WO2022152213A1 - 一种有机化合物、组合物及其在有机电子器件中的应用 - Google Patents
一种有机化合物、组合物及其在有机电子器件中的应用 Download PDFInfo
- Publication number
- WO2022152213A1 WO2022152213A1 PCT/CN2022/071813 CN2022071813W WO2022152213A1 WO 2022152213 A1 WO2022152213 A1 WO 2022152213A1 CN 2022071813 W CN2022071813 W CN 2022071813W WO 2022152213 A1 WO2022152213 A1 WO 2022152213A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- groups
- group
- atoms
- organic
- organic compound
- Prior art date
Abstract
提供了一种式(I)的有机化合物、其混合物、其组合物及其在有机电子器件中的应用,特别是在有机电致发光二极管中的应用;还提供了包含上述有机化合物的有机电子器件,特别是有机电致发光二极管,及其在显示及照明技术中的应用。通过器件结构优化,可达到较佳的器件性能,特别是可实现高性能的OLED器件,对全彩显示和照明应用提供了较好的材料和制备技术选项。
Description
本发明涉及有机电致发光技术领域,特别是涉及一种有机化合物、高聚物、混合物、组合物及其包含其的有机电子器件。
由于有机半导体材料在合成上具有多样性、制造成本相对较低和优良的光学与电学性能,有机发光二极管(OLED)在光电器件(例如平板显示器和照明)的应用方面具有很大的潜力。
有机电致发光现象是指利用有机物质将电能转化为光能的现象。利用有机电致发光现象的有机电致发光元件通常具有正极与负极以及在它们中间包含有机物层的结构。为了提高有机电致发光元件的效率与寿命,有机物层具有多层结构,每一层包含有不同的有机物质。具体的,可以包括空穴注入层、空穴传输层、发光层、电子传输层、电子注入层等。在这种有机电致发光元件中,在两个电极之间施加电压,则由正极向有机物层注入空穴,由负极向有机物层注入电子,当注入的空穴与电子相遇时形成激子,该激子跃迁回基态时发出光。这种有机电致发光元件具有自发光、高亮度、高效率、低驱动电压、广视角、高对比度、高响应性等特性。
理论和实验都已证明发光材料是决定OLED器件效率最为重要的因素。目前有机电致发光元件发光层通常使用主体材料/掺杂剂的混合体系作为发光材料,可以改进色彩纯度、发光效率以及稳定性。一般来说,使用主体材料/掺杂剂体系,主体材料的选择至关重要,因为主体材料极大地影响OLED器件的效率及稳定性。优选的,主体材料应具有合适的分子量以便在真空下沉积,同时还需要具有较高的玻璃化转变温度和热分解温度以保证热稳定性,高的电化学稳定性以保证长使用寿命,容易形成非晶态薄膜,与相邻功能层材料有良好的界面作用,不易发生分子运动。
现有专利及文献中报道了大量的主体材料。例如吲哚并咔唑类衍生物由于具有较高的载流子传输能力、光电响应性质和热稳定性等优点,成为学术界和产业界关注的焦点,并广泛应用于有机发光二极管中。但目前开发的大部分吲哚并咔唑类衍生物仍然存在着化学/环境稳定性较差的不足,主要是因为这类材料(专利WO2007063796A1;WO2007063754A1;US2016293856A1)结构中氮原子的孤对电子,共轭到苯环中,形成电子云密度较大、反应活性较高的C-H键,致使这类型化合物的化学/环境稳定性较差、器件寿命较短。研究人员也开发了吲哚并芴类衍生物(专利WO2010136109A1),但器件性能还需进一步改善。
因此,仍需改进材料,特别是适合形成共主体的主体材料体系,尤其是具有电子传输性质的n型主体材料,及和其搭配的p型材料。
发明内容
鉴于上述现有技术的不足,本发明的目的在于提供一种有机化合物、组合物及其有机电子器件中的应用,旨在解决现有OLED的效率和寿命的问题。
本发明的技术方案如下:
一种有机化合物,具有如通式(I)所示的结构:
其中,
X独立表示为N或CR
1,且至少一个X为CR
1,当相邻的X为CR
1时可相互稠合成环;
R
1选自H、D、具有1至20个C原子的直链烷基、烷氧基或硫代烷氧基基团,或者具有3至20个C原子的支链或环状的烷基、烷氧基或硫代烷氧基基团或者是甲硅烷基基团,或具有1至20个C原子的取代的酮基基团,或具有2至20个C原子的烷氧基羰基基团,或具有7至20个C原子的芳氧基羰基基团,氰基基团(-CN),氨基甲酰基基团(-C(=O)NH
2),卤甲酰基基团(-C(=O)-X其中X代表卤素原子),甲酰基基团(-C(=O)-H),异氰基基团,异氰酸酯基团,硫氰酸酯基团或异硫氰酸酯基团,羟基基团,硝基基团,CF
3基团,Cl,Br,F,可交联的基团或者具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合;其中一个或多个R
1基团可以彼此和/或与其键合的基团形成环系;
L为连接基团,选自单键、C6-C60的亚芳基、亚芴基、C2-C60的杂芳香基团、C3-C60的脂肪族环、C6-C60的芳香族环的稠环基,以及上述组成的组合;
Ar选自具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或是具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合,其中一个或多个Ar基团可以彼此和/或与其键合的环形成单环或多环的脂族或芳族环系。
一种高聚物,包含至少一个重复单元,所述重复单元包含一种上述的有机化合物对应的结构。
一种混合物,至少包含有机化合物H1和有机化合物H2,所述有机化合物H1选自上述的有机化合物或高聚物,所述有机化合物H2是至少另一种有机功能材料,且选自空穴注入材料,空穴传输材料,电子传输材料,电子注入材料,电子阻挡材料,空穴阻挡材料,发光材料,主体材料和有机染料中的一种或多种。
优选的,在上述的混合物中,所述有机化合物H2具有如下通式(III)所示的结构:
其中,A选自取代或未取代的碳原子数1-30的烷基、取代或未取代的碳原子数3-30的环烷基、取代或未取代的环原子数为5-60芳香族烃基或芳香族杂环基;D为富电子基团;p为1-6的任一整数。
一种组合物,所述组合物包含至少一种上述的有机化合物或高聚物,及至少一种有机溶剂。
一种有机电子器件,所述有机电子器件包含一功能层,所述功能层包含一种上述的有机化合物或上述的高聚物或上述的混合物。
有益效果:将本发明的有机化合物用于OLED中,特别是作为发光层材料,能提供较优器件性能。其可能的原因如下,但不限于此,本发明的有机化合物具有较平衡的载流子传输性能,有利于提高相关材料和器件的效率和寿命。
本发明提供一类有机化合物,包含其的混合物和组合物及其应用。为使本发明的目的、技术方案及效果更加清楚、明确,以下对本发明进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
在本发明中,组合物和印刷油墨,或油墨具有相同的含义,它们之间可以互换。
在本发明中,主体材料,基质材料,Host或Matrix材料具有相同的含义,它们之间可以 互换。
在本发明中,“取代”表示被取代基中的氢原子被取代基所取代。
在本发明中,“环原子数”表示原子键合成环状而得到的结构化合物(例如,单环化合物、稠环化合物、交联化合物、碳环化合物、杂环化合物)的构成该环自身的原子之中的原子数。该环被取代基所取代时,取代基所包含的原子不包括在成环原子内。关于以下所述的“环原子数”,在没有特别说明的条件下也是同样的。例如,苯环的环原子数为6,萘环的环原子数为10,噻吩基的环原子数为5。
在本发明实施例中,有机材料的能级结构,单线态能级E
S1、三线态能级E
T、HOMO、LUMO起着关键的作用。以下对这些能级的确定做一介绍。
HOMO和LUMO能级可以通过光电效应进行测量,例如XPS(X射线光电子光谱法)和UPS(紫外光电子能谱)或通过循环伏安法(以下简称CV)。最近,量子化学方法,例如密度泛函理论(以下简称DFT),也成为行之有效的计算分子轨道能级的方法。
有机材料的单线态能级E
S1可通过发光光谱来确定,三线态能级E
T1可通过低温时间分辨发光光谱来测量。E
S1和E
T1还可以通过量子模拟计算(如通过Time-dependent DFT)得到,如通过商业软件Gaussian 03W(Gaussian Inc.),具体的模拟方法可参见WO2011141110或如下在实施例中所述。ΔE
ST定义为(E
S1-E
T1)。
应该注意,HOMO、LUMO、E
S1、E
T1的绝对值取决于所用的测量方法或计算方法,甚至对于相同的方法,不同评价的方法,例如在CV曲线上起始点和峰点可给出不同的HOMO/LUMO值。因此,合理有意义的比较应该用相同的测量方法和相同的评价方法进行。本发明实施例的描述中,HOMO、LUMO、E
S1、E
T1的值是基于Time-dependent DFT的模拟,但不影响其他测量或计算方法的应用。
在发明中,(HOMO-1)定义为第二高的占有轨道能级,(HOMO-2)为第三高的占有轨道能级,以此类推。(LUMO+1)定义为第二低的未占有轨道能级,(LUMO+2)为第三低的占有轨道能级,以此类推。
本发明涉及一种有机化合物,具有如通式(I)所示的结构:
其中:X独立表示为N或CR
1,且至少一个X为CR
1,当相邻的X为CR
1时可相互稠合成环。
R
1选自H、D、具有1至20个C原子的直链烷基、烷氧基或硫代烷氧基基团,或者具有3至20个C原子的支链或环状的烷基、烷氧基或硫代烷氧基基团或者是甲硅烷基基团,或具有1至20个C原子的取代的酮基基团,或具有2至20个C原子的烷氧基羰基基团,或具有7至20个C原子的芳氧基羰基基团,氰基基团(-CN),氨基甲酰基基团(-C(=O)NH
2),卤甲酰基基团(-C(=O)-X其中X代表卤素原子),甲酰基基团(-C(=O)-H),异氰基基团,异氰酸酯基团,硫氰酸酯基团或异硫氰酸酯基团,羟基基团,硝基基团,CF
