산화물, Li[NixCoyMnzMv]O2(상기 식에서, M은 Al, Ga 및 In으로 이루어진 군에서 선택되는 어느 하나 또는 이들 중 2종 이상의 원소이고;0.3≤x<1.0, 0≤y, z≤0.5, 0≤v≤0.1, x+y+z+v=1이다), Li(LiaMb-a-b'M'b')O2-cAc(상기 식에서, 0≤a≤0.2, 0.6≤b≤1, 0≤b'≤0.2, 0≤c≤0.2이고; M은 Mn과, Ni, Co, Fe, Cr, V, Cu, Zn 및 Ti로 이루어진 군에서 선택되는 1종 이상을 포함하며; M'는 Al, Mg 및 B로 이루어진 군에서 선택되는 1종 이상이고, A는 P, F, S 및 N로 이루어진 군에서 선택되는 1종 이상이다.) 등의 층상 화합물이나 1 또는 그 이상의 전이금속으로 치환된 화합물; 화학식 Li1+yMn2-yO4 (여기서, y 는 0 내지 0.33임), LiMnO3, LiMn2O3, LiMnO2 등의 리튬 망간 산화물; 리튬 동 산화물 (Li2CuO2); LiV3O8, LiFe3O4, V2O5, Cu2V2O7 등의 바나듐 산화물; 화학식 LiNi1-yMyO2 (여기서, M=Co, Mn, Al, Cu, Fe, Mg, B 또는 Ga 이고, y=0.01 내지 0.3임)으로 표현되는 Ni 사이트형 리튬 니켈 산 화물; 화학식 LiMn2-yMyO2 (여기서, M=Co, Ni, Fe, Cr, Zn 또는 Ta 이고, y=0.01 내지 0.1임) 또는 Li2Mn3MO8 (여기서, M=Fe, Co, Ni, Cu 또는 Zn 임)으로 표현되는 리튬 망간 복합 산화물; 화학식의 Li 일부가 알칼리토금속 이온으로 치환된 LiMn2O4; 디 설파이드 화합물; Fe2(MoO4)3 등을 들 수 있지만, 이들만으로 한정되는 것은 아니다.
또한, 상기 양극 활물질은 상기 양극 활물질층 전체 중량을 기준으로 40 내지 80 중량%로 포함될 수 있다. 구체적으로, 상기 양극 활물질의 함량은 40 중량% 이상 또는 50 중량% 이상일 수 있고, 70 중량% 이하 또는 80 중량% 이하일 수 있다. 상기 양극 활물질의 함량이 40 중량% 미만이면 양극 활물질 간의 연결성 및 전기적 특성이 부족해질 수 있고, 80 중량% 초과이면 물질 전달 저항이 커질 수 있다.
또한, 상기 바인더는 양극 활물질과 도전재 등의 결합 및 집전체에 대한 결합에 조력하는 성분으로서, 스티렌-부타디엔 고무, 아크릴화 스티렌-부타디엔 고무, 아크릴로니트릴 공중합체, 아크릴로니트릴-부타디엔 고무, 니트릴 부타디엔 고무, 아크릴로니트릴-스티렌-부타디엔 공중합체, 아크릴 고무, 부틸 고무, 플 루오린 고무, 폴리테트라플루오로에틸렌, 폴리에틸렌, 폴리프로필렌, 에틸렌/프로 필렌 공중합체, 폴리부타디엔, 폴리에틸렌 옥사이드, 클로로설폰화 폴리에틸렌, 폴 리비닐피롤리돈, 폴리비닐피리딘, 폴리비닐 알코올, 폴리비닐 아세테이트, 폴리에 피클로로하이드린, 폴리포스파젠, 폴리아크릴로니트릴, 폴리스티렌, 라텍스, 아크 릴 수지, 페놀수지, 에폭시 수지, 카복시메틸셀룰로오스, 하이드록시프로필 셀룰로 오스, 셀룰로오스 아세테이트, 셀룰로오스 아세테이트 부티레이트, 셀룰로오스 아 세테이트 프로피오네이트, 시아노에틸셀룰로오스, 시아노에틸수크로스, 폴리에스테 르, 폴리아미드, 폴리에테르, 폴리이미드, 폴리카복실레이트, 폴리카복시산, 폴리 아크릴산, 폴리아크릴레이트, 리튬 폴리아크릴레이트, 폴리메타크릴산, 폴리메타크 릴레이트, 폴리아크릴아미드, 폴리우레탄, 폴리비닐리덴 플루오라이드 및 폴리(비 닐리덴 플루오라이드)-헥사플루오로프로펜으로 이루어진 군으로부터 선택되는 1종 이상을 포함할 수 있다. 바람직하기로, 상기 바인더는 스티렌-부타디엔 고무, 폴리테트라플루오로에틸렌, 카복시메틸셀룰로오스, 폴리아크릴산, 리튬 폴리아크릴레이 트 및 폴리비닐리덴 플루오라이드로 이루어진 군으로부터 선택되는 1종 이상을 포함할 수 있다.
