WO2023105206A1 - Printing ink - Google Patents
Printing ink Download PDFInfo
- Publication number
- WO2023105206A1 WO2023105206A1 PCT/GB2022/053096 GB2022053096W WO2023105206A1 WO 2023105206 A1 WO2023105206 A1 WO 2023105206A1 GB 2022053096 W GB2022053096 W GB 2022053096W WO 2023105206 A1 WO2023105206 A1 WO 2023105206A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- ink
- inkjet ink
- inkjet
- radiation
- Prior art date
Abstract
The present invention provides an inkjet ink comprising: a radiation-curable material; 2% by weight or more of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 2% by weight or more in total of one or more polymeric thioxanthone photoinitiators; and 4% by weight or more of, wherein the amounts are based on the total weight of the ink. The present invention also provides a method of inkjet printing comprising inkjet printing the inkjet ink of the present invention onto a substrate and curing the inkjet ink by exposing the inkjet ink to a curing source.
Description
Printing ink
The present invention relates to a printing ink and, in particular, to an inkjet ink which is suitable for food packaging applications.
In inkjet printing, minute droplets of black, white or coloured ink are ejected in a controlled manner from one or more reservoirs or printing heads through narrow nozzles on to a substrate, which is moving relative to the reservoirs. The ejected ink forms an image on the substrate.
For high-speed printing, the inks must flow rapidly from the printing heads, and, to ensure that this happens, they must have in use a low viscosity, typically 200 mPas or less at 25°C, although in most applications the viscosity should be 50 mPas or less, and often 25 mPas or less. Typically, when ejected through the nozzles, the ink has a viscosity of less than 25 mPas, preferably 5-15 mPas and most preferably between 7-1 1 mPas at the jetting temperature, which is often elevated to, but not limited to 40-50°C (the ink might have a much higher viscosity at ambient temperature). The inks must also be resistant to drying or crusting in the reservoirs or nozzles. For these reasons, inkjet inks for application at or near ambient temperatures are commonly formulated to contain a large proportion of a mobile liquid vehicle or solvent such as water or a low-boiling solvent or mixture of solvents.
Another type of inkjet ink contains unsaturated organic compounds, termed monomers and/or oligomers, which polymerise when cured. This type of ink has the advantage that it is not necessary to evaporate the liquid phase to dry the print; instead the print is cured, a process which is more rapid than evaporation of solvent at moderate temperatures.
Inkjet inks can be printed onto a variety of substrates. Particularly challenging substrates for inkjet printing thereon are substrates for food packaging.
Food packaging represents a particular challenge because of the strict safety limitations on the properties of materials that come into contact with food, including indirect additives like packaging inks. Accordingly, for printed food packaging, it is necessary to control and quantify the migration and/or odour of the components of the printed image on the food packaging into the food products. Specific exclusions based on their odour and/or migration properties include volatile organic solvents and many monomers typically used in curable inks.
It is also advantageous for an inkjet ink to have a high cure speed for food packaging applications, in particular for single pass printing onto food packaging. By cure speed is meant the speed at which the actinic radiation source moves relative to the substrate. An advantage of a high cure speed is that a low dose per unit area is required to achieve a fully cured film.
There are a number of sources of actinic radiation, which are commonly used to cure inkjet inks which contain radiation-curable material. The most common source of radiation is a UV source. UV sources include mercury discharge lamps, fluorescent tubes, light emitting diodes (LEDs), flash lamps and combinations thereof.
Mercury discharge lamps, fluorescent tubes and flash lamps are traditionally used as the radiation source as they have an impressive UV output performance. However, these radiation sources have several drawbacks in their operational characteristics, and LED UV light sources are an attractive alternative. In particular, when compared to, for example mercury discharge lamps (the most common UV light source used to cure inkjet inks), LEDs offer significant cost reduction, longer maintenance intervals, higher energy efficiency and are an environmentally friendlier solution. However, there are a number of challenges when utilising LED UV light sources as the radiation source.
When LEDs are used, it is necessary to use an array of multiple LEDs in order to generate enough power to provide thorough curing of the ink. In fact, even with an array of multiple LEDs, inks which are cured by LEDs are prone to poor surface cure owing to the presence of oxygen in the atmosphere adjacent to the ink surface, and the spectral output of LEDs. Compared to conventional mercury lamp UV sources, LEDs have a narrow spectral output. The UV output of LED lamps is essentially monochromatic and most commercial devices operate at 385, 395 or 405 nm. LEDs emit radiation in the UVA region having a long wavelength over a narrow range of wavelengths, which although suitable for depth cure, provides a particular challenge for effective surface cure in normal atmospheric conditions.
Poor surface cure can be reduced in a number of ways. First, it can be overcome by blanketing the irradiated area with an inert gas such as nitrogen during the cure process but this adds considerably to the complexity and cost of the printer. Secondly, it can be overcome by working the LEDs at high power, providing more energy to react with the photoinitiators and oxygen, or the total amount of photoinitiators may be increased, thus allowing more radicals to be generated. However, working the LEDs at high power generates heat, which must be removed and both approaches add to the cost and complexity of the process - regard must be had to limitations on the media range, power consumption, ink viscosity and ink stability. Thirdly, a blend of photoinitiators may be used. However, there are a limited number of blends of photoinitiators that are suitable for food packaging applications.
There is therefore a need in the art for an inkjet ink which is suitable for food packaging, which has a high UV LED cure speed and good surface cure, whilst maintaining a low viscosity.
Accordingly, the present invention provides an inkjet ink comprising: a radiation-curable material; 2% by weight or more of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 2% by weight or more in total of one or more polymeric thioxanthone photoinitiators; and 4% by weight or more of
wherein the amounts are based on the total weight of the ink.
The inventors have surprisingly found that the inclusion of the specific blend of photoinitiators in the specific amounts provides an inkjet ink that can be printed onto food packaging and which has a high UV LED cure speed and good surface cure, whilst maintaining a low viscosity.
For the avoidance of doubt, the amounts disclosed herein are to be given their standard interpretation, e.g. an amount of 2% by weight includes 1 .5 to 2.4% by weight.
The inkjet ink of the present invention comprises a radiation-curable material.
The radiation-curable material is not particularly limited and the formulator is free to include any such radiation-curable material in the ink of the present invention to improve the properties or performance of the ink. This radiation-curable material can include any radiation-curable material readily available and known in the art in inkjet inks. By “radiation-curable” is meant a material that polymerises and/or crosslinks upon irradiation, for example, when exposed to actinic radiation, in the presence of a photoinitiator.
The amount of radiation-curable material is not limited other than by the constraints imposed by the use in an inkjet ink, such as viscosity, stability, toxicity etc. In a preferred embodiment, the inkjet ink comprises 20 to 85% by weight of radiation-curable material, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises radiation-curable material that is suitable for printing onto food packaging.
In a preferred embodiment, the inkjet ink comprises a radiation-curable monomer. As is known in the art, monomers may possess different degrees of functionality, which include mono, di, tri and higher functionality monomers.
In a preferred embodiment, the inkjet ink comprises a di- and/or multifunctional radiation-curable monomer.
For the avoidance of doubt, mono and difunctional are intended to have their standard meanings, i.e. one or two groups, respectively, which take part in the polymerisation reaction on curing. Multifunctional (which does not include difunctional) is intended to have its standard meaning, i.e. three or more groups, respectively, which take part in the polymerisation reaction on curing.
In a preferred embodiment, the radiation-curable monomer is a di-, tri-, tetra-, penta- or hexafunctional monomer, i.e. the radiation curable monomer has two, three, four, five or six functional groups. In a particularly preferred embodiment, the inkjet ink comprises a difunctional monomer. In a particularly preferred embodiment, the inkjet ink comprises at least two di- and/or multifunctional radiation-curable monomers and more preferably, at least two difunctional monomers.
The functional group of the di- and/or multifunctional radiation-curable monomer, which is utilised in the ink of the present invention may be the same or different but must take part in the polymerisation reaction on curing. Examples of such functional groups include any groups that are capable of polymerising upon exposure to radiation and are preferably selected from a (meth)acrylate group and a vinyl ether group.
The di- and/or multifunctional radiation-curable monomer may possess different degrees of functionality, and a mixture including combinations of di, tri and higher functionality monomers may be used.
The substituents of the di- and/or multifunctional radiation-curable monomer are not limited other than by the constraints imposed by the use in an ink-jet ink, such as viscosity, stability, toxicity etc. The substituents are typically alkyl, cycloalkyl, aryl and combinations thereof, any of which may be interrupted by heteroatoms. Non-limiting examples of substituents commonly used in the art include C1-18 alkyl, C3-18 cycloalkyl, CB- aryl and combinations thereof, such as Cs- aryl- or C3-18 cycloalkyl-substituted C1-18 alkyl, any of which may be interrupted by 1-10 heteroatoms, such as oxygen or nitrogen, with nitrogen further substituted by any of the above described substituents. The substituents may together also form a cyclic structure.
In a preferred embodiment, the inkjet ink comprises 5 to 85% by weight of a di- and/or multifunctional radiation-curable monomer, based on the total weight of the ink.
Examples of the di- and/or multifunctional radiation-curable monomer include difunctional (meth)acrylate monomers, multifunctional (meth)acrylate monomers, divinyl ether monomers, multifunctional vinyl ether monomers and di- and/or multifunctional vinyl ether (meth)acrylate monomers. Mixtures of di- and/or multifunctional radiation-curable monomers may also be used.
In a preferred embodiment, the radiation-curable material comprises a (meth)acrylate monomer, more preferably a di- and/or multifunctional (meth) acrylate monomer. In a particularly preferred embodiment, the inkjet ink comprises a difunctional (meth)acrylate monomer.
For the avoidance of doubt, (meth)acrylate is intended herein to have its standard meaning, i.e. acrylate and/or methacrylate.