3基团,Cl,Br,F,可交联的基团,或者具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或具有5至40个环原子的芳氧基或杂芳氧基基团,或这些体系的组合;其中一个或多个基团可以彼此和/或与其键合的基团形成环系。L为连接基团,选自单键,C6-C60的亚芳基,亚芴基,C2-C60的杂芳香基团,C3-C60的脂肪族环,C6-C60的芳香族环的稠环基,以及上述基团的组合。Ar选自具有5 至40个环原子的取代或未取代的芳香基团或杂芳香基团,或是具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合,其中一个或多个Ar基团可以彼此和/或与其键合的环形成单环或多环的脂族或芳族环系。
在一些优选的实施例中,R
1每次出现时,可分别独立选自D、氰基、具有1~18个C原子的直链烷基,或具有3~18个C原子的支链或环状的烷基、烷氧基、硫代烷氧基或甲硅烷基,或具有5~30个环原子的取代或未取代的芳香基团、杂芳香基团、芳氧基或杂芳氧基;在更加优选的实施例中,R
1~R
4每次出现分别独立选自D、具有1~12个C原子的直链烷基,或具有5~20个环原子的取代或未取代的芳香基团、杂芳香基团、芳氧基或杂芳氧基;在最为优选的实施例中,R
1~R
4每次出现分别独立选自D、具有1~6个C原子的直链烷基,或具有5~15个环原子的取代或未取代的芳香基团、杂芳香基团、芳氧基或杂芳氧基。
在一些优选的实施例中,R
1每次出现时,可分别全部氘化或部分氘化。
在一些优选的实施例中,通式(I)中的X均为CR
1,且相邻的CR
1可稠合成环。
在一个特别优先的实施例中,所述的有机化合物具有如通式(II)所示的结构:
其中,L和Ar含义如上所述。R
2-R
14是取代基,在每次出现时,相同或不同地选自H、D,或具有1至20个C原子的直链烷基、烷氧基或硫代烷氧基基团,或具有3至20个C原子的支链或环状的烷基、烷氧基、硫代烷氧基基团或甲硅烷基基团,或具有1至20个C原子的取代的酮基基团,或具有2至20个C原子的烷氧基羰基基团,或具有7至20个C原子的芳氧基羰基基团,氰基基团,氨基甲酰基基团,卤甲酰基基团,甲酰基基团,异氰基基团,异氰酸酯基团,硫氰酸酯基团,异硫氰酸酯基团,羟基基团,硝基基团,CF
3基团,Cl,Br,F,可交联的基团,或具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合;其中一个或多个R
2、R
3、R
4、R
5、R
6、R
7、R
8、R
9、R
10、R
11、R
12、R
13、R
14基团可以彼此和/或与其键合的基团形成环系。
在一些优选的实施例中,所述有机化合物中的R
1~R
14、L、Ar可相同或不同地选自如下基团中的一种或它们中的组合:
其中:V在多次出现时,相互独立的选自CR
15或者N;W选自CR
16R
17,SiR
18R
19,NR
20或,C(=O),S或O;Ar
1和Ar
2的定义如上述的Ar;R
15-R
20是取代基,在每次出现时,相同或不同地选自H、D,或具有1至20个C原子的直链烷基、烷氧基或硫代烷氧基基团,或具有3至20个C原子的支链或环状的烷基、烷氧基、硫代烷氧基基团或甲硅烷基基团,或具有1至20个C原子的取代的酮基基团,或具有2至20个C原子的烷氧基羰基基团,或具有7至20个C原子的芳氧基羰基基团,氰基基团,氨基甲酰基基团,卤甲酰基基团,甲酰基基团,异氰基基团,异氰酸酯基 团,硫氰酸酯基团,异硫氰酸酯基团,羟基基团,硝基基团,CF
3基团,Cl,Br,F,可交联的基团,或具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合;其中一个或多个R
15、R
16、R
17、R
18、R
19、R
20基团可以彼此和/或与其键合的基团形成环系。
进一步的,R
15-R
20每次出现分别独立选自D、氰基、具有1~18个C原子的直链烷基,或具有3~18个C原子的支链或环状的烷基、烷氧基、硫代烷氧基或甲硅烷基,或具有5~30个环原子的取代或未取代的芳香基团、杂芳香基团、芳氧基或杂芳氧基;在更加优选的实施例中,R
5-R
7每次出现时相同或不同地选自D、具有1~12个C原子的直链烷基,或具有5~20个环原子的取代或未取代的芳香基团、杂芳香基团、芳氧基或杂芳氧基;在最为优选的实施例中,R
5-R
7每次出现时相同或不同地选自D、具有1~6个C原子的直链烷基,或具有5~15个环原子的取代或未取代的芳香基团、杂芳香基团、芳氧基或杂芳氧基。
在一个优先的实施例中,L是二联苯,或其中的一个或多个碳原子被N原子取代的结构。
在另一个优先的实施例中,L是苯,或其中的一个或多个碳原子被N原子取代的结构。
在一些更加优选的实施例中,上述有机化合物中L优选自包含如下的化学式的结构中的一个或多个的组合,其中环上的H可以被任意取代:
在一些最为优选的实施例中,上述有机化合物中L可包含如下化学式所示的结构,其中环上的H可以被任意取代:
Ar每次出现选自具有5~40个环原子的取代或未取代的芳香基团、杂芳香基团、芳氧基或杂芳氧基基团,或这些体系的组合,其中一个或多个Ar基团彼此和/或与其键合的环形成多环的脂族或芳族环系。
在一些较为优先的实施例中,Ar可选自氘代或未氘代的具有5至20个环原子的取代或未取代的芳族或杂芳族环系,或是氘代或未氘代的具有5至20个环原子的芳氧基或杂芳氧基基团,或这些体系的组合,其中一个或多个Ar基团可以彼此和/或与其键合的环形成单环或多环的脂族或芳族环系。
在一些更为优先的实施例中,Ar可选自氘代或未氘代的具有5至15个环原子的取代或未取代的芳香基团或杂芳香基团,或是氘代或未氘代的具有5至15个环原子的芳氧基或杂芳氧基基团,或这些体系的组合,其中一个或多个Ar基团可以彼此和/或与其键合的环形成单环或多环的脂族或芳族环系。
在另一些优先的实施例中,Ar选自苯、萘、菲、苯并菲、二联苯、三联苯,或这些结构中的一个或多个碳原子被N原子取代。
在本发明中,“芳香基团”指至少包含一个芳环的烃基,包括单环基团和多环的环***。“杂芳香基团”指包含至少一个芳杂环的烃基(含有杂原子),包括单环基团和多环的环***。这些多环的环可以具有两个或多个环,其中两个碳原子被两个相邻的环共用,即稠环。多环的这些环种,至少一个是芳香族的或芳杂族的。对于本发明的目的,芳香基团或杂芳香基团不仅包括芳香基或芳杂基的体系,而且,其中多个芳香基或芳杂基也可以被短的非芳族单元间断(如C、N、O、Si、S或P原子)。因此,比如9,9'-螺二芴,9,9-二芳基芴,三芳胺,二芳基醚等体系,对于该发明目的同样认为是芳香基团。
具体地,芳香基团的例子有:苯、萘、蒽、菲、二萘嵌苯、并四苯、芘、苯并芘、三亚苯、苊、芴、及其衍生物。
具体地,杂芳香基团的例子有:呋喃、苯并呋喃、噻吩、苯并噻吩、吡咯、吡唑、***、咪唑、噁唑、噁二唑、噻唑、四唑、吲哚、咔唑、吡咯并咪唑、吡咯并吡咯、噻吩并吡咯、噻吩并噻吩、呋喃并吡咯、呋喃并呋喃、噻吩并呋喃、苯并异噁唑、苯并异噻唑、苯并咪唑、吡啶、吡嗪、哒嗪、嘧啶、三嗪、喹啉、异喹啉、邻二氮萘、喹喔啉、菲啶、伯啶、喹唑啉、喹唑啉酮、及其衍生物。
在特别优选的实施例中,按照本发明的有机化合物具有电子传输功能。
在某些优选的实施例中,上述的有机化合物,Ar包含一吸电子基团或被吸电子基团所取代。合适的吸电子基团可选自F、氰基或如下基团中的一种:
其中,n为1、2或3;X
1-X
8选于CR
5或N,并且至少有一个是N;同时任意两个相邻位置的R
5可以成单环或多环的脂族或芳族环系;M
1、M
2、M
3分别独立表示N(R
6)、C(R
7)
2、Si(R
8)
2、O、C=N(R
9)、C=C(R
10)
2、P(R
11)、P(=O)R
12、S、S=O、SO
2或无;R
1-R
12的含义同上述R
1,R
1-R
12可以彼此相同或不同,且R
1-R
12中的任一基团在多次出现时可相同或不同。
在另一些优选的实施例中,上述的有机化合物,所述吸电子基团选自如下基团中的一种或多种的组合:
在某些优选的实施方案中,按照本发明的有机化合物具有较小的单线态-三线态能级差,一般是ΔE
st≤0.3eV,较好是ΔE
st≤0.2eV,更好是ΔE
st≤0.15eV,最好是ΔE
st≤0.10eV。
下面列出按照本发明的通式(I-1)和(I-2)所示的有机化合物的具体例子,但并不限定于此。
在一个较为优选的实施例中,按照通式(I)的有机化合物,其中至少有一个X选自N。
在某些实施例中,按照通式(I)的有机化合物,其中至少有两个个X选自N。
在一个优选的实施方案中,按照本发明的有机化合物选自如下通式中的一种:
其中R
1-R
14,L和Ar的定义如上述。
下面列出按照本发明的通式(I-1)所示的且在核心结构上至少有一个氮杂的有机化合物的具体例子,但并不限定于此。
在一个优选的实施例中,按照本发明的有机化合物,其玻璃化温度Tg≥100℃。在一个优选的实施例中,其Tg≥120℃。在一个较为优选的实施例中,其Tg≥140℃。在一个更为优选的实施例中,其Tg≥160℃。在一个最为优选的实施例中,其Tg≥180℃。
在一个较为优选的实施例中,按照本发明的有机化合物,是部分被氘代,较好是10%的H被氘代,更好是20%的H被氘代,很好是30%的H被氘代,最好是40%的H被氘代。
在一个优选的实施例中,按照本发明的有机化合物是一种小分子材料。
在一个优选的实施方案中,按照本发明的有机化合物用于蒸镀性OLED器件。用于这个目的,按照本发明的化合物,其分子量≤1000g/mol,优选≤900g/mol,很优选≤850g/mol,更优选≤800g/mol,最优选≤700g/mol。
本发明还涉及一种按照通式(I)的有机化合物的合成方法,其中使用含有活性基团的原料进行反应。这些活性原料包含至少一种离去基团,例如,溴,碘,硼酸或硼酸酯。形成C-C连接的适当的反应是本领域技术人员熟知的并描述于文献中,特别适当和优选的偶联反应是SUZUKI,STILLE和HECK偶联反应。
本发明还涉及一种高聚物,包含至少一个重复单元,其中至少有一个重复单元包含有如通式(I)所示的结构。在某些实施例中,所述的高聚物是非共轭高聚物,其中如通式(I)所示的结构单元在侧链上。在另一个优选的实施例中,所述的高聚物是共轭高聚物。本文中所定义的术语“小分子”是指不是聚合物,低聚物,树枝状聚合物,或共混物的分子。特别是,小分子中没有重复结构。小分子的分子量≤3000g/mol,较好是≤2000g/mol,最好是≤1500g/mol。
