WO2021123136A1 - Multi-layered security structure for fiduciary use and security document using the structure - Google Patents

Multi-layered security structure for fiduciary use and security document using the structure Download PDF

Info

Publication number
WO2021123136A1
WO2021123136A1 PCT/EP2020/086984 EP2020086984W WO2021123136A1 WO 2021123136 A1 WO2021123136 A1 WO 2021123136A1 EP 2020086984 W EP2020086984 W EP 2020086984W WO 2021123136 A1 WO2021123136 A1 WO 2021123136A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
transparent
security
pattern
dark
Prior art date
Application number
PCT/EP2020/086984
Other languages
French (fr)
Inventor
Henri Rosset
Original Assignee
Oberthur Fiduciaire Sas
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Oberthur Fiduciaire Sas filed Critical Oberthur Fiduciaire Sas
Priority to EP20833864.0A priority Critical patent/EP4076972A1/en
Publication of WO2021123136A1 publication Critical patent/WO2021123136A1/en

Abstract

The invention particularly relates to a multi-layered security structure (S) for fiduciary use, which comprises at least three different, superimposed layers which are referred to as the first upper layer (1), second intermediate layer (2) and third lower layer (3), respectively, the first layer (1) being optically variable, that is to say, having different colours depending on the angle of observation or illumination with light reflected on a dark background, and being transparent or quasi-transparent on a light background; the second intermediate layer (2) incorporating at least one thermochromic material which has a first dark colour which thus constitutes the dark background and is opaque in a first temperature range and becomes at least partially transparent at a temperature outside the first temperature range; the third layer (3) being formed by at least one pattern (30, 31) with a dark colour thereby constituting the dark background, characterised in that it comprises a transparent or translucid support material and in that the first layer (1) also forms a barrier to ultraviolet radiation.

Description

Structure de sécurité multicouches à usage fiduciaire et document de sécurité qui en fait usage Multilayer security structure for fiduciary use and security document making use of it
DOMAINE TECHNIQUE GENERAL GENERAL TECHNICAL FIELD
La présente invention se situe dans le domaine général des structures de sécurité à usage fiduciaire et des documents de sécurité tels que les billets de banque. The present invention lies in the general field of security structures for fiduciary use and security documents such as banknotes.
ETAT DE LA TECHNIQUE STATE OF THE ART
La production d’éléments de sécurité tels que des fils de sécurité impliquant des couches ou impressions de matières thermochromiques révélant des effets optiques variables ou des inscriptions ou des images cachées par perte de la couleur, du fait des calories transmises à lelément de sécurité par apport de chaleur, notamment lorsqu'on le touche, est connue et décrite dans plusieurs brevets. The production of security elements such as security threads involving layers or prints of thermochromic materials revealing variable optical effects or inscriptions or images hidden by loss of color, due to the calories transmitted to the security element by input heat, especially when touched, is known and described in several patents.
Ainsi, dans EP 0608078, on a affaire à un fil de sécurité à utiliser dans des articles de sécurité, ce fil comprenant un substrat ayant un revêtement sur une ou sur ses deux faces opposées. Le revêtement contient un matériau thermochromique choisi parmi les pigments et les colorants dont la matière passe d'un statut coloré à un statut incolore lorsqu'il est soumis à une température supérieure à sa température d'activation. Thus, in EP 0608078, we are dealing with a security thread for use in security articles, this thread comprising a substrate having a coating on one or on its two opposite faces. The coating contains a thermochromic material selected from pigments and dyes whose material changes from a colored status to a colorless status when subjected to a temperature above its activation temperature.
Dans EP 1161352 est décrit un élément de sécurité pour une utilisation avec des matériaux de sécurité. Il comporte une première couche transparente, sur laquelle est appliqué au moins un dispositif optiquement variable qui peut être discontinu. Sur la face opposée de cette première couche sont appliqués des marquages qui peuvent être fluorescents, lesquels sont revêtus d'un enduit thermochromique. L'enduit thermochromique comprend une matière thermochromique qui est colorée lorsque la température de cet enduit est en dessous d'une température d'activation, laquelle couleur masque substantiellement les marquages et améliore la visibilité du dispositif optiquement variable. La matière thermochromique devient incolore au-dessus de ladite température d'activation, de manière à révéler les marquages, et rend le dispositif optiquement variable substantiellement invisible dans la lumière réfléchie. In EP 1161352 a security element for use with security materials is described. It comprises a first transparent layer, on which is applied at least one optically variable device which may be discontinuous. On the opposite side of this first layer are applied markings which may be fluorescent, which are coated with a thermochromic coating. The thermochromic coating comprises a thermochromic material which is colored when the temperature of this coating is below an activation temperature, which color substantially masks the markings and improves the visibility of the optically variable device. The thermochromic material becomes colorless above said activation temperature, so as to reveal the markings, and makes the optically variable device substantially invisible in reflected light.
Dans WO 2009/106242 est décrit le principe de l’image cachée. Il s'agit ici d'un élément de sécurité comportant au moins une couche d'encre thermochromique, laquelle comprend une première information, qui n'est normalement pas visible, mais qui le devient grâce à un premier type d'apport de chaleur. L'encre thermochromique couvre en outre une seconde information qui n'est normalement pas visible. Toutefois, cette seconde information peut être vue grâce à un second type d'apport de chaleur. In WO 2009/106242 the principle of the hidden image is described. This is a security element comprising at least one ink layer thermochromic, which includes a first information, which is not normally visible, but which becomes visible thanks to a first type of heat input. The thermochromic ink further covers second information which is not normally visible. However, this second information can be seen thanks to a second type of heat input.
Dans DE102015005448 sont décrits des moyens pour protéger des matériaux thermochromiques encapsulés et sensibles aux UV, en faisant usage de couches de protection colorées. Plus précisément, ce document a trait à une structure (voir mode de réalisation de la figure 1) dans laquelle on a affaire (de haut en bas) à un substrat polymère qui est opaque dans certaines régions et transparent dans d’autres. En regard d’une partie d’une région transparente est imprimée une encre thermochromique. Une couche d’encre noire comportant un ajour recouvre l’encre. Enfin, une couche colorée et transparente mais optiquement variable recouvre l’ensemble. La structure comporte également un matériau support opaque dans certaines régions et transparent dans une fenêtre. In DE102015005448, means are described for protecting encapsulated thermochromic materials sensitive to UV, by making use of colored protective layers. More specifically, this document relates to a structure (see embodiment of Figure 1) in which we are dealing (from top to bottom) with a polymeric substrate which is opaque in some regions and transparent in others. Next to part of a transparent region is printed a thermochromic ink. A layer of black ink with a cutout covers the ink. Finally, a colored and transparent but optically variable layer covers the whole. The structure also has a support material that is opaque in some areas and transparent in a window.
