WO2023156980A1 - Article abrasif non-tissé et ses procédés de fabrication - Google Patents

Article abrasif non-tissé et ses procédés de fabrication Download PDF

Info

Publication number
WO2023156980A1
WO2023156980A1 PCT/IB2023/051534 IB2023051534W WO2023156980A1 WO 2023156980 A1 WO2023156980 A1 WO 2023156980A1 IB 2023051534 W IB2023051534 W IB 2023051534W WO 2023156980 A1 WO2023156980 A1 WO 2023156980A1
Authority
WO
WIPO (PCT)
Prior art keywords
prebond
composition
nonwoven
precursor composition
curable
Prior art date
Application number
PCT/IB2023/051534
Other languages
English (en)
Inventor
Michihiro Yamahara
Original Assignee
3M Innovative Properties Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Company filed Critical 3M Innovative Properties Company
Publication of WO2023156980A1 publication Critical patent/WO2023156980A1/fr

Abstract

Un article abrasif non-tissé comporte une composition de pré-collage disposée sur une bande de fibre non-tissée ouverte gonflante, une couche abrasive disposée sur, et sécurisée à, au moins une partie de la composition de pré-collage. La couche abrasive comprend une composition de liant retenant des particules abrasives. La composition de pré-collage et/ou la composition de liant comprend un produit réactionnel d'un polymère possédant une pluralité de groupes oxazolinyle. Des procédés de fabrication de l'article abrasif non-tissé sont également divulgués.
PCT/IB2023/051534 2022-02-21 2023-02-20 Article abrasif non-tissé et ses procédés de fabrication WO2023156980A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202263312146P 2022-02-21 2022-02-21
US63/312,146 2022-02-21

Publications (1)

Publication Number Publication Date
WO2023156980A1 true WO2023156980A1 (fr) 2023-08-24

Family

ID=85476184

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2023/051534 WO2023156980A1 (fr) 2022-02-21 2023-02-20 Article abrasif non-tissé et ses procédés de fabrication

Country Status (1)

Country Link
WO (1) WO2023156980A1 (fr)

