WO2020026311A1 - 非燃焼加熱型喫煙物品用の巻紙、非燃焼加熱型喫煙物品及び電気加熱型喫煙システム - Google Patents

非燃焼加熱型喫煙物品用の巻紙、非燃焼加熱型喫煙物品及び電気加熱型喫煙システム Download PDF

Info

Publication number
WO2020026311A1
WO2020026311A1 PCT/JP2018/028489 JP2018028489W WO2020026311A1 WO 2020026311 A1 WO2020026311 A1 WO 2020026311A1 JP 2018028489 W JP2018028489 W JP 2018028489W WO 2020026311 A1 WO2020026311 A1 WO 2020026311A1
Authority
WO
WIPO (PCT)
Prior art keywords
wrapping paper
heating
smoking article
paper
filler
Prior art date
Application number
PCT/JP2018/028489
Other languages
English (en)
French (fr)
Inventor
亨 櫻井
徳子 大澤
Original Assignee
日本たばこ産業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本たばこ産業株式会社 filed Critical 日本たばこ産業株式会社
Priority to PCT/JP2018/028489 priority Critical patent/WO2020026311A1/ja
Priority to EP18928607.3A priority patent/EP3832013A4/en
Priority to JP2020533910A priority patent/JP7105889B2/ja
Publication of WO2020026311A1 publication Critical patent/WO2020026311A1/ja

Abstract

２３０℃で３分間加熱する前と後のＣＩＥＬａｂ表色系における色差値を、以下の式（１）に代入して得られる判別得点が０．６２よりも低い数値を示し、ＩＳＯ白色度が８３％以上である白色部を有する、非燃焼加熱型喫煙物品用の巻紙を提供する。 判別得点（ｙ）　ｙ＝－０．１８×ΔＬ＊＋０．０８×Δａ＊＋０．１３×Δｂ＊－２．３６　（１）　（式（１）において、加熱する前と後のＣＩＥＬａｂ表色系における色差値とは、加熱した後のＬ＊、ａ＊、ｂ＊値から加熱前のＬ＊、ａ＊、ｂ＊値を引いた値である。ΔＬ＊は、前記巻紙を加熱した後と加熱する前の明度Ｌ＊の差を示し、Δａ＊は、前記巻紙を加熱した後と加熱する前の色度ａ＊の差を示し、Δｂ＊は、前記巻紙を加熱した後と加熱する前の色度ｂ＊の差を示す。）

Description

非燃焼加熱型喫煙物品用の巻紙、非燃焼加熱型喫煙物品及び電気加熱型喫煙システム
　本発明は、非燃焼加熱型喫煙物品用の巻紙、非燃焼加熱型喫煙物品及び電気加熱型喫煙システムに関する。
　たばこ刻みを含むたばこロッドの周囲から加熱を行い、揮発成分を使用者にデリバリーするタイプの非燃焼加熱型喫煙物品が知られている。非燃焼加熱型喫煙物品では、巻紙で巻装されたたばこロッドが加熱されるが、従来のシガレットとは異なり、使用後（加熱後）もたばこロッドは燃焼せずに残る。
　従来のシガレットでは、たばこ刻みを巻装するための巻紙としては、ロゴなどが付されている場合はあるものの、白色（無色）の紙を用いることが一般的である。
　非燃焼加熱型喫煙物品において、たばこ刻みを巻装する巻紙として従来のシガレットで用いられてきた巻紙を用いると、使用時の加熱によって、使用者にとって不快な変色が生じる場合があることが分かった。この課題に対して、特定の有色紙を使用して変色を目立たなくする方法もあるが、汎用性の高い白色の紙を使用するには別の工夫が必要であることが分かった。
　そこで本発明では、加熱によって発生し得る見た目に関する不快感が生じない、非燃焼加熱型喫煙物品用の巻紙を提供することを課題とする。
　上記の課題を解決するために、本発明者は、加熱前に特定の白色度を有しつつ、加熱後に特定範囲の変色域を持つ白色部を有する巻紙であることで、その不快な変色が目立たなくなることに着目した。
　パルプを主材料とする紙は、一定以上の温度で加熱されれば焦げて茶系に変色するが、原因がパルプや紙の構成成分の熱分解による物理的なものであることから、そういった変色を簡単に防ぐことはできない。しかしながら、焦げによる変色が生じたとしても、元の紙の色とそこからの変色程度が一定範囲で小さければ、不快な焦げ色として視認しにくくすることができることを見出した。
　本発明者は、この視覚的に変色程度の許容される色差変化の領域が数式で表されることを発見し、その数式に、加熱前後のＬ＊、ａ＊、ｂ＊の各値を当てはめた場合に特定の数値を示し、かつ、加熱前に特定の白色度の白色部を有する紙を巻紙として使用することで、非燃焼加熱型喫煙物品に特有の不快な変色に関わる問題を解決できることを見出した。
　具体的には、本発者は、加熱前のＩＳＯ白色度が８３％以上であり、かつ、加熱前後で色差の小さい白色部を有する紙を使用すれば、上記の不快な変色の問題を解決することができることを見出した。
　本発明の課題は、電気加熱型デバイスにより加熱される非燃焼加熱型喫煙物品に特有のものであり、従来の喫煙物品（シガレット等）では生じなかった課題である。
　すなわち、本発明は、以下のとおりである。
［１］　２３０℃で３分間加熱する前と後のＣＩＥＬａｂ表色系における色差値を、以下の式（１）に代入して得られる判別得点が０．６２よりも低い数値を示し、ＩＳＯ白色度が８３％以上である白色部を有する、非燃焼加熱型喫煙物品用の巻紙。
判別得点（ｙ）　ｙ＝－０．１８×ΔＬ＊＋０．０８×Δａ＊＋０．１３×Δｂ＊－２．３６　（１）
