WO2023163112A1 - 香味吸引物品用シート - Google Patents
香味吸引物品用シート Download PDFInfo
- Publication number
- WO2023163112A1 WO2023163112A1 PCT/JP2023/006765 JP2023006765W WO2023163112A1 WO 2023163112 A1 WO2023163112 A1 WO 2023163112A1 JP 2023006765 W JP2023006765 W JP 2023006765W WO 2023163112 A1 WO2023163112 A1 WO 2023163112A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- flavor
- sheet
- articles
- filter
- inhaling
- Prior art date
Abstract
(A)20g/m2以上の吸着剤粒子と、(B)パルプと、(C)ポリエステル繊維と、を含む香味吸引物品用シート。
Description
本発明は、香味吸引物品用シートに関する。
従来の燃焼型喫煙物品においては、好ましくない香喫味を与える成分を除去するためにアセテートフィルタ内に活性炭を充填することが知られている。例えば特許文献1には、活性炭含有紙の表面に活性炭を外添し、さらにこの紙を折り込んでラッパー内に充填してなるチャコールフィルターが開示されている。
特許文献1に開示された発明は、紙に抄き込める活性炭の量が過大となると紙が脆くなるためその量に制約があるが、活性炭を内添かつ外添することで活性炭の総量を多くするということを要点とする。しかし、活性炭を外添するためには、紙にクレープ処理等の処理を施す必要がある。当該処理はフィルタとしたときの通気抵抗を上昇させる。そこで発明者らは、シートを脆くすることなく内添する活性炭の量を増加させることができれば、理想的な香味吸引物品用シートが得られるとの着想を得た。かかる事情に鑑み、本発明は、吸着特性と取扱性に優れた香味吸引物品用シートを提供することを課題とする。
発明者らは、特定の繊維を用いること吸着剤粒子の含有量を増加させることができることに着眼し、本発明を完成した。すなわち、前記課題は以下の発明によって解決される。
態様1
(A)20g/m2以上の吸着剤粒子と、
(B)パルプと、
(C)ポリエステル繊維と、
を含む香味吸引物品用シート。
態様2
前記(A)吸着剤粒子が活性炭を含む、態様1に記載のシート。
態様3
前記(C)が、ジオール残基として、炭素鎖が2~4のアルキレングリコール残基を含み、かつ二酸残基としてテレフタル酸、イソフタル酸、またはフタル酸残基を含む、態様1または2に記載のシート。
態様4
前記(C)のポリエステルが、ジオール残基として、エチレングリコール残基を含み、かつ二酸残基としてテレフタル酸残基を含む、態様3に記載のシート。
態様5
バインダーをさらに含む、態様1~4のいずれかに記載のシート。
態様6
5N/15mm以上の引張強度を有する、態様1~5のいずれかに記載のシート。
態様7
態様1~6のいずれかに記載のシートを含んで構成される、巻包材。
態様8
態様1~6のいずれかに記載のシートを備える、香味吸引物品用部材。
態様9
先端部材、香味源を含む香味発生部材、支持部材、冷却部材、およびこれらの組合せからなる群より選択される、態様8に記載の香味吸引物品用部材。
態様10
態様1~6のいずれかに記載のシート、
態様7に記載の巻包材、または
態様8または9に記載の香味吸引物品用部材を備える、
香味吸引物品。
態様1
(A)20g/m2以上の吸着剤粒子と、
(B)パルプと、
(C)ポリエステル繊維と、
を含む香味吸引物品用シート。
態様2
前記(A)吸着剤粒子が活性炭を含む、態様1に記載のシート。
態様3
前記(C)が、ジオール残基として、炭素鎖が2~4のアルキレングリコール残基を含み、かつ二酸残基としてテレフタル酸、イソフタル酸、またはフタル酸残基を含む、態様1または2に記載のシート。
態様4
前記(C)のポリエステルが、ジオール残基として、エチレングリコール残基を含み、かつ二酸残基としてテレフタル酸残基を含む、態様3に記載のシート。
態様5
バインダーをさらに含む、態様1~4のいずれかに記載のシート。
態様6
5N/15mm以上の引張強度を有する、態様1~5のいずれかに記載のシート。
態様7
態様1~6のいずれかに記載のシートを含んで構成される、巻包材。
態様8
態様1~6のいずれかに記載のシートを備える、香味吸引物品用部材。
態様9
先端部材、香味源を含む香味発生部材、支持部材、冷却部材、およびこれらの組合せからなる群より選択される、態様8に記載の香味吸引物品用部材。
態様10
態様1~6のいずれかに記載のシート、
態様7に記載の巻包材、または
態様8または9に記載の香味吸引物品用部材を備える、
香味吸引物品。
本発明によって吸着特性と取扱性に優れた香味吸引物品用シートを提供できる。
本開示において「X~Y」はその端値であるXおよびYを含む。
1.香味吸引物品用シート
本実施態様にかかる香味吸引物品用シートは、(A)吸着剤粒子と、(B)パルプと、(C)ポリエステル繊維と、を含む。
本実施態様にかかる香味吸引物品用シートは、(A)吸着剤粒子と、(B)パルプと、(C)ポリエステル繊維と、を含む。