Le mode de réalisation de la figure 4 est sensiblement le même que celui de la figure 1, si ce n’est que deux couches sont formées de deux régions juxtaposées qui présentent des propriétés thermochromiques différentes. Dans EP 2307615, on a affaire à un élément de sécurité comprenant des cristaux liquides cholestériques qui permettent d'obtenir un effet de changement de couleur (en anglais "colorshift "), et au moins un composé thermo / photochromique. The embodiment of Figure 4 is substantially the same as that of Figure 1, except that two layers are formed of two juxtaposed regions which exhibit different thermochromic properties. In EP 2307615, we are dealing with a security element comprising cholesteric liquid crystals which make it possible to obtain a color change effect (in English "colorshift"), and at least one thermo / photochromic compound.
Enfin, dans le document WO2011 /057760 est décrite une structure conforme au préambule de la revendication 1 annexée. Finally, in document WO2011 / 057760 is described a structure in accordance with the preamble of claim 1 attached.
Dans le cadre de l’utilisation de matériaux thermochromiques notamment encapsulés et de couleur foncée, par exemple de couleur noire à une première température T1 correspondant à la température ambiante, et perdant leur couleur sous l’influence d’une température T2 correspondant à une température plus élevée due à une manipulation manuelle (par exemple une température de 31 °C), et plus particulièrement dans le but de combiner un effet visuel impliquant la révélation d’une image cachée, on ne tient pas compte de l’opacité de la couche thermochromique. In the context of the use of thermochromic materials, in particular encapsulated and dark in color, for example black in color at a first temperature T1 corresponding to ambient temperature, and losing their color under the influence of a temperature T2 corresponding to a temperature higher due to manual manipulation (for example a temperature of 31 ° C), and more particularly in order to combine a visual effect involving the revealing of a hidden image, the opacity of the layer is not taken into account thermochromic.
Ainsi, malgré la couleur noire à la température T1 et afin de dissimuler l'image cachée, il peut être nécessaire de déposer une couche thermochromique très épaisse, ce qui peut poser des problèmes en termes d’épaisseur sur le produit fini et de rentabilité économique. Thus, despite the black color at temperature T1 and in order to conceal the hidden image, it may be necessary to deposit a layer very thick thermochromic, which can pose problems in terms of thickness on the finished product and economic profitability.
Par ailleurs, l'application de couches barrières aux rayonnements ultraviolets (UV), telle que décrite dans l’art antérieur, nécessite une étape de transformation supplémentaire et occasionne une augmentation d’épaisseur sur le produit fini. Furthermore, the application of barrier layers to ultraviolet (UV) radiation, as described in the prior art, requires an additional processing step and causes an increase in thickness on the finished product.
La présente invention a pour but de pallier au moins un des problèmes identifiés ci-dessus. The object of the present invention is to overcome at least one of the problems identified above.
En d'autres termes, elle vise à proposer une structure de sécurité multicouches à usage fiduciaire qui renferme une image cachée et un matériau thermochromique, dans laquelle l'image cachée n'est aucunement visible, dans un premier état dans lequel le matériau thermochromique est opaque. In other words, it aims to provide a multilayer security structure for fiduciary use which contains a hidden image and a thermochromic material, in which the hidden image is in no way visible, in a first state in which the thermochromic material is. opaque.
Elle vise également à fournir une structure de tenue à la lumière améliorée. It is also intended to provide an improved light resistance structure.
PRESENTATION DE L'INVENTION PRESENTATION OF THE INVENTION
A cet effet, l’invention concerne en premier lieu une structure de sécurité multicouches à usage fiduciaire, qui comporte au moins trois couches distinctes et superposées, respectivement désignées première couche supérieure, deuxième couche intermédiaire et troisième couche inférieure, ladite première couche étant optiquement variable, c’est-à-dire présentant des couleurs différentes selon l’angle d’observation ou d’illumination en lumière réfléchie sur fond sombre, et étant transparente ou quasi - transparente sur fond clair ; ladite deuxième couche intermédiaire incorporant au moins un matériau thermochromique qui présente une première couleur sombre constituant ainsi ledit fond sombre, et est opaque dans une première gamme de températures, et devient au moins partiellement transparent à une température hors de ladite première gamme de température ; ladite troisième couche étant formée d’au moins un motif de couleur sombre constituant ainsi ledit fond sombre, caractérisée par le fait qu’elle comporte un matériau support transparent ou translucide et que ladite première couche forme également barrière aux rayonnements ultraviolets. To this end, the invention relates firstly to a multilayer security structure for fiduciary use, which comprises at least three distinct and superimposed layers, respectively designated first upper layer, second intermediate layer and third lower layer, said first layer being optically variable. , that is to say having different colors depending on the angle of observation or illumination in reflected light on a dark background, and being transparent or quasi - transparent on a light background; said second intermediate layer incorporating at least one thermochromic material which exhibits a first dark color thereby constituting said dark background, and is opaque in a first temperature range, and becomes at least partially transparent at a temperature outside said first temperature range; said third layer being formed of at least one pattern of dark color thus constituting said dark background, characterized in that it comprises a transparent or translucent support material and that said first layer also forms a barrier to ultraviolet radiation.
Grâce à ces caractéristiques, on obtient une structure qui renferme une image cachée laquelle riest révélée que lorsque le matériau thermochromique perd sa couleur initiale, et ce sans augmentation particulière de l'épaisseur de ce matériau. Thanks to these characteristics, a structure is obtained which contains a hidden image which is only revealed when the material thermochromic loses its initial color, without any particular increase in the thickness of this material.
Par l'expression « couleur sombre », on entend, dans l'ensemble de la présente demande, une couleur qui permet de rendre visible ladite première couche. By the expression “dark color” is meant, throughout the present application, a color which makes it possible to make said first layer visible.
Dans l’ensemble de la présente demande, y compris les revendications, on entend par l’expression « couche de pigment interférentiel », une couche comprenant des pigments présentant une structure constituée de plusieurs couches de matériaux d’indices de réfraction différents, cette structure multicouche créant des interférences constructives pour une longueur d’onde donnée, cette longueur d’onde étant dépendante de l’angle d’incidence de la lumière. Throughout the present application, including the claims, the expression “layer of interference pigment” is understood to mean a layer comprising pigments having a structure consisting of several layers of materials of different refractive indices, this structure multilayer creating constructive interference for a given wavelength, this wavelength being dependent on the angle of incidence of the light.
Ladite deuxième couche intermédiaire constitue ledit fond sombre dans ladite première gamme de température et ledit motif de la troisième couche constitue ledit fond sombre hors de ladite première gamme de températures. Said second intermediate layer constitutes said dark background in said first temperature range and said pattern of the third layer constitutes said dark background outside said first temperature range.
De plus, l’utilisation d’une couche de pigment interférentiel permet de se dispenser de cristaux liquides dont la manipulation est complexe, sans avoir l’assurance que ces cristaux liquides s’alignent sur la couche thermochromique. Il est de plus complexe de former des motifs par impression de cristaux liquides en assurant une bonne adhésion des cristaux liquides sur le support d’impression. In addition, the use of an interference pigment layer eliminates the need for liquid crystals, which are complex to handle, without ensuring that these liquid crystals align with the thermochromic layer. It is also complex to form patterns by printing liquid crystals while ensuring good adhesion of the liquid crystals to the printing medium.
