WO2021187785A1 - 투명 교정용 다중층 시트 - Google Patents

투명 교정용 다중층 시트 Download PDF

Info

Publication number
WO2021187785A1
WO2021187785A1 PCT/KR2021/002814 KR2021002814W WO2021187785A1 WO 2021187785 A1 WO2021187785 A1 WO 2021187785A1 KR 2021002814 W KR2021002814 W KR 2021002814W WO 2021187785 A1 WO2021187785 A1 WO 2021187785A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
outer layer
transparent
orthodontic
present
Prior art date
Application number
PCT/KR2021/002814
Other languages
English (en)
French (fr)
Inventor
권두연
임희정
장일석
송주동
Original Assignee
오스템임플란트 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 오스템임플란트 주식회사 filed Critical 오스템임플란트 주식회사
Publication of WO2021187785A1 publication Critical patent/WO2021187785A1/ko

Abstract

본 발명의 일 실시예는 연질 열가소성 고분자 소재로 이루어지는 제1 외부층, 연질 열가소성 고분자 소재로 이루어지는 제2 외부층 및 상기 제1 외부층과 상기 제2 외부층 사이에 구비되되, 경질 열가소성 고분자 소재로 이루어지는 중간층을 포함하는 투명 교정용 다중층 시트를 제공한다.

Description

투명 교정용 다중층 시트
본 발명은 투명 교정용 다중층 시트에 관한 것으로, 더욱 상세하게는 치열 교정시술 시 필요한 투명 교정용 소재로서 다중층으로 구성되어 교정 유지력을 높이고 환자의 고통을 경감시키며, 우수한 층간 접합력과 내구성을 갖도록 구성되어 교정 장치의 안정성 및 환자 착용 시 안전성을 높일 수 있는 투명 교정용 다중층 시트에 관한 것이다.
교정 치료는 불규칙한 치아 배열이나 상하악의 비정상적인 맞물림 상태 등을 치료하기 위하여 가해지는 치료 행위이다. 일반적으로 교정 치료를 위하여 브라켓과 와이어를 이용하여 치료가 행해지게 되는데, 치아에 교정력을 가하기 위하여 금속으로 제작된 브라켓과 와이어를 사용한다. 이러한 금속 브라켓과 와이어의 경우 심미적으로 좋지 않으며, 치아에 고정하여 치료가 진행되기 때문에 구강 내 청결에 더욱 신경을 써야 한다는 단점이 있다.
이러한 단점을 보안하기 위하여 최근 투명교정이라는 새로운 교정 치료 행위가 전세계적으로 많이 진행되고 있다. 이는 기존의 금속 재료가 아닌 고분자를 이용한 교정장치로서, 투명하여 심미적으로 우수한 장점을 가지고 있을 뿐만 아니라 탈부착이 가능해 구강 위생 관리에 어려움이 없다는 장점을 가지고 있다.
투명교정장치는 고분자 시트를 진공 열성형을 통해 환자의 구강에 알맞게 성형하여 치료에 사용된다. 종래의 대부분 고분자 시트는 Polyethylene terephthalate glycol(PETG)로 구성되어 있다. PETG를 비롯한 종래의 고분자 시트로 제작된 투명교정장치는 장치 착용 초기에 환자에게 가해지는 고통이 크며 시간에 따라 치아에 가해지는 교정력이 하락하는 특징을 가지고 있다. 이는 환자에게 불편감과 통증을 유발하며 초기와 다르게 낮은 교정력을 치아에 부여해 예측한 결과와 일치하지 않은 치아 이동 결과를 초래하게 된다.
이를 개선하기 위한 다중층 시트(Polyester-TPU)가 개발되었으나 열적 특성 차이로 인해 층간 접합력이 약한 단점이 있다. 이로 인해 교정용 제품 적용시 층간 박리현상이 발생하여 성능 저하를 유발하고 벗겨진 층은 환자의 구강에 존재하거나 소화기로 유입되어 환자의 안전에 영향을 미친다. 따라서 층간 접합력 향상을 통해 교정장치의 장기적 안정성, 환자 장치 착용 시 안전성이 증대된 소재가 필요하다.
