WO2024080268A1 - シートパッド - Google Patents
シートパッド Download PDFInfo
- Publication number
- WO2024080268A1 WO2024080268A1 PCT/JP2023/036683 JP2023036683W WO2024080268A1 WO 2024080268 A1 WO2024080268 A1 WO 2024080268A1 JP 2023036683 W JP2023036683 W JP 2023036683W WO 2024080268 A1 WO2024080268 A1 WO 2024080268A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyurethane foam
- less
- seat pad
- polyether polyol
- content
- Prior art date
Abstract
シートパッドは、ポリウレタンフォームを備え、前記ポリウレタンフォームは、たわみ係数が2.8以下であり、変位率(=t1×100/t0)が30%以上である。但し、t0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、t1は、前記平板状試料を用いて、JASO B408に準拠して減衰特性を測定したときの鉄研盤の変位量(沈み込み量)の最大値。シートパッドは、t0=50mmであるときの前記変位率が45%以上であるものが好ましい。
Description
本発明は、シートパッドに関し、さらに詳しくは、たわみ係数が小さく、かつ、変位率が大きいポリウレタンフォームを備えたシートパッドに関する。
自動車用シートは、シートクッション(座面部)とシートバック(背面部)とが分離しているタイプと、両者が一体化しているタイプとがある。
また、自動車用シートは、一般に、
(a)乗員が着座したときに、乗員の荷重を受け止めるためのシートパッドと、
(b)シートパッドを支持するためのフレームと、
(c)シートパッドの外表面を覆うトリムカバーと
を備えている。
シートパッドには、一般に、ポリウレタンフォームが用いられる。
また、自動車用シートは、一般に、
(a)乗員が着座したときに、乗員の荷重を受け止めるためのシートパッドと、
(b)シートパッドを支持するためのフレームと、
(c)シートパッドの外表面を覆うトリムカバーと
を備えている。
シートパッドには、一般に、ポリウレタンフォームが用いられる。
シートパッドを備えた自動車用シートに乗員が着座すると、シートパッドに加わる荷重の大きさに比例して、シートパッドが荷重方向に圧縮される。シートパッドに加わる荷重の大きさは、自動車用シートの形状、シートバックの傾き、自動車用シートに接触する人体の部位、乗員の姿勢、自動車が走行する路面の凹凸状態などに応じて異なる。そのため、シートパッドのたわみ係数やたわみ量(又は変位率)が不適切であると、座り心地の悪いシートとなる場合がある。
そこでこの問題を解決するために、従来から種々の提案がなされている。
例えば、特許文献1には、
(a)グリセリンにプロピレンオキシドを付加させた水酸基価168mgKOH/gの化合物(開始剤1)に、エチレンオキシド8質量%含むエチレンオキシド/プロピレンオキシド混合物を反応させることにより得られるポリオールA:60質量部と、
(b)開始剤1にプロピレンオキシドを反応させることにより得られるポリオールG5中に、ポリマー粒子が分散しているポリオールK:40質量部と、
(c)TDI-80(NOC含有量:44.8質量%):イソシアネートインデックスで105に相当する量と
を含む原料を反応させることにより得られる自動車シート用軟質ポリウレタンフォームが開示されている。
例えば、特許文献1には、
(a)グリセリンにプロピレンオキシドを付加させた水酸基価168mgKOH/gの化合物(開始剤1)に、エチレンオキシド8質量%含むエチレンオキシド/プロピレンオキシド混合物を反応させることにより得られるポリオールA:60質量部と、
(b)開始剤1にプロピレンオキシドを反応させることにより得られるポリオールG5中に、ポリマー粒子が分散しているポリオールK:40質量部と、
(c)TDI-80(NOC含有量:44.8質量%):イソシアネートインデックスで105に相当する量と
を含む原料を反応させることにより得られる自動車シート用軟質ポリウレタンフォームが開示されている。
同文献には、
(A)このような方法により、X値(=荷重883N時の静バネ定数/荷重98N時の静バネ定数)が2.94である軟質ポリウレタンフォームが得られる点、及び、
(B)このような軟質ポリウレタンフォームを自動車用シートに適用すると、座り込んだ後の底付き感が解消される点
が記載されている。
(A)このような方法により、X値(=荷重883N時の静バネ定数/荷重98N時の静バネ定数)が2.94である軟質ポリウレタンフォームが得られる点、及び、
(B)このような軟質ポリウレタンフォームを自動車用シートに適用すると、座り込んだ後の底付き感が解消される点
が記載されている。
特許文献2には、
着座部を構成するクッション本体と、
クッション本体の底面に一体的に設けられる低通気性フォームと
からなるシートパッドが開示されている。
同文献には、クッション本体の底面に低通気性フォームを一体的に設けると、乗り心地を悪化させる振動を吸収できる点が記載されている。
着座部を構成するクッション本体と、
クッション本体の底面に一体的に設けられる低通気性フォームと
からなるシートパッドが開示されている。
同文献には、クッション本体の底面に低通気性フォームを一体的に設けると、乗り心地を悪化させる振動を吸収できる点が記載されている。
特許文献3には、
(a)数平均分子量7000、平均官能基数3、水酸基価26mgKOH/gであるポリエーテルポリオール:90重量部と、
(b)数平均分子量5000、平均官能基数3、水酸基価25mgKOH/g、固形分30%であるポリマーポリオール:10重量部と、
(c)粘度7280mPa・s(25℃)、表面張力20.08mN/m(25℃)である直鎖状シリコーン系整泡剤:0.5重量部と、
(d)TDI(80重量%)とMDI(20重量%)の混合物(NCO=44.8%):イソシアネートインデックスで100に相当する量と
を含む原料を反応させることにより得られるポリウレタンフォームが開示されている。
同文献には、このような方法により、従来よりも厚みを薄くしても底突きを生じ難く、かつ通気性が大きいポリウレタンフォームを得ることができる点が記載されている。
(a)数平均分子量7000、平均官能基数3、水酸基価26mgKOH/gであるポリエーテルポリオール:90重量部と、
(b)数平均分子量5000、平均官能基数3、水酸基価25mgKOH/g、固形分30%であるポリマーポリオール:10重量部と、
(c)粘度7280mPa・s(25℃)、表面張力20.08mN/m(25℃)である直鎖状シリコーン系整泡剤:0.5重量部と、
(d)TDI(80重量%)とMDI(20重量%)の混合物(NCO=44.8%):イソシアネートインデックスで100に相当する量と
を含む原料を反応させることにより得られるポリウレタンフォームが開示されている。
同文献には、このような方法により、従来よりも厚みを薄くしても底突きを生じ難く、かつ通気性が大きいポリウレタンフォームを得ることができる点が記載されている。
