WO2021256660A1 - Protective clothing material having excellent virus-blocking performance and production method thereof - Google Patents

Protective clothing material having excellent virus-blocking performance and production method thereof Download PDF

Info

Publication number
WO2021256660A1
WO2021256660A1 PCT/KR2021/002447 KR2021002447W WO2021256660A1 WO 2021256660 A1 WO2021256660 A1 WO 2021256660A1 KR 2021002447 W KR2021002447 W KR 2021002447W WO 2021256660 A1 WO2021256660 A1 WO 2021256660A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyolefin
breathable
protective
laminated
film
Prior art date
Application number
PCT/KR2021/002447
Other languages
French (fr)
Korean (ko)
Inventor
김창복
김태경
Original Assignee
(주)이지켐
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)이지켐 filed Critical (주)이지켐
Publication of WO2021256660A1 publication Critical patent/WO2021256660A1/en

Abstract

The present invention relates to: a protective clothing material having excellent virus-blocking performance; and a production method thereof. More specifically, the present invention relates to: a protective clothing material having a structure in which a breathable laminate, in which at least two layers of breathable film are laminated, and a non-woven fabric are laminated, the clothing material having a thin thickness as a whole, thus being lightweight while having excellent virus-blocking properties, as well as excellent mechanical properties and air permeability; and a production method thereof.

Description

바이러스 차단성능이 우수한 보호복원단 및 이의 제조방법Protective recovery fabric with excellent virus blocking performance and manufacturing method thereof
본 발명은 바이러스 차단성능이 우수한 보호복원단 및 이의 제조방법에 관한 것이다. 더욱 구체적으로 본 발명은 통기성필름이 두층 이상 적층된 통기성 적층체와 부직포가 적층된 구조로, 전체 두께가 얇아 원단이 무겁지 않고 가벼우면서도 바이러스 차단성이 우수하면서, 동시에 기계적인 물성 및 통기성이 우수한 보호복원단 및 이의 제조방법에 관한 것이다.The present invention relates to a protective restoration having excellent virus blocking performance and a method for manufacturing the same. More specifically, the present invention has a structure in which a breathable laminate in which two or more layers of a breathable film are laminated and a nonwoven fabric are laminated, and the overall thickness is thin so that the fabric is not heavy and light, yet has excellent virus barrier properties, and at the same time has excellent mechanical properties and breathability. It relates to a recovery end and a method for manufacturing the same.
수술복과 보호복의 경우, 기능성을 부여하기 위해 기능성이 서로 다른 필름을 접착하여 기능성을 부여한다. 특히, 방수성 및 내화학성을 부여하기 위해 주로 탄산칼슘을 이용해 미세기공이 형성된 통기성필름과 물리적 강도를 개선하기 위한 올레핀계 부직포를 합지하여 사용하고 있다. 이러한 원단은 방수와 내화학성을 부여하기 위한 원단으로는 사용이 가능하나, 필름의 기공이 크기 때문에 바이러스를 효과적으로 방어할 수 없는 문제점이 있다. In the case of surgical clothes and protective clothing, in order to provide functionality, films with different functionalities are attached to each other to provide functionality. In particular, in order to provide waterproofness and chemical resistance, a breathable film with micropores formed mainly using calcium carbonate and an olefin-based nonwoven fabric to improve physical strength are laminated and used. Such a fabric can be used as a fabric for imparting waterproofness and chemical resistance, but there is a problem in that it cannot effectively protect against viruses because the pores of the film are large.
이러한 문제를 해결하기 위해서 폴리우레탄 멤브레인이나 투습효과가 좋은 폴리우레탄계 접착제를 통기성 필름에 전면 도포하는 방식을 적용하여 바이러스를 차단하려는 제품이 개발되었다.In order to solve this problem, a product that blocks viruses by applying a polyurethane membrane or a polyurethane adhesive with good moisture permeability to the air permeable film has been developed.
하지만 이러한 방법으로 제조된 원단의 경우 투습효과와 기계적 물성이 좋지 않아 착용감이 좋지 않다는 단점이 있다. 특히, 바이러스 방어력을 나타내는 폴리우레탄 접착제가 안정성이 좋지 않아 시간이 지남에 따라 분해됨에 따라 바이러스 방어력이 파괴되기 때문에 장기 신뢰성 확보가 어려워 사용에 제한적일 수밖에 없었다. However, in the case of the fabric manufactured in this way, there is a disadvantage that the moisture permeability and mechanical properties are not good, so the wearing comfort is not good. In particular, since the polyurethane adhesive, which exhibits virus defense, has poor stability and is decomposed over time, the virus defense is destroyed, so it is difficult to secure long-term reliability, so its use is limited.
따라서 시장에서 요구하는 기계적 물성, 투습도 및 바이러스 방어력을 동시에 만족할 수 있는 수술복 또는 방호복용 원단에 대한 연구가 많이 진행되어 왔으나, 이를 모두 만족 할 수 있는 제품은 출시되지 못하고 있었다.Therefore, many studies have been conducted on fabrics for surgical suits or protective clothing that can simultaneously satisfy the mechanical properties, moisture permeability, and virus defense required by the market, but products that can satisfy all of these have not been released.
선행기술문헌 한국 등록특허공보 제10-1996883호(2019.07.01.)Prior art document Korean Patent Publication No. 10-1996883 (2019.07.01.)
본 발명의 일 과제는 전체 원단의 두께가 얇고, 가벼우며, 종래 동일한 두께의 원단에 비하여 더욱 우수한 바이러스 차단성을 가지면서, 동시에 기계적인 물성, 투습성 및 통기성이 우수한 원단 및 이를 제조하는 새로운 방법을 제공하고자 한다.An object of the present invention is to provide a fabric with a thin, light overall thickness, and superior virus barrier properties compared to conventional fabrics of the same thickness, and at the same time have excellent mechanical properties, moisture permeability and breathability, and a new method of manufacturing the same would like to provide
본 발명의 일 과제는 수술복 또는 방호복으로 제조 시 가볍고, 사용자의 착용감이 좋은 원단 및 이를 제조하는 새로운 방법을 제공하고자 한다.An object of the present invention is to provide a fabric that is lightweight and comfortable for users to wear when manufacturing a surgical suit or protective suit, and a new method of manufacturing the same.
상기 과제를 달성하기 위하여 연구한 결과, 특정한 방법으로 통기성 필름을 제조하고, 또한 이를 특정한 구조로 적층함으로써 전체 두께가 얇아 원단이 가벼우면서도 바이러스 차단성을 가지며, 동시에 기계적인 물성, 투습성 및 통기성이 우수한 보호복원단을 제공할 수 있음을 발견하여 본 발명을 완성하였다.As a result of research to achieve the above object, by manufacturing a breathable film by a specific method and laminating it in a specific structure, the overall thickness is thin and the fabric is light and has virus blocking properties, and at the same time has excellent mechanical properties, moisture permeability and breathability The present invention was completed by discovering that it is possible to provide a protective restoration group.
구체적으로 본 발명의 일 양태는 적어도 둘 이상의 통기성 필름이 적층된 통기성 적층체 및 상기 통기성 적층체의 적어도 일면에 부직포가 적층되며,Specifically, one aspect of the present invention is a breathable laminate in which at least two or more breathable films are laminated, and a nonwoven fabric is laminated on at least one surface of the breathable laminate,
상기 통기성 필름은 투습성 폴리우레탄 접착제를 이용하여 라미네이트 되고,The breathable film is laminated using a moisture-permeable polyurethane adhesive,
상기 통기성 적층체와 부직포는 투습성 폴리우레탄 접착제 또는 가열 압착하여 라미네이트 되며,The breathable laminate and the nonwoven fabric are laminated by heat-pressing or moisture-permeable polyurethane adhesive,
JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 이상, 더욱 좋게는 5 이상인 바이러스 차단성능이 우수한 보호복원단에 관한 것이다.It relates to a protective recovery group having excellent virus blocking performance according to JIS T 8061:2015 of class 3 or more, more preferably 5 or more.
본 발명의 또 다른 양태는 a) 적어도 둘 이상의 통기성 필름을 투습성 폴리우레탄 접착제를 이용하여 라미네이트하여 통기성 적층체를 제조하는 단계;Another aspect of the present invention comprises the steps of: a) laminating at least two or more breathable films using a moisture-permeable polyurethane adhesive to prepare a breathable laminate;
b) 상기 통기성 적층체의 적어도 일면에 투습성 폴리우레탄 접착제를 도포한 후 부직포를 라미네이트하거나 또는 상기 통기성 적층체와 부직포를 가열 압착하여 라미네이트하는 단계;b) laminating a nonwoven fabric after applying a moisture-permeable polyurethane adhesive to at least one surface of the breathable laminate or by heat-compressing the breathable laminate and the nonwoven fabric;
를 포함하며, JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 이상, 더욱 좋게는 5 이상인 바이러스 차단성능이 우수한 보호복원단의 제조방법을 제공한다.It includes, and provides a method for manufacturing a protective restoration group having excellent virus blocking performance according to JIS T 8061:2015 of class 3 or more, more preferably 5 or more.
본 발명의 또 다른 양태는 습식 폴리올레핀계 통기성 필름의 양면에 투습성 폴리우레탄 접착제를 이용하여 건식 폴리올레핀계 통기성 필름을 적층한 바이러스 차단성능이 우수한 보호복원단으로서,Another aspect of the present invention is a protective restoration unit with excellent virus blocking performance in which a dry polyolefin-based breathable film is laminated on both sides of a wet polyolefin-based breathable film using a moisture-permeable polyurethane adhesive,
상기 습식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 평균입경이 100 내지 1000 nm인 유기 나노입자인 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거한 것이고, The wet polyolefin-based breathable film is a polyolefin-based resin mixed with an organic nanoparticle pore-forming additive having an average particle diameter of 100 to 1000 nm, extruded and stretched, and then the pore-forming additive is extracted and removed,
상기 건식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 평균입경이 0.5 내지 10 ㎛인 무기입자를 혼합하여 압출 및 연신하여 제조된 것인 바이러스 차단성능이 우수한 보호복원단을 제공한다.The dry polyolefin-based breathable film is prepared by mixing and extruding and stretching inorganic particles having an average particle diameter of 0.5 to 10 μm in a polyolefin-based resin, and provides a protective recovery fabric with excellent virus blocking performance.
본 발명의 일 양태에 따른 바이러스 차단성능이 우수한 보호복원단은 전체 두께가 얇아 원단 무게가 가벼우므로 착용자로 하여금 착용감이 좋은 효과가 있다.The protective restoration fabric having excellent virus blocking performance according to an aspect of the present invention has a thin overall thickness and thus a light fabric weight, so that the wearer has a good wearing effect.
또한, 전체 두께가 얇으면서도 바이러스 차단성이 우수하고, 기계적인 물성, 투습성 및 통기성이 우수한 원단을 제공할 수 있다.In addition, it is possible to provide a fabric having a thin overall thickness and excellent virus barrier properties, and excellent mechanical properties, moisture permeability and breathability.
또한, 전체 두께가 얇으면서도 바이러스 차단성이 우수하고, 기계적인 물성, 투습성 및 통기성이 우수한 원단의 새로운 제조방법을 제공할 수 있다.In addition, it is possible to provide a new method of manufacturing a fabric having a thin overall thickness and excellent virus barrier properties, and excellent mechanical properties, moisture permeability and breathability.
도 1은 본 발명의 보호복원단의 일 양태를 나타낸 단면도이다.1 is a cross-sectional view showing an aspect of the protective restoration of the present invention.
도 2는 본 발명의 보호복원단의 일 양태를 나타낸 단면도이다.Figure 2 is a cross-sectional view showing an aspect of the protective restoration of the present invention.
도 3은 본 발명의 보호복원단의 일 양태를 나타낸 단면도이다.Figure 3 is a cross-sectional view showing an aspect of the protective restoration of the present invention.
도 4는 본 발명의 보호복원단의 일 양태를 나타낸 단면도이다.Figure 4 is a cross-sectional view showing an aspect of the protective restoration of the present invention.
-부호의 설명--Description of symbols-
10 : 통기성 적층체10: breathable laminate
11 : 습식 폴리올레핀계 통기성 필름11: Wet polyolefin-based breathable film
12 : 건식 폴리올레핀계 통기성 필름12: dry polyolefin-based breathable film
20 : 부직포20: non-woven fabric
이하 첨부된 구체예 또는 실시예를 통해 본 발명을 더욱 상세히 설명한다. 다만 하기 구체예 또는 실시예는 본 발명을 상세히 설명하기 위한 하나의 참조일 뿐 본 발명이 이에 한정되는 것은 아니며, 여러 형태로 구현될 수 있다. Hereinafter, the present invention will be described in more detail through the accompanying embodiments or examples. However, the following specific examples or examples are only a reference for describing the present invention in detail, and the present invention is not limited thereto, and may be implemented in various forms.