Difunctional (meth)acrylate monomers are well known in the art and a detailed description is therefore not required. Examples include hexanediol diacrylate (HDDA), 1 ,8-octanediol diacrylate, 1 ,9-nonanediol diacrylate, 1 ,10-decanediol diacrylate (DDDA), 1 ,11-undecanediol diacrylate and 1 ,12-dodecanediol diacrylate, polyethylene glycol diacrylate (for example tetraethylene glycol diacrylate, PEG200DA, PEG300DA, PEG400DA, PEG600DA), dipropylene glycol diacrylate (DPGDA), tripropylene glycol diacrylate (TPGDA), tricyclodecane dimethanol diacrylate (TCDDMDA), neopentylglycol diacrylate, 3-methyl-1 ,5-pentanediol diacrylate (3-MPDA), and the acrylate esters of ethoxylated or propoxylated glycols and polyols, for example, propoxylated neopentylglycol diacrylate (NPGPODA), and mixtures thereof. Also included are esters of methacrylic acid (i.e. methacrylates), such as hexanediol dimethacrylate, 1 ,8-octanediol dimethacrylate, 1 ,9-nonanediol dimethacrylate, 1 ,10-decanediol dimethacrylate, 1 ,11- undecanediol dimethacrylate and 1 ,12-dodecanediol dimethacrylate, triethyleneglycol dimethacrylate, diethyleneglycol dimethacrylate, ethyleneglycol dimethacrylate, 1 ,4-butanediol dimethacrylate and mixtures thereof. 3-MPDA is particularly preferred.
Preferably, the inkjet ink comprises 5 to 85% by weight, more preferably 25-80% by weight, more preferably 40-75% by weight of a difunctional (meth)acrylate monomer, based on the total weight of the ink.
The inkjet ink may comprise a multifunctional (meth)acrylate monomer.
Suitable multifunctional (meth)acrylate monomers (which do not include difunctional (meth)acrylate monomers) include tri-, tetra-, penta-, hexa-, hepta- and octa-fu notional monomers. Examples of the multifunctional acrylate monomers that may be included in the inkjet inks include trimethylolpropane triacrylate, dipentaerythritol triacrylate, tri(propylene glycol) triacrylate, bis(pentaerythritol) hexaacrylate, and the acrylate esters of ethoxylated or propoxylated glycols and polyols, for example, ethoxylated trimethylolpropane triacrylate and ethoxylated pentaerythritol tetraacrylate (EOPETTA, also known as PPTTA), and mixtures thereof. Suitable multifunctional (meth)acrylate monomers also include esters of methacrylic acid (i.e. methacrylates), such as trimethylolpropane trimethacrylate. Mixtures of (meth)acrylates may also be used.
The amount of the multifunctional (meth)acrylate monomer, when present, is preferably 5-25% by weight, based on the total weight of the ink.
The di- and/or multifunctional radiation-curable monomer may have at least one vinyl ether functional group.
In a preferred embodiment, the inkjet ink comprises a divinyl ether monomer, a multifunctional vinyl ether monomer, a divinyl ether (meth)acrylate monomer and/or a multifunctional vinyl ether (meth)acrylate monomer. In a particularly preferred embodiment, the inkjet ink comprises a divinyl ether monomer.
Examples of a divinyl ether monomer include triethylene glycol divinyl ether (DVE-3), diethylene glycol divinyl ether, 1 ,4-cyclohexanedimethanol divinyl ether, bis[4-(vinyloxy)butyl] 1 ,6- hexanediylbiscarbamate, bis[4-(vinyloxy)butyl] isophthalate, bis[4-(vinyloxy)butyl] (methylenedi- 4,1-phenylene)biscarbamate, bis[4-(vinyloxy)butyl] succinate, bis[4-(vinyloxy)butyl]terephthalate, bis[4-(vinyloxymethyl)cyclohexylmethyl] glutarate, 1 ,4-butanediol divinyl ether and mixtures thereof. Triethylene glycol divinyl ether (DVE-3) is particularly preferred.
An example of a multifunctional vinyl ether monomer is tris[4-(vinyloxy)butyl] trimellitate.
Examples of a vinyl ether (meth)acrylate monomer include 2-(2-vinyloxy ethoxy)ethyl acrylate (VEEA), 2-(2-vinyloxy ethoxy)ethyl methacrylate (VEEM) and mixtures thereof.
In a preferred embodiment, the di- and/or multifunctional radiation-curable monomer is selected from 1 ,10-decanediol diacrylate (DDDA), hexanediol diacrylate (HDDA), polyethylene glycol diacrylate, tripropylene glycol diacrylate (TPGDA), 3-methyl 1 ,5- pentanediol diacrylate (3-MPDA), dipropylene glycol diacrylate (DPGDA), tricyclodecane dimethanol diacrylate (TCDDMDA), propoxylated neopentyl glycol diacrylate (NPGPODA), trimethylolpropane triacrylate (TMPTA), ditrimethylolpropane tetraacrylate (DiTMPTA), di-pentaerythritol hexaacrylate (DPHA), ethoxylated trimethylolpropane triacrylate (EOTMPTA), ethoxylated pentaerythritol tetraacrylate (EOPETTA), triethylene glycol divinyl ether (DVE-3) and mixtures thereof.
In a preferred embodiment, the di- and/or multifunctional radiation-curable monomer is preferably selected from 1 ,10-decanediol diacrylate (DDDA), ethoxylated (5) hexanediol diacrylate (HD(EO)DA), polyethylene glycol (600) diacrylate (PEG600DA), tripropylene glycol diacrylate (TPGDA), 3-methyl 1 ,5-pentanediol diacrylate (3-MPDA), tricyclodecane dimethanol diacrylate (TCDDMDA), propoxylated neopentyl glycol diacrylate (NPGPODA), di-trimethylolpropane tetraacrylate (DiTMPTA), di-pentaerythritol hexaacrylate (DPHA), ethoxylated trimethylolpropane triacrylate (EOTMPTA), ethoxylated penta erythritol tetraacrylate (EOPETTA), triethylene glycol divinyl ether (DVE-3) and mixtures thereof. These monomers are particularly suitable for food packaging applications, resulting in reduced odour and migration.
In a preferred embodiment, the difunctional monomer, when present, is selected from 1 ,10- decanediol diacrylate (DDDA), hexanediol diacrylate (HDDA), polyethylene glycol diacrylate, tripropylene glycol diacrylate (TPGDA), 3-methyl 1 ,5- pentanediol diacrylate (3-MPDA), dipropylene glycol diacrylate (DPGDA), tricyclodecane dimethanol diacrylate (TCDDMDA), propoxylated neopentyl glycol diacrylate (NPGPODA), triethylene glycol divinyl ether (DVE-3) and mixtures thereof.
The difunctional monomer, when present, is preferably selected from 1 ,10-decanediol diacrylate (DDDA), ethoxylated (5) hexanediol diacrylate (HD(EO)DA), polyethylene glycol (600) diacrylate (PEG600DA), tripropylene glycol diacrylate (TPGDA), 3-methyl 1 ,5-pentanediol diacrylate (3- MPDA), tricyclodecane dimethanol diacrylate (TCDDMDA), propoxylated neopentyl glycol diacrylate (NPGPODA), triethylene glycol divinyl ether (DVE-3) and mixtures thereof. These monomers are particularly suitable for food packaging applications, resulting in reduced odour and migration.
Preferably, the difunctional monomer, when present, comprises 3-methyl 1 ,5-pentanediol diacrylate (3-MPDA).
In a preferred embodiment, the radiation-curable material comprises a difunctional (meth)acrylate monomer and a divinyl ether monomer. Preferably, the radiation-curable material consists of a difunctional (meth)acrylate monomer and a divinyl ether monomer.
In a more preferred embodiment, the radiation-curable material comprises 3-methyl 1 ,5- pentanediol diacrylate (3-MPDA) and triethylene glycol divinyl ether (DVE-3). Preferably, the radiation-curable material consists of 3-methyl 1 ,5-pentanediol diacrylate (3-MPDA) and triethylene glycol divinyl ether (DVE-3).
Monomers typically have a molecular weight of less than 600, preferably more than 200 and less than 450. Monomers are typically added to inkjet inks to reduce the viscosity of the inkjet ink. They therefore preferably have a viscosity of less than 150 mPas at 25°C, more preferably less than 100mPas at 25°C and most preferably less than 20 mPas at 25°C. Monomer viscosities can be measured using an ARG2 rheometer manufactured by T.A. Instruments, which uses a 40 mm oblique 1 2° steel cone at 25°C with a shear rate of 25 s 1 .
The inkjet ink may further comprise a monofunctional monomer, such as a monofunctional (meth)acrylate monomer.
Monofunctional monomers are well known in the art. A radiation-curable monofunctional monomer has one functional group, which takes part in the polymerisation reaction on curing. The
polymerisable groups can be any group that are capable of polymerising upon exposure to radiation and are preferably selected from a (meth)acrylate group and a vinyl ether group.
The substituents of the monofunctional monomer are not limited other than by the constraints imposed by the use in an inkjet ink, such as viscosity, stability, toxicity etc. The substituents are typically alkyl, cycloalkyl, aryl and combinations thereof, any of which may be interrupted by heteroatoms. Non-limiting examples of substituents commonly used in the art include C1-18 alkyl, C3-18 cycloalkyl, CB- aryl and combinations thereof, such as Cs- aryl- or C3-18 cycloalkylsubstituted C1-18 alkyl, any of which may be interrupted by 1-10 heteroatoms, such as oxygen or nitrogen, with nitrogen further substituted by any of the above described substituents. The substituents may together also form a cyclic structure.
The amount of monofunctional monomer, when present, is preferably 1-30% by weight, more preferably 5-25% by weight, based on the total weight of the ink.
The inkjet ink may comprise a monofunctional (meth)acrylate monomer, which are well known in the art and are preferably the esters of acrylic acid. A detailed description is therefore not required. Mixtures of (meth)acrylates may also be used.
The substituents of the monofunctional (meth)acrylate monomer are not limited other than by the constraints imposed by the use in an inkjet ink, such as viscosity, stability, toxicity etc.
The monofunctional (meth)acrylate monomer may be a cyclic monofunctional (meth) acrylate monomer and/or an acyclic-hydrocarbon monofunctional (meth)acrylate monomer.