特許文献4には、シートパッドではないが、非線形粘弾性挙動を有する圧縮性材料の非線形粘弾性挙動をシミュレーションする変形解析手法が開示されている。
同文献には、一般化Maxwellモデルによる線形粘弾性部分と、静水応力に依存した降伏条件式を有する圧縮性弾塑性部分とを並列に備えたモデルを使用すると、ウレタンフォームがゆっくりと押されたときの減衰挙動を高精度で解析できる点が記載されている。
同文献には、一般化Maxwellモデルによる線形粘弾性部分と、静水応力に依存した降伏条件式を有する圧縮性弾塑性部分とを並列に備えたモデルを使用すると、ウレタンフォームがゆっくりと押されたときの減衰挙動を高精度で解析できる点が記載されている。
特許文献5には、
(a)三次元構造のネット材を金型内に配置し、金型内においてポリウレタンを発泡させることにより、ポリウレタンフォーム製のクッション材に三次元構造のネット材が組み込まれたシートバック部を成形し、
(b)シートバック部の両側部に突出しているネット材に張力を付与した状態で、ネット材をフレームに固定する
ことにより得られる自動車用シートが開示されている。
(a)三次元構造のネット材を金型内に配置し、金型内においてポリウレタンを発泡させることにより、ポリウレタンフォーム製のクッション材に三次元構造のネット材が組み込まれたシートバック部を成形し、
(b)シートバック部の両側部に突出しているネット材に張力を付与した状態で、ネット材をフレームに固定する
ことにより得られる自動車用シートが開示されている。
同文献には、
(A)このような方法により、ポリウレタンフォームからなるクッション材に三次元構造のネット材が一体的に組み込まれたシートバック部が得られる点、及び、
(B)ネット材にポリウレタンが含浸している部分は面剛性が高いので、乗員の後方から衝撃が加えられたときに、衝撃を減衰させることができる点
が記載されている。
(A)このような方法により、ポリウレタンフォームからなるクッション材に三次元構造のネット材が一体的に組み込まれたシートバック部が得られる点、及び、
(B)ネット材にポリウレタンが含浸している部分は面剛性が高いので、乗員の後方から衝撃が加えられたときに、衝撃を減衰させることができる点
が記載されている。
シートパッドの硬さや弾力性は、着座したときの座り心地に影響を与える。クッション感をより大きくするためには、高荷重域においてより大きくたわむこと、すなわち、たわみ係数が小さいことが好ましい。また、着座したときの底付き感を低減するためには、変位率が大きいことが好ましい。しかしながら、小さなたわみ係数と大きな変位率とを両立させたシートパッドが提案された例は、従来にはない。
本発明が解決しようとする課題は、ポリウレタンフォームからなり、たわみ係数が小さく、かつ、変位率が大きいシートパッドを提供することにある。
上記課題を解決するために本発明に係るシートパッドは、
ポリウレタンフォームを備え、
前記ポリウレタンフォームは、
たわみ係数が2.8以下であり、
次の式(1)で表される変位率が30%以上である。
ポリウレタンフォームを備え、
前記ポリウレタンフォームは、
たわみ係数が2.8以下であり、
次の式(1)で表される変位率が30%以上である。
変位率=t1×100/t0 …(1)
但し、
t0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、
t1は、前記平板状試料を用いて、JASO B408に準拠して減衰特性を測定したときの鉄研盤の変位量(沈み込み量)の最大値。
但し、
t0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、
t1は、前記平板状試料を用いて、JASO B408に準拠して減衰特性を測定したときの鉄研盤の変位量(沈み込み量)の最大値。
前記ポリウレタンフォームは、ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を反応させることにより得られ、
前記ポリオール成分は、
(a)EO含有率が50mol%以上であり、
(b)官能基数が2.0以上3.0以下であり、
(c)重量平均分子量が3500超である
1種又は2種以上のポリエーテルポリオールAを含み
前記ポリイソシアネート成分は、カルボジイミド変性MDIを含む
ものが好ましい。
前記ポリオール成分は、
(a)EO含有率が50mol%以上であり、
(b)官能基数が2.0以上3.0以下であり、
(c)重量平均分子量が3500超である
1種又は2種以上のポリエーテルポリオールAを含み
前記ポリイソシアネート成分は、カルボジイミド変性MDIを含む
ものが好ましい。
ポリウレタンフォームを製造する場合において、所定の条件を満たすポリエーテルポリオールAと、カルボジイミド変性MDIとを含む原料混合物を用いると、たわみ係数が2.8以下であり、かつ、変位率が30%以上であるポリウレタンフォームが得られる。
たわみ係数が2.8以下となるのは、EO含有率の高いポリエーテルポリオールAを用いているために、高分子鎖中に含まれる側鎖の数が相対的に少なくなり、高分子鎖間の絡み合いが少なくなるため、及び、これによって分子鎖が伸縮しやすくなり、ポリウレタンフォームに弾性が付与されるためと考えられる。
変位率が30%以上となるのは、重量平均分子量が大きいポリエーテルポリオールAを用いているためと考えられる。
変位率が30%以上となるのは、重量平均分子量が大きいポリエーテルポリオールAを用いているためと考えられる。
以下、本発明の一実施の形態について詳細に説明する。
[1. シートパッド]
本発明に係るシートパッドは、ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を反応させることにより得られたポリウレタンフォームからなる。原料混合物は、通常、架橋剤と、発泡剤と、触媒とをさらに含む。
[1. シートパッド]
本発明に係るシートパッドは、ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を反応させることにより得られたポリウレタンフォームからなる。原料混合物は、通常、架橋剤と、発泡剤と、触媒とをさらに含む。
[1.1. ポリウレタンフォーム]
シートパッドを構成するポリウレタンフォームは、所定の条件を満たす原料混合物を発泡及び反応させることにより得られる。ポリウレタンフォームの製造方法の詳細については、後述する。
シートパッドを構成するポリウレタンフォームは、所定の条件を満たす原料混合物を発泡及び反応させることにより得られる。ポリウレタンフォームの製造方法の詳細については、後述する。
[1.2. 特性]
[1.2.1. たわみ係数]
「たわみ係数」とは、JIS K 6400-2:2012に準拠して測定される値をいう。具体的には、「たわみ係数」とは、75%の予備圧縮の後、一定の速度で75%まで圧縮した時の、65%圧縮での力(F65%)を25%圧縮での力(F25%)で除した値(=F65%/F25%)をいう。
[1.2.1. たわみ係数]
「たわみ係数」とは、JIS K 6400-2:2012に準拠して測定される値をいう。具体的には、「たわみ係数」とは、75%の予備圧縮の後、一定の速度で75%まで圧縮した時の、65%圧縮での力(F65%)を25%圧縮での力(F25%)で除した値(=F65%/F25%)をいう。
