WO2022193292A1 - Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication - Google Patents
Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication Download PDFInfo
- Publication number
- WO2022193292A1 WO2022193292A1 PCT/CN2021/081826 CN2021081826W WO2022193292A1 WO 2022193292 A1 WO2022193292 A1 WO 2022193292A1 CN 2021081826 W CN2021081826 W CN 2021081826W WO 2022193292 A1 WO2022193292 A1 WO 2022193292A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating
- spectacle lens
- individual
- biocidal component
- metal
- Prior art date
Abstract
La présente invention concerne un verre de lunettes comprenant au moins un revêtement antibactérien et/ou antiviral et son procédé de fabrication.
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/CN2021/081826 WO2022193292A1 (fr) | 2021-03-19 | 2021-03-19 | Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication |
CN202280035951.5A CN117440755A (zh) | 2021-03-19 | 2022-03-18 | 具有抗菌和/或抗病毒特性的眼镜片及其制造方法 |
BR112023019072A BR112023019072A2 (pt) | 2021-03-19 | 2022-03-18 | Lente para óculos com propriedades antibacterianas e/ou antivirais e método de fabricação das mesma |
PCT/EP2022/057254 WO2022195121A1 (fr) | 2021-03-19 | 2022-03-18 | Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/CN2021/081826 WO2022193292A1 (fr) | 2021-03-19 | 2021-03-19 | Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022193292A1 true WO2022193292A1 (fr) | 2022-09-22 |
Family
ID=75302194
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2021/081826 WO2022193292A1 (fr) | 2021-03-19 | 2021-03-19 | Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication |
PCT/EP2022/057254 WO2022195121A1 (fr) | 2021-03-19 | 2022-03-18 | Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2022/057254 WO2022195121A1 (fr) | 2021-03-19 | 2022-03-18 | Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication |
Country Status (3)
Country | Link |
---|---|
CN (1) | CN117440755A (fr) |
BR (1) | BR112023019072A2 (fr) |
WO (2) | WO2022193292A1 (fr) |
Citations (28)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5454886A (en) | 1993-11-18 | 1995-10-03 | Westaim Technologies Inc. | Process of activating anti-microbial materials |
US20020111390A1 (en) | 2000-12-11 | 2002-08-15 | Shi Lin | Impact resistant uv curable hardcoatings |
WO2003058300A1 (fr) | 2001-12-27 | 2003-07-17 | Transitions Optical, Inc. | Article optique photochromique |
EP1433814A1 (fr) | 2001-07-27 | 2004-06-30 | Tokuyama Corporation | Composition durcissable, article durci obtenu a partir de cette composition et materiau optique photochrome et son procede de production |
GB2372044B (en) | 2001-02-07 | 2005-01-26 | Samsung Sdi Co Ltd | Functional film having improved optical and electrical properties |
JP2005034685A (ja) * | 2003-07-15 | 2005-02-10 | Proceed:Kk | 銀系酸化チタンのコーティング方法及び銀系酸化チタンのコーティング物 |
KR200375582Y1 (ko) | 2004-11-12 | 2005-03-11 | 양원동 | 나노 실버가 함유된 안경 |
US20050171231A1 (en) | 2001-12-14 | 2005-08-04 | Diggins David R. | Abrasion resistant coating composition |
EP1561571A1 (fr) | 2002-05-27 | 2005-08-10 | Tokuyama Corporation | Procede de fabrication d'article photochromique en couches |
