WO2020195026A1 - 歯科用修復材セット及び歯の修復方法 - Google Patents
歯科用修復材セット及び歯の修復方法 Download PDFInfo
- Publication number
- WO2020195026A1 WO2020195026A1 PCT/JP2020/001015 JP2020001015W WO2020195026A1 WO 2020195026 A1 WO2020195026 A1 WO 2020195026A1 JP 2020001015 W JP2020001015 W JP 2020001015W WO 2020195026 A1 WO2020195026 A1 WO 2020195026A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composite resin
- meth
- acrylate
- ionomer cement
- tooth
- Prior art date
Abstract
本発明の一態様は、歯科用修復材セットにおいて、グラスアイオノマーセメントと、コンポジットレジンを有し、前記コンポジットレジンは、酸基を有する(メタ)アクリレートを含む。
Description
本発明は、歯科用修復材セット及び歯の修復方法に関する。
従来、う蝕を治療する際に、窩洞を形成した後、グラスアイオノマーセメントを窩洞に充填し、硬化させることにより、歯を修復する。
しかしながら、修復部の表面の強度を向上させることが望まれている。
そこで、グラスアイオノマーセメント、ボンディング材及びコンポジットレジンを併用して、歯を修復するサンドイッチテクニック法が知られている(例えば、特許文献1参照)。
具体的には、まず、コンディショナーで処理した窩洞に、グラスアイオノマーセメントを填入した後、硬化させる。次に、グラスアイオノマーセメントの硬化体にボンディング材を塗布した後、光を照射し、硬化させる。最後に、ボンディング材が硬化した窩洞に、コンポジットレジンを填塞した後、硬化させる。
しかしながら、ボンディング材を使用して、歯を修復すると、歯を修復する手順が煩雑になる。
一方、ボンディング材を使用せずに、歯を修復すると、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性が低下すると共に、辺縁漏洩が発生する。
本発明の一態様は、ボンディング材を使用せずに、歯を修復しても、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性を向上させると共に、辺縁漏洩の発生を抑制することが可能な歯科用修復材セット及び歯の修復方法を提供することを目的とする。
本発明の一態様は、歯科用修復材セットにおいて、グラスアイオノマーセメントと、コンポジットレジンを有し、前記コンポジットレジンは、酸基を有する(メタ)アクリレートを含む。
本発明の他の態様は、歯の修復方法において、歯の所定の領域に、グラスアイオノマーセメントを適用する工程と、該適用されたグラスアイオノマーセメントを硬化させる工程と、該グラスアイオノマーセメントが硬化した歯の所定の領域に、コンポジットレジンを適用する工程と、該適用されたコンポジットレジンを硬化させる工程を含み、前記コンポジットレジンは、酸基を有する(メタ)アクリレートを含む。
本発明の一態様によれば、ボンディング材を使用せずに、歯を修復しても、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性を向上させると共に、辺縁漏洩の発生を抑制することが可能な歯科用修復材セット及び歯の修復方法を提供することができる。
以下、本発明を実施するための形態について説明する。本発明は、下記の実施形態に制限されることはなく、特許請求の範囲に記載された範囲を逸脱することなく、下記の実施形態に種々の変形及び置換を加えることができる。
[歯科用修復材セット]
本実施形態の歯科用修復材セットは、グラスアイオノマーセメントと、コンポジットレジンを有するため、強度が高いコンポジットレジンの硬化体で修復部の表面を構成することができる。
本実施形態の歯科用修復材セットは、グラスアイオノマーセメントと、コンポジットレジンを有するため、強度が高いコンポジットレジンの硬化体で修復部の表面を構成することができる。
本実施形態の歯科用修復材セットは、コンポジットレジンが酸基を有する(メタ)アクリレートを含むため、ボンディング材を使用せずに、歯を修復しても、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性が向上すると共に、辺縁漏洩が発生しにくくなる。
ここで、ボンディング材を使用せずに、歯を修復する場合、ボンディング材を塗布した後、光を照射し、硬化させる必要が無いため、歯を修復する手順が煩雑にならず、歯を簡便に修復することができる。
コンポジットレジンは、酸基を有さない(メタ)アクリレートと、光重合開始剤と、フィラーをさらに含むことが好ましい。これにより、コンポジットレジンに光を照射して硬化させることができる。
コンポジットレジン中のフィラーの含有量は、5質量%以上であることが好ましく、30質量%以上であることがさらに好ましい。コンポジットレジン中のフィラーの含有量が5質量%以上であると、修復部の表面の強度がさらに向上する。
なお、コンポジットレジン中のフィラーの含有量は、85質量%以下であることが好ましい。
グラスアイオノマーセメントは、フルオロアルミノシリケートガラス粉末と、ポリカルボン酸系重合体、水、(メタ)アクリレート及び光重合開始剤を含む液状組成物とを有することが好ましい。これにより、グラスアイオノマーセメントに光を照射して硬化させることができる。
本実施形態の歯科用修復材セットは、コンディショナーをさらに有することが好ましい。この場合、歯のコンディショナーが適用された領域に、グラスアイオノマーセメントを適用することにより、歯に対するグラスアイオノマーセメントの硬化体の接着性がさらに向上する。
本実施形態の歯科用修復材セットは、エッチング材をさらに有していてもよい。この場合、歯の所定の領域に、エッチング材を適用することにより、歯に対するコンポジットレジンの硬化体の接着性がさらに向上する。
本実施形態の歯科用修復材セットは、ボンディング材をさらに有していてもよい。この場合、グラスアイオノマーセメントが硬化した歯の所定の領域に、ボンディング材を適用することにより、歯に対するコンポジットレジンの硬化体の接着性がさらに向上すると共に、辺縁漏洩がさらに発生しにくくなる。
[歯の修復方法]
本実施形態の歯の修復方法は、歯の所定の領域に、グラスアイオノマーセメントを適用する工程と、適用されたグラスアイオノマーセメントを硬化させる工程と、グラスアイオノマーセメントが硬化した歯の所定の領域に、コンポジットレジンを適用する工程と、適用されたコンポジットレジンを硬化させる工程を含む。このため、強度が高いコンポジットレジンの硬化体で修復部の表面を構成することができる。
本実施形態の歯の修復方法は、歯の所定の領域に、グラスアイオノマーセメントを適用する工程と、適用されたグラスアイオノマーセメントを硬化させる工程と、グラスアイオノマーセメントが硬化した歯の所定の領域に、コンポジットレジンを適用する工程と、適用されたコンポジットレジンを硬化させる工程を含む。このため、強度が高いコンポジットレジンの硬化体で修復部の表面を構成することができる。
また、コンポジットレジンは、酸基を有する(メタ)アクリレートを含むため、ボンディング材を使用せずに、歯を修復しても、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性が向上すると共に、辺縁漏洩が発生しにくくなる。