또한 달리 정의되지 않는 한, 모든 기술적 용어 및 과학적 용어는 본 발명이 속하는 당업자 중 하나에 의해 일반적으로 이해되는 의미와 동일한 의미를 갖는다. 본 발명에서 설명에 사용되는 용어는 단지 특정 구체예를 효과적으로 기술하기 위함이고 본 발명을 제한하는 것으로 의도되지 않는다. Also, unless defined otherwise, all technical and scientific terms have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. The terminology used in the description herein is for the purpose of effectively describing particular embodiments only and is not intended to limit the invention.
또한 명세서 및 첨부된 특허청구범위에서 사용되는 단수 형태는 문맥에서 특별한 지시가 없는 한 복수 형태도 포함하는 것으로 의도할 수 있다. Also, the singular forms used in the specification and appended claims may also be intended to include the plural forms unless the context specifically dictates otherwise.
또한 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다. Also, when a part "includes" a certain component, it means that other components may be further included, rather than excluding other components, unless otherwise stated.
본 발명의 일 양태는 적어도 둘 이상의 통기성 필름이 적층된 통기성 적층체 및 상기 통기성 적층체의 적어도 일면에 부직포가 적층되며,In one aspect of the present invention, a nonwoven fabric is laminated on at least one surface of a breathable laminate in which at least two or more breathable films are laminated and the breathable laminate,
상기 통기성 필름은 투습성 폴리우레탄 접착제를 이용하여 라미네이트 되고,The breathable film is laminated using a moisture-permeable polyurethane adhesive,
상기 통기성 적층체와 부직포는 투습성 폴리우레탄 접착제 또는 가열 압착하여 라미네이트 되며,The breathable laminate and the nonwoven fabric are laminated by heat-pressing or moisture-permeable polyurethane adhesive,
JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 이상, 더욱 좋게는 5 이상인 바이러스 차단성능이 우수한 보호복원단에 관한 것이다.It relates to a protective recovery group having excellent virus blocking performance according to JIS T 8061:2015 of class 3 or more, more preferably 5 or more.
본 발명의 일 양태에서, 상기 부직포는 폴리올레핀계 부직포인 것일 수 있다.In one aspect of the present invention, the nonwoven fabric may be a polyolefin-based nonwoven fabric.
본 발명의 일 양태에서, 상기 통기성 적층체는 폴리올레핀계 수지에 무기입자를 혼합하여 연신한 건식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층되거나, 또는 폴리올레핀계 수지에 무기입자를 혼합하여 압출 및 연신한 건식 폴리올레핀계 통기성 필름과, 폴리올레핀계 수지에 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거한 습식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층된 것일 수 있다.In one aspect of the present invention, the breathable laminate is a dry polyolefin-based breathable film obtained by mixing and stretching a polyolefin-based resin by mixing inorganic particles, or by mixing at least two or more dry polyolefin-based breathable films with a polyolefin-based resin by mixing inorganic particles and extruding and stretching them. At least two or more of the polyolefin-based air-permeable film and the wet polyolefin-based air-permeable film removed by extracting and removing the pore-forming additive after extruding and stretching the polyolefin-based resin by mixing the pore-forming additive may be laminated.
본 발명의 일 양태에서, 상기 기공형성 첨가제는 평균입경이 100 내지 1000 nm인 유기 나노입자이며, 상기 유기 나노입자에 의해 상기 습식 폴리올레핀계 통기성 필름에 나노사이즈의 균일 기공이 형성된 것일 수 있다.In one aspect of the present invention, the pore-forming additive is organic nanoparticles having an average particle diameter of 100 to 1000 nm, and nano-sized uniform pores may be formed in the wet polyolefin-based breathable film by the organic nanoparticles.
본 발명의 일 양태에서, 상기 기공형성 첨가제는 평균입경이 서로 상이한 2종의 폴리메틸메타크릴레이트 나노입자를 혼합한 것이며, 상기 습식 폴리올레핀계 통기성 필름은 바이모달 입자분포의 균일 기공을 갖는 것일 수 있다.In one aspect of the present invention, the pore-forming additive is a mixture of two types of polymethyl methacrylate nanoparticles having different average particle diameters, and the wet polyolefin-based breathable film may have uniform pores with a bimodal particle distribution. have.
본 발명의 일 양태에서, 상기 기공형성 첨가제는 평균입경이 100 내지 400 nm인 제1폴리메틸메타크릴레이트 나노입자와, 평균입경이 400 내지 1000 nm인 제2폴리메틸메타크릴레이트 나노입자를 혼합하여 사용한 것일 수 있다.In one aspect of the present invention, the pore-forming additive is a mixture of first polymethyl methacrylate nanoparticles having an average particle diameter of 100 to 400 nm and second polymethyl methacrylate nanoparticles having an average particle diameter of 400 to 1000 nm may have been used.
본 발명의 일 양태에서, 상기 건식 폴리올레핀계 통기성 필름은 블로운 캐스팅 방법으로 제조된 것일 수 있다.In one aspect of the present invention, the dry polyolefin-based breathable film may be prepared by a blow casting method.
본 발명의 일 양태에서, 상기 보호복원단은 건식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층된 통기성 적층체의 일면 또는 양면에 부직포가 적층된 것일 수 있다.In one aspect of the present invention, the protective restoration may be one in which a nonwoven fabric is laminated on one side or both sides of a breathable laminate in which at least two or more dry polyolefin-based breathable films are laminated.
본 발명의 일 양태에서, 상기 보호복원단은 건식 폴리올레핀계 통기성 필름과 습식 폴리올레핀계 통기성 필름이 적층된 통기성 적층체와, 상기 통기성 적층체의 습식 폴리올레핀계 통기성 필름 상에 부직포가 적층된 것일 수 있다.In one aspect of the present invention, the protective restoration unit is a breathable laminate in which a dry polyolefin-based breathable film and a wet polyolefin-based breathable film are laminated, and a nonwoven fabric is laminated on the wet polyolefin-based breathable film of the breathable laminate. .
본 발명의 일 양태에서, 상기 보호복원단은 건식 폴리올레핀계 통기성 필름과 습식 폴리올레핀계 통기성 필름이 적층된 통기성 적층체와, 상기 통기성 적층체의 양면에 부직포가 적층된 것일 수 있다.In one aspect of the present invention, the protective restoration may be a breathable laminate in which a dry polyolefin-based breathable film and a wet polyolefin-based breathable film are laminated, and a nonwoven fabric laminated on both sides of the breathable laminate.
본 발명의 일 양태에서, 상기 보호복원단은 두께가 100 내지 300 ㎛이며, ASTM D5034에 따른 인장강도가 100 N/50mm 이상이고, 신율이 40 % 이상이고, ASTM E96에 따른 투습도가 3,000 g/㎡·24hr 이상이고, AATCC 127에 따른 내수압이 300 mbar 이상인 것일 수 있다.In one aspect of the present invention, the protective fabric has a thickness of 100 to 300 μm, a tensile strength of 100 N/50 mm or more according to ASTM D5034, an elongation of 40% or more, and a moisture permeability according to ASTM E96 of 3,000 g/ m2·24hr or more, and the water pressure in accordance with AATCC 127 may be 300 mbar or more.
본 발명의 또 다른 양태는 바이러스 차단성능이 우수한 보호복원단의 제조방법으로,Another aspect of the present invention is a method for manufacturing a protective recovery group having excellent virus blocking performance,
a) 적어도 둘 이상의 통기성 필름을 투습성 폴리우레탄 접착제를 이용하여 라미네이트하여 통기성 적층체를 제조하는 단계;a) laminating at least two or more breathable films using a moisture-permeable polyurethane adhesive to prepare a breathable laminate;
b) 상기 통기성 적층체의 적어도 일면에 투습성 폴리우레탄 접착제를 도포한 후 부직포를 라미네이트하거나 또는 상기 통기성 적층체와 부직포를 가열 압착하여 라미네이트하는 단계;b) laminating a nonwoven fabric after applying a moisture-permeable polyurethane adhesive to at least one surface of the breathable laminate or by heat-compressing the breathable laminate and the nonwoven fabric;
를 포함하며, JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 이상, 더욱 좋게는 5 이상, 더욱 좋게는 6인 바이러스 차단성능이 우수한 보호복원단의 제조방법이다.It is a method of manufacturing a protective restoration group with excellent virus blocking performance, which includes a virus barrier property according to JIS T 8061:2015 of class 3 or more, more preferably 5 or more, and even more preferably 6.
본 발명의 일 양태에서, 상기 통기성 적층체는 폴리올레핀계 수지에 무기입자를 혼합하여 연신한 건식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층되거나, 또는 폴리올레핀계 수지에 무기입자를 혼합하여 압출 및 연신한 건식 폴리올레핀계 통기성 필름과, 폴리올레핀계 수지에 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거한 습식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층된 것일 수 있다.In one aspect of the present invention, the breathable laminate is a dry polyolefin-based breathable film obtained by mixing and stretching a polyolefin-based resin by mixing inorganic particles, or by mixing at least two or more dry polyolefin-based breathable films with a polyolefin-based resin by mixing inorganic particles and extruding and stretching them. At least two or more of the polyolefin-based air-permeable film and the wet polyolefin-based air-permeable film removed by extracting and removing the pore-forming additive after extruding and stretching the polyolefin-based resin by mixing the pore-forming additive may be laminated.
본 발명의 일 양태에서, 상기 습식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 기공형성 첨가제로 평균입경이 100 내지 1000 nm인 유기 나노입자를 혼합하여 압출 및 연신한 후, 상기 유기 나노입자를 용해할 수 있으며 상기 폴리올레핀계 수지를 용해하지 않는 용매를 이용하여 상기 유기 나노입자를 추출하여 제거함으로써 나노사이즈의 균일 기공이 형성된 것일 수 있다.In one aspect of the present invention, the wet polyolefin-based breathable film is extruded and stretched by mixing organic nanoparticles having an average particle diameter of 100 to 1000 nm as a pore-forming additive in a polyolefin-based resin, and then the organic nanoparticles can be dissolved. And, by extracting and removing the organic nanoparticles using a solvent that does not dissolve the polyolefin-based resin, nano-sized uniform pores may be formed.
본 발명의 일 양태에서, 상기 유기 나노입자는 평균입경이 서로 상이한 2종의 폴리메틸메타크릴레이트 나노입자를 혼합한 것이며, 상기 습식 폴리올레핀계 통기성 필름은 바이모달 입자분포의 균일 기공을 갖는 것일 수 있다.In one aspect of the present invention, the organic nanoparticles are a mixture of two types of polymethyl methacrylate nanoparticles having different average particle diameters, and the wet polyolefin-based breathable film may have uniform pores of a bimodal particle distribution. have.
본 발명의 일 양태에서, 상기 유기 나노입자는 평균입경이 100 내지 400 nm인 제1폴리메틸메타크릴레이트 나노입자와, 평균입경이 400 내지 1000 nm인 제2폴리메틸메타크릴레이트 나노입자를 혼합하여 사용한 것일 수 있다.In one aspect of the present invention, the organic nanoparticles are mixed with first polymethyl methacrylate nanoparticles having an average particle diameter of 100 to 400 nm and second polymethyl methacrylate nanoparticles having an average particle diameter of 400 to 1000 nm may have been used.
본 발명의 일 양태에서, 상기 기공형성 첨가제는 폴리올레핀계 수지 100 중량부에 대하여, 50 내지 300 중량부를 사용하는 것일 수 있다.In one embodiment of the present invention, the pore-forming additive may be used in an amount of 50 to 300 parts by weight based on 100 parts by weight of the polyolefin-based resin.
본 발명의 일 양태에서, 상기 무기입자는 평균입경이 0.5 내지 10 ㎛인 탄산칼슘, 탈크, 클레이, 카올린, 실리카 및 규조토 등에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 것일 수 있다.In one aspect of the present invention, the inorganic particles may be any one or a mixture of two or more selected from calcium carbonate, talc, clay, kaolin, silica, and diatomaceous earth having an average particle diameter of 0.5 to 10 μm.
본 발명의 일 양태에서, 상기 건식 폴리올레핀계 통기성 필름은 블로운 캐스팅 방법으로 제조된 것일 수 있다.In one aspect of the present invention, the dry polyolefin-based breathable film may be prepared by a blow casting method.
본 발명의 또 다른 양태는 습식 폴리올레핀계 통기성 필름의 양면에 투습성 폴리우레탄 접착제를 이용하여 건식 폴리올레핀계 통기성 필름을 적층한 바이러스 차단성능이 우수한 보호복원단으로서,Another aspect of the present invention is a protective restoration unit with excellent virus blocking performance in which a dry polyolefin-based breathable film is laminated on both sides of a wet polyolefin-based breathable film using a moisture-permeable polyurethane adhesive,
상기 습식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 평균입경이 100 내지 1000 nm인 유기 나노입자인 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거한 것이고, The wet polyolefin-based breathable film is a polyolefin-based resin mixed with an organic nanoparticle pore-forming additive having an average particle diameter of 100 to 1000 nm, extruded and stretched, and then the pore-forming additive is extracted and removed,
상기 건식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 평균입경이 0.5 내지 10 ㎛인 무기입자를 혼합하여 압출 및 연신하여 제조된 것인 바이러스 차단성능이 우수한 보호복원단을 제공한다.The dry polyolefin-based breathable film is prepared by mixing and extruding and stretching inorganic particles having an average particle diameter of 0.5 to 10 μm in a polyolefin-based resin, and provides a protective recovery fabric with excellent virus blocking performance.