EP1602479A1 (fr) | 2003-02-17 | 2005-12-07 | Tokuyama Corporation | Produit en couches, piece optique, procedes pour produire ce produit et cette piece, et fluide de revetement |
WO2007101055A1 (fr) * | 2006-02-22 | 2007-09-07 | Microban Products Company | Lentilles antimicrobiennes |
US20090189303A1 (en) | 2006-05-09 | 2009-07-30 | Carl Zeiss Vision Australia Holdings Limited | Methods for forming coated high index optical elements |
EP2437084A1 (fr) | 2010-10-01 | 2012-04-04 | Carl Zeiss Vision GmbH | Lentille optique avec revêtement anti-rayure et anti-refléchissant |
EP2578649A1 (fr) | 2011-10-04 | 2013-04-10 | Carl Zeiss Vision International GmbH | Composition de préparation d'un revêtement comprenant une adhésion et une résistance à la rayure élevées |
EP2801846A1 (fr) | 2013-05-06 | 2014-11-12 | Carl Zeiss Vision International GmbH | Élément optique doté d'un revêtement à haute diffusivité |
US20150044482A1 (en) | 2013-08-06 | 2015-02-12 | Samsung Display Co., Ltd. | Multi-layer optical coating structure having an antibacterial coating layer |
EP2850484A1 (fr) | 2012-05-16 | 2015-03-25 | Essilor International (Compagnie Générale D'Optique) | Lentille ophtalmique |
CN105068270A (zh) * | 2015-07-20 | 2015-11-18 | 无锡商业职业技术学院 | 一种抗菌型眼镜片 |
CN106772713A (zh) | 2016-12-27 | 2017-05-31 | 上海康耐特光学股份有限公司 | 一种抗菌镀膜树脂镜片及其制造方法 |
US10221093B2 (en) | 2014-05-23 | 2019-03-05 | Saint-Gobain Glass France | Substrate equipped with a multilayer comprising partial metal films, glazing unit, use and process |
WO2019082001A1 (fr) | 2017-10-25 | 2019-05-02 | Politecnico Di Torino | Procédé d'application d'un revêtement antiviral sur un substrat et revêtement correspondant |
US10527760B2 (en) | 2016-02-04 | 2020-01-07 | Essilor International | Ophthalmic lens comprising a thin antireflective coating with a very low reflection in the visible region |
CN210534467U (zh) | 2019-11-25 | 2020-05-15 | 厦门朵彩光学科技有限公司 | 一种防海水腐蚀抗菌型镜片及防海水腐蚀抗菌型眼镜 |
US20200209436A1 (en) | 2017-09-21 | 2020-07-02 | Fujifilm Corporation | Antireflection film, optical element, and optical system |
WO2020138469A1 (fr) | 2018-12-28 | 2020-07-02 | ホヤ レンズ タイランド リミテッド | Verre de lunettes |
JP2020142494A (ja) | 2019-03-07 | 2020-09-10 | 伊藤光学工業株式会社 | 抗菌透明積層体及びその製造方法 |
CN211928330U (zh) * | 2020-04-04 | 2020-11-13 | 林秀斌 | 一种抗菌效果好的眼镜片 |
EP3740815A1 (fr) | 2018-02-27 | 2020-11-25 | Carl Zeiss Vision International GmbH | Verre de lunettes comprenant au moins une couche nanostructurée et/ou microstructurée |
-
2021
- 2021-03-19 WO PCT/CN2021/081826 patent/WO2022193292A1/fr active Application Filing
-
2022
- 2022-03-18 BR BR112023019072A patent/BR112023019072A2/pt unknown
- 2022-03-18 CN CN202280035951.5A patent/CN117440755A/zh active Pending
- 2022-03-18 WO PCT/EP2022/057254 patent/WO2022195121A1/fr active Application Filing
Patent Citations (28)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5454886A (en) | 1993-11-18 | 1995-10-03 | Westaim Technologies Inc. | Process of activating anti-microbial materials |
US20020111390A1 (en) | 2000-12-11 | 2002-08-15 | Shi Lin | Impact resistant uv curable hardcoatings |