또한, 상기 바인더는 상기 양극 활물질층 전체 중량을 기준으로 1 중량% 내지 30 중량%로 포함될 수 있고, 구체적으로는, 상기 바인더의 함량은 1 중량% 이상 또는 3 중량% 이상일 수 있고, 15 중량% 이하 또는 30 중량% 이하일 수 있다. 상기 바인더의 함량이 1 중량% 미만이면 양극 활물질과 양극 집전체와의 접착력이 저하될 수 있고, 30 중량%를 초과하면 접착력은 향상되지만 그만큼 양극 활물질의 함량이 감소하여 전지 용량이 낮아질 수 있다.
또한, 상기 도전재는 전고체 전지의 내부 환경에서 부반응을 방지하고, 당해 전지에 화학적 변화를 유발하지 않으면서 우수한 전기전도성을 가지는 것이라면 특별히 제한되지 않으며, 대표적으로는 흑연 또는 도전성 탄소를 사용할 수 있으며, 예컨대, 천연 흑연, 인조 흑연 등의 흑연; 카본 블랙, 아세틸렌 블랙, 케첸 블랙, 덴카 블랙, 써멀 블랙, 채널 블랙, 퍼네이스 블랙, 램프 블랙, 서머 블랙 등의 카본블랙; 결정구조가 그라펜이나 그라파이트인 탄소계 물질; 탄소 섬유, 금속 섬유 등의 도전성 섬유; 불화 카본; 알루미늄 분말, 니켈 분말 등의 금속 분말;산화 아연, 티탄산 칼륨 등의 도전성 위스키; 산화 티탄 등의 도전성 산화물; 및 폴리페닐렌 유도체 등의 도전성 고분자;를 단독으로 또는 2종 이상 혼합하여 사용 할 수 있으나, 반드시 이에 한정되는 것은 아니다.
상기 도전재는 통상적으로 상기 양극 활물질층 전체 중량을 기준으로 0.5 중량% 내지 30 중량%로 포함될 수 있으며, 구체적으로 상기 도전재의 함량은 0.5 중량% 이상 또는 1 중량% 이상일 수 있고, 20 중량% 이하 또는 30 중량% 이하일 수 있다. 상기 도전재의 함량이 0.5 중량% 미만으로 너무 적으면 전기전도성 향상 효과를 기대하기 어렵거나 전지의 전기화학적 특성이 저하될 수 있으며, 30 중량%를 초과하여 너무 많으면 상대적으로 양극 활물질의 양이 적어져 용량 및 에너지 밀도가 저하될 수 있다. 양극에 도전재를 포함시키는 방법은 크게 제한되지 않으며, 양극 활물질에의 코팅 등 당분야에 공지된 통상적인 방법을 사용할 수 있다.