When present, the monofunctional (meth) acrylate monomer may comprise a cyclic monofunctional (meth)acrylate monomer.
The substituents of the cyclic monofunctional (meth)acrylate monomer are typically cycloalkyl, aryl and combinations thereof, any of which may be interrupted by heteroatoms and/or substituted by alkyl. Non-limiting examples of substituents commonly used in the art include C3-18 cycloalkyl, CB- IO aryl and combinations thereof, any of which may substituted with alkyl (such as C1-18 alkyl) and/or any of which may be interrupted by 1-10 heteroatoms, such as oxygen or nitrogen, with nitrogen further substituted by any of the above described substituents. The substituents may together also form a cyclic structure.
The cyclic monofunctional (meth)acrylate monomer may be selected from isobornyl acrylate (IBOA), phenoxyethyl acrylate (PEA), cyclic TMP formal acrylate (CTFA), tetrahydrofurfuryl acrylate (THFA), (2-methyl-2-ethyl-1 ,3-dioxolane-4-yl)methyl acrylate (MEDA/Medol-10), 4-te/Y- butylcyclohexyl acrylate (TBCHA), 3,3,5-trimethylcyclohexyl acrylate (TMCHA), benzyl acrylate
(BA) and mixtures thereof. Preferably, the cyclic monofunctional (meth)acrylate monomer comprises benzyl acrylate (BA).
When present, the monofunctional (meth)acrylate monomer may comprise an acyclic-hydrocarbon monofunctional (meth) acrylate monomer.
The substituents of the acyclic-hydrocarbon monofunctional (meth)acrylate monomer are typically alkyl, which may be interrupted by heteroatoms. A non-limiting example of a substituent commonly used in the art is C1-18 alkyl, which may be interrupted by 1-10 heteroatoms, such as oxygen or nitrogen, with nitrogen further substituted.
The acyclic-hydrocarbon monofunctional (meth)acrylate monomer contains a linear or branched C6-C20 group. It may be selected from octadecyl acrylate (ODA), 2-(2-ethoxyethoxy)ethyl acrylate, tridecyl acrylate (TDA), isodecyl acrylate (IDA), lauryl acrylate and mixtures thereof. In a preferred embodiment, the acyclic-hydrocarbon monofunctional (meth) acrylate monomer contains a linear C6-C20 group. Preferably, the acyclic-hydrocarbon monofunctional (meth)acrylate monomer comprises lauryl acrylate.
In a preferred embodiment, when present, the monofunctional (meth)acrylate monomer is selected from isobornyl acrylate (IBOA), phenoxyethyl acrylate (PEA), cyclic TMP formal acrylate (CTFA), tetrahydrofurfuryl acrylate (THFA), (2-methyl-2-ethyl-1 ,3-dioxolane-4-yl)methyl acrylate (MEDA/Medol-10), 4-te/Y-butylcyclohexyl acrylate (TBCHA), 3,3,5-trimethylcyclohexyl acrylate (TMCHA), benzyl acrylate (BA), octadecyl acrylate (ODA), 2-(2-ethoxyethoxy)ethyl acrylate, tridecyl acrylate (TDA), isodecyl acrylate (IDA), lauryl acrylate and mixtures thereof.
In a particularly preferred embodiment, when present, the monofunctional (meth)acrylate monomer comprises benzyl acrylate (BA), lauryl acrylate and mixtures thereof. Benzyl acrylate and lauryl acrylate are particularly preferred monofunctional (meth)acrylate monomers for indirect food contact applications owing to their high migration limits.
In a preferred embodiment, the inkjet ink comprises a monofunctional (meth)acrylate monomer present in 1-30% by weight, more preferably 5-25% by weight, based on the total weight of the ink.
Tetrahydrofurfuryl acrylate (THFA) is often used to provide good adhesion to variety of substrates, as well as producing a flexible film which is less liable to cracking and delamination. A further advantage of THFA is that it can solubilise chlorinated polyolefins, which in turn provides good adhesion to polyolefin substrates. However, THFA is a hazardous monomer and bears the GHS hazard statement H314 (Causes severe skin burns and eye damage). There is also growing evidence that it may damage fertility or the unborn child. Thus, there is an urgent need in the art to move away from THFA.
The ink will still function in the presence of tetrahydrofurfuryl acrylate (THFA), in terms of its printing and curing properties. However, to avoid the hazardous nature of THFA, the ink preferably contains less than 2% by weight, more preferably less than 1 % by weight and most preferably is substantially free of THFA, where the amounts are based on the total weight of the ink.
By substantially free is meant that only small amounts will be present, for example as impurities in the radiation-curable materials present or as a component in a commercially available pigment dispersion. In other words, no THFA is intentionally added to the ink. However, minor amounts of THFA, which may be present as impurities in commercially available inkjet ink components, are tolerated. For example, the ink may comprise less than 0.5% by weight of THFA, more preferably less than 0.1 % by weight of THFA, most preferably less than 0.05% by weight of THFA, based on the total weight of the ink. In a preferred embodiment, the inkjet ink is free of THFA.
For food packaging applications, the Swiss Ordinance on Materials and Articles in Contact with Food (SR 817.023.21) sets out provisions for inks. Annex 10 lists permitted substances for the production of food packaging inks. Substances not listed should not be used for food packaging inks. Caution should still be used for some substances on the Swiss Ordinance list and there is some concern about the quality and safety of the monofunctional (meth)acrylate monomers isodecyl acrylate (IDA), octyl acrylate, phenoxyethyl acrylate (PEA) and 2-ethylhexyl acrylate (2- EHA).
The ink preferably contains less than 2% by weight, more preferably less than 1 % by weight and most preferably is substantially free of each of IDA, octyl acrylate, PEA and 2-EHA, where the amounts are based on the total weight of the ink. More preferably, the ink contains less than 5% by weight, more preferably less than 2% by weight, more preferably less than 1 % by weight and most preferably is substantially free of IDA, octyl acrylate, PEA and 2-EHA in combination, where the amounts are based on the total weight of the ink.
By substantially free is meant that only small amounts will be present, for example as impurities in the radiation-curable materials present or as a component in a commercially available pigment dispersion. In other words, no IDA, octyl acrylate, PEA and 2-EHA is intentionally added to the ink. However, minor amounts of IDA, octyl acrylate, PEA and 2-EHA, which may be present as impurities in commercially available inkjet ink components, are tolerated. For example, the ink may comprise less than 0.5% by weight of each of IDA, octyl acrylate, PEA and 2-EHA, more preferably less than 0.1 % by weight of each of IDA, octyl acrylate, PEA and 2-EHA, most preferably less than 0.05% by weight of each of IDA, octyl acrylate, PEA and 2-EHA, based on the total weight of the ink. Preferably, the ink may comprise less than 0.5% by weight of IDA, octyl acrylate, PEA and 2- EHA in combination, more preferably less than 0.1 % by weight of IDA, octyl acrylate, PEA and 2- EHA in combination, most preferably less than 0.05% by weight of IDA, octyl acrylate, PEA and 2-
EHA in combination, based on the total weight of the ink. In a preferred embodiment, the inkjet ink is free of IDA, octyl acrylate, PEA and 2-EHA.
Preferably, the monofunctional (meth) acrylate monomer is the sole monofunctional monomer present in the ink.
The ink may further include at least one N-vinyl amide monomer and/or N-(meth)acryloyl amine monomer.
N-Vinyl amide monomers are well-known monomers in the art. N-Vinyl amide monomers have a vinyl group attached to the nitrogen atom of an amide which may be further substituted in an analogous manner to the (meth)acrylate monomers. Preferred examples are N-vinyl caprolactam (NVC), N-vinyl pyrrolidone (NVP), N-vinyl piperidone, N-vinyl formamide and N-vinyl acetamide.
Similarly, N-acryloyl amine monomers are also well-known in the art. N-Acryloyl amine monomers also have a vinyl group attached to an amide but via the carbonyl carbon atom and again may be further substituted in an analogous manner to the (meth)acrylate monomers. A preferred example is N-acryloylmorpholine (ACMO).
If present, the inkjet ink preferably comprises at least one of NVC and/or ACMO. N-Vinyl amide monomers are particularly preferred, and most preferably NVC.
The inkjet ink may also comprise one or more N-vinyl monomers other than an N-vinyl amide monomer and/or N-(meth)acryloyl amine monomer. Examples include N-vinyl carbazole, N-vinyl indole and N-vinyl imidazole.
In a preferred embodiment, the amount of monofunctional monomers present in the ink is restricted as monofunctional monomers are more prone to migration and odour issues, which is problematic for food packaging applications. Accordingly, in a preferred embodiment, the ink contains less than 5% by weight, more preferably less than 2% by weight, more preferably less than 1 % by weight and most preferably is substantially free of monofunctional monomer, where the amounts are based on the total weight of the ink.
By substantially free is meant that only small amounts will be present, for example as impurities in the radiation-curable materials present or as a component in a commercially available pigment dispersion. In otherwords, no monofunctional monomer is intentionally added to the ink. However, minor amounts of monofunctional monomer, which may be present as impurities in commercially available inkjet ink components, are tolerated. For example, the ink may comprise less than 0.5% by weight of monofunctional monomer, more preferably less than 0.1 % by weight of monofunctional
monomer, most preferably less than 0.05% by weight of monofunctional monomer, based on the total weight of the ink. In a preferred embodiment, the inkjet ink is free of monofunctional monomer.
Preferably, the radiation-curable material consists of radiation-curable monomer. Put another way, the only radiation-curable material that is present in the inkjet ink is preferably radiation-curable monomer. It is surprising that such a fast cure speed can be achieved without recourse to radiation- curable oligomer.
In a preferred embodiment, the inkjet ink of the present invention may further comprise a radiation- curable (i.e. polymerisable) oligomer, such as a (meth)acrylate oligomer. Any radiation-curable oligomer that is compatible with the other ink components is suitable for use in the ink. Preferably, the inkjet ink comprises a (meth)acrylate oligomer.