L’utilisation d’un matériau support transparent ou translucide permet de discerner le motif, c'est-à-dire l’image cachée lorsque la couche thermochromique est activée, c'est-à-dire transparente. The use of a transparent or translucent support material makes it possible to discern the pattern, i.e. the image hidden when the thermochromic layer is activated, i.e. transparent.
Selon d'autres caractéristiques avantageuses et non limitatives de l'invention, prises seules ou selon une combinaison quelconque : According to other advantageous and non-limiting characteristics of the invention, taken alone or in any combination:
- ladite première couche est une couche de pigments interférentiels ; - ladite première couche est formée d'une première épaisseur de paillettes de mica synthétique avec dépôt de Sn02 et Ti02 et d'une seconde épaisseur d'un matériau barrière aux rayonnements ultraviolets ; - Said first layer is a layer of interference pigments; - Said first layer is formed of a first thickness of synthetic mica flakes with deposition of SnO 2 and TiO 2 and of a second thickness of an ultraviolet radiation barrier material;
- à ladite première gamme de températures, ladite deuxième couche intermédiaire est opaque ; - elle comporte une autre couche incorporant au moins un matériau thermochromique, ladite troisième couche étant située entre ladite deuxième couche intermédiaire et ladite autre couche ; - at said first temperature range, said second intermediate layer is opaque; it comprises another layer incorporating at least one thermochromic material, said third layer being situated between said second intermediate layer and said other layer;
- elle comporte au moins une couche additionnelle blanche et semi -opaque ; - It comprises at least one additional white and semi-opaque layer;
- elle comporte au moins une couche additionnelle constituée d'adhésif qui constitue une couche externe, c'est à dire disposée au-dessus ou au- dessous des autres couches ; - It comprises at least one additional layer consisting of adhesive which constitutes an outer layer, that is to say disposed above or below the other layers;
- elle comporte deux couches additionnelles constituées d'adhésif, qui s'étendent à l'opposé l'une de l'autre ; - It has two additional layers made of adhesive, which extend opposite to each other;
- ledit adhésif est blanc et semi -opaque ; - said adhesive is white and semi-opaque;
- ledit adhésif est positionné sur ladite première couche et il forme une barrière aux rayonnements ultraviolets ; - Said adhesive is positioned on said first layer and it forms a barrier to ultraviolet radiation;
- ladite première couche incorpore des paillettes de mica synthétique avec dépôt de Sn02 et Ti02 ; - Said first layer incorporates synthetic mica flakes with deposition of Sn02 and Ti02;
- lesdites paillettes de mica synthétique avec dépôt de Sn02 et Ti02 ont une caractéristique g ranulo métrique D50 comprise entre 10 et 30, de préférence entre 18 et 23 micromètres ; - Said synthetic mica flakes with deposit of Sn02 and Ti02 have a granulometric characteristic D50 of between 10 and 30, preferably between 18 and 23 micrometers;
- ladite première couche est dépourvue de cristaux liquides ; - Said first layer is devoid of liquid crystals;
- ledit matériau support est en matière plastique telle que du téréphtalate de polyéthylène ou du polypropylène bi -orienté ; - Said support material is plastic such as polyethylene terephthalate or bi -oriented polypropylene;
- ledit motif est un motif imprimé ou un motif résultant d'une métallisation ou d'une démétallisation ; said pattern is a printed pattern or a pattern resulting from metallization or demetallization;
- ledit motif est au moins partiellement, de préférence totalement, recouvert par ladite deuxième couche intermédiaire ; - Said pattern is at least partially, preferably totally, covered by said second intermediate layer;
- elle se présente sous la forme d'un bandeau, d'un fil de sécurité ou d'un film. - it comes in the form of a banner, a security thread or a film.
Quand la troisième couche est constituée d'un motif imprimé, alors cette troisième couche est réduite à sa plus simple expression, ce qui signifie quelle consiste uniquement en ce motif. When the third layer consists of a printed pattern, then this third layer is reduced to its simplest form, which means that it consists only of that pattern.
Un autre aspect de l'invention est relatif à un document de sécurité caractérisé par le fait qu'il intègre au moins une structure selon l'une des caractéristiques précédentes. Another aspect of the invention relates to a security document characterized in that it incorporates at least one structure according to one of the preceding characteristics.
Elle se rapporte aussi à un document de sécurité tel qu'un billet de banque, qui comprend une matière plastique, dont une partie constitue ledit matériau support de la structure selon l’une des caractéristiques précédentes. DESCRIPTION DES FIGURES It also relates to a security document such as a bank note, which comprises a plastic material, part of which constitutes said support material for the structure according to one of the preceding characteristics. DESCRIPTION OF FIGURES
D'autres caractéristiques et avantages de l'invention apparaîtront de la description qui va maintenant en être faite, en référence aux dessins annexés, qui en représentent, à titre indicatif mais non limitatif, différents modes de réalisation possibles. Other characteristics and advantages of the invention will emerge from the description which will now be given, with reference to the appended drawings, which represent, by way of indication but not limiting, various possible embodiments thereof.
Sur ces dessins : On these drawings:
La figure 1 est une vue est une vue en coupe, extrêmement simplifiée, d'une structure selon l'invention qui a la forme d'un bandeau de sécurité ; FIG. 1 is a view in section, extremely simplified, of a structure according to the invention which has the form of a safety strip;
La figure 2 est une vue analogue à la figure 1 , d'une variante de réalisation de la structure ; FIG. 2 is a view similar to FIG. 1, of an alternative embodiment of the structure;
La figure 3 est une vue de dessus d'un exemple de réalisation de la troisième couche de la structure, celle-ci étant représentée apposée sur un matériau support transparent de forme allongée ; FIG. 3 is a top view of an exemplary embodiment of the third layer of the structure, the latter being shown affixed to a transparent support material of elongated shape;
La figure 4 est une vue de dessus simplifiée d'un document de sécurité, en l'occurrence d'un billet dans lequel sont intégrés deux structures de sécurité différentes mais conformes à l'invention, à savoir sous la forme d'un bandeau et d'un film ; FIG. 4 is a simplified top view of a security document, in this case of a ticket in which are integrated two different security structures but in accordance with the invention, namely in the form of a strip and of a film ;
La figure 5 est une vue de dessus partielle du bandeau visible à la figure 4, selon un premier état ; La figure 6 est une vue de dessus partielle du bandeau visible à la figure 4, selon un deuxième état ; FIG. 5 is a partial top view of the strip visible in FIG. 4, according to a first state; FIG. 6 is a partial top view of the strip visible in FIG. 4, according to a second state;
La figure 7 est une vue de dessus partielle du bandeau visible à la figure 4, selon un troisième état. DESCRIPTION DETAILLEE DE L'INVENTION FIG. 7 is a partial top view of the strip visible in FIG. 4, according to a third state. DETAILED DESCRIPTION OF THE INVENTION
Les figures annexées ont pour fonction principale d’être informatives. Dans ces conditions, les échelles de dimensions des différents éléments décrits ci-après ne sont aucunement respectées. La figure 1 illustre une première forme de réalisation possible de la structure selon l’invention. Il s'agit ici d'un bandeau de sécurité S, mais il pourrait s'agir d'un fil de sécurité, d'un film de forme quelconque, d’un patch, etc. The main function of the appended figures is to be informative. Under these conditions, the dimension scales of the various elements described below are not respected in any way. FIG. 1 illustrates a first possible embodiment of the structure according to the invention. This is an S security strip, but it could be a security thread, some form of film, a patch, etc.
