WO2021100375A1 - 座席用表皮材、及び座席用表皮材の製造方法 - Google Patents

座席用表皮材、及び座席用表皮材の製造方法 Download PDF

Info

Publication number
WO2021100375A1
WO2021100375A1 PCT/JP2020/039038 JP2020039038W WO2021100375A1 WO 2021100375 A1 WO2021100375 A1 WO 2021100375A1 JP 2020039038 W JP2020039038 W JP 2020039038W WO 2021100375 A1 WO2021100375 A1 WO 2021100375A1
Authority
WO
WIPO (PCT)
Prior art keywords
surface layer
hole
skin material
seat skin
back surface
Prior art date
Application number
PCT/JP2020/039038
Other languages
English (en)
French (fr)
Inventor
不破　順清
Original Assignee
セーレン株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by セーレン株式会社 filed Critical セーレン株式会社
Priority to BR112022009129A priority Critical patent/BR112022009129A2/pt
Priority to US17/755,833 priority patent/US11999145B2/en
Priority to MX2022005981A priority patent/MX2022005981A/es
Priority to JP2021558223A priority patent/JPWO2021100375A1/ja
Priority to CN202080063468.9A priority patent/CN114364527A/zh
Publication of WO2021100375A1 publication Critical patent/WO2021100375A1/ja

Abstract

座席用の表皮材としての使用において蒸れ感を抑える機能を有し、且つ、意匠性が良好な座席用表皮材、及び座席用表皮材の製造方法を提供する。　表面層（１２）と、裏面層（１３）と、孔部（１５）とを備えた座席用表皮材（１１）であって、孔部（１５）の内壁が表面層（１２）により被覆されているものとする。座席用表皮材（１１）は、少なくとも表面層（１２）と裏面層（１３）とを有する基材を形成する基材形成工程と、基材を、孔部の型を備えた押し板と当該押し板と対向する受け板との間に挟み込む狭持工程と、表面層（１２）に含まれる成分が溶融しない温度で加熱しながら、押し板を受け板に押圧して基材に孔部を形成する押圧工程と、孔部が形成された基材を、押し板と受け板との間から取り出す搬出工程とを包含する製造方法によって製造される。

Description

座席用表皮材、及び座席用表皮材の製造方法
　本発明は、表面層と、裏面層と、孔部とを有する座席用表皮材、及び座席用表皮材の製造方法に関する。
　例えば、人造皮革において、使用時の蒸れ感を抑制するために、陥没穴又は貫通孔を形成したものが知られている（例えば、特許文献１を参照）。
特開２０１７－２２２９６２号公報
　特許文献１に係る人造皮革は、熱可塑性合成繊維からなる布帛に熱可塑性樹脂を付与してなるものである。このような人造皮革において、陥没穴又は貫通孔は、レーザ光線照射装置を用いてレーザ光線を人造皮革の表面に照射し、レーザ光線によって熱可塑性合成繊維と熱可塑性樹脂とを加熱することによって形成される。
　特許文献１に係る人造皮革において形成される陥没穴又は貫通孔の内壁は、レーザ光線によって加熱溶融された熱可塑性合成繊維と熱可塑性樹脂とからなる熱溶融物によって被覆されている。このため、陥没穴又は貫通孔の周りの表面層と、陥没穴又は貫通孔の内壁との質感が異なり、意匠性が良好であるとはいい難い。
　本発明は、上記の課題に鑑みてなされたものであり、座席用の表皮材としての使用において蒸れ感を抑える機能を有し、且つ、意匠性が良好な座席用表皮材、及び座席用表皮材の製造方法を提供することを目的とする。
　上記課題を解決するための本発明に係る座席用表皮材の特徴構成は、
　表面層と、裏面層と、孔部とを備えた座席用表皮材であって、
　前記孔部の内壁が前記表面層により被覆されていることにある。
　本構成の座席用表皮材によれば、座席用の表皮材としての使用において、当該座席用表皮材が備える孔部により蒸れ感を抑えることができる。また、本構成の座席用表皮材によれば、孔部の内壁が表面層その物で被覆されているので、孔部の周りの表面層と孔部の内壁との質感に統一性を持たせることができるとともに、孔部が設けられている箇所を深みのあるデザインとすることができ、意匠性が良好なものとなる。
　本発明に係る座席用表皮材において、
　前記孔部は貫通孔であり、前記裏面層における前記貫通孔の開口周縁部が前記表面層及び／又は前記裏面層に含まれる成分の融着物で構成されていることが好ましい。