The term “curable oligomer” has its standard meaning in the art, namely that the component is partially reacted to form a pre-polymer having a plurality of repeating monomer units, which is capable of further polymerisation. The oligomer preferably has a molecular weight of at least 600. The molecular weight is preferably 4,000 or less. Molecular weights (number average) can be calculated if the structure of the oligomer is known or molecular weights can be measured using gel permeation chromatography using polystyrene standards.
The oligomers may possess different degrees of functionality, and a mixture including combinations of mono, di, tri and higher functionality oligomers may be used. The degree of functionality of the oligomer determines the degree of crosslinking and hence the properties of the cured ink. The oligomer is preferably multifunctional meaning that it contains on average more than one reactive functional group per molecule. The average degree of functionality is preferably from 2 to 6.
Oligomers are typically added to inkjet inks to increase the viscosity of the inkjet ink or to provide film-forming properties such as hardness or cure speed. They therefore preferably have a viscosity of 150 mPas or above at 25°C. Preferred oligomers for inclusion in the ink of the invention have a viscosity of 0.5 to 10 Pas at 50°C. Oligomer viscosities can be measured using an ARG2 rheometer manufactured by T.A. Instruments, which uses a 40 mm oblique 12° steel cone at 60°C with a shear rate of 25 s 1.
Radiation-curable oligomers comprise a backbone, for example a polyester, urethane, epoxy or polyether backbone, and one or more radiation-curable groups.
The polymerisable group can be any group that is capable of polymerising upon exposure to radiation. Preferably the oligomers are (meth)acrylate oligomers. The oligomer may include amine functionality, as the amine acts as an activator without the drawback of migration associated with low-molecular weight amines. In a preferred embodiment, the radiation-curable oligomer is amine
modified. In a particularly preferred embodiment, the radiation-curable oligomer is an amine- modified (meth)acrylate oligomer.
Particularly preferred radiation-curable oligomers are di-, tri-, tetra-, penta- or hexa-functional acrylates.
More preferably, the radiation-curable oligomer is an amine-modified acrylate oligomer. A suitable amine-modified polyester acrylate oligomer is commercially available as UVP6600. A suitable amine-modified polyether acrylate oligomer is commercially available as CN3715LM.
Other suitable examples of radiation-curable oligomers include epoxy based materials such as bisphenol A epoxy acrylates and epoxy novolac acrylates, which have fast cure speeds and provide cured films with good solvent resistance. However, for food packaging applications where quality and safety of the materials is a concern, the ink is preferably substantially free of bisphenol A based materials such as bisphenol A epoxy acrylates. Therefore, the ink is preferably substantially free of bisphenol A epoxy acrylates.
By substantially free is meant that only small amounts will be present, for example as impurities in the radiation-curable materials present or as a component in a commercially available pigment dispersion. In other words, no bisphenol A epoxy acrylates is intentionally added to the ink. However, minor amounts of bisphenol A epoxy acrylates which may be present as impurities in commercially available inkjet ink components, are tolerated. For example, the ink may comprise less than 0.5% by weight of bisphenol A epoxy acrylates, more preferably less than 0.1 % by weight of bisphenol A epoxy acrylates, most preferably less than 0.05% by weight of bisphenol A epoxy acrylates, based on the total weight of the ink. In a preferred embodiment, the inkjet ink is free of bisphenol A epoxy acrylates.
The amount of radiation-curable oligomer, when present, is preferably 0.1-10% by weight, based on the total weight of the ink. However, the inclusion of a radiation-curable oligomer is not required to achieve a fast cure speed. Accordingly, in a preferred embodiment, the ink contains less than 10% by weight, preferably less than 5% by weight, more preferably less than 2% by weight, more preferably less than 1 % by weight and most preferably is substantially free of radiation-curable oligomer, where the amounts are based on the total weight of the ink.
By substantially free is meant that only small amounts will be present, for example as impurities in the radiation-curable material present or as a component in a commercially available pigment dispersion. In other words, no radiation-curable oligomer is intentionally added to the ink. However, minor amounts of radiation-curable oligomer, which may be present as impurities in commercially available inkjet ink components, are tolerated. For example, the ink may comprise less than 0.5% by weight, more preferably less than 0.1 % by weight, most preferably less than
0.05% by weight of radiation-curable oligomer, based on the total weight of the ink. In a preferred embodiment, the inkjet ink is free of radiation-curable oligomer.
The inkjet ink of the present invention comprises 2% by weight or more of phenylbis(2,4,6- trimethylbenzoylj-phosphine oxide; 2% by weight or more in total of one or more polymeric thioxanthone photoinitiators; and 4% by weight or more of
wherein the amounts are based on the total weight of the ink.
The inventors have surprisingly found that the inclusion of the specific blend of photoinitiators in the specific amounts provides an inkjet ink that can be printed onto food packaging, and which has a high UV LED cure speed and good surface cure, whilst maintaining low viscosity. Higher molecular weight photoinitiators reduce migration and odour for food packaging applications. This specific blend of photoinitiators surprisingly allows for efficient UV LED curing resulting in high UV LED cure speed and good surface cure, whilst maintaining low viscosity even at such high concentrations.
The inkjet ink of the present invention comprises 2% by weight or more of phenylbis(2,4,6- trimethylbenzoylj-phosphine oxide, based on the total weight of the ink.
Phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide has the structure
and is known as BAPO. It is commercially available as Omnirad 819 from IGM with CAS number 162881-26-7.
The inkjet ink of the present invention comprises 2% by weight or more of phenylbis(2,4,6- trimethylbenzoylj-phosphine oxide, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 3% by weight or more, more preferably 4% by weight or more of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 6% by weight, more preferably 3 to 6% by weight, and most preferably 4 to 6% by weight of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide,
based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 5% by weight, preferably 3 to 5% by weight, most preferably 4 to 5% by weight of phenylbis(2,4,6- trimethylbenzoyl)-phosphine oxide, based on the total weight of the ink.
The inventors have found that the presence of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide, in the claimed amount, boosts UV LED cure speed and surface cure. The inventors found that reduced UV LED cure speed and surface cure is provided when phenylbis(2,4,6-trimethylbenzoyl)- phosphine oxide is absent or when there is a reduced amount of phenylbis(2,4,6-trimethylbenzoyl)- phosphine oxide present. Phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide is also suitable for food packaging, having a high molecular weight, resulting in reduced migration and odour issues. Further, a low viscosity ink can be achieved, even with the high amount of the claimed photoinitiators present.
The inkjet ink of the present invention comprises 2% by weight or more in total of one or more polymeric thioxanthone photoinitiators, based on the total weight of the ink.
By a polymeric thioxanthone photoinitiator is meant a photoinitiator comprising two or more thioxanthone units connected by a linking unit.
R1, R2, R3, R4, R5, R6, R7 and R8 are not limited other than by the constraints imposed by the use in an ink-jet ink, such as viscosity, stability, toxicity etc. Preferably however, R1, R2, R3, R4, R5, R6, R7 and R8 are independently hydrogen, halogen, C1-12 alkyl, C2-12 alkenyl, C2-12 alkynyl, C7-12 aralkyl, C7-12 alkaryl, C6-12 aryl, C5-12 heteroaryl or the linking unit, with the proviso that one of R1, R2, R3, R4, R5, R6, R7 and R8 is the linking unit. More preferably, R2 is hydrogen or halogen, R1, R3, R4, R5 and R7 are hydrogen, and R6 and R8 are independently hydrogen or the linking unit, with the proviso that one of R6 and R8 is the linking unit. Most preferably, R2 is hydrogen or chlorine, and R1, R3, R4, R5 and R7 are hydrogen, and R6 and R8 are independently hydrogen orthe linking unit, with the proviso that one of R6 and R8 is the linking unit.
In a preferred embodiment, R1, R2, R3, R4, R5, R7 and R8 are hydrogen and R6 is the linking unit.
In another preferred embodiment, R2 is chlorine, R1, R3, R4, R5, R6 and R7 are hydrogen and R8 is the linking unit.
In a preferred embodiment, the polymeric thioxanthone photoinitiator has three or more thioxanthone units, more preferably four or more thioxanthone units. Preferably, the polymeric thioxanthone photoinitiator has up to six thioxanthone units. Preferably, the polymeric thioxanthone photoinitiator has two to six thioxanthone units, more preferably two to four thioxanthone units.
The two or more thioxanthone units may be the same or different but preferably they are the same.
The linking unit is a polymer. The polymer is not limited other than by the constraints imposed by the use in an ink-jet ink, such as viscosity, stability, toxicity etc.
Preferably, the linking unit has a core based on a polyhydroxy compound. Non-limiting examples of a polyhydroxy compound include ethylene glycol, propylene glycol, butylene glycol, glycerol, trimethylolpropane, di-trimethylolpropane, pentaerythritol and di-pentaerythritol.
Preferably, the core based on a polyhydroxy compound is connected to the two or more thioxanthone units by an ether linkage, more preferably by *OWC=O, wherein * represents the point of attachment to the thioxanthone unit, W is C1-12 alkylene or C2-12 alkenylene, and the carbonyl carbon is connected to the core based on a polyhydroxy compound.
Preferably, W is C1-10 alkylene or C2-10 alkenylene, more preferably C1-6 alkylene or C2-6 alkenylene. More preferably, Wis (CH)mR9 wherein m is a value from 1 to 6 and R9 is hydrogen, CH3 or CH2CH3. Most preferably, W is CH2.
An optional repeating monomer unit may be present between the core based on a polyhydroxy compound and the ether linkage, more preferably between the core based on a polyhydroxy compound and *OWC=O as defined above.
The repeating monomer unit is not limited other than by the constraints imposed by the use in an ink-jet ink, such as viscosity, stability, toxicity etc. Non-limiting examples include (OCH2CH2)n, (OCH(CH3)CH2)n, or (OCH2CH2CH2CH2)n, wherein n is a value from 1 to 10. For example, the core may be based on pentaerythritol bonded to repeating propylene glycol monomer units via a condensation reaction between the hydroxy groups, which is then connected to the two or more thioxanthone units by an ether linkage, more preferably by *OWC=O as defined above.