또한 기존 다중층 시트는 강한 충격을 받을 시 중간층 고분자 소재의 백화현상을 동반한 영구변형이 발생하여 장치의 성능이 급격히 저하된다. 따라서 다중층 소재의 중간층 부분이 외력에 저항할 수 있는 높은 탄성 회복력을 갖도록 하여 장치의 내구성을 증가시키는 것이 필요하다.
선행기술문헌
미국 등록특허공보 제9655691 (2017.05.23)
본 발명은 전술한 종래기술의 문제점을 해결하기 위한 것으로, 본 발명의 목적은 치열 교정시술 시 필요한 투명 교정용 소재로서 다중층으로 구성되어 교정 유지력을 높이고 환자의 고통을 경감시키며, 우수한 층간 접합력과 내구성을 갖도록 구성되어 교정 장치의 안정성 및 환자 착용 시 안전성을 높일 수 있는 투명 교정용 다중층 시트를 제공하는 것이다.
상기와 같은 목적을 달성하기 위해, 본 발명의 일 측면은 연질 열가소성 고분자 소재로 이루어지는 제1 외부층, 연질 열가소성 고분자 소재로 이루어지는 제2 외부층 및 상기 제1 외부층과 상기 제2 외부층 사이에 구비되되, 경질 열가소성 고분자 소재로 이루어지는 중간층을 포함하는 투명 교정용 다중층 시트를 제공한다.
본 발명의 일 실시예에 있어서, 상기 제1 외부층 및 상기 제2 외부층 중 적어도 하나는 연질 폴리우레탄 소재로 이루어지는 것을 특징으로 하는 투명 교정용 다중층 시트일 수 있다.
본 발명의 일 실시예에 있어서, 상기 중간층은 경질 폴리우레탄 소재로 이루어지는 것을 특징으로 하는 투명 교정용 다중층 시트일 수 있다.
본 발명의 일 실시예에 있어서, 상기 제1 외부층 및 상기 제2 외부층 중 적어도 하나는 20μm 이상 200μm 이하의 두께를 갖도록 구성되는 것을 특징으로 하는 투명 교정용 다중층 시트일 수 있다.
본 발명의 일 실시예에 있어서, 상기 중간층은 200μm 이상 1500μm 이하의 두께를 갖도록 구성되는 것을 특징으로 하는 투명 교정용 다중층 시트일 수 있다.
본 발명의 일 실시예에 있어서, 상기 제1 외부층 및 상기 제2 외부층 중 적어도 하나는 60A 이상 100A이하의 경도(hardness)를 갖도록 구성되는 것을 특징으로 하는 투명 교정용 다중층 시트일 수 있다.
본 발명의 일 실시예에 있어서, 상기 중간층은 40MPa 이상 60MPa 이하의 항복강도(Yield strength)를 갖고, 1500MPa 이상 2200MPa 이하의 탄성계수(Young's modulus)를 갖도록 구성되는 것을 특징으로 하는 투명 교정용 다중층 시트일 수 있다.
본 발명의 일 실시예에 있어서, 상기 제1 외부층 또는 상기 제2 외부층과 상기 중간층 사이의 층간 접합력을 나타내는 박리강도(Peel strength)는 0.2N/cm 이상인 것을 특징으로 하는 투명 교정용 다중층 시트일 수 있다.
본 발명의 일 측면에 따르면, 본 발명의 투명 교정용 다중층 시트는 종래 소재 대비하여 치아 변형위치에서 장기간 변형이 적어 교정 유지력이 뛰어나고, 층간 접합력이 우수하여 내구성 및 환자 착용시 안전성이 향상될 수 있다.
또한, 외부층이 연질 고분자 소재로 이루어져 유연성을 부여함에 따라 초기 교정시 환자의 고통을 경감시킬 수 있다.
그리고, 중간층이 경질 고분자 소재로 이루어지고 높은 탄성 회복력을 가짐에 따라 외부층과의 층간 접합력 및 내구성이 향상될 수 있다.
본 발명의 효과는 상기한 효과로 한정되는 것은 아니며, 본 발명의 상세한 설명 또는 특허청구범위에 기재된 발명의 구성으로부터 추론 가능한 모든 효과를 포함하는 것으로 이해되어야 한다.
도 1은 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트로 제조된 투명교정장치를 나타내는 사시도이다.
도 2는 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트를 나타내는 사시도이다.
