WO2024070613A1 - 光学ガラス、光学素子、光学系、接合レンズ、顕微鏡用対物レンズ、カメラ用交換レンズ、及び光学装置 - Google Patents
光学ガラス、光学素子、光学系、接合レンズ、顕微鏡用対物レンズ、カメラ用交換レンズ、及び光学装置 Download PDFInfo
- Publication number
- WO2024070613A1 WO2024070613A1 PCT/JP2023/032958 JP2023032958W WO2024070613A1 WO 2024070613 A1 WO2024070613 A1 WO 2024070613A1 JP 2023032958 W JP2023032958 W JP 2023032958W WO 2024070613 A1 WO2024070613 A1 WO 2024070613A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- optical
- content
- optical glass
- lens
- glass
- Prior art date
Abstract
カチオンのモル%表示で、La3+含有率:5~35%、Si4+含有率:5~25%、Nb5+含有率:5~35%、Al3+含有率:5~35%、Ti4+、Zr4+、Nb5+、Ta5+及びAl3+の総含有率(Ti4++Zr4++Nb5++Ta5++Al3+):45~80%、である、光学ガラス。
Description
本発明は、光学ガラス、光学素子、光学系、接合レンズ、顕微鏡用対物レンズ、カメラ用交換レンズ、及び光学装置に関する。本発明は2022年9月30日に出願された日本国特許の出願番号2022-158015の優先権を主張し、文献の参照による織り込みが認められる指定国については、その出願に記載された内容は参照により本出願に織り込まれる。
光学ガラスは、様々な光学素子や光学装置に用いられており、例えば、特許文献1には紫外から赤外領域に用いられるハロゲン化物ガラスが開示されている。光学装置に用いられる光学系の設計の自由度を広げるために、高い屈折率を有する光学ガラスの開発が求められている。
本発明に係る一の態様は、カチオンのモル%表示で、La3+含有率:5~35%、Si4+含有率:5~25%、Nb5+含有率:5~35%、Al3+含有率:5~35%、Ti4+、Zr4+、Nb5+、Ta5+及びAl3+の総含有率(Ti4++Zr4++Nb5++Ta5++Al3+):45~80%、である、光学ガラスである。
本発明に係る他の態様は、上述の光学ガラスを用いた、光学素子である。
本発明に係る他の態様は、上述の光学素子を含む、光学系である。
本発明に係る他の態様は、上述の光学素子を含む光学系を含む、顕微鏡用対物レンズである。
本発明に係る他の態様は、上述の光学素子を含む光学系を含む、カメラ用交換レンズである。
本発明に係る他の態様は、上述の光学素子を含む光学系を含む、光学装置である。
本発明に係る他の態様は、第1のレンズ要素と第2のレンズ要素を有し、第1のレンズ要素と第2のレンズ要素の少なくとも1つは、上述の光学ガラスである、接合レンズである。
本発明に係る他の態様は、上述の接合レンズを含む、光学系である。
本発明に係る他の態様は、上述の接合レンズを含む光学系を含む、顕微鏡用対物レンズである。
本発明に係る他の態様は、上述の接合レンズを含む光学系を含む、カメラ用交換レンズである。
本発明に係る他の態様は、上述の接合レンズを含む光学系を含む、光学装置である。
以下、本発明に係る実施形態(以下、「本実施形態」という。)について説明する。以下の本実施形態は、本発明を説明するための例示であり、本発明を以下の内容に限定する趣旨ではない。本発明は、その要旨の範囲内で適宜に変形して実施できる。
また、Q含有率が「0~N%」という表現は、Q成分を含まない場合及び、Q成分が0%を超えてN%以下である場合を含む表現である。
また、「Q成分を含まない」という表現は、このQ成分を実質的に含まないことを意味し、この構成成分の含有率が不純物レベル程度以下であることを指す。不純物レベル程度以下とは、例えば、0.01%未満であることを意味する。
「耐失透安定性」という表現は、ガラスの失透に対する耐性のことを意味する。ここで「失透」とは、ガラスをガラス転移温度以上に昇温した際、あるいは融液状態から液相温度以下に降温した際に生じる結晶化又は分相等により、ガラスの透明性が失われる現象のことを意味する。
<光学ガラス>
本実施形態に係る光学ガラスは、カチオンのモル%表示で、La3+含有率:5~35%、Si4+含有率:5~25%、Nb5+含有率:5~35%、Al3+含有率:5~35%、Ti4+、Zr4+、Nb5+、Ta5+及びAl3+の総含有率(Ti4++Zr4++Nb5++Ta5++Al3+):45~80%、である、光学ガラスである。
本実施形態に係る光学ガラスは、カチオンのモル%表示で、La3+含有率:5~35%、Si4+含有率:5~25%、Nb5+含有率:5~35%、Al3+含有率:5~35%、Ti4+、Zr4+、Nb5+、Ta5+及びAl3+の総含有率(Ti4++Zr4++Nb5++Ta5++Al3+):45~80%、である、光学ガラスである。
