WO2018148168A1 - Catalyseurs monolithiques céramiques et métalliques tridimensionnels pour la réduction de dioxyde de carbone par du soufre gazeux - Google Patents
Catalyseurs monolithiques céramiques et métalliques tridimensionnels pour la réduction de dioxyde de carbone par du soufre gazeux Download PDFInfo
- Publication number
- WO2018148168A1 WO2018148168A1 PCT/US2018/016962 US2018016962W WO2018148168A1 WO 2018148168 A1 WO2018148168 A1 WO 2018148168A1 US 2018016962 W US2018016962 W US 2018016962W WO 2018148168 A1 WO2018148168 A1 WO 2018148168A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- structured
- metal
- support material
- monolith catalyst
- catalyst
- Prior art date
Abstract
L'invention concerne un catalyseur monolithe structuré en trois tridimensions (3-D) et des méthodes de fabrication et d'utilisation. Le catalyseur tridimensionnel (3-D) contient un matériau de support structuré en trois dimensions, un sulfure métallique ou un oxysulfure métallique catalytiquement actifs, et peut être utilisé pour catalyser la conversion de dioxyde de carbone gazeux (CO2(g)) et de gaz de soufre élémentaire (S(g)) pour produire du monoxyde de carbone gazeux (CO(g)) et du dioxyde de soufre gazeux (SO2(g)).
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201762456362P | 2017-02-08 | 2017-02-08 | |
US62/456,362 | 2017-02-08 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2018148168A1 true WO2018148168A1 (fr) | 2018-08-16 |
Family
ID=63106997
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2018/016962 WO2018148168A1 (fr) | 2017-02-08 | 2018-02-06 | Catalyseurs monolithiques céramiques et métalliques tridimensionnels pour la réduction de dioxyde de carbone par du soufre gazeux |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2018148168A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112023909A (zh) * | 2020-09-10 | 2020-12-04 | 华东理工大学 | 快响应高热效率结构化电加热多孔碳基催化剂的制备方法 |
US20220314183A1 (en) * | 2018-09-21 | 2022-10-06 | California Institute Of Technology | 3d printing of metal containing structures |
CN116673017A (zh) * | 2023-04-25 | 2023-09-01 | 中南大学 | 一种分级多孔压电陶瓷催化剂及其制备方法和应用 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20050191233A1 (en) * | 2004-02-26 | 2005-09-01 | Weibin Jiang | Catalyst configuration and methods for syngas production |
US7256154B2 (en) * | 2003-10-25 | 2007-08-14 | Korea Institute Of Science And Technology | Structured catalyst for POX reforming of gasoline for fuel-cell powered vehicles applications and a method of preparing the same |
US8894842B2 (en) * | 2010-10-15 | 2014-11-25 | IFP Energies Nouvelles | Optimized catalyst for catalytic reforming |
US20160030927A1 (en) * | 2013-05-08 | 2016-02-04 | Korea Research Institute Of Chemical Technology | Monolith catalyst for carbon dioxide reforming reaction, preparation method for same, and preparation method for synthesis gas using same |
US20160107893A1 (en) * | 2014-10-17 | 2016-04-21 | Sabic Global Technologies B.V. | Carbon monoxide production from carbon dioxide reduction by elemental sulfur |
-
2018
- 2018-02-06 WO PCT/US2018/016962 patent/WO2018148168A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7256154B2 (en) * | 2003-10-25 | 2007-08-14 | Korea Institute Of Science And Technology | Structured catalyst for POX reforming of gasoline for fuel-cell powered vehicles applications and a method of preparing the same |