　本構成の座席用表皮材によれば、孔部は貫通孔であり、裏面層における貫通孔の開口周縁部が表面層及び／又は裏面層に含まれる成分の融着物で構成されているので、貫通孔であることによって通気性に優れるとともに、貫通孔の開口周縁部が融着物によって強固に接合されることから耐久性に優れるものとなる。
　本発明に係る座席用表皮材において、
　前記孔部は陥没孔であり、当該陥没孔の底面は前記裏面層の接合面よりも深い位置に形成されていることが好ましい。
　本構成の座席用表皮材によれば、孔部は陥没孔であり、当該陥没孔の底面は裏面層の接合面よりも深い位置に形成されているので、柔軟可撓で肌触りが良く、肌身に良く馴染むようになる。
　本発明に係る座席用表皮材において、
　前記孔部は、深さによって孔径が異なるように構成されていることが好ましい。
　本構成の座席用表皮材によれば、孔部は、深さによって孔径が異なるように構成されているので、変化に富んだデザインとすることができる。
　本発明に係る座席用表皮材において、
　前記表面層と前記裏面層との間に中間層が設けられていることが好ましい。
　本構成の座席用表皮材によれば、表面層と裏面層との間に中間層が設けられているので、当該中間層により強度や耐久性が向上するとともに、表皮材全体として重厚感を持たせることができる。
　本発明に係る座席用表皮材において、
　前記裏面層がクッション材で構成されていることが好ましい。
　本構成の座席用表皮材によれば、裏面層がクッション材で構成されているので、柔軟性を高めることができるとともに、表面層の側から裏面層の側に向けて縮径するような孔部を形成し易くなる。
　本発明に係る座席用表皮材において、
　前記裏面層の下面に裏布を設けてあることが好ましい。
　本構成の座席用表皮材によれば、裏面層の下面に裏布が設けられるので、孔部を形成する際に、裏面層の破壊を防止することができる。
　本発明に係る座席用表皮材において、
　前記表面層及び前記裏面層は、共に又は互いに独立して、ポリエステル樹脂、ポリアミド樹脂、ポリアクリル樹脂、ポリオレフィン樹脂、ポリ塩化ビニル樹脂、及びポリウレタン樹脂からなる群から選択される少なくとも一つの樹脂を含むように構成されることが好ましい。
　本構成の座席用表皮材によれば、表面層及び裏面層が上記の樹脂を含むように構成されるため、孔部の内壁が表面層その物で被覆されるとともに、孔部に形成される融着物は樹脂のブレンドとなってその強度を保つことができる。
　次に、本発明に係る座席用表皮材の製造方法の特徴構成は、
　孔部を有する座席用表皮材の製造方法であって、
　少なくとも表面層と裏面層とを有する基材を形成する基材形成工程と、
　前記基材を、前記孔部の型を備えた押し板と当該押し板と対向する受け板との間に挟み込む狭持工程と、
　前記表面層に含まれる成分が溶融しない温度で加熱しながら、前記押し板を前記受け板に押圧して前記基材に前記孔部を形成する押圧工程と、
　前記孔部が形成された基材を、前記押し板と前記受け板との間から取り出す搬出工程と、
を包含することにある。
　本構成の座席用表皮材の製造方法によれば、基材形成工程によって形成された、少なくとも表面層と裏面層とを有する基材に対し、孔部の型を備えた押し板と当該押し板と対向する受け板との間に挟み込む狭持工程を実施するとともに、表面層に含まれる成分が溶融しない温度で加熱しながら、押し板を受け板に押圧して基材に孔部を形成する押圧工程を実施し、その後、孔部が形成された基材を、押し板と受け板との間から取り出す搬出工程を実施することによって座席用表皮材が製造される。このようにして製造された座席用表皮材によれば、座席用の表皮材としての使用において、当該座席用表皮材が備える孔部により蒸れ感を抑えることができる。また、本構成の座席用表皮材の製造方法によって得られた座席用表皮材によれば、孔部の内壁が表面層その物で被覆されているので、孔部の周りの表面層と孔部の内壁との質感に統一性を持たせることができるとともに、孔部が設けられている箇所を深みのあるデザインとすることができ、意匠性が良好なものとなる。
　本発明に係る座席用表皮材の製造方法において、
　前記狭持工程において、前記基材と前記受け板との間に保護シートを介挿することが好ましい。
　本構成の座席用表皮材の製造方法によれば、基材と受け板との間に保護シートが介挿されるので、孔部の型の損傷を防ぐことができる。
図１は、本発明の第一実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。 図２は、本発明の第一実施形態に係る座席用表皮材の製造方法の説明図であって、（ａ）は基材形成工程の一例を示す図、（ａ´）は基材形成工程の他の例を示す図、（ｂ）は挟持工程を示す図、（ｃ）は押圧工程を示す図、（ｄ）は搬出工程を示す図である。 図３は、本発明の第二実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。 図４は、本発明の第三実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。 図５は、本発明の第四実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。 図６は、本発明の第五実施形態に係る座席用表皮材の積層構造を模式的に示す断面図であって、（ａ）は孔部が貫通孔である場合、（ｂ）は孔部が段付き貫通孔である場合、（ｃ）は孔部が陥没孔である場合、（ｄ）は孔部が段付き陥没孔である場合である。 図７は、本発明の第六実施形態に係る座席用表皮材の積層構造を模式的に示す断面図であって、（ａ）は孔部が貫通孔である場合、（ｂ）は孔部が段付き貫通孔である場合、（ｃ）は孔部が陥没孔である場合、（ｄ）は孔部が段付き陥没孔である場合である。 図８は、本発明の第七実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。