(1)(A)吸着剤粒子
吸着剤とは、一態様において香味吸引物品から発生したエアロゾル中の成分を吸着できる剤である。吸着剤としては、例えば、活性炭、ゼオライト、活性アルミナ、およびシリカゲル等が挙げられる。中でも、入手容易性等の観点から、吸着剤は活性炭を含むことが好ましく、活性炭からなることがより好ましい。
吸着剤とは、一態様において香味吸引物品から発生したエアロゾル中の成分を吸着できる剤である。吸着剤としては、例えば、活性炭、ゼオライト、活性アルミナ、およびシリカゲル等が挙げられる。中でも、入手容易性等の観点から、吸着剤は活性炭を含むことが好ましく、活性炭からなることがより好ましい。
吸着剤粒子の粒径は限定されないが、その平均粒子径は好ましくは5~150μm、より好ましくは10~100μmである。平均粒子径は画像式粒度分布測定によって測定される。
前記シート中における吸着剤粒子の量はシート単位面積当たりの量で表され、その量が過度に少ないと満足の行く吸着効果が得られない。かかる観点から、当該量は20g/m2以上である。その下限値は、好ましくは40g/m2以上である。また、シートの取扱性の観点から、その上限は、好ましくは80g/m2以下あり、より好ましくは60g/m2以下ある。前述のとおり、吸着剤は好ましくは活性炭である。
活性炭の表面積は、好ましくは500~3000m2/g、より好ましくは700~2500m2/gである。吸着剤の表面積はBET比表面積であり、窒素吸着法によって測定される。
(2)(B)パルプ
パルプとは植物原料を機械的または化学的に処理して抽出したセルロース繊維の集合体である。植物原料は木材であることが好ましい。
パルプとは植物原料を機械的または化学的に処理して抽出したセルロース繊維の集合体である。植物原料は木材であることが好ましい。
(3)(C)ポリエステル繊維
ポリエステル繊維を構成するポリエステルは、ジオール残基と二酸残基を含む。ジオール残基は、炭素鎖が2~4のアルキレングリコール残基を含むことが好ましく、エチレングリコール残基を含むことがより好ましい。二酸残基はテレフタル酸、イソフタル酸、またはフタル酸残基を含むことが好ましく、テレフタル酸残基を有することがより好ましい。このようなポリエステルは、下記式で表すことができる。式中、nは繰り返し数を示し、mは2~4の整数を示す。特に、炭素鎖が2~4のアルキレングリコール残基、あるいはイソフタル酸またはフタル酸残基を含むポリエステルは、結晶化度が過度に高くならないため、ポリエステル繊維と吸着剤粒子との接着性を向上させる。
ポリエステル繊維を構成するポリエステルは、ジオール残基と二酸残基を含む。ジオール残基は、炭素鎖が2~4のアルキレングリコール残基を含むことが好ましく、エチレングリコール残基を含むことがより好ましい。二酸残基はテレフタル酸、イソフタル酸、またはフタル酸残基を含むことが好ましく、テレフタル酸残基を有することがより好ましい。このようなポリエステルは、下記式で表すことができる。式中、nは繰り返し数を示し、mは2~4の整数を示す。特に、炭素鎖が2~4のアルキレングリコール残基、あるいはイソフタル酸またはフタル酸残基を含むポリエステルは、結晶化度が過度に高くならないため、ポリエステル繊維と吸着剤粒子との接着性を向上させる。
(4)他の成分
香味吸引物品用シートは、バインダーを含むことが好ましい。バインダーは、前記繊維同士の接着性を高め、かつ前記繊維と吸着剤との接着性を高める。バインダーとしては公知のもの使用でき、その例としてはポリビニルアルコールおよび酢酸ビニル等が挙げられる。
香味吸引物品用シートは、バインダーを含むことが好ましい。バインダーは、前記繊維同士の接着性を高め、かつ前記繊維と吸着剤との接着性を高める。バインダーとしては公知のもの使用でき、その例としてはポリビニルアルコールおよび酢酸ビニル等が挙げられる。
(5)物性
香味吸引物品用シートは、以下の特性を有することが好ましく、前記成分の配合量は当該特性を達成できるように適宜調整されてもよい。
引張強度(ISO 1924-2):5N/15mm以上、好ましくは5~30N/15mm、より好ましくは10~20N/15mm
坪量(ISO 536):50~100g/m2、より好ましくは70~90g/m2
厚み:100~300μm、より好ましくは150~250μm
ヨウ素吸着性能(JIS K 1474):300~2000mg/g、より好ましくは500~1500mg/g
通気度:0~30000CU、好ましくは0~10000CU、より好ましくは0~2000CU
香味吸引物品用シートは、以下の特性を有することが好ましく、前記成分の配合量は当該特性を達成できるように適宜調整されてもよい。
引張強度(ISO 1924-2):5N/15mm以上、好ましくは5~30N/15mm、より好ましくは10~20N/15mm
坪量(ISO 536):50~100g/m2、より好ましくは70~90g/m2
厚み:100~300μm、より好ましくは150~250μm
ヨウ素吸着性能(JIS K 1474):300~2000mg/g、より好ましくは500~1500mg/g
通気度:0~30000CU、好ましくは0~10000CU、より好ましくは0~2000CU
