WO2021234540A1 - Article abrasif composite et son procédé de fabrication et d'utilisation - Google Patents

Article abrasif composite et son procédé de fabrication et d'utilisation Download PDF

Info

Publication number
WO2021234540A1
WO2021234540A1 PCT/IB2021/054217 IB2021054217W WO2021234540A1 WO 2021234540 A1 WO2021234540 A1 WO 2021234540A1 IB 2021054217 W IB2021054217 W IB 2021054217W WO 2021234540 A1 WO2021234540 A1 WO 2021234540A1
Authority
WO
WIPO (PCT)
Prior art keywords
abrasive
composite
abrasive article
coated abrasive
coated
Prior art date
Application number
PCT/IB2021/054217
Other languages
English (en)
Inventor
John A. Worrell
Schoen A. Schuknecht
Michael A. ANNEN
Original Assignee
3M Innovative Properties Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Company filed Critical 3M Innovative Properties Company
Priority to US17/998,939 priority Critical patent/US20230226664A1/en
Priority to EP21727568.4A priority patent/EP4153380A1/fr
Publication of WO2021234540A1 publication Critical patent/WO2021234540A1/fr

Abstract

Un article abrasif composite comprend un élément de support à mailles ouvertes ayant des première et seconde surfaces principales et des éléments abrasifs revêtus fixés à la première surface principale. Indépendamment, chaque élément abrasif revêtu comprend respectivement une couche abrasive comprenant des particules abrasives fixées à un support abrasif revêtu par au moins un matériau liant. L'invention concerne également un procédé de fabrication d'un article abrasif composite.
PCT/IB2021/054217 2020-05-20 2021-05-17 Article abrasif composite et son procédé de fabrication et d'utilisation WO2021234540A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US17/998,939 US20230226664A1 (en) 2020-05-20 2021-05-17 Composite abrasive article, and method of making and using the same
EP21727568.4A EP4153380A1 (fr) 2020-05-20 2021-05-17 Article abrasif composite et son procédé de fabrication et d'utilisation

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202063027687P 2020-05-20 2020-05-20
US63/027,687 2020-05-20

Publications (1)

Publication Number Publication Date
WO2021234540A1 true WO2021234540A1 (fr) 2021-11-25

Family

ID=76076384

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2021/054217 WO2021234540A1 (fr) 2020-05-20 2021-05-17 Article abrasif composite et son procédé de fabrication et d'utilisation

Country Status (3)

Country Link
US (1) US20230226664A1 (fr)
EP (1) EP4153380A1 (fr)
WO (1) WO2021234540A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11427740B2 (en) 2017-01-31 2022-08-30 Saint-Gobain Ceramics & Plastics, Inc. Method of making shaped abrasive particles and articles comprising forming a flange from overfilling
US11453811B2 (en) 2011-12-30 2022-09-27 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle and method of forming same
US11472989B2 (en) 2015-03-31 2022-10-18 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US11590632B2 (en) 2013-03-29 2023-02-28 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US11608459B2 (en) 2014-12-23 2023-03-21 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US11643582B2 (en) 2015-03-31 2023-05-09 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US11649388B2 (en) 2012-01-10 2023-05-16 Saint-Gobain Cermaics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US11718774B2 (en) 2016-05-10 2023-08-08 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same
US11879087B2 (en) 2015-06-11 2024-01-23 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11891559B2 (en) 2014-04-14 2024-02-06 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11926781B2 (en) 2014-01-31 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle including dopant material and method of forming same
US11926019B2 (en) 2019-12-27 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles and methods of forming same
US11959009B2 (en) 2016-05-10 2024-04-16 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same

