WO2019098144A1 - 赤外線吸収体 - Google Patents
赤外線吸収体 Download PDFInfo
- Publication number
- WO2019098144A1 WO2019098144A1 PCT/JP2018/041738 JP2018041738W WO2019098144A1 WO 2019098144 A1 WO2019098144 A1 WO 2019098144A1 JP 2018041738 W JP2018041738 W JP 2018041738W WO 2019098144 A1 WO2019098144 A1 WO 2019098144A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tungsten oxide
- composite tungsten
- infrared
- resin
- infrared absorber
- Prior art date
Abstract
樹脂媒体と、前記樹脂媒体内に配置され、複合タングステン酸化物粒子が集合した複合タングステン酸化物粒子集合体とを有し、 前記複合タングステン酸化物粒子集合体が帯状、鱗片状、ロッド状から選択された1種類以上の形状を有する赤外線吸収体を提供する。
Description
本発明は、赤外線吸収体に関する。
窓材等に使用される遮光部材について従来から各種検討がなされている。
例えば特許文献1には、カーボンブラック、チタンブラック等の無機顔料や、アニリンブラック等の有機顔料等の黒色微粉末を含有する遮光層を備えた遮光フィルムが提案されている。
また、特許文献2には、赤外線反射性を有する帯状のフィルムと、赤外線吸収性を有する帯状のフィルムとを、それぞれ経糸あるいは緯糸として編織物としてなる保温用シートが提案されており、赤外線反射性を有する帯状のフィルムとして、合成樹脂フィルムにアルミ蒸着加工を施し、さらに合成樹脂フィルムを積層したものを用いた例も開示されている。
特許文献3では、透明なガラス基板上に、基板側より第1層として周期律表のIIIa族、IVa族、Vb族、VIb族及びVIIb族から成る群から選ばれた少なくとも1種の金属イオンを含有する複合タングステン酸化物膜を設け、前記第1層上に第2層として透明誘電体膜を設け、該第2層上に第3層として周期律表のIIIa族、IVa族、Vb族、VIb族及びVIIb族から成る群から選ばれた少なくとも1種の金属イオンを含有する複合タングステン酸化物膜を設け、かつ前記第2層の透明誘電体膜の屈折率が前記第1層及び前記第3層の複合タングステン酸化物膜の屈折率よりも低いことを特徴とする熱線遮断ガラスが提案されている。
特許文献4では、特許文献3と同様の方法で、透明なガラス基板上に、基板側より第1層として第1の誘電体膜を設け、該第1層上に第2層として複合酸化タングステン膜を設け、該第2層上に第3層として第2の誘電体膜を設けた熱線遮断ガラスが提案されている。
特許文献5では、特許文献3と同様な方法で、透明な基板上に、基板側より第1層として同様の金属元素を含有する複合タングステン酸化物膜を設け、前記第1層上に第2層として透明誘電体膜を設けた熱線遮断ガラスが提案されている。
特許文献6では、水素、リチウム、ナトリウム又はカリウム等の添加材料を含有する三酸化タングステン(WO3)、三酸化モリブデン(MoO3)、五酸化ニオブ(Nb2O5)、五酸化タンタル(Ta2O5)、五酸化バナジウム(V2O5)及び二酸化バナジウム(VO2)の1種以上から選択された金属酸化物膜を、CVD法あるいはスプレー法を用いて形成された太陽光遮蔽特性を有する太陽光制御ガラスシートが提案されている。
特許文献7には、透明な基体上にポリビニルピロリドンを含有する酸化タングステン膜を形成してなることを特徴とする太陽光可変調光断熱材料が提案されている。
また、本件特許出願人は、特許文献8に、六塩化タングステンをアルコールに溶解し、そのまま溶媒を蒸発させるか、若しくは加熱還流した後溶媒を蒸発させ、その後100℃~500℃で加熱することにより、三酸化タングステン若しくはその水和物又は両者の混合物からなる粉末を得ることを特徴とするエレクトロクロミック特性を示す酸化タングステン微粒子の製造方法や、該酸化タングステン微粒子を用いてエレクトロクロミック素子とすること等を提案している。
特許文献9には、メタ型タングステン酸アンモニウムと金属塩の混合水溶液の乾固物を水素還元し、タングステンブロンズを生成させることを特徴とするタングステンブロンズの製造方法が提案されている。
本件特許出願人は、特許文献10に、赤外線材料微粒子が媒体中に分散してなる赤外線遮蔽材料微粒子分散体であって、当該赤外線材料微粒子は、タングステン酸化物微粒子または/および複合タングステン酸化物微粒子を含有し、当該赤外線材料微粒子の粒子直径が1nm以上800nm以下である赤外線遮蔽材料微粒子分散体を開示した。
窓材等に用いられる遮光部材としては、特許文献10等に開示されているように、太陽光からの近赤外線等の赤外線領域の光を吸収することができる赤外線吸収体が従来から用いられ、各種検討がなされてきた。しかし、近年では多様な各種赤外線吸収体が求められるようになっており、これに対応するため、新規な構造を含む赤外線吸収体が求められていた。
本発明の一側面では、新規な構造を有する赤外線吸収体を提供することを目的とする。
本発明の一側面では、樹脂媒体と、前記樹脂媒体内に配置され、複合タングステン酸化物粒子が集合した複合タングステン酸化物粒子集合体とを有し、
前記複合タングステン酸化物粒子集合体が帯状、鱗片状、ロッド状から選択された1種類以上の形状を有する赤外線吸収体を提供する。
前記複合タングステン酸化物粒子集合体が帯状、鱗片状、ロッド状から選択された1種類以上の形状を有する赤外線吸収体を提供する。
本発明の一側面では、新規な構造を有する赤外線吸収体を提供することができる。
[赤外線吸収体]
本実施形態では、赤外線吸収体の一構成例について説明する。
本実施形態では、赤外線吸収体の一構成例について説明する。
本実施形態の赤外線吸収体は、樹脂媒体と、樹脂媒体内に配置され、複合タングステン酸化物粒子が集合した複合タングステン酸化物粒子集合体とを有することができる。
そして、複合タングステン酸化物粒子集合体は、帯状、鱗片状、ロッド状から選択された1種類以上の形状を有することができる。
そして、複合タングステン酸化物粒子集合体は、帯状、鱗片状、ロッド状から選択された1種類以上の形状を有することができる。
従来は、可視領域の光の散乱を抑制し、透明性を確保する目的から、日射遮蔽粒子を透明樹脂中に均一に分散し、日射遮蔽材料粒子分散体としていた。しかし、本発明の発明者らの検討によれば、樹脂媒体内に複合タングステン酸化物粒子が部分的に高密度に集合して存在する複合タングステン酸化物粒子集合体を配置した赤外線吸収体においても可視領域の光の散乱を抑制し、透明性を確保しつつ、赤外線領域の光を吸収できることを見出した。すなわち、複合タングステン酸化物粒子集合体を含む新規な構造を有する赤外線吸収体を見出し、本発明を完成させた。
本実施形態の赤外線吸収体が含有する各成分について以下に説明する。
(複合タングステン酸化物粒子)
本実施形態の赤外線吸収体は複合タングステン酸化物粒子を含有することができる。複合タングステン酸化物粒子は赤外線吸収材料(赤外線吸収粒子)として機能する。
(複合タングステン酸化物粒子)
本実施形態の赤外線吸収体は複合タングステン酸化物粒子を含有することができる。複合タングステン酸化物粒子は赤外線吸収材料(赤外線吸収粒子)として機能する。
複合タングステン酸化物粒子を溶媒や固体の媒体に分散した分散物の光学特性は限定されないが、例えば光の透過率について、波長350nm以上600nm以下の範囲に極大値を有し、波長800nm以上2100nm以下の範囲に極小値を有することが好ましい。特に、上記複合タングステン酸化物粒子の分散物は光の透過率について、波長440nm以上600nm以下の範囲に極大値を有し、波長1150nm以上2100nm以下の範囲に極小値を有することがより好ましい。
すなわち、上記複合タングステン酸化物粒子の分散物は、光の透過率の極大値を可視領域に有し、透過率の極小値を近赤外線領域に有することが好ましい。
複合タングステン酸化物粒子は、例えば上述のように波長1150nm以上2100nm以下の範囲を含む近赤外線領域の光を吸収することができ、吸収した光を熱に変換することができる。このように複合タングステン酸化物粒子は、赤外線を吸収し熱に変換できるので、赤外線を遮蔽する窓材や、吸収した赤外線で発熱する繊維などに応用可能である。