本発明に係るポリウレタンフォームは、後述するように、原料の1つとして、EO含有率の高いポリエーテルポリオールAを用いている。EO含有率の高いポリエーテルポリオールAを用いると、ポリウレタンフォームのたわみ係数が相対的に小さくなる。これは、高分子鎖中に含まれる側鎖の数が相対的に少なくなり、高分子鎖間の絡み合いが少なくなるため、及び、これによって分子鎖が伸縮しやすくなり、ポリウレタンフォームに弾性が付与されるためと考えられる。一般に、たわみ係数が小さくなるほど高荷重域においてより大きくたわむので、クッション感が大きくなる。
クッション感を大きくするためには、ポリウレタンフォームのたわみ係数は、2.8以下である必要がある。製造条件を最適化すると、たわみ係数は、2.7以下、2.6以下、あるいは、2.5以下となる。
一方、たわみ係数が小さくなりすぎると、たわみ量が大きくなりすぎ、底付き感が大きくなる場合がある。従って、たわみ係数は、2.0以上が好ましい。たわみ係数は、さらに好ましくは、2.1以上、あるいは、2.2以上である。
一方、たわみ係数が小さくなりすぎると、たわみ量が大きくなりすぎ、底付き感が大きくなる場合がある。従って、たわみ係数は、2.0以上が好ましい。たわみ係数は、さらに好ましくは、2.1以上、あるいは、2.2以上である。
[1.2.2. 変位率]
「変位率」とは、次の式(1)で表される値をいう。
変位率=t1×100/t0 …(1)
但し、
t0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、
t1は、前記平板状試料を用いて、JASO B408に準拠して減衰特性を測定したときの鉄研盤の変位量(沈み込み量)の最大値。
「変位率」とは、次の式(1)で表される値をいう。
変位率=t1×100/t0 …(1)
但し、
t0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、
t1は、前記平板状試料を用いて、JASO B408に準拠して減衰特性を測定したときの鉄研盤の変位量(沈み込み量)の最大値。
変位率は、厳密には、平板状試料の厚みt0に依存する。本発明に係るポリウレタンフォームは、厚みt0が異なる複数の平板状試料を用いて複数の変位率を測定したときに、少なくとも1つの変位率が以下の条件を満たしていれば良い。
一般に、変位率が大きくなるほど、着座したときのクッション性が大きくなる。このような効果を得るためには、変位率は30%以上である必要がある。変位率は、好ましくは、35%以上、40%以上、45%以上、50%以上、あるいは、55%以上である。
本発明に係るポリウレタンフォームにおいて、製造条件を最適化すると、t0=50mmであるときの変位率は、45%以上となる。製造条件をさらに最適化すると、t0=50mmであるときの変位率は、55%、60%以上、あるいは、65%以上となる。
同様に、本発明に係るポリウレタンフォームにおいて、製造条件を最適化すると、t0=100mmであるときの変位率は、50%以上となる。製造条件をさらに最適化すると、t0=100mmであるときの変位率は、55%以上となる。
同様に、本発明に係るポリウレタンフォームにおいて、製造条件を最適化すると、t0=100mmであるときの変位率は、50%以上となる。製造条件をさらに最適化すると、t0=100mmであるときの変位率は、55%以上となる。
[2. ポリウレタンフォームの製造方法]
シートパッドを構成するポリウレタンフォームは、
(a)ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を調製し、
(b)原料混合物を反応させる
ことにより得られる。
原料混合物は、通常、架橋剤と、発泡剤と、触媒とをさらに含む。
シートパッドを構成するポリウレタンフォームは、
(a)ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を調製し、
(b)原料混合物を反応させる
ことにより得られる。
原料混合物は、通常、架橋剤と、発泡剤と、触媒とをさらに含む。
[2.1. 主原料]
[2.1.1. ポリオール成分]
ポリオール成分は、ポリウレタンフォームの主原料の1つである。
本発明において、ポリオール成分は、
(a)EO含有率が50mol%以上であり、
(b)官能基数が2.0以上3.0以下であり、
(c)重量平均分子量が3500超である
ポリエーテルポリオールAを含む。
[2.1.1. ポリオール成分]
ポリオール成分は、ポリウレタンフォームの主原料の1つである。
本発明において、ポリオール成分は、
(a)EO含有率が50mol%以上であり、
(b)官能基数が2.0以上3.0以下であり、
(c)重量平均分子量が3500超である
ポリエーテルポリオールAを含む。
ポリオール成分は、このような条件を満たす1種類のポリエーテルポリオールAを含むものでも良く、あるいは、このような条件を満たす2種以上のポリエーテルポリオールAを含むものでも良い。
ポリオール成分は、
(a)EO含有率が30mol%以下であり、
(b)官能基数が2.0以上である
ポリエーテルポリオールBをさらに含むものでも良い。
(a)EO含有率が30mol%以下であり、
(b)官能基数が2.0以上である
ポリエーテルポリオールBをさらに含むものでも良い。
ポリオール成分は、このような条件を満たす1種類のポリエーテルポリオールBを含むものでも良く、あるいは、このような条件を満たす2種以上のポリエーテルポリオールBを含むものでも良い。
[A. ポリエーテルポリオールA]
[A.1. EO含有率]
ポリエーテルポリオールAの「EO含有率(mol%)」とは、ポリエーテルポリオールAに含まれるアルキレンオキサイド単位の総モル数に対する、エチレンオキサイド(EO)単位のモル数の割合をいう。
ポリエーテルポリオールAは、EO単位以外のアルキレンオキサイド単位を含むものでも良い。この場合、EO単位以外のアルキレンオキサイド単位の種類は特に限定されないが、プロピレンオキサイド(PO)単位が好ましい。
[A.1. EO含有率]
ポリエーテルポリオールAの「EO含有率(mol%)」とは、ポリエーテルポリオールAに含まれるアルキレンオキサイド単位の総モル数に対する、エチレンオキサイド(EO)単位のモル数の割合をいう。
ポリエーテルポリオールAは、EO単位以外のアルキレンオキサイド単位を含むものでも良い。この場合、EO単位以外のアルキレンオキサイド単位の種類は特に限定されないが、プロピレンオキサイド(PO)単位が好ましい。
ポリエーテルポリオールAのEO含有率は、主として、たわみ係数に影響を与える。一般に、ポリエーテルポリオールAのEO含有率が高くなるほど、たわみ係数が小さくなる。これは、EO含有率が高くなるほど、高分子鎖中に含まれる側鎖(-CH3)の数が相対的に少なくなり、高分子鎖間の絡み合いが少なくなるため、及び、これによって分子鎖が伸縮しやすくなり、ポリウレタンフォームに弾性が付与されるためと考えられる。
このような効果を得るためには、ポリエーテルポリオールAのEO含有率は、50.0mol%以上が好ましい。EO含有率は、さらに好ましくは、60.0mol%以上、70.0mol%以上、80.0mol%以上、あるいは、90.0mol%以上である。ポリエーテルポリオールAのEO含有率は、100.0mol%でも良い。
このような効果を得るためには、ポリエーテルポリオールAのEO含有率は、50.0mol%以上が好ましい。EO含有率は、さらに好ましくは、60.0mol%以上、70.0mol%以上、80.0mol%以上、あるいは、90.0mol%以上である。ポリエーテルポリオールAのEO含有率は、100.0mol%でも良い。
[A.2. 官能基数]
