WO2023137791A1 - Waterproof gas-permeable tpu hot-melt adhesive film and preparation process therefor - Google Patents
Waterproof gas-permeable tpu hot-melt adhesive film and preparation process therefor Download PDFInfo
- Publication number
- WO2023137791A1 WO2023137791A1 PCT/CN2022/074643 CN2022074643W WO2023137791A1 WO 2023137791 A1 WO2023137791 A1 WO 2023137791A1 CN 2022074643 W CN2022074643 W CN 2022074643W WO 2023137791 A1 WO2023137791 A1 WO 2023137791A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- melt adhesive
- adhesive film
- waterproof
- tpu hot
- breathable
- Prior art date
Abstract
Provided are a waterproof gas-permeable TPU hot-melt adhesive film and a preparation process therefor. The waterproof gas-permeable TPU hot-melt adhesive film comprises the following components in parts by weight: 75-90 parts of TPU; 15-40 parts of a solvent; 20-45 parts of graphene oxide; 1-3 parts of a porogen; 0.5-2 parts of a hydrophobic agent; 0.5-1 part of a reducing agent; and 0.1-0.5 parts of a light stabilizer. The waterproof gas-permeable TPU hot-melt adhesive film has a good use effect, has excellent performance, and is easy to prepare, so that the convenience and stability of production and processing are improved.
Description
本发明涉及TPU热熔胶膜领域,特别是涉及一种防水透气TPU热熔胶膜及其制备工艺。The invention relates to the field of TPU hot-melt adhesive films, in particular to a waterproof and breathable TPU hot-melt adhesive film and a preparation process thereof.
防水透气材料在近十年里取得了迅速的发展,在户外服饰、建筑装饰、水上作业等领域得到广泛的应用,在TPU薄膜中,防水透气膜材料主要分为聚酯型薄膜和聚醚型薄膜,都具有良好的防水性能,在透气性能上,聚酯型薄膜相较于聚醚型薄膜,差距效果很大。Waterproof and breathable materials have achieved rapid development in the past ten years, and have been widely used in outdoor clothing, architectural decoration, water operations and other fields. Among TPU films, waterproof and breathable membrane materials are mainly divided into polyester films and polyether films, both of which have good waterproof performance. In terms of breathability, polyester films have a large gap compared with polyether films.
发明内容Contents of the invention
为解决上述技术问题,本发明提供一种使用效果好、性能优异的防水透气TPU热熔胶膜。In order to solve the above technical problems, the present invention provides a waterproof and breathable TPU hot melt adhesive film with good use effect and excellent performance.
本发明还提供一种防水透气TPU热熔胶膜的制备工艺,制备简单,提高生产加工的便利性和稳定性。The invention also provides a preparation process of a waterproof and breathable TPU hot-melt adhesive film, which is simple in preparation and improves the convenience and stability of production and processing.
本发明采用如下技术方案:The present invention adopts following technical scheme:
一种防水透气TPU热熔胶膜,包括如下重量份数的组分:A waterproof and breathable TPU hot melt adhesive film, comprising the following components in parts by weight:
对上述技术方案的进一步改进为,所述溶剂的浓度为0.6~0.9mol/L。A further improvement to the above technical solution is that the concentration of the solvent is 0.6-0.9 mol/L.
对上述技术方案的进一步改进为,所述氧化石墨烯的浓度为21~25mg/mL。A further improvement to the above technical solution is that the concentration of the graphene oxide is 21-25 mg/mL.
对上述技术方案的进一步改进为,所述致孔剂为聚乙烯吡咯烷酮、聚乙二醇中的至少一种。A further improvement to the above technical solution is that the porogen is at least one of polyvinylpyrrolidone and polyethylene glycol.
对上述技术方案的进一步改进为,所述疏水剂为聚四氟乙烯、聚三氟氯乙烯、聚全氟乙丙烯中的一种或几种。A further improvement to the above technical solution is that the hydrophobic agent is one or more of polytetrafluoroethylene, polychlorotrifluoroethylene, and polyperfluoroethylene propylene.
