WO2023106850A1 - 고체 전해질 및 이의 제조방법 - Google Patents
고체 전해질 및 이의 제조방법 Download PDFInfo
- Publication number
- WO2023106850A1 WO2023106850A1 PCT/KR2022/019896 KR2022019896W WO2023106850A1 WO 2023106850 A1 WO2023106850 A1 WO 2023106850A1 KR 2022019896 W KR2022019896 W KR 2022019896W WO 2023106850 A1 WO2023106850 A1 WO 2023106850A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- solid electrolyte
- coating
- weight
- film
- conductive polymer
- Prior art date
Abstract
Description
고체 전해질 | ||||
혼합 전도성 고분자 | 무기물 | 리튬염 | 중량비 (혼합 전도성 고분자:리튬염:무기) |
|
실시예 1 | PEDOT:PSS | ZnO | LiTFSI | 27.5 : 55 : 1 |
실시예 2 | PEDOT:PSS | ZnO | LiTFSI | 11 : 22 : 1 |
실시예 3 | PEDOT:PSS | SiO2 | LiTFSI | 11 : 22 : 1 |
실시예 4 | 폴리피롤 | ZnO | LiTFSI | 11 : 22 : 1 |
비교예 1 | PEO | - | LiTFSI | 10 : 1 |
비교예 2 | PEDOT:PSS | - | - | - |
비교예 3 | - | ZnO | - | - |
비교예 4 | - | SiO2 | - | - |
비교예 5 | PEDOT:PSS | ZnO | - | 11 : 1 |
비교예 6 | - | ZnO | LiTFSI | 22 : 1 |
측정온도 (℃) |
두께 (㎛) |
이온 전도도 (S/cm) |
전기 전도도 (S/cm) |
|
실시예 1 | 25 | 23 | 3.28 x 10-5 | 2.595 x 10-5 |
실시예 2 | 25 | 19 | 3.59 x 10-5 | 2.824 x 10-5 |
실시예 3 | 25 | 22 | 3.55 x 10-5 | 2.799 x 10-5 |
실시예 4 | 25 | 45 | 9.12 x 10-6 | 2.775 x 10-7 |
비교예 1 | 25 | 43 | 9.26 x 10-8 | 8.778 x 10-11 |
비교예 2 | 25 | 11 | - | 2.716 x 10-6 |
비교예 3 | 25 | 689 | - | - |
비교예 4 | 25 | 721 | - | - |
비교예 5 | 25 | 32 | - | - |
비교예 6 | 25 | 755 | - | - |
Claims (18)
- 이온 전도도 및 전기 전도도 특성을 가지는 혼합 전도성 고분자, 무기물 및 리튬염을 포함하는 고체 전해질.
- 제1항에 있어서,상기 혼합 전도성 고분자는 폴리(3,4-에틸렌디옥시티오펜):폴리(스티렌설포네이트)(PEDOT:PSS, poly(3,4-ethylenedioxythiophene) : poly(styrenesulfonate)), 폴리아세틸렌(polyacetylene), 폴리파라페닐렌(poly(paraphenylene)), 폴리파라페닐렌 설파이드(poly(paraphenylene) sulfide), 폴리씨오펜(polythiophene), 폴리피롤(polypyrrole), 폴리이소시아나프탈렌(polyisothianaphtalene), 폴리파라페닐렌비닐렌(poly(paraphenylene vinylene)), 폴리아닐린(polyaniline) 및 폴리(3,4-에틸렌디옥시티오펜)(poly(3,4-ethylenedioxythiophene))로 이루어진 군에서 선택된 1종 이상을 포함하는 것인, 고체 전해질.
- 제1항에 있어서,상기 무기물은 산화물계 무기물, 질화물계 무기물 및 카바이드계 무기물로 구성된 군에서 선택되는 1종 이상을 포함하는 것인, 고체 전해질.
- 제3항에 있어서,상기 산화물계 무기물은 TiO2, ZnO2, ZnO, SrTiO3, ZrPO4, BaTiO3, KNbO3, Fe2O3, Ta2O5, WO3, SnO2, Bi2O3, NiO, Cu2O, SiO, SiO2, MoS2, RuO2 및 CeO2로 이루어진 군에서 선택되는 1종 이상을 포함하고,상기 질화물계 무기물은 AIN(Aluminium Nitride), BN(Boron Nitride) 및 Si2N4(Silicon Nitride)로 이루어진 군에서 선택되는 1종 이상을 포함하고,상기 카바이드계 무기물은 CuC, AgC 및 AuC로 이루어진 군에서 선택되는 1종 이상을 포함하는 것인, 고체 전해질.