　（式（１）において、加熱する前と後のＣＩＥＬａｂ表色系における色差値とは、加熱した後のＬ＊、ａ＊、ｂ＊値から加熱前のＬ＊、ａ＊、ｂ＊値を引いた値である。ΔＬ＊は、前記巻紙を加熱した後と加熱する前の明度Ｌ＊の差を示し、Δａ＊は、前記巻紙を加熱した後と加熱する前の色度ａ＊の差を示し、Δｂ＊は、前記巻紙を加熱した後と加熱する前の色度ｂ＊の差を示す。）
［２］　前記非燃焼加熱型喫煙物品用の巻紙が填料を含有し、填料の含有量が１５～４５重量％であり、前記非燃焼加熱型喫煙物品用の巻紙の坪量が２５～４５ｇｓｍであって、
坪量が２５ｇｓｍ以上３５ｇｓｍ以下のとき、填料が１５～４５重量％であり、
坪量が３５ｇｓｍを超えて４５ｇｓｍ以下のとき、填料が２５～４５重量％である、［１］に記載の非燃焼加熱型喫煙物品用の巻紙。
［３］　引張強度が８Ｎ／１５ｍｍ以上である、［１］または［２］に記載の非燃焼加熱型喫煙物品用の巻紙。
［４］　前記填料が炭酸カルシウムであり、前記巻紙の不透明度が６０％以上である、［２］または［３］に記載の非燃焼加熱型喫煙物品用の巻紙。
［５］　前記白色部の判別得点が０未満である、［１］～「４」のいずれかに記載の非燃焼加熱型喫煙物品用の巻紙。
［６］　前記巻紙が、助燃剤を含まない、［１］～［５］のいずれかに記載の非燃焼加熱型喫煙物品用の巻紙。
［７］　たばこ刻みとエアロゾル生成基材とを含む充填物が、該充填物を巻装する第一の巻紙で巻装されてなるたばこロッド部と、該たばこロッド部とは反対側の端部を構成するマウスピース部とを有し、前記たばこロッド部と前記マウスピース部は、前記充填物を巻装する巻紙と同じ又は別の第二の巻紙を用いて連結されている非燃焼加熱型喫煙物品であって、第１の巻紙と第２の巻紙の少なくとも一方が、［１］～［６］のいずれか一項に記載の巻紙である、非燃焼加熱型喫煙物品。
［８］　ヒーター部材と、該ヒーター部材からの熱を伝熱する伝熱部材と、該ヒーター部材の電力源となる電池ユニットと、該ヒーター部材を制御するための制御ユニットとを備える電気加熱型デバイスと、該伝熱部材に接触するように嵌合される、［７］に記載の非燃焼加熱型喫煙物品と、から構成される、電気加熱型喫煙システム。
　本発明によれば、加熱によって発生し得る見た目に関する不快感が生じない、非燃焼加熱型喫煙物品用の巻紙を提供できる。
非燃焼加熱型喫煙物品の一態様を示す概略図である。 非燃焼加熱型喫煙物品の別の一態様を示す概略図である。 電気加熱型喫煙システムの一態様を示す概略図である。 各紙サンプルの加熱前後のΔＬ＊値と外観印象の関係を示す図である。 各紙サンプルの加熱前後のΔａ＊値と外観印象の関係を示す図である。 各紙サンプルの加熱前後のΔｂ＊値と外観印象の関係を示す図である。 加熱前後の各紙サンプルのＬ＊、ａ＊、ｂ＊のΔ値と外観印象の関係を用いて行った判別分析の結果を示す図である。 加熱前後の各紙サンプルのΔａ＊値とΔｂ＊値の関係を示す図である。 巻紙における填料の含有量と判別得点の関係を坪量ごとにプロットした図である。
　以下、本発明について実施形態及び例示物等を示して詳細に説明するが、本発明は以下の実施形態及び例示物等に限定されるものではなく、本発明の要旨を逸脱しない範囲において任意に変更して実施できる。
＜非燃焼加熱型喫煙物品用の巻紙＞
　本明細書において、「非燃焼加熱型喫煙物品用の巻紙」とは、後述する非燃焼加熱型喫煙物品に用いられる巻紙である。以下、単に本発明の実施形態にかかる巻紙ともいう。本発明の実施形態にかかる巻紙の用途について、「非燃焼加熱型喫煙物品用」とは、たばこ刻みを含む充填物を巻装してたばこロッドを作製するために用いられたり、たばこロッドに隣接する部材を連結するために、それらの外周面を巻装するために用いられることを意味する。
　本発明の実施形態にかかる巻紙は、２３０℃で３分間加熱する前と後（単に加熱前後ともいう）でＬ＊、ａ＊、ｂ＊をそれぞれ測定し、加熱前後の各値の差（加熱後の値から加熱前の値を引いた値）を、それぞれΔＬ＊、Δａ＊、Δｂ＊と表現し、それらの値を以下の式（１）に代入して得られるｙ（判別得点）が、０．６２よりも小さい値を有し、ＩＳＯ白色度が８３％以上である白色部を有する。
　ｙ（判別得点）＝－０．１８×ΔＬ＊＋０．０８×Δａ＊＋０．１３×Δｂ＊－２．３６　（１）
　本発明の実施形態にかかる巻紙は、ΔＬ＊、Δａ＊、Δｂ＊の各値を上記の式（１）に代入して得られる判別得点が０．６２よりも小さい値を示す白色部を有していれば、加熱前のＬ＊、ａ＊、ｂ＊の各値には特に制限はない。
　なお、上記の判別得点を有する白色部は、本発明の実施形態にかかる巻紙の全面に存在してもよいし、少なくとも加熱を受ける部分（後述する電気加熱型デバイスによる加熱）に存在する態様であってもよい。
　ＩＳＯ白色度については、以下の方法により求めることができる。
　ＪＩＳ８１４８：２００１　紙、板紙及びパルプのＩＳＯ白色度（拡散青色光反射率）の測定方法に準拠して、白色度・不透明度測定機（製造者：村上色彩技術研究所、型番：ＷＭＳ－１）を用いて、測定する。
　上記白色部は、加熱前のＬ＊値が高いもの（明るく色の薄いもの）が、ＩＳＯ白色度が８３％以上になる傾向がある。一形態の巻紙では、白色部の加熱前のＬ＊値として、９５％以上であるものを挙げることができる。
　上記式（１）により得られるｙ（判別得点）が０．６２よりも小さければ、加熱によって発生し得る見た目に関する不快感が生じないことは、後の実施例で示されている。なお、上記式（１）により得られるｙ（判別得点）が０未満であると、加熱前後で外観が損なわれないものがより確実に含まれるようになる。
　本発明の実施形態にかかる巻紙において、加熱前後のＬ＊、ａ＊、ｂ＊の各値は、試料とする紙の白色部の５点について測定し、その単純平均の値を採用する。測定の対象とするのは紙の白色部の任意の点であるが、紙にロゴなどの文字や模様が存在する場合には、そのような文字やロゴの存在しない白色部の箇所を対象とする。Ｌ＊、ａ＊、ｂ＊の各値は分光光度計を用いることで測定できる。
　具体的には、分光光度計（Ｘ－Ｒｉｔｅ社製、品名ＳｐｅｃｔｒｏＥｙｅ）を用いる。計測は、光源Ｄ６５、光源フィルタなし、視野角２°の条件下、ＩＳＯ白色度９２％の紙の上に試料１枚を置き、その上に分光光度計の測定部を押し当てて実施する。