도 3의 (a) 및 (b)는 각각 본 발명의 일 실시예에 따른 종래 소재, 중간층 및 투명 교정용 다중층 시트 간의 항복강도(Yield strength) 및 탄성계수(Young's modulus)를 비교한 그래프이다.
도 4는 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트와 종래 소재 간의 박리강도(Peel strength)를 비교한 그래프이다.
도 5는 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트와 종래 소재 간의 변형 후 회복율을 비교한 사진이다.
도 6은 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트와 종래 소재 간의 교정력 유지율을 비교한 그래프이다.
이하에서는 첨부한 도면을 참조하여 본 발명을 설명하기로 한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며, 따라서 여기에서 설명하는 실시예로 한정되는 것은 아니다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 유사한 부분에 대해서는 유사한 도면 부호를 붙였다.
명세서 전체에서, 어떤 부분이 다른 부분과 "연결"되어 있다고 할 때, 이는 "직접적으로 연결"되어 있는 경우뿐 아니라, 그 중간에 다른 부재를 사이에 두고 "간접적으로 연결"되어 있는 경우도 포함한다. 또한 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 구비할 수 있다는 것을 의미한다.
이하 첨부된 도면을 참고하여 본 발명의 실시예를 상세히 설명하기로 한다.
도 1은 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트로 제조된 투명교정장치를 나타내는 사시도이고, 도 2는 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트를 나타내는 사시도이다.
도 1 및 도 2를 참조하면, 투명교정장치(10)는 환자의 상악 또는 하악의 치아(20)에 알맞게 성형되어 이용되는 구강내 구조물로서, 불규칙한 치아 배열이나 상하악의 비정상적인 맞물림 상태 등을 교정하기 위한 치료에 사용된다.
투명교정장치(10)에는 치아들이 끼워지는 치아홈(11)이 음각 형성된다. 그리고, 투명교정장치(10)는 상기 치아들의 상대치와 맞물리는 부분 즉 치관의 끝면(전치의 절연, 구치의 교합면)을 커버하는 구조로 형성된다.
이때, 투명교정장치(10)는 열가소성 투명 고분자 소재로 구성된 투명 교정용 다중층 시트(1000)로 이루어질 수 있다. 이처럼, 기존의 금속 재료가 아닌 고분자 소재로 이루어진 투명교정장치(10)는 투명하여 심미적으로 우수할 뿐만 아니라 치아에 탈부착이 가능해 구강 위생 관리에도 용이하다.
도 2를 참조하면, 본 발명에 따른 투명 교정용 다중층 시트(1000)는 제1 외부층(100), 제2 외부층(200) 및 중간층(300)을 포함하는 3중층 구조로 구성될 수 있다.
본 발명의 투명 교정용 다중층 시트(1000)는 종래 단일층 소재 시트와는 달리 구강 내 연조직과 맞닿는 외부층과 강성을 부여하는 내부층의 소재를 다르게 구성함으로써 시간에 따라 치아에 가해지는 교정력을 유지하면서도 환자에게 가해지는 불편감과 통증을 감소시킬 수 있다.
이때, 제1 외부층(100) 및 제2 외부층(200)은 투명 교정용 다중층 시트(1000)의 바깥층을 구성하고 구강 내 연조직과 맞닿는 부분으로서, 연질 열가소성 투명 고분자 소재로 이루어질 수 있다. 즉, 제1 외부층(100) 및 제2 외부층(200)은 연질 고분자 소재로 이루어져 투명 교정용 다중층 시트(1000)에 유연성을 부여하며, 변형력이 가해졌을 시 복합 응력이 작용하여 높은 교정 유지력 및 탄성 회복력을 제공할 수 있다.
중간층(300)은 투명 교정용 다중층 시트(1000)의 내부층을 구성하고 치아 이동을 위한 교정력을 부여하는 부분으로서, 경질 열가소성 투명 고분자 소재로 이루어질 수 있다. 즉, 중간층(300)은 경질 고분자 소재로 이루어져 투명 교정용 다중층 시트(1000)에 강도를 부여하며, 치아가 이동하고자 하는 방향으로 힘을 가하는 교정력을 제공할 수 있다.
일 실시예에 따르면, 제1 외부층(100) 및 제2 외부층(200)은 연질 열가소성 폴리우레탄(Thermoplastic Poly Urethane, TPU)으로 이루어질 수 있다.