なお、本明細書中において、特に断らない場合は、各成分の含有率は全てカチオンのモル%表示であるものとする。カチオンのモル%とは、光学ガラス中に含まれる総カチオンのモル数に対する対象のカチオンのモル数の割合のことを指す。より具体的には、SiO2 50mol%、Na2O 50mol%の場合、カチオンのモル%表示では、Si4+は33.3%、Na+は、66.7%となる。また、各カチオンの態様は特に限定されないが、例えば、酸化物等の態様で光学ガラスに含有され得る。
本実施形態に係る光学ガラスは、La2O3とNb2O5を主成分とした組成系とすることで、高屈折率、高透過率を実現した新規な光学ガラスである。本組成系は、るつぼ熔解ではガラス化せず、浮遊熔解法により得ることができる組成系であるが、低比重と高い耐失透安定性を両立することによりガラスの浮上が容易であり、浮遊熔解法でも直径10mm以上のガラスゴブを安定して作製することができる。
まず、本実施形態に係る光学ガラスの各成分について説明する。
La3+は、例えば、酸化物換算組成ではLa2O3として含まれる成分である。La3+は、屈折率及び透過率を高める効果を有する。しかし、この含有率が高まると比重が増大しやすくなる。かかる観点から、La3+の含有率は、5~35%である。そして、この含有率の下限は、好ましくは8%であり、より好ましくは12%であり、更に好ましくは15%である。また、この含有率の上限は、好ましくは32%であり、より好ましくは29%、更に好ましくは26%である。
Si4+は、例えば、酸化物換算組成ではSiO2として含まれる成分である。Si4+は、耐失透安定性を高めることができると同時に、低比重を維持することができる成分である。しかし、この含有率が高まると屈折率が低下しやすくなる。かかる観点から、Si4+の含有率は、5~25%である。そして、この含有率の下限は、好ましくは6%であり、より好ましくは8%であり、更に好ましくは10%である。また、この含有率の上限は、好ましくは24%であり、より好ましくは22%、更に好ましくは20%である。
Nb5+は、例えば、酸化物換算組成ではNb2O5として含まれる成分である。屈折率及び透過率を高める効果を有する。しかし、この含有率が高まると高比重化しやすくなる。かかる観点から、Nb5+の含有率は、5~35%である。そして、この含有率の下限は、好ましくは8%であり、より好ましくは12%であり、更に好ましくは16%である。また、この含有率の上限は、好ましくは32%であり、より好ましくは29%、更に好ましくは26%である。
Al3+は、例えば、酸化物換算組成ではAl2O3として含まれる成分である。Al3+は、耐失透安定性を高めることができると同時に、低比重を維持することができる成分である。しかし、この含有率が高まると屈折率が低下しやすくなる。かかる観点から、Al3+の含有率は、5~35%である。そして、この含有率の下限は、好ましくは8%であり、より好ましくは12%であり、更に好ましくは14%である。また、この含有率の上限は、好ましくは32%であり、より好ましくは29%、更に好ましくは26%である。
Zr4+は、例えば、酸化物換算組成ではZrO2として含まれる成分である。Zr4+は、耐失透安定性及び屈折率を高める効果を有する。かかる観点から、Zr4+の含有率は、0~15%である。そして、この含有率の下限は、好ましくは2%であり、より好ましくは4%であり、更に好ましくは6%である。また、この含有率の上限は、好ましくは14%であり、より好ましくは12%、更に好ましくは10%である。
Ti4+は、例えば、酸化物換算組成ではTiO2として含まれる成分である。Ti4+は、低比重を維持しつつ、屈折率を高める効果を有する。しかし、この含有率が高まると透過率が低下しやすくなる。かかる観点から、Ti4+の含有率は、0~20%である。そして、この含有率の下限は、好ましくは2%であり、より好ましくは4%であり、更に好ましくは6%である。また、この含有率の上限は、好ましくは20%であり、より好ましくは16%、更に好ましくは10%である。
Ta5+は、例えば、酸化物換算組成ではTa2O5として含まれる成分である。Ta5+は、低分散性を維持しつつ、耐失透安定性を高める効果を有する。しかし、この含有率が高まると比重が増大しやすくなる。かかる観点から、Ta5+の含有率は、0~15%である。そして、この含有率の下限は、好ましくは2%であり、より好ましくは3%であり、更に好ましくは5%である。また、この含有率の上限は、好ましくは12%であり、より好ましくは10%、更に好ましくは8%である。
Ti4+とZr4+とNb5+とTa5+とAl3+の総含有率(Ti4++Zr4++Nb5++Ta5++Al3+)は、45~80%である。そして、この総含有率の下限は、好ましくは50%であり、より好ましくは54%であり、更に好ましくは56%である。この総含有率の上限は、好ましくは76%であり、より好ましくは73%であり、更に好ましくは70%である。(Ti4++Zr4++Nb5++Ta5++Al3+)をかかる範囲とすることで熔解時の耐失透安定性を維持しながら高屈折率と高透過率を両立することができる。
本実施形態に係るガラス組成物は、その他の任意成分として、Y3+、B3+のいずれか1種を更に含有してもよい。
Y3+は、例えば、酸化物換算組成ではY2O3として含まれる成分である。Y3+は、低分散性を損なわずに屈折率と透過率を高めることができる成分である。かかる観点から、Y3+の含有率は、0~15%である。そして、この含有率の下限は、好ましくは2%であり、より好ましくは4%であり、更に好ましくは6%である。また、この含有率の上限は、好ましくは12%であり、より好ましくは10%、更に好ましくは8%である。そして、La3+及びY3+を、ともに含有することが好ましい。