　上記の式（１）により得られる判別得点が０．６２より小さい値を示し、ＩＳＯ白色度が８３％以上である白色部を有する紙（上記の特性を有する紙ともいう）を得るための手段については特に制限なく公知の方法を用いることができる。巻紙の全面が判別得点が０．６２より小さい値を示し、ＩＳＯ白色度が８３％以上である白色部を有するものである場合、製紙の段階でパルプ及び填料の種類及び含有量を調整することで、そのような巻紙を製造することができる。具体的には、後述する填料の含有量を増やしたり、有色材料の量を極力用いないことを挙げることができる。
　一方で、巻紙の一部に、加熱後の外観印象を損なわない範囲で有色部を有する場合には、例えば、印刷を施すことで、所望の色相を示す有色部を付与してもよい。印刷の方法は特に制限はなく、例えばグラビア印刷およびオフセット印刷を挙げることができる。有色部は、ＩＳＯ白色度が８３％未満である部分をいう。
　印刷により有色部としてロゴや部分的な模様を原紙に対して付す場合は、その印刷面（印刷箇所）は、分光光度計による測色の対象にはしない。また、巻紙に印刷により有色部を付与する場合、その面積の割合は１０％以下、好ましくは５％以下、より好ましくは３％以下を挙げることができる。逆に言えば、本発明の実施形態にかかる巻紙において、上記の白色部の面積の割合として、９０％以上、好ましくは９５％以上、より好ましくは９７％以上を挙げることができる。一方で、有色部として規則的な模様が付されており、加熱前後で外観印象に影響がない場合には、白色部の面積の割合が、５０％以上であればよいこともある。
　巻紙の表面において、少なくとも加熱される部分（電気加熱型デバイスによる加熱を受ける部分）が上記の式（１）による判別得点が０．６２よりも小さく、かつ、ＩＳＯ白色度が８３％以上であることが好ましい。巻紙の表面の中でも、後述する電気加熱型デバイスにより加熱を受ける部分が上記の特性を有することで、加熱後の外観の印象の悪化を防ぐことができる。
　本発明の実施形態にかかる巻紙原紙の坪量は、例えば通常２０ｇｓｍ以上であり、好ましくは２５ｇｓｍ以上である。一方、坪量は通常６５ｇｓｍ以下、好ましくは５０ｇｓｍ以下、さらに好ましくは４５ｇｓｍ以下、である。坪量と填料の含有量の関係については後述する。
　上記の特性を有する巻紙の厚みは、特に限定されず、剛性、通気性、及び製紙時の調整の容易性の観点から、通常１０μｍ以上であり、好ましくは２０μｍ以上であり、より好ましくは３０μｍ以上であり、また、通常１００μｍ以下であり、好ましくは７５μｍ以下であり、より好ましくは５０μｍ以下である。
　非燃焼加熱型喫煙物品用の巻紙として、その形状は正方形又は長方形を挙げることができる。たばこ刻みを巻装するため（たばこロッドを作製するため）の巻紙として利用する場合、一辺の長さとして１５～７０ｍｍ程度を挙げることができ、もう一辺の長さとして１５～２６．５ｍｍ、もう一辺の好ましい長さとして２４ｍｍを挙げることができる。
　チップペーパーのように、たばこロッドとたばこロッドに隣接するその他の部材を連結して巻装するものである場合、一辺の長さとして２０～６０ｍｍ、もう一辺の長さとして１５～２６．５ｍｍを挙げることができる。
　上記の特性を有する巻紙としては、パルプが主成分のものを挙げることができる。パルプとしては、針葉樹パルプや広葉樹パルプなどの木材パルプで抄造される以外にも、亜麻パルプ、***パルプ、サイザル麻パルプ、エスパルトなど一般的に喫煙物品用の巻紙に使用される非木材パルプを混抄して製造して得たものでもよい。
　パルプの種類としては、クラフト蒸解法、酸性・中性・アルカリ亜硫酸塩蒸解法、ソーダ塩蒸解法等による化学パルプ、グランドパルプ、ケミグランドパルプ、サーモメカニカルパルプ等を使用できる。
　上記パルプを用いて長網抄紙機、円網抄紙機、円短複合抄紙機等による抄紙工程の中で、地合いを整え均一化して巻紙を製造する。なお、必要に応じて、上述した湿潤紙力増強剤を添加して巻紙に耐水性を付与したり、サイズ剤を添加して巻紙の印刷具合の調整を行ったりすることができる。さらに、硫酸バンド、各種のアニオン性、カチオン性、ノニオン性或いは、両性の歩留まり向上剤、濾水性向上剤、及び紙力増強剤等の抄紙用内添助剤、並びに、染料、ｐＨ調整剤、消泡剤、ピッチコントロール剤、及びスライムコントロール剤等の製紙用添加剤を添加することができる。
　上記のパルプの他に、本発明の実施形態にかかる巻紙には填料が含まれる。填料の含有量は、本発明の実施形態にかかる巻紙の全重量に対して１０重量％以上６０重量％未満を挙げることができ、１５～４５重量％であることが好ましい。
　本発明の実施形態にかかる巻紙では、好ましい坪量の範囲（２５～４５ｇｓｍ）において、填料が１５～４５重量％であることが好ましい。
さらに、坪量が２５ｇｓｍ以上３５ｇｓｍ以下のとき、填料が１５～４５重量％であることが好ましく、坪量が３５ｇｓｍを超えて４５ｇｓｍ以下のとき、填料が２５～４５重量％であることが好ましい。
　填料としては、炭酸カルシウム、二酸化チタン、カオリン等を使用することができるが、喫味や白色度を高める観点等から炭酸カルシウムを使用することが好ましい。
　このような填料を含む紙は、通常は白色系の明るい色を呈し、恒久的に白さを保つことができる。そのような填料を多く含有させることで、巻紙のＩＳＯ白色度を８３％以上にすることができる。
　本発明の実施形態にかかる巻紙は、下記の測定法で測定される引張強度が８Ｎ／１５ｍｍ以上であることが、非燃焼加熱型喫煙物品の巻紙として利用する実用上の観点から好ましい。
　この引張強度については、填料の含有量を少なくすることで高めることができる。具体的には、上記で例示した各坪量の範囲において示した填料の含有量の上限よりも填料の含有量を少なくすることで、高めることができる。
＜引張強度の測定法＞
　Ｐ８１１３：２００６（ＩＳＯ１９２４－２：１９９４）　紙及び板紙－引張特性の試験方法－第２部：定速伸張法に準拠して東洋精機製作所製のストログラフＥ－Ｌを用いて、測定する。