GB2372044B (en) | 2001-02-07 | 2005-01-26 | Samsung Sdi Co Ltd | Functional film having improved optical and electrical properties |
EP1433814A1 (fr) | 2001-07-27 | 2004-06-30 | Tokuyama Corporation | Composition durcissable, article durci obtenu a partir de cette composition et materiau optique photochrome et son procede de production |
US20050171231A1 (en) | 2001-12-14 | 2005-08-04 | Diggins David R. | Abrasion resistant coating composition |
WO2003058300A1 (fr) | 2001-12-27 | 2003-07-17 | Transitions Optical, Inc. | Article optique photochromique |
EP1561571A1 (fr) | 2002-05-27 | 2005-08-10 | Tokuyama Corporation | Procede de fabrication d'article photochromique en couches |
EP1602479A1 (fr) | 2003-02-17 | 2005-12-07 | Tokuyama Corporation | Produit en couches, piece optique, procedes pour produire ce produit et cette piece, et fluide de revetement |
JP2005034685A (ja) * | 2003-07-15 | 2005-02-10 | Proceed:Kk | 銀系酸化チタンのコーティング方法及び銀系酸化チタンのコーティング物 |
KR200375582Y1 (ko) | 2004-11-12 | 2005-03-11 | 양원동 | 나노 실버가 함유된 안경 |
WO2007101055A1 (fr) * | 2006-02-22 | 2007-09-07 | Microban Products Company | Lentilles antimicrobiennes |
US20090189303A1 (en) | 2006-05-09 | 2009-07-30 | Carl Zeiss Vision Australia Holdings Limited | Methods for forming coated high index optical elements |
EP2437084A1 (fr) | 2010-10-01 | 2012-04-04 | Carl Zeiss Vision GmbH | Lentille optique avec revêtement anti-rayure et anti-refléchissant |
EP2578649A1 (fr) | 2011-10-04 | 2013-04-10 | Carl Zeiss Vision International GmbH | Composition de préparation d'un revêtement comprenant une adhésion et une résistance à la rayure élevées |
EP2850484A1 (fr) | 2012-05-16 | 2015-03-25 | Essilor International (Compagnie Générale D'Optique) | Lentille ophtalmique |
EP2801846A1 (fr) | 2013-05-06 | 2014-11-12 | Carl Zeiss Vision International GmbH | Élément optique doté d'un revêtement à haute diffusivité |
US20150044482A1 (en) | 2013-08-06 | 2015-02-12 | Samsung Display Co., Ltd. | Multi-layer optical coating structure having an antibacterial coating layer |
US10221093B2 (en) | 2014-05-23 | 2019-03-05 | Saint-Gobain Glass France | Substrate equipped with a multilayer comprising partial metal films, glazing unit, use and process |
CN105068270A (zh) * | 2015-07-20 | 2015-11-18 | 无锡商业职业技术学院 | 一种抗菌型眼镜片 |
US10527760B2 (en) | 2016-02-04 | 2020-01-07 | Essilor International | Ophthalmic lens comprising a thin antireflective coating with a very low reflection in the visible region |
CN106772713A (zh) | 2016-12-27 | 2017-05-31 | 上海康耐特光学股份有限公司 | 一种抗菌镀膜树脂镜片及其制造方法 |
US20200209436A1 (en) | 2017-09-21 | 2020-07-02 | Fujifilm Corporation | Antireflection film, optical element, and optical system |
WO2019082001A1 (fr) | 2017-10-25 | 2019-05-02 | Politecnico Di Torino | Procédé d'application d'un revêtement antiviral sur un substrat et revêtement correspondant |
EP3740815A1 (fr) | 2018-02-27 | 2020-11-25 | Carl Zeiss Vision International GmbH | Verre de lunettes comprenant au moins une couche nanostructurée et/ou microstructurée |
WO2020138469A1 (fr) | 2018-12-28 | 2020-07-02 | ホヤ レンズ タイランド リミテッド | Verre de lunettes |
JP2020142494A (ja) | 2019-03-07 | 2020-09-10 | 伊藤光学工業株式会社 | 抗菌透明積層体及びその製造方法 |