본 발명의 일 양태에서, 상기 무기입자는 탄산칼슘, 탈크, 클레이, 카올린, 실리카 및 규조토에서 선택되는 어느 하나 또는 둘 이상의 혼합물이고,In one aspect of the present invention, the inorganic particles are any one or a mixture of two or more selected from calcium carbonate, talc, clay, kaolin, silica and diatomaceous earth,
상기 유기 나노입자는 평균입경이 100 내지 400 nm인 제1폴리메틸메타크릴레이트 나노입자와, 평균입경이 400 내지 1000 nm인 제2폴리메틸메타크릴레이트 나노입자를 혼합하여 사용한 것일 수 있다.The organic nanoparticles may be a mixture of first polymethyl methacrylate nanoparticles having an average particle diameter of 100 to 400 nm and second polymethyl methacrylate nanoparticles having an average particle diameter of 400 to 1000 nm.
본 발명의 일 양태에서, 상기 습식 폴리올레핀계 통기성 필름의 양면에 투습성 폴리우레탄 접착제를 이용하여 건식 폴리올레핀계 통기성 필름을 적층한 바이러스 차단성능이 우수한 보호복원단은 JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 이상, 더욱 좋게는 5 이상, 더욱 좋게는 6인 바이러스 차단성능이 우수한 보호복원단을 제공할 수 있다.In one aspect of the present invention, a protective restoration material with excellent virus blocking performance obtained by laminating a dry polyolefin-based breathable film using a moisture-permeable polyurethane adhesive on both sides of the wet polyolefin-based breathable film is a virus barrier property according to JIS T 8061:2015 This class 3 or more, more preferably 5 or more, even more preferably 6, can provide a protective recovery group excellent in virus blocking performance.
이하, 본 발명에서 ‘건식 폴리올레핀계 통기성 필름’은 폴리올레핀계 수지에 탄산칼슘 등의 무기입자를 혼합하여 압출한 후, 연신하여 제조된 통기성 필름을 의미한다. 이때, 티다이 또는 블로운 캐스팅으로 압출하는 것이 가능하며, 블로운 캐스팅으로 압출하는 경우 핀홀이 적은 필름을 제조할 수 있으므로 더욱 바람직하다. 이와같이 제조된 건식 폴리올레핀계 통기성 필름의 두께는 15 내지 30 ㎛인 것일 수 있으며, 이에 제한되는 것은 아니지만 상기 범위에서 바이러스 차단성이 우수하며, 기계적인 물성 및 통기성이 우수한 필름을 제공할 수 있다. 또한, 평량이 10 내지 50 gsm이고, ASTM D5034에 따른 인장강도가 TD 방향이 0.1 내지 3 kgf/25mm이고, MD방향이 5 내지 30 kgf/25mm이며, 신율이 30 내지 400 %이며, ASTM E96에 따른 투습도가 8500 내지 9500 g/㎡ · 24hr인물성을 모두 만족하는 범위에서 목적으로 하는 물성을 달성하기에 바람직하다.Hereinafter, in the present invention, the 'dry polyolefin-based breathable film' refers to a breathable film manufactured by extruding a polyolefin-based resin by mixing inorganic particles such as calcium carbonate, and then stretching. At this time, it is possible to extrude by T-die or blown casting, and when extruding by blown casting, it is more preferable because a film having few pinholes can be manufactured. The thickness of the dry polyolefin-based breathable film prepared as described above may be 15 to 30 μm, but is not limited thereto, but it is possible to provide a film having excellent virus barrier properties and excellent mechanical properties and breathability in the above range. In addition, the basis weight is 10 to 50 gsm, the tensile strength according to ASTM D5034 is 0.1 to 3 kgf/25mm in the TD direction, 5 to 30 kgf/25mm in the MD direction, and the elongation is 30 to 400%, according to ASTM E96 It is preferable to achieve the desired physical properties in the range where the moisture permeability according to 8500 to 9500 g/m 2 · 24hr satisfies all of the physical properties.
또한, ‘습식 폴리올레핀계 통기성 필름’은 폴리올레핀계 수지에 유기 나노입자 또는 왁스 등의 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거함으로써 균일한 크기의 기공이 형성된 통기성 필름을 의미한다. 이와같이 제조된 습식 폴리올레핀계 통기성 필름의 두께는 1 내지 15 ㎛인 것일 수 있으며, 이에 제한되는 것은 아니지만 상기 범위에서 바이러스 차단성이 우수하며, 기계적인 물성 및 통기성이 우수한 필름을 제공할 수 있다. 또한, 평량이 5 내지 20 gsm, 더욱 좋게는 5 내지 10 gsm이고, ASTM D5034에 따른 인장강도가 MD방향 및 TD 방향이 각각 3 내지 9 kgf/25mm이고, 신율이 MD방향 및 TD 방향이 각각 10 내지 60 %, 더욱 좋게는 40 내지 60 %이며, ASTM E96에 따른 투습도가 3500 내지 22000 g/㎡ · 24hr, 더욱 좋게는 10000 내지 22000 g/㎡ · 24hr인 물성을 모두 만족하는 범위에서 목적으로 하는 물성을 달성하기에 바람직하다.In addition, the 'wet polyolefin-based breathable film' is a breathable film in which pores of uniform size are formed by mixing a polyolefin-based resin with pore-forming additives such as organic nanoparticles or wax, extruding and stretching, and then extracting and removing the pore-forming additive. means The thickness of the wet polyolefin-based breathable film prepared in this way may be 1 to 15 μm, but is not limited thereto, but it is possible to provide a film having excellent virus barrier properties and excellent mechanical properties and breathability in the above range. In addition, the basis weight is 5 to 20 gsm, more preferably 5 to 10 gsm, the tensile strength according to ASTM D5034 is 3 to 9 kgf/25mm in the MD direction and the TD direction, respectively, and the elongation is 10 in the MD direction and the TD direction, respectively to 60%, more preferably 40 to 60%, and the moisture permeability according to ASTM E96 is 3500 to 22000 g/m 2 · 24 hr, more preferably 10000 to 22000 g/m · 24 hr. It is desirable to achieve physical properties.
상기 ‘건식 폴리올레핀계 통기성 필름’ 및 ‘습식 폴리올레핀계 통기성 필름’의 제조방법은 통상의 방법으로 제조 가능하므로 구체적인 설명을 생략한다.The manufacturing method of the 'dry polyolefin-based air-permeable film' and the 'wet polyolefin-based air-permeable film' can be prepared by a conventional method, and thus a detailed description thereof will be omitted.
본 발명에서, 상기 통기성 적층체는 건식 폴리올레핀계 통기성 필름이 두층 이상 적층되거나, 또는 건식 폴리올레핀계 통기성 필름과 습식 폴리올레핀계 통기성 필름이 교번하여 적층된 것을 의미한다.In the present invention, the breathable laminate means that two or more layers of a dry polyolefin-based breathable film are laminated, or a dry polyolefin-based breathable film and a wet polyolefin-based breathable film are alternately laminated.
상기 통기성 적층체로 습식 폴리올레핀계 통기성 필름이 두층 이상 적층되는 것을 배제하는 것은 아니지만, 이 경우는 IS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 미만으로 저하될 수 있다. Although it is not excluded that two or more layers of the wet polyolefin-based breathable film are laminated as the breathable laminate, in this case, the virus barrier property according to IS T 8061:2015 may be lowered to less than class 3.
또한, 상기 통기성 적층체와 부직포의 적층하여 보호복원단으로 제조하였을 때, 습식 폴리올레핀계 통기성 필름이 2층 이상 적층된 것에 비하여, 건식 폴리올레핀계 통기성 필름이 두층 이상 적층되거나, 또는 건식 폴리올레핀계 통기성 필름과 습식 폴리올레핀계 통기성 필름이 교번하여 적층된 경우에 사용자로 하여금 통기성 및 투습성이 더욱 좋으며, 착용감이 부드럽고 두께가 얇아 원단이 가벼운 장점이 있다. 또한, 원단의 무게가 더욱 가볍고 착용감이 더욱 개선되는 관점에서는 건식 폴리올레핀계 통기성 필름과 습식 폴리올레핀계 통기성 필름이 교번하여 적층되는 것이 선호될 수 있다.In addition, when the air-permeable laminate and the nonwoven fabric are laminated to prepare a protective recovery film, compared to that in which two or more layers of the wet polyolefin-based breathable film are laminated, two or more layers of the dry polyolefin-based breathable film are laminated, or a dry polyolefin-based breathable film When the wet polyolefin-based breathable film is alternately laminated, it allows the user to have better breathability and moisture permeability, and has the advantage of being soft and the fabric is light because of its thin thickness. In addition, it may be preferable to alternately laminate the dry polyolefin-based air-permeable film and the wet polyolefin-based air-permeable film from the viewpoint of a lighter fabric weight and improved wearing comfort.
이하에서는 본 발명의 보호복원단의 적층구조를 도면을 참고하여 더욱 구체적으로 설명한다.Hereinafter, the laminated structure of the protective restoration of the present invention will be described in more detail with reference to the drawings.
본 발명의 보호복원단의 제 1 양태는 도 1에 도시된 바와 같이, 순차적으로 부직포(20), 습식 폴리올레핀계 통기성 필름(11) 및 건식 폴리올레핀계 통기성 필름(12)이 적층된 것이다. 이때, 상기 습식 폴리올레핀계 통기성 필름 및 건식 폴리올레핀계 통기성 필름은 투습성 폴리우레탄 접착제를 이용하여 라미네이트 되어 통기성 적층체(10)를 이루고, 상기 통기성 적층체(10)의 습식 폴리올레핀계 통기성 필름(11)과 부직포(20)는 투습성 폴리우레탄 접착제 또는 가열 압착하여 라미네이트 되며, JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 이상, 더욱 좋게는 5 이상인 것일 수 있다.In a first aspect of the protective restoration of the present invention, as shown in FIG. 1 , a nonwoven fabric 20, a wet polyolefin-based breathable film 11 and a dry polyolefin-based breathable film 12 are sequentially laminated. At this time, the wet polyolefin-based breathable film and the dry polyolefin-based breathable film are laminated using a moisture-permeable polyurethane adhesive to form a breathable laminate 10, and the wet polyolefin-based breathable film 11 of the breathable laminate 10 and The nonwoven fabric 20 is laminated with a moisture-permeable polyurethane adhesive or heat-compressed, and may have a virus barrier property according to JIS T 8061:2015 of class 3 or more, more preferably 5 or more.
상기 제 1 양태와 같이, 습식 폴리올레핀계 통기성 필름과 건식 폴리올레핀계 통기성 필름이 적층된 통기성 적층체(10)를 사용하는 경우, 건식 폴리올레핀계 통기성 필름이 최외층을 이루는 것이 바람직하다. 이와 같이 건식 폴리올레핀계 통기성 필름이 최외층을 이루도록 함으로써 바이러스 차단 특성 뿐만 아니라, 통기성이 더욱 우수하여 착용자로 하여금 착용감이 더욱 우수한 보호복을 제공할 수 있다.As in the first aspect, when using the breathable laminate 10 in which the wet polyolefin-based breathable film and the dry polyolefin-based breathable film are laminated, it is preferable that the dry polyolefin-based breathable film forms the outermost layer. As such, by forming the dry polyolefin-based breathable film as the outermost layer, it is possible to provide a protective suit with better wearability to the wearer due to better ventilation as well as virus blocking properties.
또한, 상기 제 1 양태와 같이, 습식 폴리올레핀계 통기성 필름과 건식 폴리올레핀계 통기성 필름이 적층된 통기성 적층체(10)를 사용하는 경우, 건식 폴리올레핀계 통기성 필름이 2층 이상 적층되는 경우에 비하여 원단의 두께가 더욱 얇으면서도 바이러스 차단성 및 통기성이 우수한 원단을 제공할 수 있다.In addition, as in the first aspect, when using the breathable laminate 10 in which the wet polyolefin-based breathable film and the dry polyolefin-based breathable film are laminated, the dry polyolefin-based breathable film is laminated in two or more layers compared to the case of the fabric. It is possible to provide a fabric having a thinner thickness and excellent virus blocking properties and air permeability.
본 발명의 보호복원단의 제 2 양태는 도 2에 도시된 바와 같이, 순차적으로 부직포(20), 습식 폴리올레핀계 통기성 필름(11), 건식 폴리올레핀계 통기성 필름(12) 및 부직포(20)가 적층된 것이다. 이외는 상기 제 1 양태와 동일하므로 중복 설명을 생략한다.In the second aspect of the protective restoration of the present invention, as shown in FIG. 2, the nonwoven fabric 20, the wet polyolefin-based breathable film 11, the dry polyolefin-based breathable film 12 and the nonwoven fabric 20 are sequentially laminated. it has become Other than that, since it is the same as that of the first aspect, a redundant description will be omitted.