　以下、本発明について、図１～図８を参照しながら説明する。ただし、本発明は、以下に説明する実施形態や図面に記載される構成に限定されることは意図しない。なお、各図において、座席用表皮材の積層構造における各層の厚み関係等は、実際の座席用表皮材における構造物間のサイズ関係を厳密に再現したものではなく、説明容易化のため適宜誇張してある。
　〔第一実施形態〕
　＜全体構成＞
　図１は、本発明の第一実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。図１に示されるように、第一実施形態に係る座席用表皮材１１は、表面層１２と、裏面層１３と、裏布１４とを有し、表面層１２の側から裏面層１３の側に向けて貫通孔１５（本発明の「孔部」に相当する。）が形成されている。なお、裏布１４は、設けることが好ましい構成であるが、省略することも可能である。
　＜表面層＞
　表面層１２としては、例えば、織物、編物、不織布等の布帛類、人工皮革、合成皮革、天然皮革等の皮革類等を用いることができる。
　表面層１２を構成する材料は、特に限定されるものではないが、貫通孔１５を形成する手段を考慮すると、その一部に熱可塑性樹脂を含有していることが好ましい。熱可塑性樹脂の形態についても特に限定されず、熱可塑性繊維を用いた布帛類であってもよいし、熱可塑性樹脂を含浸したり、熱可塑性樹脂を積層したりした皮革類であってもよい。
　表面層１２として、織物、編物、不織布等の布帛類、人工皮革、合成皮革、天然皮革等の皮革類を用いる場合、織物、編物、不織布等の布帛類、人工皮革と合成皮革の基材、及び合成皮革の裏布の糸条を構成する繊維（単繊維）の素材は、特に限定するものではなく、例えば、天然繊維、再生繊維、半合成繊維、合成繊維等が挙げられる。なかでも、耐久性、特には、機械的強度、耐熱性、耐光性の観点から、合成繊維が好ましく、合成繊維のなかでもポリエステルが好ましく、ポリエチレンテレフタレート、又はポリエチレンテレフタレートを一成分とする複合繊維がさらに好ましい。なお、織物の組織は、特に限定されるものではなく、例えば、三元組織である平織、斜文織、朱子織、これら三元組織の変化組織、なし地織等の特別組織、さらにこれらを２種以上組み合わせた混合組織等を挙げることができる。
　また、表面層１２として編物を用いる場合、例えば、丸編、横編などの緯編、トリコット編、ラッセル編、及びミラニーズ編などの経編などが挙げられるが、編物の種類は特に限定されない。
　表面層１２として不織布を用いる場合、例えば、ポリエステル系、ポリアミド系、ポリアクリル系、ポリオレフィン系等の合成樹脂製長繊維フィラメント又は短繊維（ステープル）が高密度、且つ無方向に堆積接合されたものが好ましく、これらの合成樹脂には、撥水剤、耐熱向上剤、酸化防止剤、難燃剤などを含有させてもよい。
　表面層１２として人工皮革を用いる場合、例えば、不織布、織物、編物等からなる基布に、合成樹脂（ポリ塩化ビニル樹脂、ポリウレタン樹脂など）溶液を含浸させ、起毛加工やエンボス加工などをして、スエードやヌバックなどの皮革に似せて仕上げたものが挙げられる。
　表面層１２として合成皮革を用いる場合、例えば、織物、編物、不織布等からなる基布の上に合成樹脂（ポリ塩化ビニル樹脂、ポリウレタン樹脂等）を積層し、エンボス加工やもみ加工などをして、皮革に似せて仕上げたものが挙げられる。なお、合成皮革は、湿式法、乾式法いずれの方法で形成してもよい。
　表面層１２として天然皮革を用いる場合、例えば、牛、馬、豚、山羊、羊、鹿、カンガルー等の哺乳類革、ダチョウ等の鳥類革、ウミガメ、オオトカゲ、ニシキヘビ、ワニ等の爬虫類革など従来公知の天然皮革を挙げることができる。なかでも、汎用性が高く、面積が大きく、厚さのある牛革が好ましい。また、動物の皮（原皮）を鞣して、耐久性（耐熱性、耐腐敗性、耐薬品性など）を付与するとともに、革らしさを引き出した「本革」、すなわち、従来公知の製革工程（鞣し工程、染色工程、仕上げ工程）を施したものを用いることが好ましい。
　表面層１２の厚さは、特に限定されるものではないが、貫通孔１５を形成し易いという観点から、２０ｍｍ以下であることが好ましい。また、表面層１２の側から裏面層１３の側に向けて縮径する貫通孔１５を形成し易いという観点から、０．３ｍｍ以上であることが好ましい。
　＜裏面層＞
　裏面層１３を構成する材料としては、表面層１２と同等のものを使用することができる。また、裏面層１３は、例えば、クッション材で構成されることが好ましい。裏面層１３をクッション材で構成することにより、着座感、及び触感が向上する。