Conformément à l'invention, cette structure de sécurité à usage fiduciaire comporte au moins trois couches distinctes et superposées, respectivement désignées première couche supérieure, deuxième couche intermédiaire et troisième couche. According to the invention, this security structure for fiduciary use comprises at least three distinct and superimposed layers, respectively designated the first upper layer, second intermediate layer and third layer.
A la figure 1 , ces couches sont respectivement référencées 1 , 2 et 3. In FIG. 1, these layers are respectively referenced 1, 2 and 3.
La première couche 1 est optiquement variable, ce qui signifie quelle présente des couleurs différentes selon l’angle d’observation ou d’illumination, lorsque la couche qui s'étend au-dessous d'elle présente une teinte (couleur) sombre. En revanche, ladite première couche est transparente ou sensiblement transparente lorsque la couche qui s'étend au-dessous d'elle présente une teinte claire. Cette couche optiquement variable est ici une couche de pigment interférentiel. The first layer 1 is optically variable, which means that it shows different colors depending on the angle of observation or illumination, when the layer that extends below it has a dark tint (color). On the other hand, said first layer is transparent or substantially transparent when the layer which extends below it has a light shade. This optically variable layer is here a layer of interference pigment.
Selon une forme de réalisation particulièrement avantageuse, la première couche incorpore des paillettes de mica synthétique avec dépôt de SnÛ2 et T1O2, notamment avec une caractéristique g ranulo métrique D50 comprise entre 10 et 30, de préférence entre 18 et 23 micromètres. According to a particularly advantageous embodiment, the first layer incorporates synthetic mica flakes with deposition of SnO2 and T1O2, in particular with a granulometric characteristic D50 of between 10 and 30, preferably between 18 and 23 micrometers.
Le paramètre D50 signifie que 50% des paillettes rentrent dans la fourche de valeurs indiquée ci-dessus. The D50 parameter means that 50% of the flakes fall within the range of values indicated above.
Une telle couche présente différentes couleurs selon l’angle d’observation ou d’illumination lorsque la couche qui s'étend au-dessous d'elle présente une teinte sombre. En revanche, une telle couche est transparente ou sensiblement transparente lorsque la couche qui s'étend au-dessous d'elle présente une teinte claire. Such a layer exhibits different colors depending on the angle of observation or illumination when the layer lying below it exhibits a dark tint. On the other hand, such a layer is transparent or substantially transparent when the layer which extends below it has a light shade.
Selon l’invention, la première couche forme une barrière aux rayonnements ultraviolets. A cette fin, ladite couche 1 incorpore, en plus des paillettes de mica synthétique avec dépôt de SnÛ2 et T1O2, au moins un composé ayant cette capacité de former une barrière aux rayonnements ultraviolets, par exemple un dioxyde de titane particulaire et/ou une triazine. Il s’agit de préférence d’une triazine. According to the invention, the first layer forms a barrier to ultraviolet radiation. To this end, said layer 1 incorporates, in addition to synthetic mica flakes with deposit of SnO2 and T1O2, at least one compound having this capacity to form a barrier to ultraviolet radiation, for example a particulate titanium dioxide and / or a triazine. . It is preferably a triazine.
Dans la variante représentée à la figure 2, ces deux fonctions sont dissociées. Plus précisément, la première couche 1 est formée d'une première épaisseur 10 de pigments interférentiels, qui s'étend au-dessus d'une seconde épaisseur 11 d'un dioxyde de titane particulaire ayant la capacité de former une barrière aux rayonnements ultraviolets. In the variant shown in FIG. 2, these two functions are dissociated. More precisely, the first layer 1 is formed of a first thickness 10 of interference pigments, which extends over a second thickness 11 of a particulate titanium dioxide having the ability to form a barrier to ultraviolet radiation.
La triazine est préférée au dioxyde de titane particulaire car elle a la particularité d’être plus transparente. Triazine is preferred over particulate titanium dioxide because it has the particularity of being more transparent.
Dans les deux modes de réalisation, la fonction de cette barrière est de protéger la couche intermédiaire 2 décrite ci-dessous. In both embodiments, the function of this barrier is to protect the intermediate layer 2 described below.
La deuxième couche intermédiaire 2 incorpore au moins un matériau thermochromique qui présente une première couleur et est opaque dans une première gamme de températures et devient au moins partiellement transparent à partir d'une température hors de ladite gamme de température. The second intermediate layer 2 incorporates at least one thermochromic material which exhibits a first color and is opaque in a first temperature range and becomes at least partially transparent from a temperature outside said temperature range.
Par exemple, ladite première gamme de températures est celle qui englobe des températures ambiantes habituelles et ce dans des conditions normales d'utilisation du document de sécurité dans lequel la structure S est destinée à être incorporée, ce qui englobe les températures négatives ainsi que les températures positives jusqu'à par exemple 25°C. For example, said first temperature range is that which includes usual ambient temperatures and this under normal conditions of use of the security document in which the structure S is intended to be incorporated, which includes negative temperatures as well as temperatures. positive up to for example 25 ° C.
Toujours à titre d'exemple, la température à partir de laquelle la couche devient au moins partiellement transparente est de l'ordre de 31 °C. Cette température est notamment atteinte par exemple par contact avec le corps d'un individu (doigts, paume), un objet chaud ou une source de chauffage. Still by way of example, the temperature from which the layer becomes at least partially transparent is of the order of 31 ° C. This temperature is notably reached, for example, by contact with the body of an individual (fingers, palm), a hot object or a source of heating.
Afin de renforcer le caractère opaque de la deuxième couche 2, on peut y incorporer un agent opacifiant, par exemple du dioxyde de titane. In order to reinforce the opaque character of the second layer 2, an opacifying agent, for example titanium dioxide, can be incorporated therein.
La troisième couche 3 est formée d'au moins un motif de couleur sombre. Il s'agit d'un motif de forme quelconque consistant par exemple en des caractères alphabétiques et/ou numérique, d'un dessin, etc. The third layer 3 is formed of at least one pattern of dark color. It is a pattern of any shape consisting, for example, of alphabetic and / or numeric characters, of a drawing, etc.
Cet au moins un motif est confectionné avec tout type d'encre utilisée dans le domaine de l'impression fiduciaire. Il peut être également réalisé par métallisation et/ou démétallisation. This at least one pattern is made with any type of ink used in the field of fiduciary printing. It can also be produced by metallization and / or demetallization.
Par ailleurs, cet au moins un motif peut être formé en positif ou en négatif. Moreover, this at least one pattern can be formed in positive or in negative.