複合タングステン酸化物粒子が含む複合タングステン酸化物について説明する。なお、本実施形態の赤外線吸収体が含有する複合タングステン酸化物粒子は、以下に説明する複合タングステン酸化物を含有することができる。また、上記複合タングステン酸化物粒子は、複合タングステン酸化物から構成することもできるが、この場合も不可避成分を含むことを除外するものではない。
複合タングステン酸化物を説明する前に、M元素を添加していないタングステン酸化物について説明する。
一般に、三酸化タングステン(WO3)中には有効な自由電子が存在しないため近赤外線領域の吸収反射特性が少なく、赤外線吸収材料としては有効ではない。
しかし、三酸化タングステンのタングステンに対する酸素の比率を3より低減することによって、当該タングステン酸化物中に自由電子を生成することができる。そして、本発明の発明者らは、当該タングステン酸化物におけるタングステンと酸素との組成範囲の特定部分において、赤外線吸収材料として特に有効な範囲があることを見出した。
タングステン酸化物におけるタングステンと酸素との組成範囲は、タングステンに対する酸素の物質量比(モル比)を3未満とすることで自由電子を生成でき、当該タングステン酸化物をWyOzと表記したとき、2.2≦z/y≦2.999であることが好ましい。
これは、上記z/yの値が、2.2以上の場合、当該タングステン酸化物中に目的としないWO2の結晶相が現れるのをより確実に回避することができると共に、材料としての化学的安定性を得ることができ、有効な赤外線吸収材料として適用できるからである。
また、上記z/yの値が、2.999以下であれば、当該タングステン酸化物中に必要とされる量の自由電子が生成され、効率のよい赤外線吸収材料となる。
また、タングステン酸化物において、一般式WyOzと表記したとき、2.45≦z/y≦2.999を満たす組成比を有する所謂「マグネリ相」は化学的に安定であり、近赤外線領域の光の吸収特性も良いので、赤外線吸収材料として特に好ましい。
複合タングステン酸化物は、上記タングステン酸化物へ、M元素を添加した構造を有する。
このように、M元素を添加した複合タングステン酸化物においては、自由電子が生成され、近赤外線領域に自由電子由来の吸収特性が発現し、波長1000nm付近の近赤外線を吸収できる赤外線吸収材料として特に有効となる。
ここで、M元素を添加した複合タングステン酸化物における、M元素としては特に限定されないが、例えばH、He、アルカリ金属元素、アルカリ土類金属元素、希土類元素、Mg、Zr、Cr、Mn、Fe、Ru、Co、Rh、Ir、Ni、Pd、Pt、Cu、Ag、Au、Zn、Cd、Al、Ga、In、Tl、Si、Ge、Sn、Pb、Sb、B、F、P、S、Se、Br、Te、Ti、Nb、V、Mo、Ta、Re、Be、Hf、Os、Bi、Iから選択される1種類以上の元素が挙げられる。このうち、M元素は、アルカリ金属元素およびアルカリ土類金属元素から選択される1種類以上を含有することが、後述する結晶構造の観点から望ましい。
当該複合タングステン酸化物に対し、タングステン酸化物において説明した酸素量の制御と、自由電子を生成するM元素の添加とを併用することで、より効率の良い赤外線吸収材料を得ることができる。
この酸素量の制御と、自由電子を生成するM元素の添加とを併用した複合タングステン酸化物の一般式は例えばMxWyOz(但し、Mは既述のM元素、Wはタングステン、Oは酸素)と記載することができる。
上記複合タングステン酸化物の一般式中の添加元素であるM元素と、タングステンとの物質量比(モル比)を示すx/yは、0.001≦x/y≦1.0を満たすことが好ましい。特にx/yは、0.001≦x/y≦0.5を満たすことがより好ましく、0.001≦x/y≦0.37を満たすことがさらに好ましく、0.20≦x/y≦0.37を満たすことが特に好ましい。
また、上記複合タングステン酸化物の一般式中のタングステンと酸素との物質量比(モル比)を示すz/yは、2.2≦z/y≦3.0を満たすことが好ましい。これは、上述のタングステン酸化物の場合と同様の機構が働くことに加え、z/y=3.0においても、M元素の添加量による自由電子の供給があるため、赤外線を吸収することができるからである。
以上に説明したように、本実施形態の赤外線吸収体が含有する複合タングステン酸化物粒子は、以下の一般式(1)で表される複合タングステン酸化物を含む粒子であることが好ましい。なお、該複合タングステン酸化物粒子は、以下の一般式(1)で表される複合タングステン酸化物からなる粒子とすることもできる。ただし、この場合も不可避成分を含むことを除外するものではない。
MxWyOz ・・・(1)
そして、上記一般式(1)中、M元素はH、He、アルカリ金属元素、アルカリ土類金属元素、希土類元素、Mg、Zr、Cr、Mn、Fe、Ru、Co、Rh、Ir、Ni、Pd、Pt、Cu、Ag、Au、Zn、Cd、Al、Ga、In、Tl、Si、Ge、Sn、Pb、Sb、B、F、P、S、Se、Br、Te、Ti、Nb、V、Mo、Ta、Re、Be、Hf、Os、Bi、Iから選択される1種類以上の元素であることが好ましい。M元素はアルカリ金属元素、およびアルカリ土類金属元素から選択された1種類以上の元素を含むことがより好ましい。特にM元素はCs、Rb、K、Baから選択された1種類以上を含むことがさらに好ましく、Cs、Rbから選択される1種類以上を含むことが特に好ましい。なお、M元素は例えばアルカリ金属元素、およびアルカリ土類金属元素から選択された1種類以上の元素とすることもできる。
そして、上記一般式(1)中、M元素はH、He、アルカリ金属元素、アルカリ土類金属元素、希土類元素、Mg、Zr、Cr、Mn、Fe、Ru、Co、Rh、Ir、Ni、Pd、Pt、Cu、Ag、Au、Zn、Cd、Al、Ga、In、Tl、Si、Ge、Sn、Pb、Sb、B、F、P、S、Se、Br、Te、Ti、Nb、V、Mo、Ta、Re、Be、Hf、Os、Bi、Iから選択される1種類以上の元素であることが好ましい。M元素はアルカリ金属元素、およびアルカリ土類金属元素から選択された1種類以上の元素を含むことがより好ましい。特にM元素はCs、Rb、K、Baから選択された1種類以上を含むことがさらに好ましく、Cs、Rbから選択される1種類以上を含むことが特に好ましい。なお、M元素は例えばアルカリ金属元素、およびアルカリ土類金属元素から選択された1種類以上の元素とすることもできる。
また、上記一般式(1)中、Wはタングステンを、Oは酸素をそれぞれ表している。
そして、x/yは0.001≦x/y≦1.0であることが好ましく、0.001≦x/y≦0.5であることがより好ましく、0.001≦x/y≦0.37であることがさらに好ましく、0.20≦x/y≦0.37であることが特に好ましい。
また、z/yは2.2≦z/y≦3.0であることが好ましい。
複合タングステン酸化物の結晶構造は特に限定されないが、六方晶の結晶構造を有することが好ましい。すなわち、本実施形態の赤外線吸収体が含有する複合タングステン酸化物粒子は、六方晶の結晶構造の複合タングステン酸化物を含むことが好ましい。なお、係る複合タングステン酸化物粒子は六方晶の結晶構造の複合タングステン酸化物から構成することもできる。
これは、複合タングステン酸化物が六方晶の結晶構造を有する場合、該複合タングステン酸化物を含む複合タングステン酸化物粒子は、可視領域の光の透過率が向上し、近赤外線領域の光の吸収が向上するからである。
係る六方晶の結晶構造は、WO6単位にて形成される8面体が6個集合して六角形の空隙(トンネル)が構成され、当該空隙中にM元素が配置して1つの単位を構成し、この1つの単位が多数集合して構成される。
本実施形態の赤外線吸収体の可視領域の光の透過特性を向上させ、近赤外線領域の光の吸収特性を向上させる観点から、含有する複合タングステン酸化物粒子の複合タングステン酸化物中に、上述の単位構造が含まれていることが好ましい。なお、単位構造とは、上述のようにWO6単位で形成される8面体が6個集合して六角形の空隙が構成され、当該空隙中にM元素が配置した構造を意味する。
これは、上述の六角形の空隙にM元素の陽イオンが添加されて存在することで、近赤外線領域の光の吸収が向上するからである。一般的には、イオン半径の大きなM元素を添加したとき当該六方晶が形成され易い。中でも、M元素がアルカリ金属元素、およびアルカリ土類金属元素から選択された1種類以上を含む場合、六方晶が形成され易く好ましい。さらに、M元素がCs、Rb、K、Baから選択された1種類以上を含む場合、六方晶が特に形成され易くより好ましい。特にM元素がCs、Rbから選択される1種類以上を含む複合タングステン酸化物を含有する複合タングステン酸化物粒子においては、近赤外線領域の光の吸収性能と、可視領域の光の透過性能とが特に優れるため、特に好ましい。
