WO2018112939A1 - Antifreeze glass cleaning agent - Google Patents

Antifreeze glass cleaning agent Download PDF

Info

Publication number
WO2018112939A1
WO2018112939A1 PCT/CN2016/111849 CN2016111849W WO2018112939A1 WO 2018112939 A1 WO2018112939 A1 WO 2018112939A1 CN 2016111849 W CN2016111849 W CN 2016111849W WO 2018112939 A1 WO2018112939 A1 WO 2018112939A1
Authority
WO
WIPO (PCT)
Prior art keywords
parts
fiber
cleaning agent
sodium
loofah
Prior art date
Application number
PCT/CN2016/111849
Other languages
French (fr)
Chinese (zh)
Inventor
王华勤
Original Assignee
王华勤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 王华勤 filed Critical 王华勤
Priority to PCT/CN2016/111849 priority Critical patent/WO2018112939A1/en
Publication of WO2018112939A1 publication Critical patent/WO2018112939A1/en

Abstract

Provided is an antifreeze cleaning agent for automobile glass, comprising, per one hundred parts, 10-15 parts of sodium tripolyphosphate, 5-10 parts of sodium citrate, 5-10 parts of an alkyl ether phosphate, 5-10 parts of butoxyethanol, 0.5-2 parts of an antioxidant, 1-2 parts of an antifoaming agent and 5-10 parts of plant fibers, with the balance being deionized water, wherein the above parts are parts by mass. The cleaning agent can quickly clear various types of dirt outside of an automotive body, and has a good cleaning effect; and at the same time, can effectively prevent scratches from occurring on the surface of an automobile during cleaning, is environmentally friendly when used, and can accommodate the cold weather in the north; and does not corrode rubber components, such as a windshield wiper, during use. The plant fibers can effectively protect and prolong the service life of the windshield wiper.