　表面層１２に対しクッション材（裏面層１３）を一体化する方法としては、特に限定されるものではないが、例えば、接着剤を用いる方法、フレームラミネートによる方法等を挙げることができる。工程負荷や軽量化の観点から、フレームラミネートによる方法が好ましい。表面層１２と裏面層１３とを積層シートとして一体化する場合、積層シートの厚さは、１．３～３０ｍｍとするのが好ましい。積層シートにおいて、裏面層１３としてクッション材を用いる場合、クッション材の厚さは、１．０～１０ｍｍであることが好ましい。
　クッション材の材料としては、特に限定されるものではなく、ポリウレタンフォーム等の合成樹脂発泡体、立体織物、立体編物、不織布等の布帛類等が挙げられる。表面層１２の側から裏面層１３の側に向けて縮径する貫通孔１５を形成し易いという観点から、合成樹脂発泡体が好ましく、汎用性の観点からポリウレタンフォームシートが好ましい。
　表面層１２に使用される樹脂と、裏面層１３に使用される樹脂とは、共に同種のものが選択されてもよいし、互いに独立して異種のものが選択されてもよい。表面層１２及び裏面層１３に適切な樹脂を使用することで、後述する貫通孔１５の内壁が表面層１２その物で被覆されるとともに、貫通孔１５の開口周縁部に形成される融着物１６は樹脂のブレンドとなってその強度を保つことができる。
　＜裏布＞
　裏面層１３の下面には、貫通孔１５の形成時の裏面層１３（クッション材）の破損防止等の観点から、裏布１４を設けることが好ましい。裏布１４としては、特に限定されるものではなく、例えば、ポリエステル等の合成繊維からなる布帛が挙げられる。また、貫通孔１５を形成する際の積層シートの打抜片を効率的に除去できるという観点から、低融点の繊維を用いた布帛を用いることが好ましい。なお、裏面層１３の上面と下面とについて、表面層１２と接触する側の面が上面であり、表面層１２と接触する側の面の反対側の面が下面である。
　＜貫通孔＞
　貫通孔１５は、表面層１２の側から裏面層１３の側に向けて縮径し、深さによって孔径が異なるように構成されている。このような貫通孔１５は、深みのあるデザインとなり、意匠性が向上する。
　貫通孔１５の内壁は、表面層１２その物によって被覆されている。つまり、特許文献１に係る人造皮革では熱溶融物で貫通孔の内壁が被覆されているが、これとは異なり、貫通孔１５の内壁は、表面層１２のみで被覆されている。裏面層１３における貫通孔１５の開口周縁部は、表面層１２、裏面層１３及び裏布１４の１種以上（本例では３種全て）に含まれる成分の融着物１６で構成されている。こうして、貫通孔１５であることによって通気性に優れるとともに、貫通孔１５の開口周縁部が融着物１６によって強固に接合されていることから開口周縁部がほつれ難く耐久性に優れる座席用表皮材１１を得ることができる。
　貫通孔１５を形成する方法としては、特に限定されず、表面層１２の側から裏面層１３の側に向けて押し付けすることによって貫通孔１５が形成される後述の型押部１７（本発明の「孔部の型」に相当する）を用いて表面層１２の側から裏面層１３の側に向けて押圧することにより、貫通孔１５の開口周縁部が、表面層１２、裏面層１３及び裏布１４の１種以上（本例では３種全て）に含まれる成分の融着物１６によって強固に接合されるものであればよい。例えば、加熱穿孔法、エンボス加工法、ウェルダー加工法等を挙げることができる。なかでも、加工安定性及びコストの観点からエンボス加工法が好ましく、座席用表皮材の表面に不必要な熱が当たることを防止する観点からウェルダー加工法が好ましく、目的に応じて何れかを選択すればよい。
　エンボス加工法としては、ロールエンボス加工法、平板エンボス加工法のいずれも採用できる。エンボス加工法においては、後述の型押部１７を有するエンボスロール（押し板８０）と、受けロール（受け板８１）との間に、少なくとも表面層１２と裏面層１３とが積層された積層シートを通し、エンボスロール（押し板８０）と受けロール（受け板８１）とで加熱押圧して、貫通孔１５を形成する。
　＜座席用表皮材の製造方法＞
　次に、起毛又はバフ処理が施されたポリエステル織物によって表面層１２が形成され、ポリウレタンフォームシートによって裏面層１３が形成され、ポリエステル編物によって裏布１４が形成される座席用表皮材１１をエンボス加工法（平板エンボス加工法）によって製造する方法について説明する。なお、この製造方法の説明において例示する、表面層１２、裏面層１３、及び裏布１４のそれぞれの構成材については、一例を挙げたにすぎず、ここで挙げた構成材に限定されるものではない。また、裏布１４は省略される場合がある。
　図２は、本発明の第一実施形態に係る座席用表皮材の製造方法の説明図であって、（ａ）は基材形成工程の一例を示す図、（ａ´）は基材形成工程の他の例を示す図、（ｂ）は挟持工程を示す図、（ｃ）は押圧工程を示す図、（ｄ）は搬出工程を示す図である。
　［基材形成工程］
