WO2019222308A1 - Films de graphène intégraux issus de feuilles de graphène fonctionnalisé - Google Patents

Films de graphène intégraux issus de feuilles de graphène fonctionnalisé Download PDF

Info

Publication number
WO2019222308A1
WO2019222308A1 PCT/US2019/032352 US2019032352W WO2019222308A1 WO 2019222308 A1 WO2019222308 A1 WO 2019222308A1 US 2019032352 W US2019032352 W US 2019032352W WO 2019222308 A1 WO2019222308 A1 WO 2019222308A1
Authority
WO
WIPO (PCT)
Prior art keywords
graphene
film
integral
sheets
graphene sheets
Prior art date
Application number
PCT/US2019/032352
Other languages
English (en)
Inventor
Aruna Zhamu
Bor Z. Jang
Original Assignee
Nanotek Instruments, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US15/980,015 external-priority patent/US20190352186A1/en
Priority claimed from US15/980,005 external-priority patent/US20190352185A1/en
Application filed by Nanotek Instruments, Inc. filed Critical Nanotek Instruments, Inc.
Publication of WO2019222308A1 publication Critical patent/WO2019222308A1/fr

Abstract

L'invention concerne un film de graphène intégral comprenant des feuilles de graphène chimiquement fonctionnalisé qui sont liées ou interconnectées chimiquement les unes avec les autres ayant un espacement inter-planaire d?002#191 de 0,36 nm à 1,5 nm selon une détermination par diffraction de rayons X et une teneur en élément non carboné de 0,1 % à 47 % en poids, lesdites feuilles de graphène fonctionnalisé étant sensiblement parallèles les unes aux autres et parallèles à une direction dans le plan dudit film de graphène intégral et ledit film de graphène intégral ayant une longueur de 1 cm à 10 000 m, une largeur de 1 cm à 5 m, une épaisseur de 2 nm à 500 µm, et une densité physique de 1,5 à 2,25 g/cm3. Le film de graphène intégral a typiquement un module de Young de 20 GPa à 300 GPa ou une résistance à la traction de 1,0 GPa à 3,5 GPa. L'invention concerne également un procédé de production du film de graphème intégral.
PCT/US2019/032352 2018-05-15 2019-05-15 Films de graphène intégraux issus de feuilles de graphène fonctionnalisé WO2019222308A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US15/980,005 2018-05-15
US15/980,015 US20190352186A1 (en) 2018-05-15 2018-05-15 Process for producing integral graphene films from functionalized graphene sheets
US15/980,005 US20190352185A1 (en) 2018-05-15 2018-05-15 Integral graphene films from functionalized graphene sheets
US15/980,015 2018-05-15

Publications (1)

Publication Number Publication Date
WO2019222308A1 true WO2019222308A1 (fr) 2019-11-21

Family

ID=68540874

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2019/032352 WO2019222308A1 (fr) 2018-05-15 2019-05-15 Films de graphène intégraux issus de feuilles de graphène fonctionnalisé

Country Status (1)

Country Link
WO (1) WO2019222308A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113104843A (zh) * 2021-04-20 2021-07-13 雷索新材料(苏州)有限公司 一种石墨烯及其制备方法
CN115180615A (zh) * 2022-07-27 2022-10-14 浙江大学 一种高取向石墨烯膜的制备方法
CN115231566A (zh) * 2022-07-11 2022-10-25 武汉汉烯科技有限公司 采用伽马射线增强宏观石墨烯组装膜拉伸力学性能的方法
WO2024088254A1 (fr) * 2022-10-24 2024-05-02 中国石油化工股份有限公司 Graphène modifié par greffage de bord, dispersion aqueuse de celui-ci, et sa méthode de préparation