ポリエーテルポリオールAの官能基数は、たわみ係数に影響を与える。一般に、ポリエーテルポリオールAの官能基数が大きくなるほど、ポリウレタンフォームの剛性が高くなり、圧縮残留歪みが小さくなる。このような効果を得るためには、ポリエーテルポリオールAの官能基数は、2.0以上が好ましい。官能基数は、さらに好ましくは、2.1以上、あるいは、2.2以上である。
ポリエーテルポリオールAの官能基数は、たわみ係数に影響を与える。一般に、ポリエーテルポリオールAの官能基数が大きくなるほど、ポリウレタンフォームの剛性が高くなり、圧縮残留歪みが小さくなる。このような効果を得るためには、ポリエーテルポリオールAの官能基数は、2.0以上が好ましい。官能基数は、さらに好ましくは、2.1以上、あるいは、2.2以上である。
一方、ポリエーテルポリオールAの官能基数が過剰になると、ポリウレタンフォームの硬さが過度に高くなり、たわみ係数が増大する場合がある。従って、ポリエーテルポリオールAの官能基数は、3.0以下が好ましい。官能基数は、さらに好ましくは、2.9以下、あるいは、2.8以下である。
[A.3. 重量平均分子量]
ポリエーテルポリオールAの重量平均分子量が大きくなるほど、ポリウレタンフォームの硬度が低下し、たわみやすくなる。このような効果を得るためには、ポリエーテルポリオールAの重量平均分子量は、3500超が好ましい。重量平均分子量は、さらに好ましくは、4000以上、あるいは、5000以上である。
ポリエーテルポリオールAの重量平均分子量が大きくなるほど、ポリウレタンフォームの硬度が低下し、たわみやすくなる。このような効果を得るためには、ポリエーテルポリオールAの重量平均分子量は、3500超が好ましい。重量平均分子量は、さらに好ましくは、4000以上、あるいは、5000以上である。
一方、ポリエーテルポリオールAの重量平均分子量が大きくなりすぎると、原料混合物の粘度が過度に高くなり、製造性が低下する場合がある。また、原料混合物の反応性が低下し、ポリウレタンフォームの引き裂き強度が低下する場合がある。従って、重量平均分子量は、12000以下が好ましい。重量平均分子量は、さらに好ましくは、10000以下、あるいは、8000以下である。
[A.4. 水酸基価]
ポリエーテルポリオールAの水酸基価が大きくなりすぎると、シートパッドとしたときの座り心地が悪くなる場合がある。従って、水酸基価は、70mgKOH/g以下が好ましい。水酸基価は、さらに好ましくは、60mgKOH/g以下、あるいは、55mgKOH/g以下である。
一方、ポリエーテルポリオールAの水酸基価が小さくなりすぎると、ポリウレタンフォームが硬くなりすぎ、シートパッドとして用いたときに、良好な座り心地を保つことができなくなる場合がある。従って、水酸基価は、10mgKOH/g以上が好ましい。水酸基価は、さらに好ましくは、15mgKOH/g以上、あるいは、20mgKOH/g以上である。
ポリエーテルポリオールAの水酸基価が大きくなりすぎると、シートパッドとしたときの座り心地が悪くなる場合がある。従って、水酸基価は、70mgKOH/g以下が好ましい。水酸基価は、さらに好ましくは、60mgKOH/g以下、あるいは、55mgKOH/g以下である。
一方、ポリエーテルポリオールAの水酸基価が小さくなりすぎると、ポリウレタンフォームが硬くなりすぎ、シートパッドとして用いたときに、良好な座り心地を保つことができなくなる場合がある。従って、水酸基価は、10mgKOH/g以上が好ましい。水酸基価は、さらに好ましくは、15mgKOH/g以上、あるいは、20mgKOH/g以上である。
[B. ポリエーテルポリオールB]
[B.1. EO含有率]
ポリエーテルポリオールBの「EO含有率(mol%)」とは、ポリエーテルポリオールBに含まれるアルキレンオキサイド単位の総モル数に対する、エチレンオキサイド(EO)単位のモル数の割合をいう。
ポリエーテルポリオールBは、EO単位以外のアルキレンオキサイド単位を含むものでも良い。この場合、EO単位以外のアルキレンオキサイド単位の種類は特に限定されないが、プロピレンオキサイド(PO)単位が好ましい。
[B.1. EO含有率]
ポリエーテルポリオールBの「EO含有率(mol%)」とは、ポリエーテルポリオールBに含まれるアルキレンオキサイド単位の総モル数に対する、エチレンオキサイド(EO)単位のモル数の割合をいう。
ポリエーテルポリオールBは、EO単位以外のアルキレンオキサイド単位を含むものでも良い。この場合、EO単位以外のアルキレンオキサイド単位の種類は特に限定されないが、プロピレンオキサイド(PO)単位が好ましい。
ポリエーテルポリオールBのEO含有率が高くなりすぎると、原料混合物の反応性が低下する場合がある。また、フォーム状態やフォームの通気性が悪化する場合がある。従って、EO含有率は、30mol%以下が好ましい。EO含有率は、さらに好ましくは、20mol%以下、10mol%以下、あるいは、5mol%以下である。EO含有率は、ゼロでも良い。
[B.2. 官能基数]
ポリエーテルポリオールBの官能基数は、2.0以上であれば良い。
但し、ポリエーテルポリオールBの官能基数が大きくなりすぎると、ポリウレタンフォームの伸びが低下する場合がある。従って、官能基数は、4.0以下が好ましい。官能基数は、さらに好ましくは、3.8以下、あるいは、3.6以下である。
ポリエーテルポリオールBの官能基数は、2.0以上であれば良い。
但し、ポリエーテルポリオールBの官能基数が大きくなりすぎると、ポリウレタンフォームの伸びが低下する場合がある。従って、官能基数は、4.0以下が好ましい。官能基数は、さらに好ましくは、3.8以下、あるいは、3.6以下である。
[B.3. 重量平均分子量]
ポリエーテルポリオールBの重量平均分子量は、特に限定されるものではなく、目的に応じて最適な値を選択することができる。一般に、ポリエーテルポリオールBの重量平均分子量が小さくなりすぎると、ポリウレタンフォームの伸び率や柔軟性を損ねるおそれがある。従って、重量平均分子量は、1000以上が好ましい。重量平均分子量は、さらに好ましくは、2000以上、あるいは、3000以上である。
ポリエーテルポリオールBの重量平均分子量は、特に限定されるものではなく、目的に応じて最適な値を選択することができる。一般に、ポリエーテルポリオールBの重量平均分子量が小さくなりすぎると、ポリウレタンフォームの伸び率や柔軟性を損ねるおそれがある。従って、重量平均分子量は、1000以上が好ましい。重量平均分子量は、さらに好ましくは、2000以上、あるいは、3000以上である。
一方、ポリエーテルポリオールBの重量平均分子量が大きくなりすぎると、原料混合物の粘度が過度に上昇し、製造性が低下する場合がある。従って、重量平均分子量は、12000以下が好ましい。重量平均分子量は、さらに好ましくは、10000以下、あるいは、8000以下である。
[2.1.2. ポリイソシアネート成分]
ポリイソシアネート成分は、ポリウレタンフォームの主原料の他の1つである。
本発明において、ポリイソシアネート成分は、少なくともカルボジイミド変性MDIを含む。ポリイソシアネート成分は、カルボジイミド変性MDIのみを含むものでも良く、あるいは、カルボジイミド変性MDI以外のポリイソシアネート(以下、これを「ポリイソシアネートB」ともいう)をさらに含むものでも良い。
ポリイソシアネート成分は、ポリウレタンフォームの主原料の他の1つである。