　一方、本発明の実施形態にかかる巻紙は、下記の測定法で測定される不透明度が６０％以上であることが好ましい。不透明度は、巻紙における填料の含有量を増加させることで高めることができる。具体的には、上記で例示した各坪量の範囲において示した填料の含有量の下限よりも填料の含有量を多くすることで、高めることができる。
＜不透明度の測定法＞
　不透明度は、白色度・不透明度測定機（製造者：村上色彩技術研究所、型番：ＷＭＳ－１）を用いて、ＩＳＯ２４７１に準拠して測定した値である。不透明度とは、算出式：単一シート視感反射率係数（Ｒ０）／固有視感反射率係数（Ｒ∞）×１００（％）によって算出された値である。この算出式の固有視感反射率係数（Ｒ∞）は、規定の反射率計と光源を用いて有効波長４５７ｎｍ、半値幅４４ｎｍとなる分光条件で測定した時の白色度の固有反射率係数である。
　本発明の実施形態にかかる巻紙には、上記の判別得点を満たすために、従来のたばこロッド用巻紙に含まれる助燃剤が含まれていない方が好ましい。本発明の実施形態にかかる巻紙は、後述する非燃焼加熱型喫煙物品に用いる第一の巻紙として用いてもよく、第二の巻紙として用いてもよい。
＜非燃焼加熱型喫煙物品＞
　本発明の実施形態にかかる非燃焼加熱型喫煙物品として、例えば図１の構成を有するものを挙げることができる。
　図１の非燃焼加熱型喫煙物品１０は、充填物１１と、充填物１１を巻装する第一の巻紙１２から構成されるたばこロッド部と、該たばこロッド部とは反対側の端部を構成するマウスピース部１６とを有し、前記たばこロッド部と前記マウスピース部は、前記充填物を巻装する巻紙と同じ又は別の第二の巻紙１３（図１ではチップペーパー）を用いて連結されている。なお、本発明の実施形態において、第一の巻紙及び第二の巻紙は、それぞれ一枚のみから構成されているものであっても、加熱により焼失したりすることはない。それぞれが一枚のみから構成されている方が、コストを低減することができる。
　第一の巻紙及び第二の巻紙の少なくとも一方は、上記で説明した本発明の実施形態にかかる巻紙である。少なくとも第一の巻紙が、本発明の実施形態にかかる巻紙であることが好ましい。また、第一の巻紙１２及び第二の巻紙の両方が上記で説明した本発明の実施形態にかかる巻紙であることも好ましい。
　図１に示す態様では、マウスピース部１６は、紙管部１４及びフィルター部１５とを備える。また、これらを連結するための第二の巻紙としてチップペーパー１３を備える。なお、図１ではマウスピース部１６は２つのセグメントから構成されているが、マウスピース部１６は単一のセグメントから構成されていてもよく、３つ以上のセグメントから構成されていてもよい。また、マウスピース部を構成するセグメントは、紙管部とフィルター部の両方が含まれるように構成されていてもよいし、どちらかのみから構成されていてもよい。
　図２にマウスピース部１６が３つのセグメントから構成されているものを記載する。図２の実施形態は、図１の紙管部１４とフィルター部１５との間に、中空セグメント部１７を有している。中空セグメント部１７は、１つまたは複数の中空チャネルを有する充填層と、充填層を覆うプラグラッパーとで構成される。充填層は、例えば酢酸セルロース繊維が高密度で充填されトリアセチンを含む可塑剤が酢酸セルロース重量に対して、６～２０重量％添加されて硬化された内径φ４．５～φ１．０ｍｍのロッドとすることができる。充填層は繊維の充填密度が高いため、吸引時は、空気やエアロゾルはチャネル部のみを流れることになり、充填層内はほとんど流れない。非燃焼加熱型喫煙物品において、フィルター部１５でのエアロゾル成分の濾過による減少を少なくしたいときに、フィルター部１５の長さを短くして中空セグメント部１７で置き換えることはエアロゾル成分デリバリー量を増大させるために有効である。中空セグメント部１７内部の充填層が繊維充填層であることから、使用時の外側からの触り心地は、紙管部１４と比較して、フィルター部に近いため、使用者に違和感を感じさせることが少ない。
　図１及び２で示した実施形態においては、非燃焼加熱型喫煙物品１０の長手方向の長さは、４０ｍｍ～９０ｍｍであることが好ましく、５０ｍｍ～７５ｍｍであることがより好ましく、５０ｍｍ～６０ｍｍであることがさらに好ましい。また、非燃焼加熱型喫煙物品の円周は１５ｍｍ～２５ｍｍであることが好ましく、１７ｍｍ～２４ｍｍであることがより好ましく、２０ｍｍ～２２ｍｍであることがさらに好ましい。また、図２で示した実施形態においては、たばこロッド部の長さは２０ｍｍ、紙管部の長さは２０ｍｍ、中空セグメント部の長さは８ｍｍ、フィルター部の長さは７ｍｍである態様を挙げることができるが、これら個々のセグメント長さは、製造適性、要求品質等に応じて、適宜変更できる。
　前記たばこロッドが加熱されることで生じるエアロゾル生成基材とたばこ香味成分とを含む蒸気が、紙管部１４を通過するのに従って、紙管内の空気と触れ合って冷却されることで液化してエアロゾルが生成する。
　また、非燃焼加熱型喫煙物品１０は、紙管部１４と、紙管部１４の周囲を覆う第二の巻紙１３（チップペーパー）の一部に、外部からの空気を取り入れるための微小孔を有してもよい（図示せず）。そのような微小孔が存在することで、使用時に外部から紙管部１４の内部に空気が流入し、前記たばこロッドが加熱されることで生じるエアロゾル生成基材とたばこ香味成分とを含む蒸気が、外部からの空気と接触して温度が低下することで液化し、エアロゾルの生成がより確実になる。
　紙管部１４は、例えば厚紙を円筒状に加工したものを挙げることができる。
　フィルター部１５は、例えばアセテートトウを材料として用いたものを挙げることができる。アセテートトウの単糸繊度、総繊度は特に限定されない。
　図１ではフィルター部１５は単一のセグメントから構成されているが、複数のセグメントから構成されていてもよい。複数のセグメントから構成されている場合、例えば上流側に中空のセグメントを配置し、下流側（使用者の吸口端側）のセグメントとして吸口断面がアセテートトウで充填されている態様を挙げることもできる。このような態様によれば、生成するエアロゾルの無用な損失を防ぐとともに、非燃焼加熱型喫煙物品の外観を良好にすることができる。
　また、フィルターの製造において、通気抵抗の調整や添加物（公知の吸着剤や香料、香料保持材等）の添加を適宜設計できる。