Dans les modes de réalisation représentés sur les figures, cette troisième couche 3 repose sur un matériau support 4 transparent ou translucide qui est disposé sous ladite troisième couche. Par le terme « translucide », on englobe le cas de figure dans lequel ce matériau support est blanc et semi- opaque. Dans un mode de réalisation différent, ce matériau support 4 peut être intercalé entre deux des trois couches 1 , 2 et 3 ou même au-dessus de la couche 1. In the embodiments shown in the figures, this third layer 3 rests on a transparent or translucent support material 4 which is placed under said third layer. By the term “translucent” is meant the case in which this support material is white and semi-opaque. In a different embodiment, this support material 4 can be interposed between two of the three layers 1, 2 and 3 or even above the layer 1.
Le placement de ce matériau support, en particulier quand celui-ci est transparent, n’est pas capital dans la mesure où les couches 1 à 3 précitées peuvent être placées par les techniques, notamment d’impression fiduciaires courantes les unes sur les autres d'un côté de ce matériau support, ou réparties de part et d'autre de ce dernier. The placement of this support material, in particular when the latter is transparent, is not essential insofar as the aforementioned layers 1 to 3 can be placed by the techniques, in particular current fiduciary printing one on top of the other. 'one side of this support material, or distributed on either side of the latter.
Quand le matériau support est translucide, on préfère le placer sous la troisième couche, c'est-à-dire à l’opposé des première et deuxième couches. When the support material is translucent, it is preferred to place it under the third layer, that is, on the opposite side of the first and second layers.
Bien que cela ne soit pas obligatoire, la structure S comporte avantageusement au moins une couche additionnelle constituée d'adhésif qui constitue une couche externe, c'est à dire disposée au-dessus ou au-dessous des autres couches. Although this is not obligatory, the structure S advantageously comprises at least one additional layer consisting of adhesive which constitutes an external layer, that is to say disposed above or below the other layers.
La présence d'un tel adhésif est destinée à faciliter l'incorporation de la structure S au sein d'un document de sécurité tel qu'un billet de banque. The presence of such an adhesive is intended to facilitate the incorporation of the structure S within a security document such as a bank note.
En variante, le matériau support 4 de la structure S est le substrat d’un document de sécurité. Ledit substrat est par exemple fibreux, notamment cellulosique, ou synthétique, notamment polymère. As a variant, the support material 4 of the structure S is the substrate of a security document. Said substrate is for example fibrous, in particular cellulosic, or synthetic, in particular polymer.
Aux figures 1 et 2, la couche d'adhésif 5 est placée sous le matériau support. Toutefois, dans une variante non représentée, elle pourrait être placée au-dessus de la couche 1. In Figures 1 and 2, the adhesive layer 5 is placed under the support material. However, in a variant not shown, it could be placed above layer 1.
On peut même envisager deux couches 5 d'adhésif constituant ainsi des couches externes de la structure S. It is even possible to envisage two layers of adhesive 5 thus constituting the external layers of the structure S.
La couche d’adhésif peut être opacifiante (c'est à dire blanche et semi-opaque) ou non. The adhesive layer may or may not be opacifying (ie white and semi-opaque).
Dans le cas d’une couche opacifiante, celle-ci est semi-opaque afin de permettre la vision des cleartext (c'est à dire des motifs sombres) en lumière transmise (la couche thermochromique 2 étant dans son état transparent). De plus, elle doit masquer les motifs 3 en lumière réfléchie (notamment au verso). In the case of an opacifying layer, it is semi-opaque in order to allow the vision of cleartext (ie dark patterns) in transmitted light (the thermochromic layer 2 being in its transparent state). In addition, it must mask the patterns 3 in reflected light (especially on the back).
En variante, la couche 5 est remplacée par une couche 5’ (non représentée) opacifiante telle que décrite ci-avant, et non-adhésive. La couche adhésive peut également intégrer un composant qui possède une fonction de barrière aux rayonnements ultraviolets (également appelée « fonction anti-UV »). As a variant, the layer 5 is replaced by an opacifying layer 5 ′ (not shown) as described above, and non-adhesive. The adhesive layer can also incorporate a component which has a function of barrier to ultraviolet radiation (also called "anti-UV function").
A la figure 3 est représenté un exemple de réalisation d'une structure S selon l'invention, qui a ici la forme d'un bandeau. Ce bandeau est représenté alors que l'on a porté la couche 2 incorporant un matériau thermochromique à une température telle que ce matériau est devenu transparent. In FIG. 3 is shown an embodiment of a structure S according to the invention, which here has the shape of a strip. This band is shown when the layer 2 incorporating a thermochromic material has been brought to a temperature such that this material has become transparent.
Ainsi, les motifs 3 sont révélés. Dans cet exemple, il s'agit d'un premier motif 30 qui a la forme d'un visage féminin et d'un second motif 31 formé du nombre "100". Thus, patterns 3 are revealed. In this example, there is a first pattern 30 which has the shape of a female face and a second pattern 31 formed by the number "100".
A titre purement indicatif est donné ci-après un exemple de réalisation des différentes couches de la structure S selon l'invention, sous la forme de tableaux. II s’agit de formulations base aqueuse qui peuvent être remplacées par des formulations base résine réticulable sous UV (ci-après « résines UV »), notamment en remplaçant l’eau, le liant base aqueuse et son réticulant par une base résine avec photo initiateur, le composé barrière aux rayonnements ultraviolets étant choisi parmi les composés compatible avec les résines UV. Purely by way of indication, an embodiment example of the various layers of structure S according to the invention is given below, in the form of tables. These are aqueous-based formulations which can be replaced by resin-based formulations crosslinkable under UV (hereinafter “UV resins”), in particular by replacing the water, the aqueous-based binder and its crosslinking agent with a resin base with photo. initiator, the barrier compound to ultraviolet radiation being chosen from compounds compatible with UV resins.
1 / Couche 2 thermochromique et opacifiante : environ 6,5g/m2 à l'état sec et épaisseur de l'ordre de 8 um 1 / Thermochromic and opacifying layer 2: approximately 6.5 g / m 2 in the dry state and thickness of the order of 8 μm
Tableau 1
Figure imgf000012_0001
2/ Couche optiquement variable 1 incorporant un agent de protection aux UV : environ 5,3 g/ m2 à l'état sec pour une épaisseur d'environ 4 i_im. Table 1
Figure imgf000012_0001
2 / Optically variable layer 1 incorporating a UV protection agent: approximately 5.3 g / m 2 in the dry state for a thickness of approximately 4 µm.
Tableau 2
Figure imgf000013_0001
3/ Couche thermoadhésive blanche : environ 2,5 g/m2 à l'état sec pour une épaisseur d'environ 3 um. Table 2
Figure imgf000013_0001
3 / White thermoadhesive layer: approximately 2.5 g / m 2 in the dry state for a thickness of approximately 3 μm.