B3+は、例えば、酸化物換算組成ではB2O3として含まれ、網目形成酸化物を構成する成分である。B3+は、揮発性が高い成分であるため、過剰に導入すると製造時においてガラスの組成変動を招き、脈理を顕在化させることがある。かかる観点から、B3+を実質的に含まないことが好ましい。また、B3+を含む場合は、この含有率の上限は、好ましくは10%であり、より好ましくは5%、更に好ましくは2%である。
その他必要に応じて清澄、着色、消色や光学恒数値の微調整等の目的で、公知の清澄剤や着色剤、脱泡剤、フッ素化合物等の成分をガラス組成に適量添加することができる。また、上記成分に限らず、本実施形態に係る光学ガラスの効果が得られる範囲でその他成分を添加することもできる。
原料は、不純物の含有率が少ない高純度品を使用するのが好ましい。高純度品とは、当該成分を99.85質量%以上含むものである。高純度品の使用によって、不純物量が少なくなる結果、光学ガラスの内部透過率を高くできる傾向にある。
次に、本実施形態の光学ガラスの物性値について説明する。
光学系の可視光透過率の観点から、本実施形態に係る光学ガラスは高い内部透過率を有していることが好ましい。かかる実情を踏まえれば、本実施形態に係る光学ガラスは、10mmあたりの内部透過率が80%となる波長(λ80)は420nm以下である。そして、λ80となる波長の上限は、好ましくは405nmであり、より好ましくは400nmであり、更に好ましくは395nmである。
レンズの薄型化の観点からは、本実施形態に係る光学ガラスは、高い屈折率を有している(屈折率(nd)が大きい)ことが望ましい。しかしながら、一般的に、屈折率(nd)が高いほど透過率が低下する傾向にある。かかる実情を踏まえれば、本実施形態に係る光学ガラスにおけるd線に対する屈折率(nd)は、1.95~2.15の範囲である。そして、屈折率(nd)の下限は、好ましくは1.96であり、より好ましくは1.97であり、更に好ましくは1.99である。屈折率(nd)の上限は、好ましくは2.12であり、より好ましくは2.08であり、更に好ましくは2.05である。
本実施形態に係る光学ガラスのアッベ数(νd)は、20~35の範囲である。そして、アッベ数(νd)の下限は、好ましくは22であり、より好ましくは24であり、更に好ましくは25である。アッベ数(νd)の上限は、好ましくは32であり、より好ましくは30であり、更に好ましくは29である。
レンズの収差補正の観点からは、本実施形態に係る光学ガラスの部分分散比(Pg,F)は、0.55~0.65である。そして、部分分散比(Pg,F)の下限は、好ましくは0.56であり、より好ましくは0.57であり、更に好ましくは0.58である。部分分散比(Pg,F)の上限は、好ましくは0.64であり、より好ましくは0.62であり、更に好ましくは0.61である。また、本実施形態に係る光学ガラスの部分分散比(Pg,F)は、以下の式
-0.00403×νd+0.704<Pg,F<-0.00403×νd+0.717・・・(1)
を満たすことが好ましい。なお、部分分散比(Pg,F)は、Vブロック法で測定された屈折率に基づいて算出される値である。
-0.00403×νd+0.704<Pg,F<-0.00403×νd+0.717・・・(1)
を満たすことが好ましい。なお、部分分散比(Pg,F)は、Vブロック法で測定された屈折率に基づいて算出される値である。
本実施形態に係る光学ガラスは、長軸方向の長さが10mm以上である。長軸方向の長さは、好ましくは11mm以上であり、より好ましくは12mm以上であり、更に好ましくは13mm以上である。ここでいう「長軸方向の長さ」とは、ガラスゴブの直径方向の最大値をいい、略球形の場合はその直径値をいう。
本実施形態に係る光学ガラスは、厚み(T)が4mm以上であることが好ましく、より好ましくは5mm以上であり、更に好ましくは5.5mm以上である。ここでいう「厚み」とは、ガラスゴブの直径の最大値(直径(D))に対して垂直な方向の高さをいい、略球形の場合はその直径値をいう。
本実施形態に係る光学ガラスは、重量が1.5g以上であることが好ましく、より好ましくは2.0g以上であり、更に好ましくは2.5g以上である。
本発明に係る光学ガラスは、浮遊炉を用いて製造される場合、その比重は6.0以下であることが望ましい。かかる事情を踏まえれば、本実施形態に係る光学ガラスは、比重(Sg)が4.6~5.6である。そして、比重の下限は、好ましくは4.7であり、より好ましくは4.8であり、更に好ましくは4.9である。比重の上限は、好ましくは5.5であり、より好ましくは5.3であり、更に好ましくは5.1である。
本実施形態に係る光学ガラスは、そのガラス転移温度(Tg)と結晶化開始温度(Tx)の温度差(ΔT=Tx-Tg)が大きいほど耐失透安定性が高まる。かかる実情を踏まえれば本実施形態に係る光学ガラスのガラス転移温度(Tg)と結晶化開始温度(Tx)の温度差(ΔT=Tx-Tg)は、80℃~200℃である。そして、その差の下限は、好ましくは100℃であり、より好ましくは130℃であり、更に好ましくは160℃である。そして、その差の上限は、好ましくは190℃であり、より好ましくは180℃であり、更に好ましくは170℃である。ΔTは、耐失透安定性の指標として用いることができる。一般的に、ΔTが高いことは、ガラスの耐失透安定性が高いことを意味する。そして、本実施形態において、ガラス転移温度(Tg)と結晶化開始温度(Tx)は、いずれも示差熱分析によって測定できる。