通気度(単位:コレスタユニット(CU))は差圧1kPa条件下、1cm2当たり1分間での空気通過流量(cm3)である。通気度はCerulean社製通気度計PPM1000Mを用いて測定することができる。
香味吸引物品用シート1m2における吸着剤の有効表面積は、好ましくは5000~70,000m2/m2である。有効表面積とは、シート表面に露出している吸着剤の総面積である。この数値範囲は以下に基づく。
一態様において、吸着剤のシート内に埋没している面積は、平均すると、吸着剤1つの表面積の30%~50%と考えられる。すなわち、吸着剤の露出している面積は、平均して50%~70%である。吸着剤の表面積を1000m2/g、シート中の吸着剤の含有量を10g/m2とすると、平均して50%の面積が露出している場合の有効表面積は以下のように算出される。
10g/m2×1000m2/g×50%=5000m2/m2
吸着剤の表面積を2000m2/g、前記含有量を50g/m2とすると、平均して70%の面積が露出している場合の有効表面積は以下のように算出される。
50g/m2×2000m2/g×70%=70,000m2/m2
10g/m2×1000m2/g×50%=5000m2/m2
吸着剤の表面積を2000m2/g、前記含有量を50g/m2とすると、平均して70%の面積が露出している場合の有効表面積は以下のように算出される。
50g/m2×2000m2/g×70%=70,000m2/m2
(6)香味吸引物品用シートの表面処理
一態様において、香味吸引物品用シートには表面処理がなされていていない。また、別態様において香味吸引物品用シートには表面処理がなされている。表面処理としては公知の処理が挙げられるが、好ましくはクレープ処理である。クレープ処理とはシートに、ロール等の上でドクターを用いてちりめん状のしわを形成する処理をいう。クレープ深さは、好ましくは0.1~0.5μmである。
一態様において、香味吸引物品用シートには表面処理がなされていていない。また、別態様において香味吸引物品用シートには表面処理がなされている。表面処理としては公知の処理が挙げられるが、好ましくはクレープ処理である。クレープ処理とはシートに、ロール等の上でドクターを用いてちりめん状のしわを形成する処理をいう。クレープ深さは、好ましくは0.1~0.5μmである。
2.香味吸引物品用シートの製造方法
前述の成分を用いて公知の方法で香味吸引物品用シートを製造できる。例えば、前述の成分を混合したスラリーを調製し、これを抄紙することで抄紙シートを製造できる。当該スラリーを基材上にキャストすることによってキャストシートを製造できる。当該スラリーをローラーで圧展した後に乾燥することによってラミネートシートを製造できる。当該スラリーを押し出した後に乾燥することによって、押し出しシートを製造することもできる。
前述の成分を用いて公知の方法で香味吸引物品用シートを製造できる。例えば、前述の成分を混合したスラリーを調製し、これを抄紙することで抄紙シートを製造できる。当該スラリーを基材上にキャストすることによってキャストシートを製造できる。当該スラリーをローラーで圧展した後に乾燥することによってラミネートシートを製造できる。当該スラリーを押し出した後に乾燥することによって、押し出しシートを製造することもできる。
3.用途
(1)巻包材
香味吸引物品用シートは、香味吸引物品に用いられる巻包材として有用である。巻包材としては1つの部材を巻包するラッパー、および複数の部材を巻包するチップペーパー等が挙げられる。
(1)巻包材
香味吸引物品用シートは、香味吸引物品に用いられる巻包材として有用である。巻包材としては1つの部材を巻包するラッパー、および複数の部材を巻包するチップペーパー等が挙げられる。
(2)香味吸引物品用部材
香味吸引物品用シートは、香味吸引物品用部材として有用である。香味吸引物品用部材としては、先端部材、香味源を含む香味発生部材、支持部材、冷却部材、およびフィルタが挙げられる。
香味吸引物品用シートは、香味吸引物品用部材として有用である。香味吸引物品用部材としては、先端部材、香味源を含む香味発生部材、支持部材、冷却部材、およびフィルタが挙げられる。
1)先端部材
先端部材とは、香味吸引物品の吸口端とは反対の端部に配置される部材である。香味吸引物品用シートは先端部材の充填物またはラッパーとして使用できる。このような先端部材は、香味吸引物品を保存している間に、水分を除去しうる。例えば、ラッパーである香味吸引物品用シート内に、充填物である不織布またはセルロースアセテート繊維を充填する工程を備える製造方法で先端部材を製造できる。
先端部材とは、香味吸引物品の吸口端とは反対の端部に配置される部材である。香味吸引物品用シートは先端部材の充填物またはラッパーとして使用できる。このような先端部材は、香味吸引物品を保存している間に、水分を除去しうる。例えば、ラッパーである香味吸引物品用シート内に、充填物である不織布またはセルロースアセテート繊維を充填する工程を備える製造方法で先端部材を製造できる。
2)香味源を含む香味発生部材