Tableau 3
Figure imgf000013_0002
Une fois fabriquée, la structure S selon l'invention peut éventuellement être découpée en différentes fractions, lesquelles sont avantageusement incorporées dans des documents de sécurité, notamment des billets de banque. Table 3
Figure imgf000013_0002
Once manufactured, the structure S according to the invention can optionally be cut into different fractions, which are advantageously incorporated in security documents, in particular banknotes.
Ainsi, ces fractions, qui constituent autant d'éléments de sécurité, peuvent être intégrés en fenêtre dans un document de valeur et/ou de sécurité, être intégrés en surface d'un tel document, former un film d'obturation d'une fenêtre d’un tel document, un fil de sécurité, etc. Thus, these fractions, which constitute as many security elements, can be integrated into a window in a valuable and / or security document, be integrated into the surface of such a document, form a film for sealing a window. of such a document, a security thread, etc.
Cette incorporation, quelle ait lieu partiellement en surface (c’est-à-dire en fenêtre), totalement en surface, ou dans l'épaisseur du document de sécurité, est réalisée selon les méthodologies habituelles dans le domaine de la papeterie et de l'impression fiduciaire. This incorporation, which takes place partially on the surface (that is to say in a window), totally on the surface, or in the thickness of the security document, is produced according to the usual methodologies in the field of stationery and fiduciary printing.
Ledit document de sécurité et/ou de valeur est de préférence un billet de banque. Dans le cas particulier des billets de banque dont le substrat est constitué d'un matériau polymère, on peut envisager de faire usage dudit substrat à titre de matériau support 4. Said security and / or value document is preferably a bank note. In the particular case of banknotes whose substrate is made of a polymer material, it is possible to envisage using said substrate as a support material 4.
A la figure 4 annexée est représenté, vu de dessus, un billet de banque 6 qui intègre deux structures S selon l'invention, de formes différentes. Ainsi, ce billet 6, dont seule la face recto 60 est représentée ici, comporte un bandeau de sécurité 7. Il s'étend transversalement par rapport à la plus grande dimension du billet et rejoint les grands côtés longitudinaux. In Figure 4 attached is shown, seen from above, a banknote 6 which incorporates two structures S according to the invention, of different shapes. Thus, this note 6, of which only the front face 60 is shown here, comprises a security strip 7. It extends transversely with respect to the largest dimension of the note and joins the long longitudinal sides.
Le bandeau est partiellement intégré dans le corps du billet de sorte qu'il émerge seulement en quelques endroits à la surface du corps au niveau de la face recto 60, en formant ainsi des fenêtres F. Celles-ci sont repérées sous la forme de zones de couleur noire à la figure 4. The strip is partially integrated into the body of the banknote so that it emerges only in a few places on the surface of the body at the level of the front face 60, thus forming windows F. These are identified in the form of zones. black in figure 4.
Deux fenêtres F consécutives sont ainsi séparées par un "pont" P c'est à dire à une région dans laquelle le bandeau 2 est complètement enfoui dans le corps du billet. Ces ponts sont repérés de manière grisée à la figure 4. L'autre structure S consiste en un film 8 de forme rectangulaire apposé à la surface du billet. Le film 8 peut recouvrir au moins partiellement une ouverture traversante réalisée dans le substrat dudit billet. Two consecutive windows F are thus separated by a "bridge" P, ie a region in which the strip 2 is completely buried in the body of the note. These bridges are marked in gray in FIG. 4. The other structure S consists of a film 8 of rectangular shape affixed to the surface of the note. The film 8 can at least partially cover a through opening made in the substrate of said note.
A la figure 5 est représenté partiellement le bandeau 7 de la figure 4. On considère ici que le billet 6 est à température ambiante, par exemple 20° C. In Figure 5 is partially shown the strip 7 of Figure 4. It is considered here that the ticket 6 is at room temperature, for example 20 ° C.
Dans cette situation, les fenêtres F présentent une première couleur qui est caractéristique de la couche 1 , par exemple rouge sous un illuminant donné et selon des directions d’observation et d’illumination données. Cette couleur est visible car la couche 2 qui incorpore le matériau thermochromique présente une première couleur sombre. In this situation, the windows F have a first color which is characteristic of layer 1, for example red under a given illuminant and according to given directions of observation and illumination. This color is visible because the layer 2 which incorporates the thermochromic material has a first dark color.
La situation de la figure 6 est la même que celle de la figure 5, si ce n'est que le bandeau 6 est vu sous ledit illuminant donné selon un angle d'observation et/ou d’illumination différent. Les fenêtres adoptent alors une deuxième couleur également caractéristique de la couche 1 , par exemple verte. Enfin, en référence à la figure 7, on considère qu'un utilisateur du billet 6 a apposé la paume de sa main contre le bandeau 7. Ceci se traduit par une augmentation de température qui suffit pour faire passer la couche 2 de la structure S de l'état "couleur sombre" à l'état "transparent" ou "partiellement transparent". Ce faisant, hors des zones disposées au regard desdits motifs, la couche 1 "perd" sa coloration et devient transparente ou quasi -transparente. The situation of FIG. 6 is the same as that of FIG. 5, except that the strip 6 is seen under said given illuminant at a different angle of observation and / or illumination. The windows then adopt a second color also characteristic of layer 1, for example green. Finally, with reference to FIG. 7, it is considered that a user of the ticket 6 has placed the palm of his hand against the strip 7. This results in an increase in temperature which is sufficient to pass the layer 2 of the structure S from the "dark color" state to the "transparent" or "partially transparent" state. In doing so, outside the zones arranged with respect to said patterns, layer 1 "loses" its coloring and becomes transparent or quasi-transparent.
Cela permet alors de révéler la couche 3 qui est constituée ici d’une impression des lettres O et F . Cette image cachée n’est donc visible et révélée que dans certaines conditions. Par ailleurs, on notera les points suivants. This then makes it possible to reveal layer 3 which here consists of an impression of the letters O and F. This hidden image is therefore visible and revealed only under certain conditions. Furthermore, the following points will be noted.
A. L’importance des caractéristiques de la première couche pour l’effet anti-UV. A. The importance of the characteristics of the first layer for the anti-UV effect.
En effet, quand celle-ci incorpore des pigments interférentiels, ceux-ci ont une forme plaquettaire qui réfléchit une partie de la lumière. Ces plaquettes sont majoritairement positionnées horizontalement dans la couche 1. Elles constituent donc en elles-mêmes une protection contre les UV. Si leur distribution est homogène dans la couche 1 , la protection est meilleure car il y a moins de zones non protégées. Indeed, when the latter incorporates interference pigments, they have a platelet shape which reflects part of the light. These plates are mainly positioned horizontally in the layer 1. They therefore constitute in themselves protection against UV. If their distribution is homogeneous in layer 1, the protection is better because there are fewer unprotected areas.
De même, si la quantité de pigments plaquettaires dans la couche 1 est augmentée (par une augmentation d’épaisseur ou de concentration), l’effet de protection est amélioré. Likewise, if the amount of platelet pigments in layer 1 is increased (by increasing thickness or concentration), the protective effect is enhanced.