なお、M元素は、上述のアルカリ金属元素、およびアルカリ土類金属元素から選択された1種類以上から構成することもできる。ただし、M元素が上述のアルカリ金属元素、およびアルカリ土類金属元素から選択された1種類以上の場合にのみ複合タングステン酸化物が六方晶を形成するものではない。M元素にアルカリ金属元素、及びアルカリ土類金属元素から選択された1種類以上の元素、例えばCs、Rb、K、Baから選択される1種類以上の元素を用い、さらにアルカリ金属元素や、アルカリ土類金属元素以外のM元素の候補を1種類以上加えた場合等にでも、複合タングステン酸化物が六方晶を形成することがある。
M元素の添加量を示すx/yは既述のように、0.001≦x/y≦1.0であることが好ましく、0.001≦x/y≦0.5であることがより好ましく、0.001≦x/y≦0.37であることがさらに好ましく、0.20≦x/y≦0.37であることが特に好ましい。これは、x/yが上述の範囲にある場合、複合タングステン酸化物全体が均一に、六方晶の結晶構造を取ることができるからである。特にM元素の添加量を示すx/y=0.33とした場合、z/y=3の時に、理論上添加したM元素が六角形の空隙の全てに配置されることになるため好ましい。
本実施形態の赤外線吸収体が含む複合タングステン酸化物粒子は、その平均粒子径は特に限定されないが、平均粒子径は100nm以下であることが好ましい。本実施形態の赤外線吸収体が含む複合タングステン酸化物粒子について、より優れた赤外線吸収特性(赤外線遮蔽特性)を発揮させる観点から、当該平均粒子径は10nm以上100nm以下であることがより好ましく、10nm以上80nm以下であることがさらに好ましい。
ここで、平均粒子径とは個々の複合タングステン酸化物粒子が有する粒子径の平均値であり、電子顕微鏡等で観察される集合していない個々の複合タングステン酸化物粒子の粒子径の平均値である。このため、上記平均粒子径は、例えば樹脂などの媒体に分散している複合タングステン酸化物粒子について、電子顕微鏡像を用いて測定した個々の粒子の粒子径から算出できる。
複合タングステン酸化物粒子の平均粒子径の算出方法は特に限定されないが、例えばまず断面加工で取り出した複合タングステン酸化物粒子分散体の薄片化試料を作製する。そして、作製した薄片化試料の透過型電子顕微鏡像から、複合タングステン酸化物粒子100個の粒子径を、画像処理装置を用いて測定し、その平均値を算出することで、複合タングステン酸化物粒子の平均粒子径を求めることができる。樹脂などの媒体に複合タングステン酸化物粒子を分散させた複合タングステン酸化物粒子分散体から、当該薄片化試料を取り出すための断面加工には、例えばミクロトーム、クロスセクションポリッシャ、集束イオンビーム(FIB)装置等を用いることができる。
複合タングステン酸化物粒子の結晶子径は特に限定されないが、特に優れた赤外線吸収特性を発揮させる観点から、複合タングステン酸化物粒子の結晶子径は10nm以上100nm以下であることが好ましく、10nm以上80nm以下であることがより好ましく、10nm以上60nm以下であることがさらに好ましく、10nm以上40nm以下であることが特に好ましい。複合タングステン酸化物粒子の結晶子径を10nm以上100nm以下とすることで特に優れた赤外線吸収特性を発揮することができる。
結晶子径は例えば粉末X線回折の回折パターンから、Scherrerの式を用いて算出することができる。
複合タングステン酸化物粒子は、例えばその表面をSi、Ti、Zr、Alから選択された1種類以上の元素を含有する酸化物で被覆することもできる。係る被覆を有することで、複合タングステン酸化物粒子の耐候性を特に向上させることができ、好ましい。
(樹脂媒体)
既述のように本実施形態の赤外線吸収体は、樹脂媒体を有することができる。樹脂媒体は、既述の複合タングステン酸化物粒子が集合した複合タングステン酸化物粒子集合体を保持し、赤外線吸収体の外形を形作る働きを有する。
(樹脂媒体)
既述のように本実施形態の赤外線吸収体は、樹脂媒体を有することができる。樹脂媒体は、既述の複合タングステン酸化物粒子が集合した複合タングステン酸化物粒子集合体を保持し、赤外線吸収体の外形を形作る働きを有する。
樹脂媒体としては特に限定されるものではないが、本実施形態の赤外線吸収体は例えば窓材等で用いることができることから、樹脂媒体としては可視光透過性に優れた材料を用いることが好ましい。
樹脂媒体としては、例えばポリエチレン樹脂、ポリ塩化ビニル樹脂、ポリ塩化ビニリデン樹脂、ポリビニルアルコール樹脂、ポリスチレン樹脂、ポリプロピレン樹脂、エチレン酢酸ビニル共重合体、ポリエステル樹脂、ふっ素樹脂、ポリカーボネート樹脂、アクリル樹脂、及びポリビニルブチラール樹脂からなる群から選択される1種類以上の樹脂を好ましく用いることができる。
(赤外線吸収体の構造について)
本実施形態の赤外線吸収体は、樹脂媒体中に既述の複合タングステン酸化物粒子が部分的に高密度に集合して存在する複合タングステン酸化物粒子集合体を配置した構造を有する。
(赤外線吸収体の構造について)
本実施形態の赤外線吸収体は、樹脂媒体中に既述の複合タングステン酸化物粒子が部分的に高密度に集合して存在する複合タングステン酸化物粒子集合体を配置した構造を有する。
複合タングステン酸化物粒子集合体は、複合タングステン酸化物粒子が部分的に高密度に集合して存在し、集合体を形成していればよく、その具体的な形状等は特に限定されない。ただし、本発明の発明者らの検討によれば、本実施形態の赤外線吸収体が有する複合タングステン酸化物粒子集合体は、樹脂媒体内で、帯状、鱗片状、ロッド状から選択された1種類以上の形状を有することが好ましい。
なお、帯状とは長方形形状を意味する。
鱗片状とは、鱗状の形状だけでなく、楕円状や、円状、多角形状、不定形形状等から選択された1種類以上の形状を意味する。
ロッド状とは、棒状形状を意味するが、その端部の形状は特に限定されるものではない。このため、ロッド状の形状には、例えば柱状、樹状、針状、円錐形状等の形状を含むことができる。
鱗片状とは、鱗状の形状だけでなく、楕円状や、円状、多角形状、不定形形状等から選択された1種類以上の形状を意味する。
ロッド状とは、棒状形状を意味するが、その端部の形状は特に限定されるものではない。このため、ロッド状の形状には、例えば柱状、樹状、針状、円錐形状等の形状を含むことができる。
なお、本実施形態の赤外線吸収体は、後述するように、例えば樹脂媒体と、複合タングステン酸化物粒子との混合物を延伸して形成することができ、複合タングステン酸化物粒子集合体の長手方向が、係る延伸方向に沿った形状を有する場合が多い。このため、本実施形態の赤外線吸収体を、延伸方向を含む面で観察した際に、本実施形態の赤外線吸収体が有する複合タングステン酸化物粒子集合体が上述の帯状、鱗片状、ロッド状から選択された1種類以上の形状を有することが好ましい。
既述のように、複合タングステン酸化物粒子集合体は、複数の複合タングステン酸化物粒子が部分的に高密度に存在、集合して形成される集合体である。
そして、本実施形態の赤外線吸収体は、複合タングステン酸化物粒子集合体内に存在する複合タングステン酸化物粒子の面積をA、複合タングステン酸化物粒子集合体の輪郭線で囲まれた領域の面積をBとした場合に、以下の式(2)により算出される面積率Sが50%以下である複合タングステン酸化物粒子集合体を含むことが好ましい。本実施形態の赤外線吸収体は、上記面積率Sが20%以下の複合タングステン酸化物粒子集合体を含むことがより好ましい。
A/B×100=S ・・・(2)
上記面積率Sは、複合タングステン酸化物粒子集合体の輪郭線(外周)で囲まれた領域の面積に占める、複合タングステン酸化物粒子の面積の割合を示している。このため、上記面積率Sが50%以下の複合タングステン酸化物粒子集合体は、複合タングステン酸化物粒子が適度な距離をもって集合体を形成し、該粒子間に微小な空間を有していることを意味する。従って、上記面積率Sが50%以下の複合タングステン酸化物粒子集合体に対して光を照射した場合でも光の散乱が生じることを抑制し、赤外線吸収体のヘイズを低くすることができ、好ましいからである。
上記面積率Sは、複合タングステン酸化物粒子集合体の輪郭線(外周)で囲まれた領域の面積に占める、複合タングステン酸化物粒子の面積の割合を示している。このため、上記面積率Sが50%以下の複合タングステン酸化物粒子集合体は、複合タングステン酸化物粒子が適度な距離をもって集合体を形成し、該粒子間に微小な空間を有していることを意味する。従って、上記面積率Sが50%以下の複合タングステン酸化物粒子集合体に対して光を照射した場合でも光の散乱が生じることを抑制し、赤外線吸収体のヘイズを低くすることができ、好ましいからである。
