WO2020127105A1 - Couche adhésive aqueuse - Google Patents

Couche adhésive aqueuse Download PDF

Info

Publication number
WO2020127105A1
WO2020127105A1 PCT/EP2019/085430 EP2019085430W WO2020127105A1 WO 2020127105 A1 WO2020127105 A1 WO 2020127105A1 EP 2019085430 W EP2019085430 W EP 2019085430W WO 2020127105 A1 WO2020127105 A1 WO 2020127105A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive layer
polyurethane
overlay
support
core
Prior art date
Application number
PCT/EP2019/085430
Other languages
English (en)
Inventor
Nick VALCKX
Emily May
Hubertus Van Aert
Original Assignee
Agfa-Gevaert Nv
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Agfa-Gevaert Nv filed Critical Agfa-Gevaert Nv
Publication of WO2020127105A1 publication Critical patent/WO2020127105A1/fr

Abstract

L'invention concerne une couche adhésive aqueuse comprenant un premier et un second liant, caractérisée en ce que le premier liant comprend un polymère hybride polyuréthane-acrylate, la partie polyuréthane ayant une température de transition vitreuse (Tg) comprise entre -75°C et 20°C et la partie acrylate ayant une Tg comprise entre 65°C et 200°C, et le second liant étant un polyuréthane aliphatique.
PCT/EP2019/085430 2018-12-21 2019-12-16 Couche adhésive aqueuse WO2020127105A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP18215160.5 2018-12-21
EP18215160 2018-12-21

Publications (1)

Publication Number Publication Date
WO2020127105A1 true WO2020127105A1 (fr) 2020-06-25

Family

ID=64755430

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2019/085430 WO2020127105A1 (fr) 2018-12-21 2019-12-16 Couche adhésive aqueuse

Country Status (1)

Country Link
WO (1) WO2020127105A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116529326A (zh) * 2021-03-16 2023-08-01 三菱化学株式会社 水性树脂分散体、其制造方法及含有所述分散体的油墨

Citations (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB811066A (en) 1956-05-18 1959-03-25 Ici Ltd Biaxially oriented films
US3649336A (en) 1967-09-28 1972-03-14 Agfa Gevaert Nv Plural coated sheet material
GB1441591A (en) 1972-07-17 1976-07-07 Agfa Gevaert Process for adhering hydrophilic layers to dimensionally stable polyester film support
EP1034922A1 (fr) * 1999-03-11 2000-09-13 Agfa-Gevaert N.V. Document de sécurité comprenant une couche barrière
WO2002074548A2 (fr) 2001-03-16 2002-09-26 Sherwood Technology Ltd. Compositions pouvant etre marquees au laser
WO2006018640A1 (fr) 2004-08-20 2006-02-23 Datalase Ltd. Impression polychrome
WO2006042714A1 (fr) 2004-10-15 2006-04-27 Ticona Gmbh Matieres moulables marquables au laser ; produits obtenus a partir de ces matieres et procede de marquage au laser
WO2006052842A2 (fr) 2004-11-09 2006-05-18 The Trustees Of The University Of Pennsylvania Methodes de diagnostic de syndromes myelodysplasiques (mds)
WO2007141522A1 (fr) 2006-06-08 2007-12-13 Datalase Ltd. Marquage laser
WO2008030428A2 (fr) 2006-09-05 2008-03-13 Fujifilm Hunt Chemicals U.S.A., Inc. Compositions destinées à la formation d'un revêtement marquable par laser et matériau marquable par laser contenant des additifs organiques favorisant l'absorption
US20080238086A1 (en) 2007-03-27 2008-10-02 Ingrid Geuens Security document with a transparent pattern and a process for producing a security document with a transparent pattern
WO2009063058A1 (fr) 2007-11-15 2009-05-22 Agfa-Gevaert Nv Lamelle de polyester à orientation biaxiale pour laminés de sûreté
EP2314636A1 (fr) * 2009-10-23 2011-04-27 Universidad Del Pais Vasco-Euskal Herriko Unibertsitatea Adhésifs hybrides polyuréthane/acrylique aqueux
EP2335967A2 (fr) 2009-12-19 2011-06-22 Rehau AG + Co Pièce intercalaire pour système de barres conductrices
EP2374602A1 (fr) 2010-04-08 2011-10-12 Agfa-Gevaert Laminés de sécurité à base Pet-C et documents
WO2012114121A2 (fr) 2011-02-24 2012-08-30 Datalase Ltd. Diacétylènes activables de façon réversible et leur utilisation à titre de chromogènes
EP2567812A1 (fr) 2011-09-12 2013-03-13 Agfa-Gevaert Laminés de sécurité à base Pet-C et documents
EP2648920A1 (fr) 2010-12-07 2013-10-16 Agfa-Gevaert Marquage laser couleur d'articles et précurseurs de documents de sécurité
WO2014057018A1 (fr) 2012-10-11 2014-04-17 Agfa-Gevaert Colorants infrarouges pour marquage au laser
WO2014124052A1 (fr) 2013-02-06 2014-08-14 Fujifilm Hunt Chemicals, Inc. Revêtement chimique destiné à un matériau pouvant subir un marquage au laser
US20150284598A1 (en) * 2014-04-07 2015-10-08 Avery Dennison Corporation Compositions for Removable Labels

