WO2023223724A1 - 高炉操業方法 - Google Patents
高炉操業方法 Download PDFInfo
- Publication number
- WO2023223724A1 WO2023223724A1 PCT/JP2023/014825 JP2023014825W WO2023223724A1 WO 2023223724 A1 WO2023223724 A1 WO 2023223724A1 JP 2023014825 W JP2023014825 W JP 2023014825W WO 2023223724 A1 WO2023223724 A1 WO 2023223724A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- hole
- furnace
- blast furnace
- normal operation
- molten material
- Prior art date
Abstract
カーボンレンガを損傷させることなく、休風前に従来よりも炉内に残留する溶融物を少なくできる高炉操業方法を提案する。休風した後に再立ち上げする高炉操業方法であって、高炉炉底部の炉内壁は、貫通口7が開孔される部位にある出銑口2を閉塞するマッド材3と、その他の部位に内張りされているカーボンレンガ4と、を有し、休風前の減尺操業時に、出銑口のマッド材が設けられている部位において、貫通口を、その貫通口の炉内壁面側の開孔下端7aが通常操業時の貫通口の炉内壁面側の開孔下端よりも下方の位置になるように開孔して、貫通口を通じて溶融物6を排出させる。
Description
本発明は、操業を停止して高炉を休風し、その後再度立ち上げを行う高炉操業方法に関する。
高炉は、溶銑の減産を強いられた場合低送風流量となる事で、炉芯不活性化に伴う炉況不調を招く恐れがある。溶銑の減産により出銑比1.5を下回る場合には、400kg/tを超えるコークス比で操業を継続する事になるが、コークスは高価な原料であるため経済的に合理的ではない。また、高炉の生産下方弾力性には限りがあるので、大幅な減産が強いられると高炉休止が必要となることもある。その他にも、老朽化した高炉の付帯設備を改修するために、炉内溶銑滓が凝固する規模の休風を実施することもある。このような事態に対応するため、高炉を長期間休風するバンキングと呼ばれる技術がある。
バンキングを実施する場合、羽口レベルまで原料ラインを減尺し、送風準備として炉内の残留コークスや残銑滓が常温になるまで冷却(3カ月)後、炉内に重機を投入し残留コークスの掻き出し及びコークス・枕木敷き詰め作業(2.5カ月)が必要になるので、少なくとも停止期間5.5カ月間を要する。そのため、急激な需要回復や工事期間律速の中間改修が出来ず、需要動向に応じた生産調整をする事が出来ない。
停止期間を短縮する技術として、特許文献1には、吹き卸し時に通常出銑口より下方の炉壁部に設けた炉底出銑口から炉底出銑することで、炉底部の溶銑を取り出す方法が開示されている。また、特許文献2には、吹き卸された高炉の炉下部壁に開口を設け、炉底全面に残存している炉底内容物を炉外に搬出する方法が開示されている。
しかしながら、特許文献1、2に開示された技術は、出銑口より下部に炉底出銑口や開口部を設けるので、炉底レンガであるカーボンレンガを損傷させるという問題があった。
本発明の目的は、このような課題を解消するために、カーボンレンガを損傷させることなく、休風前に従来よりも炉内に残留する溶融物を少なくできる高炉操業方法を提案することにある。
本発明の高炉操業方法は、前述の課題を解決すべく開発されたものであり、休風した後に再立ち上げする高炉操業方法であって、高炉炉底部の炉内壁は、貫通口が開孔される部位にある出銑口を閉塞するマッド材と、その他の部位に内張りされているカーボンレンガと、を有し、休風前の減尺操業時に、前記出銑口のマッド材が設けられている部位において、前記貫通口を、その貫通口の炉内壁面側の開孔下端が通常操業時の貫通口の炉内壁面側の開孔下端よりも下方の位置になるように開孔して、前記貫通口を通じて溶融物を排出させる、高炉操業方法である。
なお、本発明の高炉操業方法においては、
(1)前記高炉の炉低部の周方向に複数の出銑口が設けられ、休風前の減尺操業時に、通常操業時にマッド材で閉塞された貫通口を、順次、その貫通口の炉内壁面側の開孔下端が通常操業時の貫通口の炉内壁面側の開孔下端よりも下方の位置になるように開孔すること、