なお、上記面積率Sの下限値は特に限定されないが、複合タングステン酸化物粒子集合体として、十分な量の複合タングステン酸化物粒子が集合した形態を有するため、例えば1%以上であることが好ましく、3%以上であることがより好ましい。
上記面積率Sを評価する場合には、任意に選択した一方の面から観察し、評価を行うことが好ましい。本実施形態の赤外線吸収体は、後述するように、例えば樹脂媒体と、複合タングステン酸化物粒子との混合物を延伸して形成することができる。このため、係る延伸方向を含む面で観察し、複合タングステン酸化物粒子集合体の面積率を評価することがより好ましい。
本実施形態の赤外線吸収体が含有する複合タングステン酸化物粒子集合体は、短手方向の長さが2μm以下であることが好ましく、1μm以下であることがより好ましい。これは複合タングステン酸化物粒子集合体の短手方向の長さを2μm以下とすることで、得られる赤外線吸収体の機械的強度を高めることができ、また可視領域の光の透過性を高め、赤外線領域の光の吸収を高めることができるからである。また、複合タングステン酸化物粒子集合体の短手方向の長さを2μm以下とすることで、赤外線吸収体の可視領域の光の散乱を抑制し、透過性が高い性質、すなわち低いヘイズで透明性を高めることができる。
複合タングステン酸化物粒子集合体の短手方向の長さの下限値は特に限定されないが、例えば50nm以上とすることが好ましい。
さらに、本実施形態の赤外線吸収体が含有する複合タングステン酸化物粒子集合体は、長手方向の長さが10μm以下であることが好ましく、5μm以下であることがより好ましい。これは複合タングステン酸化物粒子集合体の長手方向の長さを10μm以下とすることで、得られる赤外線吸収体の機械的強度を高めることができ、また可視領域の光の透過性を高め、赤外線領域の光の吸収を高めることができるからである。また、複合タングステン酸化物粒子集合体の長手方向の長さを10μm以下とすることで、赤外線吸収体の可視領域の光の散乱を抑制し、透過性が高い性質、すなわち低いヘイズで透明性を高めることができる。
複合タングステン酸化物粒子集合体の長手方向の長さの下限値は特に限定されないが、例えば50nm以上とすることが好ましい。
なお、複合タングステン酸化物粒子集合体の短手方向、及び長手方向の長さを評価する場合には、任意に選択した一方の面から観察し、評価を行うことが好ましい。本実施形態の赤外線吸収体は、後述するように、例えば樹脂媒体と、複合タングステン酸化物粒子との混合物を延伸して形成することができ、複合タングステン酸化物粒子集合体の長手方向が、係る延伸方向に沿った形状を有する場合が多い。このため、係る延伸方向を含む面で観察し、複合タングステン酸化物粒子集合体の短手方向、及び長手方向の長さを評価することがより好ましい。
本実施形態の赤外線吸収体の形状は特に限定されるものではなく、用途に応じて任意の形状を有することができる。
ところで、本実施形態の赤外線吸収体は、含有する複合タングステン酸化物粒子が、赤外線領域の光を吸収することで、赤外線を遮蔽する。また、複合タングステン酸化物粒子が、赤外線領域の光を吸収すると、吸収した光を熱に変換し、赤外線吸収体を発熱させる。結果的に、赤外線吸収体は、赤外線領域の光を吸収して発熱体としても機能する。
このため、本実施形態の赤外線吸収体は、例えば赤外線の遮蔽が要求される窓材や、赤外線を吸収して発熱する高機能繊維として用いることができる。
そこで、本実施形態の赤外線吸収体は、例えばフィルム形状、テープ形状、および繊維形状から選択されたいずれかの形状を有することができる。
なお、フィルム形状とは薄膜形状を意味する。また、テープ形状とは、長手方向に沿って長く、短手方向すなわち幅が長手方向の長さと比較して狭く、かつ薄くて長い帯状の形状を意味する。テープ形状は、例えばフィルム形状の赤外線吸収体を切断等することにより形成することができる。繊維形状とは細い糸状の形状を意味する。
上述のように本実施形態の赤外線吸収体が、フィルム状に延伸され、フィルム形状を有する場合、該赤外線吸収体は赤外線吸収フィルムともいえる。
本実施形態の赤外線吸収体が、例えば赤外線吸収フィルムをテープ状に裁断してテープ形状を有する場合には、該赤外線吸収体は赤外線吸収テープともいえる。
また、本実施形態の赤外線吸収体が、繊維形状を有する場合には、該赤外線吸収体は赤外線吸収繊維ともいえる。
赤外線吸収フィルムや赤外線吸収テープは、複合タングステン酸化物粒子集合体が含まれることから赤外線領域の光を吸収し、赤外線遮蔽や赤外線による発熱の機能を発揮する。
また、繊維状に延伸された赤外線吸収繊維は、赤外線領域の光を吸収して発熱する繊維としての機能を発揮する。
既述のように、従来は可視領域の光の散乱を抑制し、透明性を確保するためには、透明樹脂中に均一に分散させる必要があると考えられていた。
しかしながら、複合タングステン酸化物粒子が集合した複合タングステン酸化物粒子集合体を有する本実施形態の赤外線吸収体においても、可視領域の光の散乱を抑制し、透明性を確保しつつ、赤外線を吸収できる。すなわち、複合タングステン酸化物粒子集合体を含む新規な構造を有する赤外線吸収体とすることができる。
本実施形態の赤外線吸収体によれば、上述のように可視領域の光の散乱を抑制し、可視光の透明性を確保しつつ、赤外線を吸収できることから、赤外線を吸収する窓材などに用いることができる。そして、本実施形態の赤外線吸収体は赤外線を吸収できるため、窓材に用いることで、室内の温度上昇を抑制することが可能になる。
また、本実施形態の赤外線吸収体は、窓材以外の用途にも用いることができ、例えば繊維等として用いることもできる。本実施形態の赤外線吸収体を繊維として用いる場合、本実施形態の赤外線吸収体は吸収した赤外線を熱に変換することもでき、可視領域の光を透過することから着色はほとんどないため発熱する高機能繊維として用いることができる。
[赤外線吸収体の製造方法]
本実施形態の赤外線吸収体の製造方法の一構成例について以下に説明する。
[赤外線吸収体の製造方法]
本実施形態の赤外線吸収体の製造方法の一構成例について以下に説明する。
なお、本実施形態の赤外線吸収体の製造方法により、既述の赤外線吸収体を製造することができる。このため、既に説明した事項の一部については説明を省略する。
ここではまず、本実施形態の赤外線吸収体の製造方法で用いる複合タングステン酸化物粒子の製造方法の一構成例について説明する。
(複合タングステン酸化物粒子の製造方法)
本実施形態の赤外線吸収体は既述のように複合タングステン酸化物粒子を含むことから、ここではまず複合タングステン酸化物粒子の製造方法の一構成例について説明する。なお、本実施形態の赤外線吸収体の製造方法における、複合タングステン酸化物粒子を製造する工程は任意の工程であり、係る工程を実施せずに例えば販売されている複合タングステン酸化物粒子等を用いることもできる。
(複合タングステン酸化物粒子の製造方法)
本実施形態の赤外線吸収体は既述のように複合タングステン酸化物粒子を含むことから、ここではまず複合タングステン酸化物粒子の製造方法の一構成例について説明する。なお、本実施形態の赤外線吸収体の製造方法における、複合タングステン酸化物粒子を製造する工程は任意の工程であり、係る工程を実施せずに例えば販売されている複合タングステン酸化物粒子等を用いることもできる。
既述のように、複合タングステン酸化物粒子が含有する複合タングステン酸化物は、一般式MxWyOzで表記できる。係る複合タングステン酸化物を含む複合タングステン酸化物粒子は、例えば複合タングステン酸化物粒子の出発原料である、タングステン及び元素Mを含有する混合物を熱処理する固相反応法で製造することができる。すなわち、複合タングステン酸化物粒子の製造方法は、例えば以下の工程を有することができる。
タングステン及び元素Mを含有する混合物を調製する混合物調製工程。
上記混合物を熱処理する熱処理工程。
以下、各工程について説明する。
(1)混合物調製工程
混合物調製工程では、タングステン及び元素Mを含有する混合物(以下、単に「混合物」とも記載する)を調製することができる。
上記混合物を熱処理する熱処理工程。
以下、各工程について説明する。
(1)混合物調製工程
混合物調製工程では、タングステン及び元素Mを含有する混合物(以下、単に「混合物」とも記載する)を調製することができる。
