WO2018130200A1 - Composite de caoutchouc, procédé de mise en œuvre, composite d'application de produit à haute résistance et procédé de fabrication - Google Patents
Composite de caoutchouc, procédé de mise en œuvre, composite d'application de produit à haute résistance et procédé de fabrication Download PDFInfo
- Publication number
- WO2018130200A1 WO2018130200A1 PCT/CN2018/072379 CN2018072379W WO2018130200A1 WO 2018130200 A1 WO2018130200 A1 WO 2018130200A1 CN 2018072379 W CN2018072379 W CN 2018072379W WO 2018130200 A1 WO2018130200 A1 WO 2018130200A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- rubber
- parts
- vulcanization
- weight
- rubber composition
- Prior art date
Abstract
L'invention concerne un composite de caoutchouc. Le composite de caoutchouc comprend un substrat de caoutchouc et un système réticulable. Le substrat de caoutchouc comprend les constituants suivants, en parties en poids : polyéthylène ramifié, dont la teneur est a : 0 < a ≤ 100 parties, caoutchouc éthylène propylène monomère, dont la teneur est b : 0 ≤ b < 100 parties, caoutchouc éthylène propylène diène monomère, dont la teneur est c : 0 ≤ c ≤ 100 parties, et, le substrat de caoutchouc correspondant à 100 parties en poids, le système réticulable, dont la teneur est d : 1 ≤ d ≤ 15 parties. Le système réticulable comprend au moins un agent de réticulation et/ou un agent auxiliaire de réticulation, le degré de ramification du polyéthylène ramifié n'est pas inférieur à 50 chaînes ramifiées/1000 atomes de carbone, la masse moléculaire moyenne en masse n'est pas inférieure à 50 000, et la viscosité Mooney n'est pas inférieure à 2 ml(1+4) à 125 °C. Le composite de caoutchouc résout efficacement le problème dans l'état de la technique d'un faible rendement de réticulation et d'une faible résistance mécanique, et simultanément acquiert de grandes performances d'isolation électrique et une grande résistance mécanique.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US16/477,414 US20190330456A1 (en) | 2017-01-13 | 2018-01-12 | Rubber composite, processing method, high-strength product applying composite, and manufacturing method |
JP2019559148A JP7152033B2 (ja) | 2017-01-13 | 2018-01-12 | ゴム組成物および加工方法、並びにそれを用いた高強度製品および製造方法 |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201710025138.0 | 2017-01-13 | ||
CN201710025138 | 2017-01-13 | ||
CN201810020833.2A CN108299740B (zh) | 2017-01-13 | 2018-01-10 | 橡胶组合物及加工方法,及应用其的高强度制品和生产方法 |
CN201810020833.2 | 2018-01-10 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2018130200A1 true WO2018130200A1 (fr) | 2018-07-19 |
Family
ID=62839314
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2018/072379 WO2018130200A1 (fr) | 2017-01-13 | 2018-01-12 | Composite de caoutchouc, procédé de mise en œuvre, composite d'application de produit à haute résistance et procédé de fabrication |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2018130200A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN114106477A (zh) * | 2020-09-01 | 2022-03-01 | 中国石油化工股份有限公司 | 用于丁基橡胶封口塞的橡胶基体、组合物、硫化胶及其制备方法 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1780876A (zh) * | 2003-04-25 | 2006-05-31 | 美利肯公司 | 抗微生物树脂固化的橡胶制品和预硫化组合物 |
CN102086287A (zh) * | 2009-12-03 | 2011-06-08 | 江苏润德医用材料有限公司 | 热塑性弹性体材料及由其制作的胶塞 |
CN102617938A (zh) * | 2012-03-26 | 2012-08-01 | 兖矿集团有限公司 | 耐寒的电缆用乙丙绝缘材料 |
CN103980596A (zh) * | 2014-05-13 | 2014-08-13 | 浙江大学 | 一种聚乙烯橡胶及其加工方法 |
CN104877225A (zh) * | 2015-06-20 | 2015-09-02 | 浙江大学 | 一种气密层材料的制备方法及其原料配方 |
-
2018