本発明において、ポリイソシアネート成分は、少なくともカルボジイミド変性MDIを含む。ポリイソシアネート成分は、カルボジイミド変性MDIのみを含むものでも良く、あるいは、カルボジイミド変性MDI以外のポリイソシアネート(以下、これを「ポリイソシアネートB」ともいう)をさらに含むものでも良い。
[A. カルボジイミド変性MDI]
カルボジイミド(-N=C=N-)変性MDIは、触媒存在下において、ジフェニルメタンジイソシアネート(MDI)の-NCO基間のCO2発生を伴う縮合により生成されたものからなる。
ポリイソシアネート成分として、カルボジイミド変性MDIを用いると、ポリウレタンフォームの弾性が高くなり、高荷重域でのたわみ量が大きくなる。
カルボジイミド(-N=C=N-)変性MDIは、触媒存在下において、ジフェニルメタンジイソシアネート(MDI)の-NCO基間のCO2発生を伴う縮合により生成されたものからなる。
ポリイソシアネート成分として、カルボジイミド変性MDIを用いると、ポリウレタンフォームの弾性が高くなり、高荷重域でのたわみ量が大きくなる。
[B. ポリイソシアネートB]
本発明において、ポリイソシアネートBの種類は、特に限定されるものではなく、目的に応じて最適なものを選択することができる。
ポリイソシアネートBとしては、具体的には、2官能の芳香族系イソシアネート、2官能の脂環式イソシアネート、2官能の脂肪族イソシアネート、官能基数が2を超えるイソシアネートなどがある。原料混合物は、これらのいずれか1種のポリイソシアネートBを含むものでも良く、あるいは、2種以上を含むものでも良い。
本発明において、ポリイソシアネートBの種類は、特に限定されるものではなく、目的に応じて最適なものを選択することができる。
ポリイソシアネートBとしては、具体的には、2官能の芳香族系イソシアネート、2官能の脂環式イソシアネート、2官能の脂肪族イソシアネート、官能基数が2を超えるイソシアネートなどがある。原料混合物は、これらのいずれか1種のポリイソシアネートBを含むものでも良く、あるいは、2種以上を含むものでも良い。
2官能の芳香族系イソシアネートとしては、例えば、
2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート、
m-フェニレンジイソシネート、p-フェニレンジイソシアネート、
4,4'-ジフェニルメタンジイソシアネート(4,4'-MDI)、
2,4'-ジフェニルメタンジイソシアネート(2,4'-MDI)、
2,2'-ジフェニルメタンジイソシアネート(2,2'-MDI)、
キシリレンジイソシアネート、
3,3'-ジメチル-4,4'-ビフェニレンジイソネート、
3,3'-ジメトキシ-4,4'-ビフェニレンジイソシアネートなどがあり、これらの混合物であっても良い。
2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート、
m-フェニレンジイソシネート、p-フェニレンジイソシアネート、
4,4'-ジフェニルメタンジイソシアネート(4,4'-MDI)、
2,4'-ジフェニルメタンジイソシアネート(2,4'-MDI)、
2,2'-ジフェニルメタンジイソシアネート(2,2'-MDI)、
キシリレンジイソシアネート、
3,3'-ジメチル-4,4'-ビフェニレンジイソネート、
3,3'-ジメトキシ-4,4'-ビフェニレンジイソシアネートなどがあり、これらの混合物であっても良い。
2官能の脂環式イソシアネートとしては、例えば、
シクロヘキサン-1,4-ジイソシアネート、イソホロンジイソシアネート、
ジシクロヘキシルメタン-4,4'-ジイソシアネート、
メチルシクロヘキサンジイソシアネートなどがある。
シクロヘキサン-1,4-ジイソシアネート、イソホロンジイソシアネート、
ジシクロヘキシルメタン-4,4'-ジイソシアネート、
メチルシクロヘキサンジイソシアネートなどがある。
2官能の脂肪族系イソシアネートとしては、例えば、
ブタン-1,4-ジイソシアネート、ヘキサメチレンジイソシアネート、
イソプロピレンジイソシアネート、メチレンジイソシアネート、リジンイソシアネート
などがある。2官能以上のイソシアネートとしては、ポリメリックMDI、3官能以上のイソシアネートなどがある。
ブタン-1,4-ジイソシアネート、ヘキサメチレンジイソシアネート、
イソプロピレンジイソシアネート、メチレンジイソシアネート、リジンイソシアネート
などがある。2官能以上のイソシアネートとしては、ポリメリックMDI、3官能以上のイソシアネートなどがある。
官能基数が2を超えるイソシアネートとしては、例えば、
1-メチルベンゾール-2,4,6-トリイソシアネート、
1,3,5-トリメチルベンゾール-2,4,6-トリイソシアネート、
ビフェニル-2,4,4'-トリイソシアネート、
ジフェニルメタン-2,4,4'-トリイソシアネート、
メチルジフェニルメタン-4,6,4'-トリイソシアネート、
4,4'-ジメチルジフェニルメタン-2,2',5,5'テトライソシアネート、
トリフェニルメタン-4,4',4"-トリイソシアネート、
などがある。
1-メチルベンゾール-2,4,6-トリイソシアネート、
1,3,5-トリメチルベンゾール-2,4,6-トリイソシアネート、
ビフェニル-2,4,4'-トリイソシアネート、
ジフェニルメタン-2,4,4'-トリイソシアネート、
メチルジフェニルメタン-4,6,4'-トリイソシアネート、
4,4'-ジメチルジフェニルメタン-2,2',5,5'テトライソシアネート、
トリフェニルメタン-4,4',4"-トリイソシアネート、
などがある。
[C. NCO基含有率(NCO%)]
「NCO基含有率(NCO%)」とは、ポリイソシアネート成分の総質量に対する、NCO基の質量の割合をいう。
ポリイソシアネート成分のNCO%は、35%未満が好ましく、30%未満がより好ましく、29.5%以下がさらに好ましい。
「NCO基含有率(NCO%)」とは、ポリイソシアネート成分の総質量に対する、NCO基の質量の割合をいう。
ポリイソシアネート成分のNCO%は、35%未満が好ましく、30%未満がより好ましく、29.5%以下がさらに好ましい。
[2.1.3. 架橋剤]
原料混合物は、架橋剤を含むものでも良い。架橋剤は、少なくとも官能基数が3以上であり、かつ、活性水素原子を持つ官能基(例えば、水酸基、アミノ基など)を含む化合物が好ましい。架橋剤は、官能基数が3以上の化合物のみからなるものでも良く、あるいは、官能基数が3以上である化合物に加えて、官能基数が2である化合物をさらに含むものでも良い。
原料混合物は、架橋剤を含むものでも良い。架橋剤は、少なくとも官能基数が3以上であり、かつ、活性水素原子を持つ官能基(例えば、水酸基、アミノ基など)を含む化合物が好ましい。架橋剤は、官能基数が3以上の化合物のみからなるものでも良く、あるいは、官能基数が3以上である化合物に加えて、官能基数が2である化合物をさらに含むものでも良い。
架橋剤の官能基数は、圧縮残留歪みに影響を与える。圧縮残留歪の小さいポリウレタンフォームを得るためには、架橋剤の官能基数は、3以上が好ましい。
一方、架橋剤の官能基数が大きくなりすぎると、ポリウレタンフォームの硬さが過度に高くなる場合がある。従って、架橋剤の官能基数は、6以下が好ましい。
一方、架橋剤の官能基数が大きくなりすぎると、ポリウレタンフォームの硬さが過度に高くなる場合がある。従って、架橋剤の官能基数は、6以下が好ましい。
架橋剤の分子量は、特に限定されるものではなく、目的に応じて最適な値を選択することができる。架橋剤の分子量は、好ましくは、1000以下、700以下、あるいは、500以下である。