B. L’intérêt d’un motif en négatif dans la troisième couche, par rapport à un motif en positif. En effet, un motif en négatif permet de conserver l’effet optiquement variable sur une surface plus importante lorsque la couche thermochromique 2 est transparente. De plus la perte d’effet thermochromique avec le temps est moins visible sur un motif en négatif. B. The value of a negative pattern in the third layer, compared to a positive pattern. Indeed, a negative pattern keeps the optically variable effect on a larger surface when the thermochromic layer 2 is transparent. In addition, the loss of thermochromic effect over time is less visible on a negative pattern.
De plus, la couche 3 est constituée de motifs imprimés (ou issus d’un procédé de métallisation/démétallisation). Ces motifs constituent une image cachée, révélée par la transparentisation de la couche 2 lorsque la température s’élève. In addition, layer 3 consists of printed patterns (or resulting from a metallization / demetallization process). These patterns constitute a hidden image, revealed by the transparency of layer 2 when the temperature rises.
Cette couche 3 est sombre. This layer 3 is dark.
Lorsque la couche 2 devient transparente avec la température lors du processus d’authentification, les zones de la couche 1 situées à l’aplomb des motifs sombres de la couche 3 présentent toujours un effet optiquement variable. Il est plus intéressant esthétiquement de conserver, lors de l’authentification, une surface optiquement variable importante, ce qui est généralement le cas lorsque le motif est imprimé en négatif. When layer 2 becomes transparent with temperature during the authentication process, the areas of layer 1 located directly above the dark patterns of layer 3 always exhibit an optically variable effect. It is aesthetically more interesting to keep, when authentication, a large optically variable surface, which is generally the case when the pattern is printed in negative.
De plus, avec un motif en négatif, si le matériau thermochromique fonctionne moins bien et devient moins opaque, moins sombre, dans le temps alors l’effet sur le caractère optiquement variable de la couche 1 est moins visible par l’utilisateur. In addition, with a negative pattern, if the thermochromic material works less well and becomes less opaque, less dark, over time then the effect on the optically variable character of layer 1 is less visible to the user.
Ci-après sont détaillés les résultats de tests de tenue lumière de la couche 2 en fonction de la nature de la couche 1 et de la nature du thermoadhésif. Pour chaque échantillon, les couches 2, 3,4 et 5 sont formées des matériaux suivants : Below are detailed the results of light resistance tests of layer 2 according to the nature of layer 1 and the nature of the thermoadhesive. For each sample, layers 2, 3, 4 and 5 are made of the following materials:
Couche 2 : formulation telle que décrite dans le Tableau 1 . Layer 2: formulation as described in Table 1.
Couche 3 : Pas de couche 3 pour ces essais labo. Layer 3: No layer 3 for these lab tests.
Couche 4 : support PET de 12pm d’épaisseur ; Couche 5 : Couches de thermoadhésif en couches externes recto et verso. Layer 4: 12 µm thick PET backing; Layer 5: Layers of thermoadhesive in outer layers front and back.
Ces tests sont réalisés selon la norme ISO 12040 modifiée comme suit : Pour chaque cycle de tests, on utilise une échelle de tissus bleus de référence avec des tenues lumière croissantes (de 1 à 8), ainsi qu’une échelle de gris externe qui permet d’évaluer la dégradation avec le temps d’exposition. These tests are carried out according to the ISO 12040 standard modified as follows: For each test cycle, a reference blue fabric scale with increasing lightfastness (from 1 to 8) is used, as well as an external gray scale which allows assess degradation over time of exposure.
Pour mesurer la solidité à la lumière (ou « solidité lumière », il faut attendre que l’éprouvette testée ait une dégradation de 3 sur l’échelle des gris puis noter quel numéro de référence bleue est aussi à 3. To measure lightfastness (or "lightfastness", wait until the test specimen has a degradation of 3 on the gray scale and then note which blue reference number is also at 3.
Par exemple, au bout de 120 heures, l’éprouvette testée est à 3 en dégradation sur l’échelle des gris. Sur l’échelle des bleus, c’est la référence 7 qui est à 3 sur l’échelle des gris. La solidité lumière est donc de 7. Une première étape de l’évaluation dite « systématique » dans la norme est réalisée, à savoir qu’on arrête le test quand le textile bleu N°3 est à 3 sur l’échelle des gris. On note alors l’éprouvette sur l’échelle des gris et on reporte le n° de l’échelle des bleus qui a la même dégradation sur l’échelle des gris. L’avantage est de connaître à l’avance la durée du test puisque l’échelle bleue se dégrade toujours à la même vitesse. Ce n’est donc pas réellement la solidité lumière telle que définie dans la norme que l’on note ici mais plutôt une évaluation visuelle de la tenue lumière (identifiée dans le tableau ci-dessous comme « Tenue lumière couche 2 - IS012040 ».
Figure imgf000017_0001
For example, at the end of 120 hours, the tested specimen is at 3 degradation on the gray scale. On the blue scale, it is reference 7 which is at 3 on the gray scale. The lightfastness is therefore 7. A first step of the so-called “systematic” evaluation in the standard is carried out, namely that the test is stopped when the blue fabric No. 3 is at 3 on the gray scale. The test piece is then noted on the gray scale and the number of the blue scale which has the same degradation on the gray scale is reported. The advantage is to know in advance the duration of the test since the blue scale always degrades at the same speed. It is therefore not really the lightfastness as defined in the standard that is noted here but rather a visual evaluation of the lightfastness (identified in the table below as "Light resistance layer 2 - IS012040".
Figure imgf000017_0001
On notera que la notation à 100% est attribuée au test présentant la meilleure notation conformément au processus expliqué plus haut. Légende du tableau ci-dessus : Note that the 100% rating is assigned to the test with the best rating in accordance with the process explained above. Legend of the table above:
Couche 1 : paillettes à base de mica recouvertes de Sn02et Ti02 ; AntiUVI : Addition d'une triazine dans la couche 5 ; Layer 1: mica-based flakes coated with Sn0 2 and Ti0 2 ; AntiUVI: Addition of a triazine in layer 5;
AntiUV2 : Addition d'une triazine (de formulation différente de la précédente dans l'adhésif. AntiUV2: Addition of a triazine (with a different formulation from the previous one in the adhesive.