　まず、図２（ａ）に示されるように、第一ドラム９１から、表面層１２を構成するポリエステル織物シートを繰り出し、第二ドラム９２から、裏面層１３を構成するポリウレタンフォームシートを繰り出し、ポリウレタンフォームシートの表面を加熱手段（本例ではバーナー９３を例示する）で加熱し、ポリウレタンフォームシートの表面が溶融したところにポリエステル織物シートを貼り合わせるように一対のピンチロール９４，９５で挟みながら下流側へと送り、ポリエステル織物シートとポリウレタンフォームシートとが重ね合わされて溶着された二層シート（積層シート）を巻取りロール９６で巻き取る。二層シートを巻き取った巻取りロール９６は、第二ドラム９２としてセットする。第一ドラム９１に裏布１４を構成するポリエステル編物シートをセットした後、これを繰り出しながら、第二ドラム９２から、二層シートを繰り出し、二層シートにおけるポリウレタンフォームシートの表面を加熱手段で加熱し、ポリウレタンフォームシートの表面が溶融したところにポリエステル編物シートを貼り合わせるように一対のピンチロール９４，９５で挟みながら下流側へと送り、ポリエステル織物シート、ポリウレタンフォームシート、及びポリエステル編物シートが重ね合わされて溶着された三層シートを座席用表皮材の基材７０として巻取りロール９６で巻き取る。
　基材形成工程の他の例としては、図２（ａ´）に示されるようなものもある。図２（ａ´）に示されるように、図示されない第一ドラムから、裏面層１３を構成するポリウレタンフォームシートを繰り出し、図示されない第二ドラムから、裏布１４を構成するポリエステル編物シートを繰り出す。ポリウレタンフォームシートの表面を加熱手段（バーナー９３）で加熱し、ポリウレタンフォームシートの表面が溶融したところにポリエステル編物シートを貼り合わせるようにピンチロール９７，９８で挟みながら下流側へと送る。ポリエステル編物シートとポリウレタンフォームシートとが重ね合わされて溶着された二層シート（積層シート）におけるポリウレタンフォームシートの表面を加熱手段（バーナー９３´）で加熱し、ポリウレタンフォームシートの表面が溶融したところに、図示されない第三ドラムから繰り出される、表面層１２を構成するポリエステル織物シートを貼り合せるようにピンチロール９８，９９で挟みながら下流側へと送る。そして、ポリエステル織物シート、ポリウレタンフォームシート、及びポリエステル編物シートが重ね合わされて溶着された三層シートを座席用表皮材の基材７０として図示されない巻取りロールで巻き取る。
　［挟持工程］
　次いで、図２（ｂ）に示されるように、上記の基材形成工程にて形成された基材７０を、貫通孔１５を形成するための型押部１７が基板１８に立設されて構成される押し板８０と、当該押し板８０と対向する受け板８１との間に挟み込む。このとき、基材７０と受け板８１との間に保護シート８２が介挿されるように、受け板８１上に保護シート８２を予め載置しておくことが好ましい。
　ここで、型押部１７の形状については、特に限定されず、所望の形状でよいが、貫通孔１５を形成しやすいという観点から、型押部１７は錐台状であることが好ましい。また、同様の理由により、型押部１７の頂面が円形であることが好ましく、さらに好ましくは型押部１７の頂面の周縁以外（頂面の内側）が凹部となっていることが好ましい。型押部１７の頂面は斜面としてもよい（片刃の断面のような形状）。これにより、基材７０に型押部１７が入り込みやすくなり、貫通孔１５の形成が容易になる。また、型押部１７は、型押部１７の頂面にさらにパンチング用のピンを設けた形状としてもよい。ピンを設けることにより、貫通孔１５の形成が容易になる。さらに、後述する押圧工程にて型押部１７が基材７０を厚み方向に押込むため、貫通孔１５の内壁をポリエステル織物シートからなる表面層１２で形成することが容易になる。
　エンボス加工法に用いる受け板８１の形状は、平滑板状でもよいし、型押部１７に対応した凹部を形成（所謂雄雌型）としてもよい。押し板８０や受け板８１の形状は、上述の形状を適宜組合せて用いることができる。
　保護シート８２は、型押部１７の損傷を防いだり、貫通孔１５を形成する際の打抜片（図示省略）を効率的に除去したり、貫通孔１５の形成を容易にしたりするために設けられるものである。保護シート８２としては、特に限定されるものではなく、例えば、紙、フィルム、織物、編物、不織布等が挙げられる。なかでも、打抜片を効率的に除去できるという観点から、織物、編物、不織布、特には、低融点の繊維からなる織物、編物、不織布が好ましく、貫通孔１５の形成を容易にするという観点から、紙が好ましい。
　［押圧工程］
　次いで、図２（ｃ）に示されるように、表面層１２を構成するポリエステル織物シートが溶融しない温度で受け板８１を図示されない電熱線で加熱しながら、押し板８０を受け板８１に近づけるように相対移動させ、押し板８０の型押部１７を受け板８１に押圧して基材７０に貫通孔１５を形成する。なお、裏面層１３を構成するポリウレタンフォームシートは、表面層１２を構成するポリエステル織物シートよりも熱によって軟化し易い。このため、座席用表皮材１１においては、図１及び図２（ｄ）に示されるように、裏面層１３と共に裏布１４が表面層１２側に引き上げられて、当該座席用表皮材１１の裏面は上凸円弧状に湾曲する（後述する図３～図８に示される第二実施形態乃至第七実施形態についても同様）。
　［搬出工程］
　次いで、図２（ｄ）に示されるように、受け板８１から押し板８０を引き離すように押し板８０を相対移動させ、貫通孔１５が形成された基材７０を、押し板８０と受け板８１との間から取り出す。こうして、貫通孔１５を有する座席用表皮材１１を製造することができる。
　上記の製造方法により製造された座席用表皮材１１においては、表面層１２の側から裏面層１３の側に向けて貫通孔１５が形成されているので、通気性を格段に向上させることができ、座席用の表皮材としての使用において、当該座席用表皮材１１が備える貫通孔１５により蒸れ感を確実に抑えることができる。また、上記の製造方法により製造された座席用表皮材１１においては、貫通孔１５の内壁が表面層１２その物で被覆されているので、貫通孔１５の周りの表面層１２と貫通孔１５の内壁との質感に統一性を持たせることができるとともに、貫通孔１５が設けられている箇所を深みのあるデザインとすることができ、意匠性が良好なものとなる。