- 제1항에 있어서,상기 리튬염은 LiTFSI(Lithium bis(trifluoromethanesulphonyl)imide), LiFSI(Lithium bis(fluorosulfonyl)imide), LiNO3, LiOH, LiCl, LiBr, LiI, LiClO4, LiBF4, LiB10Cl10, LiPF6, LiCF3SO3, LiCF3CO2, LiAsF6, LiSbF6, LiAlCl4, CH3SO3Li, CF3SO3Li, LiSCN, LiC(CF3SO2)3, (CF3SO2)2NLi 및 (FSO2)2NLi으로 이루어진 군에서 선택되는 1종 이상을 포함하는 것인, 고체 전해질.
- 제1항에 있어서,상기 고체 전해질은상기 혼합 전도성 고분자 100 중량부와, 상기 혼합 전도성 고분자 100 중량부에 대하여 무기물 2 내지 30 중량부, 및 리튬염 5 내지 300 중량부를 포함하는 것인, 고체 전해질.
- 제1항에 있어서,상기 고체 전해질은상기 혼합 전도성 고분자 100 중량부와, 상기 혼합 전도성 고분자 100 중량부에 대하여 바인더 2 내지 30 중량부, 및 리튬염 100 내지 300 중량부를 포함하는 것인, 고체 전해질.
- 제1항에 있어서,상기 고체 전해질은, 혼합 전도성 고분자와 무기물을 포함하는 혼합 전도성 고분자 매트릭스 내부에 리튬염이 해리되어 포함된 형태인 것인, 고체 전해질.
- 제1항에 있어서,상기 고체 전해질은 고체 전해질막 형태인 것인, 고체 전해질.
- 제1항에 있어서,상기 고체 전해질의 두께는 10 내지 60 ㎛ 인 것인, 고체 전해질.
- (S1) 혼합 전도성 고분자, 무기물 및 리튬염을 용매에 첨가하여 얻은 혼합용액을 기재 상에 코팅하는 단계; 및(S2) 상기 (S1) 단계에서 얻어진 코팅층을 건조하는 단계;를 포함하는 제1항에 따른 고체 전해질의 제조방법.
- 제11항에 있어서,상기 코팅 방법은 바코팅(bar coating), 롤코팅(roll coating), 스핀코팅(spin coating), 슬릿코팅(slit coating), 다이코팅(die coating), 블레이드코팅(blade coating), 콤마코팅(comma coating), 슬롯다이코팅(slot die coating), 립코팅(lip coating) 또는 솔루션캐스팅(solution casting)인 것인, 고체 전해질의 제조방법.
- 제11항에 있어서,상기 건조는 300℃ 이하에서 수행되는 것인, 고체 전해질의 제조방법.
- 제11항에 있어서,상기 기재는 스테인레스 스틸(Stainless Steel), 폴리에틸렌테레프탈레이트 필름, 폴리테트라플로오루에틸렌 필름, 폴리에틸렌 필름, 폴리프로필렌 필름, 폴리부텐 필름, 폴리부타디엔 필름, 염화비닐 공중합체 필름, 폴리우레탄 필름, 에틸렌-비닐 아세테이트 필름, 에틸렌-프로필렌 공중합체 필름, 에틸렌-아크릴산 에틸 공중합체 필름, 에틸렌-아크릴산 메틸 공중합체 필름 또는 폴리이미드 필름인 것인, 고체 전해질의 제조방법.
- 제11항에 있어서,상기 용매는 디메틸 술폭사이드(dimethylsulfoxide, DMSO), 이소프로필 알코올(isopropyl alcohol), N-메틸피롤리돈(NMP), 아세톤(acetone), 자일렌(xylene), 디메틸포름아마이드(N,N-Dimethylmethanamide, DMF), 벤젠(benzene), 테트라하이드로퓨란(tetrahydrofuran, THF) 및 물로 이루어진 군에서 선택된 1종 이상인 것인, 고체 전해질의 제조방법.
- 제1항의 고체 전해질을 포함하는 코팅층이 형성된 전고체 전지용 전극.
- 제16항에 있어서, 상기 전극은 양극 또는 음극인 것인, 전극.
- 제16항의 전극을 포함하는, 전고체 전지.