Description

一种防冻玻璃清洗剂Antifreeze glass cleaner 技术领域Technical field
本发明属于清洗液技术领域，特别涉及一种用于汽车玻璃的防冻清洗剂。The invention belongs to the technical field of cleaning liquids, and particularly relates to an antifreeze cleaning agent for automobile glass.
背景技术Background technique
汽车清洁剂主要由表面活性剂、杀菌剂、抛光剂和参透剂等组成，某些汽车清洗剂还含有独特光亮因子等环保成分；通常具有强力的除污力以及渗透力、杀菌力和抛光光亮性等特性，能迅速彻洁汽车玻璃表面，挡板，车体等。Automotive cleaners are mainly composed of surfactants, bactericides, polishing agents and penetration agents. Some automotive cleaning agents also contain environmentally friendly ingredients such as unique brightening factors; usually have strong detergency and penetration, bactericidal power and polished light. Sex and other characteristics, can quickly clean the car glass surface, baffle, car body and so on.
汽车清洁剂能除去汽车玻璃表面粘贴的各种胶纸、标贴、并能除去车轮周围、挡泥板、保险杠、车体及各种工具上的油污。汽车清洁剂使用后还可形成薄膜以保护车漆。汽车内饰清洁剂就是清洁车内的化纤、木质、皮革、布艺、丝绒、工程朔料等制品。Car cleaners remove all kinds of adhesive tape, stickers, and grease from the car's glass surface, and remove oil from the wheels, fenders, bumpers, bodywork, and various tools. Car cleaners can also be formed into a film to protect the paint. Automotive interior cleaners are chemical fiber, wood, leather, fabric, velvet, engineered materials and other products in the car.
现在国内市场上销售的汽车风窗玻璃清洗液主要是甲醇型、乙醇型或乙醇型为主的汽车风窗玻璃清洗液，大多数市场销售的产品质量不高，包括洗洁精加水勾兑，没有任何添加剂的甲醇、乙醇加水勾兑。一般的洗洁精勾兑产品难以在温度较低的环境使用，容易形成冻结造成无法清洗车窗，尤其在北方的寒冷冬季更是如此。At present, the automobile windshield cleaning liquid sold in the domestic market is mainly a windshield glass cleaning liquid mainly composed of methanol type, ethanol type or ethanol type, and the quality of products sold in most markets is not high, including detergent blending with water, no Methanol and ethanol of any additive are blended with water. The general detergent blending product is difficult to use in a low temperature environment, and it is easy to form a freeze, which makes it impossible to clean the window, especially in the cold winter in the north.
发明内容Summary of the invention
本发明的目的在于克服现有技术的缺陷，设计一种适用于北方，能够自然防冻、不划伤汽车玻璃、不腐蚀雨刷器橡胶材料的新型汽车清洗剂。The object of the present invention is to overcome the defects of the prior art and design a new type of automobile cleaning agent which is suitable for the north, can naturally prevent freezing, does not scratch the automobile glass, and does not corrode the rubber material of the wiper.
为了实现上述目的，本发明涉及的防冻玻璃清洗剂，每百份中三聚磷酸钠10-15份、柠檬酸钠5-10份、烷基醚磷酸酯5-10份、丁氧基乙醇5-10份、抗氧化剂0.5-2份、消泡剂1-2份、植物纤维5-10份、余量为去离子水，上述份数为质量份数。In order to achieve the above object, the present invention relates to an antifreeze glass cleaning agent, 10-15 parts of sodium tripolyphosphate, 5-10 parts of sodium citrate, 5-10 parts of alkyl ether phosphate, butoxyethanol 5 per hundred parts. - 10 parts, 0.5-2 parts of antioxidant, 1-2 parts of antifoaming agent, 5-10 parts of vegetable fiber, the balance being deionized water, and the above parts are parts by mass.
优选的是，所述消泡剂为甘油三羟基聚醚或高碳醇；Preferably, the antifoaming agent is a trihydroxy polyether or a higher alcohol;
优选的是，所述抗氧化剂为亚硫酸钠、焦亚硫酸钠、二丁基苯酚或亚硫酸氢钠中得一种。Preferably, the antioxidant is one of sodium sulfite, sodium metabisulfite, dibutyl phenol or sodium hydrogen sulfite.
优选的是，所述植物纤维为木质纤维、丝瓜纤维、荷纤维、小麦纤维中的两种的组合物。Preferably, the plant fiber is a combination of two of wood fiber, loofah fiber, fiber, and wheat fiber.
优选的是，所述木质纤维的制备方法为，将原料木破碎成直径为0.05～0.15mm粗的丝状，向丝状原料中喷洒质量浓度为10％的氢氧化钠水溶液，喷洒均匀后烘干、粉磨至300～1200目。Preferably, the wood fiber is prepared by crushing the raw material wood into a filament having a diameter of 0.05 to 0.15 mm, spraying a sodium hydroxide aqueous solution having a mass concentration of 10% into the filamentous raw material, spraying uniformly and then baking. Dry and grind to 300 to 1200 mesh.
优选的是，所述丝瓜纤维的制备方法为，将成熟的丝瓜晒干后，除去果肉和种子部分，只保留丝瓜网，将丝瓜网粉碎之后烘干、粉磨至300～1200目。Preferably, the loofah fiber is prepared by drying the mature loofah, removing the pulp and the seed portion, leaving only the loofah net, pulverizing the loofah net, drying and grinding to 300-1200 mesh.
优选的是，所述荷纤维的制备方法为，将荷花杆烘干后破碎成直径为0.05～0.15mm粗的 丝状，向丝状原料中喷洒质量浓度为10％的氢氧化钠水溶液，喷洒均匀后二次烘干、粉磨至300～1200目。Preferably, the charged fiber is prepared by drying the lotus rod and breaking it into a diameter of 0.05 to 0.15 mm. Filamentous, spray a 10% aqueous solution of sodium hydroxide into the filamentous raw material, spray evenly, then dry and grind to 300-1200 mesh.