　〔第二実施形態〕
　図３は、本発明の第二実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。第二実施形態において、第一実施形態と同一又は同様のものについては図に同一符号を付すに留めてその詳細な説明を省略することとし、以下においては、第二実施形態に特有の部分を中心に説明することとする（後述する第三実施形態乃至第七実施形態についても同様）。
　図３に示される第二実施形態に係る座席用表皮材２１において、貫通孔２５の内壁は、表面層１２の側から裏面層１３の側に向かう途中に形成される円環状の段面２６を有し、段面２６を境にして孔径が大きく変化するように構成されている。
　第二実施形態の座席用表皮材２１によれば、第一実施形態の座席用表皮材１１と同様の作用効果を得ることができるのは勿論のこと、深みのあるデザインとすることができる。なお、ここでは、貫通孔２５の内壁に段面２６を１つだけ設ける例を示したが、段面２６を複数設けて、深さによって孔径が複数段階で変化するようにしてもよい。
　第二実施形態に係る座席用表皮材２１の製造方法については、第一実施形態に係る座席用表皮材１１の製造方法において用いられる型押部１７に代えて、段面２６を形成するための段部を有する型押部２７が用いられること以外は第一実施形態に係る座席用表皮材１１の製造方法と同じである。
　〔第三実施形態〕
　図４は、本発明の第三実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。図４に示される第三実施形態に係る座席用表皮材３１においては、表面層１２の側から裏面層１３の側に向けて陥没孔３５（本発明の「孔部」に相当する。）が形成されている。陥没孔３５の内壁は、表面層１２その物で被覆されている。つまり、特許文献１に係る人造皮革では熱溶融物で貫通孔の内壁が被覆されているが、これとは異なり、陥没孔３５の内壁は、表面層１２のみで被覆されている。また、陥没孔３５の底面は、裏面層１３の接合面よりも深い位置に形成されている。これにより、柔軟可撓で肌触りが良く、肌身に良く馴染むようにすることができる。なお、座席用表皮材３１において、陥没孔３５を形成する場合、裏布１４は溶融しない。このため、陥没孔３５の底部下方における表面層１２と裏面層１３とは、表面層１２及び／又は裏面層１３（本例では表面層１２及び裏面層１３の両方）に含まれる成分の融着物１１６によって接合されている。
　第三実施形態に係る座席用表皮材３１の製造方法については、第一実施形態に係る座席用表皮材１１の製造方法において用いられる型押部１７に代えて、陥没孔３５を形成するために先端部に丸みを持たせた型押部３７が用いられること以外は第一実施形態に係る座席用表皮材１１の製造方法と同じである。
　第三実施形態の座席用表皮材３１によれば、表面層１２の側から裏面層１３の側に向けて陥没孔３５が形成されているので、座席用の表皮材としての使用において、当該座席用表皮材３１が備える陥没孔３５により蒸れ感を抑えることができる。また、陥没孔３５の内壁は、表面層１２その物で被覆されている。従って、陥没孔３５の周りの表面層１２と陥没孔３５の内壁との質感に統一性を持たせることができるとともに、陥没孔３５が設けられている箇所を深みのあるデザインとすることができ、意匠性が良好なものとなる。
　〔第四実施形態〕
　図５は、本発明の第四実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。図５に示される第四実施形態に係る座席用表皮材４１において、陥没孔４５の内壁は、表面層１２の側から裏面層１３の側に向かう途中に形成される円環状の段面４６を有し、段面４６を境にして孔径が大きく変化するように構成されている。なお、座席用表皮材４１において、陥没孔４５を形成する場合、裏布１４は溶融しない。このため、陥没孔４５の底部下方における表面層１２と裏面層１３とは、表面層１２及び／又は裏面層１３（本例では表面層１２及び裏面層１３の両方）に含まれる成分の融着物１１６によって接合されている。
　第四実施形態の座席用表皮材４１によっても、第三実施形態の座席用表皮材３１と同様の作用効果を得ることができるのは勿論のこと、デザイン上の深みにアクセントを設けることができる。なお、ここでは、陥没孔４５の内壁に段面４６を１つだけ設ける例を示したが、段面４６を複数設けて、深さによって孔径が複数段階で変化するようにしてもよい。
　第四実施形態に係る座席用表皮材４１の製造方法については、第一実施形態に係る座席用表皮材１１の製造方法において用いられる型押部１７に代えて、陥没孔４５を形成するために先端部に丸みを持たせ、且つ段面４６を形成するための段部を有する型押部４７が用いられること以外は第一実施形態に係る座席用表皮材１１の製造方法と同じである。
　〔第五実施形態〕