ここで、ボンディング材を使用せずに、歯を修復する場合、ボンディング材を塗布した後、光を照射し、硬化させる必要が無いため、歯を修復する手順が煩雑にならず、歯を簡便に修復することができる。
グラスアイオノマーセメントを適用する領域としては、例えば、窩洞、歯冠の欠損部における象牙質が形成されていた領域等が挙げられる。
コンポジットレジンを適用する領域としては、例えば、グラスアイオノマーセメントの硬化体が形成されている、窩洞、歯冠の欠損部におけるエナメル質が形成されていた領域等が挙げられる。
なお、グラスアイオノマーセメントが、フルオロアルミノシリケートガラス粉末と、ポリカルボン酸系重合体、水、(メタ)アクリレート及び光重合開始剤を含む液状組成物とを有する場合、適用されたグラスアイオノマーセメントに光を照射して硬化させることができる。
また、コンポジットレジンが、酸基を有さない(メタ)アクリレートと、光重合開始剤と、フィラーをさらに含む場合、適用されたコンポジットレジンに光を照射して硬化させることができる。
本実施形態の歯の修復方法は、歯の所定の領域に、コンディショナーを適用する工程をさらに含み、歯のコンディショナーが適用された領域に、グラスアイオノマーセメントを適用することが好ましい。これにより、歯に対するグラスアイオノマーセメントの硬化体の接着性がさらに向上する。
コンディショナーを適用する領域としては、例えば、窩洞、歯冠の欠損部における象牙質の表面等が挙げられる。
本実施形態の歯の修復方法は、歯の所定の領域に、エッチング材を適用する工程をさらに含み、エッチング材が適用された歯の所定の領域に、コンポジットレジンを適用することが好ましい。これにより、歯に対するコンポジットレジンの硬化体の接着性がさらに向上する。
エッチング材を適用する領域としては、例えば、窩洞、歯冠の欠損部におけるエナメル質の表面等が挙げられる。
本実施形態の歯の修復方法は、グラスアイオノマーセメントが硬化した歯の所定の領域に、ボンディング材を適用する工程と、適用されたボンディング材を硬化させる工程をさらに含み、ボンディング材が硬化した歯の所定の領域に、コンポジットレジンを適用してもよい。これにより、歯に対するコンポジットレジンの硬化体の接着性がさらに向上すると共に、辺縁漏洩がさらに発生しにくくなる。
ボンディング材を適用する領域としては、例えば、窩洞、歯冠の欠損部におけるグラスアイオノマーセメントの硬化体の表面、エナメル質の表面等が挙げられる。
図1を用いて、窩洞が形成されている歯の修復方法の一例を説明する。
まず、窩洞Cの象牙質Dの表面を、コンディショナーで処理する。次に、窩洞Cの象牙質Dが形成されていた領域に、グラスアイオノマーセメントを填入した後、硬化させ、グラスアイオノマーセメントの硬化体1を形成する。次に、窩洞Cのエナメル質Eの表面を、エッチング材で処理する。次に、窩洞Cのグラスアイオノマーセメントの硬化体1上のエナメル質Eが形成されていた領域に、コンポジットレジンを填塞した後、硬化させ、コンポジットレジンの硬化体2を形成する。
なお、コンポジットレジンを填塞する前のグラスアイオノマーセメントの硬化体1上に、ボンディング材を塗布した後、硬化させてもよい。
図2を用いて、歯冠の一部(象牙質D及びエナメル質Eの一部)が欠損している歯の修復方法の一例を説明する。
まず、欠損部の象牙質Dの表面を、コンディショナーで処理する。次に、欠損部の象牙質Dが形成されていた領域に、グラスアイオノマーセメントを適用した後、硬化させ、グラスアイオノマーセメントの硬化体1を形成する。次に、欠損部のエナメル質Eの表面を、エッチング材で処理する。次に、欠損部のグラスアイオノマーセメントの硬化体1上のエナメル質Eが形成されていた領域に、コンポジットレジンを適用した後、硬化させ、コンポジットレジンの硬化体2を形成する。
ここで、グラスアイオノマーセメントの硬化体1及びコンポジットレジンの硬化体2を形成する際に、マトリックスバンド等を使用する。
なお、コンポジットレジンを適用する前のグラスアイオノマーセメントの硬化体1上に、ボンディング材を塗布した後、硬化させてもよい。
図3を用いて、歯冠の一部(象牙質D及びエナメル質Eの一部)が欠損している歯の修復方法の他の例を説明する。
まず、欠損部のエナメル質Eの表面を、エッチング材で処理する。次に、欠損部のエナメル質Eが形成されていた領域の一部に、コンポジットレジンを適用した後、硬化させ、コンポジットレジンの硬化体2aを形成する。次に、欠損部の象牙質Dの表面を、コンディショナーで処理する。次に、欠損部の象牙質Dが形成されていた領域の一部に、グラスアイオノマーセメントを填塞した後、硬化させ、グラスアイオノマーセメントの硬化体1を形成する。次に、コンポジットレジンの硬化体2a及びグラスアイオノマーセメントの硬化体1上に、コンポジットレジンを適用した後、硬化させ、コンポジットレジンの硬化体2bを形成する。
ここで、コンポジットレジンの硬化体2a及びコンポジットレジンの硬化体2bを形成する際に、マトリックスバンド等を使用する。
なお、コンポジットレジンを適用する前のグラスアイオノマーセメントの硬化体1上に、ボンディング材を塗布した後、硬化させてもよい。
[コンポジットレジン]
コンポジットレジンは、酸基を有する(メタ)アクリレートと、酸基を有さない(メタ)アクリレートと、重合開始剤と、フィラーを含むが、前述したように、光重合開始剤を含むことが好ましい。
コンポジットレジンは、酸基を有する(メタ)アクリレートと、酸基を有さない(メタ)アクリレートと、重合開始剤と、フィラーを含むが、前述したように、光重合開始剤を含むことが好ましい。
(酸基を有する(メタ)アクリレート)
本明細書及び特許請求の範囲において、(メタ)アクリレートとは、メタクリロイルオキシ基及び/又はアクリロイルオキシ基(以下、(メタ)アクリロイルオキシ基という)を1個以上有する化合物(例えば、モノマー、オリゴマー、プレポリマー等)を意味する。
本明細書及び特許請求の範囲において、(メタ)アクリレートとは、メタクリロイルオキシ基及び/又はアクリロイルオキシ基(以下、(メタ)アクリロイルオキシ基という)を1個以上有する化合物(例えば、モノマー、オリゴマー、プレポリマー等)を意味する。
酸基を有する(メタ)アクリレートは、リン酸基、チオリン酸基又はカルボキシル基を1個以上有することが好ましい。
リン酸基を有する(メタ)アクリレートとしては、例えば、2-(メタ)アクリロイルオキシエチルジハイドロジェンホスフェート、ビス[2-(メタ)アクリロイルオキシエチル]ハイドロジェンホスフェート、2-(メタ)アクリロイルオキシエチルフェニルハイドロジェンホスフェート、6-(メタ)アクリロイルオキシヘキシルジハイドロジェンホスフェート、6-(メタ)アクリロイルオキシヘキシルフェニルハイドロジェンホスフェート、10-(メタ)アクリロイルオキシデシルジハイドロジェンホスフェート、1,3-ジ(メタ)アクリロイルプロパン-2-ジハイドロジェンホスフェート、1,3-ジ(メタ)アクリロイルプロパン-2-フェニルハイドロジェンホスフェート、ビス[5-{2-(メタ)アクリロイルオキシエトキシカルボニル}ヘプチル]ハイドロジェンホスフェート等が挙げられる。