또한, 상기 양극 집전체는 양극 집전체는 상기 양극 활물질층을 지지하며, 외부 도선과 양극 활물질층 사이에서 전자를 전달하는 역할을 하는 것이다.
상기 양극 집전체는 전고체 전지에 화학적 변화를 유발하지 않으면서 높은 전자 전도성을 가지는 것이라면 특별히 제한되는 것은 아니다. 예를 들어, 상기 양극 집전체로 구리, 스테인리스 스틸, 알루미늄, 니켈, 티타늄, 팔라듐, 소성 탄소, 구리나 스테인리스 스틸 표면에 카본, 니켈, 은 등으로 표면 처리한 것, 알루미늄-카드뮴 합금 등이 사용될 수 있다.
상기 양극 집전체는 양극 활물질층과의 결합력을 강화시키기 위해 양극 집전체의 표면에 미세한 요철 구조를 가지거나 3차원 다공성 구조를 채용할 수 있다. 이에 따라, 상기 양극 집전체는 필름, 시트, 호일, 메쉬, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태를 포함할 수 있다.
상기와 같은 양극은 통상의 방법에 따라 제조될 수 있으며, 구체적으로는 양극 활물질과 도전재 및 바인더를 유기 용매 상에서 혼합하여 제조한 양극 활물질층 형성용 조성물을 양극 집전체 위에 도포 및 건조하고, 선택적으로 전극 밀도의 향상을 위하여 집전체에 압축 성형하여 제조할 수 있다. 이때, 상기 유기 용 매로는 양극 활물질, 바인더 및 도전재를 균일하게 분산시킬 수 있으며, 쉽게 증발되는 것을 사용하는 것이 바람직하다. 구체적으로는 아세토나이트릴, 메탄올, 에탄올, 테트라히드로퓨란, 물, 이소프로필알코올, 디메틸설폭사이드(DMSO, Dimethyl sulfoxide), 메틸피롤리돈(NMP, N-Methyl-2-Pyrrolidone) 등을 들 수 있다.
한편, 상기 전고체 전지에 포함된 상기 음극은 음극 활물질층을 포함하며, 상기 음극 활물질층은 음극 집전체의 일 면에 형성된 것일 수 있다.
상기 음극 활물질은 리튬 (Li+)을 가역적으로 삽입(intercalation) 또는 탈삽입(deintercalation)할 수 있는 물질, 리튬 이온과 반응하여 가역적으로 리튬 함유 화합물을 형성할 수 있는 물질, 리튬 금속 또는 리튬 합금을 포함할 수 있다.
상기 리튬 이온(Li+)을 가역적으로 삽입 또는 탈삽입할 수 있는 물질은 예컨대 결정질 탄소, 비정질 탄소 또는 이들의 혼합물일 수 있다. 상기 리튬 이온(Li+)과 반응하여 가역적으로 리튬 함유 화합물을 형성할 수 있는 물질은 예를 들어, 산화주석, 티타늄나이트레이트 또는 실리콘일 수 있다. 상기 리튬 합금은 예 를 들어, 리튬(Li)과 나트륨(Na), 칼륨(K), 루비듐(Rb), 세슘(Cs), 프랑슘(Fr), 베 릴륨(Be), 마그네슘(Mg), 칼슘(Ca), 스트론튬(Sr), 바륨(Ba), 라듐(Ra), 알루미늄 (Al) 및 주석(Sn)으로 이루어지는 군에서 선택되는 금속의 합금일 수 있다.
바람직하게 상기 음극 활물질은 리튬 금속일 수 있으며, 구체적으로, 리튬 금속 박막 또는 리튬 금속 분말의 형태일 수 있다.
상기 음극 활물질은 상기 음극 활물질층 전체 중량을 기준으로 40 내지 80 중량%로 포함될 수 있다. 구체적으로, 상기 음극 활물질의 함량은 40 중량 % 이상 또는 50 중량% 이상일 수 있고, 70 중량% 이하 또는 80 중량% 이하일 수 있다. 상기 음극 활물질의 함량이 40 중량% 미만이면 전기적 특성이 충분치 않을 수 있고, 80 중량% 초과이면 물질 전달 저항이 커질 수 있다.