　第二の巻紙１３（チップペーパー）の材料は特に制限されないが、本発明の実施形態にかかる巻紙を一部または全部に用いてもよい。第二の巻紙１３は、例えば酢酸ビニル系の糊を用いて、上記のたばこロッド、紙管部１４、フィルター部１５の周囲を巻装した後に固定する態様を挙げることができる。
　たばこロッドは、充填物１１としてたばこ刻みを含み、当該たばこ刻みの材料は特に限定されず、ラミナや中骨等の公知のものを用いることができる。たばこロッド中の充填物の含有量の範囲は、円周２２ｍｍ、長さ２０ｍｍのたばこロッドの場合、２００～４００ｍｇ／ロッドを挙げることができ、２５０～３２０ｍｇ／ロッドが好ましい。充填物の水分含有量は１０～１５重量％を挙げることができ、１１～１３重量％であることが好ましい。このような水分含有量であると、巻染みの発生を抑制し、たばこロッドの製造時の巻上適性を良好にする。
　充填物として用いるたばこ刻みの大きさやその調製法については特に制限はない。例えば、乾燥したたばこ葉を、幅０．８～１．２ｍｍに刻んだものを用いてもよい。
　また、乾燥したたばこ葉を平均粒径が２０～２００μｍ程度になるように粉砕して均一化したものをシート加工し、それを幅０．８～１．２ｍｍに刻んだものを用いてもよい。
　さらに、上記のシート加工したものについて刻まずにギャザー加工したものを充填物として用いてもよい。
　充填物は、エアロゾル煙を生成するエアロゾル生成基材を含む。当該エアロゾル生成基材の種類は、特に限定されず、用途に応じて種々の天然物からの抽出物質および／またはそれらの構成成分を選択することができる。エアロゾル生成基材としては、グリセリン、プロピレングリコール、トリアセチン、１，３－ブタンジオール、及びこれらの混合物を挙げることができる。
　充填物中のエアロゾル生成基材の含有量は、特に限定されず、十分にエアロゾルを生成させるとともに、良好な喫味の付与の観点から、通常５重量％以上であり、好ましくは１０重量％以上であり、また、通常５０重量％以下であり、好ましくは２０重量％以下である。
　充填物は、香料を含んでいてもよい。当該香料の種類は、特に限定されず、良好な喫味の付与の観点から、アセトアニソール、アセトフェノン、アセチルピラジン、２－アセチルチアゾール、アルファルファエキストラクト、アミルアルコール、酪酸アミル、トランス－アネトール、スターアニス油、リンゴ果汁、ペルーバルサム油、ミツロウアブソリュート、ベンズアルデヒド、ベンゾインレジノイド、ベンジルアルコール、安息香酸ベンジル、フェニル酢酸ベンジル、プロピオン酸ベンジル、２，３－ブタンジオン、２－ブタノール、酪酸ブチル、酪酸、カラメル、カルダモン油、キャロブアブソリュート、β－カロテン、ニンジンジュース、Ｌ－カルボン、β－カリオフィレン、カシア樹皮油、シダーウッド油、セロリーシード油、カモミル油、シンナムアルデヒド、ケイ皮酸、シンナミルアルコール、ケイ皮酸シンナミル、シトロネラ油、ＤＬ－シトロネロール、クラリセージエキストラクト、ココア、コーヒー、コニャック油、コリアンダー油、クミンアルデヒド、ダバナ油、δ－デカラクトン、γ－デカラクトン、デカン酸、ディルハーブ油、３，４－ジメチル－１，２－シクロペンタンジオン、４，５－ジメチル－３－ヒドロキシ－２，５－ジヒドロフラン－２－オン、３，７－ジメチル－６－オクテン酸、２，３－ジメチルピラジン、２，５－ジメチルピラジン、２，６－ジメチルピラジン、２－メチル酪酸エチル、酢酸エチル、酪酸エチル、ヘキサン酸エチル、イソ吉草酸エチル、乳酸エチル、ラウリン酸エチル、レブリン酸エチル、エチルマルトール、オクタン酸エチル、オレイン酸エチル、パルミチン酸エチル、フェニル酢酸エチル、プロピオン酸エチル、ステアリン酸エチル、吉草酸エチル、エチルバニリン、エチルバニリングルコシド、２－エチル－３，（５または６）－ジメチルピラジン、５－エチル－３－ヒドロキシ－４－メチル－２（５Ｈ）－フラノン、２－エチル－３－メチルピラジン、ユーカリプトール、フェネグリークアブソリュート、ジェネアブソリュート、リンドウ根インフュージョン、ゲラニオール、酢酸ゲラニル、ブドウ果汁、グアヤコール、グァバエキストラクト、γ－ヘプタラクトン、γ－ヘキサラクトン、ヘキサン酸、シス－３－ヘキセン－１－オール、酢酸ヘキシル、ヘキシルアルコール、フェニル酢酸ヘキシル、ハチミツ、４－ヒドロキシ－３－ペンテン酸ラクトン、４－ヒドロキシ－４－（３－ヒドロキシ－１－ブテニル）－３，５，５－トリメチル－２－シクロヘキセン－１－オン、４－（パラ－ヒドロキシフェニル）－２－ブタノン、４－ヒドロキシウンデカン酸ナトリウム、インモルテルアブソリュート、β－イオノン、酢酸イソアミル、酪酸イソアミル、フェニル酢酸イソアミル、酢酸イソブチル、フェニル酢酸イソブチル、ジャスミンアブソリュート、コーラナッツティンクチャー、ラブダナム油、レモンテルペンレス油、カンゾウエキストラクト、リナロール、酢酸リナリル、ロベージ根油、マルトール、メープルシロップ、メンソール、メントン、酢酸Ｌ－メンチル、パラメトキシベンズアルデヒド、メチル－２－ピロリルケトン、アントラニル酸メチル、フェニル酢酸メチル、サリチル酸メチル、４’－メチルアセトフェノン、メチルシクロペンテノロン、３－メチル吉草酸、ミモザアブソリュート、トウミツ、ミリスチン酸、ネロール、ネロリドール、γ－ノナラクトン、ナツメグ油、δ－オクタラクトン、オクタナール、オクタン酸、オレンジフラワー油、オレンジ油、オリス根油、パルミチン酸、ω－ペンタデカラクトン、ペパーミント油、プチグレインパラグアイ油、フェネチルアルコール、フェニル酢酸フェネチル、フェニル酢酸、ピペロナール、プラムエキストラクト、プロペニルグアエトール、酢酸プロピル、３－プロピリデンフタリド、プルーン果汁、ピルビン酸、レーズンエキストラクト、ローズ油、ラム酒、セージ油、サンダルウッド油、スペアミント油、スチラックスアブソリュート、マリーゴールド油、ティーディスティレート、α－テルピネオール、酢酸テルピニル、５，６，７，８－テトラヒドロキノキサリン、１，５，５，９－テトラメチル－１３－オキサシクロ（８．３．０．０（４．９））トリデカン、２，３，５，６－テトラメチルピラジン、タイム油、トマトエキストラクト、２－トリデカノン、クエン酸トリエチル、４－（２，６，６－トリメチル－１－シクロヘキセニル）２－ブテン－４－オン、２，６，６－トリメチル－２－シクロヘキセン－１，４－ジオン、４－（２，６，６－トリメチル－１，３－シクロヘキサジエニル）２－ブテン－４－オン、２，３，５－トリメチルピラジン、γ－ウンデカラクトン、γ－バレロラクトン、バニラエキストラクト、バニリン、ベラトルアルデヒド、バイオレットリーフアブソリュートが挙げられ、特に好ましくはメンソールである。また、これらの香料は１種を単独で、又は２種以上を併用してもよい。