チオリン酸基を有する(メタ)アクリレートとしては、例えば、2-(メタ)アクリロイルオキシエチルジハイドロジェンチオホスフェート、3-(メタ)アクリロイルオキシプロピルジハイドロジェンチオホスフェート、4-(メタ)アクリロイルオキシブチルジハイドロジェンチオホスフェート、5-(メタ)アクリロイルオキシペンチルジハイドロジェンチオホスフェート、6-(メタ)アクリロイルオキシヘキシルジハイドロジェンチオホスフェート、7-(メタ)アクリロイルオキシヘプチルジハイドロジェンチオホスフェート、8-(メタ)アクリロイルオキシオクチルジハイドロジェンチオホスフェート、9-(メタ)アクリロイルオキシノニルジハイドロジェンチオホスフェート、10-(メタ)アクリロイルオキシデシルジハイドロジェンチオホスフェート、11-(メタ)アクリロイルオキシウンデシルジハイドロジェンチオホスフェート、12-(メタ)アクリロイルオキシドデシルジハイドロジェンチオホスフェート、13-(メタ)アクリロイルオキシトリデシルジハイドロジェンチオホスフェート、14-(メタ)アクリロイルオキシテトラデシルジハイドロジェンチオホスフェート、15-(メタ)アクリロイルオキシペンタデシルジハイドロジェンチオホスフェート、16-(メタ)アクリロイルオキシヘキサデシルジハイドロジェンチオホスフェート、17-(メタ)アクリロイルオキシヘプタデシルジハイドロジェンチオホスフェート、18-(メタ)アクリロイルオキシオクタデシルジハイドロジェンチオホスフェート、19-(メタ)アクリロイルオキシノナデシルジハイドロジェンチオホスフェート、20-(メタ)アクリロイルオキシイコシルジハイドロジェンチオホスフェート等が挙げられる。
カルボキシル基を有する(メタ)アクリレートとしては、例えば、4-(メタ)アクリロイルオキシエチルトリメリット酸、4-(メタ)アクリロイルオキシエチルトリメリット酸無水物、4-(メタ)アクリロイルオキシデシルトリメリット酸、4-(メタ)アクリロイルオキシデシルトリメリット酸無水物、11-(メタ)アクリロイルオキシ-1,1-ウンデカンジカルボン酸、1,4-ジ(メタ)アクリロイルオキシピロメリット酸、2-(メタ)アクリロイルオキシエチルマレイン酸、2-(メタ)アクリロイルオキシエチルフタル酸、2-(メタ)アクリロイルオキシエチルヘキサヒドロフタル酸等が挙げられる。
これらの中でも、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性の点から、2-メタクロイルオキシエチルアシッドホスフェート、10-メタクリロイルオキシデシルジハイドロジェンホスフェートが特に好ましい。
なお、酸基を有する(メタ)アクリレートは、二種以上を併用してもよい。
酸基を有する(メタ)アクリレートは、(メタ)アクリロイルオキシ基を2個以上有することが好ましい。これにより、修復部の表面の強度がさらに向上する。
コンポジットレジン中の酸基を有する(メタ)アクリレートの含有量は、1~30質量%であることが好ましく、3~20質量%であることがさらに好ましい。コンポジットレジン中の酸基を有する(メタ)アクリレートの含有量が1質量%以上であることにより、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性がさらに向上し、30質量%以下であることにより、コンポジットレジンの保存安定性が向上する。
(酸基を有さない(メタ)アクリレート)
酸基を有さない(メタ)アクリレートとしては、例えば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、イソプロピル(メタ)アクリレート、n-ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、ヒドロキシプロピル(メタ)アクリレート、テトラヒドロフルフリル(メタ)アクリレート、グリシジル(メタ)アクリレート、2-ヒドロキシエチル(メタ)アクリレート、2-ヒドロキシプロピル(メタ)アクリレート、3-ヒドロキシプロピル(メタ)アクリレート、2-メトキシエチル(メタ)アクリレート、2-エトキシエチル(メタ)アクリレート、2-メチルヘキシル(メタ)アクリレート、2-エチルヘキシル(メタ)アクリレート、ベンジル(メタ)アクリレート、2-ヒドロキシ-1,3-ジ(メタ)アクリロイルオキシプロパン、エチレングリコールジ(メタ)アクリレート、ジエチレングリコールジ(メタ)アクリレート、トリエチレングリコールジ(メタ)アクリレート、ブチレングリコールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、1,3-ブタンジオールジ(メタ)アクリレート、1,4-ブタンジオールジ(メタ)アクリレート、1,6-ヘキサンジオールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、トリメチロールエタントリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、トリメチロールメタントリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ポリブチレングリコールジ(メタ)アクリレート、ビスフェノールAジグリシジル(メタ)アクリレート、ジ-2-(メタ)アクリロイルオキシエチル-2,2,4-トリメチルヘキサメチレンジカルバメート、1,3,5-トリス[1,3-ビス{(メタ)アクリロイルオキシ}-2-プロポキシカルボニルアミノヘキサン]-1,3,5-(1H,3H,5H)トリアジン-2,4,6-トリオン、2,2-ビス[4-(3-(メタ)アクリロイルオキシ-2-ヒドロキシプロピル)]フェニルプロパン、N,N’-(2,2,4-トリメチルヘキサメチレン)ビス〔2-(アミノカルボキシ)プロパン-1,3-ジオール〕テトラメタクリレート、2,2’-ビス(4-ヒドロキシシクロヘキシル)プロパンと2-オキシパノンとヘキサメチレンジイソシアネートと2-ヒドロキシエチル(メタ)アクリレートとからなるウレタンオリゴマーの(メタ)アクリレート、1,3-ブタンジオールとヘキサメチレンジイソシアネートと2-ヒドロキシエチル(メタ)アクリレートとからなるウレタンオリゴマーの(メタ)アクリレート等が挙げられる。
酸基を有さない(メタ)アクリレートとしては、例えば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、イソプロピル(メタ)アクリレート、n-ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、ヒドロキシプロピル(メタ)アクリレート、テトラヒドロフルフリル(メタ)アクリレート、グリシジル(メタ)アクリレート、2-ヒドロキシエチル(メタ)アクリレート、2-ヒドロキシプロピル(メタ)アクリレート、3-ヒドロキシプロピル(メタ)アクリレート、2-メトキシエチル(メタ)アクリレート、2-エトキシエチル(メタ)アクリレート、2-メチルヘキシル(メタ)アクリレート、2-エチルヘキシル(メタ)アクリレート、ベンジル(メタ)アクリレート、2-ヒドロキシ-1,3-ジ(メタ)アクリロイルオキシプロパン、エチレングリコールジ(メタ)アクリレート、ジエチレングリコールジ(メタ)アクリレート、トリエチレングリコールジ(メタ)アクリレート、ブチレングリコールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、1,3-ブタンジオールジ(メタ)アクリレート、1,4-ブタンジオールジ(メタ)アクリレート、1,6-ヘキサンジオールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、トリメチロールエタントリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、トリメチロールメタントリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ポリブチレングリコールジ(メタ)アクリレート、ビスフェノールAジグリシジル(メタ)アクリレート、ジ-2-(メタ)アクリロイルオキシエチル-2,2,4-トリメチルヘキサメチレンジカルバメート、1,3,5-トリス[1,3-ビス{(メタ)アクリロイルオキシ}-2-プロポキシカルボニルアミノヘキサン]-1,3,5-(1H,3H,5H)トリアジン-2,4,6-トリオン、2,2-ビス[4-(3-(メタ)アクリロイルオキシ-2-ヒドロキシプロピル)]フェニルプロパン、N,N’-(2,2,4-トリメチルヘキサメチレン)ビス〔2-(アミノカルボキシ)プロパン-1,3-ジオール〕テトラメタクリレート、2,2’-ビス(4-ヒドロキシシクロヘキシル)プロパンと2-オキシパノンとヘキサメチレンジイソシアネートと2-ヒドロキシエチル(メタ)アクリレートとからなるウレタンオリゴマーの(メタ)アクリレート、1,3-ブタンジオールとヘキサメチレンジイソシアネートと2-ヒドロキシエチル(メタ)アクリレートとからなるウレタンオリゴマーの(メタ)アクリレート等が挙げられる。