上述した観点から、本実施形態に係る光学ガラスは、例えば、光学機器が備える光学素子として好適に用いることができる。このような光学素子には、ミラー、レンズ、プリズム、フィルタ等が含まれる。また上記光学素子が用いられる光学系としては、例えば、対物レンズ、集光レンズ、結像レンズ、カメラ用交換レンズ等が挙げられる。そして、これらの光学系は、レンズ交換式カメラ、レンズ非交換式カメラ等の撮像装置、蛍光顕微鏡や多光子顕微鏡等の顕微鏡装置の各種光学装置に好適に使用できる。かかる光学装置は、上述した撮像装置や顕微鏡に限られず、望遠鏡、双眼鏡、レーザ距離計、プロジェクタ等も含まれるが、これらに限られない。以下に、これらの一例を説明する。
<撮像装置>
図1は、本実施形態に係る光学装置を撮像装置とした一例を示す斜視図である。撮像装置1はいわゆるデジタル一眼レフカメラ(レンズ交換式カメラ)であり、撮影レンズ103(光学系)は本実施形態に係る光学ガラスを母材とする光学素子を備えたものである。カメラボディ101のレンズマウント(不図示)にレンズ鏡筒102が着脱自在に取り付けられる。そして、該レンズ鏡筒102のレンズ103を通した光が、カメラボディ101の背面側に配置されたマルチチップモジュール106のセンサチップ(固体撮像素子)104上に結像される。このセンサチップ104は、いわゆるCMOSイメージセンサー等のベアチップであり、マルチチップモジュール106は、例えばセンサチップ104がガラス基板105上にベアチップ実装されたCOG(Chip On Glass)タイプのモジュールである。
図1は、本実施形態に係る光学装置を撮像装置とした一例を示す斜視図である。撮像装置1はいわゆるデジタル一眼レフカメラ(レンズ交換式カメラ)であり、撮影レンズ103(光学系)は本実施形態に係る光学ガラスを母材とする光学素子を備えたものである。カメラボディ101のレンズマウント(不図示)にレンズ鏡筒102が着脱自在に取り付けられる。そして、該レンズ鏡筒102のレンズ103を通した光が、カメラボディ101の背面側に配置されたマルチチップモジュール106のセンサチップ(固体撮像素子)104上に結像される。このセンサチップ104は、いわゆるCMOSイメージセンサー等のベアチップであり、マルチチップモジュール106は、例えばセンサチップ104がガラス基板105上にベアチップ実装されたCOG(Chip On Glass)タイプのモジュールである。
図2及び図3は、本実施形態に係る光学装置を撮像装置とした他の例を示す概略図である。図2は、撮像装置CAMの正面図を示し、図3は、撮像装置CAMの背面図を示す。撮像装置CAMはいわゆるデジタルスチルカメラ(レンズ非交換式カメラ)であり、撮影レンズWL(光学系)は本実施形態に係る光学ガラスを母材とする光学素子を備えたものである。
撮像装置CAMは、電源ボタン(不図示)を押すと、撮影レンズWLのシャッタ(不図示)が開放されて、撮影レンズWLで被写体(物体)からの光が集光され、像面に配置された撮像素子に結像される。撮像素子に結像された被写体像は、撮像装置CAMの背後に配置された液晶モニタM1に表示される。撮影者は、液晶モニタM1を見ながら被写体像の構図を決めた後、レリーズボタンB1を押し下げて被写体像を撮像素子で撮像し、メモリー(不図示)に記録保存する。
撮像装置CAMには、被写体が暗い場合に補助光を発光する補助光発光部EF、撮像装置CAMの種々の条件設定等に使用するファンクションボタンB2等が配置されている。
このようなデジタルカメラ等に用いられる光学系には、より高い解像度、低い色収差、小型化が求められる。これらを実現するには光学系に分散特性が互いに異なるガラスを用いることが有効である。特に、低分散でありながらより高い部分分散比(Pg,F)を有するガラスの需要は高い。このような観点から、本実施形態に係る光学ガラスは、かかる光学機器の部材として好適である。なお、本実施形態において適用可能な光学機器としては、上述した撮像装置に限らず、例えばプロジェクタ等も挙げられる。光学素子についても、レンズに限らず、例えばプリズム等も挙げられる。
<顕微鏡>
図4は、本実施形態に係る多光子顕微鏡2の構成の例を示すブロック図である。多光子顕微鏡2は、対物レンズ206、集光レンズ208、結像レンズ210を備える。対物レンズ206、集光レンズ208、結像レンズ210のうち少なくとも1つは、本実施形態に係る光学ガラスを母材とする光学素子を備えたものである。以下、多光子顕微鏡2の光学系を中心に説明する。
図4は、本実施形態に係る多光子顕微鏡2の構成の例を示すブロック図である。多光子顕微鏡2は、対物レンズ206、集光レンズ208、結像レンズ210を備える。対物レンズ206、集光レンズ208、結像レンズ210のうち少なくとも1つは、本実施形態に係る光学ガラスを母材とする光学素子を備えたものである。以下、多光子顕微鏡2の光学系を中心に説明する。
パルスレーザ装置201は、例えば、近赤外波長(約1000nm)であって、パルス幅がフェムト秒単位の(例えば、100フェムト秒の)超短パルス光を射出する。パルスレーザ装置201から射出された直後の超短パルス光は、一般に所定の方向に偏光された直線偏光となっている。