Citations (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2958593A (en) 1960-01-11 1960-11-01 Minnesota Mining & Mfg Low density open non-woven fibrous abrasive article
US3839350A (en) 1970-06-15 1974-10-01 Commercial Solvents Corp Production of vinyl oxazoline esters
US4314827A (en) 1979-06-29 1982-02-09 Minnesota Mining And Manufacturing Company Non-fused aluminum oxide-based abrasive mineral
US4623364A (en) 1984-03-23 1986-11-18 Norton Company Abrasive material and method for preparing the same
US4652275A (en) 1985-08-07 1987-03-24 Minnesota Mining And Manufacturing Company Erodable agglomerates and abrasive products containing the same
US4744802A (en) 1985-04-30 1988-05-17 Minnesota Mining And Manufacturing Company Process for durable sol-gel produced alumina-based ceramics, abrasive grain and abrasive products
US4770671A (en) 1985-12-30 1988-09-13 Minnesota Mining And Manufacturing Company Abrasive grits formed of ceramic containing oxides of aluminum and yttrium, method of making and using the same and products made therewith
US4799939A (en) 1987-02-26 1989-01-24 Minnesota Mining And Manufacturing Company Erodable agglomerates and abrasive products containing the same
US4881951A (en) 1987-05-27 1989-11-21 Minnesota Mining And Manufacturing Co. Abrasive grits formed of ceramic containing oxides of aluminum and rare earth metal, method of making and products made therewith
US5152917A (en) 1991-02-06 1992-10-06 Minnesota Mining And Manufacturing Company Structured abrasive article
US5201916A (en) 1992-07-23 1993-04-13 Minnesota Mining And Manufacturing Company Shaped abrasive particles and method of making same
US5213591A (en) 1992-07-28 1993-05-25 Ahmet Celikkaya Abrasive grain, method of making same and abrasive products
US5366523A (en) 1992-07-23 1994-11-22 Minnesota Mining And Manufacturing Company Abrasive article containing shaped abrasive particles
US5435816A (en) 1993-01-14 1995-07-25 Minnesota Mining And Manufacturing Company Method of making an abrasive article
US5556437A (en) 1990-11-14 1996-09-17 Minnesota Mining And Manufacturing Company Coated abrasive having an overcoating of an epoxy resin coatable from water
US5591239A (en) 1994-08-30 1997-01-07 Minnesota Mining And Manufacturing Company Nonwoven abrasive article and method of making same
US5672097A (en) 1993-09-13 1997-09-30 Minnesota Mining And Manufacturing Company Abrasive article for finishing
US5946991A (en) 1997-09-03 1999-09-07 3M Innovative Properties Company Method for knurling a workpiece
US5975987A (en) 1995-10-05 1999-11-02 3M Innovative Properties Company Method and apparatus for knurling a workpiece, method of molding an article with such workpiece, and such molded article
US20060178090A1 (en) * 2005-02-04 2006-08-10 3M Innovative Properties Company Abrasive cleaning article and method of making
US20090169816A1 (en) 2007-12-27 2009-07-02 3M Innovative Properties Company Shaped, fractured abrasive particle, abrasive article using same and method of making
US20090165394A1 (en) 2007-12-27 2009-07-02 3M Innovative Properties Company Method of making abrasive shards, shaped abrasive particles with an opening, or dish-shaped abrasive particles
US20100092746A1 (en) * 2008-10-14 2010-04-15 Jean-Marie Coant Nonwoven material containing benefiting particles and method of making
US8142531B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with a sloping sidewall
US8142891B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Dish-shaped abrasive particles with a recessed surface
US8142532B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with an opening
US20120227333A1 (en) 2009-12-02 2012-09-13 Adefris Negus B Dual tapered shaped abrasive particles
US20130040537A1 (en) 2010-04-27 2013-02-14 Mark G. Schwabel Ceramic shaped abrasive particles, methods of making the same, and abrasive articles containing the same
US20130125477A1 (en) 2010-08-04 2013-05-23 3M Innovative Properties Company Intersecting plate shaped abrasive particles
US9771504B2 (en) 2012-04-04 2017-09-26 3M Innovative Properties Company Abrasive particles, method of making abrasive particles, and abrasive articles
US20210078138A1 (en) * 2017-07-14 2021-03-18 3M Innovative Properties Company Abrasive article with anionic water solubilizing material and method of making