본 발명의 보호복원단의 제 3 양태는 도 3에 도시된 바와 같이, 순차적으로 부직포(20), 제1건식 폴리올레핀계 통기성 필름(12) 및 제2건식 폴리올레핀계 통기성 필름(12)이 적층된 것이다. 이외는 상기 제 1 양태와 동일하므로 중복 설명을 생략한다.A third aspect of the protective restoration of the present invention, as shown in FIG. 3, sequentially a nonwoven fabric 20, a first dry polyolefin-based breathable film 12 and a second dry polyolefin-based breathable film 12 are laminated will be. Other than that, since it is the same as that of the first aspect, a redundant description will be omitted.
본 발명의 보호복원단의 제 4 양태는 도 4에 도시된 바와 같이, 순차적으로 부직포(20), 제1건식 폴리올레핀계 통기성 필름(12), 제2건식 폴리올레핀계 통기성 필름(12) 및 부직포(20)가 적층된 것이다. 이외는 상기 제 1 양태와 동일하므로 중복 설명을 생략한다.As shown in FIG. 4, the fourth aspect of the protective restoration of the present invention is sequentially a nonwoven fabric 20, a first dry polyolefin-based breathable film 12, a second dry polyolefin-based breathable film 12 and a nonwoven fabric ( 20) is stacked. Other than that, since it is the same as that of the first aspect, a redundant description will be omitted.
본 발명의 보호복원단의 제 5 양태는 도 5에 도시된 바와 같이, 순차적으로 제1건식 폴리올레핀계 통기성 필름(12), 습식 폴리올레핀계 통기성 필름(11) 및 제2건식 폴리올레핀계 통기성 필름(12)이 적층된 것이다.As shown in FIG. 5, a fifth aspect of the protective restoration of the present invention is sequentially a first dry polyolefin-based breathable film 12, a wet polyolefin-based breathable film 11 and a second dry polyolefin-based breathable film 12 ) are stacked.
이하는 본 발명의 각 구성에 대하여 보다 구체적으로 설명한다.Hereinafter, each configuration of the present invention will be described in more detail.
먼저 건식 폴리올레핀계 통기성 필름에 대하여 설명하면, 폴리올레핀계 수지에 무기입자를 혼합하여 연신한 것이다. First, the dry polyolefin-based breathable film is described by mixing inorganic particles with a polyolefin-based resin and stretching.
상기 폴리올레핀계 수지로는 특별한 제한은 없으나, 폴리에틸렌수지 단독 또는 폴리에틸렌수지와 폴리프로필렌 수지를 혼합하여 사용할 수 있다.The polyolefin-based resin is not particularly limited, but a polyethylene resin alone or a mixture of a polyethylene resin and a polypropylene resin may be used.
상기 폴리에틸렌 수지는 중량평균 분자량이 300,000~500,000 g/mol인 것일 수 있으며, 이에 제한되는 것은 아니다. 상기 폴리프로필렌 수지는 중량평균분자량이 200,000~400,000 g/mol인 것이 바람직하며, 이에 제한되는 것은 아니다. 또한이들을 혼합하여 사용하는 경우, 폴리에틸렌 수지 100 중량부에 대하여, 폴리프로필렌 수지 5~50 중량부를 첨가하여 사용하는 것이 더욱 좋다.The polyethylene resin may have a weight average molecular weight of 300,000 to 500,000 g/mol, but is not limited thereto. The polypropylene resin preferably has a weight average molecular weight of 200,000 to 400,000 g/mol, but is not limited thereto. In addition, in the case of using a mixture of these, it is more preferable to use by adding 5 to 50 parts by weight of a polypropylene resin with respect to 100 parts by weight of the polyethylene resin.
상기 폴리에틸렌 수지는 더욱 구체적으로, 저밀도폴리에틸(LDPE) 및 선형저밀도폴리에틸렌(LLDPE)에서 선택되는 어느 하나 또는 이들의 혼합물을 사용하는 것일 수 있으며, 이들을 혼합하여 사용하는 경우 더욱 부드럽고 착용감이 좋다. 구체적으로 예를 들면, 용융지수가 1 내지 10 g/10min(190℃, 2.16kg)이고, 밀도가 0.8 내지 1.0g/㎤(23℃)인 저밀도폴리에틸(LDPE)과, 용융지수가 1 내지 10 g/10min(190℃, 2.16kg)이고, 밀도가 0.8 내지 1.0g/㎤(23℃)인 선형저밀도폴리에틸렌(LLDPE)를 혼합하여 사용할 수 있다. More specifically, the polyethylene resin may be any one selected from low-density polyethylene (LDPE) and linear low-density polyethylene (LLDPE) or a mixture thereof, and when used as a mixture, it is softer and more comfortable to wear. Specifically, for example, low-density polyethylene (LDPE) having a melt index of 1 to 10 g/10 min (190° C., 2.16 kg) and a density of 0.8 to 1.0 g/cm 3 (23° C.), and a melt index of 1 to Linear low-density polyethylene (LLDPE) of 10 g/10min (190° C., 2.16 kg) and a density of 0.8 to 1.0 g/cm 3 (23° C.) may be mixed and used.
상기 무기입자는 통상적으로 해당 분야에서 사용되는 것이라면 제한되지 않고 사용할 수 있지만, 구체적으로 예를 들면 탄산칼슘, 탈크, 클레이, 카올린, 실리카 및 규조토 등에서 선택되는 어느 하나 또는 둘 이상의 혼합물을 사용할 수 있다. 상기 탄산칼슘은 평균입경이 0.5 내지 10 ㎛, 더욱 좋게는 1 내지 5 ㎛인 것을 사용할 수 있으며, 이에 제한되는 것은 아니지만 상기 범위에서 우수한 통기성 및 바이러스 차단성을 제공할 수 있다.The inorganic particles may be used without limitation as long as they are conventionally used in the relevant field, and specifically, for example, any one or a mixture of two or more selected from calcium carbonate, talc, clay, kaolin, silica and diatomaceous earth may be used. The calcium carbonate may have an average particle diameter of 0.5 to 10 μm, more preferably 1 to 5 μm, and is not limited thereto, but may provide excellent air permeability and virus protection in the above range.
또한, 상기 무기입자는 필름 전체 중량 중 30 내지 55 중량%, 더욱 구체적으로 40 내지 50 중량%를 사용하는 것일 수 있다. 상기 범위에서 통기성이 우수한 필름을 제공할 수 있으나, 이에 제한되는 것은 아니다.In addition, the inorganic particles may be used in an amount of 30 to 55% by weight, more specifically 40 to 50% by weight of the total weight of the film. In the above range, a film having excellent ventilation may be provided, but the present invention is not limited thereto.
다음으로 습식 폴리올레핀계 통기성 필름에 대하여 설명하면, 폴리올레핀계 수지에 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거 함으로써, 통기성 필름에 나노사이즈의 균일 기공이 형성된 것이다.Next, describing the wet polyolefin-based breathable film, the pore-forming additive is mixed with the polyolefin-based resin, extruded and stretched, and then the pore-forming additive is extracted and removed, thereby forming nano-sized uniform pores in the breathable film.
상기 폴리올레핀계 수지는 앞서 설명한 바와 같으므로 중복 설명을 생략한다.Since the polyolefin-based resin is the same as described above, redundant description thereof will be omitted.
상기 기공형성 첨가제로는 예컨대 비부틸프탈레이트(Dibutyl phthalate), 디헥실프탈레이트(Dihexylphthalate) 등 프탈산 에스테르(Phthalic acid)류; 또는 디 페닐에테르(Diphenyl ether) 등의 방향족 에테르류를 사용할 수 있다. 또한, 고상 파라핀왁스와 액상 파라핀 오일을 사용할 수 있고, 폴리올레핀계 수지 100 중량부에 대하여, 중량평균 분자량이 3,000~5,000 g/mol인 고상 파라핀 왁스 80~100 중량부와 중량평균 분자량이 400~1,000 g/mol인 액상 파라핀 오일 60~80 중량부를 혼합하여 사용할 수도 있다. Examples of the pore-forming additive include phthalic acid such as dibutyl phthalate and dihexylphthalate; Alternatively, aromatic ethers such as diphenyl ether may be used. In addition, solid paraffin wax and liquid paraffin oil can be used, and with respect to 100 parts by weight of the polyolefin-based resin, 80 to 100 parts by weight of a solid paraffin wax having a weight average molecular weight of 3,000 to 5,000 g/mol and a weight average molecular weight of 400 to 1,000 60 to 80 parts by weight of liquid paraffin oil of g/mol may be mixed and used.
더욱 좋게는 평균입경이 100 내지 1000 nm인 유기 나노입자를 사용할 수 있다. 상기 유기 나노입자는 폴리올레핀 수지와 혼련성이 우수한 아크릴계 나노입자를 사용할 수 있으며, 구체적으로 평균입경이 서로 상이한 2종의 폴리메틸메타크릴레이트(PMMA) 나노입자를 혼합하여 사용하는 것이 좋다. 이에 따라, 상기 습식 폴리올레핀계 통기성 필름은 바이모달 입자분포의 균일 기공을 갖는 것일 수 있다. 본 발명에서 ‘균일 기공’이란, 상기 유기 나노입자가 제거되면서, 상기 유기 나노입자가 있던 자리에 유기 나노입자의 크기와 동일한 크기 및 형상의 기공이 형성되는 것을 의미한다.More preferably, organic nanoparticles having an average particle diameter of 100 to 1000 nm may be used. As the organic nanoparticles, acrylic nanoparticles having excellent kneading properties with the polyolefin resin may be used. Specifically, it is preferable to use a mixture of two types of polymethyl methacrylate (PMMA) nanoparticles having different average particle diameters. Accordingly, the wet polyolefin-based breathable film may have uniform pores having a bimodal particle distribution. In the present invention, 'uniform pores' means that while the organic nanoparticles are removed, pores having the same size and shape as those of the organic nanoparticles are formed in the place where the organic nanoparticles were.
이와 같이 바이모달 입자 크기를 가지며, 균일한 크기의 기공이 형성됨에 따라 더욱 우수한 통기성과 바이러스 차단성을 제공할 수 있다.As such, it has a bimodal particle size, and as pores of a uniform size are formed, it is possible to provide better air permeability and virus blocking properties.
상기 기공형성 첨가제는 폴리올레핀계 수지 100 중량부에 대하여, 50 내지 300 중량부를 사용하는 것일 수 있다. 더욱 구체적으로, 상기 기공형성 첨가제는 평균입경이 100 내지 400 nm인 제1폴리메틸메타크릴레이트 나노입자와, 평균입경이 400 내지 1000 nm인 제2폴리메틸메타크릴레이트 나노입자를 혼합하여 사용하는 것일 수 있으며, 이들의 혼합비율을 제한되는 것은 아니지만 폴리올레핀계 수지 100 중량부에 대하여, 제1폴리메틸메타크릴레이트 나노입자 100 내지 120 중량부와 제2폴리메틸메타크릴레이트 나노입자 80 내지 100 중량부를 사용하는 것일 수 있다.The pore-forming additive may be used in an amount of 50 to 300 parts by weight based on 100 parts by weight of the polyolefin-based resin. More specifically, the pore-forming additive is a mixture of first polymethyl methacrylate nanoparticles having an average particle diameter of 100 to 400 nm and second polymethyl methacrylate nanoparticles having an average particle diameter of 400 to 1000 nm. may be, and their mixing ratio is not limited, but based on 100 parts by weight of the polyolefin-based resin, 100 to 120 parts by weight of the first polymethyl methacrylate nanoparticles and 80 to 100 parts by weight of the second polymethyl methacrylate nanoparticles It could be the use of wealth.
또한, 상기 기공형성 첨가제를 추출하는 방법은 상기 폴리올레핀계 수지는 용해하지 않으면서, 상기 기공형성 첨가제 만을 용해할 수 있는 용매를 사용하여 추출할 수 있다. 이에 따라 상기 구형의 기공형성 첨가제가 있던 자리에 기공이 형성이 되며, 균일한 크기의 기공형성 첨가제를 사용함에 따라 기공형성 첨가제와 동일한 크기의 균일하고 연속적인 기공이 형성될 수 있다. 또한, 보다 미세한 크기의 나노사이즈의 기공 형성이 가능하므로 바이러스 차단성이 더욱 우수한 필름을 제조할 수 있다.In addition, in the method of extracting the pore-forming additive, the polyolefin-based resin may not be dissolved, and extraction may be performed using a solvent capable of dissolving only the pore-forming additive. Accordingly, pores are formed in the place where the spherical pore-forming additive was, and by using the pore-forming additive of a uniform size, uniform and continuous pores having the same size as the pore-forming additive can be formed. In addition, since nano-sized pores having a finer size can be formed, a film having better virus blocking properties can be prepared.