また、架橋剤の分子量は、60以上、90以上、あるいは、120以上が好ましい。
また、架橋剤の分子量は、60以上、90以上、あるいは、120以上が好ましい。
架橋剤としては、例えば、グリセリン、ジエタノールアミン(DEA)、多官能ポリオールなどがある。
原料混合物には、これらのいずれか1種の架橋剤が含まれていても良く、あるいは、2種以上が含まれていても良い。
原料混合物には、これらのいずれか1種の架橋剤が含まれていても良く、あるいは、2種以上が含まれていても良い。
[2.1.4. 発泡剤]
「発泡剤」とは、液状の原料混合物が樹脂化していく過程で原料混合物中に気泡を生成させるための添加剤をいう。
本発明において、発泡剤は、
(a)圧力低下又は加熱によりガスを発生させる物理発泡剤、又は、
(b)熱分解又は化学反応によりガスを発生させる化学発泡剤
のいずれであっても良い。
「発泡剤」とは、液状の原料混合物が樹脂化していく過程で原料混合物中に気泡を生成させるための添加剤をいう。
本発明において、発泡剤は、
(a)圧力低下又は加熱によりガスを発生させる物理発泡剤、又は、
(b)熱分解又は化学反応によりガスを発生させる化学発泡剤
のいずれであっても良い。
物理発泡剤としては、例えば、
(a)シクロペンタン、イソペンタン、ノルマルペンタンなどの炭化水素、
(b)塩化メチレン、トリクロロフルオロメタン、ジクロロジフルオロメタン、ノナフルオロブチルメチルエーテル、ペンタフルオロエチルメチルエーテル、ペンタフルオロイソプロピルメチルエーテルなどのハロゲン系化合物、
などがある。
(a)シクロペンタン、イソペンタン、ノルマルペンタンなどの炭化水素、
(b)塩化メチレン、トリクロロフルオロメタン、ジクロロジフルオロメタン、ノナフルオロブチルメチルエーテル、ペンタフルオロエチルメチルエーテル、ペンタフルオロイソプロピルメチルエーテルなどのハロゲン系化合物、
などがある。
化学発泡剤としては、例えば、
(a)イソシアネート基と反応してCO2を発生させる水、
(b)熱分解によって、窒素、一酸化炭素、二酸化炭素、又は、アンモニアガスを発生させるアゾジカルボンアミド
などがある。
(a)イソシアネート基と反応してCO2を発生させる水、
(b)熱分解によって、窒素、一酸化炭素、二酸化炭素、又は、アンモニアガスを発生させるアゾジカルボンアミド
などがある。
原料混合物には、これらのいずれか1種の発泡剤が含まれていても良く、あるいは、2種以上が含まれていても良い。
これらの中でも、発泡剤は、水が好ましい。発泡剤として水を用いると、水とイソシアネート基とが反応することにより発生したCO2ガスが発泡を促す。また、水とイソシアネート基との反応熱が樹脂の硬化を促進する。
これらの中でも、発泡剤は、水が好ましい。発泡剤として水を用いると、水とイソシアネート基とが反応することにより発生したCO2ガスが発泡を促す。また、水とイソシアネート基との反応熱が樹脂の硬化を促進する。
[2.1.5. 触媒]
「触媒」とは、樹脂化反応を促進する作用が大きい触媒、及び/又は、泡化反応を促進する作用が大きい触媒をいう。
なお、発泡剤として、化学発泡剤(水)を用いない場合には、樹脂化反応を促進する作用が大きい触媒を用いるのが好ましい。
「触媒」とは、樹脂化反応を促進する作用が大きい触媒、及び/又は、泡化反応を促進する作用が大きい触媒をいう。
なお、発泡剤として、化学発泡剤(水)を用いない場合には、樹脂化反応を促進する作用が大きい触媒を用いるのが好ましい。
触媒としては、例えば、アミン系触媒、金属触媒などがある。アミン系触媒は、樹脂化反応と泡化反応の双方を促進する作用が大きい触媒である。金属触媒は、樹脂化反応を促進する作用が大きい触媒である。原料混合物には、これらのいずれか1種の触媒が含まれていても良く、あるいは、2種以上が含まれていても良い。
アミン系触媒としては、例えば、
N,N-ジメチルシクロヘキシルアミン、N,N-ジメチルベンジルアミン、
N,N-ジメチルアミノエタノール、
N,N’,N’-トリメチルアミノエチルピペラジン、トリエチレンジアミン
等が挙げられる。
N,N-ジメチルシクロヘキシルアミン、N,N-ジメチルベンジルアミン、
N,N-ジメチルアミノエタノール、
N,N’,N’-トリメチルアミノエチルピペラジン、トリエチレンジアミン
等が挙げられる。
金属触媒としては、例えば、
(a)スタナスオクトエート、ジブチルチンジラウレートなどの錫触媒、
(b)フェニル水銀プロピオン酸塩などの水銀触媒、
(c)オクテン酸鉛などの鉛触媒
等が挙げられる。
(a)スタナスオクトエート、ジブチルチンジラウレートなどの錫触媒、
(b)フェニル水銀プロピオン酸塩などの水銀触媒、
(c)オクテン酸鉛などの鉛触媒
等が挙げられる。
[2.2. 副原料]
原料混合物は、上述した主原料に加えて、以下の1種又は2種以上の副原料をさらに含むものでも良い。副原料としては、具体的には、以下のようなものがある。
原料混合物は、上述した主原料に加えて、以下の1種又は2種以上の副原料をさらに含むものでも良い。副原料としては、具体的には、以下のようなものがある。
[2.2.1. 整泡剤]
「整泡剤」とは、気泡の大きさや分布を均一化する作用がある添加剤をいう。
原料混合物に整泡剤を添加すると、気泡の大きさや分布が均一なポリウレタンフォームを得ることができる。整泡剤としては、例えば、シリコーン系整泡剤、含フッ素化合物系整泡剤、公知の界面活性剤などがある。
「整泡剤」とは、気泡の大きさや分布を均一化する作用がある添加剤をいう。
原料混合物に整泡剤を添加すると、気泡の大きさや分布が均一なポリウレタンフォームを得ることができる。整泡剤としては、例えば、シリコーン系整泡剤、含フッ素化合物系整泡剤、公知の界面活性剤などがある。
[2.2.2. 難燃剤]
「難燃剤」とは、ポリウレタンフォームを難燃化させる作用がある添加剤をいう。
難燃剤としては、例えば、ハロゲン系難燃剤、リン系難燃剤、金属水酸化物系難燃剤、アンチモン系難燃剤などがある。
「難燃剤」とは、ポリウレタンフォームを難燃化させる作用がある添加剤をいう。
難燃剤としては、例えば、ハロゲン系難燃剤、リン系難燃剤、金属水酸化物系難燃剤、アンチモン系難燃剤などがある。
[2.3. 配合量、含有量]
[2.3.1. 主原料の配合量、含有量]
[A. ポリエーテルポリオールAの配合量]
「ポリエーテルポリオールAの配合量(質量部)」とは、ポリオール成分の総質量を100としたときの、ポリオール成分中のポリエーテルポリオールAの総質量をいう。
[2.3.1. 主原料の配合量、含有量]
[A. ポリエーテルポリオールAの配合量]
「ポリエーテルポリオールAの配合量(質量部)」とは、ポリオール成分の総質量を100としたときの、ポリオール成分中のポリエーテルポリオールAの総質量をいう。
一般に、ポリエーテルポリオールAの配合量が多くなるほど、ポリウレタンフォームのたわみ係数が小さくなる。このような効果を得るためには、ポリエーテルポリオールAの配合量は、50質量部以上が好ましい。配合量は、さらに好ましくは、60質量部以上、あるいは、70質量部以上である。
ポリエーテルポリオールAの配合量は、100質量部でも良い。しかしながら、ポリエーテルポリオールAの配合量が過剰になると、フォームの成形性が低下する場合がある。従って、ポリエーテルポリオールAの配合量は、90質量部以下が好ましい。
[B. カルボジイミド変性MDIの含有量]
「カルボジイミド変性MDIの含有量(質量%)」とは、ポリイソシアネート成分の総質量に対する、カルボジイミド変性MDIの質量の割合をいう。