Citations (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4734104A (en) 1984-05-09 1988-03-29 Minnesota Mining And Manufacturing Company Coated abrasive product incorporating selective mineral substitution
US4737163A (en) 1984-05-09 1988-04-12 Minnesota Mining And Manufacturing Company Coated abrasive product incorporating selective mineral substitution
US4751138A (en) 1986-08-11 1988-06-14 Minnesota Mining And Manufacturing Company Coated abrasive having radiation curable binder
US5058247A (en) 1989-01-31 1991-10-22 The Procter & Gamble Company Mechanical fastening prong
US5152917A (en) 1991-02-06 1992-10-06 Minnesota Mining And Manufacturing Company Structured abrasive article
US5203884A (en) 1992-06-04 1993-04-20 Minnesota Mining And Manufacturing Company Abrasive article having vanadium oxide incorporated therein
US5378251A (en) 1991-02-06 1995-01-03 Minnesota Mining And Manufacturing Company Abrasive articles and methods of making and using same
US5417726A (en) 1991-12-20 1995-05-23 Minnesota Mining And Manufacturing Company Coated abrasive backing
US5436063A (en) 1993-04-15 1995-07-25 Minnesota Mining And Manufacturing Company Coated abrasive article incorporating an energy cured hot melt make coat
US5496386A (en) 1993-03-18 1996-03-05 Minnesota Mining And Manufacturing Company Coated abrasive article having diluent particles and shaped abrasive particles
US5520711A (en) 1993-04-19 1996-05-28 Minnesota Mining And Manufacturing Company Method of making a coated abrasive article comprising a grinding aid dispersed in a polymeric blend binder
US5556437A (en) 1990-11-14 1996-09-17 Minnesota Mining And Manufacturing Company Coated abrasive having an overcoating of an epoxy resin coatable from water
US5609706A (en) 1991-12-20 1997-03-11 Minnesota Mining And Manufacturing Company Method of preparation of a coated abrasive belt with an endless, seamless backing
US5766277A (en) 1996-09-20 1998-06-16 Minnesota Mining And Manufacturing Company Coated abrasive article and method of making same
US5954844A (en) 1996-05-08 1999-09-21 Minnesota Mining & Manufacturing Company Abrasive article comprising an antiloading component
US5961674A (en) 1995-10-20 1999-10-05 3M Innovative Properties Company Abrasive article containing an inorganic metal orthophosphate
US5975988A (en) 1994-09-30 1999-11-02 Minnesota Mining And Manfacturing Company Coated abrasive article, method for preparing the same, and method of using a coated abrasive article to abrade a hard workpiece
US6077601A (en) 1998-05-01 2000-06-20 3M Innovative Properties Company Coated abrasive article
US6228133B1 (en) 1998-05-01 2001-05-08 3M Innovative Properties Company Abrasive articles having abrasive layer bond system derived from solid, dry-coated binder precursor particles having a fusible, radiation curable component
US20120000135A1 (en) * 2010-07-02 2012-01-05 3M Innovative Properties Company Coated abrasive articles
US8142532B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with an opening
US8142531B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with a sloping sidewall
US8142891B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Dish-shaped abrasive particles with a recessed surface
US20120227333A1 (en) 2009-12-02 2012-09-13 Adefris Negus B Dual tapered shaped abrasive particles
US20130040537A1 (en) 2010-04-27 2013-02-14 Mark G. Schwabel Ceramic shaped abrasive particles, methods of making the same, and abrasive articles containing the same
US20130125477A1 (en) 2010-08-04 2013-05-23 3M Innovative Properties Company Intersecting plate shaped abrasive particles
KR20140143563A (ko) * 2013-06-07 2014-12-17 (주)인성다이아몬드 연마용 다이아몬드 페이퍼의 제조방법 및 그 다이아몬드 페이퍼

Patent Citations (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4737163A (en) 1984-05-09 1988-04-12 Minnesota Mining And Manufacturing Company Coated abrasive product incorporating selective mineral substitution
US4734104A (en) 1984-05-09 1988-03-29 Minnesota Mining And Manufacturing Company Coated abrasive product incorporating selective mineral substitution
US4751138A (en) 1986-08-11 1988-06-14 Minnesota Mining And Manufacturing Company Coated abrasive having radiation curable binder
US5058247A (en) 1989-01-31 1991-10-22 The Procter & Gamble Company Mechanical fastening prong
US5556437A (en) 1990-11-14 1996-09-17 Minnesota Mining And Manufacturing Company Coated abrasive having an overcoating of an epoxy resin coatable from water
US5152917A (en) 1991-02-06 1992-10-06 Minnesota Mining And Manufacturing Company Structured abrasive article
US5378251A (en) 1991-02-06 1995-01-03 Minnesota Mining And Manufacturing Company Abrasive articles and methods of making and using same
US5152917B1 (en) 1991-02-06 1998-01-13 Minnesota Mining & Mfg Structured abrasive article
US5609706A (en) 1991-12-20 1997-03-11 Minnesota Mining And Manufacturing Company Method of preparation of a coated abrasive belt with an endless, seamless backing
US5417726A (en) 1991-12-20 1995-05-23 Minnesota Mining And Manufacturing Company Coated abrasive backing
US5203884A (en) 1992-06-04 1993-04-20 Minnesota Mining And Manufacturing Company Abrasive article having vanadium oxide incorporated therein
US5496386A (en) 1993-03-18 1996-03-05 Minnesota Mining And Manufacturing Company Coated abrasive article having diluent particles and shaped abrasive particles
US5436063A (en) 1993-04-15 1995-07-25 Minnesota Mining And Manufacturing Company Coated abrasive article incorporating an energy cured hot melt make coat
US5520711A (en) 1993-04-19 1996-05-28 Minnesota Mining And Manufacturing Company Method of making a coated abrasive article comprising a grinding aid dispersed in a polymeric blend binder
US5975988A (en) 1994-09-30 1999-11-02 Minnesota Mining And Manfacturing Company Coated abrasive article, method for preparing the same, and method of using a coated abrasive article to abrade a hard workpiece
US5961674A (en) 1995-10-20 1999-10-05 3M Innovative Properties Company Abrasive article containing an inorganic metal orthophosphate
US5954844A (en) 1996-05-08 1999-09-21 Minnesota Mining & Manufacturing Company Abrasive article comprising an antiloading component
US5766277A (en) 1996-09-20 1998-06-16 Minnesota Mining And Manufacturing Company Coated abrasive article and method of making same
US6077601A (en) 1998-05-01 2000-06-20 3M Innovative Properties Company Coated abrasive article
US6228133B1 (en) 1998-05-01 2001-05-08 3M Innovative Properties Company Abrasive articles having abrasive layer bond system derived from solid, dry-coated binder precursor particles having a fusible, radiation curable component
US8142532B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with an opening
US8142531B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Shaped abrasive particles with a sloping sidewall
US8142891B2 (en) 2008-12-17 2012-03-27 3M Innovative Properties Company Dish-shaped abrasive particles with a recessed surface
US20120227333A1 (en) 2009-12-02 2012-09-13 Adefris Negus B Dual tapered shaped abrasive particles
US20130040537A1 (en) 2010-04-27 2013-02-14 Mark G. Schwabel Ceramic shaped abrasive particles, methods of making the same, and abrasive articles containing the same
US20120000135A1 (en) * 2010-07-02 2012-01-05 3M Innovative Properties Company Coated abrasive articles
US20130125477A1 (en) 2010-08-04 2013-05-23 3M Innovative Properties Company Intersecting plate shaped abrasive particles
KR20140143563A (ko) * 2013-06-07 2014-12-17 (주)인성다이아몬드 연마용 다이아몬드 페이퍼의 제조방법 및 그 다이아몬드 페이퍼