香味源を含む香味発生部材とは、香味を発生する部材であり、例えばたばこ部材が挙げられる。香味吸引物品用シートは香味発生部材のラッパーとして使用できる。香味吸引物品用シートを含む香味発生部材は、香味吸引物品を保存している間に、水分を除去できるという効果を奏する。また、香味吸引物品用シートは香味発生部材の充填物の一部としても使用できる。このような香味発生部材は、香味吸引物品を保存している間または香味吸引中に、水分または好ましくない香味を与える成分を除去できる。例えば、ラッパーである香味吸引物品用シート内に、充填物であるたばこ材料を充填する工程を備える製造方法で香味源を含む香味発生部材を製造できる。あるいは、香味吸引物品用シートを裁刻して得たシート刻またはストランド刻をたばこ材料と混合して混合刻を得る工程、および当該混合刻をラッパー内に充填する工程を備える製造方法で香味源を含む香味発生部材を製造できる。
香味源を含む香味発生部材とは、香味を発生する部材であり、例えばたばこ部材が挙げられる。香味吸引物品用シートは香味発生部材のラッパーとして使用できる。香味吸引物品用シートを含む香味発生部材は、香味吸引物品を保存している間に、水分を除去できるという効果を奏する。また、香味吸引物品用シートは香味発生部材の充填物の一部としても使用できる。このような香味発生部材は、香味吸引物品を保存している間または香味吸引中に、水分または好ましくない香味を与える成分を除去できる。例えば、ラッパーである香味吸引物品用シート内に、充填物であるたばこ材料を充填する工程を備える製造方法で香味源を含む香味発生部材を製造できる。あるいは、香味吸引物品用シートを裁刻して得たシート刻またはストランド刻をたばこ材料と混合して混合刻を得る工程、および当該混合刻をラッパー内に充填する工程を備える製造方法で香味源を含む香味発生部材を製造できる。
3)支持部材
支持部材とは、香味吸引物品の強度を高めるための部材であり、例えばセンターホールフィルタが挙げられる。香味吸引物品用シートは当該センターホールフィルタを構成する材料として使用できる。このような支持部材は、香味吸引物品を保存している間または香味吸引中に、水分または好ましくない香味を与える成分を除去しうる。例えば、香味吸引物品用シートで中空管を形成し、これを充填物としてラッパーである香味吸引物品用シート内に充填する工程を備える製造方法で支持部材を製造できる。また中空の支持部材を長くすることで、後述する冷却部材を兼ねることもできる。
支持部材とは、香味吸引物品の強度を高めるための部材であり、例えばセンターホールフィルタが挙げられる。香味吸引物品用シートは当該センターホールフィルタを構成する材料として使用できる。このような支持部材は、香味吸引物品を保存している間または香味吸引中に、水分または好ましくない香味を与える成分を除去しうる。例えば、香味吸引物品用シートで中空管を形成し、これを充填物としてラッパーである香味吸引物品用シート内に充填する工程を備える製造方法で支持部材を製造できる。また中空の支持部材を長くすることで、後述する冷却部材を兼ねることもできる。
4)冷却部材
冷却部材とは加熱された香味を冷却する部材である。香味吸引物品用シートは冷却部材を構成する材料として有用である。このような冷却部材は、香味吸引物品を保存している間または香味吸引中に、水分または好ましくない香味を与える成分を除去しうる。例えば、香味吸引物品用シートで管を形成し、これを冷却部材とすることができる。必要に応じてベンチレーションを設けてもよい。また上述の通り、冷却部材は支持部材を兼ねることもできる。
冷却部材とは加熱された香味を冷却する部材である。香味吸引物品用シートは冷却部材を構成する材料として有用である。このような冷却部材は、香味吸引物品を保存している間または香味吸引中に、水分または好ましくない香味を与える成分を除去しうる。例えば、香味吸引物品用シートで管を形成し、これを冷却部材とすることができる。必要に応じてベンチレーションを設けてもよい。また上述の通り、冷却部材は支持部材を兼ねることもできる。
5)フィルタ
フィルタはエアロゾルが通過する際に、不要な成分を除去する。香味吸引物品用シートはフィルタ用シートとして特に有用である。当該フィルタは、香味吸引物品用シートを準備する工程1、および筒状のラッパーと、当該ラッパー内に配置された前記シートを備えるフィルタを準備する工程2と、を備える方法で製造されることが好ましい。
フィルタはエアロゾルが通過する際に、不要な成分を除去する。香味吸引物品用シートはフィルタ用シートとして特に有用である。当該フィルタは、香味吸引物品用シートを準備する工程1、および筒状のラッパーと、当該ラッパー内に配置された前記シートを備えるフィルタを準備する工程2と、を備える方法で製造されることが好ましい。
工程1は、前述のとおりである。工程2は、公知の方法で実施できる。例えば、筒状のラッパー内に、折り畳まれた香味吸引物品用シートを充填する、または裁断された香味吸引物品用シートを充填することでフィルタを製造できる。あるいは、香味吸引物品用シートを折り畳んで柱状に成形しこれをラッパーで巻装することでフィルタを製造できる。工程2の前に、香味吸引物品用シートに前記表面処理を施す工程を設けてもよい。
4.非燃焼加熱型香味吸引物品
香味吸引物品は、燃焼型香味吸引物品(シガレット)および非燃焼加熱型香味吸引物品に大別される。以下、非燃焼加熱型香味吸引物品を例にして説明する。図1は非燃焼加熱型香味吸引物品の一態様を示す。図中、10は非燃焼加熱型香味吸引物品、1はたばこ部材、3は冷却部材、5はマウスピース、51は第1フィルタ、52は第2フィルタ、Vはベンチレーションである。非燃焼加熱型香味吸引物品のサイズは限定されない。例えば、その長さは50~80mm、断面直径は5.5~7.5mm程度であってよい。前述のとおり、香味吸引物品用シートはフィルタ用シートとして特に有用であるので、第2フィルタが当該シートを含む態様を例にして、以下、説明する。