Preferably, the linking unit has the structure:
-W. .X. /V. *0 y y o- o o wherein W is C1-12 alkylene or C2-12 alkenylene; X is (OCFhCF nY, (OCH(CH3)CH2)nY, or (OCH2CH2CH2CH2)nY, wherein n is a value from 0 to 10 and Y is O, OCH2CH(OZC=OWO*)CH2OZ, OCH2C(CH2OZC=OWO*)(CH2CH3)CH2OZ,
OCH2C(CH2OZC=OWO*)(CH2C OCH2C(CH2OZC=OWO*)2CH2O wherein W is as defined above
wherein n is as defined above; and * represents the point of attachment to the thioxanthone unit.
Preferably, W is C1-10 alkylene or C2-10 alkenylene, more preferably C1-6 alkylene or C2-6 alkenylene. More preferably, Wis (CH)mR9 wherein m is a value from 1 to 6 and R9 is hydrogen, CH3 or CH2CH3. Most preferably, W is CH2.
In a preferred embodiment, X is (OCH2CH2CH2CH2)nO, wherein n is a value from 0 to 10.
In a particularly preferred embodiment, R1, R2, R3, R4, R5, R7 and R8 are hydrogen, R6 is the linking unit, W is CH2 and X is (OCH2CH2CH2CH2)nO, wherein n is a value from 0 to 10.
In another preferred embodiment, X is (OCH(CH3)CH2)nOCH2C(CH2OZC=OWO*)2CH2OZ, wherein n is a value from 0 to 10, W and Z are as defined above and * represents the point of attachment to the thioxanthone unit. More preferably, X is
(OCH(CH3)CH2)nOCH2C(CH2O(CH2CH(CH3)O)nC=OCH2O*)2CH2O(CH2CH(CH3)O)n, wherein n is a value from 0 to 10 and * represents the point of attachment to the thioxanthone unit. In this embodiment, the total value of n in X is preferably a value from 1 to 20, more preferably from 1 to 15.
In a preferred embodiment, R2 is chlorine, R1, R3, R4, R5, R6 and R7 are hydrogen, R8 is the linking unit, X is (OCH(CH3)CH2)nOCH2C(CH2OZC=OWO*)2CH2OZ, wherein n is a value from 0 to 10, W and Z are as defined above and * represents the point of attachment to the thioxanthone unit. In a particularly preferred embodiment, R2 is chlorine, R1, R3, R4, R5, R6 and R7 are hydrogen, R8 is the linking unit, W is CH2 and X is
(OCH(CH3)CH2)nOCH2C(CH2O(CH2CH(CH3)O)nC=OCH2O*)2CH2O(CH2CH(CH3)O)n, wherein n is a value from 0 to 10 and * represents the point of attachment to the thioxanthone unit. In this embodiment, the total value of n in X is preferably a value from 1 to 20, more preferably from 1 to 15.
Preferably, the one or more polymeric thioxanthone photoinitiators have a molecular weight of more than 500 g/mol, more preferably more than 600 g/mol and most preferably more than 700 g/mol. Preferably, the one or more polymeric thioxanthone photoinitiators have a molecular weight of less than 2000 g/mol, more preferably less than 1500 g/mol and most preferably less than 1000 g/mol. In a preferred embodiment, the one or more polymeric thioxanthone photoinitiators have a molecular weight of more than 500 g/mol to less than 2000 g/mol, more preferably more than 600 g/mol to less than 2000 g/mol and most preferably more than 700 g/mol to less than 2000 g/mol. Molecularweights (number average) can be calculated if the structure of the photoinitiator is known
or molecular weights can be measured using gel permeation chromatography using polystyrene standards.
The inkjet ink of the present invention comprises 2% by weight or more in total of one or more polymeric thioxanthone photoinitiators, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 4% by weight or more, more preferably 6% by weight or more in total of one or more polymeric thioxanthone photoinitiators, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12% by weight, most preferably 6 to 12% by weight in total of one or more polymeric thioxanthone photoinitiators, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10% by weight, most preferably 6 to 10% by weight in total of one or more polymeric thioxanthone photoinitiators, based on the total weight of the ink. Most preferably, the inkjet ink comprises 2 to 8% by weight, more preferably 4 to 8% by weight, most preferably 6 to 8% by weight in total of one or more polymeric thioxanthone photoinitiators, based on the total weight of the ink.
The inventors have found that the presence of one or more polymeric thioxanthone photoinitiators, in the claimed amount, is required to provide high UV LED cure speed and good surface cure. The inventors found that poor UV LED cure speed and surface cure is provided when a polymeric thioxanthone photoinitiator is absent or when there is a reduced amount of polymeric thioxanthone photoinitiator present. Polymeric thioxanthone photoinitiators are also suitable for food packaging, having a high molecular weight, resulting in reduced migration and odour issues. Further, a low viscosity ink can be achieved, even with the high amount of the claimed photoinitiators present.
The polymeric thioxanthone photoinitiator may be used alone or two or more polymeric thioxanthone photoinitiators may be used together. Examples of suitable polymeric thioxanthone photoinitiators that are commercially available include Speedcure 7010 from Lambson, Omnipol TX from IGM, Genopol TX-2 from Rahn and JRCure 1508 from Jiuri.
Preferably, the one or more polymeric thioxanthone photoinitiators comprise
The photoinitiator
wherein a+b+c+d is a value from 1 to 20, is 1 ,3-di({a-[1-chloro-9-oxo-9H-thioxanthen-4- yl)oxy]acetylpoly[oxy(1 -methylethylene)]} oxy)-2,2-bis({a-[1 -chloro-9-oxo-9H-thioxanthen-4- yl)oxy]acetylpoly[oxy(1-methylethylene)]}oxymethyl) propane. This photoinitiator is commercially available as Speedcure 7010 from Lambson. It is also commercially available as Speedcure 7010L from Lambson containing 40% Speedcure 7010 in 60% trimethylolpropane ethoxylate triacrylate.
Speedcure 7010 has the CAS number 1003567-83-6 and trimethylolpropane ethoxylate triacrylate has the CAS number 28961-43-5.
The value of a+b+c+d in the chemical formula of Speedcure 7010 is equal to 1 to 20. In a preferred embodiment, the value of a+b+c+d in the chemical formula of Speedcure 7010 is equal to 1 to 15. The photoinitiator
wherein q is a value from 1 to 10, is a photoinitiator having two repeating thioxanthone monomer units. It is commercially available as Omnipol TX from IGM, with a molecular weight of 790 g/mol and with CAS number 813452-37-8. It is also commercially available as Genopol TX-2 from Rahn, with a molecular weight of 980 g/mol.
The inkjet ink of the present invention preferably comprises 2% by weight or more in total of at least one of Speedcure 7010, Omnipol TX and/or Genopol TX-2, based on the total weight of the ink. By this, it is meant that the inkjet ink may comprise: Speedcure 7010; Omnipol TX; Genopol TX-2; Speedcure 7010 and Omnipol TX; Speedcure 7010 and Genopol TX-2; Omnipol TX and Genopol TX-2; or Speedcure 7010, Omnipol TX and Genopol TX-2. And the total amount of at least one of Speedcure 7010, Omnipol TX and/or Genopol TX-2 in the inkjet ink in combination is preferably 2% by weight or more, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 4% by weight or more, more preferably 6% by weight or more in total of at least one of Speedcure 7010, Omnipol TX and/or Genopol TX-2, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12%, most preferably 6 to 12% by weight in total of at least one of Speedcure 7010, Omnipol TX and/or Genopol TX-2, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10%, most preferably 6 to 10% in total of at least one of Speedcure 7010, Omnipol TX and/or Genopol TX-2, based on the total weight of the ink. Most preferably, the inkjet ink comprises 2 to 8% by weight, more preferably 4 to 8%, most preferably 6 to 8% in total of at least one of Speedcure 7010, Omnipol TX and/or Genopol TX-2, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 2% by weight or more, more preferably 4% by weight or more, most preferably 6% by weight or more of Speedcure 7010, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12% by weight, most preferably 6 to 12% by weight of Speedcure 7010, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10% by weight, most preferably 6 to 10% by weight of Speedcure 7010, based on the total weight of the ink. Most preferably, the inkjet ink comprises 2 to 8% by weight, more preferably 4 to 8% by weight, most preferably 6 to 8% by weight of Speedcure 7010, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 2% by weight or more, more preferably 4% by weight or more, most preferably 6% by weight or more of Omnipol TX, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12% by weight, most preferably 6 to 12% by weight of Omnipol TX, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10% by weight, most preferably 6 to 10% by weight of Omnipol TX, based on the total weight of the ink. Most
preferably, the inkjet ink comprises 2 to 8% by weight, more preferably 4 to 8% by weight, most preferably 6 to 8% by weight of Omnipol TX, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 2% by weight or more, more preferably 4% by weight or more, most preferably 6% by weight or more of Genopol TX-2, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12% by weight, most preferably 6 to 12% by weight of Genopol TX-2, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10% by weight, most preferably 6 to 10% by weight of Genopol TX-2, based on the total weight of the ink. Most preferably, the inkjet ink comprises 2 to 8% by weight, more preferably 4 to 8% by weight, most preferably 6 to 8% by weight of Genopol TX-2, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 2% by weight or more, more preferably 4% by weight or more, most preferably 6% by weight or more in total of Speedcure 7010 and Omnipol TX, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12% by weight, most preferably 6 to 12% by weight in total of Speedcure 7010 and Omnipol TX, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10% by weight, most preferably 6 to 10% by weight in total of Speedcure 7010 and Omnipol TX, based on the total weight of the ink. Most preferably, the inkjet ink comprises 2 to 8% by weight, more preferably 4 to 8% by weight, most preferably 6 to 8% by weight in total of Speedcure 7010 and Omnipol TX, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 2% by weight or more, more preferably 4% by weight or more, most preferably 6% by weight or more in total of Speedcure 7010 and Genopol TX-2, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12% by weight, most preferably 6 to 12% by weight in total of Speedcure 7010 and Genopol TX-2, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10% by weight, most preferably 6 to 10% by weight in total of Speedcure 7010 and Genopol TX-2, based on the total weight of the ink. Most preferably, the inkjet ink comprises 2 to 8% by weight, more preferably 4 to 8% by weight, most preferably 6 to 8% by weight in total of Speedcure 7010 and Genopol TX-2, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 2% by weight or more, more preferably 4% by weight or more, most preferably 6% by weight or more in total of Omnipol TX and Genopol TX-2, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12% by weight, most preferably 6 to 12% by weight in total of Omnipol TX and Genopol TX-2, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10% by weight, most preferably 6 to 10% by weight in total of Omnipol TX and Genopol TX-2, based on the total weight of the ink. Most preferably, the inkjet ink
comprises 2 to 8% by weight, more preferably 4 to 8% by weight, most preferably 6 to 8% by weight in total of Omnipol TX and Genopol TX-2, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises 2% by weight or more, more preferably 4% by weight or more, most preferably 6% by weight or more in total of Speedcure 7010, Omnipol TX and Genopol TX-2, based on the total weight of the ink. Preferably, the inkjet ink comprises 2 to 12% by weight, more preferably 4 to 12% by weight, most preferably 6 to 12% by weight in total of Speedcure 7010, Omnipol TX and Genopol TX-2, based on the total weight of the ink. More preferably, the inkjet ink comprises 2 to 10% by weight, more preferably 4 to 10% by weight, most preferably 6 to 10% by weight in total of Speedcure 7010, Omnipol TX and Genopol TX-2, based on the total weight of the ink. Most preferably, the inkjet ink comprises 2 to 8% by weight, more preferably 4 to 8% by weight, most preferably 6 to 8% by weight in total of Speedcure 7010, Omnipol TX and Genopol TX-2, based on the total weight of the ink.