또한, 상기 바인더는 상기 양극 활물질층에서 상술한 바와 같다.
또한, 상기 도전재는 상기 양극 활물질층에서 상술한 바와 같다.
또한, 상기 음극 집전체는 당해 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되지 않으며, 예를 들면, 상기 음극 집전체는 구리, 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 구리나 스테인리스 스틸의 표면에 카본, 니켈, 티탄, 은 등으로 표면 처리한 것, 알루미늄-카드뮴 합금 등이 사용될 수 있다. 또한, 상기 음극 집전체는 양극 집전체와 마찬가지로, 표면에 미세한 요철이 형성된 필름, 시트, 호일, 네트, 다공질체, 발포체, 부 직포체 등 다양한 형태가 사용될 수 있다.
상기 음극의 제조방법은 특별히 제한되지 않으며, 음극 집전체 상에 당업계에서 통상적으로 사용되는 층 또는 막의 형성방법을 이용하여 음극 활물질층을 형성하여 제조할 수 있다. 예컨대 압착, 코팅, 증착 등의 방법을 이용할 수 있 다. 또한, 상기 음극 집전체에 리튬 박막이 없는 상태로 전지를 조립한 후 초기 충 전에 의해 금속판 상에 금속 리튬 박막이 형성되는 경우도 본 발명의 음극에 포함된다.
한편, 발명의 추가적인 구현예에 따르면, 상기 전고체 전지를 단위전지로 포함하는 전지모듈, 상기 전지모듈을 포함하는 전지팩, 및 상기 전지팩을 전원으로 포함하는 디바이스를 제공한다.
이 때, 상기 디바이스의 구체적인 예로는, 전지적 모터에 의해 동력을 받아 움직이는 파워 툴(power tool); 전기자동차(Electric Vehicle, EV), 하이브리드 전기자동차(Hybrid Electric Vehicle, HEV), 플러그-인 하이브리드 전기자 동차(Plug-in Hybrid Electric Vehicle, PHEV) 등을 포함하는 전기차; 전기 자전거 (E-bike), 전기 스쿠터(E-scooter)를 포함하는 전기 이륜차; 전기 골프 카트 (electric golf cart); 전력저장용 시스템 등을 들 수 있으나, 이에 한정되는 것은 아니다.
이하, 발명의 이해를 돕기 위해 바람직한 실시예를 제시하지만, 하기의 실시예는 발명을 보다 쉽게 이해하기 위하여 제공되는 것일 뿐 발명이 이에 한정되는 것은 아니다.
실시예
실시예 1: 복합 고체 전해질의 제조
1 단계) 코폴리머를 포함하는 고분자 제조
하기 화학식 1a의 폴리에틸렌옥사이드(PEO)계 코폴리머를 제조하였다:
[화학식 1a]
상기 화학식 1a에서, R1은 -CH2-O-(CH2-CH2-O)k-CH3이고, R2는 -CH2-O-CH2-CH= CH2이고, k는 2이고, l : m : n의 비율은 85 : 13 : 2이고, 상기 코폴리머의 중량 평균 분자량(Mw)는 약 2,000,000g/mol인 것이었다.
상기 화학식 1a의 코폴리머는 가교 결합성 작용기로서 메틸렌 옥사이드 링커를 매개로 결합된 알릴기(allyl group)를 갖는 것이다.
