WO2021214108A1 - Vitrage à faible émissivité et procédé de production associé - Google Patents
Vitrage à faible émissivité et procédé de production associé Download PDFInfo
- Publication number
- WO2021214108A1 WO2021214108A1 PCT/EP2021/060326 EP2021060326W WO2021214108A1 WO 2021214108 A1 WO2021214108 A1 WO 2021214108A1 EP 2021060326 W EP2021060326 W EP 2021060326W WO 2021214108 A1 WO2021214108 A1 WO 2021214108A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- functional metal
- alloy
- glazing
- glass substrate
- Prior art date
Abstract
Le présent document décrit un vitrage sous la forme d'un verre à vitre qui comprend un substrat en verre transparent, et un revêtement, qui comprend, dans l'ordre à partir du substrat de verre transparent vers l'extérieur, une couche de germe et une couche d'alliage métallique d'Ag fonctionnelle. La couche d'alliage d'Ag métallique fonctionnelle comprend un alliage d'Ag constitué essentiellement d'Ag et d'Al Une teneur en Al est de 0,05-0,20 % at, de préférence de 0,08-0,14 % at ou de manière davantage préférée de 0,10 à 0,12 % at de l'alliage d'Ag, le reste étant de l'Ag, et la couche d'alliage métallique d'Ag fonctionnelle a une épaisseur de 5 à 20 nm, de préférence de 8 à 15 nm ou de manière davantage préférée de 8 à 12 nm. Le vitrage présente une transmittance directe solaire d'au moins 30 %, de préférence d'au moins 40 %, de manière davantage préférée d'au moins 50 % telle que déterminée selon la norme européenne EN 410.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP21721046.7A EP4139259A1 (fr) | 2020-04-21 | 2021-04-21 | Vitrage à faible émissivité et procédé de production associé |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SE2050462-7 | 2020-04-21 | ||
SE2050462 | 2020-04-21 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2021214108A1 true WO2021214108A1 (fr) | 2021-10-28 |
Family
ID=75660023
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2021/060326 WO2021214108A1 (fr) | 2020-04-21 | 2021-04-21 | Vitrage à faible émissivité et procédé de production associé |
Country Status (2)
Country | Link |
---|---|
EP (1) | EP4139259A1 (fr) |
WO (1) | WO2021214108A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2023275793A1 (fr) * | 2021-06-29 | 2023-01-05 | Agp America S.A. | Revêtement solaire amélioré, procédé de fabrication et stratifié en verre comprenant un tel revêtement |
WO2023066491A1 (fr) * | 2021-10-21 | 2023-04-27 | Mimsi Materials Ab | Vitrage à faible émissivité et procédés de production associés |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060255727A1 (en) | 2002-05-08 | 2006-11-16 | Han Nee | Silver alloy thin film reflector and transparent electrical conductor |
EP2804843A1 (fr) * | 2012-01-16 | 2014-11-26 | Saint-Gobain Glass France | Substrat muni d'un empilement a proprietes thermiques comportant quatre couches fonctionnelles metalliques |
EP3435385A1 (fr) * | 2016-03-23 | 2019-01-30 | Mitsubishi Materials Corporation | Film conducteur transparent stratifié, film de câblage stratifié, et procédé de fabrication d'un film de câblage stratifié |
WO2020083873A1 (fr) * | 2018-10-22 | 2020-04-30 | Mimsi Materials Ab | Vitrification et procédé destiné à sa production |
-
2021
- 2021-04-21 EP EP21721046.7A patent/EP4139259A1/fr active Pending
- 2021-04-21 WO PCT/EP2021/060326 patent/WO2021214108A1/fr unknown
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060255727A1 (en) | 2002-05-08 | 2006-11-16 | Han Nee | Silver alloy thin film reflector and transparent electrical conductor |
EP2804843A1 (fr) * | 2012-01-16 | 2014-11-26 | Saint-Gobain Glass France | Substrat muni d'un empilement a proprietes thermiques comportant quatre couches fonctionnelles metalliques |
EP3435385A1 (fr) * | 2016-03-23 | 2019-01-30 | Mitsubishi Materials Corporation | Film conducteur transparent stratifié, film de câblage stratifié, et procédé de fabrication d'un film de câblage stratifié |
WO2020083873A1 (fr) * | 2018-10-22 | 2020-04-30 | Mimsi Materials Ab | Vitrification et procédé destiné à sa production |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2023275793A1 (fr) * | 2021-06-29 | 2023-01-05 | Agp America S.A. | Revêtement solaire amélioré, procédé de fabrication et stratifié en verre comprenant un tel revêtement |
WO2023066491A1 (fr) * | 2021-10-21 | 2023-04-27 | Mimsi Materials Ab | Vitrage à faible émissivité et procédés de production associés |
Also Published As
Publication number | Publication date |
---|---|
EP4139259A1 (fr) | 2023-03-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP3870548B1 (fr) | Vitrification et procédé destiné à sa production | |
JP6113794B2 (ja) | 低放射コーティングを包含する被覆物品、被覆物品を包含する断熱ガラスユニット、及び/又はそれらの製造方法 | |
EP0331201B1 (fr) | Film amorphe à base d'oxyde et objet recouvert d'un tel film | |
EP0486475B1 (fr) | Film amorphe à base d'oxyde et objet recouvert d'un tel film | |
EP1430332B1 (fr) | Revetements optiques et procedes associes | |
WO2014191472A2 (fr) | Vitrage à faible émissivité | |
KR20180048917A (ko) | 강화된 태양광 제어 성능을 갖는 태양광 제어 코팅 | |
US20230202913A1 (en) | Solar control glazing and method of its production | |
WO2021214108A1 (fr) | Vitrage à faible émissivité et procédé de production associé | |
US20230159382A1 (en) | Solar control glazing and method of its production | |
EP4139261A1 (fr) | Vitrage à faible émissitivé et procédé de production associé | |
US9296651B2 (en) | Heat stable SnAl and SnMg based dielectrics | |
US10604834B2 (en) | Titanium nickel niobium alloy barrier for low-emissivity coatings | |
WO2014165202A1 (fr) | Nouvelle conception pour améliorer la décoloration d'un revêtement basse émissivité à lsg élevé après traitement par la chaleur | |
AU2018253120B2 (en) | Solar control coating for laminated glazing | |
JP2018514499A (ja) | 低放射率コーティング用のチタンニッケルニオブ合金バリア |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21721046 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 2021721046 Country of ref document: EP Effective date: 20221121 |