パルス分割装置202は、超短パルス光を分割し、超短パルス光の繰り返し周波数を高くして射出する。
ビーム調整部203は、パルス分割装置202から入射される超短パルス光のビーム径を、対物レンズ206の瞳径に合わせて調整する機能、試料Sから発せられる光の波長と超短パルス光の波長との軸上の色収差(ピント差)を補正するために超短パルス光の集光及び発散角度を調整する機能、超短パルス光のパルス幅が光学系を通過する間に群速度分散により広がってしまうのを補正するために、逆の群速度分散を超短パルス光に与えるプリチャープ機能(群速度分散補償機能)等を有する。
パルスレーザ装置201から射出された超短パルス光は、パルス分割装置202によりその繰り返し周波数が大きくされ、ビーム調整部203により上記した調整が行われる。そして、ビーム調整部203から射出された超短パルス光は、ダイクロイックミラー204によりダイクロイックミラーの方向に反射され、ダイクロイックミラー205を通過し、対物レンズ206により集光されて試料Sに照射される。このとき、走査手段(不図示)を用いることにより、超短パルス光を試料Sの観察面上に走査させてもよい。
例えば、試料Sを蛍光観察する場合、試料Sの超短パルス光の被照射領域及びその近傍では、試料Sが染色されている蛍光色素が多光子励起され、赤外波長である超短パルス光より波長が短い蛍光(以下、「観察光」という。)が発せられる。
試料Sから対物レンズ206の方向に発せられた観察光は、対物レンズ206によりコリメートされ、その波長に応じて、ダイクロイックミラー205により反射されたり、あるいは、ダイクロイックミラー205を透過する。
ダイクロイックミラー205により反射された観察光は、蛍光検出部207に入射する。蛍光検出部207は、例えば、バリアフィルタ、PMT(photo multiplier tube:光電子増倍管)等により構成され、ダイクロイックミラー205により反射された観察光を受光し、その光量に応じた電気信号を出力する。また、蛍光検出部207は、超短パルス光が試料Sの観察面において走査されるのに合わせて、試料Sの観察面にわたる観察光を検出する。
なお、ダイクロイックミラー205を光路から外すことにより、試料Sから対物レンズ206の方向に発せられた全ての観察光を蛍光検出部211で検出するようにしてもよい。その場合、観察光は、走査手段(不図示)によりデスキャンされ、ダイクロイックミラー204を透過し、集光レンズ208により集光され、対物レンズ206の焦点位置とほぼ共役な位置に設けられているピンホール209を通過し、結像レンズ210を透過して、蛍光検出部211に入射する。
蛍光検出部211は、例えば、バリアフィルタ、PMT等により構成され、結像レンズ210により蛍光検出部211の受光面において結像した観察光を受光し、その光量に応じた電気信号を出力する。また、蛍光検出部211は、超短パルス光が試料Sの観察面において走査されるのに合わせて、試料Sの観察面にわたる観察光を検出する。
なお、ダイクロイックミラー205を光路から外すことにより、試料Sから対物レンズ206の方向に発せられた全ての観察光を蛍光検出部211で検出するようにしてもよい。
また、試料Sから対物レンズ206と逆の方向に発せられた観察光は、ダイクロイックミラー212により反射され、蛍光検出部213に入射する。蛍光検出部113は、例えば、バリアフィルタ、PMT等により構成され、ダイクロイックミラー212により反射された観察光を受光し、その光量に応じた電気信号を出力する。また、蛍光検出部213は、超短パルス光が試料Sの観察面において走査されるのに合わせて、試料Sの観察面にわたる観察光を検出する。
蛍光検出部207、211、213からそれぞれ出力された電気信号は、例えば、コンピュータ(不図示)に入力され、そのコンピュータは、入力された電気信号に基づいて、観察画像を生成し、生成した観察画像を表示したり、観察画像のデータを記憶したりすることができる。
<接合レンズ>
図5は、本実施形態に係る接合レンズの一例を示す概略図である。接合レンズ3は、第1のレンズ要素301と第2のレンズ要素302とを有する複合レンズである。第1のレンズ要素と第2のレンズ要素の少なくとも1つは、本実施形態に係る光学ガラスを用いる。第1のレンズ要素と第2のレンズ要素は、接合部材303を介して接合されている。接合部材303としては、公知の接着剤等を用いることができる。なお、「レンズ要素」とは、単レンズ又は接合レンズを構成する各々のレンズのことを意味する。
図5は、本実施形態に係る接合レンズの一例を示す概略図である。接合レンズ3は、第1のレンズ要素301と第2のレンズ要素302とを有する複合レンズである。第1のレンズ要素と第2のレンズ要素の少なくとも1つは、本実施形態に係る光学ガラスを用いる。第1のレンズ要素と第2のレンズ要素は、接合部材303を介して接合されている。接合部材303としては、公知の接着剤等を用いることができる。なお、「レンズ要素」とは、単レンズ又は接合レンズを構成する各々のレンズのことを意味する。
本実施形態に係る接合レンズは、色収差補正の観点で有用であり、上述した光学素子や光学系や光学装置等に好適に使用できる。そして、接合レンズを含む光学系は、カメラ用交換レンズや光学装置等にとりわけ好適に使用できる。なお、上述の態様では2つのレンズ要素を用いた接合レンズについて説明したが、これに限られず、3つ以上のレンズ要素を用いた接合レンズとしてもよい。3つ以上のレンズ要素を用いた接合レンズとする場合、3つ以上のレンズ要素のうち少なくとも1つが本実施形態に係る光学ガラスを用いて形成されていればよい。
