WO2021019258A1 - Substrat revêtu et trempable - Google Patents

Substrat revêtu et trempable Download PDF

Info

Publication number
WO2021019258A1
WO2021019258A1 PCT/GB2020/051856 GB2020051856W WO2021019258A1 WO 2021019258 A1 WO2021019258 A1 WO 2021019258A1 GB 2020051856 W GB2020051856 W GB 2020051856W WO 2021019258 A1 WO2021019258 A1 WO 2021019258A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
coated
toughenable
glass substrate
layers
Prior art date
Application number
PCT/GB2020/051856
Other languages
English (en)
Inventor
John William OLDFIELD
Original Assignee
Pilkington Group Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pilkington Group Limited filed Critical Pilkington Group Limited
Priority to EP20751653.5A priority Critical patent/EP4007743A1/fr
Publication of WO2021019258A1 publication Critical patent/WO2021019258A1/fr

Abstract

La présente invention concerne un substrat en verre flotté revêtu et trempable, son procédé de préparation et son utilisation, ledit substrat en verre flotté comprenant une première surface et une seconde surface, au moins une première surface du substrat en verre revêtu étant revêtue d'une ou de plusieurs couches appliquées par dépôt physique en phase vapeur (PVD) ; et ladite ou lesdites couches étant appliquées par dépôt physique en phase vapeur (PVD) comprennent au moins une couche métallique fonctionnelle ; et au moins une couche absorbante à base de Ti, V, Cr, Fe, ou W, Ni Nb, et leurs alliages et des nitrures ; et la seconde surface comprenant en outre au moins une couche protectrice appliquée en contact direct avec la seconde surface du substrat en verre avant le dépôt de la ou des couches appliquées par dépôt physique en phase vapeur (PVD), et le substrat en verre flotté revêtu présentant une valeur de couleur de transmission selon l'espace colorimétrique CIE inférieure ou égale à 3 et une réflexion côté verre inférieure ou égale à -4.
PCT/GB2020/051856 2019-08-01 2020-07-31 Substrat revêtu et trempable WO2021019258A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP20751653.5A EP4007743A1 (fr) 2019-08-01 2020-07-31 Substrat revêtu et trempable

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GBGB1910976.8A GB201910976D0 (en) 2019-08-01 2019-08-01 Toughenable coated substrate
GB1910976.8 2019-08-01

Publications (1)

Publication Number Publication Date
WO2021019258A1 true WO2021019258A1 (fr) 2021-02-04

Family

ID=67990714

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2020/051856 WO2021019258A1 (fr) 2019-08-01 2020-07-31 Substrat revêtu et trempable

Country Status (3)

Country Link
EP (1) EP4007743A1 (fr)
GB (1) GB201910976D0 (fr)
WO (1) WO2021019258A1 (fr)

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10146687C1 (de) 2001-09-21 2003-06-26 Flabeg Solarglas Gmbh & Co Kg Glas mit einer porösen Antireflex-Oberflächenbeschichtung sowie Verfahren zur Herstellung des Glases und Verwendung eines derartigen Glases
EP1328483A1 (fr) 2000-10-18 2003-07-23 Flabeg Solarglas GmbH & Co. KG Verre trempe thermiquement pourvu d'une couche antireflet en sio2, poreuse et resistante a l'usure
EP1429997A1 (fr) 2001-09-21 2004-06-23 MERCK PATENT GmbH Nouveau sol hybride pour la realisation de couches antireflets sio 2 resistantes a l'usure
WO2004063111A1 (fr) 2003-01-09 2004-07-29 Guardian Industries Corp. Article enrobe pouvant subir un traitement thermique, presentant une couche reflechissant les infrarouges (ir) comprenant du nitrure de niobium, et son procede de fabrication
WO2004108619A1 (fr) * 2003-06-06 2004-12-16 Pilkington Plc Verre a couche
US6918957B2 (en) 2000-10-18 2005-07-19 Merck Patent Gmbh Aqueous coating solution for abrasion-resistant SiO2 antireflection layers
WO2006124503A2 (fr) * 2005-05-12 2006-11-23 Agc Flat Glass North America, Inc. Revetement a faible emissivite presentant un faible coefficient d'apport par rayonnement solaire, des proprietes chimiques et mecaniques ameliorees et procede de fabrication associe
WO2008075107A1 (fr) * 2006-12-21 2008-06-26 Pilkington Group Limited Plaques de verre à couches et leur procédé de fabrication
WO2010142926A1 (fr) * 2009-06-12 2010-12-16 Saint-Gobain Glass France Procede de depot de couche mince et produit obtenu
GB2518899A (en) * 2013-10-07 2015-04-08 Pilkington Group Ltd Heat treatable coated glass pane
WO2019097192A1 (fr) * 2017-11-20 2019-05-23 Saint-Gobain Glass France Materiau comprenant une seule couche fonctionnelle a base d'argent et une couche absorbante