高聚物,即Polymer,包括均聚物(homopolymer),共聚物(copolymer),镶嵌共聚物(block copolymer)。另外在本发明中,高聚物也包括树状物(dendrimer),有关树状物的合成及应用请参见[Dendrimers and Dendrons,Wiley-VCH Verlag GmbH&Co.KGaA,2002,Ed.George R.Newkome,Charles N.Moorefield,Fritz Vogtle.]。
共轭高聚物(conjugated polymer)是一高聚物,它的主链backbone主要是由C原子的sp2杂化轨道构成,著名的例子有:聚乙炔polyacetylene和poly(phenylene vinylene),其主链上的C原子的也可以被其他非C原子取代,而且当主链上的sp2杂化被一些自然的缺陷打断时,仍然被认为是共轭高聚物。另外在本发明中共轭高聚物也包括主链上包含有芳基胺(aryl amine)、芳基磷化氢(aryl phosphine)及其他杂环芳烃(heteroarmotics)、有机金属络合物(organometallic complexes)等。
在一个优选的实施例中,其中的高聚物的合成方法选自SUZUKI-,YAMAMOTO-,STILLE-, NIGESHI-,KUMADA-,HECK-,SONOGASHIRA-,HIYAMA-,FUKUYAMA-,HARTWIG-BUCHWALD-和ULLMAN。
在一个优先的实施例中,按照本发明的高聚物,其玻璃化温度(Tg)≥100℃,优选为≥120℃,更优为≥140℃,更更优为≥160℃,最优为≥180℃。
在一个优先的实施例中,按照本发明的高聚物,其分子量分布(PDI)取值范围优选为1~5;较优选为1~4;更优选为1~3,更更优选为1~2,最优选为1~1.5。
在一个优先的实施例中,按照本发明的高聚物,其重均分子量(Mw)取值范围优选为1万~100万;较优选为5万~50万;更优选为10万~40万,更更优选为15万~30万,最优选为20万~25万。
本发明还提供一种混合物,包含有机化合物H1和有机化合物H2,其中H1是按照本发明的有机化合物,H2是另一种有机功能材料,H2可选于空穴注入材料(HIM),空穴传输材料(HTM),p-dopant,电子传输材料(ETM),电子注入材料(EIM),电子阻挡材料(EBM),空穴阻挡材料(HBM),发光材料(Emitter),主体材料(Host)和有机染料。例如在US2017092880A1,US2018006247A1和EP3301097A2中对各种有机功能材料有详细的描述,特此将此3篇专利文件中的全部内容并入本文作为参考。
在一个优选的实施例中,所述的混合物,包含至少一种按照本发明的有机化合物或高聚物和一种空穴传输材料(HTM)。
在一个较优选的实施例中,所述的混合物,包含至少一种按照本发明的有机化合物或高聚物和一种发光材料,所述的发光材料选自单重态发光体(荧光发光体),三重态发光体(磷光发光体)或TADF发光体。
在某些实施例中,所述的混合物,包含至少一种按照本发明的有机化合物或高聚物和一种荧光发光体,其中所述的荧光发光体重量百分比为≤10wt%,较好是≤9wt%,更好是≤8wt%,特别好是≤7wt%,最好是≤5wt%。
在一个优选的实施例中,所述的混合物,包含至少一种按照本发明的有机化合物或高聚物和一种磷光发光体,其中所述的磷光发光体重量百分比为≤20wt%,较好是≤15wt%,更好是≤10wt%。
在另一个更优选的实施例中,所述的一种混合物,包含少一种按照本发明的有机化合物或高聚物,和一种TADF材料;其中TADF材料的功能优选为:1)与按照本发明的有机化合物形成共主体材料,其间的重量比从1:6到6:1;2)与按照本发明的有机化合物形成Exciplex,或用作辅助发光体,其中所述的TADF材料的重量百分比为≤15wt%,较好是≤10wt%,更好是≤8wt%。
在一个特别优选的实施例中,所述的混合物,包含至少一种按照本发明的有机化合物或高聚物和有机化合物H2(即另一种有机功能材料)。这样的混合物可以作为磷光混合主体材料,可以进一步包含一磷光发光体,其中所述的磷光发光体重量百分比为≤20wt%,较好是≤15wt%,更好是≤10wt%。
下面对所述的包含有机化合物H1和有机化合物H2的混合物作为磷光混合主体材料做一详细的说明。
在一个优先的实施例中,所述的H2具有空穴传输特性。
更为优选的,所述有机化合物H2具有空穴传输特性的同时也具有电子传输特性。
一般的,有机化合物H1与有机化合物H2的摩尔比范围为1:9至9:1。
优选地,有机化合物H1与有机化合物H2的摩尔比范围为3:7至7:3。
更优地,有机化合物H1与有机化合物H2的摩尔比范围为4:6至6:4。
最优地,有机化合物H1与有机化合物H2的摩尔比为5:5。
在一个优先的实施例中,所述的混合物中,有机化合物H2选自如下通式(III)所示的化合物:
其中,A选自取代或未取代的碳原子数1~30的烷基、取代或未取代的碳原子数3~30的环烷基、取代或未取代的环原子数为5~60芳香基团或杂芳香基团;D为富电子基团;p为1-6的任一整数。
在某些优选的实施例中,通式(III)中的富电子(或供电子)基团D,包含有如下任一基团:
其中,Ar
11表示环原子数为5~40的芳香基团或杂芳香基团;Z
1、Z
2、Z
3分别独立选自单键、CR
21R
22、SiR
23R
24、NR
25、O、C(=O)、S、S=O或SO
2,且Z
2和Z
3不同时为单键;R
13-R
25含义同R
1。
在一些更加优选的实施例中,通式(III)中包含的富电子(或供电子)基团D,包含有如下任一基团:
R
13、R
19、R
20、R
25的含义如上所述。
在某些优选的实施例中,p为1-4的任一整数;在更加优选的实施例中,p为1-3的任一整数;在最为优选的实施例中,p为1或2。
在一些较为优先的实施例中,按照本发明的混合物,其中有机化合物H2选自如下结构式中的一个:
其中,A的含义如上所述,Ar
3的含义与Ar相同。
某些实施例中,按照本发明的混合物中,H1和/或H2具有较高的三线态能级T1,一般是T1≥2.0eV,较优是T1≥2.1eV,更优是T1≥2.2eV,更更优是T1≥2.4eV,最优是T1≥2.6eV。
在某些优先的实施方案中,所述的有机混合物,其中H1和H2形成II型异质结结构,即H1的最高占有轨道能级(HOMO)低于H2的HOMO,H1的最低未占有轨道能级(LUMO)低于于H2的LUMO。
在一个更加优先的实施方案中,所述的混合物,min((LUMO(H1)-HOMO(H2),LUMO(H2)-HOMO(H1))≤min(ET(H1),ET(H2))+0.1eV,其中LUMO(H1),HOMO(H1)及ET(H1)分别是H1的最低未占有轨道,最高占有轨道,三线态的能级,LUMO(H2),HOMO(H2)及ET(H2)分别是H2的最低未占有轨道,最高占有轨道,三线态的能级。
在一个优先的实施例中,所述的混合物,min((LUMO(H1)-HOMO(H2),LUMO(H2)-HOMO(H1))≤min(ET(H1),ET(H2))。
在一个较为优先的实施例中,所述的混合物,min((LUMO(H1)-HOMO(H2),LUMO(H2)-HOMO(H1))≤min(ET(H1),ET(H2))-0.05eV。
在一个更为优先的实施例中,所述的混合物,min((LUMO(H1)-HOMO(H2),LUMO(H2)-HOMO(H1))≤min(ET(H1),ET(H2))-0.1eV。
在一个非常优先的实施例中,所述的混合物,min((LUMO(H1)-HOMO(H2),LUMO(H2)-HOMO(H1))≤min(ET(H1),ET(H2))-0.15eV。
在一个最为优先的实施例中,所述的混合物,min((LUMO(H1)-HOMO(H2),LUMO(H2)-HOMO(H1))≤min(ET(H1),ET(H2))-0.2eV。
下面举例按照通式(III)所示的有机化合物H2的具体例子,但并不限定于:
在一个较为优先的实施例中,按照本发明的混合物,其中H1和H2中至少有一个,优先是H1,其((LUMO+1)-LUMO)≥0.1eV,较好是≥0.15eV,更好是≥0.20eV,更更好是≥0.25eV,最好是≥0.30eV。
在另一个较为优先的实施例中,按照本发明的混合物,其中H1和H2中至少有一个,优先是H2,其(HOMO-(HOMO-1))≥0.2eV,较好是≥0.25eV,更好是≥0.30eV,更更好是≥0.35eV,最好是≥0.40eV。
在某些实施方案中,所述的有机混合物,其中H1和H2形成I型异质结结构,即H1的最高占有轨道能级(HOMO)高于H2的HOMO,H1的最低未占有轨道能级(LUMO)低于于H2的LUMO;较为优先的,所述的H1是按照本发明的化合物,而且其ΔE
st≤0.3eV,较好是ΔE
st≤0.2eV,更好是ΔE
st≤0.15eV,最好是ΔE
st≤0.10eV。
本发明的一个目的是为蒸镀型OLED提供材料解决方案。
在一个优选的实施方案中,按照本发明的混合物用于蒸镀性OLED器件。用于这个目的,按照本发明的稠环有机化合物或混合物中H1和H2,其分子量≤1000g/mol,优选≤900g/mol,很优选≤850g/mol,更优选≤800g/mol,最优选≤700g/mol。
在一个优选的实施例中,所述的混合物,其中H1和H2的分子量的差不超过100Dalton;优选的分子量的差不超过60Dalton;更加优选的分子量的差不超过30Dalton。
在另一个优选的实施例中,所述的混合物,其中H1和H2的升华温度的差不超过30K;优选的升华温度的差不超过20K;更加优选的升华温度的差不超过10K。
本发明的另一个目的是为印刷OLED提供材料解决方案。
用于这个目的,按照本发明的稠环有机化合物或混合物中的H1和H2,至少有一个较好是两个都,其分子量≥700g/mol,优选≥800g/mol,很优选≥900g/mol,更优选≥1000g/mol,最优选≥1100g/mol。