「カルボジイミド変性MDIの含有量(質量%)」とは、ポリイソシアネート成分の総質量に対する、カルボジイミド変性MDIの質量の割合をいう。
一般に、カルボジイミド変性MDIの含有量が多くなるほど、ポリウレタンフォームのたわみ係数が小さくなり、かつ、変位率が大きくなる。このような効果を得るためには、カルボジイミド変性MDIの含有量は、50質量%以上が好ましい。含有量は、さらに好ましくは、60質量%以上、あるいは、70質量%以上である。
カルボジイミド変性MDIの含有量は、100質量%でも良い。カルボジイミド変性MDIの含有量は、好ましくは、90質量%以下、あるいは、80質量%以下である。
カルボジイミド変性MDIのNCO含有率は、40%以下、35%以下、あるいは、32%以下が好ましく、特に30%以下が好ましい。また、NCO含有率は、15%以上、20%以上、25%以上、あるいは、27%以上が好ましい。
カルボジイミド変性MDIのNCO含有率は、40%以下、35%以下、あるいは、32%以下が好ましく、特に30%以下が好ましい。また、NCO含有率は、15%以上、20%以上、25%以上、あるいは、27%以上が好ましい。
[C. 架橋剤の配合量]
「架橋剤の配合量(質量部)」とは、ポリオール成分の総質量を100としたときの、架橋剤の質量をいう。
「架橋剤の配合量(質量部)」とは、ポリオール成分の総質量を100としたときの、架橋剤の質量をいう。
一般に、架橋剤の配合量が多くなるほど、ポリウレタンフォームの圧縮残留歪が小さくなる。このような効果を得るためには、架橋剤の配合量は、0質量部超が好ましい。配合量は、さらに好ましくは、1質量部以上、あるいは、2質量部以上である。
一方、架橋剤の配合量が過剰になると、ポリウレタンフォームの硬さが過度に高くなる場合がある。従って、架橋剤の配合量は、10質量部以下が好ましい。配合量は、さらに好ましくは、8質量部以下、あるいは、6質量部以下である。
[D. ポリエーテルポリオールBの配合量]
「ポリエーテルポリオールBの配合量(質量部)」とは、ポリオール成分の総質量を100としたときの、ポリオール成分中のポリエーテルポリオールBの質量をいう。
「ポリエーテルポリオールBの配合量(質量部)」とは、ポリオール成分の総質量を100としたときの、ポリオール成分中のポリエーテルポリオールBの質量をいう。
一般に、ポリエーテルポリオールBの配合量が過剰になると、相対的にポリエーテルポリオールAの配合量が少なくなる。その結果、ポリウレタンフォームのたわみ係数が大きくなり、あるいは、変位率が低下する場合がある。従って、ポリエーテルポリオールBの配合量は、50質量部未満が好ましい。配合量は、さらに好ましくは、40質量部以下、あるいは、30質量部以下である。
[E. イソシアネートインデックス]
「イソシアネートインデックス」とは、原料混合物中の活性水素基の当量に対する、原料混合物中のポリイソシアネートのイソシアネート基の当量の比に100を掛けた値をいう。
「イソシアネートインデックス」とは、原料混合物中の活性水素基の当量に対する、原料混合物中のポリイソシアネートのイソシアネート基の当量の比に100を掛けた値をいう。
本発明において、イソシアネートインデックスは、特に限定されるものではなく、目的に応じて最適な値を選択することができる。一般に、イソシアネートインデックスが大きくなるほど、圧縮残留歪が小さくなる。このような効果を得るためには、イソシアネートインデックスは、90以上が好ましい。イソシアネートインデックスは、さらに好ましくは、95以上である。
一方、イソシアネートインデックスが大きくなりすぎると、ポリウレタンフォームの硬度が過度に高くなる場合がある。従って、イソシアネートインデックスは、115以下が好ましい。
一方、イソシアネートインデックスが大きくなりすぎると、ポリウレタンフォームの硬度が過度に高くなる場合がある。従って、イソシアネートインデックスは、115以下が好ましい。
[2.3.2. 副原料の配合量]
本発明において、副原料の配合量は特に限定されるものではなく、目的に応じて最適な含有量を選択することができる。
本発明において、副原料の配合量は特に限定されるものではなく、目的に応じて最適な含有量を選択することができる。
[2.4. 原料混合物の反応]
本発明に係るポリウレタンフォームの製造方法における発泡は、スラブ発泡及びモールド発泡のいずれを採用することもできる。
スラブ発泡は、ポリウレタンフォーム製造用組成物(ポリウレタンフォームの原料)を混合してベルトコンベア上に吐出し、大気圧下、常温で発泡させる方法である。
本発明に係るポリウレタンフォームの製造方法における発泡は、スラブ発泡及びモールド発泡のいずれを採用することもできる。
スラブ発泡は、ポリウレタンフォーム製造用組成物(ポリウレタンフォームの原料)を混合してベルトコンベア上に吐出し、大気圧下、常温で発泡させる方法である。
一方、モールド発泡は、モールド(金型)のキャビティにポリウレタンフォーム製造用原料(ポリウレタンフォームの原料)を混合して注入し、キャビティ形状に発泡させる方法である。モールド発泡は、シートパッドの形状に近い形状を有するポリウレタンフォームが得られる点で好ましい。
なお、モールド成形する場合には、ポリイソシアネートは、粘度が低いものが好ましく、例えば、プレポリマータイプのポリイソシアネートは好ましくない。
なお、モールド成形する場合には、ポリイソシアネートは、粘度が低いものが好ましく、例えば、プレポリマータイプのポリイソシアネートは好ましくない。
[3. 作用]
ポリウレタンフォームを製造する場合において、所定の条件を満たすポリエーテルポリオールAと、カルボジイミド変性MDIとを含む原料混合物を用いると、たわみ係数が2.8以下であり、かつ、変位率が30%以上であるポリウレタンフォームが得られる。
このようなポリウレタンフォームをシートパッドとして用いた場合には、薄肉(例えば、50mm以下)でも、優れたたわみ係数を有し、優れた減衰特性におけるたわみ量(変位率)を有する。
ポリウレタンフォームを製造する場合において、所定の条件を満たすポリエーテルポリオールAと、カルボジイミド変性MDIとを含む原料混合物を用いると、たわみ係数が2.8以下であり、かつ、変位率が30%以上であるポリウレタンフォームが得られる。
このようなポリウレタンフォームをシートパッドとして用いた場合には、薄肉(例えば、50mm以下)でも、優れたたわみ係数を有し、優れた減衰特性におけるたわみ量(変位率)を有する。
たわみ係数が2.8以下となるのは、EO含有率の高いポリエーテルポリオールAを用いているために、高分子鎖中に含まれる側鎖の数が相対的に少なくなり、高分子鎖間の絡み合いが少なくなるため、及び、これによって分子鎖が伸縮しやすくなり、ポリウレタンフォームに弾性が付与されるためと考えられる。
変位率が30%以上となるのは、重量平均分子量が大きいポリエーテルポリオールAを用いているためと考えられる。
変位率が30%以上となるのは、重量平均分子量が大きいポリエーテルポリオールAを用いているためと考えられる。
(実施例1~4、比較例1~2)
[1. 試料の作製]
ポリエーテルポリオール、架橋剤、発泡剤、触媒、及び、整泡剤を所定の比率で配合し、混合液(以下、「成分A」ともいう)を得た。
また、ポリメリックMDI、カルボジイミド変性MDIを含有するMDI(NCO含有率:29%、カルボジイミド変性MDIの含有量:75質量%)、及び、MDIプレポリマー(NCO含有率:28.5%)を所定の比率で配合し、混合液(以下、「成分B」ともいう)を得た。