香味吸引物品は、燃焼型香味吸引物品(シガレット)および非燃焼加熱型香味吸引物品に大別される。以下、非燃焼加熱型香味吸引物品を例にして説明する。図1は非燃焼加熱型香味吸引物品の一態様を示す。図中、10は非燃焼加熱型香味吸引物品、1はたばこ部材、3は冷却部材、5はマウスピース、51は第1フィルタ、52は第2フィルタ、Vはベンチレーションである。非燃焼加熱型香味吸引物品のサイズは限定されない。例えば、その長さは50~80mm、断面直径は5.5~7.5mm程度であってよい。前述のとおり、香味吸引物品用シートはフィルタ用シートとして特に有用であるので、第2フィルタが当該シートを含む態様を例にして、以下、説明する。
(1)たばこ部材
たばこ部材とは、たばこ原料に含まれる香喫味成分を発生するための略円柱状の部材である。たばこ部材はたばこ材料とその周囲を巻装する巻紙(ラッパー)を備える。巻紙内に充填されるたばこ材料の形状は限定されず、例えばたばこシート、または当該たばこシートを幅0.8~1.2mmに裁刻したもの、あるいは幅0.8~1.2mmに裁刻された刻などが挙げられる。たばこシートは限定されず、公知の方法で製造できる。例えばたばこシートは、抄紙シート、スラリーを基材上にキャストして製造したキャストシート、スラリーをローラーで圧展した後に乾燥して得たラミネートシート、スラリーを押し出した後に乾燥して得た押し出しシートなどであってよい。前記たばこシートを裁刻せずにギャザー加工、折り畳み、あるいは渦巻き状にして巻紙内に充填してたばこ部材としてもよい。また、当該たばこシートを短冊状に裁断してこれらを同心円状にあるいは短冊の長手方向がたばこ部材の長手方向と平行になるように充填してたばこ部材としてもよい。
たばこ部材とは、たばこ原料に含まれる香喫味成分を発生するための略円柱状の部材である。たばこ部材はたばこ材料とその周囲を巻装する巻紙(ラッパー)を備える。巻紙内に充填されるたばこ材料の形状は限定されず、例えばたばこシート、または当該たばこシートを幅0.8~1.2mmに裁刻したもの、あるいは幅0.8~1.2mmに裁刻された刻などが挙げられる。たばこシートは限定されず、公知の方法で製造できる。例えばたばこシートは、抄紙シート、スラリーを基材上にキャストして製造したキャストシート、スラリーをローラーで圧展した後に乾燥して得たラミネートシート、スラリーを押し出した後に乾燥して得た押し出しシートなどであってよい。前記たばこシートを裁刻せずにギャザー加工、折り畳み、あるいは渦巻き状にして巻紙内に充填してたばこ部材としてもよい。また、当該たばこシートを短冊状に裁断してこれらを同心円状にあるいは短冊の長手方向がたばこ部材の長手方向と平行になるように充填してたばこ部材としてもよい。
たばこ材料の充填密度は特に限定されないが、非燃焼加熱型香味吸引物品の特性を担保し、良好な喫味を付与する観点から、通常200mg/cm3以上であり、好ましくは250mg/cm3以上である。また、その上限は通常800mg/cm3以下であり、好ましくは600mg/cm3以下である。たばこ部材1の長さは限定されないが10~25mmであることが好ましい。その直径も限定されないが6~8mmであることが好ましい。
たばこ材料は、加熱に伴って蒸気を発生してもよい。加熱温度は限定されないが30~400℃程度である。エアロゾルの発生を促進するために、たばこ材料にグリセリン、プロピレングリコール、1,3-ブタンジオール等のポリオール等のエアロゾル源を添加してもよい。エアロゾル源の添加量は、たばこ材料の乾燥重量に対して5~50重量%が好ましく、10~30重量%がより好ましい。その他、たばこ材料には公知の香料等を添加してもよい。前述のとおり、香味吸引物品用シートをたばこ部材のラッパーとして使用することもできる。
(2)冷却部材
冷却部材3は、たばこ部材1の下流側に接続されている。下流とは吸口端への方向をいう。冷却部材3は、たばこ部材1で発生した香喫味成分や蒸気を冷却する等してエアロゾル化を促進するための部材である。冷却部材は中空の紙管であってよい。紙管は巻紙やチップペーパーよりも剛性の高いカードボードで構成されることが好ましい。また、紙管は前述のとおり、香味吸引物品用シートで構成されてもよい。当該紙管には、ベンチレーションV(開孔)が設けられてもよい。ベンチレーションは紙管の円周に沿って複数設けられることが好ましい。また冷却部材内には、熱交換効率を高めるためにギャザー付けされたシートが充填されてもよい。冷却部材の寸法は限定されないが、長さは10~25mmであることが好ましく、直径は5.5~7.5mmであることが好ましい。
冷却部材3は、たばこ部材1の下流側に接続されている。下流とは吸口端への方向をいう。冷却部材3は、たばこ部材1で発生した香喫味成分や蒸気を冷却する等してエアロゾル化を促進するための部材である。冷却部材は中空の紙管であってよい。紙管は巻紙やチップペーパーよりも剛性の高いカードボードで構成されることが好ましい。また、紙管は前述のとおり、香味吸引物品用シートで構成されてもよい。当該紙管には、ベンチレーションV(開孔)が設けられてもよい。ベンチレーションは紙管の円周に沿って複数設けられることが好ましい。また冷却部材内には、熱交換効率を高めるためにギャザー付けされたシートが充填されてもよい。冷却部材の寸法は限定されないが、長さは10~25mmであることが好ましく、直径は5.5~7.5mmであることが好ましい。