본 발명의 일 양태에서, 상기 부직포는 스펀본드, 또는 스펀레이스 등으로 제조하는 부직포 등을 사용할 수 있다. 대표적으로 부직포에 대하여 설명하다면 다음과 같다. 부직포란 통상의 스펀본드법, 또는 스펀레이스법으로 제조된 부직포를 의미하는 것으로, 제한되지 않으나 폴리에스테르, 나일론, 폴리에틸렌, 폴리프로필렌에서 선택되는 어느 한 종의 수지, 보다 바람직하게는 폴리프로필렌 수지를 사용한 스펀본드를 사용하는 것이 바람직하며, 통상의 스펀본드법, 또는 스펀레이스법에 의해 부직포로 제조된 것을 사용할 수 있다. 예를 들면 평량이 10 ~ 300 gsm인 스펀본드 부직포를 사용할 수 있다. 본 발명은 이러한 부직포를 사용함으로써 통기성이 우수한 효과를 또한 달성할 수 있다. In one embodiment of the present invention, the nonwoven fabric may be a nonwoven fabric made of spunbond or spunlace. Representatively, the nonwoven fabric is described as follows. Non-woven fabric refers to a non-woven fabric produced by a conventional spunbond method or a spunlace method, but is not limited to, but is not limited to, any one resin selected from polyester, nylon, polyethylene, and polypropylene, more preferably a polypropylene resin. It is preferable to use the used spunbond, and a nonwoven fabric manufactured by a conventional spunbonding method or a spunlace method may be used. For example, a spunbond nonwoven fabric having a basis weight of 10 to 300 gsm may be used. The present invention can also achieve the effect of excellent air permeability by using such a nonwoven fabric.
본 발명에 따른 보호복원단은 두께가 100 내지 300 ㎛이며, ASTM D5034에 따른 인장강도가 100 N/50mm 이상이고, 신율이 40 % 이상이고, ASTM E96에 따른 투습도가 3000 g/㎡ · 24hr 이상이고, AATCC 127에 따른 내수압이 300 mbar 이상인 물성을 동시에 만족할 수 있다.The protective restoration fabric according to the present invention has a thickness of 100 to 300 μm, a tensile strength of 100 N/50 mm or more according to ASTM D5034, an elongation of 40% or more, and a moisture permeability of 3000 g/m 2 · 24hr or more according to ASTM E96 and the water pressure resistance of 300 mbar or more according to AATCC 127 can be satisfied at the same time.
다음으로 본 발명의 보호복원단을 제조하는 방법에 대하여 설명한다.Next, a method for manufacturing the protective clothing of the present invention will be described.
본 발명의 JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 5 이상인 보호복원단의 제조방법의 일 양태는One aspect of the method for manufacturing a protective restoration group having a virus barrier property of class 5 or higher according to JIS T 8061:2015 of the present invention is
a) 적어도 둘 이상의 통기성 필름을 투습성 폴리우레탄 접착제를 이용하여 라미네이트하여 통기성 적층체를 제조하는 단계;a) laminating at least two or more breathable films using a moisture-permeable polyurethane adhesive to prepare a breathable laminate;
b) 상기 통기성 적층체의 적어도 일면에 투습성 폴리우레탄 접착제를 도포한 후 부직포를 라미네이트하거나 또는 상기 통기성 적층체와 부직포를 가열 압착하여 라미네이트하는 단계;b) laminating a nonwoven fabric after applying a moisture-permeable polyurethane adhesive to at least one surface of the breathable laminate or by heat-compressing the breathable laminate and the nonwoven fabric;
를 포함한다.includes
상기 a)단계에서 사용되는 투습성 폴리우레탄 접착제는 통상적으로 해당 분에서 사용되는 것이라면 제한되지 않고 사용될 수 있다. The moisture-permeable polyurethane adhesive used in step a) may be used without limitation, as long as it is commonly used in the corresponding minutes.
상기 통기성 폴리우레탄 접착제는 폴리에틸렌 글리콜 디올(Polyethylene glycol diol) 또는 폴리프로필렌 글리콜 디올(Polypropylene glycol diol), 또는 이들의 혼합 디올에서 선택되는 디올 성분을 함유하는 폴리올, 이소시아네이트를 포함하며, 좋게는 쇄연장제, 촉매 및 유기용매를 더 포함할 수 있다. 본 발명의 통기성 폴리 우레탄의 중합법으로는 통상적으로 알려져 있는 용액 중합법 등의 것이므로 더 이상의 구체적인 설명은 생략한다. 통기성 폴리우레탄 수지(접착제)는 100~50,000gram/㎡ x 24시간(ASTM E96) 범위의 투습도를 가지는 것이 본 발명의 목적에 적합하다.The breathable polyurethane adhesive includes a polyol containing a diol component selected from polyethylene glycol diol or polypropylene glycol diol, or a mixed diol thereof, and isocyanate, preferably a chain extender , a catalyst and an organic solvent may be further included. As the polymerization method of the air-permeable polyurethane of the present invention, a solution polymerization method, which is commonly known, and the like, a detailed description thereof will be omitted. It is suitable for the purpose of the present invention that the breathable polyurethane resin (adhesive) has a moisture permeability in the range of 100 to 50,000 gram/m 2 x 24 hours (ASTM E96).
구체적으로 예를 들면, 수평균분자량 100 내지 500,000의 폴리에틸렌글리콜, 폴리프로필렌글리콜 디올, 또는 이의 혼합디올 성분을 포함하는 폴리올로 제조한 폴리우레탄접착제 조성물을 사용할 수 있다.Specifically, for example, a polyurethane adhesive composition prepared from a polyol containing polyethylene glycol having a number average molecular weight of 100 to 500,000, polypropylene glycol diol, or a mixed diol component thereof may be used.
상기 폴리올은 폴리에틸렌에테르글리콜 디올, 폴리프로필렌에테르글리콜 디올 또는 이의 혼합디올 성분을 포함하는 폴리올성분을 사용하며, 그의 수평균 분자량은 100 내지 500,000의 범주에 속하고, 통기성 폴리우레탄 접착제조성물의 고형분 100 중량부에 대하여 폴리에틸렌에테르글리콜 디올, 폴리프로필렌에테르글리콜 디올 또는 이의 혼합디올 성분을 포함하는 폴리올 성분의 함량은 10 내지 90 중량부의 범위로 사용하여 통기성을 유지하도록 한다.The polyol uses a polyol component comprising polyethylene ether glycol diol, polypropylene ether glycol diol or a mixed diol component thereof, and its number average molecular weight is in the range of 100 to 500,000, and the air permeable polyurethane adhesive composition has a solid content of 100 weight The content of the polyol component including polyethylene ether glycol diol, polypropylene ether glycol diol or a mixed diol component thereof is used in the range of 10 to 90 parts by weight to maintain air permeability.
상기 통기성 폴리우레탄 수지(접착제)의 이소시아네이트로는 1,6-헥사메틸렌디이소시아네이트(1,6-Hexamethylene diisocyanate, HDI), 이소프론디이소시아네이트(Isophoronediisocyanate, IPDI), 메타-자인렌디이소시아네이트(m-Xylenediisocyanate, m-XDI), 수소첨가 메틸렌디페닐렌디이소시아네이트(Hydrogenated Diphenylenedimethylenediisocyanate, H 12 MDI),메타-테트라메틸자일렌디이소시아네이트(m-Tetramethylxylennediisocyanate, m-TMXDI)중에서 하나 또는 하나 이상을 병용하여 사용할 수 있다. As isocyanates of the air-permeable polyurethane resin (adhesive), 1,6-hexamethylene diisocyanate (1,6-Hexamethylene diisocyanate, HDI), isophoronediisocyanate (IPDI), meta-Xylenediisocyanate (m-Xylenediisocyanate) , m-XDI), hydrogenated methylenediphenylene diisocyanate (Hydrogenated Diphenylenedimethylenediisocyanate, H 12 MDI), and meta-tetramethylxylene diisocyanate (m-Tetramethylxylennediisocyanate, m-TMXDI), one or more of them can be used in combination.
상기 통기성 폴리우레탄 수지(접착제)의 쇄연장제로는 에틸렌글리콜(Ethyleneglycol, EG), 1, 4-부탄디올(1,4-Butanediol. 1,4-BD), 1,6-헥산디올(1,6-Hexanediol, 1,6-HD), 1,2-프로필렌글리콜(, 1,2-Propyleneglycol, 1,2-PG), 1,3-프로판 디올(1,3-Propanediol, 1,3-PDO), 네오펜틸글리콜(Neopentylglycol, NPG), 2-메틸1,3-프로판디올(2-Methyl-1,3-Propanediol, 2-MPD), 3-메틸-1,5-펜탄디올(3-Methyl-1,5-Pentanediol, 3-MPD), 2-부틸-2-에틸-1,3-프로탄디올(2-Butyl-2-ethyl-1,3-propanediol, BEPD)등에서 하나 또는 하나이상을 병용하여 사용하나 특정하지는 않는다. 사용하는 경우 그 함량은 전체 고형분의 0.01~5중량부를 사용하는 것이 좋지만 반드시 이에 한정되는 것은 아니다.As a chain extender of the breathable polyurethane resin (adhesive), ethylene glycol (Ethyleneglycol, EG), 1,4-butanediol (1,4-Butanediol. 1,4-BD), 1,6-hexanediol (1,6) -Hexanediol, 1,6-HD), 1,2-propylene glycol (, 1,2-Propyleneglycol, 1,2-PG), 1,3-propanediol (1,3-Propanediol, 1,3-PDO) , Neopentylglycol (NPG), 2-methyl 1,3-propanediol (2-Methyl-1,3-Propanediol, 2-MPD), 3-methyl-1,5-pentanediol (3-Methyl- 1,5-Pentanediol, 3-MPD), 2-butyl-2-ethyl-1,3-propanediol (2-Butyl-2-ethyl-1,3-propanediol, BEPD), etc. or one or more in combination used, but not specified. When used, the content is preferably 0.01 to 5 parts by weight of the total solid content, but is not necessarily limited thereto.
통기성 폴리우레탄 수지(접착제) 제조 시 촉매는 폴리우레탄 산업계에서 사용하는 촉매를 사용하나 어느 하나를 특정하지는 않으며, 사용하지 않을 수도 있다. When producing a breathable polyurethane resin (adhesive), the catalyst used in the polyurethane industry is used, but any one is not specified and may not be used.
폴리우레탄 수지(접착제) 제조 시 유기용매로는 아세톤(Acetone), 톨루엔(Toluene), Xylene, Ethyl acetate, 2-Butanone, Cyclohexanone, N,N-Dimethylacetamine, N,N-Dimethylformamide, N-Methylpyrroridinone, Dichloromethane, Ethanol, Isopropyl alcohol, Methanol중에서 1종 또는 2종 이상을 혼용하여 사용한다. Acetone, toluene, Xylene, Ethyl acetate, 2-Butanone, Cyclohexanone, N,N-Dimethylacetamine, N,N-Dimethylformamide, N-Methylpyrroridinone, Dichloromethane , Ethanol, Isopropyl alcohol, and Methanol are used in combination with one or two or more.
상기 통기성 폴리우레탄 접착제 조성물을 고형분이 1~90중량%, 좋게는 10~85중량%의 용액으로 사용하는 것이 좋으며, 코팅방법은 전면을 코팅할 수 있는 롤코팅, 딥코팅, 플로우 코팅, 그라비아코팅, 슬롯다이코팅 등의 코팅법을 채택할 수 있다.It is recommended to use the breathable polyurethane adhesive composition as a solution of 1 to 90% by weight, preferably 10 to 85% by weight of solids, and the coating method is roll coating, dip coating, flow coating, gravure coating that can coat the entire surface. , a coating method such as slot die coating can be adopted.
본 발명은 통기성 적층체와 부직포를 통기성 폴리우레탄접착제로 적층시킴으로써 강도와 동시에 수분에 대한 저항력을 향상시킬 수 있었으며, 합지시 통기성을 유지하면서도 접착 강도가 향상되어 장기 사용에도 각층들이 분리되는 것을 방지할 수 있는 추가적인 효과도 가짐을 알게 되어 장기 안정적 사용이 가능하다.The present invention was able to improve strength and resistance to moisture at the same time by laminating a breathable laminate and a nonwoven fabric with a breathable polyurethane adhesive, and while maintaining breathability during lamination, the adhesive strength is improved to prevent separation of each layer even after long-term use It has been found that it has additional effects that can be used, so that it can be used stably for a long time.
또한, 상기 통기성 적층체는 폴리올레핀계 수지에 무기입자를 혼합하여 연신한 건식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층되거나, 또는 폴리올레핀계 수지에 무기입자를 혼합하여 압출 및 연신한 건식 폴리올레핀계 통기성 필름과, 폴리올레핀계 수지에 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거한 습식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층된 것일 수 있다. In addition, the air-permeable laminate includes at least two or more dry polyolefin-based air-permeable films obtained by mixing and stretching a polyolefin-based resin by mixing inorganic particles, or a dry polyolefin-based air-permeable film obtained by mixing and stretching a polyolefin-based resin by mixing inorganic particles and stretching. , After extruding and stretching the polyolefin-based resin by mixing the pore-forming additive, the pore-forming additive is extracted and removed, and at least two or more wet polyolefin-based breathable films may be laminated.