酸基を有さない(メタ)アクリレートは、(メタ)アクリロイルオキシ基を2個以上有することが好ましい。これにより、修復部の表面の強度がさらに向上する。
コンポジットレジン中の酸基を有さない(メタ)アクリレートの含有量は、0.5~90質量%であることが好ましく、10~60質量%であることがさらに好ましい。コンポジットレジン中の酸基を有さない(メタ)アクリレートの含有量が0.5質量%以上であると、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性がさらに向上し、90質量%以下であると、コンポジットレジンの保存安定性が向上する。
(重合開始剤)
重合開始剤としては、化学重合開始剤及び/又は光重合開始剤を用いることができる。
重合開始剤としては、化学重合開始剤及び/又は光重合開始剤を用いることができる。
化学重合開始剤は、酸化剤及び還元剤から構成される。
化学重合開始剤における酸化剤としては、例えば、クメンヒドロペルオキシド、ジイソプロピルベンゼンヒドロペルオキシド、ジ-t-ブチルペルオキシド、ラウロイルペルオキシド、ベンゾイルペルオキシド、t-ブチルペルオキシイソプロピルカーボネート、t-ブチルペルオキシ-2-エチルヘキサノエート等の過酸化物、アゾビスイソブチロニトリル、1,1’-アゾビス(シクロヘキサンカルボニトリル)、2,2’-アゾビス(2,4-ジメチルバレロニトリル)、ジメチル2,2’-アゾビス(2-メチルプロピオネート)等のアゾ化合物、過酸化水素、過硫酸塩等が挙げられる。
なお、酸化剤は、二種以上を併用してもよい。
コンポジットレジン中の酸化剤の含有量は、0.001~10質量%であることが好ましく、0.01~5質量%であることがさらに好ましい。コンポジットレジン中の酸化剤の含有量が0.001質量%以上であると、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性がさらに向上し、10質量%以下であると、コンポジットレジンの保存安定性が向上する。
化学重合開始剤における還元剤としては、アミン化合物、スルフィン酸類、チオ尿素類、システイン類、アスコルビン酸類等を用いることができる。
アミン化合物としては、例えば、N,N-ジメチル-p-トルイジン、N,N-ジエチル-p-トルイジン、N,N-ジメチルアニリン、N,N-ビス(2-ヒドロキシエチル)-p-トルイジン、N,N-ジメチルアミノエチルメタクリレート、トリエタノールアミン、4-ジメチルアミノ安息香酸メチル、4-ジメチルアミノ安息香酸エチル、4-ジメチルアミノ安息香酸イソアミル、トリエチルアミン、N-エチルジエタノールアミン、トリエタノールアミン等のアミン化合物、N-フェニルグリシン等が挙げられる。
スルフィン酸類としては、例えば、p-トルエンスルフィン酸ナトリウム、p-トルエンスルフィン酸リチウム、ベンゼンスルフィン酸、ベンゼンスルフィン酸ナトリウム、p-トルエンスルホニルクロライド、p-トルエンスルホニルフルオライド、o-トルエンスルホニルイソシアネート、p-アセトアミドベンゼンスルフィン酸ナトリウム等が挙げられる。
チオ尿素類としては、例えば、チオ尿素、エチレンチオ尿素、N-メチルチオ尿素、N-エチルチオ尿素、N-プロピルチオ尿素、N-ブチルチオ尿素、N-ラウリルチオ尿素、N-フェニルチオ尿素、N-シクロヘキシルチオ尿素、N,N-ジメチルチオ尿素、N,N-ジエチルチオ尿素、N,N-ジプロピルチオ尿素、N,N-ジ-ブチルチオ尿素、N,N-ジラウリルチオ尿素、N,N-ジフェニルチオ尿素、N,N-ジシクロヘキシルチオ尿素、トリメチルチオ尿素、テトラメチルチオ尿素、N-アセチルチオ尿素、N-ベンゾイルチオ尿素、1-アリル-3-(2-ヒドロキシエチル)-2-チオ尿素、1-(2-テトラヒドロフルフリル)-2-チオ尿素等が挙げられる。
システイン類としては、例えば、システイン、システインメチル、システインエチル、N-メチルシステイン、N-エチルシステイン、N-アセチルシステイン、N,N-ジメチルシステイン、N,N-ジエチルシステイン、N,N-ジアセチルシステイン、グルタチオン等が挙げられる。
アスコルビン酸類としては、例えば、アスコルビン酸、アスコルビン酸ナトリウム、アスコルビン酸カルシウム、アスコルビン酸カリウム等が挙げられる。
なお、還元剤は、二種以上を併用してもよい。
コンポジットレジン中の還元剤の含有量は、0.001~10質量%であることが好ましく、0.01~5質量%であることがさらに好ましい。コンポジットレジン中の還元剤の含有量が0.001質量%以上であると、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性がさらに向上し、10質量%以下であると、コンポジットレジンの保存安定性が向上する。
光重合開始剤としては、ケトン系化合物、α-ジケトン系化合物、ケタール系化合物、アントラキノン系化合物、チオキサントン系化合物、ベンゾインアルキルエーテル系化合物、アシルホスフィンオキシド系化合物等を用いることができる。
ケトン系化合物としては、例えば、ベンゾフェノン、ビス(4-ジメチルアミノフェニル)ケトン、4,4’-ビス(ジエチルアミノ)ベンゾフェノン等が挙げられる。
α-ジケトン系化合物としては、例えば、カンファーキノン、ベンジル、ジアセチル、アセナフテンキノン、9,10-フェナントラキノン等が挙げられる。
ケタール系化合物としては、例えば、ベンジルケタール、ジアセチルケタール、ベンジルジメチルケタール、ベンジルジエチルケタール、ベンジルビス(β-フェニルエチル)ケタール、ベンジルビス(2-メトキシエチル)ケタール、4,4’-ジメチル(ベンジルジメチルケタール)等が挙げられる。
アントラキノン系化合物としては、例えば、アントラキノン、1-クロロアントラキノン、2-クロロアントラキノン、1,2-ベンズアントラキノン、1-ヒドロキシアントラキノン、1-メチルアントラキノン、2-エチルアントラキノン、1-ブロモアントラキノン等が挙げられる。
チオキサントン系化合物としては、例えば、チオキサントン、2-イソプロピルチオキサントン、2-ニトロチオキサントン、2-メチルチオキサントン、2,4-ジメチルチオキサントン、2,4-ジエチルチオキサントン、2,4-ジイソプロピルチオキサントン、2-クロロ-7-トリフルオロメチルチオキサントン、チオキサントン-10,10-ジオキシド、チオキサントン-10-オキシド、2-エチルチオキサントン、2-クロロチオキサントン、2-ヒドロキシ-3-(3,4-ジメチル-9-オキソ-9H-チオキサンテン-2-イルオキシ)-N,N,N-トリメチル-1-プロパンアミニウムクロライド等が挙げられる。
ベンゾインアルキルエーテル系化合物としては、例えば、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインプロピルエーテル、ベンゾインイソブチルエーテル等が挙げられる。