(3)マウスピース
マウスピースは吸口端を構成する部材である。一態様においてマウスピース5は、第1フィルタ51と第2フィルタ52を備える。第1フィルタ51は、通常、当該分野で使用されるフィルタであってよく、中実なアセテートフィルタとすることができる。第2フィルタ52は、ラッパーと、ラッパー内に充填された香味吸引物品用シートを備えてもよい。第2フィルタ52の長さは特に限定されないが、5~20mmとすることができ、好ましくは10~15mm程度である。
マウスピースは吸口端を構成する部材である。一態様においてマウスピース5は、第1フィルタ51と第2フィルタ52を備える。第1フィルタ51は、通常、当該分野で使用されるフィルタであってよく、中実なアセテートフィルタとすることができる。第2フィルタ52は、ラッパーと、ラッパー内に充填された香味吸引物品用シートを備えてもよい。第2フィルタ52の長さは特に限定されないが、5~20mmとすることができ、好ましくは10~15mm程度である。
別の実施態様を図2~7に示す。
図2は、たばこ部材1のラッパーW(巻紙)が香味吸引物品用シートで構成され、第2フィルタ52が中空フィルタ、第1フィルタ51が中実のアセテートフィルタである態様を示す。
図3は、第2フィルタ52が香味吸引物品用シート充填フィルタ、第1フィルタ51がペーパーフィルタである態様を示す。
図4は、第2フィルタ52が香味吸引物品用シート充填フィルタ、第1フィルタ51がペーパーフィルタであって、破砕性カプセルCを内包するフィルタである態様を示す。
図5は、第2フィルタ52が香味吸引物品用シート充填フィルタ、第1フィルタ51がペーパーフィルタであって、第1フィルタ51と第2フィルタ52の間に中空部を有し、かつ当該中空部に破砕性カプセルCを内包するフィルタである態様を示す。
図6は、図1の態様においてたばこ部材1の上流側に先端部材9を、下流側に支持部材7を配置した態様を示す。
図7は、図6の態様における支持部材7と冷却部材3を、ベンチレーションを設けた支持部材7に置換した態様を示す。
これらの図における寸法は、一例であり、寸法は適宜調整される。
図2は、たばこ部材1のラッパーW(巻紙)が香味吸引物品用シートで構成され、第2フィルタ52が中空フィルタ、第1フィルタ51が中実のアセテートフィルタである態様を示す。
図3は、第2フィルタ52が香味吸引物品用シート充填フィルタ、第1フィルタ51がペーパーフィルタである態様を示す。
図4は、第2フィルタ52が香味吸引物品用シート充填フィルタ、第1フィルタ51がペーパーフィルタであって、破砕性カプセルCを内包するフィルタである態様を示す。
図5は、第2フィルタ52が香味吸引物品用シート充填フィルタ、第1フィルタ51がペーパーフィルタであって、第1フィルタ51と第2フィルタ52の間に中空部を有し、かつ当該中空部に破砕性カプセルCを内包するフィルタである態様を示す。
図6は、図1の態様においてたばこ部材1の上流側に先端部材9を、下流側に支持部材7を配置した態様を示す。
図7は、図6の態様における支持部材7と冷却部材3を、ベンチレーションを設けた支持部材7に置換した態様を示す。
これらの図における寸法は、一例であり、寸法は適宜調整される。
5.非燃焼加熱型香味吸引システム
非燃焼加熱型香味吸引物品と加熱ユニットの組合せを非燃焼加熱型香味吸引システムともいう。図8に当該システムの一態様を示す。図中、100は非燃焼加熱型香味吸引システム、10は非燃焼加熱型香味吸引物品、30はヒーターを備える加熱ユニットである。加熱ユニットは、ヒーターとハウジングと電源等を備える。
非燃焼加熱型香味吸引物品と加熱ユニットの組合せを非燃焼加熱型香味吸引システムともいう。図8に当該システムの一態様を示す。図中、100は非燃焼加熱型香味吸引システム、10は非燃焼加熱型香味吸引物品、30はヒーターを備える加熱ユニットである。加熱ユニットは、ヒーターとハウジングと電源等を備える。
ヒーターは、好ましくは電気的にたばこ部材1を加熱する。ヒーターは、たばこ部材1の外周部から加熱するタイプ、たばこ部材1に挿入して内部から加熱するタイプのいずれであってもよい。
また、非燃焼加熱型香味吸引システムは、IH(Induction Heating)加熱式のシステムであってもよい。この態様においては、加熱ユニット30は誘導コイルで構成される。当該加熱ユニットは、通常、たばこ部材1の外周部に配置される。そして、たばこ部材1は、誘導コイルの通電により発生する磁界により加熱されるサセプタを含みうる。
以下に、実施態様を記載する。
態様1
(A)20g/m2以上の吸着剤粒子と、
(B)パルプと、
(C)ポリエステル繊維と、
を含む香味吸引物品用シート。
態様2
前記(A)吸着剤粒子が活性炭を含む、態様1に記載のシート。
態様3
前記(C)が、ジオール残基として、炭素鎖が2~4のアルキレングリコール残基を含み、かつ二酸残基としてテレフタル酸、イソフタル酸、またはフタル酸残基を含む、態様1または2に記載のシート。
態様4