상기 습식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 기공형성 첨가제로 평균입경이 100 내지 1000 nm인 유기 나노입자를 혼합하여 압출 및 연신한 후, 상기 유기 나노입자를 용해할 수 있으며 상기 폴리올레핀계 수지를 용해하지 않는 용매를 이용하여 상기 유기 나노입자를 추출하여 제거함으로써 나노사이즈의 균일 기공이 형성된 것일 수 있다.The wet polyolefin-based breathable film is extruded and stretched by mixing organic nanoparticles having an average particle diameter of 100 to 1000 nm as a pore-forming additive in a polyolefin-based resin, and then the organic nanoparticles can be dissolved and the polyolefin-based resin is dissolved By extracting and removing the organic nanoparticles using a solvent not used, nano-sized uniform pores may be formed.
다음으로 b)단계에서, 상기 통기성 적층체의 적어도 일면에 투습성 폴리우레탄 접착제를 도포한 후 부직포를 라미네이트하거나 또는 상기 통기성 적층체와 부직포를 가열 압착하여 라미네이트하여 JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 5 이상인 바이러스 차단성능이 우수한 보호복원단을 제조한다.Next, in step b), after applying a moisture-permeable polyurethane adhesive to at least one surface of the air-permeable laminate, the non-woven fabric is laminated or the air-permeable laminate and the non-woven fabric are heat-compressed and laminated to form a virus barrier property according to JIS T 8061:2015 We manufacture protective clothing with excellent virus blocking performance of this class 5 or higher.
이때 투습성 폴리우레탄 접착제는 상기한 바와 동일하므로 중복 설명을 생략한다.At this time, since the moisture-permeable polyurethane adhesive is the same as described above, redundant description is omitted.
상기 가열 압착은 통상적인 공정에 따라, 통기성 적층체의 통기성을 저해하지 않으면서 부직포와 가열 접착될 수 있는 온도 및 압력을 가하여 일체화하는 것일 수 있다. 따라서 온도 및 압력은 수지의 종류에 따라 변경가능하며, 구체적으로 제한되지 않는다.The heat compression may be integrated by applying a temperature and pressure that can be heat-bonded with the nonwoven fabric without inhibiting the air permeability of the air-permeable laminate according to a conventional process. Therefore, the temperature and pressure can be changed according to the type of resin, and is not specifically limited.
이하 실시예 및 비교예를 바탕으로 본 발명을 더욱 상세히 설명한다. 다만 하기 실시예 및 비교예는 본 발명을 더욱 상세히 설명하기 위한 하나의 예시일 뿐, 본 발명이 하기 실시예 및 비교예에 의해 제한되는 것은 아니다. Hereinafter, the present invention will be described in more detail based on Examples and Comparative Examples. However, the following examples and comparative examples are merely examples for explaining the present invention in more detail, and the present invention is not limited by the following examples and comparative examples.
물성은 다음과 같이 측정하였다.Physical properties were measured as follows.
1) 인장강도 : ASTM D5034에 따라 종방향(기계방향) 및 횡방향(기계수직방향)에 따른 파단 시 인장강도를 측정하였다.1) Tensile strength: In accordance with ASTM D5034, the tensile strength at break in the longitudinal (machine direction) and transverse (machine vertical direction) directions was measured.
2)　신율 : ASTM D5034에 따라 종방향(기계방향) 및 횡방향(기계수직방향)에 따른 파단 시 신율을 측정하였다.2) 　 Elongation: According to ASTM D5034, the elongation at break was measured in the longitudinal (machine direction) and transverse (machine vertical direction) directions.
3）투습도 : ASTM E96에 준하여, 항온항습 조건하에 일정시간 보관 후 무게증가에 따른 투습도를 측정하였다.3) Moisture permeability: In accordance with ASTM E96, the moisture permeability was measured according to weight increase after storage for a certain period of time under constant temperature and humidity conditions.
4）내수압 : AATCC 127에 준하여 내수압성을 측정하였다.　4) Water pressure resistance: Water pressure resistance was measured according to AATCC 127.
5）바이러스 차단성 : 일본 공인 시험기관 KAKEN에 의뢰하여 측정하였다. 5) Virus blocking properties: Measured by requesting a Japanese authorized testing institute, KAKEN.
JIS T 8061:2015에 따라 측정되었으며, Class 1 내지 6으로 구분되고, Class 6가 바이러스 차단 국제 기준 최고 등급으로 가장 우수한 것이다. Measured according to JIS T 8061:2015, it is classified into Class 1 to 6, and Class 6 is the best as the highest grade of international virus protection standards.
[제조예 1] 건식 통기성 필름의 제조[Preparation Example 1] Preparation of dry breathable film
저밀도폴리에틸(LDPE, 용융지수 5.3g/10min(190℃, 2.16kg)이고, 밀도가 0.919g/㎤(23℃), 한화석유화학 제품명: 960) 10 중량%, 선형저밀도폴리에틸렌(LLDPE, 용융지수가 3.2g/10min(190℃, 2.16kg)이고, 밀도가 0.923g/㎤(23℃), 한화석유화학, 제품명: HS 1700) 40 중량%, 평균입경 1㎛ 탄산칼슘 45 중량% 및 첨가제로 활제 (Ca-St) 5 중량%를 배합기에서 혼합 한 후 건조시켜 함량 1% 이하가 되도록 하였다.Low-density polyethylene (LDPE, melt index 5.3g/10min (190℃, 2.16kg), density 0.919g/cm3 (23℃), Hanwha Petrochemical product name: 960) 10% by weight, linear low-density polyethylene (LLDPE, melt Index of 3.2g/10min (190℃, 2.16kg), density of 0.923g/cm3 (23℃), Hanwha Petrochemical, product name: HS 1700) 40% by weight, average particle diameter of 1㎛ 45% by weight of calcium carbonate and additives After mixing 5% by weight of a lubricant (Ca-St) in a blender, it was dried so that the content was 1% or less.
이렇게 건조된 혼합물을 트윈익스트루더(twin Extruder, 75mm, L/D 48)에 230℃의 온도로 용융 혼련하였다. 이때 상기 용융혼련과정을 2회 반복하여 균일하게 혼합된 컴파운드조성물을 제조한 후, 티-다이를 통하여 압출하여 평량 40gsm인 필름을 제조하였다.The dried mixture was melt-kneaded in a twin extruder (75 mm, L/D 48) at a temperature of 230°C. At this time, the melt-kneading process was repeated twice to prepare a uniformly mixed compound composition, and then extruded through a T-die to prepare a film having a basis weight of 40 gsm.
이렇게 제조한 필름을 기계방향으로 2 배 연신하여 평량이 20gsm인 건식 통기성 필름을 제조하였다.The thus prepared film was stretched twice in the machine direction to prepare a dry air permeable film having a basis weight of 20 gsm.
제조된 필름은 두께가 17㎛, 투습도가 8862 g/㎡24hr, 인장강도가 MD방향 18 kgf/25mm, TD 방향 0.2 kgf/25mm, 신율이 MD방향 38 %, TD 방향 385 %이었다.The prepared film had a thickness of 17 μm, a moisture permeability of 8862 g/m 24 hr, a tensile strength of 18 kgf/25 mm in the MD direction, 0.2 kgf/25 mm in the TD direction, and an elongation of 38% in the MD direction and 385% in the TD direction.
[제조예 2] 습식 통기성 필름의 제조[Preparation Example 2] Preparation of wet breathable film
중량평균분자량이 380,000 g/mol인 폴리에틸렌 수지 100 중량부에 대하여, 중량평균분자량이 350,000 g/mol인 폴리프로필렌 10 중량부를 첨가하고, 기공형성 첨가제로써 평균 입자경이 200㎚인 PMMA(Poly(methylmethacrylate)) 나노입자 110 중량부와 평균 입자경이 500㎚인 PMMA 나노입자 83 중량부를 혼합하여 원료수지 혼합물을 제조하였다.To 100 parts by weight of a polyethylene resin having a weight average molecular weight of 380,000 g/mol, 10 parts by weight of polypropylene having a weight average molecular weight of 350,000 g/mol is added, and PMMA (Poly(methylmethacrylate)) having an average particle diameter of 200 nm as a pore-forming additive ) A raw material resin mixture was prepared by mixing 110 parts by weight of nanoparticles and 83 parts by weight of PMMA nanoparticles having an average particle diameter of 500 nm.
상기 원료수지 혼합물을 티다이(T-die)가 장착된 압출기 내에 투입하고, 220℃의 온도에서 이축 스크류의 회전속도를 500rpm으로 유지하면서 티다이를 통해 압출하여 두께가 1,500㎛인 겔상 시트를 제조한 다음, 상기 겔상 시트를 캐스팅롤과 닙롤 사이로 통과시키면서 냉각하였다.The raw resin mixture was put into an extruder equipped with a T-die, and extruded through the T-die while maintaining the rotation speed of the twin screw at 500 rpm at a temperature of 220 ° C. to prepare a gel-like sheet having a thickness of 1,500 μm. Then, the gel-like sheet was cooled while passing it between the casting roll and the nip roll.
이어 이축 연신기를 사용하여 상기 시트를 120℃ 온도에서 MD방향으로 8배, TD 방향으로 6배 연신한 후, 연신된 시트를 테트라하이드로퓨란(Tetrahydrofuran) 용액에 침적하여 상기 기공형성 첨가제를 추출, 제거하였다. 연신된 시트를 프레임에 고정하여 130 ℃ 오븐 속에서 4분동안 열고정하여 평량이 8 gsm인 습식 통기성필름을 제조하였다. 기공형성 첨가제가 제거되면서 일정간격으로 균일한 크기의 바이모달 기공이 형성된 것을 확인하였다.Then, the sheet was stretched 8 times in the MD direction and 6 times in the TD direction at a temperature of 120° C. using a biaxial stretching machine, and then the stretched sheet was immersed in a tetrahydrofuran solution to extract and remove the pore-forming additive. did The stretched sheet was fixed to a frame and heat-set in an oven at 130° C. for 4 minutes to prepare a wet breathable film having a basis weight of 8 gsm. As the pore-forming additive was removed, it was confirmed that bimodal pores of uniform size were formed at regular intervals.
제조된 필름은 두께가 11 ㎛, 투습도가 10967 g/㎡24hr, 인장강도가 MD방향 5.5 kgf/25mm, TD 방향 5.5 kgf/25mm, 신율이 MD방향 53 %, TD 방향 50 %이었다.The prepared film had a thickness of 11 μm, a moisture permeability of 10967 g/m 24 hr, a tensile strength of 5.5 kgf/25mm in the MD direction, 5.5 kgf/25mm in the TD direction, and an elongation of 53% in the MD direction and 50% in the TD direction.
[제조예 3][Production Example 3]
상기 실시예 1과 동일한 원료를 사용하여, 블로운 캐스팅 방법으로 2배 연신하여 필름을 제조하였다. 제조된 필름은 평량이 18 gsm, 두께가 17㎛, 투습도가 8620 g/㎡24hr, 인장강도가 MD방향 15 kgf/25mm, TD 방향 15 kgf/25mm, 신율이 MD방향 40 %, TD 방향 41 %이었다. 또한, 제조예 1에서 제조된 필름에 비하여 핀홀의 발생이 적은 것을 확인하였다.Using the same raw material as in Example 1, the film was prepared by stretching twice by the blow casting method. The manufactured film had a basis weight of 18 gsm, a thickness of 17㎛, a moisture permeability of 8620 g/m224hr, a tensile strength of 15 kgf/25mm in the MD direction, 15 kgf/25mm in the TD direction, and an elongation of 40% in the MD direction, 41% in the TD direction. it was In addition, it was confirmed that the occurrence of pinholes was less than that of the film prepared in Preparation Example 1.
[실시예 1] 건식 통기성 필름/건식 통기성필름/부직포층 삼중 구조 제조방법 [Example 1] Dry air permeable film / dry air permeable film / non-woven fabric layer triple structure manufacturing method
상기 제조예 1에서 제조한 건식 폴리올레핀계 통기성필름 2장을 투습성 폴리우레탄 접착제(제조사 : 삼호화성 , 제품명 : SUA-3180)를 이용하여 드라이라미네이팅 장치를 이용하여 합지하여 통기성 적층체를 제조하였다.The two dry polyolefin-based breathable films prepared in Preparation Example 1 were laminated using a dry laminating device using a moisture-permeable polyurethane adhesive (manufacturer: Samhohwaseong, product name: SUA-3180) to prepare a breathable laminate.