(2)前記貫通口の炉内壁面側の開孔下端が、前記マッド材が設けられている出銑口の炉内壁面側の下端に位置するように、前記貫通口を開孔すること、
(3)前記貫通口の傾斜角度を、通常操業時の貫通口の傾斜角度よりも大きくすること、
(4)前記貫通口より溶融物を排出させるため、羽口からの送風圧を150~250kPaとすること、
(5)前記休風前の貫通口を通じての溶融物の排出後、マッド材を用いて前記貫通口を閉塞させて休風し、再立ち上げの際には通常操業時の位置になるように貫通口を開孔し、前記貫通口から炉内溶融物を排出させることで立上げ時の溶融物の温度低下を抑制すること、
がより好ましい解決手段となるものと考えられる。
(1)前記高炉の炉低部の周方向に複数の出銑口が設けられ、休風前の減尺操業時に、通常操業時にマッド材で閉塞された貫通口を、順次、その貫通口の炉内壁面側の開孔下端が通常操業時の貫通口の炉内壁面側の開孔下端よりも下方の位置になるように開孔すること、
(2)前記貫通口の炉内壁面側の開孔下端が、前記マッド材が設けられている出銑口の炉内壁面側の下端に位置するように、前記貫通口を開孔すること、
(3)前記貫通口の傾斜角度を、通常操業時の貫通口の傾斜角度よりも大きくすること、
(4)前記貫通口より溶融物を排出させるため、羽口からの送風圧を150~250kPaとすること、
(5)前記休風前の貫通口を通じての溶融物の排出後、マッド材を用いて前記貫通口を閉塞させて休風し、再立ち上げの際には通常操業時の位置になるように貫通口を開孔し、前記貫通口から炉内溶融物を排出させることで立上げ時の溶融物の温度低下を抑制すること、
がより好ましい解決手段となるものと考えられる。
本発明の高炉操業方法によれば、炉底レンガを損傷させることなく、休風後に炉内に残留する凝固した溶融物を少なくできる。これにより、再立ち上げ時に得られる溶融物の温度低下を抑制でき、よりスムーズな高炉の再立ち上げが実現できる。
以下、本発明の実施の形態について具体的に説明する。なお、以下の実施形態は、本発明の技術的思想を具体化するための装置や方法を例示するものであり、構成を下記のものに特定するものでない。すなわち、本発明の技術的思想は、特許請求の範囲に記載された技術的範囲内において、種々の変更を加えることができる。また、以下の実施形態では、本発明の対象となる高炉操業方法の一例を説明した後、本発明の高炉操業方法の特徴について説明する。
<本発明の対象となる高炉の通常操業の一実施形態について>
図1(a)、(b)は、それぞれ、高炉の通常操業における出銑口の状態を示す断面模式図である。図1(a)、(b)は高炉1の炉底部の一部を示しており、高炉炉底部の炉内壁は、貫通口7が開孔される部位にある出銑口2を閉塞するマッド材3と、その他の部位に内張りされているカーボンレンガ4と、から構成されている。なお、5は羽口である。
図1(a)、(b)は、それぞれ、高炉の通常操業における出銑口の状態を示す断面模式図である。図1(a)、(b)は高炉1の炉底部の一部を示しており、高炉炉底部の炉内壁は、貫通口7が開孔される部位にある出銑口2を閉塞するマッド材3と、その他の部位に内張りされているカーボンレンガ4と、から構成されている。なお、5は羽口である。
高炉1には、通常、複数個所例えば4個所の出銑口2が備えられており、これらの出銑口2を交互に使用して高炉の通常操業が行われる。具体的には、一つの出銑口2に着目すると、図1(a)に示すように、炉内の溶融物6の出銑を行う出銑口2では、出銑口2を閉塞しているマッド材3に貫通口7を炉外から炉内まで貫通させて設けることで、貫通口7を通じて炉内の溶融物6を出銑する。そして、図1(b)に示すように、炉内の溶融物6の出銑を行わない出銑口2はマッド材3により閉塞され、炉内の溶融物6がその出銑口2から炉外に排出されないよう構成される。そして、炉内の溶融物6の出銑が完了した後は、再び出銑口2をマッド材3により閉塞する。以上の操作を連続的に行うことで、高炉の通常操業が行われている。なお、8は出銑した炉内の溶融物6を炉外に搬送する出銑樋である。
<本発明に係る高炉操業方法の一実施形態について>
高炉1の減産や補修対応のために長期間の休風(以下、バンキングとも記載する)を実施する場合においては、減尺操業を実施して、例えば、羽口5のレベルまで原料(溶融物6)のラインを減尺する。本実施形態に係る高炉操業では、休風前の減尺操業時に、出銑口2のマッド材3が設けられている部位において、貫通口7を、その貫通口7の炉内壁面側の開孔下端7a(図2(a))が、通常操業時の出銑口2の炉内壁面側の開孔下端7a(図2(b))よりも下方の位置になるように開孔して、貫通口7を通じて溶融物6を排出させる。