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1328483A1 (fr) 2000-10-18 2003-07-23 Flabeg Solarglas GmbH & Co. KG Verre trempe thermiquement pourvu d'une couche antireflet en sio2, poreuse et resistante a l'usure
US6918957B2 (en) 2000-10-18 2005-07-19 Merck Patent Gmbh Aqueous coating solution for abrasion-resistant SiO2 antireflection layers
DE10146687C1 (de) 2001-09-21 2003-06-26 Flabeg Solarglas Gmbh & Co Kg Glas mit einer porösen Antireflex-Oberflächenbeschichtung sowie Verfahren zur Herstellung des Glases und Verwendung eines derartigen Glases
EP1429997A1 (fr) 2001-09-21 2004-06-23 MERCK PATENT GmbH Nouveau sol hybride pour la realisation de couches antireflets sio 2 resistantes a l'usure
WO2004063111A1 (fr) 2003-01-09 2004-07-29 Guardian Industries Corp. Article enrobe pouvant subir un traitement thermique, presentant une couche reflechissant les infrarouges (ir) comprenant du nitrure de niobium, et son procede de fabrication
WO2004108619A1 (fr) * 2003-06-06 2004-12-16 Pilkington Plc Verre a couche
WO2006124503A2 (fr) * 2005-05-12 2006-11-23 Agc Flat Glass North America, Inc. Revetement a faible emissivite presentant un faible coefficient d'apport par rayonnement solaire, des proprietes chimiques et mecaniques ameliorees et procede de fabrication associe
WO2008075107A1 (fr) * 2006-12-21 2008-06-26 Pilkington Group Limited Plaques de verre à couches et leur procédé de fabrication
WO2010142926A1 (fr) * 2009-06-12 2010-12-16 Saint-Gobain Glass France Procede de depot de couche mince et produit obtenu
GB2518899A (en) * 2013-10-07 2015-04-08 Pilkington Group Ltd Heat treatable coated glass pane
WO2019097192A1 (fr) * 2017-11-20 2019-05-23 Saint-Gobain Glass France Materiau comprenant une seule couche fonctionnelle a base d'argent et une couche absorbante

Also Published As

Publication number Publication date
GB201910976D0 (en) 2019-09-18
EP4007743A1 (fr) 2022-06-08

Similar Documents

Publication Publication Date Title
EP2681169B1 (fr) Couches barrière comprenant ni et ti, articles revêtus comprenant des couches barrière, et leurs procédés de fabrication
EP2010459B1 (fr) Vitre revêtue
EP2173677B1 (fr) Panneau de verre revêtu apté au traitement thermique
EP2675762B1 (fr) Carreau de verre à couche pouvant être traité thermiquement
EP2678286B1 (fr) Article revêtu comprenant un revêtement à faible émissivité, unité de verre isolant comprenant l'article revêtu et procédés pour les préparer
EP1979287B1 (fr) Vitre revêtue par traitement thermique
EP1734019B1 (fr) Article revêtu avec couche de réflexion IR et procédé de fabrication de cet article
EP3725751B1 (fr) Carreau de vitre revêtu thermotraitable
EP3055264B1 (fr) Panneau de verre revêtu pouvant recevoir un traitement thermique
EP3793959B1 (fr) Articles revêtus ajustables à faible émissivité ayant une couche de germe dopée sous l'argent, et procédés correspondants
EP0883584B1 (fr) Article transparent de verre revetu resistant a la trempe a chaud
KR20150087262A (ko) 추가의 금속을 갖는 아연 산화물 함유 층을 포함하는 저-e 코팅을 갖는 코팅 제품
KR20130051521A (ko) 열처리 가능한 저방사 유리 및 그 제조방법
EP4058417B1 (fr) Substrat de verre revêtu
EP2102126A1 (fr) Plaques de verre à couches et leur procédé de fabrication
WO2021019259A1 (fr) Substrat revêtu
WO2021019257A1 (fr) Substrat revêtu durcissable
WO2021019258A1 (fr) Substrat revêtu et trempable
EP3922615A2 (fr) Articles revêtus ajustables à faible émissivité ayant une couche de germe dopée sous l'argent, et procédés correspondants
EP4377275A1 (fr) Vitre revêtue

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20751653

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2020751653

Country of ref document: EP

Effective date: 20220301