对上述技术方案的进一步改进为,所述还原剂为葡萄糖、二甲基胺硼烷中的一种或两种。A further improvement to the above technical solution is that the reducing agent is one or both of glucose and dimethylamine borane.
对上述技术方案的进一步改进为,所述光稳定剂为癸二酸二(2,2,6,6-四甲基-4-哌啶)酯、聚[[6-[(1,1,3,3-四甲基丁基)胺]-1,3,5-三嗪-2,4-二基][(2,2,6,6-四甲基-4-哌啶)亚胺]-1,6-二己二基[(2,2,6,6-四甲基-4-哌啶)亚胺]]]、双(1,2,2,6,6-五甲基-4-哌啶基)癸二酸酯中的任意一种或至少两种的混合物。A further improvement to the above technical solution is that the light stabilizer is bis(2,2,6,6-tetramethyl-4-piperidine) sebacate, poly[[6-[(1,1,3,3-tetramethylbutyl)amine]-1,3,5-triazine-2,4-diyl][(2,2,6,6-tetramethyl-4-piperidine)imine]-1,6-dihexanediyl[(2,2,6,6-tetramethyl-4- Any one or a mixture of at least two of piperidine) imine]]], bis(1,2,2,6,6-pentamethyl-4-piperidinyl) sebacate.
一种防水透气TPU热熔胶膜的制备方法,包括如下步骤:A preparation method of a waterproof and breathable TPU hot-melt adhesive film, comprising the steps of:
S1、将氧化石墨烯分散在水中,然后加入过氧化氢溶液,110~120℃反应1h~8h,反应完成后加入还原剂继续反应3~4h后离心或过滤收集固体产物,得到多孔石墨烯;S1. Disperse graphene oxide in water, then add hydrogen peroxide solution, and react at 110-120°C for 1h-8h. After the reaction is completed, add a reducing agent to continue the reaction for 3-4h, then centrifuge or filter to collect the solid product to obtain porous graphene;
S2、将步骤S1中的多孔石墨烯分散在溶剂中,然后加入疏水剂,反应30~60min后,加入适量的致孔剂,搅拌均匀得到改性多孔石墨烯分散液;S2, dispersing the porous graphene in step S1 in a solvent, then adding a hydrophobic agent, after reacting for 30 to 60 minutes, adding an appropriate amount of porogen, and stirring evenly to obtain a modified porous graphene dispersion;
S3、将TPU置于溶剂中,然后在95~100℃进行搅拌,溶解完全;S3. Put the TPU in the solvent, and then stir at 95-100°C to dissolve completely;
S4、将步骤S2的多孔石墨烯分散液与步骤S3的TPU溶液混合,再加入光稳定剂,搅拌均匀后,在0.07~0.1MPa下脱泡35~50min,将脱泡后的混合溶液通过涂布的方式均匀涂布在离型纸上,然后将涂布后的离型纸送入烘箱中进行烘干干燥,将干燥后的产品常温固化,完全固化后即可得到防水透气TPU热熔胶膜。S4. Mix the porous graphene dispersion in step S2 with the TPU solution in step S3, add a light stabilizer, stir evenly, and defoam at 0.07 to 0.1 MPa for 35 to 50 minutes. Apply the defoamed mixed solution evenly on the release paper by coating, then send the coated release paper into an oven for drying and drying, and cure the dried product at room temperature. After complete curing, a waterproof and breathable TPU hot melt adhesive film can be obtained.
对上述技术方案的进一步改进为,在所述步骤S4中,所述涂布的间隙为0.6-1mm。A further improvement to the above technical solution is that in the step S4, the coating gap is 0.6-1 mm.
对上述技术方案的进一步改进为,在所述步骤S4中,所述烘箱的温度设为130-150℃。A further improvement to the above technical solution is that in the step S4, the temperature of the oven is set to 130-150°C.