<光学ガラスの製造方法>
本実施形態に係る光学ガラスは、例えば、浮遊炉を用いて製造することができる。浮遊炉には、静電式、電磁式、音波式、磁気式、及びガスジェット式等があり、特に限定されるものではないが、酸化物の浮遊熔解にはガスジェット式の浮遊炉を用いることが好ましい。以下、ガスジェット式の浮遊炉を用いる製造方法を一例として説明する。
本実施形態に係る光学ガラスは、例えば、浮遊炉を用いて製造することができる。浮遊炉には、静電式、電磁式、音波式、磁気式、及びガスジェット式等があり、特に限定されるものではないが、酸化物の浮遊熔解にはガスジェット式の浮遊炉を用いることが好ましい。以下、ガスジェット式の浮遊炉を用いる製造方法を一例として説明する。
図6は、ガスジェット式の浮遊炉の全体構成の模式図を示し、図7は、ガスジェット式の浮遊炉のステージ上の台座の拡大模式図である。
ガスジェット式の浮遊炉4では、原料Mは、ステージ401上の台座402に配置される。そして、レーザ光源403から出射されたレーザ光Lは、ミラー404とミラー405を介して原料Mへ照射される。レーザ光Lの照射により加熱される原料Mの温度は、放射温度計406でモニタされる。放射温度計406がモニタする原料Mの温度情報に基づき、レーザ光源403の出力がコンピュータ407によって制御される。また、原料Mの状態はCCDカメラ408によって撮像され、それがモニタ409へ出力される(図6参照)。なお、レーザ光源としては、例えば、炭酸ガスレーザを使用できる。
ガスジェット式の浮遊炉4では、台座に送り込まれるガスによって原料Mが浮遊する状態にある(図7参照)。台座に送り込まれるガスの流量は、ガス流量調節器410によって制御される。例えば、円錐状の孔を設けたノズルからガスを噴射し、原料Mを浮遊させた状態でレーザ光Lによる非接触加熱を行うことができる。原料Mが熔解すると自身の表面張力によって球形、又は楕円体形状となりその状態で浮遊する。
その後、レーザ光Lを遮断すると融液状態となった原料は冷却され、透明なガラスが得られる。なお、ガスの種類は特に限定されず、公知のものを適宜採用することができ、例えば、酸素、窒素、二酸化炭素、アルゴン、空気等が挙げられる。また、ノズルの形状や加熱方式は特に限定されず、公知の方法を適宜採用することができる。
従来において、例えば、るつぼ等の容器を用いて光学ガラスを製造する場合、SiO2、B2O3、P2O5、GeO2等の網目形成酸化物を多く含ませてガラス形成能を高めることが必要であった。そのため、網目形成酸化物でない材料を多量に含有し、上述した網目形成酸化物の含有量が少ないガラス組成とした場合には、容器-融液界面を起点とした結晶化(不均一核生成)が発生して、ガラス化できないことが多いといった事情があった。また、各種光学機器の光学レンズの材料としてガラスゴブが用いられることがあるが、このガラスゴブについては大型なものを安定して作製できることが望まれている。
この点、本実施形態では、例えば、上述した浮遊炉を用いる方法によって光学ガラスを製造する場合、容器と融液の接触がないため、不均一核生成を最大限抑制することができる。結果、融液のガラス形成を大きく促進し、るつぼ熔解では製造不可能な、網目形成酸化物の含有量が少ない、或いは一切含まない組成であってもガラス化することが可能になる。かかる製造方法を採用することで、従来ではガラス化させることができなかった本実施形態に係る組成系の光学ガラスを製造することができる。さらに、上述したような大型のガラスゴブも作製することができる。加えて、本実施形態に係る光学ガラスは、高屈折率かつ高アッベ数である。本実施形態に係る光学ガラスはこのような利点を多々有するため、高屈低分散硝材や広帯域透過材料としての応用が可能である。
次に、本発明の実施例及び比較例について説明する。なお、本発明はこれらに限定されるものではない。
<光学ガラスの作製>
各実施例及び各比較例に係る光学ガラスは、図6及び図7に示すガスジェット式の浮遊炉4を用い、以下の手順で作製した。まず、各表に記載の組成(カチオンのモル%)となるよう、酸化物から選ばれるガラス原料を秤量した。また、ガラス原料を水酸化物、炭酸塩、硝酸塩、硫酸塩から選んでも良い。次に、秤量した原料をアルミナ製乳鉢で混合した。この原料を20MPaで一軸加圧し円柱形のペレットに成形した。得られたペレットを電気炉で1000~1300℃、大気中で3~6時間焼成し、焼結体を作製した。得られた焼結体を粗く砕き、50~4000mgを採取して台座のノズルに設置した。そして、空気ガスを噴射しながら炭酸ガスレーザを上方から照射することで原料を熔解させた。熔解した原料は、自身の表面張力で球形又は楕円体形状になり、ガスの圧力で浮遊状態とした。原料が完全に熔解した状態でレーザ出力を遮断することで、原料を冷却した。さらに760~810℃の温度で10時間アニールを行い、各実施例については直径10.30~14.55mm、厚み5.20~6.04mmのゴブ(ガラス球)を得た。各実施例のガラスについては、いずれも熔解中に視認できる揮発は確認されず、泡や失透についても確認されなかった。