또한, 상기 건식 폴리올레핀계 통기성 필름의 일면에 스펀본드 부직포(수지:폴리프로필렌(PP), 평량:30gsm, 두께:156㎛, 인장강도:MD방향 6.801 kgf/50mm, TD 방향 4.214 kgf/50mm, 신율:MD방향 120 %, TD 방향 146 %)를 투습성 폴리우레탄 접착제(제조사 : 삼호화성, 제품명 : SUA-3180)를 이용하여 드라이라미네이팅 장치를 이용하여 합지하여 보호복원단을 제조하였다.In addition, spunbond nonwoven fabric (resin: polypropylene (PP), basis weight: 30 gsm, thickness: 156 μm, tensile strength: 6.801 kgf/50 mm in MD direction, 4.214 kgf/50 mm in TD direction, elongation on one side of the dry polyolefin-based breathable film : MD direction 120%, TD direction 146%) was laminated using a dry laminating device using a moisture-permeable polyurethane adhesive (manufacturer: Samho Hwaseong, product name: SUA-3180) to prepare a protective fabric.
이렇게 제조한 3중 구조를 갖는 합지 원단에 대한 물성을 측정하여 표 1에 나타내었다.The physical properties of the laminated fabric having a triple structure prepared in this way were measured and shown in Table 1.
[실시예 2] 건식 통기성 필름/습식 통기성필름/부직포층 삼중 구조 제조방법 [Example 2] Dry breathable film/wet breathable film/non-woven fabric layer triple structure manufacturing method
상기 제조예 1에서 제조한 건식 폴리올레핀계 통기성필름과 상기 제조예 2에서 제조한 습식 폴리올레핀계 통기성필름을 투습성 폴리우레탄 접착제(제조사 : 삼호화성, 제품명 : SUA-3180)를 이용하여 드라이라미네이팅 장치를 이용하여 합지하여 통기성 적층체를 제조하였다.The dry polyolefin-based air-permeable film prepared in Preparation Example 1 and the wet polyolefin-based air-permeable film prepared in Preparation Example 2 were subjected to a dry laminating device using a moisture-permeable polyurethane adhesive (manufacturer: Samseonghwaseong, product name: SUA-3180). and laminated to prepare a breathable laminate.
또한, 상기 습식 폴리올레핀계 통기성 필름의 일면에 스펀본드 부직포(수지: 폴리프로필렌(PP), 평량:20gsm, 두께:108㎛, 인장강도:MD방향 4.284 kgf/50mm, TD 방향 2.884 kgf/50mm, 신율: MD방향 76 %, TD 방향 72 %)를 투습성 폴리우레탄 접착제(제조사 : 삼호화성, 제품명 : SUA-3180)를 이용하여 드라이라미네이팅 장치를 이용하여 합지하여 보호복원단을 제조하였다.In addition, spunbond nonwoven fabric (resin: polypropylene (PP), basis weight: 20 gsm, thickness: 108 μm, tensile strength: 4.284 kgf/50mm in MD direction, 2.884 kgf/50mm in TD direction, elongation on one side of the wet polyolefin-based breathable film : MD direction 76%, TD direction 72%) was laminated using a dry laminating device using a moisture-permeable polyurethane adhesive (manufacturer: Samho Hwaseong, product name: SUA-3180) to prepare a protective restoration fabric.
이렇게 제조한 3중 구조를 갖는 합지 원단에 대한 물성을 측정하여 표 1에 나타내었다.The physical properties of the laminated fabric having a triple structure prepared in this way were measured and shown in Table 1.
[실시예 3] 건식 통기성 필름/건식 통기성필름/부직포층 삼중 구조 제조방법 [Example 3] Dry air permeable film / dry air permeable film / non-woven fabric layer triple structure manufacturing method
상기 제조예 3에서 제조한 건식 폴리올레핀계 통기성필름 2장을 투습성 폴리우레탄 접착제(제조사 : 삼호화성 , 제품명 : SUA-3180)를 이용하여 드라이라미네이팅 장치를 이용하여 합지하여 통기성 적층체를 제조하였다.The two dry polyolefin-based breathable films prepared in Preparation Example 3 were laminated using a dry laminating device using a moisture-permeable polyurethane adhesive (manufacturer: Samhohwaseong, product name: SUA-3180) to prepare a breathable laminate.
또한, 상기 건식 폴리올레핀계 통기성 필름의 일면에 스펀본드 부직포(수지:폴리프로필렌(PP), 평량:30gsm, 두께:156㎛, 인장강도:MD방향 6.801 kgf/50mm, TD 방향 4.214 kgf/50mm, 신율:MD방향 120 %, TD 방향 146 %)를 투습성 폴리우레탄 접착제(제조사 : 삼호화성, 제품명 : SUA-3180)를 이용하여 드라이라미네이팅 장치를 이용하여 합지하여 보호복원단을 제조하였다.In addition, spunbond nonwoven fabric (resin: polypropylene (PP), basis weight: 30 gsm, thickness: 156 μm, tensile strength: 6.801 kgf/50 mm in MD direction, 4.214 kgf/50 mm in TD direction, elongation on one side of the dry polyolefin-based breathable film : MD direction 120%, TD direction 146%) was laminated using a dry laminating device using a moisture-permeable polyurethane adhesive (manufacturer: Samho Hwaseong, product name: SUA-3180) to prepare a protective fabric.
이렇게 제조한 3중 구조를 갖는 합지 원단에 대한 물성을 측정하여 표 1에 나타내었다.The physical properties of the laminated fabric having a triple structure prepared in this way were measured and shown in Table 1.
[실시예 4] 건식 통기성 필름/습식 통기성 필름/건식 통기성필름 삼중 구조 제조방법 [Example 4] Dry breathable film/wet breathable film/dry breathable film triple structure manufacturing method
상기 제조예 2에서 제조한 습식 폴리올레핀계 통기성필름의 양면에, 투습성 폴리우레탄 접착제(제조사 : 삼호화성, 제품명 : SUA-3180)를 이용하여 상기 제조예 1에서 제조한 건식 폴리올레핀계 통기성필름을 합지하여 통기성 적층체를 제조하였다. On both sides of the wet polyolefin-based air-permeable film prepared in Preparation Example 2, the dry polyolefin-based air-permeable film prepared in Preparation Example 1 was laminated using a moisture-permeable polyurethane adhesive (manufacturer: Samseonghwaseong, product name: SUA-3180). A breathable laminate was prepared.
이렇게 제조한 3중 구조를 갖는 합지 원단에 대한 물성을 측정하여 표 1에 나타내었다.The physical properties of the laminated fabric having a triple structure prepared in this way were measured and shown in Table 1.
[비교예 1] 건식 통기성 필름/부직포층 이중 구조 제조방법 [Comparative Example 1] Dry-breathable film/non-woven fabric layer dual structure manufacturing method
상기 제조예 1에서 제조한 건식 폴리올레핀계 통기성필름과 스펀본드 부직포(수지:폴리프로필렌(PP), 평량:30gsm, 두께:173㎛, 인장강도:MD방향 6.684 kgf/50mm, TD 방향 4.231 kgf/50mm, 신율:MD방향 105 %, TD 방향 127 %)를 투습성 폴리우레탄 접착제(제조사 : 삼호화성, 제품명 : SUA-3180)로 접착하여 합지필름을 제조하였다.The dry polyolefin-based breathable film and spunbond nonwoven fabric prepared in Preparation Example 1 (resin: polypropylene (PP), basis weight: 30 gsm, thickness: 173 μm, tensile strength: 6.684 kgf/50mm in MD direction, 4.231 kgf/50mm in TD direction , elongation: 105% in the MD direction, 127% in the TD direction) was adhered with a moisture-permeable polyurethane adhesive (manufacturer: Samho Hwaseong, product name: SUA-3180) to prepare a laminated film.
[비교예 2] 습식 통기성 필름/부직포층 이중 구조 제조방법 [Comparative Example 2] Wet breathable film/non-woven fabric layer dual structure manufacturing method
상기 제조예 2에서 제조한 건식 폴리올레핀계 통기성필름과 스펀본드 부직포(수지:폴리프로필렌(PP), 평량:30gsm, 두께:173㎛, 인장강도:MD방향 6.684 kgf/50mm, TD 방향 4.231 kgf/50mm, 신율:MD방향 105 %, TD 방향 127 %)를 투습성 폴리우레탄 접착제(제조사 : 삼호화성, 제품명 : SUA-3180)로 접착하여 합지필름을 제조하였다.The dry polyolefin-based breathable film and spunbond nonwoven fabric prepared in Preparation Example 2 (resin: polypropylene (PP), basis weight: 30 gsm, thickness: 173 μm, tensile strength: 6.684 kgf/50mm in MD direction, 4.231 kgf/50mm in TD direction , elongation: 105% in the MD direction, 127% in the TD direction) was adhered with a moisture-permeable polyurethane adhesive (manufacturer: Samho Hwaseong, product name: SUA-3180) to prepare a laminated film.
평가 결과Evaluation results 실시예1Example 1 실시예2Example 2 실시예3Example 3 실시예4Example 4 비교예1Comparative Example 1 비교예2Comparative Example 2
인장강도(MD/TD)
(N/50mm)Tensile strength (MD/TD)
(N/50mm) 		116/49116/49 159/142159/142 125/118125/118 162/142162/142 87/4487/44 72/7172/71
신율(MD/TD)
(%)Elongation (MD/TD)
(%) 		50/12450/124 46/4246/42 50/5250/52 34/4234/42 52/13252/132 51/5551/55
투습도(g/m 2·24hrs)Water vapor permeability (g/m 2 ·24hrs) 46364636 76087608 53805380 58005800 890890 82038203
내수압 (mbar)Water pressure (mbar) 310310 500500 400400 500500 292292 600600
바이러스
차단성virus
barrier 		Class 6Class 6 Class 6Class 6 Class 6Class 6 Class 6Class 6 failfail failfail
이상과 같이 본 발명에서는 특정된 사항들과 한정된 실시예 및 도면에 의해 설명되었으나 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. As described above, the present invention has been described with reference to specific matters and limited examples and drawings, but these are only provided to help a more general understanding of the present invention, and the present invention is not limited to the above embodiments, and the present invention is not limited to the above embodiments. Various modifications and variations are possible from these descriptions by those of ordinary skill in the art.
따라서, 본 발명의 사상은 설명된 실시예에 국한되어 정해져서는 아니되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등하거나 등가적 변형이 있는 모든 것들은 본 발명 사상의 범주에 속한다고 할 것이다.Therefore, the spirit of the present invention should not be limited to the described embodiments, and not only the claims to be described later, but also all those with equivalent or equivalent modifications to the claims will be said to belong to the scope of the spirit of the present invention. .

Claims (22)

  1. 적어도 둘 이상의 통기성 필름이 적층된 통기성 적층체 및 상기 통기성 적층체의 적어도 일면에 부직포가 적층되며,A nonwoven fabric is laminated on at least one surface of a breathable laminate in which at least two or more breathable films are laminated and the breathable laminate,
    상기 통기성 필름은 투습성 폴리우레탄 접착제를 이용하여 라미네이트 되고,The breathable film is laminated using a moisture-permeable polyurethane adhesive,
    상기 통기성 적층체와 부직포는 투습성 폴리우레탄 접착제 또는 가열 압착하여 라미네이트 되며,The breathable laminate and the nonwoven fabric are laminated by heat-pressing or moisture-permeable polyurethane adhesive,
    JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 이상인 바이러스 차단성능이 우수한 보호복원단.A protective restoration group with excellent virus blocking performance of class 3 or higher in virus barrier according to JIS T 8061:2015.
  2. 제 1항에 있어서,The method of claim 1,
    상기 부직포는 폴리올레핀계 부직포인 바이러스 차단성능이 우수한 보호복원단.The non-woven fabric is a polyolefin-based non-woven fabric, a protective recovery fabric with excellent virus blocking performance.
  3. 제 1항에 있어서,The method of claim 1,
    상기 통기성 적층체는 폴리올레핀계 수지에 무기입자를 혼합하여 연신한 건식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층되거나, 또는The air-permeable laminate is a dry polyolefin-based air-permeable film stretched by mixing inorganic particles in a polyolefin-based resin is laminated, or
    폴리올레핀계 수지에 무기입자를 혼합하여 압출 및 연신한 건식 폴리올레핀계 통기성 필름과, 폴리올레핀계 수지에 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거한 습식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층된 것인 바이러스 차단성능이 우수한 보호복원단.At least a dry polyolefin-based air-permeable film obtained by extruding and stretching a polyolefin-based resin mixed with inorganic particles, and a wet polyolefin-based air-permeable film removed by extracting the pore-forming additive after extruding and stretching by mixing a pore-forming additive with a polyolefin-based resin Two or more layered protective restorations with excellent virus blocking performance.
  4. 제 3항에 있어서,4. The method of claim 3,
    상기 기공형성 첨가제는 평균입경이 100 내지 1000 nm인 유기 나노입자이며, 상기 유기 나노입자에 의해 상기 습식 폴리올레핀계 통기성 필름에 나노사이즈의 균일 기공이 형성된 것인 바이러스 차단성능이 우수한 보호복원단.The pore-forming additive is an organic nanoparticle having an average particle diameter of 100 to 1000 nm, and nano-sized uniform pores are formed in the wet polyolefin-based breathable film by the organic nanoparticles.