폴리우레탄은 고무와 플라스틱의 특징을 모두 가지고 있으며, 환경호르몬, TVOC등의 유해물질이 없는 무독성 소재이다. 또한, 별도의 가소재가 필요 없는 탄성체로, 열에 의한 소성가공이 가능한 열가소성 엘라스토머 중 내마모성이 가장 높은 성질을 갖는 소재이다.
이에 따라, 본 발명의 제1 외부층(100) 및 제2 외부층(200)은 변형 회복률이 높은 연질 폴리우레탄으로 이루어져 투명 교정용 다중층 시트(1000)에 유연성을 부여할 수 있으며, 이에 따라 교정 초기 환자에게 가해지는 고통을 경감시킬 수 있게 된다.
한편, 본 발명의 제1 외부층(100) 및 제2 외부층(200)은 20μm 이상 200μm 이하의 두께를 갖도록 구성될 수 있다. 이때, 상기 제1 외부층(100) 및 제2 외부층(200)의 두께가 20μm 미만이면 탄성 변형을 충분히 받아주지 못해 투명 교정용 다중층 시트(1000)의 유연성이 저하될 수 있으며, 상기 제1 외부층(100) 및 제2 외부층(200)의 두께가 200μm 초과면 투명 교정용 다중층 시트(1000)의 두께가 지나치게 두꺼워져 환자의 착용감이 저하될 수 있다.
이때, 제1 외부층(100) 및 제2 외부층(200)는 60A 이상 100A이하의 경도(hardness)를 갖도록 구성되는 것이 바람직하다. 제1 외부층(100) 및 제2 외부층(200)의 경도가 60A 미만이면 치아와 맞닿을 시 교정력 유지를 위한 충분한 강도를 제공하지 못할 우려가 있으며, 100A 초과면 외부층의 강도가 지나치게 증가하여 충분한 탄성을 제공하지 못해 환자의 고통 경감이 저하될 수 있다.
일 실시예에 따르면, 중간층(300)은 경질 열가소성 폴리우레탄(Thermoplastic Poly Urethane, TPU)으로 이루어질 수 있다.
종래의 다중층 소재 중 중간층 소재는 교정력, 즉 강도 확보용 소재로서 PET, PE, PC 등의 투명 고분자 소재가 사용되었으나, 이러한 소재들은 공통적으로 변형에 대한 회복률이 낮으며, 층간 접합력이 낮은 특징을 가지고 있다.
또한, 종래의 다중층 시트는 강한 충격을 받는 경우, 중간층 고분자 소재의 백화현상을 동반한 영구변형이 발생하여 성능이 급격히 저하되는 문제가 있다. 즉 다중층 소재의 중간층은 교정력을 확보할 수 있는 강도를 가지면서 외력에 저항할 수 있는 높은 탄성 회복력을 갖도록 하여 다중층 소재의 내구성을 증가시키는 것이 요구된다.
본 발명의 중간층(300)은 제1 외부층(100) 및 제2 외부층(200)과의 층간 접합력을 높여 내구성을 향상시키는 경질 폴리우레탄으로 이루어져 투명 교정용 다중층 시트(1000)에 강성 및 높은 변형 회복률을 부여할 수 있으며, 이에 따라 향상된 치아 교정력을 제공할 수 있게 된다.
한편, 본 발명의 중간층(300)은 200μm 이상 1500μm 이하의 두께를 갖도록 구성될 수 있다. 이때, 상기 중간층(300)의 두께가 200μm 미만이면 교정력 유지를 위한 충분한 강도 확보가 어려울 수 있으며, 상기 중간층(300)의 두께가 1500μm 초과면 투명 교정용 다중층 시트(1000)의 두께가 지나치게 두꺼워져 환자의 착용감이 저하될 수 있다.
이때, 중간층(300)은 40MPa 이상 60MPa 이하의 항복강도(Yield strength)를 갖고, 1500MPa 이상 2200MPa 이하의 탄성계수(Young's modulus)를 갖도록 구성되는 것이 바람직하다. 중간층(300)의 항복강도가 40MPa 미만이고 탄성계수가 1500MPa 미만이면 충분한 탄성 변형을 제공하지 못해 교정력 확보를 위한 충분한 기계적 강도를 제공하는 것이 어려울 수 있으며, 항복강도가 60MPa 초과이고 탄성계수가 2200MPa초과면 교정 초기 환자의 고통 경감이 어려울 수 있다.