各実施例及び各比較例に係る光学ガラスは、図6及び図7に示すガスジェット式の浮遊炉4を用い、以下の手順で作製した。まず、各表に記載の組成(カチオンのモル%)となるよう、酸化物から選ばれるガラス原料を秤量した。また、ガラス原料を水酸化物、炭酸塩、硝酸塩、硫酸塩から選んでも良い。次に、秤量した原料をアルミナ製乳鉢で混合した。この原料を20MPaで一軸加圧し円柱形のペレットに成形した。得られたペレットを電気炉で1000~1300℃、大気中で3~6時間焼成し、焼結体を作製した。得られた焼結体を粗く砕き、50~4000mgを採取して台座のノズルに設置した。そして、空気ガスを噴射しながら炭酸ガスレーザを上方から照射することで原料を熔解させた。熔解した原料は、自身の表面張力で球形又は楕円体形状になり、ガスの圧力で浮遊状態とした。原料が完全に熔解した状態でレーザ出力を遮断することで、原料を冷却した。さらに760~810℃の温度で10時間アニールを行い、各実施例については直径10.30~14.55mm、厚み5.20~6.04mmのゴブ(ガラス球)を得た。各実施例のガラスについては、いずれも熔解中に視認できる揮発は確認されず、泡や失透についても確認されなかった。
<物性評価>
図8、図9は、各実施例の光学恒数値をプロットしたグラフである。
図8、図9は、各実施例の光学恒数値をプロットしたグラフである。
結晶化開始温度(Tx)、ガラス転移温度(Tg)、その温度差(ΔT)の測定
結晶化開始温度(Tx)と、ガラス転移温度(Tg)は、いずれも昇温過程における示差熱分析(昇温温度10℃/分)によって測定し、Tx-Tgを温度差(ΔT)とした。
結晶化開始温度(Tx)と、ガラス転移温度(Tg)は、いずれも昇温過程における示差熱分析(昇温温度10℃/分)によって測定し、Tx-Tgを温度差(ΔT)とした。
比重(Sg)
各サンプルの比重(Sg)は、アルキメデス法によって測定した。比重の値は、小数点以下第3位までとした。
各サンプルの比重(Sg)は、アルキメデス法によって測定した。比重の値は、小数点以下第3位までとした。
直径(D)、厚み(T)
各サンプルの直径(D)及び各サンプルの厚み(T)は、電子ノギスで測定した。
各サンプルの直径(D)及び各サンプルの厚み(T)は、電子ノギスで測定した。
屈折率(nd)とアッベ数(νd)
実施例のサンプルを90度のプリズム加工を行い、屈折率測定器(カルニュー光学工業社製;「KPR-3000」)を用いてVブロック法により屈折率を測定し、アッベ数と部分分散比を算出した。
実施例のサンプルを90度のプリズム加工を行い、屈折率測定器(カルニュー光学工業社製;「KPR-3000」)を用いてVブロック法により屈折率を測定し、アッベ数と部分分散比を算出した。
比較例は、プリズムカプラ(Metricon製、モデル「2010/M」)を用いてプリズムカップリング法により屈折率を測定及びアッベ数を算出した。プリズムカップリング法ではガラス試料を研磨し、研磨面を単結晶ルチルプリズムに密着させ、測定波長の光を入射させた際の全反射角を測定して屈折率を求めた。473nm、594.1nm、656nmの3波長で各5回測定し、平均値を測定値とした。さらに、得られた実測値に対し、以下のDrude-Voigtの分散式を用いて最小二乗法によるフィッティングを行い、d線(587.562nm)、F線(486.133nm)、C線(656.273nm)における屈折率と、アッベ数(νd)を算出した。
(n:屈折率、m:電子質量、c:光速度、e:電荷素量、N:単位体積当たりの分子数、f:振動子強度、λ0:固有共鳴波長、λ:波長)
ndは、587.562nmの光に対するガラスの屈折率を示す。アッベ数(νd)は、以下の式(2)より求めた。nC、nF、はそれぞれ波長656.273nm、486.133nmの光に対するガラスの屈折率を示す。
νd=(nd-1)/(nF-nC)・・・(2)
屈折率の値は、小数点以下第6位までとした。
νd=(nd-1)/(nF-nC)・・・(2)
屈折率の値は、小数点以下第6位までとした。
部分分散比(Pg,F)
各サンプルの部分分散比(Pg,F)は、主分散(nF-nC)に対する部分分散(ng-nF)の比を示し、以下の式(3)より求めた。ngは、波長435.835nmの光に対するガラスの屈折率を示す。部分分散比(Pg,F)の値は、小数点以下第4位までとした。
Pg,F=(ng-nF)/(nF-nC)・・・(3)
各サンプルの部分分散比(Pg,F)は、主分散(nF-nC)に対する部分分散(ng-nF)の比を示し、以下の式(3)より求めた。ngは、波長435.835nmの光に対するガラスの屈折率を示す。部分分散比(Pg,F)の値は、小数点以下第4位までとした。
Pg,F=(ng-nF)/(nF-nC)・・・(3)
内部透過率
各サンプルの内部透過率は、4~9mm厚の平行研磨品の波長300~700nmにおける透過率を分光光度計(日立ハイテクサイエンス社製;「紫外可視赤外分光光度計 UH4150」)を用いて測定し、さらに屈折率測定データを用いて各波長における反射率による透過率への寄与を取り除いて補正し、10mm厚の透過率に換算した値である。h,g,F',F,e,d,C',C,r,t線の10輝線のVブロック法における屈折率データから以下の分散曲線方程式を用いて最小二乗法によるフィッティングを行った。
各サンプルの内部透過率は、4~9mm厚の平行研磨品の波長300~700nmにおける透過率を分光光度計(日立ハイテクサイエンス社製;「紫外可視赤外分光光度計 UH4150」)を用いて測定し、さらに屈折率測定データを用いて各波長における反射率による透過率への寄与を取り除いて補正し、10mm厚の透過率に換算した値である。h,g,F',F,e,d,C',C,r,t線の10輝線のVブロック法における屈折率データから以下の分散曲線方程式を用いて最小二乗法によるフィッティングを行った。