さらに、イソシアネートインデックスが所定の値となるように、成分Aと成分Bとを混合し、原料混合物を得た。表1に、成分A及び成分Bの組成を示す。
[1. 試料の作製]
ポリエーテルポリオール、架橋剤、発泡剤、触媒、及び、整泡剤を所定の比率で配合し、混合液(以下、「成分A」ともいう)を得た。
また、ポリメリックMDI、カルボジイミド変性MDIを含有するMDI(NCO含有率:29%、カルボジイミド変性MDIの含有量:75質量%)、及び、MDIプレポリマー(NCO含有率:28.5%)を所定の比率で配合し、混合液(以下、「成分B」ともいう)を得た。
さらに、イソシアネートインデックスが所定の値となるように、成分Aと成分Bとを混合し、原料混合物を得た。表1に、成分A及び成分Bの組成を示す。
なお、実施例1は、ポリエーテルポリオールAとして、ポリエーテルポリオール2(分子量:4000、官能基数:2、EO含有率:80mol%)のみを用いた例である。
実施例2、3は、ポリエーテルポリオールAとして、
(a)ポリエーテルポリオール2(分子量:4000、官能基数:2、EO含有率:80mol%)と、
(b)ポリエーテルポリオール3(分子量:5000、官能基数:3、EO含有率:80mol%)と
の混合物を用いた例である。
実施例4は、ポリエーテルポリオールAとして、ポリエーテルポリオール3のみを用いた例である。
実施例2、3は、ポリエーテルポリオールAとして、
(a)ポリエーテルポリオール2(分子量:4000、官能基数:2、EO含有率:80mol%)と、
(b)ポリエーテルポリオール3(分子量:5000、官能基数:3、EO含有率:80mol%)と
の混合物を用いた例である。
実施例4は、ポリエーテルポリオールAとして、ポリエーテルポリオール3のみを用いた例である。
得られた原料混合物を、400mm×400mm×100mmの金型に注入し、型温約60℃で発泡及び硬化させた。なお、キュア時間は5分とした。
[2. 試験方法]
[2.1. コア密度]
得られた発泡体からスキン層を取り除き、コア密度測定用の試料とした。得られた試料を用いて、JIS K 7222に準拠してコア密度を測定した。
[2.1. コア密度]
得られた発泡体からスキン層を取り除き、コア密度測定用の試料とした。得られた試料を用いて、JIS K 7222に準拠してコア密度を測定した。
[2.2. 25%硬さ]
JIS K 6400-2 D法に準拠して、25%硬さを測定した。
JIS K 6400-2 D法に準拠して、25%硬さを測定した。
[2.3. ヒステリシスロス]
JIS K 6400-2 E法に準拠して、ヒステリシスロスを測定した。
JIS K 6400-2 E法に準拠して、ヒステリシスロスを測定した。
[2.4. たわみ係数]
JIS K 6400-2 E法に準拠して、たわみ係数を測定した。たわみ係数は、65%圧縮荷重を25%圧縮荷重で割ることにより求めた。
JIS K 6400-2 E法に準拠して、たわみ係数を測定した。たわみ係数は、65%圧縮荷重を25%圧縮荷重で割ることにより求めた。
[2.5. 応力緩和]
JIS K 6400-4に準拠して、応力緩和を求めた。荷重は196Nとし、加圧時間は5分とした。
JIS K 6400-4に準拠して、応力緩和を求めた。荷重は196Nとし、加圧時間は5分とした。
[2.6. 減衰特性]
図1に、減衰試験機の模式図を示す。試料の上方20mmの位置に、質量50kgの鉄研盤を配置した。その位置から鉄研盤を試料に向かって自由落下させた。落下後の鉄研盤の変位や、振動が停止するまでの時間から、試料の振動特性を評価した。
図1に、減衰試験機の模式図を示す。試料の上方20mmの位置に、質量50kgの鉄研盤を配置した。その位置から鉄研盤を試料に向かって自由落下させた。落下後の鉄研盤の変位や、振動が停止するまでの時間から、試料の振動特性を評価した。
[3. 結果]
表2に、結果を示す。なお、表2には、テストピースサイズ、及び、各物性値の評価試験方法も併せて示した。図2に、実施例1~4及び比較例1~2で得られたポリウレタンフォームのFSカーブを示す。図3に、実施例1~4及び比較例1~2で得られたポリウレタンフォーム(厚み100mm)の減衰試験の結果を示す。図4に、実施例1~4及び比較例1~2で得られたポリウレタンフォーム(厚み50mm)の減衰試験の結果を示す。表2及び図2~図4より、以下のことが分かる。
表2に、結果を示す。なお、表2には、テストピースサイズ、及び、各物性値の評価試験方法も併せて示した。図2に、実施例1~4及び比較例1~2で得られたポリウレタンフォームのFSカーブを示す。図3に、実施例1~4及び比較例1~2で得られたポリウレタンフォーム(厚み100mm)の減衰試験の結果を示す。図4に、実施例1~4及び比較例1~2で得られたポリウレタンフォーム(厚み50mm)の減衰試験の結果を示す。表2及び図2~図4より、以下のことが分かる。
(1)比較例1は、t0=50mmにおける変位率及びt0=100mmにおける変位率が、いずれも30%未満となった。これは、重量平均分子量が3500を超えるポリエーテルポリオールAを含まないためと考えられる。
(2)比較例2は、変位率は大きいが、たわみ係数が2.8を超えた。これは、ポリエーテルポリオールAの含有量が過度に少ないためと考えられる。
(3)実施例1~4は、いずれも、たわみ係数が2.8以下であった。また、試料の厚みt0によらず、いずれも、変位率が50%以上であった。
(2)比較例2は、変位率は大きいが、たわみ係数が2.8を超えた。これは、ポリエーテルポリオールAの含有量が過度に少ないためと考えられる。
(3)実施例1~4は、いずれも、たわみ係数が2.8以下であった。また、試料の厚みt0によらず、いずれも、変位率が50%以上であった。
以上、本発明の実施の形態について詳細に説明したが、本発明は上記実施の形態に何ら限定されるものではなく、本発明の要旨を逸脱しない範囲内で種々の改変が可能である。
本発明に係るシートパッドは、自動車、航空機、鉄道車両の座席のシートパッド、ソファーやマットレス及びそれらのクッション材として使用することができる。
Claims (5)
- ポリウレタンフォームを備えるシートパッドであって、
前記ポリウレタンフォームは、
たわみ係数が2.8以下であり、
次の式(1)で表される変位率が30%以上である
シートパッド。
変位率=t1×100/t0 …(1)
但し、
t0は、前記ポリウレタンフォームから切り出された平板状試料の厚み、
t1は、前記平板状試料を用いて、JASO B408に準拠して減衰特性を測定したときの鉄研盤の変位量(沈み込み量)の最大値。 - t0=50mmであるときの前記変位率が45%以上である請求項1に記載のシートパッド。
- t0=100mmであるときの前記変位率が50%以上である請求項1に記載のシートパッド。
- 前記ポリウレタンフォームは、ポリオール成分と、ポリイソシアネート成分とを含む原料混合物を反応させることにより得られ、
前記ポリオール成分は、
(a)EO含有率が50mol%以上であり、
(b)官能基数が2.0以上3.0以下であり、
(c)重量平均分子量が3500超である
1種又は2種以上のポリエーテルポリオールAを含み
前記ポリイソシアネート成分は、カルボジイミド変性MDIを含む
請求項1に記載のシートパッド。 - 前記ポリオール成分は、
(a)EO含有率が30mol%以下であり、
(b)平均官能基数が2.0以上である
1種又は2種以上のポリエーテルポリオールBをさらに含む
請求項4に記載のシートパッド。