For the avoidance of doubt, when Speedcure 7010L is used, it is the total amount of photoinitiator (Speedcure 7010) that is relevant when assessing the total amount of Speedcure 7010 present in the ink.
The inventors have found that the presence of at least one of Speedcure 7010, Omnipol TX and/or Genopol TX-2 in the ink, in the claimed amount, is particularly beneficial in providing high UV LED cure speed and good surface cure. Speedcure 7010, Omnipol TX and Genopol TX-2 are also suitable for food packaging, having a high molecular weight, resulting in reduced migration and odour issues. Further, a low viscosity ink can be achieved, even with a high amount of at least one of Speedcure 7010, Omnipol TX and/or Genopol TX-2 present.
The inkjet ink of the present invention comprises 4% by weight or more of
based on the total weight of the ink. This photoinitiator is ethyl (2,4,6-trimethylbenzoyl) phenyl phosphinate and is known as TPO-L. It is commercially available as Speedcure TPO-L from Lambson with CAS number 84434-11-7.
In a preferred embodiment, the ink comprises 4 to 20% by weight, more preferably 4 to 16% by weight of
based on the total weight of the ink.
More preferably, the inkjet ink of the present invention comprises 6 to 20% by weight, more preferably 6 to 16% by weight of ethyl (2,4,6-trimethylbenzoyl) phenyl phosphinate, based on the total weight of the ink. Most preferably, the inkjet ink of the present invention comprises 8 to 20% by weight, more preferably 8 to 16% by weight of ethyl (2,4,6-trimethylbenzoyl) phenyl phosphinate, based on the total weight of the ink.
The inventors have found that the presence of TPO-L in the ink, in the claimed amount, is required to provide high UV LED cure speed and good surface cure. The inventors found that poor UV LED cure speed and surface cure is provided when this photoinitiator is absent or when there is a reduced amount of this photoinitiator present. Further, a low viscosity ink can be achieved, even with the high amount of the claimed photoinitiators present.
In a preferred embodiment, the inkjet ink comprises: 2% by weight or more, preferably 2 to 6% by weight, of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 2% by weight or more, preferably 2 to 12% by weight, in total of one or more polymeric thioxanthone photoinitiators, wherein the one or more polymeric thioxanthone photoinitiators comprise
wherein a+b+c+d is a value from 1 to 20; and 8 to 20% by weight of
wherein the amounts are based on the total weight of the ink. More preferably, the inkjet ink comprises: 2% by weight or more, preferably 2 to 6% by weight, of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 2% by weight or more, preferably 2 to 12% by weight, of
wherein a+b+c+d is a value from 1 to 20; and 8 to 20% by weight of
wherein the amounts are based on the total weight of the ink.
In a preferred embodiment, the inkjet ink comprises: 6 to 10% by weight, more preferably 8% by weight in total of one or more polymeric thioxanthone photoinitiators; and 6 to 10% by weight, more preferably 8% by weight of
wherein the amounts are based on the total weight of the ink. These amounts provide the ideal balance of cure speed and viscosity. More preferably, the inkjet ink comprises: 3 to 6% by weight, more preferably 4 to 5% by weight of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 6 to 10% by weight, more preferably 8% by weight in total of one or more polymeric thioxanthone photoinitiators; and 6 to 10% by weight, more preferably 8% by weight of
wherein the amounts are based on the total weight of the ink. These amounts provide the ideal balance of cure speed and viscosity.
Most preferably, the inkjet ink comprises: 3 to 6% by weight, more preferably 4 to 5% by weight of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 6 to 10% by weight, more preferably 8% by weight of
wherein a+b+c+d is a value from 1 to 20; and 6 to 10% by weight, more preferably 8% by weight of
wherein the amounts are based on the total weight of the ink. These amounts of these photoinitiators provide the ideal balance of cure speed and viscosity.
In a preferred embodiment, the inkjet ink comprises: 4 to 8% by weight, more preferably 6% by weight in total of one or more polymeric thioxanthone photoinitiators; and 10 to 14% by weight, more preferably 12% by weight of
based on the total weight of the ink. These amounts provide the ideal balance of cure speed and viscosity.
More preferably, the inkjet ink comprises: 3 to 6% by weight, more preferably 4 to 5% by weight of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 4 to 8% by weight, more preferably 6% by weight in total of one or more polymeric thioxanthone photoinitiators; and 10 to 14% by weight, more preferably 12% by weight of
based on the total weight of the ink. These amounts provide the ideal balance of cure speed and viscosity.
Most preferably, the inkjet ink comprises: 3 to 6% by weight, more preferably 4 to 5% by weight of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 4 to 8% by weight, more preferably 6% by weight in total of
wherein a+b+c+d is a value from 1 to 20; and 10 to 14% by weight, more preferably 12% by weight of
based on the total weight of the ink. These amounts of these photoinitiators provide the ideal balance of cure speed and viscosity.
In another preferred embodiment, the ink comprises one or more additional photoinitiators. By an additional photoinitiator is meant a photoinitiator other than phenylbis(2,4,6-trimethylbenzoyl)- phosphine oxide, the one or more polymeric thioxanthone photoinitiators and TPO-L. The one or more additional photoinitiators are not particularly limited.
Preferred one or more additional photoinitiators are photoinitiators which produce free radicals on irradiation (free radical photoinitiators) such as, for example, benzophenone, 1 -hydroxycyclohexyl phenyl ketone, 2-benzyl-2-dimethylamino-(4-morpholinophenyl)butan-1-one, benzil dimethylketal, diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO), 1-[4-(2-hydroxyethoxyl)-phenyl]-2- hydroxy-2-methylpropanone (Omnirad 2959), 2-hydroxy-1-[4-[4-(2-hydroxy-2- methylpropanoyl)phenoxy]phenyl]-2-methylpropan-1-one (KIP160), polyethylene glycol di (0-4[4- (2-dimethylamino-2-benzyl)butaonylphenyl] piperazine) propionate (Omnipol 910) or mixtures
thereof. Such photoinitiators are known and commercially available such as, for example, under the trade names Omnirad (from IGM) and Esacure (from Lamberti).
Preferably, the ink further comprises two or more additional photoinitiators. In a preferred embodiment, the ink contains up to five photoinitiators.
In a preferred embodiment, the ink comprises 8-50% by weight in total of all photoinitiators, more preferably 8-45% by weight, most preferably 8-35% by weight, based on the total weight of the ink. The present inventors have found that it is possible to achieve a low viscosity inkjet ink, despite such a high amount of photoinitiators being present, through the use of the claimed blend of photoinitiators.
In a preferred embodiment, the inkjet ink preferably contains less than 5% by weight, more preferably less than 2% by weight, more preferably less than 1 % by weight, and more preferably is substantially free of any additional photoinitiators. The ink is therefore preferably substantially free of any photoinitiators, other than phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide, the one or more polymeric thioxanthone photoinitiators and TPO-L. Put another way, in a preferred embodiment, phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide, the one or more polymeric thioxanthone photoinitiators and TPO-L are the only photoinitiators present in the inkjet ink.
By substantially free is meant that only small amounts will be present, for example as impurities in the radiation-curable materials present. In other words, no additional photoinitiator is intentionally added to the ink. However, minor amounts of additional photoinitiator, which may be present as impurities in commercially available inkjet ink components, are tolerated. For example, the ink may comprise less than 0.5% by weight of additional photoinitiator, more preferably less than 0.1 % by weight of additional photoinitiator, most preferably less than 0.05% by weight of additional photoinitiator, based on the total weight of the ink. In a preferred embodiment, the inkjet ink is free of additional photoinitiator.
The ink may also contain a resin. The resin preferably has a weight-average molecular weight of 20-200 KDa and preferably 20-60 KDa, as determined by GPC with polystyrene standards. The resin is preferably solid at 25°C. It is preferably soluble in the liquid medium of the ink (the radiation- curable diluent and, when present, additionally the solvent).
The resin is a passive (i.e. inert) resin, in the sense that it is not radiation curable and hence does not undergo cross-linking under the curing conditions to which the ink is subjected.
The resin may improve adhesion of the ink to the substrate. It is preferably soluble in the ink. The resin, when present, is preferably present at 0.1-5% by weight, based on the total weight of the ink.
In a preferred embodiment, the inkjet ink of the present invention also includes a colouring agent, which may be either dissolved or dispersed in the liquid medium of the ink. The colouring agent can be any of a wide range of suitable colouring agents that would be known to the person skilled in the art.