本发明的有益效果为:The beneficial effects of the present invention are:
本发明的防水透气TPU热熔胶膜兼顾胶膜的透湿性和力学性能,还具有良好的抗张强度,同时具有优异的防水透气性;制备工艺十分简单,能耗低,含石墨烯的多孔膜的性能易控制。The waterproof and breathable TPU hot-melt adhesive film of the present invention takes into account the moisture permeability and mechanical properties of the film, and also has good tensile strength and excellent waterproof and air permeability; the preparation process is very simple, the energy consumption is low, and the performance of the graphene-containing porous film is easy to control.
为更好地理解本发明,下面结合实施例对本发明作进一步说明,但是本发明的实施方式不限于此。In order to better understand the present invention, the present invention will be further described below in conjunction with examples, but the embodiments of the present invention are not limited thereto.
一种防水透气TPU热熔胶膜,包括如下重量份数的组分:A waterproof and breathable TPU hot melt adhesive film, comprising the following components in parts by weight:
优选地,所述溶剂的浓度为0.6~0.9mol/L。Preferably, the concentration of the solvent is 0.6-0.9 mol/L.
优选地,所述氧化石墨烯的浓度为21~25mg/mL。Preferably, the concentration of the graphene oxide is 21-25 mg/mL.
优选地,所述致孔剂为聚乙烯吡咯烷酮、聚乙二醇中的至少一种。Preferably, the porogen is at least one of polyvinylpyrrolidone and polyethylene glycol.
优选地,所述疏水剂为聚四氟乙烯、聚三氟氯乙烯、聚全氟乙丙烯中的一种或几种。Preferably, the hydrophobic agent is one or more of polytetrafluoroethylene, polychlorotrifluoroethylene, and polyperfluoroethylene propylene.
优选地,所述还原剂为葡萄糖、二甲基胺硼烷中的一种或两种。Preferably, the reducing agent is one or both of glucose and dimethylamine borane.
优选地,所述光稳定剂为癸二酸二(2,2,6,6-四甲基-4-哌啶)酯、聚[[6-[(1,1,3,3-四甲基丁基)胺]-1,3,5-三嗪-2,4-二基][(2,2,6,6-四甲基-4-哌啶)亚胺]-1,6-二己二基[(2,2,6,6-四甲基-4-哌啶)亚胺]]]、双(1,2,2,6,6-五甲基-4-哌啶基)癸二酸酯中的任意一种或至少两种的混合物。Preferably, the light stabilizer is bis(2,2,6,6-tetramethyl-4-piperidine) sebacate, poly[[6-[(1,1,3,3-tetramethylbutyl)amine]-1,3,5-triazine-2,4-diyl][(2,2,6,6-tetramethyl-4-piperidine)imine]-1,6-dihexanediyl[(2,2,6,6-tetramethyl-4-piperidine)imine] ]], bis(1,2,2,6,6-pentamethyl-4-piperidinyl) sebacate, or a mixture of at least two.
一种防水透气TPU热熔胶膜的制备方法,包括如下步骤:A preparation method of a waterproof and breathable TPU hot-melt adhesive film, comprising the steps of:
S1、将氧化石墨烯分散在水中,然后加入过氧化氢溶液,110~120℃反应1h~8h,反应完成后加入还原剂继续反应3~4h后离心或过滤收集固体产物,得到多孔石墨烯;S1. Disperse graphene oxide in water, then add hydrogen peroxide solution, and react at 110-120°C for 1h-8h. After the reaction is completed, add a reducing agent to continue the reaction for 3-4h, then centrifuge or filter to collect the solid product to obtain porous graphene;
S2、将步骤S1中的多孔石墨烯分散在溶剂中,然后加入疏水剂,反应30~60min后,加入适量的致孔剂,搅拌均匀得到改性多孔石墨烯分散液;S2, dispersing the porous graphene in step S1 in a solvent, then adding a hydrophobic agent, after reacting for 30 to 60 minutes, adding an appropriate amount of porogen, and stirring evenly to obtain a modified porous graphene dispersion;
S3、将TPU热熔胶置于溶剂中,然后在95~100℃进行搅拌,溶解完全;S3. Put the TPU hot melt adhesive in a solvent, and then stir at 95-100°C to dissolve completely;
S4、将步骤S2的多孔石墨烯分散液与步骤S3的TPU溶液混合,再加入光稳定剂,搅拌均匀后,在0.07~0.1MPa下脱泡35~50min,将脱泡后的混合溶液通过涂布的方式均匀涂布在离型纸上,然后将涂布后的离型纸送入烘箱中进行烘干干燥,将干燥后的产品常温固化,完全固化后即可得到防水透气TPU热熔胶膜。S4. Mix the porous graphene dispersion in step S2 with the TPU solution in step S3, add a light stabilizer, stir evenly, and defoam at 0.07 to 0.1 MPa for 35 to 50 minutes. Apply the defoamed mixed solution evenly on the release paper by coating, then send the coated release paper into an oven for drying and drying, and cure the dried product at room temperature. After complete curing, a waterproof and breathable TPU hot melt adhesive film can be obtained.