Patent Citations (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB811066A (en) 1956-05-18 1959-03-25 Ici Ltd Biaxially oriented films
US3649336A (en) 1967-09-28 1972-03-14 Agfa Gevaert Nv Plural coated sheet material
GB1441591A (en) 1972-07-17 1976-07-07 Agfa Gevaert Process for adhering hydrophilic layers to dimensionally stable polyester film support
EP1034922A1 (fr) * 1999-03-11 2000-09-13 Agfa-Gevaert N.V. Document de sécurité comprenant une couche barrière
WO2002074548A2 (fr) 2001-03-16 2002-09-26 Sherwood Technology Ltd. Compositions pouvant etre marquees au laser
WO2006018640A1 (fr) 2004-08-20 2006-02-23 Datalase Ltd. Impression polychrome
WO2006042714A1 (fr) 2004-10-15 2006-04-27 Ticona Gmbh Matieres moulables marquables au laser ; produits obtenus a partir de ces matieres et procede de marquage au laser
WO2006052842A2 (fr) 2004-11-09 2006-05-18 The Trustees Of The University Of Pennsylvania Methodes de diagnostic de syndromes myelodysplasiques (mds)
WO2007141522A1 (fr) 2006-06-08 2007-12-13 Datalase Ltd. Marquage laser
WO2008030428A2 (fr) 2006-09-05 2008-03-13 Fujifilm Hunt Chemicals U.S.A., Inc. Compositions destinées à la formation d'un revêtement marquable par laser et matériau marquable par laser contenant des additifs organiques favorisant l'absorption
US20080238086A1 (en) 2007-03-27 2008-10-02 Ingrid Geuens Security document with a transparent pattern and a process for producing a security document with a transparent pattern
WO2009063058A1 (fr) 2007-11-15 2009-05-22 Agfa-Gevaert Nv Lamelle de polyester à orientation biaxiale pour laminés de sûreté
EP2314636A1 (fr) * 2009-10-23 2011-04-27 Universidad Del Pais Vasco-Euskal Herriko Unibertsitatea Adhésifs hybrides polyuréthane/acrylique aqueux
EP2335967A2 (fr) 2009-12-19 2011-06-22 Rehau AG + Co Pièce intercalaire pour système de barres conductrices
EP2374602A1 (fr) 2010-04-08 2011-10-12 Agfa-Gevaert Laminés de sécurité à base Pet-C et documents
EP2648920A1 (fr) 2010-12-07 2013-10-16 Agfa-Gevaert Marquage laser couleur d'articles et précurseurs de documents de sécurité
WO2012114121A2 (fr) 2011-02-24 2012-08-30 Datalase Ltd. Diacétylènes activables de façon réversible et leur utilisation à titre de chromogènes
EP2567812A1 (fr) 2011-09-12 2013-03-13 Agfa-Gevaert Laminés de sécurité à base Pet-C et documents
US20140193638A1 (en) * 2011-09-12 2014-07-10 Agfa-Gevaert N.V. PET-C Based Security Laminates and Documents
WO2014057018A1 (fr) 2012-10-11 2014-04-17 Agfa-Gevaert Colorants infrarouges pour marquage au laser
WO2014124052A1 (fr) 2013-02-06 2014-08-14 Fujifilm Hunt Chemicals, Inc. Revêtement chimique destiné à un matériau pouvant subir un marquage au laser
US20150284598A1 (en) * 2014-04-07 2015-10-08 Avery Dennison Corporation Compositions for Removable Labels

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
"Glossary of Security Documents - Security features and other related technical terms", CONSILIUM OF THE COUNCIL OF THE EUROPEAN UNION, 25 August 2008 (2008-08-25), Retrieved from the Internet <URL:http://www.consilium.europa.eu/prado/EN/glossaryPopup.html>

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116529326A (zh) * 2021-03-16 2023-08-01 三菱化学株式会社 水性树脂分散体、其制造方法及含有所述分散体的油墨

Similar Documents

Publication Publication Date Title
EP2335937B1 (fr) Film de sécurité pouvant être marqué au laser
EP2567825B1 (fr) Procédés de marquage laser en couleur de précurseurs de documents de sécurité
US8973830B2 (en) PET-C based security laminates and documents
CN102202908A (zh) 安全证件和生产安全证件的方法
CN101254671A (zh) 可激光标记的膜
WO2009071068A2 (fr) Procédé de fabrication d&#39;un document de sécurité et/ou de valeur comportant des informations personnalisées
EP3075559B1 (fr) Feuille transparente de marquage au laser, stratifié, et procédé pour marquage au laser
EP2725063A1 (fr) Feuille pour carte
EP2335938B1 (fr) Film de sécurité pouvant être marqué au laser
WO2020127105A1 (fr) Couche adhésive aqueuse
EP2567812B1 (fr) Laminés de sécurité à base Pet-C et documents
CN100568107C (zh) 具有有光泽且可写的面的电子照相印刷品
WO2020126753A1 (fr) Couche adhésive aqueuse
KR20230092915A (ko) 가시적 보안 요소로서의 각인을 갖는 층 구조물
EP3489030B1 (fr) Procédé permettant de fournir un élément de sécurité sur un document de sécurité par marquage au laser
WO2015040055A1 (fr) Procédé de production d&#39;un signe de sécurité d&#39;un produit de valeur ou de sécurité et procédé de fabrication d&#39;un tel produit
WO2022215386A1 (fr) Corps stratifié, carte, passeport et leur procédé de fabrication
JP2007007979A (ja) 被記録材
JP2003141491A (ja) Ｉｃカード
JP2003108957A (ja) Ｉｃカード
WO2018215420A1 (fr) Feuilles avec un revêtement résistant aux rayures en tant que couche supérieure et composite stratifié comprenant de telles feuilles

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19818106

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19818106

Country of ref document: EP

Kind code of ref document: A1