상기 폴리에틸렌옥사이드 코폴리머에 아세토나이트릴을 용매로 하여, 가교제로 트라이메틸올프로페인 트라이메타크릴레이트를, 개시제로 벤조일퍼 옥사이드를, 리튬염으로 LiTFSI를, 세라믹 화합물로 LSTP를 혼합하여 고분자와 세라믹 화합물의 혼합 용액을 제조한 후, 이를 24시간 동안 마그네틱 바를 이용하여 교반하였다. 이때, 상기 폴리에틸렌옥사이드 코폴리머와 세라믹 화합물의 혼합 용액의 조성은 폴리에틸렌옥사이드 코폴리머 100 중량부에 대해서, 가교제인 트라이메틸올프로페인 트라이메타크릴레이트 20 중량부, 개시제인 벤조일퍼옥사이드 1 중량부, 리튬염인 LiTFSI 36 중량부 및 세라믹 화합물인 LSTP 40 중량부를 혼합하였으며, 상기 혼합 용액에 포함된 고분자인 폴리에틸렌옥사이드 코폴리머의 농도가 11.1 중량%가 되도록 하고, 상기 고분자인 폴리에틸렌옥사이드 코폴리머와 세라믹 화합 물의 농도는 14.9 중량%가 되도록 아세토나이트릴 용매를 사용하였다.
상기 제조된 혼합 용액을 코인셀 하부 기판에 용액 캐스팅한 후, 상온에서 12시간 동안 1차 건조한 후, 100℃에서 3시간 동안 2차 건조하여 200㎛ 두께의 전해질 필름을 제조하였다.
2 단계) 복합 고체 전해질의 제조
상기 고분자를 챔버 상판에 부착시키고, 챔버 하부에 에틸메틸카보네이트(EMC) 용매를 채워 놓은 후 상온에서 72시간 동안 자연 증발시켜 챔버 상부에 부착된 고분자의 내부로 EMC 증기를 유입시켜 고분자에 증착시켜 복합 고체 전해질을 제조하였다.
비교예:
비교예 1: 개질된 PEO + 세라믹 화합물만 포함하는 복합 고체 전해질 (용매 미포함)
상기 실시예 1의 2) 단계인 EMC 용매를 증기 증착 시키는 단계를 수행하지 않은 것을 제외하고는, 상기 실시예 1에서 제조된 것과 동일한 방법으로 복합 고체 전해질을 제조하였다.
비교예 2: 개질된 PEO + 세라믹 화합물 + 용매 다량 포함하는 복합 고체 전해질
상기 실시예 1의 1) 단계에서 제조한 복합 고체 전해질에 EMC 용매(12 중량%)를 증기 증착하지 않고 액상 용매를 직접 주입하는 것을 제외하고는, 상기 실시예 1에서 제조된 것과 동일한 방법으로 복합 고체 전해질을 제조하였다. 제조된 복합 고체 전해질 총 중량 대비 EMC 용매의 함량이 12 중량%가 되도록 직접 주입하였다.
비교예 3: 개질되지 않은 PEO + 세라믹 화합물 + 극성 용매 증착한 복합 고체 전해질
가교 결합성 작용기가 치환되지 않은 폴리에틸렌 옥사이드(PEO) 단일 중합체(중량 평균 분자량: 약 4,000,000g/mol)를 사용하고, 가교제 및 개시제를 추가하지 않은 것을 제외하고는, 상기 실시예 1에서 제조된 것과 동일한 방법으로 복합 고체 전해질을 제조하였다.
비교예 4: 개질된 PEO + 극성 용매 증착한 고분자 고체 전해질
세라믹 화합물을 추가하지 않은 것을 제외하고는, 상기 실시예 1에서 제조된 것과 동일한 방법으로 고분자 고체 전해질을 제조하였다.
실험예
실험예 1: 극성 화합물의 함량 측정
극성 화합물의 함량은 저울을 이용하여, 고체 전해질 시편을 가열하면서 시간이 경과함에 따라 증발되는 액상의 무게를 모니터링하는 방법으로 측정될 수 있다. 예컨대, 가열식 전자저울(AND사 MS-70)을 이용하여 시편을 55 내지 70℃의 온도에서, 또는 60℃의 온도에서 가열하면서 시간이 경과함에 따라 증발되는 액 상의 무게를 모니터링하여 측정될 수 있다. 시간 경과에 따라 증발되는 극성 화합 물의 양이 포화 상태에 이르게 될 때, 그 때의 포화량을 고체 전해질 내부에 포함된 극성 화합물의 총량을 간주하였다. 실시예 및 비교예에서 극성 화합물은 에틸메틸카보네이트(EMC)인 것일 수 있다.