前記(C)のポリエステルが、ジオール残基として、エチレングリコール残基を含み、かつ二酸残基としてテレフタル酸残基を含む、態様3に記載のシート。
態様5
バインダーをさらに含む、態様1~4のいずれかに記載のシート。
態様6
5N/15mm以上の引張強度を有する、態様1~5のいずれかに記載のシート。
態様7
態様1~6のいずれかに記載のシートを含んで構成される、巻包材。
態様8
態様1~6のいずれかに記載のシートを備える、香味吸引物品用部材。
態様9
先端部材、香味源を含む香味発生部材、支持部材、冷却部材、およびこれらの組合せからなる群より選択される、態様8に記載の香味吸引物品用部材。
態様10
態様1~6のいずれかに記載のシート、
態様7に記載の巻包材、または
態様8または9に記載の香味吸引物品用部材を備える、
香味吸引物品。
態様1
(A)20g/m2以上の吸着剤粒子と、
(B)パルプと、
(C)ポリエステル繊維と、
を含む香味吸引物品用シート。
態様2
前記(A)吸着剤粒子が活性炭を含む、態様1に記載のシート。
態様3
前記(C)が、ジオール残基として、炭素鎖が2~4のアルキレングリコール残基を含み、かつ二酸残基としてテレフタル酸、イソフタル酸、またはフタル酸残基を含む、態様1または2に記載のシート。
態様4
前記(C)のポリエステルが、ジオール残基として、エチレングリコール残基を含み、かつ二酸残基としてテレフタル酸残基を含む、態様3に記載のシート。
態様5
バインダーをさらに含む、態様1~4のいずれかに記載のシート。
態様6
5N/15mm以上の引張強度を有する、態様1~5のいずれかに記載のシート。
態様7
態様1~6のいずれかに記載のシートを含んで構成される、巻包材。
態様8
態様1~6のいずれかに記載のシートを備える、香味吸引物品用部材。
態様9
先端部材、香味源を含む香味発生部材、支持部材、冷却部材、およびこれらの組合せからなる群より選択される、態様8に記載の香味吸引物品用部材。
態様10
態様1~6のいずれかに記載のシート、
態様7に記載の巻包材、または
態様8または9に記載の香味吸引物品用部材を備える、
香味吸引物品。
[実施例A1]
吸着剤粒子としての中賦活活性炭と、パルプと、ポリエステル繊維とを含むシートを調製し、評価した。評価方法は後述のとおりとした。活性炭の量、当該シートの物性を表1に示した。次いで、定法に従い、当該シートがラッパー内に折畳まれて充填されたフィルタを製造した。折畳まれることによって形成された稜線は当該フィルタの長手方向に略平行であった。フィルタの物性も表1に示した。当該シートは、優れた機械的特性を有し取扱性に優れていた。さらに当該シートは活性炭を多く含むので、吸着特性に優れたフィルタを与える。
吸着剤粒子としての中賦活活性炭と、パルプと、ポリエステル繊維とを含むシートを調製し、評価した。評価方法は後述のとおりとした。活性炭の量、当該シートの物性を表1に示した。次いで、定法に従い、当該シートがラッパー内に折畳まれて充填されたフィルタを製造した。折畳まれることによって形成された稜線は当該フィルタの長手方向に略平行であった。フィルタの物性も表1に示した。当該シートは、優れた機械的特性を有し取扱性に優れていた。さらに当該シートは活性炭を多く含むので、吸着特性に優れたフィルタを与える。
[実施例A2]
吸着剤粒子として高賦活活性炭を用いた以外は、実施例A1と同じ方法でシートおよびフィルタを製造し、評価した。当該シートは、優れた機械的特性を有し取扱性に優れていた。さらに当該シートは活性炭を多く含むので、吸着特性に優れたフィルタを与える。
吸着剤粒子として高賦活活性炭を用いた以外は、実施例A1と同じ方法でシートおよびフィルタを製造し、評価した。当該シートは、優れた機械的特性を有し取扱性に優れていた。さらに当該シートは活性炭を多く含むので、吸着特性に優れたフィルタを与える。
実施例A1、A2において製造された各シートの、SEM写真を図10に示した。シートに白金蒸着を施した後、印可電圧を10kVとして、800倍、10000倍で観察した。図に示すとおり、所望のシートが得られていることが確認された。
表1には、特許文献1の比較例1の「基材A」およびこれから製造されたフィルタの物性も示した。基材Aは活性炭を内添した紙であり、ポリエステル繊維を含んでいない。
[実施例B1~B4]
パルプとポリエステル繊維と活性炭とバインダーとを含むシートを準備した。定法に従い、当該シートがラッパー内に折畳まれて充填された、図1に示す第2フィルタを調製した。折畳まれることによって形成された稜線は当該フィルタの長手方向に略平行であった。当該フィルタについて、フィルタ品質測定器(SODIM社製 品名:SODIMAX)を用いて通気抵抗を測定した。具体的に、試料をその側面から空気が流入しないように空気不透過性のゴムで覆い、その一端から17.5cm3/秒の流量で吸引したときの試料の両端面における差圧(mmH2O)を通気抵抗として測定した。表2に各フィルタの物性を示した。
パルプとポリエステル繊維と活性炭とバインダーとを含むシートを準備した。定法に従い、当該シートがラッパー内に折畳まれて充填された、図1に示す第2フィルタを調製した。折畳まれることによって形成された稜線は当該フィルタの長手方向に略平行であった。当該フィルタについて、フィルタ品質測定器(SODIM社製 品名:SODIMAX)を用いて通気抵抗を測定した。具体的に、試料をその側面から空気が流入しないように空気不透過性のゴムで覆い、その一端から17.5cm3/秒の流量で吸引したときの試料の両端面における差圧(mmH2O)を通気抵抗として測定した。表2に各フィルタの物性を示した。
