WO2022216460A1 - Dry process for forming an electrode - Google Patents
Dry process for forming an electrode Download PDFInfo
- Publication number
- WO2022216460A1 WO2022216460A1 PCT/US2022/021676 US2022021676W WO2022216460A1 WO 2022216460 A1 WO2022216460 A1 WO 2022216460A1 US 2022021676 W US2022021676 W US 2022021676W WO 2022216460 A1 WO2022216460 A1 WO 2022216460A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- lithium
- group
- electrode material
- metal powder
- dry
- Prior art date
Abstract
Description
Claims