优选地,在所述步骤S4中,所述涂布的间隙为0.6-1mm。Preferably, in the step S4, the coating gap is 0.6-1 mm.
优选地,在所述步骤S4中,所述烘箱的温度设为130-150℃。Preferably, in the step S4, the temperature of the oven is set at 130-150°C.
实施例1Example 1
一种防水透气TPU热熔胶膜的制备方法,包括如下步骤:A preparation method of a waterproof and breathable TPU hot-melt adhesive film, comprising the steps of:
S1、将30份氧化石墨烯分散在水中,然后加入过氧化氢溶液,120℃反应8h,反应完成后加入0.5份还原剂继续反应4h后离心或过滤收集固体产物,得到多孔石墨烯;S1. Disperse 30 parts of graphene oxide in water, then add hydrogen peroxide solution, and react at 120°C for 8 hours. After the reaction is completed, add 0.5 parts of reducing agent to continue the reaction for 4 hours, then centrifuge or filter to collect the solid product to obtain porous graphene;
S2、将步骤S1中的多孔石墨烯分散在溶剂中,然后加入1份疏水剂,反应60min后,加入1.5份致孔剂,搅拌均匀得到改性多孔石墨烯分散液;S2, disperse the porous graphene in the step S1 in the solvent, then add 1 part of hydrophobic agent, after reacting for 60min, add 1.5 parts of porogen, stir to obtain the modified porous graphene dispersion;
S3、将75份TPU热熔胶置于15份酒精溶液中,然后在100℃进行搅拌,溶解完全;S3. Put 75 parts of TPU hot melt adhesive in 15 parts of alcohol solution, and then stir at 100°C to dissolve completely;
S4、将步骤S2的多孔石墨烯分散液与步骤S3的TPU溶液混合,再加入0.2份光稳定剂,搅拌均匀后,在0.1MPa下脱泡40min,将脱泡后的混合溶液通过涂布的方式均匀涂布在离型纸上,然后将涂布后的离型纸送入烘箱中进行烘干干燥,将干燥后的产品常温固化,完全固化后即可得到防水透气TPU热熔胶膜。S4. Mix the porous graphene dispersion in step S2 with the TPU solution in step S3, then add 0.2 parts of light stabilizer, stir evenly, defoam at 0.1 MPa for 40 minutes, evenly coat the degassed mixed solution on the release paper by coating, then send the coated release paper into an oven for drying and drying, and cure the dried product at room temperature. After complete curing, a waterproof and breathable TPU hot-melt adhesive film can be obtained.