蒸镀型OLED中的以Premix形式的共主体中,要求两个主体材料具有类似的化学性质或物性,如分子量,升华温度。本发明发现,在溶液加工OLED中,两个具有不同性质的主体材料可能会提高成膜性能,从而提高器件的性能。所述的性质,除了分子量,升华温度外,还可以是其他的,如玻璃化温度,不同的分子体积等。从而印刷OLED,按照本发明的混合物的优先实施方案有:
1)H1的分子量和H2的分子量之差≥120g/mol,较好为≥140g/mol,更好为≥160g/mol,最好为≥180g/mol。
2)H1的升华温度和H2的升华温度之差≥60K,较好为≥70K,更好为≥75K,最好为≥80K。
3)H1的玻璃化温度和H2的玻璃化温度之差≥20K,较好为≥30K,更好为≥40K,最好为 ≥45K。
4)H1的分子体积和H2的分子体积之差≥20%,较好为≥30%,更好为≥40%,最好为≥45%。
在另一些实施例中,按照本发明的稠环有机化合物或混合物中H1和H2,至少有一个较好是两个都,在25℃时,在甲苯中的溶解度≥2mg/ml,优选≥3mg/ml,更优选≥4mg/ml,最优选≥5mg/ml。
在一个优选的实施例中,所述的混合物,其中H1和H2的摩尔比为从2:8到8:2;优选的摩尔比为3:7到7:3;更加优选的摩尔比为4:6到6:4。
下面对HTM,磷光发光体,磷光主体材料和TADF发光体作一些详细的描述(但不限于此)。
1.三重态主体材料(Triplet Host):
三重态主体材料的例子并不受特别的限制,任何金属络合物或有机化合物都可能被用作为主体,只要其三重态能级比发光体,特别是三重态发光体或磷光发光体更高,可用作三重态主体(Host)的金属络合物的例子包括(但不限于)如下的一般结构:
M3是一金属;(Y
3-Y
4)是一两齿配体,Y
3和Y
4独立地选自C,N,O,P,和S;L是一个辅助配体;r2是一整数,其值从1到此金属的最大配位数。
在一个优先的实施方案中,可用作三重态主体的金属络合物有如下形式:
(O-N)是一两齿配体,其中金属与O和N原子配位,r2是一整数,其值从1到此金属的最大配位数。
在某一个实施方案中,M3可选于Ir和P。
可作为三重态主体的有机化合物的例子选自包含有环芳香烃基的化合物,例如苯、联苯、三苯基苯、苯并芴;包含有芳香杂环基的化合物,如二苯并噻吩、二苯并呋喃、二苯并硒吩、呋喃、噻吩、苯并呋喃、苯并噻吩、苯并硒吩、咔唑、二苯并咔唑,吲哚咔唑、吡啶吲哚、吡咯二吡啶、吡唑、咪唑、***类、恶唑、噻唑、恶二唑、恶***、二恶唑、噻二唑、吡啶、哒嗪、嘧啶、吡嗪、三嗪类、恶嗪、恶噻嗪、恶二嗪、吲哚、苯并咪唑、吲唑、恶唑、二苯并恶唑、苯异恶唑、苯并噻唑、喹啉、异喹啉、邻二氮杂萘、喹唑啉、喹喔啉、萘、酞、蝶啶、氧杂蒽、吖啶、吩嗪、吩噻嗪、吩恶嗪、苯并呋喃吡啶、呋喃并吡啶、苯并噻吩吡啶、噻吩吡啶、苯并硒吩吡啶和硒吩苯并二吡啶;包含有2至10环结构的基团,它们可以是相同或不同类型的环芳香烃基团或芳香杂环基团,并彼此直接或通过至少一个以下的基团连结在一起,如氧原子、氮原子、硫原子、硅原子、磷原子、硼原子、链结构单元和脂肪环基团。其中,这些基团可以进一步被取代,取代基可选为氢、氘、氰基、卤素、烷基、烷氧基、氨基、烯、炔、芳烷基、杂烷基、芳基和杂芳基。
在一个优先的实施方案中,三重态主体材料可选于包含至少一个以下基团的化合物:
X
9选于CR
38R
39或NR
40;Y选自CR
41R
42或NR
43或O或S;R
26-R
43的含义同上述R
1;n2选自1-3的任一整数,X
1–X
8的含义同上所述,Ar
4~Ar
6的含义同上所述Ar
1。
在下面列出合适的三重态主体材料的例子但不局限于:
2.三重态发光体(Triplet Emitter)
三重态发光体也称磷光发光体。在一个优先的实施方案中,三重态发光体是有通式M(L)n的金属络合物,其中M是一金属原子,L每次出现时可以是相同或不同,是一有机配体,它通过一个或多个位置键接或配位连接到金属原子M上,n是一个大于1的整数,较好选是1,2,3,4,5或6。可选地,这些金属络合物通过一个或多个位置联接到一个聚合物上,最好是通过有机配体。
在一个优先的实施方案中,金属原子M选于过渡金属元素或镧系元素或锕系元素,优先选择Ir,Pt,Pd,Au,Rh,Ru,Os,Sm,Eu,Gd,Tb,Dy,Re,Cu或Ag,特别优先选择Os,Ir,Ru,Rh,Re,Pd,Au或Pt。
优先地,三重态发光体包含有螯合配体,即配体,通过至少两个结合点与金属配位,特别优先考虑的是三重态发光体包含有两个或三个相同或不同的双齿或多齿配体。螯合配体有利于提高金属络合物的稳定性。
有机配体的例子可选自苯基吡啶衍生物,7,8-苯并喹啉衍生物,2(2-噻吩基)吡啶衍生物,2(1-萘基)吡啶衍生物,或2苯基喹啉衍生物。所有这些有机配体都可能被取代,例如被含氟或三氟甲基取代。辅助配体可优先选自乙酸丙酮或苦味酸。
在一个优先的实施方案中,可用作三重态发光体的金属络合物有如下形式:
其中M是一金属,选于过渡金属元素或镧系或锕系元素,特别优先的是Ir,Pt,Au。
Ar
7每次出现时可以是相同或不同,是一个环状基团,其中至少包含有一个施主原子,即有一孤对电子的原子,如氮或磷,通过它环状基团与金属配位连接;Ar
8每次出现时可以是相同或不同,是一个环状基团,其中至少包含有一个C原子,通过它环状基团与金属连接;Ar
7和Ar
8由共价键联接在一起,可各自携带一个或多个取代基团,它们也可再通过取代基团联接在一起;L'每次出现时可以是相同或不同,是一个双齿螯合的辅助配体,最好是单阴离子双齿螯合配体;q1可以是0,1,2或3,优先地是2或3;q2可以是0,1,2或3,优先地是1或0。
一些三重态发光体的材料极其应用的例子可在下述专利文件和文献中找到:WO 200070655,WO 200141512,WO 200202714,WO 200215645,EP 1191613,EP 1191612,EP 1191614,WO 2005033244,WO 2005019373,US 2005/0258742,WO 2009146770,WO 2010015307,WO 2010031485,WO 2010054731,WO 2010054728,WO 2010086089,WO 2010099852,WO 2010102709,US 20070087219 A1,US 20090061681 A1,US 20010053462 A1,Baldo,Thompson et al.Nature 403,(2000),750-753,US 20090061681 A1,US 20090061681 A1,Adachi et al.Appl.Phys.Lett.78(2001),1622-1624,J.Kido et al.Appl.Phys.Lett.65(1994),2124,Kido et al.Chem.Lett.657,1990,US 2007/0252517 A1,Johnson et al.,JACS 105,1983,1795,Wrighton,JACS 96,1974,998,Ma et al.,Synth.Metals 94,1998,245,US 6824895,US 7029766,US 6835469,US 6830828,US 20010053462 A1,WO 2007095118 A1,US 2012004407A1,WO 2012007088A1,WO2012007087A1,WO 2012007086A1,US 2008027220A1,WO 2011157339A1,CN 102282150A,WO 2009118087A1,WO 2013107487A1,WO 2013094620A1,WO 2013174471A1,WO 2014031977A1,WO 2014112450A1,WO 2014007565A1,WO 2014038456A1,WO 2014024131A1,WO 2014008982A1,WO2014023377A1。特此将上述列出的专利文件和文献中的全部内容并入本文作为参考。
在下面列出一些合适的三重态发光体的例子:
3.TADF材料
传统有机荧光材料只能利用电激发形成的25%单线态激子发光,器件的内量子效率较低(最高为25%)。尽管磷光材料由于重原子中心强的自旋-轨道耦合增强了系间穿越,可以有效利用电激发形成的单线态激子和三线态激子发光,使器件的内量子效率达到100%。但磷光材料昂贵,材料稳定性差,器件效率滚降严重等问题限制了其在OLED中的应用。热激活延迟荧光发光材料是继有机荧光材料和有机磷光材料之后发展的第三代有机发光材料。该类材料一般具有小的单线态-三线态能级差(ΔEst),三线态激子可以通过反系间穿越转变成单线态激子发光。这可以充分利用电激发下形成的单线态激子和三线态激子。器件内量子效率可达到100%。同时材料结构可控,性质稳定,价格便宜无需要贵金属,在OLED领域的应用前景广阔。
TADF材料需要具有较小的单线态-三线态能级差,较好是ΔEst<0.3eV,次好是ΔEst<0.2eV,最好是ΔEst<0.1eV。在一个优先的实施方案中,TADF材料有比较小的ΔEst,在另一个优先的实施方案中,TADF有较好的荧光量子效率。一些TADF发光的材料可在下述专利文件中找到:CN103483332(A),TW201309696(A),TW201309778(A),TW201343874(A),TW201350558(A),US20120217869(A1),WO2013133359(A1),WO2013154064(A1),Adachi,et.al.Adv.Mater.,21,2009,4802,Adachi,et.al.Appl.Phys.Lett.,98,2011,083302,Adachi,et.al.Appl.Phys.Lett.,101,2012,093306,Adachi,et.al.Chem.Commun.,48,2012,11392,Adachi,et.al.Nature Photonics,6,2012,253,Adachi,et.al.Nature,492,2012,234,Adachi,et.al.J.Am.Chem.Soc,134,2012,14706,Adachi,et.al.Angew.Chem.Int.Ed,51,2012,11311,Adachi,et.al.Chem.Commun.,48,2012,9580,Adachi,et.al.Chem.Commun.,48,2013,10385,Adachi,et.al.Adv.Mater.,25,2013,3319,Adachi,et.al.Adv.Mater.,25,2013,3707,Adachi,et.al.Chem.Mater.,25,2013,3038,Adachi,et.al.Chem.Mater.,25,2013,3766,Adachi,et.al.J.Mater.Chem.C.,1,2013,4599,Adachi,et.al.J.Phys.Chem.A.,117,2013,5607,特此将上述列出的专利或文章文件中的全部内容并入本文作为参考。
