WO2021187099A1 - Feuille de polarisation circulaire et stratifié optique - Google Patents
Feuille de polarisation circulaire et stratifié optique Download PDFInfo
- Publication number
- WO2021187099A1 WO2021187099A1 PCT/JP2021/008086 JP2021008086W WO2021187099A1 WO 2021187099 A1 WO2021187099 A1 WO 2021187099A1 JP 2021008086 W JP2021008086 W JP 2021008086W WO 2021187099 A1 WO2021187099 A1 WO 2021187099A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- polarizing plate
- retardation
- liquid crystal
- film
- Prior art date
Abstract
La présente invention concerne une feuille de polarisation circulaire, et un stratifié optique et un dispositif d'affichage comprenant la feuille de polarisation circulaire, ladite feuille de polarisation circulaire étant apte à supprimer des différences dans la teinte de la lumière réfléchie lorsqu'elle est vue depuis une direction oblique par rapport à lorsqu'elle est vue depuis l'avant, même après avoir été exposée à une flexion dans un dispositif d'affichage tel qu'un dispositif d'affichage souple. La feuille de polarisation circulaire comprend, dans l'ordre suivant, une couche optique qui comprend au moins une couche de polarisation linéaire, une première couche de liaison, une première couche de déphasage , une seconde couche de liaison et une seconde couche de déphasage. La première couche de déphasage comprend une première couche de cristaux liquides, qui est une couche durcie d'un composé de cristaux liquides polymérisable. Si le module d'élasticité à une température de 25 °C de la première couche de liaison et de la seconde couche de liaison est respectivement G'1 [kPa] et G'2 [kPa], et l'épaisseur de la première couche de liaison et de la seconde couche de liaison est respectivement d1 [μm] et d2 [μm], la relation de formule (1) est satisfaite. (1) G'1/d1 ≥ G'2/d2
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020227026847A KR20220150283A (ko) | 2020-03-19 | 2021-03-03 | 원 편광판 및 광학 적층체 |
CN202180021465.3A CN115280202A (zh) | 2020-03-19 | 2021-03-03 | 圆偏振片和光学层叠体 |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2020049392 | 2020-03-19 | ||
JP2020-049392 | 2020-03-19 | ||
JP2021021642A JP2021152641A (ja) | 2020-03-19 | 2021-02-15 | 円偏光板及び光学積層体 |
JP2021-021642 | 2021-02-15 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2021187099A1 true WO2021187099A1 (fr) | 2021-09-23 |
Family
ID=77768086
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2021/008086 WO2021187099A1 (fr) | 2020-03-19 | 2021-03-03 | Feuille de polarisation circulaire et stratifié optique |
Country Status (4)
Country | Link |
---|---|
KR (1) | KR20220150283A (fr) |
CN (1) | CN115280202A (fr) |
TW (1) | TW202138851A (fr) |
WO (1) | WO2021187099A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2023090051A1 (fr) * | 2021-11-22 | 2023-05-25 | 住友化学株式会社 | Corps stratifié optique |
WO2023132164A1 (fr) * | 2022-01-05 | 2023-07-13 | 住友化学株式会社 | Polariseur |
WO2024024119A1 (fr) * | 2022-07-29 | 2024-02-01 | 住友化学株式会社 | Stratifié optique |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2019022156A1 (fr) * | 2017-07-26 | 2019-01-31 | 富士フイルム株式会社 | Dispositif d'affichage électroluminescent organique |
WO2019093474A1 (fr) * | 2017-11-10 | 2019-05-16 | 住友化学株式会社 | Plaque de polarisation circulaire et dispositif d'affichage |
JP2019091029A (ja) * | 2017-11-10 | 2019-06-13 | 住友化学株式会社 | 複合位相差板、光学積層体、及び画像表示装置 |