Preferably, the colouring agent is a pigment, of the types known in the art and commercially available such as under the trade-names Paliotol (available from BASF pic), Cinquasia, Irgalite (both available from Ciba Speciality Chemicals) and Hostaperm (available from Clariant UK). The pigment may be of any desired colour such as, for example, Pigment Yellow 13, Pigment Yellow 83, Pigment Red 9, Pigment Red 184, Pigment Blue 15:3, Pigment Green 7, Pigment Violet 19, Pigment Black 7. Especially useful are black and the colours required for trichromatic process printing. Mixtures of pigments may be used.
In one aspect the following pigments are preferred. Cyan: phthalocyanine pigments such as Phthalocyanine blue 15.4. Yellow: azo pigments such as Pigment yellow 120, Pigment yellow 151 and Pigment yellow 155. Magenta: quinacridone pigments, such as Pigment violet 19 or mixed crystal quinacridones such as Cromophtal Jet magenta 2BC and Cinquasia RT-355D. Black: carbon black pigments such as Pigment black 7.
Pigment particles dispersed in the ink should be sufficiently small to allow the ink to pass through an inkjet nozzle, typically having a particle size less than 8 pm, preferably less than 5 pm, more preferably less than 1 pm and particularly preferably less than 0.5 pm.
The colorant is preferably present in an amount of 0.2-20% by weight, preferably 0.5-15% by weight, based on the total weight of the ink. A higher concentration of pigment may be required for white inks, for example up to and including 30% by weight, or 25% by weight, based on the total weight of the ink.
The inkjet ink preferably dries primarily by curing, i.e. by the polymerisation of the monomers present, as discussed hereinabove, and hence is a curable ink. The ink does not, therefore, require the presence of water or a volatile organic solvent to effect drying of the ink. Preferably, the inkjet ink comprises less than 5% by weight of water and volatile organic solvent combined, preferably less than 3% by weight combined, more preferably, less than 2% by weight combined and more preferably less than 1 % by weight combined, and most preferably, the inkjet ink is substantially free of water and volatile organic solvents, where the amounts are based on the total weight of the ink.
By substantially free is meant that only small amounts will be present, for example some water will typically be absorbed by the ink from the air and solvents may be present as impurities in the components of the inks, but such low levels are tolerated. In other words, no water or a volatile organic solvent is intentionally added to the ink. However, minor amounts of water or a volatile
organic solvent, which may be present as impurities in commercially available inkjet ink components, are tolerated. For example, the ink may comprise less than 0.5% by weight of water or a volatile organic solvent, more preferably less than 0.1 % by weight ofwater or a volatile organic solvent, most preferably less than 0.05% by weight of water or a volatile organic solvent, based on the total weight of the ink. In a preferred embodiment, the inkjet ink is free of water or a volatile organic solvent.
In a preferred embodiment, the ink of the present invention comprises a surfactant. The surfactant controls the surface tension of the ink. Surfactants are well-known in the art and a detailed description is not required. An example of a suitable surfactant is BYK307. In a preferred embodiment, the inkjet ink comprises an acrylated surfactant. Acrylated surfactants are particularly preferred as they can be partially included in the crosslink network on cure. Preferred examples of acrylated surfactants are commercially available as Tego Rad 2010 and Tego Rad 2300.
Adjustment of the surface tension of the inks allows control of the surface wetting of the inks on various substrates, for example, plastic substrates. Too high a surface tension can lead to ink pooling and/or a mottled appearance in high coverage areas of the print. Too low a surface tension can lead to excessive ink bleed between different coloured inks. Surface tension is also critical to ensuring stable jetting (nozzle plate wetting and sustainability). The surface tension is preferably in the range of 18-40 rnNm 1, more preferably 20-35 mNm 1 and most preferably 20-30 mNm 1.
Other components of types known in the art may be present in the ink of the present invention to improve the properties or performance. These components may be, for example, additional surfactants, defoamers, dispersants, synergists, stabilisers against deterioration by heat or light other than an aerobic stabiliser, reodorants, flow or slip aids, biocides and identifying tracers.
The amounts by weight provided herein are based on the total weight of the ink.
The ink or inkjet ink sets may be prepared by known methods such as stirring with a high-speed water-cooled stirrer, or milling on a horizontal bead-mill.
The ink exhibits a desirable low viscosity, less than 100 mPas, preferably 30 mPas or less, more preferably 22 mPas or less and most preferably 20 mPas or less at 25°C. The ink most preferably has a viscosity of less than 20 mPas at 25°C. Viscosity may be measured using a rotational viscometer fitted with a thermostatically controlled cup and spindle arrangement, running at 20 rpm at 25°C.
The present invention also provides an inkjet ink set, wherein the inkjet ink set of the invention has at least one ink that falls within the scope of the inkjet ink according to the present invention.
Preferably, all of the inks in the set fall within the scope of the inkjet ink according to the present invention.
Usually, the inkjet ink set of the present invention is in the form of a multi-chromatic inkjet ink set, which typically comprises a cyan ink, a magenta ink, a yellow ink and a black ink (a so-called trichromatic set). This set is often termed CMYK. The inks in a trichromatic set can be used to produce a wide range of colours and tones.
The present invention also provides a method of inkjet printing comprising inkjet printing the inkjet ink as defined herein onto a substrate and curing the inkjet ink by exposing the inkjet ink to a curing source.
In the method of inkjet printing of the present invention, the inkjet ink is inkjet printed onto a substrate. Printing is performed by inkjet printing, e.g. on a single-pass inkjet printer, for example for printing (directly) onto a substrate, on a roll-to-roll printer or a flat-bed printer. As discussed above, inkjet printing is well known in the art and a detailed description is not required.
The ink is jetted from one or more reservoirs or printing heads through narrow nozzles on to a substrate to form a printed image.
Print heads account for a significant portion of the cost of an entry level printer and it is therefore desirable to keep the number of print heads (and therefore the number of inks in the ink set) low. Reducing the number of print heads can reduce print quality and productivity. It is therefore desirable to balance the number of print heads in order to minimise cost without compromising print quality and productivity.
Substrates include those for packaging applications and in particular, flexible packaging applications. Examples include substrates composed of polyvinyl chloride (PVC), polystyrene, polyester, polyethylene terephthalate (PET), polyethylene terephthalate glycol modified (PETG) and polyolefin (e.g. polyethylene, polypropylene or mixtures or copolymers thereof). Further substrates include all cellulosic materials such as paper and board, or their mixtures/blends with the aforementioned synthetic materials.
Particularly preferred substrates are a food packaging. Food packaging is typically formed of flexible and rigid plastics (e.g. food-grade polystyrene and PE/PP films), paper and board (e.g. corrugated board). Printing onto a food packaging substrate represents a particular challenge on account of the strict safety limitations on the properties of materials which come into contact with food, including indirect additives like packaging inks. For printed food packaging, it is necessary to control and quantify the migration and/or odour of the components of the printed image on the food packaging into the food products. Specific exclusions based on their odour and/or migration
properties include volatile organic solvents and many monomers typically used in UV curing inks. Preferably, the monomers present in the ink of the present invention are suitable for food packaging applications.
When discussing the substrate, it is the surface which is most important, since it is the surface which is wetted by the ink. Thus, at least the surface of substrate is composed of the abovediscussed material.
In a preferred embodiment, the substrate is a laminate carton material comprising the following layers, in order: an inner polyethylene layer; an aluminium layer; a board layer; and an outer polyethylene layer. By inner is meant a surface of the substrate that would come into contact with food and by outer is meant a surface of the substrate that would come into contact with the inkjet ink used in the method of the present invention. More preferably, the polyethylene layer is corona treated to a surface tension of more than 45 dynes/cm using a Vetaphone unit. This provides improved adhesion of the ink.
The present invention may also provide a printed substrate having the ink as defined herein printed thereon. Preferably, the substrate is a food packaging.
In order to produce a high quality printed image a small jetted drop size is desirable. Preferably the inkjet ink is jetted at drop sizes below 90 picolitres, preferably below 35 picolitres and most preferably below 10 picolitres.
To achieve compatibility with print heads that are capable of jetting drop sizes of 90 picolitres or less, a low viscosity ink is required. A viscosity of 30 mPas or less at 25°C is preferred, more preferably less than 20 mPas at 25°C. For example, 8 to 12 mPas, 18 to 20 mPas, or 24 to 26 mPas. Ink viscosity may be measured using a rotational viscometer fitted with a thermostatically controlled cup and spindle arrangement, running at 20 rpm at 25°C.
The ink of the present invention is cured by any means known in the art, such as exposure to actinic radiation and low-energy electron beam radiation.
It should be noted that the terms “dry” and “cure” are often used interchangeably in the art when referring to radiation-curable inkjet inks to mean the conversion of the inkjet ink from a liquid to solid by polymerisation and/or crosslinking of the radiation-curable material. Herein, however, by “drying” is meant the removal of the water by evaporation and by “curing” is meant the polymerisation and/or crosslinking of the radiation-curable material. Further details of the printing, drying and curing process are provided in WO 201 1/021052.
In a preferred embodiment, the ink is cured by exposing the printed ink to a source of actinic radiation.
The source of actinic radiation can be any source of actinic radiation that is suitable for curing radiation-curable inks but is preferably a UV source. Suitable UV sources are well known in the art and a detailed description is not required. These include mercury discharge lamps, fluorescent tubes, light emitting diodes (LEDs), flash lamps and combinations thereof
In a particularly preferred embodiment, the source of actinic radiation is LEDs. The inventors have surprisingly found that the ink of the present invention comprising the specific blend of photoinitiators in the specific amounts allows for increased cure speed and improved surface cure when curing with a UV LED curing source. It is particularly challenging to provide improved surface cure and a high cure speed when curing with a UV LED curing source. This is even more challenging when the formulator’s choice of ink components is restricted when providing inkjet inks for food packaging. The present inventors have been able to prepare an inkjet ink that is suitable for food packaging and which also obtains improved surface cure and cure speed, whilst maintaining a low viscosity, by providing an ink having the specific blend of photoinitiators in the amounts as claimed.