在下面列出一些合适的TADF发光材料的例子:
4.HTM
合适的有机HTM材料可选包含有如下结构单元的化合物:酞菁、卟啉、胺、芳香胺、联苯类三芳胺、噻吩、并噻吩、吡咯、苯胺、咔唑、氮茚并氮芴及它们的衍生物。
可用作HTM的环芳香胺衍生化合物的例子包括(但不限于)如下的一般结构:
每个Ar
1~Ar
9可独立选自环芳香烃化合物,如苯、联苯、三苯基、苯并、萘、蒽、非那烯、菲、芴、芘、屈、苝、薁;芳香杂环化合物,如二苯并噻吩、二苯并呋喃、呋喃、噻吩、苯并呋喃、苯并噻吩、咔唑、吡唑、咪唑、三氮唑、异恶唑、噻唑、恶二唑、恶***、二恶唑、噻二唑、吡啶、哒嗪、嘧啶、吡嗪、三嗪、恶嗪、恶噻嗪、恶二嗪、吲哚、苯并咪唑、吲唑、吲哚嗪、苯并恶唑、苯异恶唑、苯并噻唑、喹啉、异喹啉、邻二氮(杂)萘、喹唑啉、喹喔啉、萘、酞、蝶啶、氧杂蒽、吖啶、吩嗪、吩噻嗪、吩恶嗪、二苯并硒吩、苯并硒吩、苯并呋喃吡啶、吲哚咔唑、吡啶吲哚、吡咯二吡啶、呋喃二吡啶、苯并噻吩吡啶、噻吩吡啶、苯并硒吩吡啶和硒吩二吡啶;包含有2至10环结构的基团,它们可以是相同或不同类型的环芳香烃基团或芳香杂环基团,并彼此直接或通过至少一个以下的基团连结在一起,如氧原子、氮原子、硫原子、硅原子、磷原子、硼原子、链结构单元和脂肪环基团。其中,Ar
1~Ar
9可以进一步被取代,取代基可选为氢、氘、烷基、烷氧基、氨基、烯、炔、芳烷基、杂烷基、芳基和杂芳基。
在一个方面,Ar
1~Ar
9可独立选自包含如下结构单元的基团:
n是1到20的整数;X
1到X
8是CH或N;Ar
10定义同Ar
1。
环芳香胺衍生化合物的另外的例子可参见US3567450,US4720432,US5061569,US3615404和US5061569。
在下面的表中列出合适的可作为HTM化合物的例子:
本发明进一步涉及一种组合物或油墨,包含如上任一项所述的稠环有机化合物或混合物,及至少一种有机溶剂。
用于印刷工艺时,油墨的粘度,表面张力是重要的参数。合适的油墨的表面张力参数适合于特定的基板和特定的印刷方法。
在一个优选的实施例中,按照本发明的油墨在工作温度或在25℃下的表面张力约在19dyne/cm到50dyne/cm范围;更好是在22dyne/cm到35dyne/cm范围;最好是在25dyne/cm到33dyne/cm范围。
在另一个优选的实施例中,按照本发明的油墨在工作温度或25℃下的粘度约在1cps到100cps范围;较好是在1cps到50cps范围;更好是在1.5cps到20cps范围;最好是在4.0cps到20cps范围。如此配制的组合物将便于喷墨印刷。
粘度可以通过不同的方法调节,如通过合适的溶剂选取和油墨中功能材料的浓度。按照本发明的包含有所述地金属有机配合物或高聚物的油墨可方便人们将印刷油墨按照所用的印刷方法在适当的范围调节。一般地,按照本发明的组合物包含的功能材料的重量比为0.3%~30wt%范围,较好的为0.5%~20wt%范围,更好的为0.5%~15wt%范围,更更好的为0.5%~10wt%范围,最好的为1%~5wt%范围。
按照本发明的一种组合物,所述的至少一种有机溶剂选自芳族或杂芳族、酯、芳族酮或芳族醚、脂肪族酮或脂肪族醚、脂环族或烯烃类化合物,或硼酸酯或磷酸酯类化合物,或两种及两种以上溶剂的混合物。
在一个优选的实施例中,按照本发明的一种组合物,所述的至少一种有机溶剂选自基于芳族或杂芳族的溶剂。
适合本发明的基于芳族或杂芳族溶剂的例子有,但不限制于:对二异丙基苯、戊苯、四氢萘、环己基苯、氯萘、1,4-二甲基萘、3-异丙基联苯、对甲基异丙苯、二戊苯、三戊苯、戊基甲苯、邻二乙苯、间二乙苯、对二乙苯、1,2,3,4-四甲苯、1,2,3,5-四甲苯、1,2,4,5-四甲苯、丁苯、十二烷基苯、二己基苯、二丁基苯、对二异丙基苯、环己基苯、苄基丁基苯、二甲基萘、3-异丙基联苯、对甲基异丙苯、1-甲基萘、1,2,4-三氯苯、4,4-二氟二苯甲烷、1,2-二甲氧基-4-(1-丙烯基)苯、二苯甲烷、2-苯基吡啶、3-苯基吡啶、N-甲基二苯胺、4-异丙基联苯、二氯二苯甲烷、4-(3-苯基丙基)吡啶、苯甲酸苄酯、1,1-双(3,4-二甲基苯基)乙烷、2-异丙基萘、喹啉、异喹啉、2-呋喃甲酸甲酯、2-呋喃甲酸乙酯等。
适合本发明的基于芳族酮溶剂的例子有,但不限制于:1-四氢萘酮,2-四氢萘酮,2-(苯基环氧)四氢萘酮,6-(甲氧基)四氢萘酮,苯乙酮、苯丙酮、二苯甲酮、及它们的衍生物,如 4-甲基苯乙酮、3-甲基苯乙酮、2-甲基苯乙酮、4-甲基苯丙酮、3-甲基苯丙酮、2-甲基苯丙酮等。
适合本发明的基于芳族醚溶剂的例子有,但不限制于:3-苯氧基甲苯、丁氧基苯、对茴香醛二甲基乙缩醛、四氢-2-苯氧基-2H-吡喃、1,2-二甲氧基-4-(1-丙烯基)苯、1,4-苯并二噁烷、1,3-二丙基苯、2,5-二甲氧基甲苯、4-乙基本***、1,3-二丙氧基苯、1,2,4-三甲氧基苯、4-(1-丙烯基)-1,2-二甲氧基苯、1,3-二甲氧基苯、缩水甘油基苯基醚、二苄基醚、4-叔丁基茴香醚、反式-对丙烯基茴香醚、1,2-二甲氧基苯、1-甲氧基萘、二苯醚、2-苯氧基甲醚、2-苯氧基四氢呋喃、乙基-2-萘基醚。
在一些优选的实施例中,按照本发明的组合物,所述的至少一种的有机溶剂可选自:脂肪族酮,例如,2-壬酮、3-壬酮、5-壬酮、2-癸酮、2,5-己二酮、2,6,8-三甲基-4-壬酮、葑酮、佛尔酮、异佛尔酮、二正戊基酮等;或脂肪族醚,例如,戊醚、己醚、二辛醚、乙二醇二丁醚、二乙二醇二***、二乙二醇丁基甲醚、二乙二醇二丁醚、三乙二醇二甲醚、三乙二醇乙基甲醚、三乙二醇丁基甲醚、三丙二醇二甲醚、四乙二醇二甲醚等。
在另一些优选的实施例中,按照本发明的组合物,所述的至少一种的有机溶剂可选自基于酯的溶剂:辛酸烷酯、癸二酸烷酯、硬脂酸烷酯、苯甲酸烷酯、苯乙酸烷酯、肉桂酸烷酯、草酸烷酯、马来酸烷酯、烷内酯、油酸烷酯等。特别优选辛酸辛酯、癸二酸二乙酯、邻苯二甲酸二烯丙酯、异壬酸异壬酯。
所述的溶剂可以是单独使用,也可以是作为两种或多种有机溶剂的混合物使用。
在某些优选的实施例中,按照本发明的一种组合物,包含如上任一项所述的稠环有机化合物或混合物,及至少一种有机溶剂,还可进一步包含另一种有机溶剂,另一种有机溶剂的例子,包括(但不限于):甲醇、乙醇、2-甲氧基乙醇、二氯甲烷、三氯甲烷、氯苯、邻二氯苯、四氢呋喃、苯甲醚、吗啉、甲苯、邻二甲苯、间二甲苯、对二甲苯、1,4二氧杂环己烷、丙酮、甲基乙基酮、1,2二氯乙烷、3-苯氧基甲苯、1,1,1-三氯乙烷、1,1,2,2-四氯乙烷、醋酸乙酯、醋酸丁酯、二甲基甲酰胺、二甲基乙酰胺、二甲基亚砜、四氢萘、萘烷、茚和/或它们的混合物。
本发明还涉及所述的一种组合物作为印刷油墨在制备有机电子器件时的用途,特别优选的是通过打印或涂布的制备方法。
其中,适合的打印或涂布技术包括(但不限于)喷墨打印,活版印刷,丝网印刷,浸涂,旋转涂布,刮刀涂布,辊筒印花,扭转辊印刷,平版印刷,柔版印刷,轮转印刷,喷涂,刷涂或移印,狭缝型挤压式涂布等。首选的是凹版印刷,丝网印刷及喷墨印刷。凹版印刷,喷墨印刷将在本发明的实施例中应用。溶液或悬浮液可以另外包括一个或多个组份例如表面活性化合物,润滑剂,润湿剂,分散剂,疏水剂,粘接剂等,用于调节粘度,成膜性能,提高附着性等。有关打印技术,及其对有关溶液的相关要求,如溶剂及浓度,粘度等,的详细信息请参见Helmut Kipphan主编的《印刷媒体手册:技术和生产方法》(Handbook of Print Media:Technologies and Production Methods),ISBN 3-540-67326-1。
如上所述的制备方法,形成的一功能层,其厚度在5nm-1000nm。
本发明还涉及如上所述稠环有机化合物或混合物在有机电子器件中的应用。
本发明进一步涉及一种有机电子器件,包含一种如上所述的稠环有机化合物或高聚物或混合物。
所述的有机电子器件可选于,但不限于,有机发光二极管(OLED),有机光伏电池(OPV),有机发光电池(OLEEC),有机场效应管(OFET),有机发光场效应管,有机激光器,有机自旋电子器件,光电二极管,有机传感器及有机等离激元发射二极管(Organic Plasmon Emitting Diode)等,特别优选的是有机电致发光器件,如OLED,OLEEC,有机发光场效应管。
在某些特别优先的实施例中,所述有机电子器件为有机电致发光器件,其中至少包含有一发光层,所述的发光层包含一种如上所述的稠环有机化合物或混合物。
在以上所述的有机电致发光器件,特别是OLED中,包括一基片,一阳极,至少一发光层,一阴极。
基片可以是不透明或透明。一个透明的基板可以用来制造一个透明的发光元器件。例如可参见,Bulovic等Nature 1996,380,p29,和Gu等,Appl.Phys.Lett.1996,68,p2606。基片可以是刚性的或弹性的。基片可以是塑料,金属,半导体晶片或玻璃。最好是基片有一个平滑的表面。无表面缺陷的基板是特别理想的选择。在一个优选的实施例中,基片是柔性的,可选于聚合物薄膜或塑料,其玻璃化温度Tg为150℃以上,较好是超过200℃,更好是超过250℃,最好是超过300℃。合适的柔性基板的例子有聚(对苯二甲酸乙二醇酯)(PET)和聚乙二醇(2,6-萘)(PEN)。