既述の一般式MxWyOzで表記される複合タングステン酸化物粒子を得るための出発原料には、例えばタングステン含有材料と、M元素含有材料との混合物を用いることができる。このため、混合物調製工程は、タングステン含有材料と、M元素含有材料とを混合する工程とすることができる。
なお、タングステン含有材料としては、後述するようにタングステン単体や、タングステンを含有する化合物を用いることができる。また、M元素含有材料としてはM元素の単体や、M元素を含有する化合物を用いることができる。
混合物調製工程では、例えば、タングステン含有材料であるタングステン含有粉末と、M元素含有材料であるM元素含有粉末とを混合し、混合物である混合粉末を調製することができる。
なお、タングステン含有粉末としては、例えば三酸化タングステン粉末、二酸化タングステン粉末、タングステン酸化物の水和物、六塩化タングステン粉末、タングステン酸アンモニウム粉末、六塩化タングステンをアルコール中に溶解させた後乾燥して得られるタングステン酸化物の水和物粉末、六塩化タングステンをアルコール中に溶解させたのち水を添加して沈殿させこれを乾燥して得られるタングステン酸化物の水和物粉末、タングステン酸アンモニウム水溶液を乾燥して得られるタングステン化合物粉末、及び金属タングステン粉末から選択された1種類以上を好ましく用いることができる。
ここでは、出発原料として混合粉末を用いる例を挙げて説明したが、係る形態に限定されるものではない。例えば、複合タングステン酸化物粒子を得るための出発原料であるタングステン含有材料として、タングステン含有溶液または分散液を用いることもできる。タングステン含有材料がタングステン含有溶液または分散液の場合、得られる混合物に含まれる各元素は特に容易に均一混合可能となる。
タングステン含有材料であるタングステン含有溶液または分散液としては、例えば六塩化タングステンのアルコール溶液や、タングステン酸アンモニウム水溶液、六塩化タングステンをアルコール中に溶解させた後、水を添加して沈殿を生成させた分散液等が挙げられる。
なお、タングステン含有材料としてタングステン含有溶液または分散液を用いる場合、M元素含有材料としては、既述の場合と同様にM元素含有粉末を用いることもできるが、M元素含有溶液を用いることもできる。このため、例えば、上述のタングステン含有溶液または分散液と、M元素含有粉末もしくはM元素含有溶液とを混合し、その後乾燥した混合粉末を熱処理工程に供する混合物として用いることもできる。
また、出発原料であるM元素含有材料としてM元素含有溶液を用い、タングステン含有材料としてタングステン含有粉末を用いることもできる。この場合、例えば、上述のタングステン含有粉末と、M元素含有溶液とを混合し、その後乾燥した混合粉末を熱処理工程に供する混合物として用いることができる。
M元素含有材料としては特に限定されないが、例えばM元素の単体や、M元素のタングステン酸塩、塩化物塩、硝酸塩、硫酸塩、シュウ酸塩、酸化物、炭酸塩、水酸化物等から選択された1種類以上が挙げられる。なお、上述のようにM元素含有材料を溶液とする場合には、水等の溶媒を添加した場合に、溶液状になるM元素含有材料を用いることができる。
複合タングステン酸化物粒子を工業的に製造する場合には有毒なガス等が発生しにくい原料を用いることが好ましい。このため、例えば、タングステン含有化合材料としてタングステン酸化物の水和物粉末や三酸化タングステン粉末を、M元素含有材料としてM元素の炭酸塩や水酸化物をそれぞれ用いると、熱処理等の段階で有害なガス等が発生することが無いため好ましい。
タングステン含有材料と、M元素含有材料との混合物に含まれるM元素の物質量xと、タングステンの物質量yとの物質量比(モル比)を示すx/yは、目的とする複合タングステン酸化物の組成比に応じた値を有することが好ましい。具体的には例えば複合タングステン酸化物の組成の説明において既述のようにx/yは0.001≦x/y≦1.0であることが好ましく、0.001≦x/y≦0.5であることがより好ましく、0.001≦x/y≦0.37であることがさらに好ましく、0.20≦x/y≦0.37であることが特に好ましい。
(2)熱処理工程
熱処理工程では、混合物調製工程で調製した混合物の熱処理を行うことができる。
(2)熱処理工程
熱処理工程では、混合物調製工程で調製した混合物の熱処理を行うことができる。
熱処理工程における熱処理は、還元性ガス雰囲気、還元性ガスと不活性ガスとの混合ガス雰囲気、または不活性ガス雰囲気のいずれかの雰囲気中で実施することが好ましい。
ここで、熱処理工程における熱処理条件は特に限定されないが、例えば熱処理の雰囲気等に応じて選択することができる。
熱処理工程の原料となる混合物を、還元性ガス雰囲気中、または還元性ガスと不活性ガスとの混合ガス雰囲気中にて熱処理する場合、熱処理温度は、複合タングステン酸化物粒子が含有する複合タングステン酸化物が結晶化する温度よりも高いことが好ましい。
熱処理工程の原料となる混合物を、還元性ガス雰囲気中、または還元性ガスと不活性ガスとの混合ガス雰囲気中で熱処理する場合、その熱処理温度は500℃以上1000℃以下が好ましく、500℃以上800℃以下がより好ましい。
なお、還元性ガス雰囲気、または還元性ガスと不活性ガスとの混合ガス雰囲気中で熱処理を行った後、所望によりさらに不活性ガス雰囲気中で500℃以上1200℃以下の温度で熱処理しても良い。
上述のように還元性ガスを用いる場合、還元性ガスは特に限定されないがH2(水素)を用いることが好ましい。また、還元性ガスと不活性ガスとの混合ガスを用いる場合、還元性ガス、及び不活性ガスの種類は特に限定されないが、例えば還元性ガスとしてはH2を、不活性ガスとしてはAr(アルゴン)や、N2(窒素)等から選択された1種類以上を用いることができる。
還元性ガスと不活性ガスとの混合ガスを用いる場合、還元性ガスの濃度は、焼成温度や、出発原料である混合物の物量、還元性ガスの種類等に応じて適宜選択すればよく特に限定されない。
例えば還元性ガスと不活性ガスとの混合ガスにおいて、還元性ガスとしてH2を用いる場合、その濃度は例えば、0.1体積%以上であることが好ましく、2体積%以上であることが好ましい。これは還元性ガスと不活性ガスとの混合ガス中のH2ガス濃度を0.1体積%以上とすることで効率よく還元を進めることができ、得られる複合タングステン酸化物のタングステンに対する酸素の割合を容易に所望の範囲に調整できるからである。
また、還元性ガスと不活性ガスとの混合ガスにおいて、還元性ガスとしてH2を用いる場合、H2濃度は例えば20体積%以下であることが好ましく、10体積%以下であることがより好ましく、7体積%以下であることがさらに好ましい。還元性ガスの濃度が20体積%以下であれば、急速な還元による赤外線吸収能を有しないWO2が生成するのをより確実に回避できるからである。
熱処理工程の原料となる混合物を、不活性ガス雰囲気中にて熱処理する場合、熱処理温度は650℃以上1000℃以下が好ましい。650℃以上1000℃以下で熱処理された混合物は、十分な赤外線吸収能を有し赤外線吸収粒子として効率が良い。
なお、不活性ガスとしては例えばAr、N2等から選択された1種類以上の不活性ガスを用いることが良い。
上述の熱処理温度や熱処理時間等を調整し、得られる複合タングステン酸化物粒子が含有する複合タングステン酸化物中のタングステンと酸素との物質量比(モル比)を示すz/yを既述のように2.2≦z/y≦3.0となるようにすることが好ましい。
ここまで、混合物調製工程で調製した混合物を、熱処理工程で熱処理することで複合タングステン酸化物粒子を調製する固相反応法の例を示したが、複合タングステン含有粒子の製造方法は係る方法に限定されるものではない。複合タングステン酸化物粒子は、例えば、熱プラズマ法でも製造することができる。熱プラズマ法により複合タングステン酸化物粒子を製造する場合、例えば、熱プラズマ中に原料供給する際の供給速度、原料供給に用いるキャリアガスの流量、プラズマ領域を保持するプラズマガスの流量、および、プラズマ領域のすぐ外側を流すシースガスの流量等を調整し、所望の組成の複合タングステン酸化物粒子を得ることができる。
なお、複合タングステン酸化物粒子の製造方法は、上記混合物調製工程と、熱処理工程のみに限定されるものではなく、それ以外に任意の工程を有することもできる。
複合タングステン酸化物粒子の製造方法は、例えば熱処理工程後、得られた複合タングステン酸化物粒子を所定の粒子径となるように粉砕処理等で微粒子化する粉砕工程を有することもできる。
また、複合タングステン酸化物粒子の製造方法は、熱処理工程や、粉砕工程にて得られた複合タングステン酸化物粒子の表面をSi、Ti、Zr、Alから選択される1種類以上の金属を含有する酸化物で被覆する被覆工程を有することもできる。