　充填物中の香料の含有量は、特に限定されず、良好な喫味の付与の観点から、通常１００００ｐｐｍ以上であり、好ましくは２００００ｐｐｍ以上であり、より好ましくは２５０００ｐｐｍ以上であり、また、通常５００００ｐｐｍ以下であり、好ましくは４００００ｐｐｍ以下であり、より好ましくは３３０００ｐｐｍ以下である。
　充填物の充填密度は、特に限定されないが、非燃焼加熱型喫煙物品の性能を担保し、良好な喫味の付与の観点から、通常２５０ｍｇ／ｃｍ３以上であり、好ましくは３２０ｍｇ／ｃｍ３以上であり、また、通常５２０ｍｇ／ｃｍ３以下であり、好ましくは４２０ｍｇ／ｃｍ３以下である。
　本発明の実施形態にかかる非燃焼加熱型喫煙物品の製造において、上記の本発明の実施形態にかかる巻紙を使用することができる。具体的には、たばこ刻みとエアロゾル生成基材を含む充填物を成形し、その後、本発明の実施形態にかかる巻紙を用いて、成形された充填物を巻装することでたばこロッドを得ることができる。さらに、そのたばこロッドとマウスピース部を構成する部材とをチップペーパー（又は本発明の実施形態にかかる巻紙）で巻装することで、非燃焼加熱型喫煙物品を得ることができる。なお、巻装の際には公知の巻取装置を用いることができる。
　非燃焼加熱型喫煙物品の製造時に、本発明の実施形態にかかる巻紙を、たばこロッドの巻紙として、及び／又はチップペーパーとして使用することで、使用後（加熱後）に外観の印象が損なわれない非燃焼加熱型喫煙物品を提供できる。
　本発明の一実施形態である非燃焼加熱型喫煙物品１０は、充填物１１と巻紙１２（本発明の実施形態にかかる巻紙）から構成されるたばこロッドと、紙管部１４、及びフィルター部１５と、これらを連結するための第二の巻紙１３を備える。また、非燃焼加熱型喫煙物品１０は、紙管部１４と、紙管部１４の周囲を覆う第二の巻紙１３の一部に、外部からの空気を取り入れるための微小孔を有してもよい（図示せず）。そのような微小孔が存在することで、使用時に外部から紙管部１４の内部に空気が流入し、前記たばこロッドが加熱されることで生じるエアロゾル生成基材とたばこ香味成分とを含む蒸気が、外部からの空気と接触して温度が低下することで液化し、エアロゾルの生成がより確実になる。
＜電気加熱型喫煙システム＞
　電気加熱型喫煙システムの一態様を図３に図示する。電気加熱型喫煙システム３０は、電気加熱型デバイス２０の内部に配置された、ヒーター２４に接する伝熱部材２５に、上記で説明した非燃焼加熱型喫煙物品１０が接触するように嵌装されて使用される。
　電気加熱型デバイス２０は、例えば樹脂性の躯体２３の内部に、電池ユニット２１と制御ユニット２２とを有する。
　上記のように非燃焼加熱型喫煙物品は、充填物１１と、充填物１１を巻装する第一の巻紙１２から構成されるたばこロッド部と、該たばこロッド部とは反対側の端部を構成するマウスピース部１６とを有し、前記たばこロッド部と前記マウスピース部は、前記充填物を巻装する巻紙と同じ又は別の第二の巻紙を用いて連結されている。非燃焼加熱型喫煙物品のマウスピース部１６は、図１のように紙管部１４とフィルター部１５とから構成されていてもよいし、図２のように、紙管部１４とフィルター部１５の間に充填層１７から構成される中空セグメントを有していてもよい。
　非燃焼加熱型喫煙物品を電気加熱型デバイスに嵌装すると、該たばこロッドの外周面と、該たばこロッドと紙管部１４とを接続する第二の巻紙（チップペーパー１３）から構成される外周面の一部が、電気加熱型デバイス２０の内部の伝熱部材２５と接触する。
　電気加熱型デバイス２０の内部のヒーター２４は、制御ユニット２２による制御により発熱する。その熱が伝熱部材２５を介して非燃焼加熱型喫煙物品のたばこロッドに伝わることで、たばこロッドの充填物１１に含まれるエアロゾル生成基材と香味成分とが共に揮発する。
　ヒーター２４による加熱により、前記たばこロッドは概ね１５０～２５０℃にまで加熱される。
　上記のＬ＊、ａ＊、ｂ＊を測定する際の、巻紙の加熱温度を２３０℃とし、その時間を３分間とするのは、本発明の実施形態にかかる電気加熱型喫煙システムの使用を前提として設定されたものである。
　加熱により生じるエアロゾル生成基材と香味成分を含む蒸気は、前記で説明したメカニズムにより紙管部１４の内部でエアロゾル化し、非燃焼加熱型喫煙物品１０のフィルター部１５を通して使用者の口腔内に到達する。
　本発明を実施例によって更に具体的に説明するが、本発明はその要旨を超えない限り、以下の実施例の記載に限定されるものではない。
＜加熱前後の紙サンプルの準備＞
　ＣＩＥＬａｂ表色系における明度Ｌ＊、色度ａ＊、色度ｂ＊について、様々な数値を有する紙を準備した。有色の紙としては、例えばグラビア印刷品、白色の通常パルプに未晒パルプを漉きこんだ混抄品、微細なたばこ葉を漉きこんだたばこシートなどを準備した。全く着色していない紙サンプルとして１００％バージンパルプを使用した通常のチップペーパー原紙と巻紙を対照として準備した。全部で２６種類の紙を準備した。
　その内容を以下の表１に示す。
Figure JPOXMLDOC01-appb-T000001
＜加熱条件＞
　マッフル炉（品名：Muffle Furnace FO410型、ヤマト科学製）をあらかじめ２３０℃に調整した。扉を開けて紙サンプルを家庭用アルミホイル（材質：アルミニウム箔　厚さ：１１μｍ）に載せ、マッフル炉内に入れて、扉を閉めた。前記動作は素早く行い（３秒以内）、マッフル炉内の温度低下を最小限にした。本実施例での加熱条件（マッフル炉温度設定２３０℃、紙サンプル加熱時間３分）においては、実際の紙の温度は扉を閉めた後遅くとも１分後にはマッフル炉設定温度と同じ２３０℃程度であった。これは、色変色温度試験紙（サーモラベル５Ｅ－１７０／サーモラベル５Ｅ－２１０（日油技研工業製）を用いて確認した。