阳极可包括一导电金属或金属氧化物,或导电聚合物。阳极可以容易地注入空穴到空穴注入层(HIL)或空穴传输层(HTL)或发光层中。在一个优选的实施例中,阳极的功函数和发光层中的发光体或作为HIL或HTL或电子阻挡层(EBL)的p型半导体材料的HOMO能级或价带能级的差的绝对值小于0.5eV,较好是小于0.3eV,最好是小于0.2eV。阳极材料的例子包括但不限于:Al、Cu、Au、Ag、Mg、Fe、Co、Ni、Mn、Pd、Pt、ITO、铝掺杂氧化锌(AZO)等。其他合适的阳极材料是已知的,本领域普通技术人员可容易地选择使用。阳极材料可以使用任何合适的技术沉积,如一合适的物理气相沉积法,包括射频磁控溅射,真空热蒸发,电子束(e-beam)等。在某些实施例中,阳极是图案结构化的。图案化的ITO导电基板可在市场上买到,并且可以用来制备根据本发明的器件。
阴极可包括一导电金属或金属氧化物。阴极可以容易地注入电子到EIL或ETL或直接到发光层中。在一个优选的实施例中,阴极的功函数和发光层中发光体或作为电子注入层(EIL)或电子传输层(ETL)或空穴阻挡层(HBL)的n型半导体材料的LUMO能级或导带能级的差的绝对值小于0.5eV,较好是小于0.3eV,最好是小于0.2eV。原则上,所有可用作OLED的阴极的材料都可能作为本发明器件的阴极材料。阴极材料的例子包括但不限于:Al、Au、Ag、Ca、Ba、Mg、LiF/Al、MgAg合金、BaF2/Al、Cu、Fe、Co、Ni、Mn、Pd、Pt、ITO等。阴极材料可以使用任何合适的技术沉积,如一合适的物理气相沉积法,包括射频磁控溅射,真空热蒸发,电子束(e-beam)等。
OLED还可以包含其他功能层,如空穴注入层(HIL)、空穴传输层(HTL)、电子阻挡层(EBL)、电子注入层(EIL)、电子传输层(ETL)、空穴阻挡层(HBL)。适合用于这些功能层中的材料在上面及在WO2010135519A1、US20090134784A1和WO2011110277A1中有详细的描述,特此将此3篇专利文件中的全部内容并入本文作为参考。
在一个优选的实施例中,按照本发明的有机电致发光器件中,其发光层包含本发明的有机化合物或混合物。
在另一个优选的实施例中,所述的有机电致发光器件,其中的发光层可由如下方法中一种形成:
(1)包含有H1和H2的混合物是作为一个源通过真空蒸镀的方法沉积而成。
(2)H1和H2是分别作为单独的两个源通过真空蒸镀的方法沉积而成。
(3)利用所述的组合物通过溶液加工的方法,特别是打印的方法沉积而成。
按照本发明的发光器件,其发光波长在300到1000nm之间,较好的是在350到900nm之间,更好的是在400到800nm之间。
本发明还涉及按照本发明的有机电致发光器件在各种电子设备中的应用,包含但不限于,显示设备,照明设备,光源,传感器等等。
下面将结合优选实施例对本发明进行了说明,但本发明并不局限于下述实施例,应当理解,所附权利要求概括了本发明的范围在本发明构思的引导下本领域的技术人员应意识到,对本发明的各实施例所进行的一定的改变,都将被本发明的权利要求书的精神和范围所覆盖。
具体实施例
1.化合物的合成
Comp 1的合成:
将1,8-二萘胺(100g,632mmol)、200mL醋酸、1L乙醇加入2000mL干燥洁净的三口烧瓶,抽真空充氮气循环五次后,在0-5℃下滴加130mL的亚硝酸异戊酯(400mL乙醇稀释),滴加毕自然升至室温搅拌反应过夜。反应完全后抽滤,滤饼用1L乙醇多次泡洗后室温旋干得174g粗产品1a。
在2000mL干燥洁净的三口烧瓶中加入中间体1a(107g,633mmol)、1100mL 40%氢溴酸溶液和81.74g溴化亚铜用氢溴酸溶解后缓慢滴加到体系中,滴加完升温60℃搅拌反应2h。降温至室温,加入600mL的冰水,室温用碳酸钠调节体系pH在7-8之间,加入1L的乙酸乙酯萃取三次,合并有机相并用饱和食盐水洗涤后浓缩,柱层析分离得淡红色固体,石油醚打浆一次后抽滤,在50℃真空干燥得到90g粗产物1b。
在2000mL干燥洁净的三口烧瓶,加入中间体1b(20g,90mmol)、170mL去离子水,室温下缓慢加入400mL盐酸,抽真空充氮气循环五次后,在-10℃滴加7.49g的亚硝酸钠溶液(50mL水溶解),滴加毕保温搅拌2小时。二水合氯化亚锡(51.13g,226mmol)用100mL的盐酸溶解缓慢滴加到体系中,滴加完再次保温反应3小时。抽滤,滤饼用20mL的水泡洗一次后50℃真空干燥得到75g粗产品1c。
在1000mL干燥洁净的三口烧瓶,加入中间体1c(24.48g,90.5mmol)、环己酮(8.88g,90.5mmol)、500mL乙醇,氮气置换4-5次后升温回流反应1.5h。降温至室温,加入硅胶拌样浓缩柱层析得20.39g产品1d。
在500mL干燥洁净的三口烧瓶,加入中间体1d(6.64g,22.2mmol)、乙腈100mL、四氢呋喃100mL,氮气置换4-5次后降温至0-5℃滴加20.16g二氯二氰基苯醌溶液(50mL乙腈,50mL的四氢呋喃溶解稀释),滴加完自然升温至室温反应2小时。浓缩后加入乙酸乙酯和饱和磷酸钾溶液萃取,有机层用饱和磷酸钾洗涤3-4后浓缩,柱层析得到淡黄色固体1.2g即为中间体1e。
在氮气气氛下,将中间体1e(7.0g,22.8mmol)、邻氟苯胺(8.2g,22.7mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基 膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后旋转蒸发除去溶剂,然后用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20)。将所得产物与碳酸铯(13g,40mmol)依次将入到250mL三口烧瓶,加入100mL N,N-二甲基吡咯烷酮,加热至180℃反应24小时,反应结束后旋转蒸发除去溶剂,然后用将产物溶解在热的甲苯中,趁热经过保温硅胶柱,收集溶液后用二甲苯重结晶,得到10g中间体1f,产率82%。
在氮气气氛下,将中间体1f(7.0g,22.8mmol)、化合物1g(8.2g,22.7mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到7.79g固体粉末,产率58.6%。
Comp 2的合成:
在氮气气氛下,将中间体1f(7.0g,22.8mmol)、化合物2a(8.2g,22.7mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到8.24g固体粉末,产率62%。
Comp 3的合成:
在氮气气氛下,将中间体1f(10.0g,32.6mmol)、化合物3a(12.7g,32.6mmol)、三二亚苄基丙酮二钯(1.5g,1.63mmol)和叔丁醇钠(3.76g,39.1mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(6.6g,32.6mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:16),得到11.06g固体粉末,产率55.2%。
Comp 4的合成:
在氮气气氛下,将中间体1f(8.0g,26.1mmol)、化合物4a(8.9g,26.1mmol)、三二亚苄基丙酮二钯(1.2g,1.3mmol)和叔丁醇钠(2.5g,26.1mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(5.28g,26.1mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:10),得到8.1g固体粉末,产率54.7%。
Comp 5的合成:
在氮气气氛下,将中间体1f(8.0g,26.1mmol)、化合物5a(8.9g,26.1mmol)、三二亚苄基丙酮二钯(1.2g,1.3mmol)和叔丁醇钠(2.5g,26.1mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(5.28g,26.1mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:10),得到9.3g固体粉末,产率62.9%。
Comp 6的合成:
在氮气气氛下,将化合物6a(18.0g,51.9mmol)、化合物6b(8.9g,51.9mmol)、四(三苯基膦)钯(0.6g,0.52mmol)和X-Phos(0.6g,1.3mmol)依次加入到500mL三口烧瓶中,然后将200mL甲苯注入烧瓶并抽真空氮气置换三次,最后将溶解有磷酸钾(13.2g,62.3mmol)的50mL水溶液缓慢滴加到烧瓶中,加热至110℃回流反应8小时,旋转蒸发除去溶剂并用二氯甲烷和去离子水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂石油醚),得到16.8g中间体6c,产率72.6%。
在氮气气氛下,将中间体1f(12.4g,40.6mmol)、中间体6c(16g,40.6mmol)、 三二亚苄基丙酮二钯(1.86g,2.03mmol)和叔丁醇钠(4.68g,48.7mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(8.2g,40.6mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到18.9g固体粉末,产率70.3%。
Comp 7的合成:
氮气气氛下,将化合物7a(20.2g,50mmol)、化合物6a(17.2g,100mmol)、四(三苯基磷)钯(3.5g,3mmol)、四丁基溴化铵(8.1g,25mmol)和氢氧化钠(4g,100mmol)依次加入到500mL的三口瓶中,再将200mL甲苯和50mL去离子水加入,抽真空氮气置换三次后加热110℃搅拌反应24小时,结束反应,将反应液旋转蒸发掉大部分溶剂,用二氯甲烷溶解水洗三次,合并有机相经硅胶柱层析分离纯化(淋洗剂石油醚),得到18.7g中间体7b,产率75%。
