WO2020120799A1 - Remplissage de gazon artificiel et gazon artificiel - Google Patents
Remplissage de gazon artificiel et gazon artificiel Download PDFInfo
- Publication number
- WO2020120799A1 WO2020120799A1 PCT/EP2019/085381 EP2019085381W WO2020120799A1 WO 2020120799 A1 WO2020120799 A1 WO 2020120799A1 EP 2019085381 W EP2019085381 W EP 2019085381W WO 2020120799 A1 WO2020120799 A1 WO 2020120799A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- particles
- coating
- turf
- artificial turf
- infill
- Prior art date
Abstract
Priority Applications (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CA3118800A CA3118800A1 (fr) | 2018-12-14 | 2019-12-16 | Remplissage de gazon artificiel et gazon artificiel |
AU2019398780A AU2019398780B2 (en) | 2018-12-14 | 2019-12-16 | Artificial turf infill and artificial turf |
US17/299,830 US20220042252A1 (en) | 2018-12-14 | 2019-12-16 | Artificial turf infill and artificial turf |
EP19817754.5A EP3894632A1 (fr) | 2018-12-14 | 2019-12-16 | Remplissage de gazon artificiel et gazon artificiel |
AU2023202696A AU2023202696A1 (en) | 2018-12-14 | 2023-05-02 | Artificial turf infill and artificial turf |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP18212783.7 | 2018-12-14 | ||
EP18212783.7A EP3666976B1 (fr) | 2018-12-14 | 2018-12-14 | Matériau de remplissage de gazon artificiel et gazon artificiel |
EP18212778.7 | 2018-12-14 | ||
EP18212778.7A EP3666975A1 (fr) | 2018-12-14 | 2018-12-14 | Gazon artificiel et matériau de remplissage pour gazon artificiel |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2020120799A1 true WO2020120799A1 (fr) | 2020-06-18 |
Family
ID=68841143
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2019/085381 WO2020120799A1 (fr) | 2018-12-14 | 2019-12-16 | Remplissage de gazon artificiel et gazon artificiel |
PCT/EP2019/085384 WO2020120800A1 (fr) | 2018-12-14 | 2019-12-16 | Remplissage de gazon synthétique et gazon synthétique |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2019/085384 WO2020120800A1 (fr) | 2018-12-14 | 2019-12-16 | Remplissage de gazon synthétique et gazon synthétique |
Country Status (6)
Country | Link |
---|---|
US (1) | US20220042252A1 (fr) |
EP (1) | EP3894632A1 (fr) |
AU (2) | AU2019398780B2 (fr) |
CA (1) | CA3118800A1 (fr) |
MA (1) | MA54444A (fr) |
WO (2) | WO2020120799A1 (fr) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112746547A (zh) * | 2020-12-08 | 2021-05-04 | 江苏联创人造草坪股份有限公司 | 一种运动型人造草坪及其制备方法 |
EP4008432A2 (fr) | 2020-11-13 | 2022-06-08 | Pigmentsolution GmbH | Granulés de linoléum pour l'usage extérieur |
WO2022234142A1 (fr) * | 2021-05-07 | 2022-11-10 | Goe-Ip As | Particule de remplissage pour gazon artificiel, procédé de production d'une telle particule de remplissage et utilisation de ladite particule de remplissage |
IT202100021329A1 (it) * | 2021-08-05 | 2023-02-05 | Adalberto Principi | Processo per la realizzazione di materiale riempitivo per manti erbosi sintetici, relativa struttura e composizione |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4337283A (en) * | 1980-09-11 | 1982-06-29 | Haas Jr Frederick T | Synthetic turf playing surface with resilient top-dressing |
US20120258811A1 (en) * | 2009-02-09 | 2012-10-11 | Sapturf, Llc | Synthetic turf having cooling layer |
EP2749350A2 (fr) * | 2012-12-28 | 2014-07-02 | Benoit Pintat | Composition destinée à réguler la présence d'eau sur une surface extérieure |
KR20140112167A (ko) * | 2013-03-13 | 2014-09-23 | 김동현 | 인조잔디 충진용 sebs 고무칩 제조방법 및 그 방법에 따른 sebs 고무칩 |
US20150308056A1 (en) * | 2014-04-25 | 2015-10-29 | Profile Products Llc | Artificial turf field system |
EP3216821A1 (fr) * | 2016-03-11 | 2017-09-13 | Polytex Sportbeläge Produktions-GmbH | Remplissage de gazon artificiel |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6582819B2 (en) * | 1998-07-22 | 2003-06-24 | Borden Chemical, Inc. | Low density composite proppant, filtration media, gravel packing media, and sports field media, and methods for making and using same |
JP4417903B2 (ja) * | 2005-11-22 | 2010-02-17 | ヨコハマポリマー化成株式会社 | 人工芝構造体及び人工芝競技場 |
KR100995211B1 (ko) * | 2009-10-26 | 2010-11-17 | 마명열 | 천연 코르크를 이용한 인조잔디용 탄성 칩 조성물 및 제조방법 |
WO2012058555A2 (fr) * | 2010-10-29 | 2012-05-03 | The Quantum Group, Inc. | Systèmes de gazon artificiel et applications associées |
US9683334B2 (en) * | 2015-05-15 | 2017-06-20 | Covestro Llc | Free-flowing coated rubber particles, methods for their production and use |