分散曲線方程式により算出した各波長λにおける屈折率値nλを用いて各波長の表面反射率Rと、入射光の表面および裏面における多重反射を考慮して算出される内部における光の吸収がないものと仮定したときの透過率Tthを次式により算出した。厚みtmmにおける外部透過率測定値TexpとTthを用いて内部透過率T(tmm)を算出した。
以上により算出した厚みtmmにおける内部透過率T(tmm)を用いて10mm厚の透過率値T(10mm)は次式を用いて算出した。
各表に、各実施例及び各比較例の組成及びその物性値をそれぞれ示す。なお、特に断りがない限り、各成分の含有率はカチオンのモル%基準である。また、各物性値は、プレスを施していない状態のガラスについての値である。
以上より、各実施例の光学ガラスは、高屈折率、高透過率、低比重及び耐失透安定性を高いレベルで兼ね備え、更に浮遊熔解法で製造した場合に直径10mm以上に大型化できることが確認された。
1・・・撮像装置、101・・・カメラボディ、102・・・レンズ鏡筒、103・・・レンズ、104・・・センサチップ、105・・・ガラス基板、106・・・マルチチップモジュール、CAM・・・撮像装置(レンズ非交換式カメラ)、WL・・・撮影レンズ、M1・・・液晶モニタ、EF・・・補助光発光部、B1・・・レリーズボタン、B2・・・ファンクションボタン、2・・・多光子顕微鏡、201・・・パルスレーザ装置、202・・・パルス分割装置、203・・・ビーム調整部、204,205,212・・・ダイクロイックミラー、206・・・対物レンズ、207,211,213・・・蛍光検出部、208・・・集光レンズ、209・・・ピンホール、210・・・結像レンズ、S・・・試料、3・・・接合レンズ、301・・・第1のレンズ要素、302・・・第2のレンズ要素、303・・・接合部材、4・・・ガス浮遊炉、401・・・ステージ、402・・・台座、403・・・レーザ光源、404,405・・・ミラー、406・・・放射温度計、407・・・コンピュータ、408・・・CCDカメラ、409・・・モニタ、410・・・ガス流量調節器、L・・・レーザ光、M・・・原料
Claims (24)
- カチオンのモル%表示で、
La3+含有率:5~35%、
Si4+含有率:5~25%、
Nb5+含有率:5~35%、
Al3+含有率:5~35%、
Ti4+、Zr4+、Nb5+、Ta5+及びAl3+の総含有率(Ti4++Zr4++Nb5++Ta5++Al3+):45~80%、である、光学ガラス。 - カチオンのモル%表示で、Ti4+含有率:0~20%である、請求項1に記載の光学ガラス。
- カチオンのモル%表示で、
La3+含有率:5~35%、
Si4+含有率:5~25%、
Nb5+含有率:5~35%、
Ti4+含有率:0~20%、
Ti4+、Zr4+、Nb5+、Ta5+及びAl3+の総含有率(Ti4++Zr4++Nb5++Ta5++Al3+):45~80%、である、光学ガラス。 - カチオンのモル%表示で、Zr4+含有率:0~15%である、請求項1~3のいずれか一項に記載の光学ガラス。
- カチオンのモル%で、Ta5+含有率:0~15%である、請求項1~4のいずれか一項に記載の光学ガラス。
- カチオンのモル%表示で、
Y3+含有率:0~15%、である、請求項1~5のいずれか一項に記載の光学ガラス。 - B3+を実質的に含有しない、請求項1~6のいずれか一項に記載の光学ガラス。
- 前記光学ガラスの10mmあたりの内部透過率が80%となる波長(λ80)が420nm以下である、請求項1~7のいずれか一項に記載の光学ガラス。
- 前記光学ガラスのd線に対する屈折率が、1.95~2.15である、請求項1~8のいずれか一項に記載の光学ガラス。
- 前記光学ガラスのアッベ数が、20~35である、請求項1~9のいずれか一項に記載の光学ガラス。
- 前記光学ガラスの部分分散比(Pg,F)が、以下の式
-0.00403×νd+0.704<Pg,F<-0.00403×νd+0.717・・・(1)
を満たす請求項1~10のいずれか一項に記載の光学ガラス。 - 前記光学ガラスの比重(Sg)が、4.6~5.6である、請求項1~11のいずれか一項に記載の光学ガラス。
- 前記光学ガラスのガラス転移温度(Tg)と結晶化開始温度(Tx)の温度差(ΔT=Tx-Tg)が、80~200℃である、請求項1~12のいずれか一項に記載の光学ガラス。
- 前記光学ガラスの長軸方向の長さが10mm以上である、請求項1~13のいずれか一項に記載の光学ガラス。
- 請求項1~14のいずれか一項に記載の光学ガラスを用いた光学素子。
- 請求項15に記載の光学素子を含む、光学系。
- 請求項16に記載の光学系を含む、顕微鏡用対物レンズ。
- 請求項16に記載の光学系を含む、カメラ用交換レンズ。
- 請求項16に記載の光学系を含む、光学装置。
- 第1のレンズ要素と第2のレンズ要素とを有し、
前記第1のレンズ要素と前記第2のレンズ要素の少なくとも1つは、請求項1~14のいずれか一項に記載の光学ガラスである、接合レンズ。 - 請求項20に記載の接合レンズを含む、光学系。
- 請求項21に記載の光学系を含む、顕微鏡用対物レンズ。
- 請求項21に記載の光学系を含む、カメラ用交換レンズ。
- 請求項21に記載の光学系を含む、光学装置。