- 2018-01-12 WO PCT/CN2018/072379 patent/WO2018130200A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1780876A (zh) * | 2003-04-25 | 2006-05-31 | 美利肯公司 | 抗微生物树脂固化的橡胶制品和预硫化组合物 |
CN102086287A (zh) * | 2009-12-03 | 2011-06-08 | 江苏润德医用材料有限公司 | 热塑性弹性体材料及由其制作的胶塞 |
CN102617938A (zh) * | 2012-03-26 | 2012-08-01 | 兖矿集团有限公司 | 耐寒的电缆用乙丙绝缘材料 |
CN103980596A (zh) * | 2014-05-13 | 2014-08-13 | 浙江大学 | 一种聚乙烯橡胶及其加工方法 |
CN104877225A (zh) * | 2015-06-20 | 2015-09-02 | 浙江大学 | 一种气密层材料的制备方法及其原料配方 |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN114106477A (zh) * | 2020-09-01 | 2022-03-01 | 中国石油化工股份有限公司 | 用于丁基橡胶封口塞的橡胶基体、组合物、硫化胶及其制备方法 |
CN114106477B (zh) * | 2020-09-01 | 2023-07-21 | 中国石油化工股份有限公司 | 用于丁基橡胶封口塞的橡胶基体、组合物、硫化胶及其制备方法 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP7118450B2 (ja) | ゴム組成物および加工方法、並びにそれを用いたゴムベルト、ゴムローラおよび製造方法 | |
WO2018130194A1 (fr) | Composite de caoutchouc, procédé de traitement, produits en caoutchouc mettant en application le composite, et procédé de fabrication | |
JP7250341B2 (ja) | ゴム組成物、それを用いた老化防止ゴム製品および製造方法 | |
WO2018130197A1 (fr) | Composite de caoutchouc, procédé de traitement, applications et procédé de fabrication de produits ignifuges | |
WO2018130195A1 (fr) | Composite de caoutchouc, procédé de traitement, applications, procédé de fabrication des applications | |
CN108314850B (zh) | 橡胶组合物及加工方法,及应用其的橡胶制品和生产方法 | |
WO2018130196A1 (fr) | Composite de caoutchouc, applications dans un produit mousseux, et procédé de fabrication | |
JP7152033B2 (ja) | ゴム組成物および加工方法、並びにそれを用いた高強度製品および製造方法 | |
JP7162903B2 (ja) | ゴム組成物及び加工方法、並びにそれを用いたブレーキ液耐性製品及び製造方法 | |
WO2018130199A1 (fr) | Composite de caoutchouc, procédé de traitement, tube de caoutchouc mettant en application un composite et procédé de fabrication | |
JP7156709B2 (ja) | 光架橋によるゴム組成物およびその応用、並びに該応用の製造方法 | |
JP7104426B2 (ja) | ゴム組成物及び加工方法、並びにそれを用いたコンベアベルト及び製造方法 | |
CN108299745B (zh) | 橡胶组合物及加工方法,及应用其的胶管和生产方法 | |
CN108314851B (zh) | 橡胶组合物及加工方法和应用,及该应用的生产方法 | |
JP7166639B2 (ja) | ゴム組成物、および発泡製品への応用と製造方法 | |
WO2018130188A1 (fr) | Composite de caoutchouc, procédé de traitement, courroie en caoutchouc et rouleau en caoutchouc utilisant le composite, et procédé de fabrication | |
WO2020011004A1 (fr) | Composition de caoutchouc polaire anti-vieillissement, procédé de traitement associé et application associée | |
WO2018130189A1 (fr) | Composite de caoutchouc, traitement, courroie transporteuse mettant en application un composite, et procédé de fabrication | |
WO2018130187A1 (fr) | Composite de caoutchouc, procédé de traitement, applications et procédé de fabrication de produits en caoutchouc à haute résistance | |
CN108299743B (zh) | 橡胶组合物及加工方法与应用,及生产阻燃制品的方法 | |
WO2018130198A1 (fr) | Composite de caoutchouc, procédé de traitement, composite d'application de produit liquide résistant au freinage et procédé de fabrication | |
WO2018130191A1 (fr) | Composite de caoutchouc à photoréticulation, applications et procédé de fabrication pour les applications | |
WO2018130186A1 (fr) | Composite de caoutchouc, procédé de traitement, élément d'étanchéité mettant en application un composite et procédé de fabrication | |
WO2018130192A1 (fr) | Composite de caoutchouc, produit de caoutchouc résistant au vieillissement utilisant ce composite, et procédé de fabrication | |
JP7084048B2 (ja) | ゴム組成物及び加工方法、並びに該ゴム組成物を用いたシール及び製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 18738448 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2019559148 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 18738448 Country of ref document: EP Kind code of ref document: A1 |