또한, 중간층(300)는 93% 이상 97% 이하의 투과도(Transmittance)를 갖도록 구성될 수 있다.
이처럼, 본 발명의 따른 투명 교정용 시트(1000)는 열적 특성이 비슷한 연질 폴리우레탄과 경질 폴리우레탄의 다중층으로 구성됨에 따라 치아 교정 유지력을 높이고 환자의 고통을 경감시키며, 우수한 층간 접합력으로 인해 내구성이 향상되어 환자 착용 시 안전성을 높일 수 있다.
이하에서는, 본 발명의 투명 교정용 다중층 시트(1000)와 종래 소재 간의 기계적 물성 값을 비교하는 실험 내용을 설명하며, 각각의 기계적 물성 값은 만능시험기(Universal Testing Machine, UTM)를 통해 측정되었다.
실험에 사용된 투명 교정용 다중층 시트(1000)의 제1 외부층(100) 및 제2 외부층(200)은 연질 폴리우레탄으로 이루어지고, 중간층(300)은 경질 폴리우레탄으로 이루어지도록 구성되었다. 그리고, 종래 소재의 바깥층은 연질 폴리우레탄으로 이루어지고, 내부층은 경질 폴리에스테르로 이루어지도록 구성되었다.
이때, 만능시험기(UTM)는 고분자 재료의 가장 기본적인 기계적인 특성을 알아내기 위해 재료에 응력을 가한 뒤, 이에 따른 변형율을 측정하여 재료의 물적 특성을 알아내는 실험 기구이다. 실험의 종류에는 인장, 박리, 굽힘 등의 실험이 있는데 모두 각 시편에 대한 힘을 가해주었을 때 그 힘에 대해 시편이 변형을 일으킬 때까지의 LOAD값을 측정하는 방식으로 진행되었다. 자세한 실험 방법은 공지의 사실이므로 생략하기로 한다.
도 3의 (a) 및 (b)는 각각 본 발명의 일 실시예에 따른 종래 소재, 중간층 및 투명 교정용 다중층 시트 간의 항복강도(Yield strength) 및 탄성계수(Young's modulus)를 비교한 그래프이다.
도 3을 참조하면, 종래 소재는 대략 30MPa 내지 40MPa의 항복강도와 1500 MPa 내지 1700MPa의 탄성계수를 갖는 것으로 측정되었으며, 본 발명의 투명 교정용 다중층 시트(1000)는 대략 40MPa 내지 60MPa의 항복강도와 1200MPa 내지 2000MPa의 탄성계수를 갖는 것으로 측정되었다.
즉, 본 발명의 투명 교정용 다중층 시트(1000)는 종래 소재에 비해 더 큰 탄성 변형을 허용함으로써 교정 초기 환자에게 가해지는 고통을 경감시키고 환자 착용시 안전성을 향상시킬 수 있다.
도 4는 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트와 종래 소재 간의 박리강도(Peel strength)를 비교한 그래프이다.
도 4를 참조하면, 본 발명의 투명 교정용 다중층 시트(1000)와 종래 소재를 외부층과 중간층이 접합되지 않은 면을 포함하는 시편을 제작하여 만능시험기로 박리강도를 측정하였다. 도 4에 나타난 바와 같이, 종래 소재는 대략 0.1N/cm 내지 0.15N/cm의 박리강도를 갖는 것으로 측정되었으며, 본 발명의 투명 교정용 다중층 시트(1000)는 대략 0.2N/cm 이상의 박리강도를 갖는 것으로 측정되었다.
즉, 본 발명의 투명 교정용 다중층 시트(1000)는 종래 소재에 비해 대략 2배 내지 3배 정도의 박리강도를 갖음으로써 층간 접합력을 향상시켜 층간 박리현상 발생을 방지할 수 있다. 이에 따라, 박리현상으로 인한 성능 저하 및 벗겨진 층이 환자의 구강에 존재하거나 소화기로 유입되어 환자의 안전을 저해하는 것을 방지할 수 있다.
도 5는 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트와 종래 소재 간의 변형 후 회복율을 비교한 사진이고, 도 6은 본 발명의 일 실시예에 따른 투명 교정용 다중층 시트와 종래 소재 간의 교정력 유지율을 비교한 그래프이다.