JP2019091030A (ja) * | 2017-11-10 | 2019-06-13 | 住友化学株式会社 | 複合位相差板、光学積層体、及び画像表示装置 |
WO2019216076A1 (fr) * | 2018-05-10 | 2019-11-14 | 住友化学株式会社 | Stratifié optique et appareil d'affichage |
JP2020003520A (ja) * | 2018-06-25 | 2020-01-09 | 住友化学株式会社 | 積層体 |
Family Cites Families (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2019091091A (ja) | 2013-02-07 | 2019-06-13 | 日東電工株式会社 | 円偏光板および屈曲可能な表示装置 |
JP6605682B2 (ja) | 2017-11-10 | 2019-11-13 | 住友化学株式会社 | 円偏光板 |
-
2021
- 2021-03-03 KR KR1020227026847A patent/KR20220150283A/ko unknown
- 2021-03-03 WO PCT/JP2021/008086 patent/WO2021187099A1/fr active Application Filing
- 2021-03-03 CN CN202180021465.3A patent/CN115280202A/zh active Pending
- 2021-03-11 TW TW110108606A patent/TW202138851A/zh unknown
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2019022156A1 (fr) * | 2017-07-26 | 2019-01-31 | 富士フイルム株式会社 | Dispositif d'affichage électroluminescent organique |
WO2019093474A1 (fr) * | 2017-11-10 | 2019-05-16 | 住友化学株式会社 | Plaque de polarisation circulaire et dispositif d'affichage |
JP2019091029A (ja) * | 2017-11-10 | 2019-06-13 | 住友化学株式会社 | 複合位相差板、光学積層体、及び画像表示装置 |
JP2019091030A (ja) * | 2017-11-10 | 2019-06-13 | 住友化学株式会社 | 複合位相差板、光学積層体、及び画像表示装置 |
WO2019216076A1 (fr) * | 2018-05-10 | 2019-11-14 | 住友化学株式会社 | Stratifié optique et appareil d'affichage |
JP2020003520A (ja) * | 2018-06-25 | 2020-01-09 | 住友化学株式会社 | 積層体 |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2023090051A1 (fr) * | 2021-11-22 | 2023-05-25 | 住友化学株式会社 | Corps stratifié optique |
WO2023132164A1 (fr) * | 2022-01-05 | 2023-07-13 | 住友化学株式会社 | Polariseur |
WO2024024119A1 (fr) * | 2022-07-29 | 2024-02-01 | 住友化学株式会社 | Stratifié optique |
Also Published As
Publication number | Publication date |
---|---|
TW202138851A (zh) | 2021-10-16 |
CN115280202A (zh) | 2022-11-01 |
KR20220150283A (ko) | 2022-11-10 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2021187099A1 (fr) | Feuille de polarisation circulaire et stratifié optique | |
KR102312066B1 (ko) | 광학 적층체 및 표시장치 | |
WO2021085000A1 (fr) | Stratifié optique et dispositif d'affichage | |
WO2021230010A1 (fr) | Plaque de polarisation circulaire | |
KR20210114869A (ko) | 광학 적층체 및 표시장치 | |
JP2021152641A (ja) | 円偏光板及び光学積層体 | |
WO2021187098A1 (fr) | Feuille de polarisation circulaire et stratifié optique | |
WO2021149358A1 (fr) | Empilement optique et procédé de production associé | |
WO2021166434A1 (fr) | Stratifié optique et dispositif d'affichage le comportant | |
WO2021193348A1 (fr) | Stratifié | |
WO2021176853A1 (fr) | Empilement optique et dispositif d'affichage d'image souple | |
WO2020230493A1 (fr) | Stratifié optique et dispositif d'affichage | |
JP2021144209A (ja) | 光学積層体 | |
JP2021152640A (ja) | 円偏光板及び光学積層体 | |
KR20210064180A (ko) | 광학 적층체 및 표시장치 | |
KR20200106451A (ko) | 광학 적층체 및 그 제조방법 | |
WO2021182030A1 (fr) | Corps multicouche optique | |
KR102345851B1 (ko) | 광학 적층체 및 표시장치 | |
WO2021182056A1 (fr) | Stratifié optique | |
WO2021149359A1 (fr) | Empilement optique et dispositif d'affichage | |
WO2020195631A1 (fr) | Corps multicouche et dispositif d'affichage d'image | |
JP2022148467A (ja) | 光学積層体 | |
KR20210157340A (ko) | 적층체, 화상 표시 장치 및 제조 방법 | |
KR20210157339A (ko) | 적층체, 화상 표시 장치 및 제조 방법 | |
KR20210114868A (ko) | 광학 적층체 및 표시장치 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21771551 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 21771551 Country of ref document: EP Kind code of ref document: A1 |