Claims

REVENDICATIONS
1. Structure (S) de sécurité multicouches à usage fiduciaire, qui comporte au moins trois couches distinctes et superposées, respectivement désignées première couche supérieure (1 ), deuxième couche intermédiaire (2) et troisième couche inférieure (3), ladite première couche (1 ) étant optiquement variable, c'est-à-dire présentant des couleurs différentes selon l’angle d’observation ou d’illumination en lumière réfléchie sur fond sombre, et étant transparente ou quasi -transparente sur fond clair ; ladite deuxième couche intermédiaire (2) incorporant au moins un matériau thermochromique qui présente une première couleur sombre constituant ainsi ledit fond sombre, et est opaque dans une première gamme de températures, et devient au moins partiellement transparent à une température hors de ladite première gamme de température ; ladite troisième couche (3) étant formée d'au moins un motif (30,31 ) de couleur sombre constituant ainsi ledit fond sombre, caractérisée par le fait qu’elle comporte un matériau support (4) transparent ou translucide et que ladite première couche (1 ) forme également barrière aux rayonnements ultraviolets. 1. Multilayer security structure (S) for fiduciary use, which comprises at least three distinct and superimposed layers, respectively designated first upper layer (1), second intermediate layer (2) and third lower layer (3), said first layer ( 1) being optically variable, that is to say having different colors depending on the angle of observation or illumination in reflected light on a dark background, and being transparent or quasi-transparent on a light background; said second intermediate layer (2) incorporating at least one thermochromic material which exhibits a first dark color thus constituting said dark background, and is opaque in a first temperature range, and becomes at least partially transparent at a temperature outside said first range of temperature ; said third layer (3) being formed of at least one pattern (30,31) of dark color thus constituting said dark background, characterized in that it comprises a transparent or translucent support material (4) and that said first layer (1) also forms a barrier to ultraviolet radiation.
2. Structure (S) selon la revendication 1 , caractérisée par le fait que ladite première couche (1 ) est une couche de pigment interférentiel. 2. Structure (S) according to claim 1, characterized in that said first layer (1) is a layer of interference pigment.
3. Structure (S) selon la revendication 1 ou 2, caractérisée en ce que ladite première couche (1 ) est formée d'une première épaisseur (10) de paillettes de mica synthétique avec dépôt de SnÛ2 et T1Ό2 et d'une seconde épaisseur (11 ) d'un matériau barrière aux rayonnements ultraviolets. 3. Structure (S) according to claim 1 or 2, characterized in that said first layer (1) is formed of a first thickness (10) of synthetic mica flakes with deposition of SnO2 and T1Ό2 and of a second thickness. (11) of a barrier material to ultraviolet radiation.
4. Structure (S) selon l'une des revendications 1 à 3, caractérisée par le fait quelle comporte une autre couche incorporant au moins un matériau thermochromique, ladite troisième couche (3) étant située entre ladite deuxième couche intermédiaire (2) et ladite autre couche. 4. Structure (S) according to one of claims 1 to 3, characterized in that it comprises another layer incorporating at least one thermochromic material, said third layer (3) being located between said second intermediate layer (2) and said other layer.
5. Structure (S) selon l’une des revendications précédentes, caractérisée par le fait qu’elle comporte au moins une couche additionnelle blanche et semi-opaque. 5. Structure (S) according to one of the preceding claims, characterized in that it comprises at least one additional white and semi-opaque layer.
6. Structure (S) selon l'une des revendications 1 à 5, caractérisée par le fait quelle comporte au moins une couche additionnelle (5) constituée d'adhésif qui constitue une couche externe, c'est à dire disposée au-dessus ou au- dessous des autres couches. 6. Structure (S) according to one of claims 1 to 5, characterized in that it comprises at least one additional layer (5) formed adhesive which constitutes an outer layer, that is to say disposed above or below the other layers.
7. Structure (S) selon la revendication 6, caractérisée par le fait quelle comporte deux couches additionnelles (5) constituées d'adhésif, qui s'étendent à l'opposé l'une de l'autre. 7. Structure (S) according to claim 6, characterized in that it comprises two additional layers (5) made of adhesive, which extend opposite one another.
8. Structure (S) selon la revendication 6 ou 7, caractérisée par le fait que ledit adhésif est blanc et semi -opaque. 8. Structure (S) according to claim 6 or 7, characterized in that said adhesive is white and semi-opaque.
9. Structure (S) selon l’une des revendications 6 à 8, caractérisée par le fait que ledit adhésif est positionné sur ladite première couche (1 ) et qu’il forme une barrière aux rayonnements ultraviolets. 9. Structure (S) according to one of claims 6 to 8, characterized in that said adhesive is positioned on said first layer (1) and that it forms a barrier to ultraviolet radiation.
10. Structure (S) l'une des revendications précédentes, caractérisée par le fait que ladite première couche (1 ) incorpore des paillettes de mica synthétique avec dépôt de SnÛ2 et T1O2. 10. Structure (S) one of the preceding claims, characterized in that said first layer (1) incorporates synthetic mica flakes with deposition of SnO2 and T1O2.
11. Structure (S) selon la revendication précédente, caractérisée par le fait que lesdites paillettes de mica synthétique avec dépôt de SnÛ2 et T1O2 ont une caractéristique g ranulo métrique D50 comprise entre 10 et 30, de préférence entre 18 et 23 micromètres. 11. Structure (S) according to the preceding claim, characterized in that said synthetic mica flakes with deposit of SnO2 and T1O2 have a granulometric characteristic D50 of between 10 and 30, preferably between 18 and 23 micrometers.
12. Structure (S) selon l'une des revendications précédentes, caractérisée par le fait que ledit matériau support (4) est en matière plastique telle que du téréphtalate de polyéthylène ou du polypropylène bi -orienté. 12. Structure (S) according to one of the preceding claims, characterized in that said support material (4) is made of plastic such as polyethylene terephthalate or bi-oriented polypropylene.
13. Structure (S) selon l'une des revendications précédentes, caractérisée par le fait que ledit motif (30,31) est un motif imprimé ou un motif résultant d'une métallisation ou d'une démétallisation. 13. Structure (S) according to one of the preceding claims, characterized in that said pattern (30,31) is a printed pattern or a pattern resulting from metallization or demetallization.
14. Structure (S) selon l'une des revendications précédentes, caractérisée par le fait que ledit motif (30,31) est au moins partiellement, de préférence totalement, recouvert par ladite deuxième couche intermédiaire (2). 14. Structure (S) according to one of the preceding claims, characterized in that said pattern (30,31) is at least partially, preferably completely, covered by said second intermediate layer (2).
15. Structure (S) selon l'une des revendications précédentes, caractérisé par le fait quelle se présente sous la forme d'un bandeau (7), d'un fil de sécurité ou d'un film (8). 15. Structure (S) according to one of the preceding claims, characterized in that it is in the form of a strip (7), a security thread or a film (8).
16. Structure (S) selon l'une des revendications précédentes, caractérisée par le fait que ladite première couche (1 ) est exempte de cristaux liquides. 16. Structure (S) according to one of the preceding claims, characterized in that said first layer (1) is free from liquid crystals.
17. Document de sécurité tel qu'un billet de banque (6), caractérisé par le fait qu'il intègre au moins une structure (S) selon l'une des revendications précédentes. 17. Security document such as a banknote (6), characterized in that it incorporates at least one structure (S) according to one of the preceding claims.
18. Document de sécurité tel qu'un billet de banque (6) selon la revendication 17, qui comprend une matière plastique dont une partie constitue ledit matériau support (4) de la structure (S) selon l’une des revendications 1 à 13. 18. A security document such as a bank note (6) according to claim 17, which comprises a plastic material, a part of which constitutes said support material (4) of the structure (S) according to one of claims 1 to 13. .
PCT/EP2020/086984 2019-12-20 2020-12-18 Multi-layered security structure for fiduciary use and security document using the structure WO2021123136A1 (en)