WO2021077209A1 - Aluminum alloy with improved extrudability and corrosion resistance - Google Patents
Aluminum alloy with improved extrudability and corrosion resistance Download PDFInfo
- Publication number
- WO2021077209A1 WO2021077209A1 PCT/CA2020/051370 CA2020051370W WO2021077209A1 WO 2021077209 A1 WO2021077209 A1 WO 2021077209A1 CA 2020051370 W CA2020051370 W CA 2020051370W WO 2021077209 A1 WO2021077209 A1 WO 2021077209A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- extruded
- aluminum alloy
- brazed
- product
- alloy comprises
- Prior art date
Abstract
Description
Claims