실험예 2: 복합 고체 전해질의 이온 전도도 측정
실시예 및 비교예에서 제조된 복합 고체 전해질의 이온 전도도를 측정하기 위하여, 1.7671cm2 크기의 코인셀의 하부 기판에 상기 복합 고체 전해질을 형성시킨 후, SUS를 비활성 전극(blocking electrode)으로 사용하여 이온 전도도 측정을 위한 코인셀을 제조하였다.
전기화학 임피던스 스펙트로미터(electrochemical impedance spectrometer, EIS, VM3, Bio Logic Science Instrument)를 사용하여 25℃에서 amplitude 10 mV 및 스캔 범위 1Hz에서 0.1 MHz까지의 조건으로 저항을 측정한 후 하기 식 1을 이용하여, 상기 복합 고체 전해질의 이온 전도도를 계산하였다.
[식 1]
상기 식 1에서 σi는 복합 고체 전해질의 이온 전도도(S/cm)이고, R 은 상기 전기화학 임피던스 스펙트로미터로 측정한 복합 고체 전해질의 저항(Ω)이 고, L은 복합 고체 전해질의 두께(㎛)이고, A는 복합 고체 전해질의 면적(cm2)을 의 미한다. 상기 복합 고체 전해질 시료는 L=200㎛이고, A=1.7671cm2인 것을 사용하였다.
하기 표 1은 복합(또는 고분자) 고체 전해질에 증기 증착(또는 포함)된 EMC의 함량 및 이온 전도도 측정 결과를 나타낸 것이다.
고체 전해질 전체 중량 대비 EMC의 함량(중량%) | 이온 전도도 (S/cm) | |
실시예 1 | 1.2 | 1.3 x 10-3 |
비교예 1 | - | 1.4 x 10-4 |
비교예 2 | 12 | 3.8 x 10-4 |
비교예 3 | 1.5 | 측정 불가 |
비교예 4 | 1.2 | 5.1 x 10-4 |
개질된 PEO 기반의 고체 전해질(비교예 1) 및 액체 상태의 EMC를 직접 주입한 고체 전해질(비교예 2)의 이온 전도도가 10-4 S/cm 수준인 것에 비해 개질된 PEO에 증기 증착 공정으로 기체 상태의 극성 용매(EMC)가 포함되고 세라믹 화합물이 분산된 복합 고체 전해질(실시예 1)은 이온 전도도가 10-3 S/cm 수준으로 개선된 것을 확인할 수 있었다. 이는 상기 극성 용매(EMC)의 증기 증착으로 인해, 기체 상태의 극성 용매 화합물이 PEO의 가교된 3차원 네트워크 구조 내에 확산되거나, 고분자 사슬 상에 흡착 또는 결합되어, 리튬 이온의 이동성을 향상시킬 수 있기 때문으로 보인다.
또한, 비교예 3과 같이 가교 및 개질되지 않은 일반 PEO 기반 고체 전해질의 경우 극성 용매의 증기 증착으로 인한 이온 전도도 개선 효과가 관찰되지 않았으며, 특히 가교 구조의 결여로 인한 고분자 내부 구조 붕괴로 이온 전도도의 측정이 불가한 내부 단락(internal short) 상태가 확인되었다.
또한, 비교예 4와 같이 개질된 PEO에 증기 증착 공정으로 극성 용매 (EMC)가 포함되나, 세라믹 화합물을 미포함하는 고체 전해질은 이온 전도도가 10-4 S/cm 수준으로, 실시예 1과 비교하여 세라믹 화합물을 포함하지 않음으로 인하여 이온 전도도가 다소 저하된다는 것이 확인되었다.