当該フィルタを第2フィルタとして用いて図1に示す非燃焼加熱型吸引物品を製造した。構造とサイズは以下のとおりとした。
たばこ部材/紙管/第2フィルタ/第1フィルタ=20/20/12/8(mm)
たばこ部材/紙管/第2フィルタ/第1フィルタ=20/20/12/8(mm)
前記非燃焼加熱型香味吸引物品のたばこ部材側端を、図8に示す加熱デバイスに挿入した。ヒーター温度を295℃とし、たばこ部材を当該ヒーターで加熱した。当該物品の吸口端側にケンブリッジフィルター(Borgwaldt KC Inc.製、CM-133)およびDNPH(2,4-dinitrophenylhydrazine)溶液の入ったインピンジャーを配置し、喫煙機による喫煙試験に供した。具体的には、自動喫煙器(Borgwaldt KC Inc.製LM-1)を用いて、サンプルを吸煙容量27.5ml/秒、吸煙時間2秒/パフ、吸煙頻度2パフ/分、10パフの条件で自動喫煙を実施した。
ニコチンおよびグリセリンの分析は以下の方法で行った。喫煙試験後のケンブリッジフィルターを、メタノール(和光純薬工業株式会社製、試薬特級)10mL中で振盪して分析試料を得た。得られた分析試料1μLをマイクロシリンジに採取し、ガスクロマトグラフ質量分析(Agilent製GC-MSD、GC:7890A、MS:5975C)にて分析した。結果を表2に示した。
カルボニル成分のうちホルムアルデヒド、アセトアルデヒドおよびアクロレインの分析は以下の方法で行った。喫煙試験後のケンブリッジフィルターを、インピンジャー捕集液に浸漬し振とうした後、メンブレンフィルターで固形分を濾過した。さらに、Trizma base溶液に所定量の濾液を加えて振とうし、誘導体化反応を停止させた。溶液を再びメンブレンフィルター濾過後、HPLC-DADに供してカルボニル成分を分析した。カルボニル成分の分析方法は、WO2004/026054公報およびCORESTA Recommended Method No. 96 - Determination of Formaldehyde and Acetaldehyde in E-Vapour Product Aerosol February 2021の開示を参照した。結果を表3に示した。また、Ch/PDとホルムアルデヒド量との関係を図9に示した。
[比較例B1~B2]
センターホールフィルタとペーパーフィルタを準備した。当該フィルタの物性を表2に示した。第2フィルタ52の代わりに、当該センターホールフィルタとペーパーフィルタをそれぞれ用いた以外は、実施例B1と同じ方法で非燃焼加熱型香味吸引物品を調製し、たばこ煙中粒状物質を定量した。結果を表3に示した。
センターホールフィルタとペーパーフィルタを準備した。当該フィルタの物性を表2に示した。第2フィルタ52の代わりに、当該センターホールフィルタとペーパーフィルタをそれぞれ用いた以外は、実施例B1と同じ方法で非燃焼加熱型香味吸引物品を調製し、たばこ煙中粒状物質を定量した。結果を表3に示した。
実施例Bで製造したフィルタは、香喫味に好ましくない影響を与える成分、特に従来のフィルタでは除去が困難であったホルムアルデヒド、アセトアルデヒド、およびアクロレインの除去に有効であることが明らかである。
10 非燃焼加熱型香味吸引物品
1 たばこ部材
3 冷却部材
5 マウスピース
51 第1フィルタ
52 第2フィルタ
7 支持部材
9 先端部材
V ベンチレーション
W ラッパー
C カプセル
100 非燃焼加熱型香味吸引システム
30 ヒーターを備える加熱ユニット
1 たばこ部材
3 冷却部材
5 マウスピース
51 第1フィルタ
52 第2フィルタ
7 支持部材
9 先端部材
V ベンチレーション
W ラッパー
C カプセル
100 非燃焼加熱型香味吸引システム
30 ヒーターを備える加熱ユニット
Claims (10)
- (A)20g/m2以上の吸着剤粒子と、
(B)パルプと、
(C)ポリエステル繊維と、
を含む香味吸引物品用シート。 - 前記(A)吸着剤粒子が活性炭を含む、請求項1に記載のシート。
- 前記(C)が、ジオール残基として、炭素鎖が2~4のアルキレングリコール残基を含み、かつ二酸残基としてテレフタル酸、イソフタル酸、またはフタル酸残基を含む、請求項1または2に記載のシート。
- 前記(C)のポリエステルが、ジオール残基として、エチレングリコール残基を含み、かつ二酸残基としてテレフタル酸残基を含む、請求項3に記載のシート。
- バインダーをさらに含む、請求項1~4のいずれかに記載のシート。
- 5N/15mm以上の引張強度を有する、請求項1~5のいずれかに記載のシート。
- 請求項1~6のいずれかに記載のシートを含んで構成される、巻包材。
- 請求項1~6のいずれかに記載のシートを備える、香味吸引物品用部材。
- 先端部材、香味源を含む香味発生部材、支持部材、冷却部材、およびこれらの組合せからなる群より選択される、請求項8に記載の香味吸引物品用部材。
- 請求項1~6のいずれかに記載のシート、
請求項7に記載の巻包材、または
請求項8または9に記載の香味吸引物品用部材を備える、
香味吸引物品。