＜色差測定＞
　加熱前後の各サンプルについて分光光度計（Ｘ－Ｒｉｔｅ社製、品名ＳｐｅｃｔｒｏＥｙｅ）を用いて色相を計測した。計測は、光源Ｄ６５、光源フィルタなし、視野角２°の条件下、ＩＳＯ白色度９２％の紙の上に試料１枚を置き、その上に分光光度計の測定部を押し当てて実施した。
　測定は５か所を繰り返し行い、平均値を解析に使用した。Ｌ＊、ａ＊、ｂ＊は測定をそのまま、ΔＬ＊、Δａ＊、Δｂ＊は加熱変色後の値から加熱変色前の値を差し引いて求めた。
　色合い評価には様々な評価、分類系があるが　ＣＩＥＬａｂ表色系はＣＩＥ（国際照明委員会）にて策定された表色系であり、ＪＩＳ　Ｚ　８７８１－４、ＩＳＯ　１１６６４－４の基となっている。人間の感覚に近似し、ごく一般的に使用され、色合いを３次元で数値化できる便利な分類系である。なお、Ｌ＊は明度、ａ＊は青～黄、ｂ＊は青緑～赤紫を代表する軸であり、Ｌ＊は値が高いほど明るく、ａ＊、ｂ＊は０に近いほど彩度が落ちる。例えば、Ｌ＊、ａ＊、ｂ＊＝１００，０，０は白であり、０，０，０は黒である。
＜官能評価＞
　２０名のパネル一人一人に加熱前後の紙サンプルを見せ、その色合いから受ける見た目の汚さを問い、パネル２０名のうち、汚く見えて不快だと回答した人数が１１人以上の場合には、そのサンプルの外観印象を×と判定し、また１１人未満の場合は、そのサンプルの外観印象を○と判定し、それらの結果を解析に使用した。
＜解析＞
　加熱前後のΔＬ＊、Δａ＊、Δｂ＊値と、外観の印象の優劣に関係性は見られなかった（図４Ａ～４Ｃ）。
　色相単体の値の差による単純な図からは加熱後の紙の色合いの良し悪しを推定できないことから、色差データを用いた判別分析を行うことを検討し、複数因子の関連性を知るために判別分析を行った。その結果、以下のような、判別率９６．２％と高い確率で外観印象を判定可能なΔＬ＊、Δａ＊、Δｂ＊値をパラメータとした関数を得ることができた。判別式のＰ値は０．００１より小さく統計的に高度に有意であり、一般的に判別率は７５％を超えれば推定に使えるといわれていることから、判別率が９６．２％であることは、ほぼ完全に推定可能なレベルであるという事を意味する。
　判別得点　ｙ＝－０．１８×ΔＬ＊＋０．０８×Δａ＊＋０．１３×Δｂ＊－２．３６　（１）
判別得点０．６２以上：×（悪い）
判別得点０．６２未満：○（良い）
　式（１）は、加熱後の外観印象は加熱前の紙サンプルと加熱後の紙サンプルの色差であるΔＬ＊、Δａ＊、Δｂ＊でほぼ決定づけられることを意味しており、例えば、ΔＬ＊が低く、Δａ＊、Δｂ＊の値が高くなるほど判別得点が上がる。つまり、その紙の加熱後の印象が悪い方向に位置することになる。
この結果をまとめたのが図５である。
　なお、判別分析はＢｅｌｌ　Ｃｕｒｖｅ社製　エクセル統計Ｖｅｒ.２．１５　多変量解析の判別分析２群を使用し、以下の条件にて分析した。
（１）増減法Ｐ値:投入０．２除去０．２
（２）線形結合している変数を除いて分析する
　図６は、更に詳しく説明するために、今回調査した紙サンプルのΔａ＊とΔｂ＊の関係を表したものである。
　３次元的に明示することができないため、ΔＬ＊の値については便宜的に－１０で二値化し、－１０よりも値が低い（暗く変色）ものについて、黒丸または太字の×で表した。
　評価で外観印象が悪かったものは「×」で表しており、Δａ＊、Δｂ＊の値が共に高い所に位置している。これは加熱により、赤紫や黄色、あるいはそれらが合わさった茶色方向への変色が大きいことを意味しており、また相対的にΔＬ＊も低いものが多く見られる。つまり、これらのサンプルは、視覚的にはいわゆる薄い焦げ色から濃い焦げ色に近づくサンプル群であり、直感的にも外観印象が悪い群であることが理解できる。
　これらサンプル群は加熱前はＬ＊値が比較的高く、またａ＊値、ｂ＊値も低い、つまり明るく彩度の低いものが多かった。こういった明るく薄い色相のサンプルは加熱による茶色の変化が目立ちやすく外観印象の悪さに結びつくと考えられる。
　反対に外観印象が良かった「○」のサンプルについては、Δａ＊、Δｂ＊の値が共に低い所に位置している。これは加熱により、青や緑色、あるいはそれらが合わさった青緑の方向への変色が大きいことを意味している。中には相対的にΔＬ＊値が低い、即ち明度が小さく暗いにもかかわらず○のものも見られる。これらのサンプル群は、×の場合とは反対に、加熱前は比較的Ｌ＊値が低く、またａ＊値とｂ＊値も高い、つまり暗めの彩度の高いものが多い。こういった濃いめの色相のサンプルは加熱による変化が目立ちにくいため、外観印象の良さに結びつくと考えられる。
　プロットを全体的に見ると、Δａ＊は±２０、Δｂ＊は±３０と幅広い範囲にプロットが分布していることから、この実験が部分的ではなく、様々な色相の変化をするサンプルを網羅していることが分かる。
　本発明では、紙の加熱前後の色の変化程度に着目し、その領域を数値として把握することで有効な範囲を規定することができた。
　本来、こういったパラメータ化には単純に加熱前の色相で領域を規定するのが考えやすいと想像されるが、今回の統計的手法では、色差ではない加熱前の紙のＬ＊、ａ＊、ｂ＊の値のみから有用な数式は得られなかった。それは、色に含まれる顔料や、染料、等の有色成分はそれぞれ異なる熱分解挙動を持つために、加熱後の変色程度も色成分ごとに異なるためと考えられる。従って、元の紙の色のみではなく、変色程度で正確に外観印象を推定できる本発明の考え方は合理的である。
　そして、上記の試験結果に基づくと、判別得点が０．６２未満の数値を有する紙は、加熱前後で変色の度合いが少なく、観察を行った人に対して、不快な印象を与えないことが分かった。