将(14.9g,30mmol)的中间体7b和100mL N,N-二甲基甲酰胺加入250mL单口瓶中,冰浴下滴加30mmolNBS的N,N-二甲基甲酰胺溶液,避光搅拌反应12小时,结束反应,将反应液倒入到300mL水中,抽滤,滤渣重结晶,得到17.3g中间体7c,产率90%。
在氮气气氛下,将中间体中间体7c(34.4g,20mmol)、中间体化合物7d(11.5g,20mmol)、四(三苯基磷)钯(0.7g,0.6mmol)和四丁基溴化铵(3.2g,10mmol)和氢氧化钠(1.6g,40mmol)依次加入到500mL三口烧瓶中,然后将200mL甲苯和50mL去离子水注入烧瓶并抽真空氮气置换三次,加热至110℃回流反应12小时,结束反应后旋转蒸发除去溶剂,然后用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:10),得到18.7g固体粉末,产率85%。
Comp 8的合成:
氮气环境下,将中间体7c(11.5g,20mmol)、化合物8a(44.4g,20mmol)、四(三苯基磷)钯(0.7g,0.6mmol)、四丁基溴化铵(3.2g,10mmol)、氢氧化钠(1.6g,40mmol)、(10mL)水和(80mL)甲苯加入250mL的三口瓶中,加热110℃搅拌反应12小时,结束反应,将反应液旋转蒸发掉大部分溶剂,用二氯甲烷溶解水洗三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:10),得到21.8g固体粉末,产率85%。
Comp 9的合成:
在氮气气氛下,将中间体1e(7.0g,22.8mmol)、9a(8.2g,22.7mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后旋转蒸发除去溶剂,然后用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20)。将所得产物与碳酸铯(13g,40mmol)依次将入到250mL三口烧瓶,加入100mL N,N-二甲基吡咯烷酮,加热至180℃反应24小时,反应结束后旋转蒸发除去溶剂,然后用将产物溶解在热的甲苯中,趁热经过保温硅胶柱,收集溶液后用二甲苯重结晶,得到10.6g中间体9b,产率83%。
在氮气气氛下,将中间体9b(7.0g,20.3mmol)、化合物1g(10.4g,20.1mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.32g,20.5mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到6.62g固体粉末,产率50.1%。
Comp 10的合成:
在氮气气氛下,将中间体9b(7.0g,20.3mmol)、化合物3a(10.4g,20.1mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,20.5mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到7.23g固体粉末,产率56.5%。
Comp 11的合成:
在1000mL干燥洁净的三口烧瓶,加入中间体1c(24.48g,90.5mmol)、11a(8.88g,90.5mmol)、500mL乙醇,氮气置换4-5次后升温回流反应1.5h。降温至室温,加入硅胶拌样浓缩柱层析得21.23g产品11b。
在500mL干燥洁净的三口烧瓶,加入中间体11b(6.64g,22.2mmol)、乙腈100mL、四氢呋喃100mL,氮气置换4-5次后降温至0-5℃滴加20.16g二氯二氰基苯醌溶液(50mL乙腈,50mL的四氢呋喃溶解稀释),滴加完自然升温至室温反应2小时。浓缩后加入乙酸乙酯和饱和磷酸钾溶液萃取,有机层用饱和磷酸钾洗涤3-4后浓缩,柱层析得到淡黄色固体0.5g即为中间体11c。
在氮气气氛下,将中间体11c(7.0g,22.8mmol)、11d(8.2g,22.7mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后旋转蒸发除去溶剂,然后用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20)。将所得产物与碳酸铯(13g,40mmol)依次将入到250mL三口烧瓶,加入100mL N,N-二甲基吡咯烷酮,加热至180℃反应24小时,反应结束后旋转蒸发除去溶剂,然后用将产物溶解在热的甲苯中,趁热经过保温硅胶柱,收集溶液后用二甲苯重结晶,得到10.3g中间体11e,产率83%。
在氮气气氛下,将中间体11e(7.0g,20.1mmol)、化合物2a(8.2g,20.2mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到6.85g固体粉末,产率52.6%。
Comp 12的合成:
在氮气气氛下,将中间体1e(7.0g,22.8mmol)、12a(8.2g,22.7mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后旋转蒸发除去溶剂,然后用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离 纯化(淋洗剂二氯甲烷:石油醚=1:20)。将所得产物与碳酸铯(13g,40mmol)依次将入到250mL三口烧瓶,加入100mL N,N-二甲基吡咯烷酮,加热至180℃反应24小时,反应结束后旋转蒸发除去溶剂,然后用将产物溶解在热的甲苯中,趁热经过保温硅胶柱,收集溶液后用二甲苯重结晶,得到10g中间体12b,产率82%。
在氮气气氛下,将中间体12b(7.0g,20.1mmol)、化合物4a(8.2g,20.1mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到7.45g固体粉末,产率57.2%。
Comp 13的合成:
在1000mL干燥洁净的三口烧瓶,加入中间体1c(24.48g,90.5mmol)、11a(8.88g,90.5mmol)、500mL乙醇,氮气置换4-5次后升温回流反应1.5h。降温至室温,加入硅胶拌样浓缩柱层析得20.39g产品13a。
在500mL干燥洁净的三口烧瓶,加入中间体13a加20.16g二氯二氰基苯醌溶液(50mL乙腈,50mL的四氢呋喃溶解稀释),滴加完自然升温至室温反应2小时。浓缩后加入乙酸乙酯和饱和磷酸钾溶液萃取,有机层用饱和磷酸钾洗涤3-4后浓缩,柱层析得到淡黄色固体1.2g即为中间体13b。
在氮气气氛下,将中间体13b(7.0g,22.8mmol)、邻氟苯胺(8.2g,22.7mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后旋转蒸发除去溶剂,然后用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20)。将所得产物与碳酸铯(13g,40mmol)依次将入到250mL三口烧瓶,加入100mL N,N-二甲基吡咯烷酮,加热至180℃反应24小时,反应结束后旋转蒸发除去溶剂,然后用将产物溶解在热的甲苯中,趁热经过保温硅胶柱,收集溶液后用二甲苯重结晶,得到10g中间体13c,产率82%。
在氮气气氛下,将中间体13c(7.0g,20.1mmol)、化合物5a(8.2g,20.2mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔 丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到7.69g固体粉末,产率58.1%。
Comp 14的合成:
在氮气气氛下,将中间体6c(7.0g,20.1mmol)、化合物13c(8.2g,20.1mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到8.23g固体粉末,产率61%。
Comp 15的合成:
在1000mL干燥洁净的三口烧瓶,加入中间体1c(24.48g,90.5mmol)、15a(8.88g,90.5mmol)、500mL乙醇,氮气置换4-5次后升温回流反应1.5h。降温至室温,加入硅胶拌样浓缩柱层析得20.39g产品15b。
在500mL干燥洁净的三口烧瓶,加入中间体15b加20.16g二氯二氰基苯醌溶液(50mL乙腈,50mL的四氢呋喃溶解稀释),滴加完自然升温至室温反应2小时。浓缩后加入乙酸乙酯和饱和磷酸钾溶液萃取,有机层用饱和磷酸钾洗涤3-4后浓缩,柱层析得到淡黄色固体1.2g即为中间体15c。
在氮气气氛下,将中间体15c(7.0g,22.8mmol)、15d(8.2g,22.7mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后旋转 蒸发除去溶剂,然后用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20)。将所得产物与碳酸铯(13g,40mmol)依次将入到250mL三口烧瓶,加入100mL N,N-二甲基吡咯烷酮,加热至180℃反应24小时,反应结束后旋转蒸发除去溶剂,然后用将产物溶解在热的甲苯中,趁热经过保温硅胶柱,收集溶液后用二甲苯重结晶,得到10g中间体15e,产率82%。
在氮气气氛下,将中间体15f(7.0g,20.1mmol)、化合物1g(8.2g,20.2mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到7.23g固体粉末,产率58.2%。
Comp 16的合成:
在氮气气氛下,将中间体15f(7.0g,20.1mmol)、化合物5a(8.2g,20.2mmol)、三二亚苄基丙酮二钯(1.04g,1.14mmol)和叔丁醇钠(2.63g,27.4mmol)依次加入到500mL三口烧瓶中,然后将200mL干燥的甲苯注入烧瓶并抽真空氮气置换三次,最后将三叔丁基膦(4.6g,22.8mmol)缓慢滴加到烧瓶中,加热至110℃回流反应12小时,结束反应后将反应混合液倒入500mL去离子水中并快速搅拌,期间不断有产物析出,抽滤后再次用二氯甲烷将产物溶解并用饱和食盐水萃取三次,合并有机相经硅胶柱层析分离纯化(淋洗剂二氯甲烷:石油醚=1:20),得到7.21g固体粉末,产率58.1%。