Patent Citations (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2958593A (en) 1960-01-11 1960-11-01 Minnesota Mining & Mfg Low density open non-woven fibrous abrasive article
US3839350A (en) 1970-06-15 1974-10-01 Commercial Solvents Corp Production of vinyl oxazoline esters
US4314827A (en) 1979-06-29 1982-02-09 Minnesota Mining And Manufacturing Company Non-fused aluminum oxide-based abrasive mineral
US4623364A (en) 1984-03-23 1986-11-18 Norton Company Abrasive material and method for preparing the same
US4744802A (en) 1985-04-30 1988-05-17 Minnesota Mining And Manufacturing Company Process for durable sol-gel produced alumina-based ceramics, abrasive grain and abrasive products
US4652275A (en) 1985-08-07 1987-03-24 Minnesota Mining And Manufacturing Company Erodable agglomerates and abrasive products containing the same
US4770671A (en) 1985-12-30 1988-09-13 Minnesota Mining And Manufacturing Company Abrasive grits formed of ceramic containing oxides of aluminum and yttrium, method of making and using the same and products made therewith
US4799939A (en) 1987-02-26 1989-01-24 Minnesota Mining And Manufacturing Company Erodable agglomerates and abrasive products containing the same
US4881951A (en) 1987-05-27 1989-11-21 Minnesota Mining And Manufacturing Co. Abrasive grits formed of ceramic containing oxides of aluminum and rare earth metal, method of making and products made therewith
US5556437A (en) 1990-11-14 1996-09-17 Minnesota Mining And Manufacturing Company Coated abrasive having an overcoating of an epoxy resin coatable from water
US5152917A (en) 1991-02-06 1992-10-06 Minnesota Mining And Manufacturing Company Structured abrasive article
US5152917B1 (en) 1991-02-06 1998-01-13 Minnesota Mining & Mfg Structured abrasive article
US5201916A (en) 1992-07-23 1993-04-13 Minnesota Mining And Manufacturing Company Shaped abrasive particles and method of making same
US5366523A (en) 1992-07-23 1994-11-22 Minnesota Mining And Manufacturing Company Abrasive article containing shaped abrasive particles
US5213591A (en) 1992-07-28 1993-05-25 Ahmet Celikkaya Abrasive grain, method of making same and abrasive products
US5435816A (en) 1993-01-14 1995-07-25 Minnesota Mining And Manufacturing Company Method of making an abrasive article
US5672097A (en) 1993-09-13 1997-09-30 Minnesota Mining And Manufacturing Company Abrasive article for finishing
US6129540A (en) 1993-09-13 2000-10-10 Minnesota Mining & Manufacturing Company Production tool for an abrasive article and a method of making same
US5591239A (en) 1994-08-30 1997-01-07 Minnesota Mining And Manufacturing Company Nonwoven abrasive article and method of making same
US5975987A (en) 1995-10-05 1999-11-02 3M Innovative Properties Company Method and apparatus for knurling a workpiece, method of molding an article with such workpiece, and such molded article
US5946991A (en) 1997-09-03 1999-09-07 3M Innovative Properties Company Method for knurling a workpiece
US20060178090A1 (en) * 2005-02-04 2006-08-10 3M Innovative Properties Company Abrasive cleaning article and method of making
US20090169816A1 (en) 2007-12-27 2009-07-02 3M Innovative Properties Company Shaped, fractured abrasive particle, abrasive article using same and method of making
US20090165394A1 (en) 2007-12-27 2009-07-02 3M Innovative Properties Company Method of making abrasive shards, shaped abrasive particles with an opening, or dish-shaped abrasive particles
US20100092746A1 (en) * 2008-10-14 2010-04-15 Jean-Marie Coant Nonwoven material containing benefiting particles and method of making
US8142531B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with a sloping sidewall
US8142891B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Dish-shaped abrasive particles with a recessed surface
US8142532B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with an opening
US20120227333A1 (en) 2009-12-02 2012-09-13 Adefris Negus B Dual tapered shaped abrasive particles
US20130040537A1 (en) 2010-04-27 2013-02-14 Mark G. Schwabel Ceramic shaped abrasive particles, methods of making the same, and abrasive articles containing the same
US20130125477A1 (en) 2010-08-04 2013-05-23 3M Innovative Properties Company Intersecting plate shaped abrasive particles
US9771504B2 (en) 2012-04-04 2017-09-26 3M Innovative Properties Company Abrasive particles, method of making abrasive particles, and abrasive articles
US10301518B2 (en) 2012-04-04 2019-05-28 3M Innovative Properties Company Abrasive particles, method of making abrasive particles, and abrasive articles
US20210078138A1 (en) * 2017-07-14 2021-03-18 3M Innovative Properties Company Abrasive article with anionic water solubilizing material and method of making

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
LIU ET AL.: "Continuous Production of Water-Borne Polyurethanes: A Review", POLYMERS, vol. 12, 2020, pages 2875

Similar Documents

Publication Publication Date Title
CN108349070B (zh) 磨料制品及其制备方法
US11691248B2 (en) Abrasive articles including an anti-loading size layer
US10850368B2 (en) Nonwoven abrasive articles and methods of making the same
EP3283258B1 (fr) Article abrasif non tissé et procédé de fabrication de ce dernier
EP2598291B1 (fr) Manique abrasive hybride et procédé d'abrasion d'une surface
EP3046730A1 (fr) Article abrasif non tissé comprenant un composé anti-encrassement à base de cire et procédé d'utilisation associé
WO2008055021A1 (fr) Article abrasif et son procédé de fabrication et d'utilisation
JP4554942B2 (ja) 目詰まり防止処理剤
AU2002248225B2 (en) Anti-loading treatments
AU2002248225A1 (en) Anti-loading treatments
CN113474122B (zh) 磨料制品及其制备和使用方法
WO2023156980A1 (fr) Article abrasif non-tissé et ses procédés de fabrication
US20230089669A1 (en) Abrasive articles including an anti-loading size layer with enhanced manufacturability

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23708904

Country of ref document: EP

Kind code of ref document: A1