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11453811B2 (en) 2011-12-30 2022-09-27 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle and method of forming same
US11859120B2 (en) 2012-01-10 2024-01-02 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles having an elongated body comprising a twist along an axis of the body
US11649388B2 (en) 2012-01-10 2023-05-16 Saint-Gobain Cermaics & Plastics, Inc. Abrasive particles having complex shapes and methods of forming same
US11590632B2 (en) 2013-03-29 2023-02-28 Saint-Gobain Abrasives, Inc. Abrasive particles having particular shapes and methods of forming such particles
US11926781B2 (en) 2014-01-31 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particle including dopant material and method of forming same
US11891559B2 (en) 2014-04-14 2024-02-06 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11608459B2 (en) 2014-12-23 2023-03-21 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US11926780B2 (en) 2014-12-23 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same
US11643582B2 (en) 2015-03-31 2023-05-09 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US11472989B2 (en) 2015-03-31 2022-10-18 Saint-Gobain Abrasives, Inc. Fixed abrasive articles and methods of forming same
US11879087B2 (en) 2015-06-11 2024-01-23 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles
US11718774B2 (en) 2016-05-10 2023-08-08 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same
US11959009B2 (en) 2016-05-10 2024-04-16 Saint-Gobain Ceramics & Plastics, Inc. Abrasive particles and methods of forming same
US11549040B2 (en) 2017-01-31 2023-01-10 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles having a tooth portion on a surface
US11427740B2 (en) 2017-01-31 2022-08-30 Saint-Gobain Ceramics & Plastics, Inc. Method of making shaped abrasive particles and articles comprising forming a flange from overfilling
US11932802B2 (en) 2017-01-31 2024-03-19 Saint-Gobain Ceramics & Plastics, Inc. Abrasive article including shaped abrasive particles comprising a particular toothed body
US11926019B2 (en) 2019-12-27 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Abrasive articles and methods of forming same

Also Published As

Publication number Publication date
EP4153380A1 (fr) 2023-03-29
US20230226664A1 (en) 2023-07-20

Similar Documents

Publication Publication Date Title
US20230226664A1 (en) Composite abrasive article, and method of making and using the same
US7258705B2 (en) Abrasive article and methods of making same
EP1838497B1 (fr) Article abrasif et procedes de fabrication
US7252694B2 (en) Abrasive article and methods of making same
US11097398B2 (en) Abrasive article and method of making the same
US20070066186A1 (en) Flexible abrasive article and methods of making and using the same
CN108349070B (zh) 磨料制品及其制备方法
AU2006294911B2 (en) Conformable abrasive articles and methods of making and using the same
KR101464800B1 (ko) 코팅된 연마 라미네이트 디스크 및 그의 제조 방법
EP2598291A1 (fr) Manique abrasive hybride et procédé d'abrasion d'une surface
WO2020165683A1 (fr) Articles abrasifs et leurs procédés de fabrication et d'utilisation
WO2024069578A1 (fr) Composition de revêtement de supertaille, article abrasif et procédé de fabrication d'article abrasif
WO2021234494A1 (fr) Article abrasif revêtu poreux et son procédé de réalisation

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21727568

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2021727568

Country of ref document: EP

Effective date: 20221220