アシルホスフィンオキシド系化合物としては、例えば、2,4,6-トリメチルベンゾイルジフェニルホスフィンオキシド、2,4,6-トリメトキシベンゾイルジフェニルホスフィンオキシド、2,6-ジメチルベンゾイルジフェニルホスフィンオキシド、2,6-ジメトキシベンゾイルジフェニルホスフィンオキシド等が挙げられる。
なお、光重合開始剤は、二種以上を併用してもよい。
コンポジットレジン中の光重合開始剤の含有量は、0.001~10質量%であることが好ましく、0.01~5質量%であることがさらに好ましい。コンポジットレジン中の光重合開始剤の含有量が0.001質量%以上であることにより、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性がさらに向上し、10質量%以下であることにより、コンポジットレジンの保存安定性が向上する。
(光重合促進剤)
コンポジットレジンが光重合開始剤を含む場合、コンポジットレジンは、光重合促進剤をさらに含んでいてもよい。
コンポジットレジンが光重合開始剤を含む場合、コンポジットレジンは、光重合促進剤をさらに含んでいてもよい。
光重合促進剤としては、例えば、N,N-ジメチル-p-トルイジン、トリエタノールアミン、トリルジエタノールアミン、4-ジメチルアミノ安息香酸メチル、4-ジメチルアミノ安息香酸エチル、4-ジメチルアミノ安息香酸イソアミル等の3級アミン、バルビツール酸、1,3-ジメチルバルビツール酸、1,3,5-トリメチルバルビツール酸、1,3,5-トリエチルバルビツール酸、5-ブチルバルビツール酸、1-ベンジル-5-フェニルバルビツール酸、1-シクロヘキシル-5-エチルバルビツール酸等のバルビツール酸誘導体等が挙げられる。
なお、光重合促進剤は、二種以上を併用してもよい。
コンポジットレジン中の光重合促進剤の含有量は、0.001~5質量%であることが好ましく、0.01~1質量%であることがさらに好ましい。コンポジットレジン中の光重合促進剤の含有量が0.001質量%以上であると、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性がさらに向上し、5質量%以下であると、コンポジットレジンの保存安定性が向上する。
(フィラー)
フィラーは、有機フィラー及び無機フィラーのいずれであってもよいが、無機フィラーであることが好ましい。
フィラーは、有機フィラー及び無機フィラーのいずれであってもよいが、無機フィラーであることが好ましい。
無機フィラーとしては、例えば、シリカ粉末、アルミナ粉末、ガラス粉末(例えば、バリウムガラス粉末、ストロンチウムガラス粉末)等が挙げられる。
無機フィラーは、必要に応じて、シランカップリング剤等の表面処理剤で処理されていてもよい。
なお、フィラーは、二種以上を併用してもよい。
(他の成分)
コンポジットレジンは、重合禁止剤等をさらに含んでいてもよい。
コンポジットレジンは、重合禁止剤等をさらに含んでいてもよい。
重合禁止剤としては、例えば、ジブチルヒドロキシトルエン、2,6-t-ブチル-2,4-キシレノール等が挙げられる。
なお、重合禁止剤は、二種以上を併用してもよい。
コンポジットレジン中の重合禁止剤の含有量は、0.001~1質量%であることが好ましく、0.01~0.1質量%であることがさらに好ましい。
[グラスアイオノマーセメント]
グラスアイオノマーセメントは、フルオロアルミノシリケートガラス粉末と、ポリカルボン酸系重合体及び水を含む液状組成物を有するが、前述したように、液状組成物は、(メタ)アクリレート及び光重合開始剤をさらに含むことが好ましい。
グラスアイオノマーセメントは、フルオロアルミノシリケートガラス粉末と、ポリカルボン酸系重合体及び水を含む液状組成物を有するが、前述したように、液状組成物は、(メタ)アクリレート及び光重合開始剤をさらに含むことが好ましい。
(フルオロアルミノシリケートガラス粉末)
フルオロアルミノシリケートガラス粉末中のフッ素(F)の含有量は、1~35質量%であることが好ましく、3~25質量%であることがさらに好ましい。
フルオロアルミノシリケートガラス粉末中のフッ素(F)の含有量は、1~35質量%であることが好ましく、3~25質量%であることがさらに好ましい。
フルオロアルミノシリケートガラス粉末中のアルミニウムの含有量は、酸化アルミニウム(Al2O3)に換算した量で15~40質量%であることが好ましく、20~35質量%であることがさらに好ましい。
フルオロアルミノシリケートガラス粉末中のケイ素の含有量は、酸化ケイ素(SiO2)に換算した量で15~50質量%であることが好ましく、20~40質量%であることがさらに好ましい。
フルオロアルミノシリケートガラス粉末中のリンの含有量は、酸化リン(V)(P2O5)に換算した量で0~15質量%であることが好ましく、1~7質量%であることがさらに好ましい。
フルオロアルミノシリケートガラス粉末中のカルシウムの含有量は、酸化カルシウム(CaO)に換算した量で0~30質量%であることが好ましく、1~20質量%であることがさらに好ましい。
フルオロアルミノシリケートガラス粉末中のストロンチウムの含有量は、酸化ストロンチウム(SrO)に換算した量で0~40質量%であることが好ましく、10~30質量%であることがさらに好ましい。
(ポリカルボン酸系重合体)
ポリカルボン酸系重合体としては、特に限定されないが、α,β-不飽和カルボン酸の単独重合体又は共重合体を用いることができる。
ポリカルボン酸系重合体としては、特に限定されないが、α,β-不飽和カルボン酸の単独重合体又は共重合体を用いることができる。
α,β-不飽和カルボン酸としては、例えば、アクリル酸、メタクリル酸、2-クロロアクリル酸、3-クロロアクリル酸、アコニット酸、メサコン酸、マレイン酸、イタコン酸、フマル酸、グルタコン酸、シトラコン酸等が挙げられる。
また、ポリカルボン酸系重合体は、α,β-不飽和カルボン酸と、α,β-不飽和カルボン酸と共重合することが可能なモノマーとの共重合体であってもよい。
α,β-不飽和カルボン酸と共重合することが可能なモノマーとしては、例えば、アクリルアミド、アクリロニトリル、メタクリル酸エステル、アクリル酸塩類、塩化ビニル、塩化アリル、酢酸ビニル等が挙げられる。
この場合、ポリカルボン酸系重合体を構成するモノマーに対するα,β-不飽和カルボン酸の割合は、50質量%以上であることが好ましい。
ポリカルボン酸系重合体は、アクリル酸又はイタコン酸の単独重合体又は共重合体であることが好ましい。
なお、ポリカルボン酸系重合体は、少なくとも一部が粉末であってもよい。
((メタ)アクリレート)
(メタ)アクリレートとしては、コンポジットレジンにおける酸基を有する(メタ)アクリレート及び酸基を有さない(メタ)アクリレートと同様の化合物を用いることができる。
(メタ)アクリレートとしては、コンポジットレジンにおける酸基を有する(メタ)アクリレート及び酸基を有さない(メタ)アクリレートと同様の化合物を用いることができる。
(光重合開始剤)
光重合開始剤としては、コンポジットレジンにおける光重合開始剤と同様の化合物を用いることができる。
光重合開始剤としては、コンポジットレジンにおける光重合開始剤と同様の化合物を用いることができる。
[グラスアイオノマーセメントの適用方法]
グラスアイオノマーセメントは、フルオロアルミノシリケートガラス粉末と、液状組成物を練和して、歯の所定の領域に適用する。
グラスアイオノマーセメントは、フルオロアルミノシリケートガラス粉末と、液状組成物を練和して、歯の所定の領域に適用する。