US20050191233A1 (en) * | 2004-02-26 | 2005-09-01 | Weibin Jiang | Catalyst configuration and methods for syngas production |
US8894842B2 (en) * | 2010-10-15 | 2014-11-25 | IFP Energies Nouvelles | Optimized catalyst for catalytic reforming |
US20160030927A1 (en) * | 2013-05-08 | 2016-02-04 | Korea Research Institute Of Chemical Technology | Monolith catalyst for carbon dioxide reforming reaction, preparation method for same, and preparation method for synthesis gas using same |
US20160107893A1 (en) * | 2014-10-17 | 2016-04-21 | Sabic Global Technologies B.V. | Carbon monoxide production from carbon dioxide reduction by elemental sulfur |
Non-Patent Citations (1)
Title |
---|
CLARK, P. D. ET AL.: "Mechanisms of CO and COS Formation in the Claus Furnace", INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, vol. 40, no. 2, 2001, pages 497 - 508, XP055397135 * |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20220314183A1 (en) * | 2018-09-21 | 2022-10-06 | California Institute Of Technology | 3d printing of metal containing structures |
CN112023909A (zh) * | 2020-09-10 | 2020-12-04 | 华东理工大学 | 快响应高热效率结构化电加热多孔碳基催化剂的制备方法 |
CN116673017A (zh) * | 2023-04-25 | 2023-09-01 | 中南大学 | 一种分级多孔压电陶瓷催化剂及其制备方法和应用 |
CN116673017B (zh) * | 2023-04-25 | 2024-02-13 | 中南大学 | 一种分级多孔压电陶瓷催化剂及其制备方法和应用 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
RU2732126C2 (ru) | Afx цеолит | |
US10843174B2 (en) | Catalyst manufacturing method | |
EP2613879B2 (fr) | Procédé de fabrication de catalyseur | |
Avila et al. | Monolithic reactors for environmental applications: A review on preparation technologies | |
KR101346465B1 (ko) | 수소-풍부 기체로부터 일산화탄소를 제거하기 위한, 백금,구리 및 철을 함유하는 개선된 선택적 산화 촉매 | |
US20100331571A1 (en) | Molding and method for producing the same, and catalyst and method for producing the same | |
JP2017537786A5 (fr) | ||
WO1991018832A1 (fr) | Catalyseurs monolithiques servant a la conversion de dioxyde de soufre en trioxyde de soufre | |
CN101585004A (zh) | 蜂窝结构体 | |
JPS61212331A (ja) | 集積高表面積相を有するモノリシツク触媒担体の調製 | |
WO2018148168A1 (fr) | Catalyseurs monolithiques céramiques et métalliques tridimensionnels pour la réduction de dioxyde de carbone par du soufre gazeux | |
JPH0259047A (ja) | 触媒活性を示す単一複合構造 | |
JPH0736895B2 (ja) | 気体流出物処理のための触媒及び上記流出物処理のための方法 | |
KR101700433B1 (ko) | 평판형 선택적촉매환원 촉매용 나노복합 이산화티타늄의 제조방법 | |
WO2008079051A1 (fr) | Catalyseur de synthèse fischer-tropsch et procédé de production associé | |
HUANG et al. | Preparation of honeycombed holmium-modified Fe-Mn/TiO2 catalyst and its performance in the low temperature selective catalytic reduction of NOx | |
JP7076241B2 (ja) | 酸化触媒の粉末、触媒担持構造体、酸化触媒の粉末の製造方法、および、触媒担持構造体の製造方法 | |
US7304013B2 (en) | Metal oxide catalysts | |
JP4296430B2 (ja) | 水性ガスシフト反応用の触媒及びその製造方法 | |
WO2007083779A1 (fr) | Catalyseur de purification de gaz d'échappement | |
RU2756660C1 (ru) | Каталитический элемент регулярной сотовой структуры для гетерогенных реакций | |
JP3945446B2 (ja) | セラミック担体とその製造方法 | |
RU2106908C1 (ru) | Катализатор для окисления аммиака до окислов азота | |
JP2012229142A (ja) | チタン酸アルミニウム質ハニカム構造体 | |
JP2003112048A (ja) | セラミック触媒体 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 18751667 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 18751667 Country of ref document: EP Kind code of ref document: A1 |