LEDs are increasingly used to cure inkjet inks. UV light is emitted from a UV LED light source. UV LED light sources comprise one or more LEDs and are well known in the art. Thus, a detailed description is not required.
It will be understood that UV LED light sources emit radiation having a spread of wavelengths. The emission of UV LED light sources is identified by the wavelength which corresponds to the peak in the wavelength distribution. Compared to conventional mercury lamp UV sources, UV LED light sources emit UV radiation over a narrow range of wavelengths on the wavelength distribution. The width of the range of wavelengths on the wavelength distribution is called a wavelength band. LEDs therefore have a narrow wavelength output when compared to other sources of UV radiation. By a narrow wavelength band, it is meant that at least 90%, preferably at least 95%, of the radiation emitted from the UV LED light source has a wavelength within a wavelength band having a width of 50 nm or less, preferably, 30 nm or less, most preferably 15 nm or less.
In a preferred embodiment, at least 90%, preferably at least 95%, of the radiation emitted from the UV LED light source has a wavelength in a band having a width of 50 nm or less, preferably 30 nm or less, most preferably 15 nm or less.
LEDs have a longer lifetime and exhibit no change in the power/wavelength output overtime. LEDs also have the advantage of switching on instantaneously with no thermal stabilisation time and their use results in minimal heating of the substrate.
The ink may also be cured by exposing the printed ink to low-energy electron beam (ebeam).
The source of low-energy electron beam (ebeam) can be any source of low-energy electron beam that is suitable for curing radiation-curable inks. Suitable low-energy electron beam radiation sources include commercially available ebeam curing units, such as the EB Lab from ebeam Technologies with energy of 80-300 keV and capable of delivering a typical dose of 30-50 kGy at line speeds of up to 30 m/min. By “low-energy” for the ebeam, it is meant that it delivers an electron beam having a dose at the substrate of 100 kGy or less, preferably 70 kGy or less.
Ebeam curing is characterised by dose (energy per unit mass, measured in kilograys (kGy)) deposited in the substrate via electrons. Electron beam surface penetration depends upon the mass, density and thickness of the material being cured. Compared with UV penetration, electrons penetrate deeply through both lower and higher density materials. Unlike UV curing, photoinitiators are not required for ebeam curing to take place.
Ebeam curing is well-known in the art and therefore a detailed explanation of the curing method is not required. In order to cure the printed ink, the ink of the invention is exposed to the ebeam, which produces sufficient energy to instantaneously break chemical bonds and enable polymerisation or crosslinking.
There is no restriction on the ebeam dose that is used to cure the inkjet inks of the present invention other than that the dose is sufficient to fully cure the ink. Preferably, the dose is more than 10 kGy, more preferably more than 20 kGy, more preferably more than 30 kGy and most preferably more than 40 kGy. Preferably, the dose is less than 100 kGy, more preferably less than 90 kGy, more preferably less than 80 kGy and most preferably less than 70 kGy. Preferably, the dose is more than 30 kGy but less than 70 kGy, more preferably more than 30 kGy but less than 60 kGy and most preferably, more than 30 kGy but 50 kGy or less. Doses above 50 kGy may cause damage to the substrate, particularly the substrates used for food packaging applications, and so doses of 50 kGy or less are preferred.
The energy associated with these doses is 80-300 keV, more preferably 70-200 keV and most preferably 100 keV.
The ink cures to form a relatively thin polymerised film. The ink of the present invention typically produces a printed film having a thickness of 1 to 20 pm, preferably 1 to 10 pm, for example 2 to 5 pm. Film thicknesses can be measured using a confocal laser scanning microscope.
The invention will now be described with reference to the following examples, which are not intended to be limiting.
Examples
Example 1
Inkjet inks were prepared according to the formulations set out in Tables 1 and 2. The inkjet ink formulations were prepared by mixing the components in the given amounts. Amounts are given as weight percentages based on the total weight of the ink.
The cyan pigment dispersion contains 30% blue pigment, 20% polymeric dispersing aid and 50% DVE-3. The dispersion was prepared by mixing the components in the given amounts and passing the mixture through a bead mill until the dispersion had a particle size of less than 0.3 microns. Amounts are given as weight percentages based on the total weight of the dispersion.
The inks of Tables 1 and 2 have varying amounts of TPO-L and Speedcure 7010, which are set out in Table 3.
Surface cure at varying cure speed
The surface cure at varying cure speeds for the inks of Tables 1 and 2 was then assessed.
In order to assess the surface cure at varying cure speeds, the inks were drawn down in a 12 pm film using a 12 pm wire wound K-bar onto a PP60 Top White substrate available from Avery Dennison.
The 12 pm drawdowns were then passed under a 16 W, 40 mm LED lamp (16 W 395 nm LED, Phoseon FireLine FL440 225 x 40 mm) at varying belt speeds to provide a cured ink film.
The cured ink film had a piece of Epson photo paper placed face down on the cured ink film. The back of the photo paper was rubbed by hand in both direction 10 times. The photo paper was then pulled away from the cured ink film.
If the film is cured and has good surface cure, the photo paper will separate with no offset and no noise. If the film is not fully cured and has poor surface cure, the ink will offset to the photo paper and/or noise is observed as force is required to separate the partially cured ink film and the photo paper.
The cure was assessed at increasing belt speeds and the cure speed (the maximum belt speed at which a pass for cure can be achieved) was recorded for each ink.
The cure results for the inks of Tables 1 and 2 are shown in Table 4.
As can be seen from the cure speed results, improved surface cure and cure speed is achieved when BAPO, Speedcure 7010 and TPO-L are used in combination in the claimed amounts.
Adequate surface cure and cure speed is not achieved using Inks 2A-2I in the absence of Speedcure 7010 and/or TPO-L, even at high concentrations of Speedcure 7010 or TPO-L.
The inventors have surprisingly found that the inkjet ink comprising the claimed blend of photoinitiators in the claimed amounts provides improved surface cure and cure speed, even when curing with UV LEDs.
Viscosity
The viscosity of the inks of Tables 1 and 2 was measured using a Brookfield viscometer running at 30 rpm at 25°C.
The viscosity results for the inks of Tables 1 and 2 are shown in Table 5.
Table 5
As can be seen from the viscosity results, even with a high amount of photoinitiators present in the ink, the inks of Table 1 all have a surprisingly low viscosity. The high cure speeds of Table 4 were a surprise given the low viscosity of the inks.
Example 2
A comparative inkjet ink was prepared according to the formulation set out in Table 6. The comparative inkjet ink formulation was prepared by mixing the components in the given amounts. Amounts are given as weight percentages based on the total weight of the ink.
The cyan pigment dispersion was the same as that used in Example 1 .
Ink 3 is the same as ink K of Example 1 except BAPO has been replaced with additional 3MPDA.
Surface cure at varying cure speed
The surface cure for ink 3 was then assessed in the same way as for the inks of Example 1 .
The cure speed (the maximum belt speed at which a pass for cure can be achieved) for ink 3 was recorded as 160 m/min. This is in contrast to the recorded cure speed of 240 m/min for ink K.
Inks 3 and K contain the same amount of TPO-L and Speedcure 7010 but BAPO is absent from ink 3. Therefore, improved surface cure and cure speed is achieved when BAPO is used in combination with Speedcure 7010 and TPO-L in the claimed amounts.
The inventors have surprisingly found that the inkjet ink comprising the claimed blend of photoinitiators in the claimed amounts provides improved surface cure and cure speed, even when curing with UV LEDs.
Viscosity
The viscosity of ink 3 was measured in the same was as for the inks of Example 1 . Ink 3 had a viscosity of 11 .6 mPa.s.
Claims
1. An inkjet ink comprising: a radiation-curable material; 2% by weight or more of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide; 2% by weight or more in total of one or more polymeric thioxanthone photoinitiators; and 4% by weight or more of
wherein the amounts are based on the total weight of the ink.
2. An inkjet ink as claimed in claim 1 , wherein the inkjet ink comprises 2 to 6% by weight of phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide, based on the total weight of the ink.
3. An inkjet ink as claimed in claim 1 or 2, wherein the one or more polymeric thioxanthone photoinitiators comprise two or more thioxanthone units connected by a linking unit, wherein the thioxanthone unit has the structure:
wherein R1 , R2, R3, R4, R5, R6, R7 and R8 are independently hydrogen, halogen, C1-12 alkyl, C2-12 alkenyl, C2-12 alkynyl, C7-12 aralkyl, C7-12 alkaryl, C6-12 aryl, C5-12 heteroaryl or the linking unit, with the proviso that one of R1, R2, R3, R4, R5, R6, R7 and R8 is the linking unit; and the linking unit is a polymer.
4. An inkjet ink as claimed in claim 3, wherein the one or more polymeric thioxanthone photoinitiators comprise
43
5. An inkjet ink as claimed in claim 4, wherein the one or more polymeric thioxanthone photoinitiators comprise
6. An inkjet ink as claimed in any preceding claim, wherein the inkjet ink comprises 2 to 12% by weight in total of the one or more polymeric thioxanthone photoinitiators, based on the total weight of the ink.
8. An inkjet ink as claimed in any preceding claim, wherein the ink comprises 8-35% by weight in total of all photoinitiators.
9. An inkjet ink as claimed in any preceding claim, wherein the ink has a viscosity of less than 30 mPas at 25°C.
45
10. An inkjet ink as claimed in any preceding claim, wherein the radiation-curable material comprises a radiation-curable monomer.
11. An inkjet ink as claimed in claim 10, wherein the radiation-curable monomer comprises a di- and/or multifunctional radiation-curable monomer, preferably a difunctional monomer.
12. A method of inkjet printing comprising inkjet printing the inkjet ink as claimed in any preceding claim onto a substrate and curing the inkjet ink by exposing the inkjet ink to a curing source.
13. A method of inkjet printing as claimed in claim 12, wherein the curing source is a UV LED light.
14. A method of inkjet printing as claimed in claims 12 or 13, wherein the substrate is food packaging.
15. A substrate having the inkjet ink as claimed in claims 1 to 11 printed thereon, preferably wherein the substrate is food packaging.