도 5를 참조하면, 본 발명의 투명 교정용 다중층 시트(1000)와 종래 소재를 1X8cm 시편으로 제작하여 굽힘 후 24시간 동안의 변화량을 측정하였다. 도 5에 나타난 바와 같이, 종래 소재의 경우 굽힘 후 24시간 동안 상대적으로 큰 각도를 유지하고 있어 변형 후 회복율이 상대적으로 낮은 것을 확인할 수 있으며, 본 발명의 투명 교정용 다중층 시트(1000)의 경우 굽힘 후 24시간 동안 거의 초기 상태와 비슷하게 회복된 것으로 보아 변형 후 회복율이 상대적으로 큰 것을 확인할 수 있다.
도 6을 참조하면, 본 발명의 투명 교정용 다중층 시트(1000)와 종래 소재를 굴곡강도(flexural) 측정용 시편으로 제작하여 만능시험기를 이용한 변형 회복율을 통해 교정력 유지율을 측정하였다. 도 6에 나타난 바와 같이, 종래 소재의 경우 시간에 따른 교정력이 상대적으로 빠르게 감소하여 일정 시간이 지나고 나면 교정력이 현저히 낮아지는 것을 확인할 수 있으며, 본 발명의 투명 교정용 다중층 시트(1000)의 경우 시간에 따른 교정력이 상대적으로 느리게 감소하여 일정 시간이 지나더라도 교정력이 일정 수준 유지되는 것을 확인할 수 있다.
이처럼, 본 발명에 따른 투명 교정용 다중층 시트(1000)는 종래 소재 대비하여 치아 변형위치에서 장기간 변형이 적어 교정 유지력이 뛰어나고, 층간 접합력이 우수하여 내구성 및 환자 착용시 안전성이 향상될 수 있다.
전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명되어 있는 각 구성 요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성 요소들도 결합된 형태로 실시될 수 있다.
본 발명의 범위는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
부호의 설명
1000 투명 교정용 다중층 시트
100 제1 외부층
200 제2 외부층
300 중간층
10 투명교정장치
11 치아홈

Claims (8)

  1. 연질 열가소성 고분자 소재로 이루어지는 제1 외부층;
    연질 열가소성 고분자 소재로 이루어지는 제2 외부층; 및
    상기 제1 외부층과 상기 제2 외부층 사이에 구비되되, 경질 열가소성 고분자 소재로 이루어지는 중간층을 포함하는 투명 교정용 다중층 시트.
  2. 제1항에 있어서,
    상기 제1 외부층 및 상기 제2 외부층 중 적어도 하나는 연질 폴리우레탄 소재로 이루어지는 것을 특징으로 하는 투명 교정용 다중층 시트.
  3. 제1항에 있어서,
    상기 중간층은 경질 폴리우레탄 소재로 이루어지는 것을 특징으로 하는 투명 교정용 다중층 시트.
  4. 제1항에 있어서,
    상기 제1 외부층 및 상기 제2 외부층 중 적어도 하나는 20μm 이상 200μm 이하의 두께를 갖도록 구성되는 것을 특징으로 하는 투명 교정용 다중층 시트.
  5. 제1항에 있어서,
    상기 중간층은 200μm 이상 1500μm 이하의 두께를 갖도록 구성되는 것을 특징으로 하는 투명 교정용 다중층 시트.
  6. 제1항에 있어서,
    상기 제1 외부층 및 상기 제2 외부층 중 적어도 하나는 60A 이상 100A이하의 경도(hardness)를 갖도록 구성되는 것을 특징으로 하는 투명 교정용 다중층 시트.
  7. 제1항에 있어서,
    상기 중간층은 40MPa 이상 60MPa 이하의 항복강도(Yield strength)를 갖고, 1500MPa 이상 2200MPa 이하의 탄성계수(Young's modulus)를 갖도록 구성되는 것을 특징으로 하는 투명 교정용 다중층 시트.
  8. 제1항에 있어서,
    상기 제1 외부층 또는 상기 제2 외부층과 상기 중간층 사이의 층간 접합력을 나타내는 박리강도(Peel strength)는 0.2N/cm 이상인 것을 특징으로 하는 투명 교정용 다중층 시트.
PCT/KR2021/002814 2020-03-19 2021-03-08 투명 교정용 다중층 시트 WO2021187785A1 (ko)