高炉1の減産や補修対応のために長期間の休風(以下、バンキングとも記載する)を実施する場合においては、減尺操業を実施して、例えば、羽口5のレベルまで原料(溶融物6)のラインを減尺する。本実施形態に係る高炉操業では、休風前の減尺操業時に、出銑口2のマッド材3が設けられている部位において、貫通口7を、その貫通口7の炉内壁面側の開孔下端7a(図2(a))が、通常操業時の出銑口2の炉内壁面側の開孔下端7a(図2(b))よりも下方の位置になるように開孔して、貫通口7を通じて溶融物6を排出させる。
図3は、本発明に係る高炉操業方法における減尺終了直前の状態を説明するための断面模式図である。図3に示すように、炉内に残留した溶融物6(スラグ6aと溶銑6b)は、バンキング時に凝固して凝固した溶融物となる。このような凝固した溶融物は、再送風時において製造される溶銑の熱を奪い溶融物の温度を低下させ、溶融物の流動性を低下させるので、スムーズな立ち上げを阻害する。これに対し、本発明に係る高炉操業方法の実施によりバンキング後に炉内に残留する凝固した溶融物を少なくできれば、高炉の再立ち上げ時に得られる溶融物の温度低下を抑制でき、スムーズな高炉の再立ち上げが実現できる。
図4は、本発明に係る高炉操業方法における出銑口の開孔方法を説明するための断面模式図である。図4に示す例において、実線は、通常操業時の出銑の場合において、開孔機11のロッドを出銑口2のマッド材3の中心に向け貫通口7を開孔する方法を示している。また、破線および一点鎖線は、それぞれ、本発明に係る高炉操業方法の休風前の減尺操業時において、開孔機11のロッドを出銑口2のマッド材3に対し、通常操業時の貫通口7よりも貫通口7が下方の位置になるように貫通口7を開孔する方法を示している。ここで、破線の例は、減尺操業時における開孔を行う際、出銑口2を形成するカーボンレンガ4がほとんど損耗していない状態を示す。また、一点鎖線の例は、減尺操業時における開孔を行う際、出銑口2を形成するカーボンレンガ4が損耗している状態を示す。通常、火入れから減尺操業まで、カーボンレンガ4は約0.1°/年損耗する。そのため、火入れからの年数に応じて、一点鎖線で示した例のように、開孔機11のロッドによる開孔する貫通口7の角度を高くしてもカーボンレンガ4を損傷させることなく、炉内溶融物取り出しの最大効果を得ることができる。
一例として、実線の通常操業時の出銑の場合では、出銑口2のマッド材3に対し貫通口7の角度を10°として開孔機11のロッドで開孔する。また、破線の減尺操業の場合では、出銑口2のマッド材3に対し貫通口7の角度を13.8°として開孔機11のロッドで開孔する。さらに、一点鎖線の減尺操業の場合では、出銑口2のマッド材3に対し貫通口7の角度を15°として開孔機11のロッドで開孔する。
図4に示す破線または一点鎖線の例のように、出銑口2のマッド材3に対する貫通口7の傾斜角度を通常操業時の貫通口7よりも高くすれば、炉内壁面側の貫通口7の下端7aは、通常操業時の貫通口7の下端7aよりも下方にすることができる。このように、炉内壁面側の貫通口7の下端位置7aが通常操業時の貫通口7の下端7aよりも下方にするには、開孔機11の開孔角度を従来よりも高くすることが好ましい。開孔機11の高さを変えることは困難であるので、開孔機11の傾斜角度を変えるだけで対応できれば、容易に炉内壁面側の貫通口の下端を下げることができる。
下記表1に、貫通口7の傾斜角度を変えた場合における、溶融物6の液面レベル、液面降下、減少する溶融物の体積及び減量する溶融物の質量を示す。ここで、貫通口角度10°は、通常操業時の貫通口7の傾斜角度を示す。また、貫通口角度13.8°および15°は、貫通口7の下端7aが、マッド材3が設けられる出銑口2の炉内側下端となる傾斜角度である。貫通口角度13.8°および15°の場合の溶融物低減効果は、貫通口角度10°の通常操業時の場合を0として、それに対する溶融物の低減量として求めた。
表1に示すように、貫通口7の角度を高くして貫通口7の下端位置7aを下げるに従い溶融物の液面レベルは下がり、炉内に残留する溶融物6の体積および質量は減少する。また、貫通口7の下端位置7aの下限はマッド材3が設けられている出銑口2の炉内側下端である。このことから、貫通口7の下端位置7aが、マッド材3が設けられている出銑口2の炉内側下端位置となるように貫通口7を設けることが好ましく、これにより、カーボンレンガ4を破損させない範囲では、炉内に残留する溶融物6を最小にできる。この結果、高炉の再立ち上げ時に得られる溶融物6の温度低下をさらに抑制でき、よりスムーズな高炉の再立ち上げが実現できる。なお、本実施形態では、本発明の高炉操業方法において、減尺操業時の貫通口7の角度を13.8°~15°とすることが好ましいことがわかる。