  5. 제 4항에 있어서,5. The method of claim 4,
    상기 기공형성 첨가제는 평균입경이 서로 상이한 2종의 폴리메틸메타크릴레이트 나노입자를 혼합한 것이며, 상기 습식 폴리올레핀계 통기성 필름은 바이모달 입자분포의 균일 기공을 갖는 것인 바이러스 차단성능이 우수한 보호복원단.The pore-forming additive is a mixture of two types of polymethyl methacrylate nanoparticles having different average particle diameters, and the wet polyolefin-based breathable film has uniform pores of a bimodal particle distribution. only.
  6. 제 5항에 있어서,6. The method of claim 5,
    상기 기공형성 첨가제는 평균입경이 100 내지 400 nm인 제1폴리메틸메타크릴레이트 나노입자와, 평균입경이 400 내지 1000 nm인 제2폴리메틸메타크릴레이트 나노입자를 혼합하여 사용한 것인 바이러스 차단성능이 우수한 보호복원단.The pore-forming additive is a virus blocking performance that uses a mixture of first polymethyl methacrylate nanoparticles having an average particle diameter of 100 to 400 nm and second polymethyl methacrylate nanoparticles having an average particle diameter of 400 to 1000 nm This excellent protective restoration team.
  7. 제 3항에 있어서,4. The method of claim 3,
    상기 건식 폴리올레핀계 통기성 필름은 블로운 캐스팅 방법으로 제조된 것인 바이러스 차단성능이 우수한 보호복원단.The dry polyolefin-based breathable film is a protective recovery fabric with excellent virus blocking performance that is manufactured by a blow casting method.
  8. 제 3항에 있어서,4. The method of claim 3,
    상기 보호복원단은 건식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층된 통기성 적층체의 일면 또는 양면에 부직포가 적층된 것인 바이러스 차단성능이 우수한 보호복원단.The protective recovery group is a protective recovery group with excellent virus blocking performance in which a nonwoven fabric is laminated on one or both sides of a breathable laminate in which at least two dry polyolefin-based breathable films are laminated.
  9. 제 3항에 있어서,4. The method of claim 3,
    상기 보호복원단은 건식 폴리올레핀계 통기성 필름과 습식 폴리올레핀계 통기성 필름이 적층된 통기성 적층체와, 상기 통기성 적층체의 습식 폴리올레핀계 통기성 필름 상에 부직포가 적층된 것인 바이러스 차단성능이 우수한 보호복원단.The protective recovery group is a breathable laminate in which a dry polyolefin-based breathable film and a wet polyolefin-based breathable film are laminated, and a nonwoven fabric is laminated on the wet polyolefin-based breathable film of the breathable laminate. .
  10. 제 3항에 있어서,4. The method of claim 3,
    상기 보호복원단은 건식 폴리올레핀계 통기성 필름과 습식 폴리올레핀계 통기성 필름이 적층된 통기성 적층체와, 상기 통기성 적층체의 양면에 부직포가 적층된 것인 바이러스 차단성능이 우수한 보호복원단.The protective recovery group is a breathable laminate in which a dry polyolefin-based breathable film and a wet polyolefin-based breathable film are laminated, and a nonwoven fabric is laminated on both sides of the breathable laminate.
  11. 제 1항에 있어서,The method of claim 1,
    상기 보호복원단은 두께가 100 내지 300 ㎛이며, ASTM D5034에 따른 인장강도가 100 N/50mm 이상이고, 신율이 40 % 이상이고, ASTM E96에 따른 투습도가 3000 g/㎡ · 24hr 이상이고, AATCC 127에 따른 내수압이 300 mbar 이상인 바이러스 차단성능이 우수한 보호복원단.The protective restoration has a thickness of 100 to 300 μm, a tensile strength of 100 N/50 mm or more according to ASTM D5034, an elongation of 40% or more, and a moisture permeability of 3000 g/m 2 · 24hr or more according to ASTM E96, AATCC 127, a protective restoration with excellent anti-virus performance with a water pressure of 300 mbar or higher.
  12. a) 적어도 둘 이상의 통기성 필름을 투습성 폴리우레탄 접착제를 이용하여 라미네이트하여 통기성 적층체를 제조하는 단계;a) preparing a breathable laminate by laminating at least two or more breathable films using a moisture-permeable polyurethane adhesive;
    b) 상기 통기성 적층체의 적어도 일면에 투습성 폴리우레탄 접착제를 도포한 후 부직포를 라미네이트하거나 또는 상기 통기성 적층체와 부직포를 가열 압착하여 라미네이트하는 단계;b) applying a moisture-permeable polyurethane adhesive to at least one surface of the air-permeable laminate and then laminating a nonwoven fabric or laminating the air-permeable laminate and the nonwoven fabric by thermal compression;
    를 포함하며, JIS T 8061:2015에 따른 바이러스 배리어성이 클래스 3 이상인 바이러스 차단성능이 우수한 보호복원단의 제조방법.Including, a method of manufacturing a protective restoration group having excellent virus blocking performance according to JIS T 8061:2015 with a virus barrier property of class 3 or higher.
  13. 제 12항에 있어서,13. The method of claim 12,
    상기 통기성 적층체는 폴리올레핀계 수지에 무기입자를 혼합하여 연신한 건식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층되거나, 또는The air-permeable laminate is a dry polyolefin-based air-permeable film stretched by mixing inorganic particles in a polyolefin-based resin is laminated, or
    폴리올레핀계 수지에 무기입자를 혼합하여 압출 및 연신한 건식 폴리올레핀계 통기성 필름과, 폴리올레핀계 수지에 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거한 습식 폴리올레핀계 통기성 필름이 적어도 둘 이상 적층된 것인 바이러스 차단성능이 우수한 보호복원단의 제조방법.At least a dry polyolefin-based air-permeable film obtained by extruding and stretching a polyolefin-based resin mixed with inorganic particles, and a wet polyolefin-based air-permeable film removed by extracting the pore-forming additive after extruding and stretching by mixing a pore-forming additive with a polyolefin-based resin A method of manufacturing a protective fabric with excellent virus blocking performance, which is a layered product of two or more.
  14. 제 13항에 있어서,14. The method of claim 13,
    상기 습식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 기공형성 첨가제로 평균입경이 100 내지 1000 nm인 유기 나노입자를 혼합하여 압출 및 연신한 후, 상기 유기 나노입자를 용해할 수 있으며 상기 폴리올레핀계 수지를 용해하지 않는 용매를 이용하여 상기 유기 나노입자를 추출하여 제거함으로써 나노사이즈의 균일 기공이 형성된 것인 바이러스 차단성능이 우수한 보호복원단의 제조방법.The wet polyolefin-based breathable film is extruded and stretched by mixing organic nanoparticles having an average particle diameter of 100 to 1000 nm as a pore-forming additive in a polyolefin-based resin, and then dissolving the organic nanoparticles and dissolving the polyolefin-based resin A method of manufacturing a protective recovery fabric with excellent virus blocking performance in which uniform nano-sized pores are formed by extracting and removing the organic nanoparticles using a solvent that is not used.
  15. 제 14항에 있어서,15. The method of claim 14,
    상기 유기 나노입자는 평균입경이 서로 상이한 2종의 폴리메틸메타크릴레이트 나노입자를 혼합한 것이며, 상기 습식 폴리올레핀계 통기성 필름은 바이모달 입자분포의 균일 기공을 갖는 것인 바이러스 차단성능이 우수한 보호복원단의 제조방법.The organic nanoparticles are a mixture of two types of polymethyl methacrylate nanoparticles having different average particle diameters, and the wet polyolefin-based breathable film has uniform pores of a bimodal particle distribution. A method of manufacturing a dandelion.
  16. 제 15항에 있어서,16. The method of claim 15,
    상기 유기 나노입자는 평균입경이 100 내지 400 nm인 제1폴리메틸메타크릴레이트 나노입자와, 평균입경이 400 내지 1000 nm인 제2폴리메틸메타크릴레이트 나노입자를 혼합하여 사용한 것인 바이러스 차단성능이 우수한 보호복원단의 제조방법.The organic nanoparticles are the first polymethyl methacrylate nanoparticles having an average particle diameter of 100 to 400 nm and the second polymethyl methacrylate nanoparticles having an average particle diameter of 400 to 1000 nm. Virus blocking performance The manufacturing method of this excellent protective clothing.
  17. 제 14항에 있어서,15. The method of claim 14,
    상기 기공형성 첨가제는 폴리올레핀계 수지 100 중량부에 대하여, 50 내지 300 중량부를 사용하는 것인 바이러스 차단성능이 우수한 보호복원단의 제조방법.The pore-forming additive is 50 to 300 parts by weight based on 100 parts by weight of the polyolefin-based resin.
  18. 제 13항에 있어서,14. The method of claim 13,
    상기 무기입자는 평균입경이 0.5 내지 10 ㎛인 탄산칼슘, 탈크, 클레이, 카올린, 실리카 및 규조토에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 바이러스 차단성능이 우수한 보호복원단의 제조방법.The inorganic particles are any one or a mixture of two or more selected from calcium carbonate, talc, clay, kaolin, silica and diatomaceous earth having an average particle diameter of 0.5 to 10 μm.
  19. 제 13항에 있어서,14. The method of claim 13,
    상기 건식 폴리올레핀계 통기성 필름은 블로운 캐스팅 방법으로 제조된 것인 바이러스 차단성능이 우수한 보호복원단의 제조방법.The dry polyolefin-based breathable film is a method of manufacturing a protective fabric having excellent virus blocking performance that is manufactured by a blow casting method.
  20. 제 12항에 있어서,13. The method of claim 12,
    상기 보호복원단은 두께가 100 내지 300 ㎛이며, ASTM D5034에 따른 인장강도가 100 N/50mm 이상이고, 신율이 40 % 이상이고, ASTM E96에 따른 투습도가 3000 g/㎡ · 24hr 이상이고, AATCC 127에 따른 내수압이 300 mbar 이상인 바이러스 차단성능이 우수한 보호복원단의 제조방법. The protective restoration has a thickness of 100 to 300 μm, a tensile strength of 100 N/50 mm or more according to ASTM D5034, an elongation of 40% or more, and a moisture permeability of 3000 g/m 2 · 24hr or more according to ASTM E96, AATCC According to 127, a method for manufacturing a protective fabric with excellent virus blocking performance with a water pressure of 300 mbar or more.
  21. 습식 폴리올레핀계 통기성 필름의 양면에 투습성 폴리우레탄 접착제를 이용하여 건식 폴리올레핀계 통기성 필름을 적층한 바이러스 차단성능이 우수한 보호복원단으로서,As a protective restoration material with excellent virus blocking performance, a dry polyolefin-based breathable film is laminated on both sides of a wet polyolefin-based breathable film using a moisture-permeable polyurethane adhesive,
    상기 습식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 평균입경이 100 내지 1000 nm인 유기 나노입자인 기공형성 첨가제를 혼합하여 압출 및 연신한 후 상기 기공형성 첨가제를 추출하여 제거한 것이고, The wet polyolefin-based breathable film is a polyolefin-based resin mixed with an organic nanoparticle pore-forming additive having an average particle diameter of 100 to 1000 nm, extruded and stretched, and then the pore-forming additive is extracted and removed,
    상기 건식 폴리올레핀계 통기성 필름은 폴리올레핀계 수지에 평균입경이 0.5 내지 10 ㎛인 무기입자를 혼합하여 압출 및 연신하여 제조된 것인 바이러스 차단성능이 우수한 보호복원단.The dry polyolefin-based breathable film is a protective recovery fabric with excellent virus blocking performance that is manufactured by mixing inorganic particles having an average particle diameter of 0.5 to 10 μm with a polyolefin-based resin, extruding and stretching.
  22. 제 21항에 있어서,22. The method of claim 21,
    상기 무기입자는 탄산칼슘, 탈크, 클레이, 카올린, 실리카 및 규조토에서 선택되는 어느 하나 또는 둘 이상의 혼합물이고,The inorganic particles are any one or a mixture of two or more selected from calcium carbonate, talc, clay, kaolin, silica and diatomaceous earth,
    상기 유기 나노입자는 평균입경이 100 내지 400 nm인 제1폴리메틸메타크릴레이트 나노입자와, 평균입경이 400 내지 1000 nm인 제2폴리메틸메타크릴레이트 나노입자를 혼합하여 사용한 것인 바이러스 차단성능이 우수한 보호복원단.The organic nanoparticles are the first polymethyl methacrylate nanoparticles having an average particle diameter of 100 to 400 nm and the second polymethyl methacrylate nanoparticles having an average particle diameter of 400 to 1000 nm. Virus blocking performance This excellent protective restoration team.
PCT/KR2021/002447 2020-06-17 2021-02-26 Protective clothing material having excellent virus-blocking performance and production method thereof WO2021256660A1 (en)