　図６は、本発明の第五実施形態に係る座席用表皮材の積層構造を模式的に示す断面図で、（ａ）は孔部が貫通孔である場合、（ｂ）は孔部が段付き貫通孔である場合、（ｃ）は孔部が陥没孔である場合、（ｄ）は孔部が段付き陥没孔である場合である。図６（ａ）～（ｄ）に示されるように、第五実施形態に係る座席用表皮材５１Ａ～５１Ｄは、表面層（表面組織）１１２に編み込まれた図示されない接結糸と、裏面層（裏面組織）１１３に編み込まれた図示されない接結糸とが互いに交絡することにより、表面層１１２と裏面層１１３とが接結されてなるダブルラッセル経編地を用いたものである。これら座席用表皮材５１Ａ～５１Ｄにおいては、表面層１１２の側から裏面層１１３の側に向けて貫通孔５５Ａ（図６（ａ）参照）、及び段付き貫通孔５５Ｂ（図６（ｂ）参照）、並びに陥没孔５５Ｃ（図６（ｃ）参照）、及び段付き陥没孔５５Ｄ（図６（ｄ）参照）が形成されている。なお、座席用表皮材５１Ａ，５１Ｂにおいて、裏面層１１３における貫通孔５５Ａ，５５Ｂの開口周縁部は、表面層１１２、裏面層１１３、及び接結糸の１種以上（本例では３種全て）に含まれる成分の融着物２１６によって接合されている。また、座席用表皮材５１Ｃ，５１Ｄにおいて、陥没孔５５Ｃ，５５Ｄの底部下方における表面層１１２と裏面層１１３とは、表面層１１２、裏面層１１３、及び接結糸の１種以上（本例では接結糸）に含まれる成分の融着物３１６によって接合されている。
　第五実施形態の座席用表皮材５１Ａ～５１Ｄにおいても、表面層１１２の側から裏面層１１３の側に向けて貫通孔５５Ａ，５５Ｂ、及び陥没孔５５Ｃ，５５Ｄが形成されているので、通気性を向上させることができ、座席用の表皮材としての使用において、当該座席用表皮材５１Ａ～５１Ｄが備える貫通孔５５Ａ，５５Ｂ、及び陥没孔５５Ｃ，５５Ｄにより蒸れ感を抑えることができる。また、貫通孔５５Ａ，５５Ｂ、及び陥没孔５５Ｃ，５５Ｄの各々の内壁は、表面層１１２その物で被覆されている。従って、貫通孔５５Ａ，５５Ｂ、及び陥没孔５５Ｃ，５５Ｄの周りの表面層１１２と貫通孔５５Ａ，５５Ｂ、及び陥没孔５５Ｃ，５５Ｄの内壁との質感に統一性を持たせることができるとともに、貫通孔５５Ａ，５５Ｂ、及び陥没孔５５Ｃ，５５Ｄが設けられている箇所を深みのあるデザインとすることができ、意匠性が良好なものとなる。
　第五実施形態に係る座席用表皮材５１Ａ～５１Ｄの製造方法については、第一実施形態に係る座席用表皮材１１の製造方法において用いられる型押部１７に代えて、貫通孔５５Ａ，５５Ｂ、及び陥没孔５５Ｃ，５５Ｄを形成するのに適した形状等を備えた型押部５７Ａ～５７Ｄが用いられること以外は第一実施形態に係る座席用表皮材１１の製造方法と同じである。
　〔第六実施形態〕
　図７は、本発明の座席用表皮材の第六実施形態の説明図である。図７（ａ）～（ｄ）に示される座席用表皮材６１Ａ，６１Ｂ，６１Ｃ，６１Ｄは、第一実施形態乃至第四実施形態の座席用表皮材１１，２１，３１，４１において、表面層１２と裏面層１３との間に中間層２００を設けるようにしたものである。こうして、中間層２００を設けることにより、重厚感を持たせることができる。中間層２００としては、例えば、織物、編物、不織布等の布帛類等や、ポリウレタンフォーム等の合成樹脂発泡体を用いることができる。なお、座席用表皮材６１Ａ，６１Ｂにおいて、裏面層１３における貫通孔１５，２５の開口周縁部は、表面層１２、中間層２００、裏面層１３、及び裏布１４の１種以上（本例では４種全て）に含まれる成分の融着物４１６によって接合されている。また、座席用表皮材６１Ｃ，６１Ｄにおいて、陥没孔３５，４５を形成する場合、裏布１４は溶融しない。このため、陥没孔３５，４５の底部下方における表面層１２と中間層２００と裏面層１３とは、表面層１２、中間層２００、及び裏面層１３の１種以上（本例では３種全て）に含まれる成分の融着物５１６によって接合されている。
　上記の第一～第六実施形態においては、表面層１２の側から裏面層１３の側に向けて孔部（貫通孔、陥没孔）が形成された例を示したが、これに限定されるものではなく、裏面層１３の側から表面層１２の側に向けて孔部（貫通孔、陥没孔）が形成される態様例もある。
　〔第七実施形態〕
　図８は、本発明の第七実施形態に係る座席用表皮材の積層構造を模式的に示す断面図である。図８に示される第七実施形態に係る座席用表皮材７１においては、貫通孔７５の内壁が、表面層１２で被覆された部分だけでなく、裏面層１３や裏布１４等が露出した部分が存在している。このような構造となるケースとしては、例えば、裏面からの孔開け加工の場合や、表面層１２の加熱押圧によるダメージを防ぐために加熱押圧の条件を弱くした場合などが挙げられる。この場合、表面層１２及び／又は裏面層１３に含まれる成分の融着物が必ずしも存在するとは限らない。このような第七実施形態の座席用表皮材７１によっても、当該座席用表皮材７１が備える貫通孔７５により蒸れ感を抑えることができるとともに、意匠性や耐久性を向上することできる。なお、第七実施形態に係る座席用表皮材７１の製造に際しては、貫通孔７５を形成するのに適した形状の型押部７７が用いられる。
　以上、本発明の座席用表皮材、及び座席用表皮材の製造方法について、複数の実施形態に基づいて説明したが、本発明は上記実施形態に記載した構成に限定されるものではなく、各実施形態に記載した構成を適宜組み合わせる等、その趣旨を逸脱しない範囲において適宜その構成を変更することができるものである。具体的な別実施形態は以下のとおりである。
　〔別実施形態〕