실험예 3: 복합 고체 전해질의 저온 이온 전도도 측정
실시예 1 및 비교예 1의 복합 고체 전해질에 대해, -30℃ 내지 0℃의 온도에서 이온 전도도를 측정하여, 하기 표 2에 나타내었다. 단, 위 측정 온도를 제외한 이온 전도도의 측정 방법 및 조건은 실험예 2와 동일하게 진행하였다.
온도 [℃] | 이온전도도 [mS/cm] | |
실시예 1 | 비교예 1 | |
-30 | 0.1312 | 0.00003 |
-20 | 0.2376 | 0.0003 |
-10 | 0.4270 | 0.0023 |
0 | 0.6719 | 0.0112 |
상기 표 2를 참고하면, 실시예 1의 복합 고체 전해질은 비교예 1에 비해 저온에서도 매우 우수한 이온 전도도를 나타냄이 확인되었다.
Claims (19)
- 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머를 포함하는 고분자; 세라믹 화합물; 및 극성 화합물을 포함하고,상기 가교 결합성 작용기의 적어도 일부는 서로 가교 결합을 형성하여, 상기 고분자가 3차원 네트워크 구조를 형성하고 있고,상기 극성 화합물은 기체 상태로 상기 3차원 네트워크 구조 내에 포함되거나, 상기 고분자 사슬 상에 결합되어 있는 복합 고체 전해질.
- 제1항에 있어서, 상기 기체 상태의 극성 화합물은 상기 3차원 네트워크 구조를 형성한 고분자 사슬 사이에 분산되어 있거나, 상기 고분자 사슬의 표면 또는 내부에 흡착 또는 결합되어 있는 복합 고체 전해질.
- 제1항에 있어서, 상기 복합 고체 전해질은 가교제를 더 포함하는 복합 고체 전해질.
- 제3항에 있어서, 상기 복합 고체 전해질은 상기 가교 결합성 작용기의 적어도 일부는 상기 가교제를 매개로 서로 가교 결합을 형성하고 있는 복합 고체 전해질.
- 제1항에 있어서, 상기 PEO계 코폴리머는 2종 이상의 가교 결합성 작용기를 포함하는 복합 고체 전해질.
- 제1항에 있어서, 상기 가교 결합성 작용기는 상기 PEO계 코폴리머에 탄소수 0 내지 10의 알킬렌 링커 또는 알킬렌 옥사이드 링커(단, 탄소수 0인 알킬렌 링커는 단일 결합을 나타낸다)를 매개로 결합되어 있고,히드록시기(hydroxyl group), 카복실기(carboxyl group), 이소시아네이트기(isocyanate group), 니트로기(nitro group), 시아노기 (cyano group), 아민기(amine group), 아미드기(amide group), 에폭시기(epoxy group) 및 알릴기(allyl group)로 이루어진 군에서 선택되는 복합 고체 전해질.
- 제1항에 있어서, 상기 복합 고체 전해질은 리튬염을 더 포함하는 복합 고체 전해질.
- 제1항에 있어서, 상기 PEO(polyethylene oxide)계 코폴리머는 하기 화학식 1 내지 3의 반복 단위를 포함하는 공중합체인 복합 고체 전해질:[화학식 1][화학식 2][화학식 3]상기 화학식 1 내지 3에서, R1은 -CH2-O-(CH2-CH2-O)k-R3 를 나타내며, k는 0 내지 20이고, R3는 탄소수 1 내지 5의 알킬기를 나타내고,R2는 히드록시기(hydroxyl group), 카복실기(carboxyl group), 이소시아네이트기(isocyanate group), 니트로기(nitro group), 시아노기(cyano group), 아민기(amine group), 아미드기(amide group), 에폭시기 (epoxy group) 및 알릴기(allyl group)로 이루어진 군에서 선택된 1종 이상의 가교 결합성 작용기가 탄소수 0 내지 10의 알킬렌 링커 또는 알킬렌 옥사이드 링커(단, 탄소수 0인 알킬렌 링커는 단일 결합을 나타낸다)를 매개로 고분자 사슬에 결합된 치환기를 나타내며,l, m 및 n은 반복 단위의 반복수로, l 및 n은 각각 독립적으로 1 내지 1000의 정수이고, m은 0 내지 1000의 정수이다.