实施例2Example 2
一种防水透气TPU热熔胶膜的制备方法,包括如下步骤:A preparation method of a waterproof and breathable TPU hot-melt adhesive film, comprising the steps of:
S1、将35份氧化石墨烯分散在水中,然后加入过氧化氢溶液,110℃反应2h,反应完成后加入0.5份还原剂继续反应3h后离心或过滤收集固体产物,得到多孔石墨烯;S1. Disperse 35 parts of graphene oxide in water, then add hydrogen peroxide solution, and react at 110°C for 2 hours. After the reaction is completed, add 0.5 parts of reducing agent to continue the reaction for 3 hours, then centrifuge or filter to collect the solid product to obtain porous graphene;
S2、将步骤S1中的多孔石墨烯分散在酒精溶液中,然后加入1份疏水剂,反应30min后,加入1份致孔剂,搅拌均匀得到改性多孔石墨烯分散液;S2, disperse the porous graphene in the step S1 in the alcohol solution, then add 1 part of hydrophobic agent, after reacting for 30min, add 1 part of porogen, stir to obtain the modified porous graphene dispersion;
S3、将75份TPU置于20份酒精溶液中,然后在95℃进行搅拌,溶解完全;S3. Put 75 parts of TPU in 20 parts of alcohol solution, and then stir at 95°C to dissolve completely;
S4、将步骤S2的多孔石墨烯分散液与步骤S3的TPU溶液混合,再加入0.4份光稳定剂,搅拌均匀后,在0.07MPa下脱泡35min,将脱泡后的混合溶液通过涂布的方式均匀涂布在离型纸上,然后将涂布后的离型纸送入烘箱中进行烘干干燥,将干燥后的产品常温固化,完全固化后即可得到防水透气TPU热熔胶膜。S4. Mix the porous graphene dispersion in step S2 with the TPU solution in step S3, then add 0.4 parts of light stabilizer, stir evenly, defoam at 0.07MPa for 35 minutes, evenly coat the degassed mixed solution on the release paper by coating, then send the coated release paper into an oven for drying and drying, and cure the dried product at room temperature. After complete curing, a waterproof and breathable TPU hot melt adhesive film can be obtained.
实施例3Example 3
一种防水透气TPU热熔胶膜的制备方法,包括如下步骤:A preparation method of a waterproof and breathable TPU hot-melt adhesive film, comprising the steps of:
S1、将45份氧化石墨烯分散在水中,然后加入过氧化氢溶液,115℃反应5h,反应完成后加入1份还原剂继续反应3.5h后离心或过滤收集固体产物,得到多孔石墨烯;S1. Disperse 45 parts of graphene oxide in water, then add hydrogen peroxide solution, and react at 115°C for 5 hours. After the reaction is completed, add 1 part of reducing agent to continue the reaction for 3.5 hours, then centrifuge or filter to collect the solid product to obtain porous graphene;
S2、将步骤S1中的多孔石墨烯分散在酒精溶液中,然后加入1.5份疏水剂,反应40min后,加入2份致孔剂,搅拌均匀得到改性多孔石墨烯分散液;S2, disperse the porous graphene in the step S1 in the alcohol solution, then add 1.5 parts of hydrophobic agents, after reacting for 40min, add 2 parts of porogens, stir to obtain the modified porous graphene dispersion;
S3、将80份TPU置于25份酒精溶液中,然后在100℃进行搅拌,溶解完全;S3. Put 80 parts of TPU in 25 parts of alcohol solution, and then stir at 100°C to dissolve completely;
S4、将步骤S2的多孔石墨烯分散液与步骤S3的TPU溶液混合,再加入0.3份光稳定剂,搅拌均匀后,在0.1MPa下脱泡45min,将脱泡后的混合溶液通过涂布的方式均匀涂布在离型纸上,然后将涂布后的离型纸送入烘箱中进行烘干干燥,将干燥后的产品常温固化,完全固化后即可得到防水透气TPU热熔胶膜。S4. Mix the porous graphene dispersion in step S2 with the TPU solution in step S3, then add 0.3 parts of light stabilizer, stir evenly, defoam at 0.1 MPa for 45 minutes, evenly coat the degassed mixed solution on the release paper by coating, then send the coated release paper into an oven for drying, and dry the dried product at room temperature. After complete curing, a waterproof and breathable TPU hot-melt adhesive film can be obtained.
对比例1Comparative example 1
本对比例的的原料组成及重量份如下:致孔剂为0份;The raw material composition and parts by weight of this comparative example are as follows: porogen is 0 part;
制备方法同实施例1。The preparation method is the same as in Example 1.