　以上を踏まえ、さらに以下の表２に示す実験例１～１８で示される処方の巻紙を調製した。具体的には、実験例１～１８において、坪量と填料の含有量を表１に記載のように変更した。これらの実験例において、パルプとして（木材パルプ）を用い、填料として炭酸カルシウム（白石工業社製）を用いた。抄紙は手すきで行い、方法はＪＩＳ Ｐ－８２２２「パルプ－試験用手すき紙の調製方法」に準拠した。また、通常のシガレット用巻紙を準備した。実験例１～１８の巻紙には助燃剤が含まれておらず、一方で通常のシガレット用巻紙には助燃剤（クエン酸ナトリウム）が１．０重量％含まれている。
　これらの巻紙について、２３０℃で３分間加熱を行った後のＬ＊、ａ＊、ｂ＊のそれぞれの値から、加熱前に測定しておいたＬ＊、ａ＊、ｂ＊のそれぞれの値の引き、Δ値を求め、それぞれの値を上記の判別得点を算出する式に代入し、判別得点を求めた。加熱の仕方は上記のサンプル１～２６と同じである。
　また、これらの巻紙については、加熱前にＩＳＯ白色度を測定した。さらに、上記で説明したＰ８１１３：２００６（ＩＳＯ１９２４－２：１９９４）に準拠して、測定装置として東洋精機製作所製のストログラフＥ－Ｌを用いて引張強度を測定した。結果を表２に示す。
Figure JPOXMLDOC01-appb-T000002
　表２の結果から、加熱前のＩＳＯ白色度が８３％未満である実験例１、７、１３は、判別得点が０．６２よりも大きく、加熱後の外観印象が悪くなっていた。一方で、加熱前のＩＳＯ白色度が８３％以上のものであり、かつ、坪量と填料の含有量が所定のものについては、加熱前の色が白色のもの、言い方を変えると、Ｌ＊値が高く、加熱後の外観印象が悪くなりやすいと考えられるものであっても、加熱後の外観印象は損なわれなかった。また、助燃剤を含有する通常のシガレット用巻紙の判別得点は０．６２よりも大きく、加熱後の外観印象が悪かった。また、いずれの坪量においても、填料の含有量が４５重量％を超えると、巻紙の引張強度が低下する傾向が見られた。また、填料の含有量が多すぎる巻紙は、たばこロッドの高速巻上特性に劣る。
　次に、表２の結果に基づき、坪量ごとに、横軸に填料の含有量をプロットし、縦軸に判別得点をプロットした図を作成した（図７）。図７の結果から、坪量が小さくなるほど、また、填料の含有量が多くなるほど、判別得点が小さくなる傾向が見られた。
　次に、表２の結果について、填料の含有量及び坪量と、判別得点との関係を分かりやすくするためにまとめた表３を以下に示す。
Figure JPOXMLDOC01-appb-T000003
　図７及び表３の記載に基づくと、外観印象の観点から、巻紙の坪量が２５ｇｓｍ以上３５ｇｓｍ以下のとき、填料が１５～４５重量％であることが望ましく、坪量が３５ｇｓｍを超えて４５ｇｓｍ以下のとき、填料が２５～４５重量％であることが望ましいことが分かる。なお、上記の各坪量の範囲において、填料の含有量がそれぞれの下限値以下の場合、不透明度が小さく、巻紙として使用した場合に中身の刻みが透けてしまう傾向がある。また、坪量および填料の含有量が上記の範囲内であっても、助燃剤が含まれているものは外観印象の観点から望ましくないことが分かる。
１０　非燃焼加熱型喫煙物品
１１　充填物
１２　第一の巻紙
１３　第二の巻紙（チップペーパー）
１４　紙管部
１５　フィルター部
１６　マウスピース部
１７　中空セグメント部
２０　電気加熱型デバイス
２１　電池ユニット
２２　制御ユニット
２３　躯体
２４　ヒーター部材
２５　伝熱部材
３０　電気加熱型喫煙システム

Claims (8)

  1. 　２３０℃で３分間加熱する前と後のＣＩＥＬａｂ表色系における色差値を、以下の式（１）に代入して得られる判別得点が０．６２よりも低い数値を示し、ＩＳＯ白色度が８３％以上である白色部を有する、非燃焼加熱型喫煙物品用の巻紙。
    判別得点（ｙ）　ｙ＝－０．１８×ΔＬ＊＋０．０８×Δａ＊＋０．１３×Δｂ＊－２．３６　（１）
    　（式（１）において、加熱する前と後のＣＩＥＬａｂ表色系における色差値とは、加熱した後のＬ＊、ａ＊、ｂ＊値から加熱前のＬ＊、ａ＊、ｂ＊値を引いた値である。ΔＬ＊は、前記巻紙を加熱した後と加熱する前の明度Ｌ＊の差を示し、Δａ＊は、前記巻紙を加熱した後と加熱する前の色度ａ＊の差を示し、Δｂ＊は、前記巻紙を加熱した後と加熱する前の色度ｂ＊の差を示す。）
  2. 　前記非燃焼加熱型喫煙物品用の巻紙が填料を含有し、填料の含有量が１５～４５重量％であり、前記非燃焼加熱型喫煙物品用の巻紙の坪量が２５～４５ｇｓｍであって、
    　坪量が２５ｇｓｍ以上３５ｇｓｍ以下のとき、填料が１５～４５重量％であり、
    　坪量が３５ｇｓｍを超えて４５ｇｓｍ以下のとき、填料が２５～４５重量％である、請求項１に記載の非燃焼加熱型喫煙物品用の巻紙。
  3. 　引張強度が８Ｎ／１５ｍｍ以上である、請求項１または２に記載の非燃焼加熱型喫煙物品用の巻紙。
  4. 　前記填料が炭酸カルシウムであり、前記巻紙の不透明度が６０％以上である、請求項２または３に記載の非燃焼加熱型喫煙物品用の巻紙。
  5. 　前記白色部の判別得点が０未満である、請求項１～４のいずれか一項に記載の非燃焼加熱型喫煙物品用の巻紙。
  6. 　前記巻紙が、助燃剤を含まない、請求項１～５のいずれか一項に記載の非燃焼加熱型喫煙物品用の巻紙。
  7. 　たばこ刻みとエアロゾル生成基材とを含む充填物が、該充填物を巻装する第一の巻紙で巻装されてなるたばこロッド部と、該たばこロッド部とは反対側の端部を構成するマウスピース部とを有し、前記たばこロッド部と前記マウスピース部は、前記充填物を巻装する巻紙と同じ又は別の第二の巻紙を用いて連結されている非燃焼加熱型喫煙物品であって、第１の巻紙と第２の巻紙の少なくとも一方が、請求項１～６のいずれか一項に記載の巻紙である、非燃焼加熱型喫煙物品。
  8. 　ヒーター部材と、該ヒーター部材からの熱を伝熱する伝熱部材と、該ヒーター部材の電力源となる電池ユニットと、該ヒーター部材を制御するための制御ユニットとを備える電気加熱型デバイスと、該伝熱部材に接触するように嵌合される、請求項７に記載の非燃焼加熱型喫煙物品と、から構成される、電気加熱型喫煙システム。
PCT/JP2018/028489 2018-07-30 2018-07-30 非燃焼加熱型喫煙物品用の巻紙、非燃焼加熱型喫煙物品及び電気加熱型喫煙システム WO2020026311A1 (ja)