KR101800412B1 (ko) * | 2017-06-13 | 2017-11-22 | 강태순 | 인조잔디 충진재 및 이의 제조방법 |
-
2019
- 2019-12-16 EP EP19817754.5A patent/EP3894632A1/fr not_active Withdrawn
- 2019-12-16 WO PCT/EP2019/085381 patent/WO2020120799A1/fr unknown
- 2019-12-16 US US17/299,830 patent/US20220042252A1/en active Pending
- 2019-12-16 MA MA054444A patent/MA54444A/fr unknown
- 2019-12-16 AU AU2019398780A patent/AU2019398780B2/en not_active Ceased
- 2019-12-16 WO PCT/EP2019/085384 patent/WO2020120800A1/fr active Application Filing
- 2019-12-16 CA CA3118800A patent/CA3118800A1/fr active Pending
-
2023
- 2023-05-02 AU AU2023202696A patent/AU2023202696A1/en not_active Abandoned
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4337283A (en) * | 1980-09-11 | 1982-06-29 | Haas Jr Frederick T | Synthetic turf playing surface with resilient top-dressing |
US20120258811A1 (en) * | 2009-02-09 | 2012-10-11 | Sapturf, Llc | Synthetic turf having cooling layer |
EP2749350A2 (fr) * | 2012-12-28 | 2014-07-02 | Benoit Pintat | Composition destinée à réguler la présence d'eau sur une surface extérieure |
KR20140112167A (ko) * | 2013-03-13 | 2014-09-23 | 김동현 | 인조잔디 충진용 sebs 고무칩 제조방법 및 그 방법에 따른 sebs 고무칩 |
US20150308056A1 (en) * | 2014-04-25 | 2015-10-29 | Profile Products Llc | Artificial turf field system |
EP3216821A1 (fr) * | 2016-03-11 | 2017-09-13 | Polytex Sportbeläge Produktions-GmbH | Remplissage de gazon artificiel |
WO2017153261A1 (fr) | 2016-03-11 | 2017-09-14 | Polytex Sportbeläge Produktions-Gmbh | Remplissage de gazon artificiel et son procédé de fabrication |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP4008432A2 (fr) | 2020-11-13 | 2022-06-08 | Pigmentsolution GmbH | Granulés de linoléum pour l'usage extérieur |
CN112746547A (zh) * | 2020-12-08 | 2021-05-04 | 江苏联创人造草坪股份有限公司 | 一种运动型人造草坪及其制备方法 |
WO2022234142A1 (fr) * | 2021-05-07 | 2022-11-10 | Goe-Ip As | Particule de remplissage pour gazon artificiel, procédé de production d'une telle particule de remplissage et utilisation de ladite particule de remplissage |
IT202100021329A1 (it) * | 2021-08-05 | 2023-02-05 | Adalberto Principi | Processo per la realizzazione di materiale riempitivo per manti erbosi sintetici, relativa struttura e composizione |
EP4130382A1 (fr) * | 2021-08-05 | 2023-02-08 | Adalberto Principi | Procédé de fabrication de matériau de remplissage pour gazon synthétique, matériau de remplissage pour gazon synthétique et substance de revêtement |
Also Published As
Publication number | Publication date |
---|---|
WO2020120800A1 (fr) | 2020-06-18 |
AU2023202696A1 (en) | 2023-05-18 |
AU2019398780A1 (en) | 2021-07-01 |
CA3118800A1 (fr) | 2020-06-18 |
MA54444A (fr) | 2022-03-23 |
AU2019398780B2 (en) | 2023-02-02 |
EP3894632A1 (fr) | 2021-10-20 |
US20220042252A1 (en) | 2022-02-10 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AU2019398780B2 (en) | Artificial turf infill and artificial turf | |
AU2017229156B2 (en) | Artificial turf infill and method for making it | |
US20240060248A1 (en) | Artificial turf infill with natural fiber and rubber granulate | |
KR102031639B1 (ko) | 환경 친화형 탄성 충진제가 포함된 인조잔디 | |
KR102374726B1 (ko) | 인조잔디 구조체 | |
US20190292731A1 (en) | Natural fiber coated artificial turf infill | |
EP3604677A1 (fr) | Matériau de remplissage de gazon artificiel avec des granulés d'épi de maïs revêtus de polyuréthane | |
EP3666976B1 (fr) | Matériau de remplissage de gazon artificiel et gazon artificiel | |
EP3666975A1 (fr) | Gazon artificiel et matériau de remplissage pour gazon artificiel | |
US20200216673A1 (en) | Thermoplastic synthetic turf infill comprising organic filler | |
EP3336251A1 (fr) | Materiau de remplissage de gazon artificiel avec des fibres naturelles et des granulés de caoutchouc | |
US11946206B2 (en) | Artificial turf system and support layer | |
KR101926680B1 (ko) | 친환경 인조잔디용 충진재 조성물 | |
KR101729307B1 (ko) | 롤 시트 전용 접착제, 그 제조방법 및 이를 이용한 체육시설 탄성포장재 제조방법 | |
EP3604676A1 (fr) | Matériau de remplissage de gazon artificiel avec des granulés de coques dures de noix enrobés de pu |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19817754 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 3118800 Country of ref document: CA |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 2019398780 Country of ref document: AU Date of ref document: 20191216 Kind code of ref document: A |
|
ENP | Entry into the national phase |
Ref document number: 2019817754 Country of ref document: EP Effective date: 20210714 |