- 제8항에 있어서, 상기 PEO계 코폴리머는 상기 R2가 서로 다른 가교 결합성 작용기로 되는 2종 이상의 화학식 3의 반복 단위를 포함하는 복합 고체 전해질.
- 제1항에 있어서, 상기 극성 화합물의 함량이 복합 고체 전해질의 총 중량 기준으로, 0.1 중량 % 이상 내지 10 중량% 미만인 복합 고체 전해질.
- 제1항에 있어서, 상기 극성 화합물은 카보네이트계 화합물 및 설포닐계 화합물로 이루어진 군에서 선택되는 1종 이상을 포함하는 복합 고체 전해질.
- 제1항에 있어서, 상기 극성 화합물은 에틸메틸카보네이트(Ethyl Methyl carbonate, EMC), 디메틸카보네이트(Dimethyl Carbonate, DMC), 디에틸카보네이트(Diethyl Carbonate, DEC), 에틸렌카보네이트(Ethylene Carbonate, EC), 프로필렌카보네이트(Propylene Carbonate, PC), 비닐렌카보네이트(Vinylene Carbonate, VC) 및 술폴레인 (Sulfolane)로 이루어진 군에서 선택되는 1종 이상을 포함하는 복합 고체 전 해질.
- 제1항에 있어서, 상기 세라믹 화합물은 리튬 금속 산화물 또는 리튬 금속 인산화물의 산화물계 고체 전해질을 포함하는 복합 고체 전해질.
- 제1항에 있어서, 상기 세라믹 화합물은 리튬-란타늄-지르코늄 산화물계(LLZO) 화합물, 리튬-실리콘티타늄 인산염계(LSTP) 화합물, 리튬-란타늄-티타늄 산화물계(LLTO) 화합물, 리튬-알루미늄-티타늄 인산염계(LATP) 화합물, 리튬-알루미늄-게르마늄 인산염계(LAGP) 화합물 및 리튬-란타늄-지르코늄-티타늄 산화물계(LLZTO) 화합물로 이루어진 군에서 선택되는 1종 이상의 산화물계 고체 전해질을 포함하는 복합 고체 전해질.
- (S1) 가교 결합성 작용기를 포함하는 PEO(polyethylene oxide)계 코폴리머와 세라믹 화합물을 혼합한 후, 상기 혼합물에 포함된 상기 PEO계 코폴리머에 대해 가교 결합 반응을 진행하는 단계; 및(S2) 상기 (S1) 단계에서 가교된 고분자를 포함하는 혼합물에 극성 용매를 증기 증착 시키는 단계;를 포함하는 제 1 항의 복합 고체 전해질의 제조방법.
- 제15항에 있어서, 상기 (S1) 단계는 가교제 및 개시제로 이루어진 군에서 선택되 는 1종 이상의 추가 존재 하에 진행되는 복합 고체 전해질의 제조방법.
- 제15항에 있어서, 상기 극성 용매는 카보네이트계 용매 및 설포닐계 용매로 이루어지는 군에서 선택되는 1종 이상을 포함하는 복합 고체 전해질의 제조방법.
- 제15항에 있어서, 상기 (S2) 단계에서, 상기 극성 용매의 함량이 복합 고체 전해질의 총 중량 기준으로, 0.1 중량% 이상 내지 10 중량% 미만이 되도록, 상기 고분자에 상기 극성 용매의 증기를 증착 시키는 복합 고체 전해질의 제조방법.
- 제1항 내지 제14항 중 어느 한 항의 복합 고체 전해질을 포함한 전해질층을 포함하는 전고체 전지.