WO2021205340A1 - Fibres et polymères thermoplastiques partiellement fluorés - Google Patents

Fibres et polymères thermoplastiques partiellement fluorés Download PDF

Info

Publication number
WO2021205340A1
WO2021205340A1 PCT/IB2021/052848 IB2021052848W WO2021205340A1 WO 2021205340 A1 WO2021205340 A1 WO 2021205340A1 IB 2021052848 W IB2021052848 W IB 2021052848W WO 2021205340 A1 WO2021205340 A1 WO 2021205340A1
Authority
WO
WIPO (PCT)
Prior art keywords
thv
polymer
fiber
mole percent
fluoroplastic
Prior art date
Application number
PCT/IB2021/052848
Other languages
English (en)
Inventor
Harald Kaspar
Thomas J. Blong
Karl D. WEILANDT
James E. Anderson
Michael R. Berrigan
Timothy J. Lindquist
Original Assignee
3M Innovative Properties Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Company filed Critical 3M Innovative Properties Company
Publication of WO2021205340A1 publication Critical patent/WO2021205340A1/fr

Abstract

L'invention concerne des polymères thermoplastiques partiellement fluorés comprenant du tétrafluoroéthylène, de l'hexafluoropropylène et du fluorure de vinylidène. Ces polymères fluoroplastiques à base de THV présentent à la fois une température de fusion élevée et un indice de fluidité élevé. L'invention concerne également des fibres, incluant des fibres cœur/gaine préparées à partir de tels polymères thermoplastiques partiellement fluorés.
PCT/IB2021/052848 2020-04-08 2021-04-06 Fibres et polymères thermoplastiques partiellement fluorés WO2021205340A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202063007165P 2020-04-08 2020-04-08
US63/007,165 2020-04-08

Publications (1)

Publication Number Publication Date
WO2021205340A1 true WO2021205340A1 (fr) 2021-10-14

Family

ID=75478120

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2021/052848 WO2021205340A1 (fr) 2020-04-08 2021-04-06 Fibres et polymères thermoplastiques partiellement fluorés

Country Status (1)

Country Link
WO (1) WO2021205340A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09302524A (ja) * 1996-05-10 1997-11-25 Teijin Ltd 撥水性ポリエステル繊維およびその製造方法
JP2002156533A (ja) * 2000-11-17 2002-05-31 Toray Ind Inc プラスチック光ファイバコード
WO2003057961A2 (fr) * 2002-01-03 2003-07-17 Pall Corporation Nontisses de fusion-soufflage hydrofuges et permeables a l'air et articles utilisant de tels materiaux
WO2009009361A2 (fr) * 2007-07-11 2009-01-15 3M Innovative Properties Company Procédés de traitement par fusion de fluoropolymères thermoplastiques
WO2014031252A1 (fr) 2012-08-21 2014-02-27 3M Innovative Properties Company Résines thermoplastiques semi-fluorées à faible teneur en gel

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09302524A (ja) * 1996-05-10 1997-11-25 Teijin Ltd 撥水性ポリエステル繊維およびその製造方法
JP2002156533A (ja) * 2000-11-17 2002-05-31 Toray Ind Inc プラスチック光ファイバコード
WO2003057961A2 (fr) * 2002-01-03 2003-07-17 Pall Corporation Nontisses de fusion-soufflage hydrofuges et permeables a l'air et articles utilisant de tels materiaux
WO2009009361A2 (fr) * 2007-07-11 2009-01-15 3M Innovative Properties Company Procédés de traitement par fusion de fluoropolymères thermoplastiques
EP2170990B1 (fr) 2007-07-11 2016-10-05 3M Innovative Properties Company Procédés de traitement par fusion de fluoropolymères thermoplastiques
WO2014031252A1 (fr) 2012-08-21 2014-02-27 3M Innovative Properties Company Résines thermoplastiques semi-fluorées à faible teneur en gel

Similar Documents

Publication Publication Date Title
US9688796B2 (en) High melting PTFE polymers for melt-processing
EP1963380B1 (fr) Dispersion fluoropolymère et procédé de préparation associé
CA2041559C (fr) Copolymeres de 1,1-difluoroethylene et d'hexafluoropropene; methode de preparation
US6927265B2 (en) Melt-processible thermoplastic fluoropolymers having improved processing characteristics and method of producing same
CN107207815B (zh) 偏二氟乙烯的多相双连续共聚物
EP1891153A2 (fr) Procede aqueux de fabrication de fluoropolymeres
US6586546B2 (en) Process for manufacture of a copolymer of tetrafluoroethylene and perfluoro (alkyl vinyl ether)
EP2928933A1 (fr) Polymères hautement fluorés
US6417279B2 (en) Thermoplastic fluorinated polymers
WO2014088804A1 (fr) Polymères partiellement fluorés
US20140005325A1 (en) High melting fluoropolymers
US7863384B2 (en) Fluoropolymers having improved whiteness
KR101385921B1 (ko) 신규의 불화 비닐리덴 공중합체 및 그 제조 방법
US5962610A (en) Ethylene fluoro-containing copolymers
WO2021205340A1 (fr) Fibres et polymères thermoplastiques partiellement fluorés
JP2012503677A (ja) エチレン／テトラフルオロエチレンコポリマーの応用

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21718227

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21718227

Country of ref document: EP

Kind code of ref document: A1