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150086881A1 (en) * 2013-09-23 2015-03-26 Aruna Zhamu Large-grain graphene thin film current collector and secondary batteries containing same
US20150239741A1 (en) * 2014-02-21 2015-08-27 David Joseph Burton Production of graphene materials in a cavitating fluid
WO2017095699A1 (fr) * 2015-12-03 2017-06-08 Nanotek Instruments, Inc. Film de graphène hautement orienté et conducteur, et procédé de production
US20170225233A1 (en) * 2016-02-09 2017-08-10 Aruna Zhamu Chemical-free production of graphene-reinforced inorganic matrix composites
US9957164B2 (en) * 2014-04-03 2018-05-01 Nanotek Instruments, Inc. Highly conducting graphitic films from graphene liquid crystals

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150086881A1 (en) * 2013-09-23 2015-03-26 Aruna Zhamu Large-grain graphene thin film current collector and secondary batteries containing same
US20150239741A1 (en) * 2014-02-21 2015-08-27 David Joseph Burton Production of graphene materials in a cavitating fluid
US9957164B2 (en) * 2014-04-03 2018-05-01 Nanotek Instruments, Inc. Highly conducting graphitic films from graphene liquid crystals
WO2017095699A1 (fr) * 2015-12-03 2017-06-08 Nanotek Instruments, Inc. Film de graphène hautement orienté et conducteur, et procédé de production
US20170225233A1 (en) * 2016-02-09 2017-08-10 Aruna Zhamu Chemical-free production of graphene-reinforced inorganic matrix composites

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113104843A (zh) * 2021-04-20 2021-07-13 雷索新材料(苏州)有限公司 一种石墨烯及其制备方法
CN115231566A (zh) * 2022-07-11 2022-10-25 武汉汉烯科技有限公司 采用伽马射线增强宏观石墨烯组装膜拉伸力学性能的方法
CN115180615A (zh) * 2022-07-27 2022-10-14 浙江大学 一种高取向石墨烯膜的制备方法
WO2024088254A1 (fr) * 2022-10-24 2024-05-02 中国石油化工股份有限公司 Graphène modifié par greffage de bord, dispersion aqueuse de celui-ci, et sa méthode de préparation

Similar Documents

Publication Publication Date Title
US11469009B2 (en) Production process for highly conducting and oriented graphene film
US10005099B2 (en) Production of highly oriented graphene oxide films and graphitic films derived therefrom
US10059592B1 (en) Process for producing highly oriented graphene films
WO2019222308A1 (fr) Films de graphène intégraux issus de feuilles de graphène fonctionnalisé
US9957164B2 (en) Highly conducting graphitic films from graphene liquid crystals
US20190352186A1 (en) Process for producing integral graphene films from functionalized graphene sheets
US9193132B2 (en) Highly oriented graphene structures and process for producing same
US10934637B2 (en) Process for producing fabric of continuous graphene fiber yarns from functionalized graphene sheets
US10479690B2 (en) Process for producing monolithic film of integrated highly oriented halogenated graphene sheets or molecules
KR102399147B1 (ko) 고도로 배향된 일체화 할로겐화 그래핀의 모노리식 필름
US10927478B2 (en) Fabric of continuous graphene fiber yarns from functionalized graphene sheets
US9988273B2 (en) Process for producing highly oriented humic acid films and highly conducting graphitic films derived therefrom
US10865502B2 (en) Continuous graphene fibers from functionalized graphene sheets
JP7042800B2 (ja) 高配向フミン酸フィルムおよびそれから得られる高導電性黒鉛フィルムならびに同フィルムを含有するデバイス
US10731931B2 (en) Highly oriented humic acid films and highly conducting graphitic films derived therefrom and devices containing same
US20190345647A1 (en) Process for producing continuous graphene fibers from functionalized graphene sheets
US20190352185A1 (en) Integral graphene films from functionalized graphene sheets
US10553357B2 (en) Monolithic film of integrated highly oriented halogenated graphene
WO2019222175A1 (fr) Fibres de graphène continues à partir de feuilles de graphène fonctionnalisées
WO2019226513A1 (fr) Tissu de fils de fibres de graphène continues à partir de feuilles de graphène fonctionnalisées
Mondella One-pot functionalization and exfoliation of graphene-based adducts for antimicrobial applications

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19803600

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19803600

Country of ref document: EP

Kind code of ref document: A1