WO2024019707A1 - Cellules photovoltaïques - Google Patents

Cellules photovoltaïques Download PDF

Info

Publication number
WO2024019707A1
WO2024019707A1 PCT/US2022/037595 US2022037595W WO2024019707A1 WO 2024019707 A1 WO2024019707 A1 WO 2024019707A1 US 2022037595 W US2022037595 W US 2022037595W WO 2024019707 A1 WO2024019707 A1 WO 2024019707A1
Authority
WO
WIPO (PCT)
Prior art keywords
examples
ink composition
liquid
photovoltaic
hole transport
Prior art date
Application number
PCT/US2022/037595
Other languages
English (en)
Inventor
Israel Patla
Faina KOGAN
Anna RAZGON
Itay EYAL
Mark Sandler
Yaron Grinwald
Original Assignee
Hewlett-Packard Development Company, L.P.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hewlett-Packard Development Company, L.P. filed Critical Hewlett-Packard Development Company, L.P.
Priority to PCT/US2022/037595 priority Critical patent/WO2024019707A1/fr
Publication of WO2024019707A1 publication Critical patent/WO2024019707A1/fr

Abstract

L'invention concerne une composition d'encre électrophotographique liquide (LEP) de transport de trous comprenant : un matériau capable de transporter des trous d'électrons ; une résine thermoplastique comprenant un copolymère d'un monomère d'alkylène et un monomère éthyléniquement insaturé comprenant un époxyde ; et un support liquide. L'invention concerne également un ensemble d'encres comprenant la composition d'encre LEP de transport de trous et une composition d'encre photovoltaïque LEP, ainsi qu'un procédé de production de cellules photovoltaïques faisant appel à la composition d'encre LEP de transport de trous et des cellules photovoltaïques produites à partir de celle-ci.
PCT/US2022/037595 2022-07-19 2022-07-19 Cellules photovoltaïques WO2024019707A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/US2022/037595 WO2024019707A1 (fr) 2022-07-19 2022-07-19 Cellules photovoltaïques

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2022/037595 WO2024019707A1 (fr) 2022-07-19 2022-07-19 Cellules photovoltaïques

Publications (1)

Publication Number Publication Date
WO2024019707A1 true WO2024019707A1 (fr) 2024-01-25

Family

ID=82850238

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2022/037595 WO2024019707A1 (fr) 2022-07-19 2022-07-19 Cellules photovoltaïques

Country Status (1)

Country Link
WO (1) WO2024019707A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019143338A1 (fr) * 2018-01-18 2019-07-25 Hewlett-Packard Development Company, L.P. Compositions d'encre active électrophotographique
WO2021096567A1 (fr) * 2019-11-15 2021-05-20 Hewlett-Packard Development Company, L.P. Compositions d'encre électrophotographique liquide

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019143338A1 (fr) * 2018-01-18 2019-07-25 Hewlett-Packard Development Company, L.P. Compositions d'encre active électrophotographique
WO2021096567A1 (fr) * 2019-11-15 2021-05-20 Hewlett-Packard Development Company, L.P. Compositions d'encre électrophotographique liquide

Similar Documents

Publication Publication Date Title
US9899124B2 (en) Electrostatic ink compositions
EP2875080A1 (fr) Particules de pigments métalliques à revêtement polymère, leur procédé de fabrication et encres électrostatiques
US20240053690A1 (en) Liquid electrophotographic ink compositions
WO2013044991A1 (fr) Composition d'encre electrostatique
US10114305B2 (en) Liquid toner containing a low symmetry electrically conducting material for printing conductive traces
US9745488B2 (en) Electrostatic inks and method for their production
EP3394678B1 (fr) Compositions d'encre électrostatique
WO2024019707A1 (fr) Cellules photovoltaïques
US11810731B2 (en) Photovoltaic cells
US11810729B2 (en) Photovoltaic cells
US20170205724A1 (en) Electrostatic ink compositions
US20230125335A1 (en) Light emitting electrochemical cells, electrostatic inks and methods of making electrostatic inks
US11696378B2 (en) Electroluminescent cells
EP3580282B1 (fr) Encre(s) électrostatique(s)

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22753882

Country of ref document: EP

Kind code of ref document: A1