フルオロアルミノシリケートガラス粉末と、液状組成物を練和する際の、液状組成物に対するフルオロアルミノシリケートガラス粉末の質量比(以下、粉液比という)は、1~6であることが好ましく、1.5~4.5であることがさらに好ましい。粉液比が1以上であると、グラスアイオノマーセメントの硬化体の圧縮強度が高くなり、6以下であると、フルオロアルミノシリケートガラス粉末と、液状組成物を練和しやすくなる。
[コンディショナー]
コンディショナーとしては、公知のコンディショナーを用いることができる。
コンディショナーとしては、公知のコンディショナーを用いることができる。
グラスアイオノマーセメントが(メタ)アクリレート又は光重合開始剤を含まない場合、例えば、ポリアクリル酸又はクエン酸と、水を含むコンディショナーを用いることができる。
また、グラスアイオノマーセメントが(メタ)アクリレート及び光重合開始剤を含む場合、例えば、酸基を有する(メタ)アクリレートと、水と、エタノールと、酸基を有さない(メタ)アクリレートと、光重合開始剤を含むコンディショナーを用いることができる。
ここで、酸基を有する(メタ)アクリレート、酸基を有さない(メタ)アクリレート及び光重合開始剤としては、それぞれコンポジットレジンにおける酸基を有する(メタ)アクリレート、酸基を有さない(メタ)アクリレート及び光重合開始剤と同様の化合物を用いることができる。
[エッチング材]
エッチング材としては、公知のエッチング材を用いることができる。
エッチング材としては、公知のエッチング材を用いることができる。
[ボンディング材]
ボンディング材としては、公知のボンディング材を用いることができる。
ボンディング材としては、公知のボンディング材を用いることができる。
以下、本発明の実施例を説明するが、本発明は、実施例に限定されない。
[実施例1~6、比較例1~3]
[グラスアイオノマーセメントの作製]
(フルオロアルミノシリケートガラス粉末の作製)
酸化アルミニウム(21質量%)、無水ケイ酸(44質量%)、フッ化カルシウム(12質量%)、リン酸カルシウム(14質量%)、炭酸ストロンチウム(9質量%)を十分混合し、原料組成物を得た。次に、高温電気炉を用いて、原料組成物を1200℃で5時間保持し、溶融させた後、冷却し、フルオロアルミノシリケートガラスを得た。次に、ボールミルを用いて、フルオロアルミノシリケートガラスを10時間粉砕した後、200メッシュ(ASTM)のふるいを通過させ、フルオロアルミノシリケートガラス粉末を得た。
[グラスアイオノマーセメントの作製]
(フルオロアルミノシリケートガラス粉末の作製)
酸化アルミニウム(21質量%)、無水ケイ酸(44質量%)、フッ化カルシウム(12質量%)、リン酸カルシウム(14質量%)、炭酸ストロンチウム(9質量%)を十分混合し、原料組成物を得た。次に、高温電気炉を用いて、原料組成物を1200℃で5時間保持し、溶融させた後、冷却し、フルオロアルミノシリケートガラスを得た。次に、ボールミルを用いて、フルオロアルミノシリケートガラスを10時間粉砕した後、200メッシュ(ASTM)のふるいを通過させ、フルオロアルミノシリケートガラス粉末を得た。
(ポリアクリル酸水溶液の作製)
ポリアクリル酸を水に溶解させ、50質量%ポリアクリル酸水溶液を得た。
ポリアクリル酸を水に溶解させ、50質量%ポリアクリル酸水溶液を得た。
(練和)
フルオロアルミノシリケートガラス粉末と、ポリアクリル酸水溶液を、粉液比1.8で練和し、グラスアイオノマーセメントの練和物を得た。
フルオロアルミノシリケートガラス粉末と、ポリアクリル酸水溶液を、粉液比1.8で練和し、グラスアイオノマーセメントの練和物を得た。
[コンポジットレジンの作製]
表1に示す配合量[質量部]で、リン酸基を有するメタクリレート、無機フィラー、酸基を有さないメタクリレート、光重合開始剤、重合禁止剤を混合し、コンポジットレジンを得た。
表1に示す配合量[質量部]で、リン酸基を有するメタクリレート、無機フィラー、酸基を有さないメタクリレート、光重合開始剤、重合禁止剤を混合し、コンポジットレジンを得た。
なお、表1における略称の意味及び作製方法は、以下の通りである。
P-2M:ビス(2-メタクリロイルオキシエチル)ハイドロジェンホスフェート
MDP:10-メタクリロイルオキシデシルジハイドロジェンホスフェート
シリカ粉末:アエロジルR812(日本アエロジル製)
Bis-MEPP:ビスメタクリル酸イソプロピリデンビス[(4,1-フェニレン)オキシエチレン]
UDMA:ジ-2-メタクリロイルオキシエチル-2,2,4-トリメチルヘキサメチレンジカルバメート
TEGDMA:トリエチレングリコールジメタクリレート
CQ:カンファーキノン
TPO:2,4,6-トリメチルベンゾイルジフェニルホスフィンオキシド
EPA:4-ジメチルアミノ安息香酸エチル
BHT:ジブチルヒドロキシトルエン
(ストロンチウムガラス粉末の作製)
SiO2(55質量%)、Al2O3(10質量%)、SrO(20質量%)、B2O3(15質量%)を十分混合し、原料組成物を得た。次に、高温電気炉を用いて、原料組成物を1200℃で5時間保持し、溶融させた後、冷却し、ストロンチウムガラスを得た。次に、ボールミルを用いて、ストロンチウムガラスを10時間粉砕した後、200メッシュ(ASTM)のふるいを通過させ、ストロンチウムガラス粉末を得た。
MDP:10-メタクリロイルオキシデシルジハイドロジェンホスフェート
シリカ粉末:アエロジルR812(日本アエロジル製)
Bis-MEPP:ビスメタクリル酸イソプロピリデンビス[(4,1-フェニレン)オキシエチレン]
UDMA:ジ-2-メタクリロイルオキシエチル-2,2,4-トリメチルヘキサメチレンジカルバメート
TEGDMA:トリエチレングリコールジメタクリレート
CQ:カンファーキノン
TPO:2,4,6-トリメチルベンゾイルジフェニルホスフィンオキシド
EPA:4-ジメチルアミノ安息香酸エチル
BHT:ジブチルヒドロキシトルエン
(ストロンチウムガラス粉末の作製)
SiO2(55質量%)、Al2O3(10質量%)、SrO(20質量%)、B2O3(15質量%)を十分混合し、原料組成物を得た。次に、高温電気炉を用いて、原料組成物を1200℃で5時間保持し、溶融させた後、冷却し、ストロンチウムガラスを得た。次に、ボールミルを用いて、ストロンチウムガラスを10時間粉砕した後、200メッシュ(ASTM)のふるいを通過させ、ストロンチウムガラス粉末を得た。
(バリウムガラス粉末の作製)
SiO2(55質量%)、Al2O3(10質量%)、BaO(30質量%)、B2O3(10質量%)を十分混合し、原料組成物を得た。次に、高温電気炉を用いて、原料組成物を1200℃で5時間保持し、溶融させた後、冷却し、バリウムガラスを得た。次に、ボールミルを用いて、バリウムガラスを10時間粉砕した後、200メッシュ(ASTM)のふるいを通過させ、バリウムガラス粉末を得た。
SiO2(55質量%)、Al2O3(10質量%)、BaO(30質量%)、B2O3(10質量%)を十分混合し、原料組成物を得た。次に、高温電気炉を用いて、原料組成物を1200℃で5時間保持し、溶融させた後、冷却し、バリウムガラスを得た。次に、ボールミルを用いて、バリウムガラスを10時間粉砕した後、200メッシュ(ASTM)のふるいを通過させ、バリウムガラス粉末を得た。
(エッチング材)
エッチング材として、エッチャント(ジーシー製)を用いた。
エッチング材として、エッチャント(ジーシー製)を用いた。
(ボンディング材)
ボンディング材として、Gプレミオボンド(ジーシー製)を用いた。
ボンディング材として、Gプレミオボンド(ジーシー製)を用いた。
(歯科用修復材セット)
グラスアイオノマーセメントと、コンポジットレジンを、必要に応じて、エッチング材及び/又はボンディング材と組み合わせて、歯科用修復材セットとした。