被覆工程を実施し、複合タングステン酸化物粒子の表面を被覆することで、耐候性を向上させることができ、好ましい。被覆方法は特に限定されないが、当該複合タングステン酸化物粒子を分散した溶液中へ、Si、Ti、Zr、Alから選択される1種類以上の金属のアルコキシドを添加する方法が挙げられる。
(赤外線吸収体の製造方法)
次に、本実施形態の赤外線吸収体の製造方法の一構成例について説明する。
(赤外線吸収体の製造方法)
次に、本実施形態の赤外線吸収体の製造方法の一構成例について説明する。
本実施形態の赤外線吸収体の製造方法により得られる赤外線吸収体は、樹脂媒体中に複合タングステン酸化物粒子集合体が存在する。このため、本実施形態の赤外線吸収体の製造方法では、樹脂媒体に複合タングステン酸化物粒子を混合し形成することができる。
本実施形態の赤外線吸収体の製造方法の具体的な構成例について以下に説明する。
本実施形態の赤外線吸収体の製造方法は、例えば以下の工程を有することができる。
複合タングステン酸化物粒子を溶媒に分散し、複合タングステン酸化物粒子分散液を調製する分散液調製工程。
複合タングステン酸化物粒子分散液から、複合タングステン酸化物粒子含有マスターバッチを調製するマスターバッチ調製工程。
複合タングステン酸化物粒子含有マスターバッチを成形する成形工程。
複合タングステン酸化物粒子分散液から、複合タングステン酸化物粒子含有マスターバッチを調製するマスターバッチ調製工程。
複合タングステン酸化物粒子含有マスターバッチを成形する成形工程。
以下、工程ごとに説明する。
(1)分散液調製工程
分散液調製工程では、複合タングステン酸化物粒子を溶媒中に混合、分散し、複合タングステン酸化物粒子分散液を調製することができる。
(1)分散液調製工程
分散液調製工程では、複合タングステン酸化物粒子を溶媒中に混合、分散し、複合タングステン酸化物粒子分散液を調製することができる。
分散液調製工程で複合タングステン酸化物粒子を分散する溶媒は特に限定されるものではなく、後述するマスターバッチ調製工程におけるマスターバッチとする際の加工への適用性等を考慮して選択することができる。
溶媒としては例えば、水、エタノ-ル、プロパノ-ル、ブタノ-ル、イソプロピルアルコ-ル、イソブチルアルコ-ル、ジアセトンアルコ-ルなどのアルコ-ル類、メチルエ-テル、エチルエ-テル、プロピルエ-テルなどのエ-テル類、エステル類、アセトン、メチルエチルケトン、ジエチルケトン、シクロヘキサノン、イソブチルケトン、メチルイソブチルケトン(MIBK)などのケトン類、トルエンなどの芳香族炭化水素類等から選択された1種類以上の溶媒を用いることができる
なお、当該溶媒は、上述の溶媒に限定されるものではなく、例えば樹脂のモノマーやオリゴマーを用いてもよい。
なお、当該溶媒は、上述の溶媒に限定されるものではなく、例えば樹脂のモノマーやオリゴマーを用いてもよい。
複合タングステン酸化物粒子分散液における溶媒の含有量は特に限定されないが、複合タングステン酸化物粒子100質量部に対し溶媒を80質量部以上含むことが好ましい。これは、複合タングステン酸化物粒子100質量部に対する溶媒の割合を80質量部以上とすることで、分散液としての保存性を担保し易く、その後の複合タングステン酸化物粒子含有マスターバッチを作製する際の作業性を高めることもできるからである。
複合タングステン酸化物粒子100質量部に対する溶媒の割合の上限値は特に限定されないが、複合タングステン酸化物粒子含有マスターバッチを製造する際に容易に溶媒を除去できるように複合タングステン酸化物粒子100質量部に対する溶媒の割合は400質量部以下とすることが好ましい。また、複合タングステン酸化物粒子含有マスターバッチ中に溶剤が多量に残留すると発泡等の原因となることから、該マスターバッチでの有機溶媒の残留量は0.5質量%以下であることが望ましい。
得られる複合タングステン酸化物粒子分散液、ならびに赤外線吸収体における複合タングステン酸化物粒子の分散状態を調整するために、分散液に各種の分散剤、界面活性剤、カップリング剤、樹脂改質剤等を添加することもできる。
本実施形態の複合タングステン酸化物粒子分散液に分散剤等を添加する場合、該分散剤等としては特に限定されるものではない。各種分散剤としては例えば、アミンを含有する基、水酸基、カルボキシル基、またはエポキシ基を官能基として有するものを好ましく用いることができる。
これらの官能基は、複合タングステン酸化物粒子の表面に吸着して次工程で得るマスターバッチ中での複合タングステン酸化物粒子間の距離を調整する機能を有する。これらの官能基のいずれかを分子中にもつ高分子系分散剤を分散剤等としてより好ましく用いることができる。
このような分散剤等として、ソルスパース(登録商標)9000、12000、17000、20000、21000、24000、26000、27000、28000、32000、32500、35100、41000、53095、54000、250、ソルプラス(登録商標) DP310、DP320、DP330、L300、L400、K500、R700(日本ルーブリゾール株式会社製)、EFKA(登録商標)4008、4009、4010、4015、4046、4047、4060、4080、7462、4020、4050、4055、4400、4401、4402、4403、4300、4320、4330、4340、4416、4425、4575、4585、4590、6220、6225、6700、6780、6782、8503(エフカアディティブズ社製)、アジスパー(登録商標)PA111、PB821、PB822、PB824、PN411、フェイメックスL-12(味の素ファインテクノ株式会社製)、DisperBYK(登録商標)101、102、106、108、111、116、130、140、142、145、161、162、163、164、166、167、168、170、171、174、180、182、192、193、2000、2001、2012、2013、2020、2025、2050、2070、2155、2164、220S、300、306、320、322、325、330、340、350、377、378、380N、410、425、430、BYK(登録商標)9076、9077、P4100、P4101、P4102(ビックケミー・ジャパン株式会社製)、ディスパロン(登録商標)1751N、1831、1850、1860、1934、DA-400N、DA-703-50、DA-725、DA-705、DA-7301、DN-900、NS-5210、NVI-8514L(楠本化成株式会社製)、アルフォン(登録商標)UC-3000、UF-5022、UG-4010、UG-4035、UG-4070(東亞合成株式会社製)、TERPLUS(登録商標) D1180、D1330、MD1000(大塚化学株式会社製)、KBM-573、575、903、KBE-9007、9103(信越化学株式会社製)等が挙げられる。
複合タングステン酸化物粒子の溶媒への分散方法は特に限定されないが、例えば、ビ-ズミル、ボ-ルミル、サンドミル、ペイントシェーカー、超音波ホモジナイザ-等から選択された1種類以上の分散装置を用いる方法等が挙げられる。
これらの分散装置を用いた機械的な分散処理によって、複合タングステン酸化物粒子の溶媒中への分散と同時に、複合タングステン酸化物粒子同士の衝突などにより微粒子化が進む。
なお、複合タングステン酸化物粒子分散液に含まれる複合タングステン酸化物粒子の粒子径、結晶子径等について、所望の範囲となるように、分散処理条件(粉砕条件、微粒子化条件等ともいう)を選択することができる。
分散液調製工程で得られる複合タングステン酸化物粒子分散液の状態は、複合タングステン酸化物粒子を溶媒中に分散した時の複合タングステン酸化物粒子の分散状態を測定することで確認することができる。
複合タングステン酸化物粒子分散液の状態は、例えば複合タングステン酸化物粒子が、溶媒中において粒子および粒子の集合状態として存在する液から試料をサンプリングし、市販されている種々の粒度分布計で測定することで確認することができる。粒度分布計としては、例えば、動的光散乱法を原理とした大塚電子社製ELS-8000等やマクロトラックベル社製ナノトラック(登録商標)等の公知の測定装置を用いることができる。
複合タングステン酸化物粒子分散液の状態の指針の一例として、複合タングステン酸化物粒子の分散粒子径や粒度分布が挙げられる。光学特性の観点から大塚電子社製ELS-8000で測定される分散粒子径は、800nm以下であることが好ましく、200nm以下であることがより好ましく、100nm以下であることがさらに好ましい。なお、分散粒子径の下限値は特に限定されないが、例えば10nm以上とすることができる。