对比例2Comparative example 2
本对比例的的原料组成及重量份如下:氧化石墨烯和致孔剂均为0份;The raw material composition and parts by weight of this comparative example are as follows: graphene oxide and porogen are 0 parts;
制备方法同实施例2。The preparation method is the same as in Example 2.
对实施例1-3和对比例1-2制备的TPU薄膜进行水蒸气透过率测试、耐水压测试以及抗张强度测试。其中,水蒸气透过率测试采用GB/T 1037-1988中所述的方法以及性能参数,测试结果如下表所示:The TPU films prepared in Examples 1-3 and Comparative Examples 1-2 were subjected to a water vapor transmission rate test, a water pressure resistance test and a tensile strength test. Among them, the water vapor transmission rate test adopts the method and performance parameters described in GB/T 1037-1988, and the test results are shown in the following table:
the | 水蒸气透过率(g/m 2·24h) Water vapor transmission rate (g/m 2 ·24h) | 静水压/mHydrostatic pressure/m | 抗张强度/MPaTensile strength/MPa |
实施例1Example 1 | 14913.214913.2 | 4.74.7 | 20.220.2 |
实施例2Example 2 | 15019.615019.6 | 4.94.9 | 21.821.8 |
实施例3Example 3 | 17579.117579.1 | 4.44.4 | 22.122.1 |
对比例1Comparative example 1 | 9243.29243.2 | 3.63.6 | 19.219.2 |
对比例2Comparative example 2 | 8987.88987.8 | 3.03.0 | 17.417.4 |
上述说明示出并描述了本发明的优选实施例,如前所述,应当理解本发明并非局限于本文所披露的形式,不应看作是对其他实施例的排除,而可用于各种其他组合、修改和环境,并能够在本文所述发明构想范围内,通过上述教导或相关领域的技术或知识进行改动。而本领域人员所进行的改动和变化不脱离本发明的精神和范围,则都应在本发明所附权利要求的保护范围内。The above description shows and describes the preferred embodiments of the present invention. As mentioned above, it should be understood that the present invention is not limited to the forms disclosed herein, and should not be regarded as excluding other embodiments, but can be used in various other combinations, modifications and environments, and can be modified within the scope of the inventive concept described herein, through the above teachings or technology or knowledge in related fields. However, changes and changes made by those skilled in the art do not depart from the spirit and scope of the present invention, and should all be within the protection scope of the appended claims of the present invention.
Claims (10)
- 根据权利要求1所述的防水透气TPU热熔胶膜,其特征在于,所述溶剂的浓度为0.6~0.9mol/L。The waterproof and breathable TPU hot melt adhesive film according to claim 1, characterized in that the concentration of the solvent is 0.6-0.9 mol/L.
- 根据权利要求1所述的防水透气TPU热熔胶膜,其特征在于,所述氧化石墨烯的浓度为21~25mg/mL。The waterproof and breathable TPU hot-melt adhesive film according to claim 1, wherein the concentration of the graphene oxide is 21-25 mg/mL.
- 根据权利要求1所述的防水透气TPU热熔胶膜,其特征在于,所述致孔剂为聚乙烯吡咯烷酮、聚乙二醇中的至少一种。The waterproof and breathable TPU hot-melt adhesive film according to claim 1, wherein the porogen is at least one of polyvinylpyrrolidone and polyethylene glycol.
- 根据权利要求1所述的防水透气TPU热熔胶膜,其特征在于,所述疏水剂为聚四氟乙烯、聚三氟氯乙烯、聚全氟乙丙烯中的一种或几种。The waterproof and breathable TPU hot-melt adhesive film according to claim 1, wherein the hydrophobic agent is one or more of polytetrafluoroethylene, polychlorotrifluoroethylene, and polyperfluoroethylene propylene.
- 根据权利要求1所述的防水透气TPU热熔胶膜,其特征在于,所述还原剂为葡萄糖、二甲基胺硼烷中的一种或两种。The waterproof and breathable TPU hot-melt adhesive film according to claim 1, wherein the reducing agent is one or both of glucose and dimethylamine borane.