グラスアイオノマーセメントと、コンポジットレジンを、必要に応じて、エッチング材及び/又はボンディング材と組み合わせて、歯科用修復材セットとした。
次に、歯科用修復材セットを用いて、辺縁漏洩、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性、コンポジットレジンの硬化体の曲げ強さを評価した。
[辺縁漏洩]
(試験片の作製)
内径3mm、深さ2mmの窩洞を、抜去牛歯に形成した。次に、窩洞の象牙質が形成されていた領域(深さ1mm)に、グラスアイオノマーセメントの練和物を填入した後、37℃、95%RHの環境下で10分間保管して、グラスアイオノマーセメントを硬化させた。次に、必要に応じて、エッチング材で前処理した。具体的には、エッチング材を窩壁部に塗布して、30秒間静置し、エナメル質をエッチングした後、水洗した。さらに、必要に応じて、ボンディング材で前処理した。具体的には、窩壁部及びグラスアイオノマーセメントの硬化体に、ボンディング材を塗布し、エアブローした後、歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、光を照射して、ボンディング材を硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、ボンディング材の全体に光が照射されるまで繰り返した。次に、窩洞からやや盛り上がるように、窩洞のエナメル質が形成されていた領域に、コンポジットレジンを填塞した後、歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、光を照射して、コンポジットレジンを硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、コンポジットレジンの全体に光が照射されるまで繰り返した。次に、37℃の水中で試験片を24時間保管した後、1200番耐水研磨紙を用いて、修復部が平坦になるように、注水研磨し、試験片を得た。
(試験片の作製)
内径3mm、深さ2mmの窩洞を、抜去牛歯に形成した。次に、窩洞の象牙質が形成されていた領域(深さ1mm)に、グラスアイオノマーセメントの練和物を填入した後、37℃、95%RHの環境下で10分間保管して、グラスアイオノマーセメントを硬化させた。次に、必要に応じて、エッチング材で前処理した。具体的には、エッチング材を窩壁部に塗布して、30秒間静置し、エナメル質をエッチングした後、水洗した。さらに、必要に応じて、ボンディング材で前処理した。具体的には、窩壁部及びグラスアイオノマーセメントの硬化体に、ボンディング材を塗布し、エアブローした後、歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、光を照射して、ボンディング材を硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、ボンディング材の全体に光が照射されるまで繰り返した。次に、窩洞からやや盛り上がるように、窩洞のエナメル質が形成されていた領域に、コンポジットレジンを填塞した後、歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、光を照射して、コンポジットレジンを硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、コンポジットレジンの全体に光が照射されるまで繰り返した。次に、37℃の水中で試験片を24時間保管した後、1200番耐水研磨紙を用いて、修復部が平坦になるように、注水研磨し、試験片を得た。
(サーマル試験)
試験片のサーマル試験を実施した。具体的には、5℃の水槽と、55℃の水槽に、試験片を交互に30秒間ずつ浸漬する操作を5000回繰り返した。次に、1質量%メチレンブルー水溶液に試験片を4時間浸漬させた後、試験片を取り出した。次に、精密切断機ISOMET(BUEHLER製)を用いて、窩洞部を垂直に切断した後、メチレンブルーの侵入度合いを観察し、辺縁漏洩を評価した。なお、辺縁漏洩は、以下の基準で判定した。
試験片のサーマル試験を実施した。具体的には、5℃の水槽と、55℃の水槽に、試験片を交互に30秒間ずつ浸漬する操作を5000回繰り返した。次に、1質量%メチレンブルー水溶液に試験片を4時間浸漬させた後、試験片を取り出した。次に、精密切断機ISOMET(BUEHLER製)を用いて、窩洞部を垂直に切断した後、メチレンブルーの侵入度合いを観察し、辺縁漏洩を評価した。なお、辺縁漏洩は、以下の基準で判定した。
スコア0:コンポジットレジンの硬化体と歯質の境界部にメチレンブルーが侵入していない場合
スコア1:コンポジットレジンの硬化体と歯質の境界部までメチレンブルーが浸入している場合
スコア2:グラスアイオノマーセメントの硬化体と歯質の境界部までメチレンブルーが侵入している場合
[グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性]
(被着体試料の作製)
内径4mm、深さ6mmのステンレス鋼製の金型に、グラスアイオノマーセメントの練和物を充填した後、両端をステンレス鋼板で挟んでクランプで固定し、グラスアイオノマーセメントを37℃で1時間硬化させた。次に、金型からグラスアイオノマーセメントの硬化体を取り出した後、37℃の水中でグラスアイオノマーセメントの硬化体を23時間保管した。
スコア1:コンポジットレジンの硬化体と歯質の境界部までメチレンブルーが浸入している場合
スコア2:グラスアイオノマーセメントの硬化体と歯質の境界部までメチレンブルーが侵入している場合
[グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性]
(被着体試料の作製)
内径4mm、深さ6mmのステンレス鋼製の金型に、グラスアイオノマーセメントの練和物を充填した後、両端をステンレス鋼板で挟んでクランプで固定し、グラスアイオノマーセメントを37℃で1時間硬化させた。次に、金型からグラスアイオノマーセメントの硬化体を取り出した後、37℃の水中でグラスアイオノマーセメントの硬化体を23時間保管した。
アクリル樹脂ユニファストII(ジーシー製)を用いて、グラスアイオノマーセメントの硬化体の端面が露出するように包埋し、被着体試料を得た。
(試験片の作製)
被着体試料のグラスアイオノマーセメントの硬化体の露出部に、内径2.4mm、深さ1mmのプラスチック製の金型を載せた後、必要に応じて、ボンディング材で前処理した。具体的には、ボンディング材を塗布し、エアブローした後、歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、光を照射して、ボンディング材を硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、ボンディング材の全体に光が照射されるまで繰り返した。次に、コンポジットレジンを金型に充填した後、歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、光を照射して、コンポジットレジンを硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、コンポジットレジンの全体に光が照射されるまで繰り返し、試験片を得た。次に、金型から試験片を取り出した後、37℃の水中で試験片を保管した。