複合タングステン酸化物粒子の分散粒子径を800nm以下とすることで、最終的に得られる赤外線吸収体(フィルム、テープ、繊維など各種形状を含む)の色が、灰色系になることを回避できるからである。
(2)マスターバッチ調製工程
マスターバッチ調製工程では、複合タングステン酸化物粒子分散液から、複合タングステン酸化物粒子含有マスターバッチを調製することができる。
(2)マスターバッチ調製工程
マスターバッチ調製工程では、複合タングステン酸化物粒子分散液から、複合タングステン酸化物粒子含有マスターバッチを調製することができる。
複合タングステン酸化物粒子分散液から、複合タングステン酸化物粒子含有マスターバッチ(以下、単に「マスターバッチ」と記載する)を調製する方法は特に限定されない。
マスターバッチ調製工程は、例えば以下の各ステップを有することができる。
複合タングステン酸化物粒子分散液に含まれる溶媒を、マスターバッチに残留が許容される量以下まで低減、除去する溶媒除去ステップ。
なお、溶媒除去ステップでは、溶媒を大幅に低減、除去し、複合タングステン酸化物粒子分散粉とすることもできる。
そして、溶媒除去工程で得られた複合タングステン酸化物粒子分散液や、分散粉を樹脂媒体と混練し、成形することでマスターバッチとする混練・成形ステップ。
なお、溶媒除去ステップでは、溶媒を大幅に低減、除去し、複合タングステン酸化物粒子分散粉とすることもできる。
そして、溶媒除去工程で得られた複合タングステン酸化物粒子分散液や、分散粉を樹脂媒体と混練し、成形することでマスターバッチとする混練・成形ステップ。
各ステップについて説明する。
まず、溶媒除去ステップについて説明する。
溶媒除去ステップでは上述のように複合タングステン酸化物粒子分散液から溶媒を低減、除去することができる。
複合タングステン酸化物粒子分散液から溶媒を除去する方法としては特に限定されないが、例えば複合タングステン酸化物粒子分散液を減圧乾燥する方法を好ましく用いることができる。具体的には、複合タングステン酸化物粒子分散液を撹拌しながら減圧乾燥し、複合タングステン酸化物粒子含有組成物と溶媒成分とを分離する。減圧する際の圧力値は特に限定されず、例えば溶媒除去ステップの時間等に応じて適宜選択できる。なお、複合タングステン酸化物粒子分散粉を得るには、複合タングステン酸化物粒子分散液に、既述の高分子系分散剤が含まれていることが好ましい。
溶媒除去ステップにおいて減圧乾燥法を用いることで、複合タングステン酸化物粒子分散液からの溶媒の除去効率が向上するとともに、溶媒除去ステップ後に得られる複合タングステン酸化物粒子分散液や、複合タングステン酸化物粒子分散粉が高温に曝される時間を抑制できる。このため、当該分散液や、分散粉中に分散している複合タングステン酸化物粒子の集合が過度に進行せず好ましい。さらに複合タングステン酸化物粒子分散粉の生産性も上がり、蒸発した溶媒を回収することも容易で、環境的配慮からも好ましい。
溶媒除去ステップ後に得られた複合タングステン酸化物粒子分散液や、複合タングステン酸化物粒子分散粉において、残留する有機溶媒は5質量%以下であることが好ましい。残留する有機溶媒が5質量%以下であれば、当該複合タングステン酸化物粒子分散液や、複合タングステン酸化物粒子分散粉を、マスターバッチに加工した際に気泡が発生せず、最終的に得られるマスターバッチ粉砕物にも気泡が含まれない。このため、耐薬品性の観点から好ましい。
溶媒除去ステップに用いる設備としては、特に限定されないが、加熱および減圧が可能で、当該分散粉の混合や回収がし易いという観点から、例えば真空流動乾燥機、振動流動乾燥機等を好ましく用いることができる。
マスターバッチは、複合タングステン酸化物粒子を、樹脂媒体と混練し、樹脂媒体中に分散させて得た混練物をペレット化することで得られる。
具体的には、溶媒除去ステップ後に得られた複合タングステン酸化物粒子分散液や複合タングステン酸化物粒子分散粉と、樹脂媒体の粉粒体またはペレットと、必要に応じて他の添加剤とを混合し溶融した後、ベント式一軸、もしくは二軸の押出機で混練する。そして、一般的な溶融押出された混練物をカットする方法によりペレット状に成形、加工することによって、マスターバッチを得られる(混練・成形ステップ)。
なお、この際、得られるマスターバッチ内に複合タングステン酸化物粒子集合体が残るように、予備試験等を行い、混練の程度、条件を調整することが好ましい。
マスターバッチの形状としては特に限定されないが、例えば円柱形状や角柱形状のものを挙げることができる。また、溶融押出物を直接カットするいわゆるホットカット法を採ることも可能である。この場合、マスターバッチは、球状に近い形状とすることが一般的である。
(3)成形工程
成形工程では、マスターバッチを成形することができる。
(3)成形工程
成形工程では、マスターバッチを成形することができる。
成形工程では、具体的には、複合タングステン酸化物粒子を含有する既述のマスターバッチを延伸することができる。これにより、本実施形態に係る赤外線吸収体を得ることができる。
マスターバッチ中で複合タングステン酸化物粒子は複数の粒子が緩く集合した集合物を形成しており、延伸によりこの集合体が引き伸ばされることで複合タングステン酸化物粒子集合体が樹脂媒体中に形成される。
この延伸は、フィルムやテープを形成する為の一軸延伸や二軸延伸でも良く、また繊維を形成する為の一方向への延伸でも良い。延伸の条件は、赤外線吸収体に発生する張力などの条件を適宜選択すればよい。
なお、成形工程では、マスターバッチに樹脂媒体を加えて混練した樹脂混練物を成形することもできる。
成形工程により得られる赤外線吸収体内に、複合タングステン酸化物粒子集合体が形成されるように、例えば予備試験により、成形工程後に得られる赤外線吸収体中の複合タングステン酸化物粒子集合体の発生状態等を確認しながら、延伸条件等を選択することが好ましい。
マスターバッチを用いて、フィルム形状を有する赤外線吸収体である赤外線吸収フィルムを製造する構成例を説明する。
マスターバッチを加熱溶融し、Tダイ等を用いる溶融押出成型法により溶融物をシート状に成形する。成形されたシートを二軸延伸して、赤外線吸収体である赤外線吸収フィルムを得ることができる。
以下、実施例を挙げて本発明をより具体的に説明するが、本発明はこれに限定されるものではない。
(評価方法)
以下の、各実施例、比較例における、評価方法について説明する。
(1)可視光透過率、日射透過率、ヘイズ
以下の、実施例、参考例における、赤外線吸収体の可視光透過率、日射透過率は、ISO 9050及びJIS R 3106(1998)に準拠して測定を行った。具体的には、日立製作所(株)製の分光光度計U-4100を用いて透過率を測定し、太陽光のスペクトルに応じた係数を乗じて算出した。透過率の測定に当たっては波長300nm以上2100nm以下の範囲について、5nm間隔で測定を行っている。なお、日射透過率は、赤外線吸収体の熱線遮蔽特性を示す指標である。
(評価方法)
以下の、各実施例、比較例における、評価方法について説明する。
(1)可視光透過率、日射透過率、ヘイズ
以下の、実施例、参考例における、赤外線吸収体の可視光透過率、日射透過率は、ISO 9050及びJIS R 3106(1998)に準拠して測定を行った。具体的には、日立製作所(株)製の分光光度計U-4100を用いて透過率を測定し、太陽光のスペクトルに応じた係数を乗じて算出した。透過率の測定に当たっては波長300nm以上2100nm以下の範囲について、5nm間隔で測定を行っている。なお、日射透過率は、赤外線吸収体の熱線遮蔽特性を示す指標である。
ヘイズ値は株式会社村上色彩技術研究所製ヘイズメーターHM-150を用いて測定した。
(2)分散粒子径
複合タングステン酸化物粒子分散液の分散粒子径は、粒度分布計ELS-8000(大塚電子株式会社製)を用いて測定した。
(3)平均粒子径
まず、得られた複合タングステン酸化物粒子を樹脂中に均一に分散させた複合タングステン酸化物粒子分散体を作製した。そして、断面加工により複合タングステン酸化物粒子分散体の薄片化試料を作製した。
(2)分散粒子径
複合タングステン酸化物粒子分散液の分散粒子径は、粒度分布計ELS-8000(大塚電子株式会社製)を用いて測定した。
(3)平均粒子径
まず、得られた複合タングステン酸化物粒子を樹脂中に均一に分散させた複合タングステン酸化物粒子分散体を作製した。そして、断面加工により複合タングステン酸化物粒子分散体の薄片化試料を作製した。