- 根据权利要求1所述的防水透气TPU热熔胶膜,其特征在于,所述光稳定剂为癸二酸二(2,2,6,6-四甲基-4-哌啶)酯、聚[[6-[(1,1,3,3-四甲基丁基)胺]-1,3,5-三嗪-2,4-二基][(2,2,6,6-四甲基-4-哌啶)亚胺]-1,6-二己二基[(2,2,6,6-四甲基-4-哌啶)亚胺]]]、双(1,2,2,6,6-五甲基-4-哌啶基)癸二酸酯中的任意一种或至少两种的混合物。The waterproof and breathable TPU hot-melt adhesive film according to claim 1, wherein the light stabilizer is bis(2,2,6,6-tetramethyl-4-piperidine) sebacate, poly[[6-[(1,1,3,3-tetramethylbutyl)amine]-1,3,5-triazine-2,4-diyl][(2,2,6,6-tetramethyl-4-piperidine)imine]-1,6-dihexanediyl[(2,2, Any one of 6,6-tetramethyl-4-piperidinyl)imine]]], bis(1,2,2,6,6-pentamethyl-4-piperidinyl) sebacate or a mixture of at least two.
- 一种防水透气TPU热熔胶膜的制备方法,其特征在于,包括如下步骤:A kind of preparation method of waterproof breathable TPU hot-melt adhesive film is characterized in that, comprises the steps:S1、将氧化石墨烯分散在水中,然后加入过氧化氢溶液,110~120℃反应1h~8h,反应完成后加入还原剂继续反应3~4h后离心或过滤收集固体产物,得到多孔石墨烯;S1. Disperse graphene oxide in water, then add hydrogen peroxide solution, and react at 110-120°C for 1h-8h. After the reaction is completed, add a reducing agent to continue the reaction for 3-4h, then centrifuge or filter to collect the solid product to obtain porous graphene;S2、将步骤S1中的多孔石墨烯分散在溶剂中,然后加入疏水剂,反应30~60min后,加入适量的致孔剂,搅拌均匀得到改性多孔石墨烯分散液;S2, dispersing the porous graphene in step S1 in a solvent, then adding a hydrophobic agent, after reacting for 30 to 60 minutes, adding an appropriate amount of porogen, and stirring evenly to obtain a modified porous graphene dispersion;S3、将TPU置于溶剂中,然后在95~100℃进行搅拌,溶解完全;S3. Put the TPU in the solvent, and then stir at 95-100°C to dissolve completely;S4、将步骤S2的多孔石墨烯分散液与步骤S3的TPU溶液混合,再加入光稳定剂,搅拌均匀后,在0.07~0.1MPa下脱泡35~50min,将脱泡后的混合溶液通过涂布的方式均匀涂布在离型纸上,然后将涂布后的离型纸送入烘箱中进行烘干干燥,将干燥后的产品常温固化,完全固化后即可得到防水透气TPU热熔胶膜。S4. Mix the porous graphene dispersion in step S2 with the TPU solution in step S3, add a light stabilizer, stir evenly, and defoam at 0.07 to 0.1 MPa for 35 to 50 minutes. Apply the defoamed mixed solution evenly on the release paper by coating, then send the coated release paper into an oven for drying and drying, and cure the dried product at room temperature. After complete curing, a waterproof and breathable TPU hot melt adhesive film can be obtained.
- 根据权利要求8所述的防水透气TPU热熔胶膜的制备方法,其特征在于,在所述步骤S4中,所述涂布的间隙为0.6-1mm。The method for preparing a waterproof and breathable TPU hot-melt adhesive film according to claim 8, characterized in that, in the step S4, the coating gap is 0.6-1 mm.
- 根据权利要求8所述的防水透气TPU热熔胶膜的制备方法,其特征在于,在所述步骤S4中,所述烘箱的温度设为130-150℃。The method for preparing a waterproof and breathable TPU hot-melt adhesive film according to claim 8, characterized in that, in the step S4, the temperature of the oven is set at 130-150°C.