また、減尺前の高炉羽口5からの送風圧は、150~250kPaであることが好ましい。炉内側の溶融物6のレベルは炉外側の貫通口7の位置よりも低いため、高い炉内の圧力(送風圧力)と大気圧との圧力差によって、炉内の溶融物6が貫通口7を介して排出される。このため、高炉羽口5からの送風圧を150kPa以上として炉内圧力を高め、上記圧力差を大きくすることが好ましい。これにより、さらに多くの溶融物6が貫通口7を介して排出できるようになる。一方、送風圧を高め過ぎると送風流量が多くなり、生成される溶融物量が増加するので好ましくない。したがって、高炉羽口5からの送風圧は250kPa以下であることが好ましい。
溶融物6を排出した後においては、マッド材3を用いて貫通口7を閉塞させてバンキングを実施する。その後、高炉を再立ち上げする際には、通常操業時の貫通口位置になるように出銑口2のマッド材3を開孔して貫通口7を形成し、当該貫通口7から炉内溶融物を排出させることが好ましい。このように、減尺操業時の貫通口位置を再立ち上げの際の貫通口位置よりも下げることで、再立ち上げの際に貫通口前に凝固した溶融物が存在しない排出空間を確保できる。これにより、再立ち上げの際の溶融物の温度低下がさらに抑制されるので、さらにスムーズな高炉の再立ち上げが実現できる。
なお、上述した説明では1つの出銑口2に着目したが、高炉は、基本的に4本の出銑口を有する。また、基本的には使用される出銑口は4本のうち2本か、または、多いケースでも3本である。複数の出銑口の開孔は、例えば、以下のような順番で行うことができる。
まず初めに1つの出銑口を開孔したら、次にその対角にある出銑口を開孔する。出銑口を3本使用する場合は、開孔した2つの出銑口の間の出銑口を開孔する。出銑口の開孔は、例えば上記のような順番で順次開孔しても良いし、それ以外の順番でも良く、開孔の順番は特に限定されない。例えば、樋補修の兼ね合いを考慮して開孔の順番を決めても良い。
また、出銑口の開孔の時間間隔は特に限定されず、その時の炉況や風量によって決定される。そのため、開孔の時間間隔は、5分、10分、1時間等、さまざまなバリエーションがあり、特に限定されない。
本発明に係る高炉操業方法によれば、高炉の再稼働だけでなく、高炉以外の様々の竪型溶解炉においても、安定した操業方法を提供できる。
1 高炉
2 出銑口
3 マッド材
4 カーボンレンガ
5 羽口
6 溶融物
6a スラグ
6b 溶銑
7 貫通口
7a 下端
8 出銑樋
11 開孔機
2 出銑口
3 マッド材
4 カーボンレンガ
5 羽口
6 溶融物
6a スラグ
6b 溶銑
7 貫通口
7a 下端
8 出銑樋
11 開孔機
Claims (6)
- 休風した後に再立ち上げする高炉操業方法であって、
高炉炉底部の炉内壁は、貫通口が開孔される部位にある出銑口を閉塞するマッド材と、その他の部位に内張りされているカーボンレンガと、を有し、
休風前の減尺操業時に、前記出銑口のマッド材が設けられている部位において、前記貫通口を、その貫通口の炉内壁面側の開孔下端が通常操業時の貫通口の炉内壁面側の開孔下端よりも下方の位置になるように開孔して、前記貫通口を通じて溶融物を排出させる、高炉操業方法。 - 前記高炉の炉低部の周方向に複数の出銑口が設けられ、休風前の減尺操業時に、通常操業時にマッド材で閉塞された貫通口を、順次、その貫通口の炉内壁面側の開孔下端が通常操業時の貫通口の炉内壁面側の開孔下端よりも下方の位置になるように開孔する、請求項1に記載の高炉操業方法。
- 前記貫通口の炉内壁面側の開孔下端が、前記マッド材が設けられている出銑口の炉内壁面側の下端に位置するように、前記貫通口を開孔する、請求項1または2に記載の高炉操業方法。
- 前記貫通口の傾斜角度を、通常操業時の貫通口の傾斜角度よりも大きくする、請求項1または2に記載の高炉操業方法。
- 前記貫通口より溶融物を排出させるため、羽口からの送風圧を150~250kPaとする、請求項1または2に記載の高炉操業方法。
- 前記休風前の貫通口を通じての溶融物の排出後、マッド材を用いて前記貫通口を閉塞させて休風し、再立ち上げの際には通常操業時の位置になるように貫通口を開孔し、前記貫通口から炉内溶融物を排出させることで立上げ時の溶融物の温度低下を抑制する、請求項1または2に記載の高炉操業方法。