CN210534467U (zh) | 2019-11-25 | 2020-05-15 | 厦门朵彩光学科技有限公司 | 一种防海水腐蚀抗菌型镜片及防海水腐蚀抗菌型眼镜 |
CN211928330U (zh) * | 2020-04-04 | 2020-11-13 | 林秀斌 | 一种抗菌效果好的眼镜片 |
Non-Patent Citations (4)
Title |
---|
GEORGIOS A. SOTIRIOU ET AL: "Antibacterial Activity of Nanosilver Ions and Particles", ENVIRONMENTAL SCIENCE & TECHNOLOGY, vol. 44, no. 14, 15 July 2010 (2010-07-15), US, pages 5649 - 5654, XP055751644, ISSN: 0013-936X, DOI: 10.1021/es101072s * |
GLADSKIKH ET AL.: "Optical Properties of Silver and Gold Clusters in Silica Matrices", NANOCON, 18 October 2017 (2017-10-18), pages 821 - 825 |
MIOLA ET AL.: "Silver nanocluster-silica composite antibacterial coatings for materials to be used in mobile telephones", APPLIED SURFACE SCIENCE, vol. 313, 2014, pages 107 - 115, XP029039187, DOI: 10.1016/j.apsusc.2014.05.151 |
S. GALDIERO ET AL.: "Silver Nanoparticles as Potential Antiviral Agents", MOLECULES, vol. 16, 2011, pages 8894 - 8918, XP055492993, DOI: 10.3390/molecules16108894 |
Also Published As
Publication number | Publication date |
---|---|
BR112023019072A2 (pt) | 2023-12-05 |
CN117440755A (zh) | 2024-01-23 |
WO2022195121A1 (fr) | 2022-09-22 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN107111000B (zh) | 包括在紫外区域具有高反射率的干涉涂层的光学物品 | |
US20230280504A1 (en) | Spectacle lens with antibacterial and/or antiviral properties and method for manufacturing the same | |
US20220011601A1 (en) | Optical Lens Having a Filtering Interferential Coating and a Multilayer System for Improving Abrasion-Resistance | |
KR20020042425A (ko) | 증착 조성물의 제조방법, 증착 조성물 및 반사방지막을갖는 광학부품의 제조방법 | |
EP3076226B1 (fr) | Verre de lunettes | |
US20020181108A1 (en) | Optical element with mirror coating and method for forming said coating | |
US11940596B2 (en) | Spectacle lens with antibacterial and/or antiviral properties and method for manufacturing the same | |
WO2022193292A1 (fr) | Verre de lunettes à propriétés antibactériennes et/ou antivirales et son procédé de fabrication | |
EP3279706B1 (fr) | Verre de lunettes et son procédé de fabrication, et lunettes | |
JP2023010987A (ja) | 眼鏡レンズおよび眼鏡 | |
JP2023009170A (ja) | 眼鏡レンズの製造方法 | |
US20130258278A1 (en) | Lens comprising a polymeric substrate, a hardening layer and a metallic layer | |
KR102207188B1 (ko) | 저방사 유리 | |
EP4109141A1 (fr) | Lentille optique comportant un revêtement interférentiel absorbant la lumière | |
JP7203147B2 (ja) | 眼鏡レンズの製造方法 | |
EP4102265A1 (fr) | Lentille optique comportant un revêtement antireflet réfléchissant la lumière bleue nocive | |
JP7242753B2 (ja) | 眼鏡レンズおよび眼鏡 | |
US20240230956A1 (en) | Optical lens having an antireflection coating reflecting blue light | |
JP7385894B2 (ja) | プラスチック基材ndフィルタ及び眼鏡用プラスチック基材ndフィルタ | |
WO2021234030A1 (fr) | Article transparent, en particulier verre de lunettes, à propriétés antibactériennes et/ou antivirales et son procédé de fabrication | |
JPH03173763A (ja) | 透明物品 | |
KR20020074635A (ko) | 자외선 차폐용 다층박막 안경렌즈 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21711168 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 21711168 Country of ref document: EP Kind code of ref document: A1 |