被着体試料のグラスアイオノマーセメントの硬化体の露出部に、内径2.4mm、深さ1mmのプラスチック製の金型を載せた後、必要に応じて、ボンディング材で前処理した。具体的には、ボンディング材を塗布し、エアブローした後、歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、光を照射して、ボンディング材を硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、ボンディング材の全体に光が照射されるまで繰り返した。次に、コンポジットレジンを金型に充填した後、歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、光を照射して、コンポジットレジンを硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、コンポジットレジンの全体に光が照射されるまで繰り返し、試験片を得た。次に、金型から試験片を取り出した後、37℃の水中で試験片を保管した。
(せん断接着試験)
試験片を作製してから24時間後に、試験片のせん断接着試験を実施した。具体的には、オートグラフ(島津製作所製)を用いて、グラスアイオノマーセメントの硬化体と、コンポジットレジンの硬化体の接合面に対して、せん断方向の負荷を印加して破断させた後、破断面を観察し、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性を評価した。なお、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性は、以下の基準で判定した。
試験片を作製してから24時間後に、試験片のせん断接着試験を実施した。具体的には、オートグラフ(島津製作所製)を用いて、グラスアイオノマーセメントの硬化体と、コンポジットレジンの硬化体の接合面に対して、せん断方向の負荷を印加して破断させた後、破断面を観察し、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性を評価した。なお、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性は、以下の基準で判定した。
優:グラスアイオノマーセメントの硬化体が凝集破壊している場合
不可:グラスアイオノマーセメントの硬化体と、コンポジットレジンの硬化体の界面で破壊している場合
[コンポジットレジンの硬化体の曲げ強さ]
(試験片の作製)
25mm×2mm×2mmのステンレス鋼製の金型にコンポジットレジンを充填した後、プラスチックフィルムを介して、スライドガラスで挟んで圧接した。歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、スライドガラス越しに、光を照射して、コンポジットレジンを硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、コンポジットレジンの全体に光が照射されるまで繰り返し、2枚のスライドガラス越しに、同様に光を照射した。次に、プラスチックフィルムを除去した後、金型から試験片を取り出した。次に、耐水研磨紙(#320)を用いて、バリを除去した後、37℃の水中で試験片を保管した。
不可:グラスアイオノマーセメントの硬化体と、コンポジットレジンの硬化体の界面で破壊している場合
[コンポジットレジンの硬化体の曲げ強さ]
(試験片の作製)
25mm×2mm×2mmのステンレス鋼製の金型にコンポジットレジンを充填した後、プラスチックフィルムを介して、スライドガラスで挟んで圧接した。歯科用LED光照射器GライトプリマII(ジーシー製)を用いて、スライドガラス越しに、光を照射して、コンポジットレジンを硬化させた。このとき、光を10秒間照射した後、照射窓の直径の半分ずつずらす操作を、コンポジットレジンの全体に光が照射されるまで繰り返し、2枚のスライドガラス越しに、同様に光を照射した。次に、プラスチックフィルムを除去した後、金型から試験片を取り出した。次に、耐水研磨紙(#320)を用いて、バリを除去した後、37℃の水中で試験片を保管した。
(曲げ試験)
ISO 4049:2009 7.11に準じて、試験片の曲げ試験を実施した。具体的には、37℃の水から試験片を取り出した後、マイクロメータを用いて、試験片の寸法を測定した。次に、試験片を作製してから24時間後に、オートグラフ(島津製作所製)を用いて、クロスヘッドスピード1mm/minの条件で、試験片の曲げ強さを測定した。
ISO 4049:2009 7.11に準じて、試験片の曲げ試験を実施した。具体的には、37℃の水から試験片を取り出した後、マイクロメータを用いて、試験片の寸法を測定した。次に、試験片を作製してから24時間後に、オートグラフ(島津製作所製)を用いて、クロスヘッドスピード1mm/minの条件で、試験片の曲げ強さを測定した。
表1に、辺縁漏洩、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性、コンポジットレジンの硬化体の曲げ強さの評価結果を示す。
これに対して、比較例1の歯科用修復材セットは、ボンディング材と、酸基を有する(メタ)アクリレートを含まないコンポジットレジンを有するため、歯を修復する手順が煩雑になる。
また、比較例2、3の歯科用修復材セットは、ボンディング材を有さず、酸基を有する(メタ)アクリレートを含まないコンポジットレジンを有するため、グラスアイオノマーセメントの硬化体に対するコンポジットレジンの硬化体の接着性が低く、辺縁漏洩が発生する。
本願は、日本特許庁に2019年3月27日に出願された基礎出願2019-061731号の優先権を主張するものであり、その全内容を参照によりここに援用する。
1 グラスアイオノマーセメントの硬化体
2、2a、2b コンポジットレジンの硬化体
C 窩洞
D 象牙質
E エナメル質
2、2a、2b コンポジットレジンの硬化体
C 窩洞
D 象牙質
E エナメル質
Claims (9)
- グラスアイオノマーセメントと、
コンポジットレジンを有し、
前記コンポジットレジンは、酸基を有する(メタ)アクリレートを含む、歯科用修復材セット。 - 前記コンポジットレジンは、酸基を有さない(メタ)アクリレートと、光重合開始剤と、フィラーをさらに含む、請求項1に記載の歯科用修復材セット。
- 前記フィラーの含有量が30質量%以上である、請求項2に記載の歯科用修復材セット。
- 前記グラスアイオノマーセメントは、フルオロアルミノシリケートガラス粉末と、ポリカルボン酸系重合体、水、(メタ)アクリレート及び光重合開始剤を含む液状組成物とを有する、請求項1に記載の歯科用修復材セット。
- エッチング材をさらに有する、請求項1に記載の歯科用修復材セット。
- 歯の所定の領域に、グラスアイオノマーセメントを適用する工程と、
該適用されたグラスアイオノマーセメントを硬化させる工程と、
該グラスアイオノマーセメントが硬化した歯の所定の領域に、コンポジットレジンを適用する工程と、
該適用されたコンポジットレジンを硬化させる工程を含み、
前記コンポジットレジンは、酸基を有する(メタ)アクリレートを含む、歯の修復方法。 - 前記グラスアイオノマーセメントは、フルオロアルミノシリケートガラス粉末と、ポリカルボン酸系重合体、水、(メタ)アクリレート及び光重合開始剤を含む液状組成物とを有し、
前記適用されたグラスアイオノマーセメントに光を照射して硬化させる、請求項6に記載の歯の修復方法。 - 前記コンポジットレジンは、酸基を有さない(メタ)アクリレートと、光重合開始剤と、フィラーをさらに含み、
前記適用されたコンポジットレジンに光を照射して硬化させる、請求項6に記載の歯の修復方法。 - 前記歯の所定の領域に、エッチング材を適用する工程をさらに含み、
該エッチング材が適用された歯の所定の領域に、前記コンポジットレジンを適用する、請求項6に記載の歯の修復方法。