作製した薄片化試料の透過型電子顕微鏡像から、複合タングステン酸化物粒子100個の粒子径を、画像処理装置を用いて測定し、その平均値を算出することで、複合タングステン酸化物粒子の平均粒子径を求めた。
[実施例1]
水6.70kgに、炭酸セシウム(Cs2CO3)7.43kgを溶解して、溶液を得た。当該溶液を、三酸化タングステンの一水和物であるタングステン酸(H2WO4)34.57kgに添加して十分撹拌混合した後、撹拌しながら乾燥し、混合物を得た。この際得られた混合物中のWとCsとの物質量比(モル比)は1:0.33となっている(混合物調製工程)。
[実施例1]
水6.70kgに、炭酸セシウム(Cs2CO3)7.43kgを溶解して、溶液を得た。当該溶液を、三酸化タングステンの一水和物であるタングステン酸(H2WO4)34.57kgに添加して十分撹拌混合した後、撹拌しながら乾燥し、混合物を得た。この際得られた混合物中のWとCsとの物質量比(モル比)は1:0.33となっている(混合物調製工程)。
乾燥後に得られた混合物を、N2ガスをキャリア-とした5体積%H2ガスを供給しながら加熱し、800℃の温度で5.5時間焼成した、その後、当該供給ガスをN2ガスのみに切り替えて、室温まで降温してセシウムタングステン複合酸化物粒子aを得た(熱処理工程)。
セシウムタングステン複合酸化物粒子a25質量%と、分散剤a15質量%と、溶媒のMIBK60質量%とを秤量し、0.3mmφZrO2ビ-ズを入れたペイントシェーカー(浅田鉄工社製)に装填し、20時間粉砕・分散処理することによって複合タングステン酸化物粒子分散液(A-1液)を調製した(分散液調製工程)。
なお、分散剤aとして、高分子系分散剤であり、官能基としてアミンを含有する基を有する変性アクリル系ブロック共重合体(アミン価29、酸価13)を用いた。
得られた複合タングステン酸化物粒子分散液の分散粒子径を測定したところ、分散粒子径は70nmであった。
得られた複合タングステン酸化物粒子分散液(A-1液)を真空流動乾燥機を用いて減圧乾燥法により、MIBKが2質量%となるまで溶媒を除去して実施例1に係る複合タングステン酸化物粒子分散粉(A-1粉)を得た(溶媒除去ステップ)。
得られたA-1粉100質量部に対しポリエチレンテレフタレート樹脂ペレット1400質量部を混合し、二軸押出機を用いて溶融混練して混練物を得て、紐状に押出し、紐状物を得た。なお、溶融混練する際の溶融温度は270℃であった。
得られた紐状物を長さ4mmのペレット状に切断し、マスターバッチ(A-1マスターバッチ)を得た(混練・成形ステップ)。
得られたA-1マスターバッチを270℃として一軸押出機に投入後、Tダイを用いる溶融押出成型法で、温度65℃の冷媒が循環する冷却ロール上に押出して、厚さ300μmのシートを得た。得られた、シートを5cm四方に切断し、厚さ40μmのフィルムになるように二軸延伸を行って、赤外線吸収体である赤外線吸収フィルムを得た。得られた赤外線吸収フィルムの延伸方向の面を電子顕微鏡で観察したところ、短手方向の長さである幅が500nm、長手方向の長さが1μmのセシウムタングステン複合酸化物粒子集合体が観察された。
また、セシウムタングステン複合酸化物粒子集合体に含まれる個々のセシウムタングステン複合酸化物粒子の平均粒子径は、数平均で22nmであった。
さらに、電子顕微鏡の視野にあるセシウムタングステン複合酸化物粒子集合体の面積率Sは18%であった。図1と図2に赤外線吸収体の透過型電子顕微鏡写真を示す。
図1は延伸方向Aと平行な面での観察写真を示しており、図2は、延伸方向A、及び得られた赤外線吸収体のフィルムの厚さ方向Bと平行な面での観察写真を示している。なお、図2におけるブロック矢印Cに沿って赤外線吸収体を観察した際の観察写真が図1に相当する。
図1、図2に示したように、得られた赤外線吸収体10は、複合タングステン酸化物粒子集合体11を有することが確認できた。図1、図2に示した赤外線吸収体10は、楕円形で板状、すなわち鱗片状の複合タングステン酸化物粒子集合体11を有することを確認できた。
なお、図1、図2において、写真の背景に、試料を固定する部材12が写り込んでいるがこれは赤外線吸収体を構成するものではない。
得られた赤外線吸収体である赤外線吸収フィルムの可視光透過率、日射透過率、波長500nmにおける透過率、及び波長1000nmにおける透過率、ヘイズ値を測定した。結果を表1に示す。
[参考例1]
実施例1に係るA-1液100質量部にUV硬化樹脂100質量部加え、十分に混合し塗布液(B-1液)を得た。バーコーターによってB-1液を可視光透過率が90.5%の透明PETフィルムに塗布し、70℃で1分間保持することで乾燥させて溶媒のMIBKを除去した後、紫外線を照射して赤外線吸収体である紫外線硬化膜を得た。得られた紫外線硬化膜の電子顕微鏡写真を図3に示す。図3に示すように、紫外線硬化膜30ではセシウムタングステン複合酸化物粒子31が集合せず、均一に分散して存在することを確認できる。
[参考例1]
実施例1に係るA-1液100質量部にUV硬化樹脂100質量部加え、十分に混合し塗布液(B-1液)を得た。バーコーターによってB-1液を可視光透過率が90.5%の透明PETフィルムに塗布し、70℃で1分間保持することで乾燥させて溶媒のMIBKを除去した後、紫外線を照射して赤外線吸収体である紫外線硬化膜を得た。得られた紫外線硬化膜の電子顕微鏡写真を図3に示す。図3に示すように、紫外線硬化膜30ではセシウムタングステン複合酸化物粒子31が集合せず、均一に分散して存在することを確認できる。
得られた赤外線吸収体である紫外線硬化膜の可視光透過率、日射透過率、波長500nmにおける透過率、及び波長1000nmにおける透過率、ヘイズ値を測定した。結果を表1に示す。
つまり、新規な構造である、複合タングステン酸化物粒子集合体を含む赤外線吸収体であっても、複合タングステン酸化物粒を均一に分散した赤外線吸収体の場合と同様な光学特性が得られることを確認できた。
以上に赤外線吸収体を、実施形態および実施例等で説明したが、本発明は上記実施形態および実施例等に限定されない。特許請求の範囲に記載された本発明の要旨の範囲内において、種々の変形、変更が可能である。
本出願は、2017年11月14日に日本国特許庁に出願された特願2017-219399号に基づく優先権を主張するものであり、特願2017-219399号の全内容を本国際出願に援用する。
10 赤外線吸収体
11 複合タングステン酸化物粒子集合体
11 複合タングステン酸化物粒子集合体
Claims (8)
- 樹脂媒体と、前記樹脂媒体内に配置され、複合タングステン酸化物粒子が集合した複合タングステン酸化物粒子集合体とを有し、
前記複合タングステン酸化物粒子集合体が帯状、鱗片状、ロッド状から選択された1種類以上の形状を有する赤外線吸収体。 - 前記複合タングステン酸化物粒子集合体の短手方向の長さが2μm以下である請求項1に記載の赤外線吸収体。
- 前記複合タングステン酸化物粒子集合体の長手方向の長さが10μm以下である請求項1または2に記載の赤外線吸収体。
- 前記複合タングステン酸化物粒子が以下の一般式(1)で表される複合タングステン酸化物を含む請求項1から請求項3のいずれか一項に記載の赤外線吸収体。
MxWyOz ・・・(1)
(上記一般式(1)中、M元素はアルカリ金属元素およびアルカリ土類金属元素から選択された1種類以上の元素を含み、Wはタングステンを、Oは酸素をそれぞれ表し、x、yおよびzはそれぞれ0.001≦x/y≦0.37、2.2≦z/y≦3.0を満たす。) - 前記複合タングステン酸化物粒子が六方晶の結晶構造の複合タングステン酸化物を含む請求項1から請求項4のいずれか一項に記載の赤外線吸収体。
- 前記複合タングステン酸化物粒子集合体内に存在する前記複合タングステン酸化物粒子の面積をA、前記複合タングステン酸化物粒子集合体の輪郭線で囲まれた領域の面積をBとした場合に、
以下の式(2)により算出される面積率Sが50%以下である請求項1から請求項5のいずれか一項に記載の赤外線吸収体。
A/B×100=S ・・・(2) - 前記樹脂媒体が、ポリエチレン樹脂、ポリ塩化ビニル樹脂、ポリ塩化ビニリデン樹脂、ポリビニルアルコール樹脂、ポリスチレン樹脂、ポリプロピレン樹脂、エチレン酢酸ビニル共重合体、ポリエステル樹脂、ふっ素樹脂、ポリカーボネート樹脂、アクリル樹脂、及びポリビニルブチラール樹脂からなる群から選択される1種類以上の樹脂である請求項1から請求項6のいずれか一項に記載の赤外線吸収体。
- フィルム形状、テープ形状、および繊維形状から選択されたいずれかの形状を有する請求項1から請求項7のいずれか一項に記載の赤外線吸収体。