　上記の実施形態においては、エンボス加工法（平板エンボス加工法）により座席用表皮材１１，２１，３１，４１，５１Ａ～５１Ｄ，６１Ａ～６１Ｄ，７１を製造する例を示したが、ウェルダー加工法により座席用表皮材１１，２１，３１，４１，５１Ａ～５１Ｄ，６１Ａ～６１Ｄ，７１を製造することもできる。図示による詳細説明は省略するが、ウェルダー加工法においては、型押部１７，２７，３７，４７，５７Ａ～５７Ｄを取り付けた可動定盤と、固定定盤上の絶縁紙との間に、基材７０を通し、高周波により加熱された型押部１７，２７，３７，４７，５７Ａ～５７Ｄによって、基材７０を加熱押圧することで貫通孔１５，２５，５５Ａ，５５Ｂ、又は陥没孔３５，４５，５５Ｃ，５５Ｄを形成する。ウェルダー加工法に用いられる型押部１７，２７，３７，４７，５７Ａ～５７Ｄの形状については、エンボス加工法と同様の形状を用いることができる。ウェルダー加工法に用いられる絶縁紙としては、例えば、シリコーンシート、テフロン（登録商標）シート、ベークライト板、紙等が挙げられ、これらを単独、又は組み合わせて使用することができる。なかでも、貫通孔１５，２５，５５Ａ，５５Ｂの形成し易さの観点から、紙を用いることが好ましい。なお、ウェルダー加工法においても、上記のエンボス加工法と同様に、型押部の損傷を防いだり、貫通孔を形成する際の打抜片を効率的に除去したり、貫通孔の形成を容易にしたりするために、保護シート（例えば、フィルム等）を併せて用いることもある。
　本発明の座席用表皮材は、例えば車両内装材や椅子張り地において利用可能である。
　１１，２１，３１，４１　　　　　　座席用表皮材
　５１Ａ～５１Ｄ　　　　　　　　　　座席用表皮材
　６１Ａ～６１Ｄ　　　　　　　　　　座席用表皮材
　７１　　　　　　　　　　　　　　　座席用表皮材
　１２　　　　　　　　　　　　　　　表面層
　１３　　　　　　　　　　　　　　　裏面層
　１４　　　　　　　　　　　　　　　裏布
　１５，２５，５５Ａ，５５Ｂ，７５　貫通孔（孔部）
　１６，１１６，２１６　　　　　　　融着物
　３１６，４１６，５１６　　　　　　融着物
　１７，２７，５７Ａ，５７Ｂ，７７　型押部（孔部の型）
　１８　　　　　　　　　　　　　　　基板
　２６，４６　　　　　　　　　　　　円環状の段面
　３５，４５，５５Ｃ，５５Ｄ　　　　陥没孔（孔部）
　３７，４７，５７Ｃ，５７Ｄ　　　　型押部（孔部の型）
　７０　　　　　　　　　　　　　　　基材
　８０　　　　　　　　　　　　　　　押し板
　８１　　　　　　　　　　　　　　　受け板
　８２　　　　　　　　　　　　　　　保護シート
　９１　　　　　　　　　　　　　　　第一ドラム
　９２　　　　　　　　　　　　　　　第二ドラム
　９３，９３´　　　　　　　　　　　バーナー
　９４，９５　　　　　　　　　　　　ピンチロール
　９６　　　　　　　　　　　　　　　巻き取りロール
　９７，９８，９９　　　　　　　　　ピンチロール
　１１２　　　　　　　　　　　　　　表面層（表面組織）
　１１３　　　　　　　　　　　　　　裏面層（裏面組織）
　２００　　　　　　　　　　　　　　中間層

Claims (10)

  1. 　表面層と、裏面層と、孔部とを備えた座席用表皮材であって、
    　前記孔部の内壁が前記表面層により被覆されている座席用表皮材。
  2. 　前記孔部は貫通孔であり、前記裏面層における前記貫通孔の開口周縁部が前記表面層及び／又は前記裏面層に含まれる成分の融着物で構成されている請求項１に記載の座席用表皮材。
  3. 　前記孔部は陥没孔であり、当該陥没孔の底面は前記裏面層の接合面よりも深い位置に形成されている請求項１に記載の座席用表皮材。
  4. 　前記孔部は、深さによって孔径が異なるように構成されている請求項１～３の何れか一項に記載の座席用表皮材。
  5. 　前記表面層と前記裏面層との間に中間層が設けられている請求項１～４の何れか一項に記載の座席用表皮材。
  6. 　前記裏面層がクッション材で構成されている請求項１～５の何れか一項に記載の座席用表皮材。
  7. 　前記裏面層の下面に裏布を設けてある請求項１～６の何れか一項に記載の座席用表皮材。
  8. 　前記表面層及び前記裏面層は、共に又は互いに独立して、ポリエステル樹脂、ポリアミド樹脂、ポリアクリル樹脂、ポリオレフィン樹脂、ポリ塩化ビニル樹脂、及びポリウレタン樹脂からなる群から選択される少なくとも一つの樹脂を含むように構成される請求項１～７の何れか一項に記載の座席用表皮材。
  9. 　孔部を有する座席用表皮材の製造方法であって、
    　少なくとも表面層と裏面層とを有する基材を形成する基材形成工程と、
    　前記基材を、前記孔部の型を備えた押し板と当該押し板と対向する受け板との間に挟み込む狭持工程と、
    　前記表面層に含まれる成分が溶融しない温度で加熱しながら、前記押し板を前記受け板に押圧して前記基材に前記孔部を形成する押圧工程と、
    　前記孔部が形成された基材を、前記押し板と前記受け板との間から取り出す搬出工程と、
    を包含する座席用表皮材の製造方法。
  10. 　前記狭持工程において、前記基材と前記受け板との間に保護シートを介挿する請求項９に記載の座席用表皮材の製造方法。
PCT/JP2020/039038 2019-11-18 2020-10-16 座席用表皮材、及び座席用表皮材の製造方法 WO2021100375A1 (ja)