2.有机化合物的能量结构
有机材料的能级可通过量子计算得到,比如利用TD-DFT(含时密度泛函理论)通过Gaussian03W(Gaussian Inc.),具体的模拟方法可参见WO2011141110。首先用半经验方法“Ground State/Semi-empirical/Default Spin/AM1”(Charge 0/Spin Singlet)来优化分子几何结构,然后有机分子的能量结构由TD-DFT(含时密度泛函理论)方法算得“TD-SCF/DFT/Default Spin/B3PW91”与基组“6-31G(d)”(Charge 0/Spin Singlet)。HOMO和LUMO能级按照下面的校准公式计算,S1和T1直接使用。
HOMO(eV)=((HOMO(G)×27.212)-0.9899)/1.1206
LUMO(eV)=((LUMO(G)×27.212)-2.0041)/1.385
其中HOMO(G)和LUMO(G)是Gaussian 03W的直接计算结果,单位为Hartree。结果如表1所示:
表1
3.OLED器件的制备及测量
下面通过具体实施例来详细说明采用上述的OLED器件的制备过程,红光OLED器件的结构为:ITO/HI/HI-1/HT-2/EML/ET:Liq/Liq/Al。
制备步骤如下:
a、ITO(铟锡氧化物)导电玻璃基片的清洗:使用各种溶剂(例如氯仿、丙酮或异丙醇中的一种或几种)清洗,然后进行紫外臭氧处理。
b、HI(30nm),HT-1(60nm),HT-2(10nm),主体材料:3%RD(40nm),ET:Liq(50:50;30nm),Liq(1nm),Al(100nm)在高真空(1×10
-6毫巴)中热蒸镀而成;将ITO基片移入真空气相沉积设备中,在高真空(1×10
-6毫巴)下,采用电阻加热蒸发源形成厚度为30nm的HI层,在HI层上依次加热形成60nm的HT-1以及10nm的HT-2层。随后comp 1置于一个蒸发单元,并且将化合物RD置于另外一个蒸发单元作为掺杂剂,使材料按不同速率气化,使得comp 1:Dopant的重量比在100:3,在空穴传输层上形成40nm的发光层。接着将ET和LiQ置于不同的蒸发单元,使其分别以50重量%的比例进行共沉积,在发光层上形成30nm的电子传输层,随后在电子传输层上沉积1nm的LiQ作为电子注入层,最后在所述电子注入层上沉积厚度为100nm的Al阴极。
c、封装:器件在氮气手套箱中用紫外线硬化树脂封装。
器件实施例2-7的实施方法同器件实施例1。除了用comp 2,comp 4以及不同的共主体代替comp 2。其中共主体是指两个化合物分别置于不同的蒸发单元,控制材料的重量比。
红光OLED器件的电流电压及发光(IVL)特性通过表征设备来表征,同时记录重要的参数如效率,寿命及驱动电压。红光OLED器件的性能总结在表2中。其中的寿命是相对对比例的值。
表2
经检测,器件实施例1-22的发光效率和寿命与对比例1相比有明显提高。可见,采用本发明的有机化合物制备的OLED器件,其发光效率和寿命均得到大大提高。
以上所述实施例的各技术特征可以进行任意的组合,为使描述简洁,未对上述实施例中的各个技术特征所有可能的组合都进行描述,然而,只要这些技术特征的组合不存在矛盾,都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式,其描述较为具体和详细,但并不能因此而理解为对发明专利范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。因此,本发明专利的保护范围应以所附权利要求为准。
Claims (15)
- 一种有机化合物,具有如通式(I)所示的结构:其中:X独立表示为N或CR 1,且至少一个X为CR 1,当相邻的X为CR 1时可相互稠合成环;R 1选自H、D、具有1至20个C原子的直链烷基、烷氧基或硫代烷氧基基团,或具有3至20个C原子的支链或环状的烷基、烷氧基、硫代烷氧基基团或甲硅烷基基团,或具有1至20个C原子的取代的酮基基团,或具有2至20个C原子的烷氧基羰基基团,或具有7至20个C原子的芳氧基羰基基团,氰基基团,氨基甲酰基基团,卤甲酰基基团,甲酰基基团,异氰基基团,异氰酸酯基团,硫氰酸酯基团,异硫氰酸酯基团,羟基基团,硝基基团,CF 3基团,Cl,Br,F,可交联的基团,或具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合,其中一个或多个R 1基团可以彼此和/或与其键合的基团形成环系;L为连接基团,选自单键,C6-C60的亚芳基,亚芴基,C2-C60的杂芳香基团,C3-C60的脂肪族环,C6-C60的芳香族环的稠环基,以及上述基团的组合;Ar选自具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或是具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合,其中一个或多个Ar基团可以彼此和/或与其键合的环形成单环或多环的脂族或芳族环系。
- 根据权利要求1所述的有机化合物,其特征在于,至少有一个X选自N。
- 根据权利要求1所述的有机化合物,其特征在于,所述有机化合物具有通式(II)所示的结构:其中:L和Ar含义同权利要求1所述;R 2-R 14是取代基,在每次出现时,相同或不同地选自H、D,或具有1至20个C原子的直链烷基、烷氧基或硫代烷氧基基团,或具有3至20个C原子的支链或环状的烷基、烷氧基、硫代烷氧基基团或甲硅烷基基团,或具有1至20个C原子的取代的酮基基团,或具有2至20个C原子的烷氧基羰基基团,或具有7至20个C原子的芳氧基羰基基团,氰基基团,氨基甲酰基基团,卤甲酰基基团,甲酰基基团,异氰基基团,异氰酸酯基团,硫氰酸酯基团,异硫氰酸酯基团,羟基基团,硝基基团,CF 3基团,Cl,Br,F,可交联的基团,或具有5至40个环原 子的取代或未取代的芳香基团或杂芳香基团,或具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合;其中一个或多个基团可以彼此和/或与其键合的基团形成环系。
- 根据权利要求3所述的有机化合物,其特征在于,R 1-R 14、L、Ar可相同或不同地选自如下基团中的一种或它们中的组合:其中:V在多次出现时,相互独立的选自CR 15或者N;W选自CR 16R 17,SiR 18R 19,NR 20或,C(=O),S或O;Ar 1和Ar 2的定义同权利要求1中的Ar;R 15-R 20在每次出现时,相同或不同地选自H、D,或具有1至20个C原子的直链烷基、烷氧基或硫代烷氧基基团,或具有3至20个C原子的支链或环状的烷基、烷氧基、硫代烷氧基基团或甲硅烷基基团,或具有1至20个C原子的取代的酮基基团,或具有2至20个C原子的烷氧基羰基基团,或具有7至20个C原子的芳氧基羰基基团,氰基基团,氨基甲酰基基团,卤甲酰基基团,甲酰基基团,异氰基基团,异氰酸酯基团,硫氰酸酯基团,异硫氰酸酯基团,羟基基团,硝基基团,CF 3基团,Cl,Br,F,可交联的基团,或具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合,其中一个或多个基团可以彼此和/或与其键合的基团形成环系。
- 根据权利要求1-4任一项所述的有机化合物,其特征在于,Ar包含一吸电子基团。
- 一种高聚物,包含至少一个重复单元,其特征在于,所述重复单元包含一种如权利要求1-6任一项所述的有机化合物所对应的结构。
- 一种混合物,至少包含有机化合物H1和有机化合物H2,其特征在于,所述有机化合物H1选自权利要求1-6任一项所述的有机化合物或如权利要求7所述的高聚物,所述有机化合 物H2是另一种有机功能材料,且选自空穴注入材料、空穴传输材料、电子传输材料、电子注入材料、电子阻挡材料、空穴阻挡材料、发光材料、主体材料、有机染料中的一种或多种。
- 根据权利要求9所述的混合物,其特征在于,所述富电子基团包含有如下任一基团:其中,Ar 11表示环原子数为5-40的芳香基团或杂芳香基团;Z 1、Z 2、Z 3分别独立选自单键、CR 21R 22、SiR 23R 24、NR 25、O、C(=O)、S、S=O或SO 2,且Z 2和Z3不同时为单键;R 13-R 25选自H、D、具有1至20个C原子的直链烷基、烷氧基或硫代烷氧基基团,或具有3至20个C原子的支链或环状的烷基、烷氧基、硫代烷氧基基团或甲硅烷基基团,或具有1至20个C原子的取代的酮基基团,或具有2至20个C原子的烷氧基羰基基团,或具有7至20个C原子的芳氧基羰基基团,氰基基团,氨基甲酰基基团,卤甲酰基基团,甲酰基基团,异氰基基团,异氰酸酯基团,硫氰酸酯基团,异硫氰酸酯基团,羟基基团,硝基基团,CF 3基团,Cl,Br,F,可交联的基团,或具有5至40个环原子的取代或未取代的芳香基团或杂芳香基团,或具有5至40个环原子的芳氧基或杂芳氧基基团,或这些基团的组合,其中一个或多个R 1基团可以彼此和/或与其键合的基团形成环系。
- 根据权利要求8-10任一项所述的一种混合物,其特征在于,所述混合物还包含一种发光材料,所述发光材料选于单重态发光体、三重态发光体或TADF材料。
- 一种组合物,其特征在于,包含至少一种如权利要求1-6任一项所述的有机化合物或如权利要求7所述的高聚物或如权利要求8-11任一项所述的混合物,及至少一种有机溶剂。
- 一种有机电子器件,所述有机电子器件包含功能层,其特征在于,所述功能层包含一种如权利要求1-6任一项所述的有机化合物或如权利要求7所述的高聚物或如权利要求8-11中任一项所述的混合物。
- 根据权利要求13所述的有机电子器件,其特征在于,所述有机电子器件选于有机发光二极管、有机光伏电池、有机发光电池、有机场效应管、有机发光场效应管、有机激光器、有机自旋电子器件、光电二极管、有机传感器及有机等离激元发射二极管。
- 根据权利要求14所述的有机电子器件,其特征在于,所述有机电子器件是有机电致发光器件,且至少包含一种如权利要求1-6任一项所述的有机化合物或如权利要求7所述的高聚物或如权利要求8-11中任一项所述的混合物。