优选的是，所述小麦纤维的制备方法为，将小麦清洗干净后加工，取麸皮，麸皮烘干后粉磨至300～1200目。Preferably, the wheat fiber is prepared by washing the wheat and processing it, taking the bran, and drying the bran to 300-1200 mesh.
本发明涉及的防冻玻璃清洗剂，能够快速清除汽车车体外部的各种污物，清洗效果好；同时能够有效避免清洗过程中对汽车表面造成划痕，使用环境友好，能够适应北方的寒冷天气；使用过程中不会腐蚀雨刷器等橡胶部件，植物纤维能够有效保护及延长雨刷器的使用寿命。The anti-freeze glass cleaning agent of the invention can quickly remove various dirt on the exterior of the automobile body, and has good cleaning effect; at the same time, it can effectively avoid scratching the surface of the automobile during the cleaning process, and is environmentally friendly and can adapt to the cold weather in the north. The rubber parts such as the wiper are not corroded during use, and the plant fiber can effectively protect and extend the life of the wiper.
具体实施方式detailed description
下面通过具体实施例结合附图对本发明作进一步描述：The present invention will be further described below by way of specific embodiments with reference to the accompanying drawings:
实施例一Embodiment 1
本实施例的防冻玻璃清洗剂，每百份中三聚磷酸钠15份、柠檬酸钠10份、烷基醚磷酸酯10份、丁氧基乙醇10份、抗氧化剂2份、消泡剂2份、植物纤维10份、余量为去离子水，上述份数为质量份数。The antifreeze glass cleaning agent of the embodiment has 15 parts of sodium tripolyphosphate, 10 parts of sodium citrate, 10 parts of alkyl ether phosphate, 10 parts of butoxyethanol, 2 parts of antioxidant, and defoaming agent 2 per hundred parts. Parts, plant fibers 10 parts, the balance is deionized water, the above parts are parts by mass.
所述消泡剂为高碳醇；所述抗氧化剂为亚硫酸氢钠；所述植物纤维为木质纤维、丝瓜纤维的组合物。The antifoaming agent is a high carbon alcohol; the antioxidant is sodium hydrogen sulfite; and the plant fiber is a composition of wood fiber and loofah fiber.
所述木质纤维的制备方法为，将原料木破碎成直径为0.05～0.15mm粗的丝状，向丝状原料中喷洒质量浓度为10％的氢氧化钠水溶液，喷洒均匀后烘干、粉磨至300～1200目。The method for preparing the wood fiber comprises: breaking the raw material wood into a filament having a diameter of 0.05 to 0.15 mm, spraying a sodium hydroxide aqueous solution having a mass concentration of 10% into the filamentous raw material, spraying uniformly, drying, and grinding. Up to 300 to 1200 mesh.
所述丝瓜纤维的制备方法为，将成熟的丝瓜晒干后，除去果肉和种子部分，只保留丝瓜网，将丝瓜网粉碎之后烘干、粉磨至300～1200目。The loofah fiber is prepared by drying the mature loofah, removing the pulp and the seed part, leaving only the loofah net, pulverizing the loofah net, drying and grinding to 300-1200 mesh.
实施例二Embodiment 2
本实施例的防冻玻璃清洗剂，每百份中三聚磷酸钠10份、柠檬酸钠5份、烷基醚磷酸酯5份、丁氧基乙醇5份、抗氧化剂0.5份、消泡剂1份、植物纤维5份、余量为去离子水，上述份数为质量份数。The antifreeze glass cleaning agent of the embodiment has 10 parts of sodium tripolyphosphate, 5 parts of sodium citrate, 5 parts of alkyl ether phosphate, 5 parts of butoxyethanol, 0.5 parts of antioxidant, and defoaming agent 1 per hundred parts. Parts, 5 parts of plant fiber, the balance is deionized water, the above parts are parts by mass.
所述消泡剂为甘油三羟基聚醚；所述抗氧化剂为二丁基苯酚；所述植物纤维为荷纤维、小麦纤维中的组合物。The antifoaming agent is a trihydroxy polyether; the antioxidant is dibutyl phenol; and the plant fiber is a composition of a fiber and a wheat fiber.
所述荷纤维的制备方法为，将荷花杆烘干后破碎成直径为0.05～0.15mm粗的丝状，向丝状原料中喷洒质量浓度为10％的氢氧化钠水溶液，喷洒均匀后二次烘干、粉磨至300～1200目。 The method for preparing the charged fiber is that after the lotus rod is dried, it is broken into a filament having a diameter of 0.05 to 0.15 mm, and a sodium hydroxide aqueous solution having a mass concentration of 10% is sprayed into the filamentous raw material, and sprayed uniformly twice. Dry and grind to 300 to 1200 mesh.
所述小麦纤维的制备方法为，将小麦清洗干净后加工，取麸皮，麸皮烘干后粉磨至300～1200目。The wheat fiber is prepared by washing and cleaning the wheat, taking the bran, and drying the bran to 300-1200 mesh.
实施例三Embodiment 3
本实施例的防冻玻璃清洗剂，每百份中三聚磷酸钠11份、柠檬酸钠6份、烷基醚磷酸酯6份、丁氧基乙醇6份、抗氧化剂1份、消泡剂2份、植物纤维6份、余量为去离子水，上述份数为质量份数。The antifreeze glass cleaning agent of the present embodiment has 11 parts of sodium tripolyphosphate, 6 parts of sodium citrate, 6 parts of alkyl ether phosphate, 6 parts of butoxyethanol, 1 part of antioxidant, and defoaming agent 2 per hundred parts. Parts, 6 parts of plant fiber, the balance is deionized water, the above parts are parts by mass.
所述消泡剂为甘油三羟基聚醚；所述抗氧化剂为亚硫酸钠，所述植物纤维为木质纤维、小麦纤维中的组合物。The antifoaming agent is a trihydroxy polyether; the antioxidant is sodium sulfite, and the plant fiber is a composition of lignocellulose and wheat fiber.
所述木质纤维的制备方法为，将原料木破碎成直径为0.05～0.15mm粗的丝状，向丝状原料中喷洒质量浓度为10％的氢氧化钠水溶液，喷洒均匀后烘干、粉磨至300～1200目。The method for preparing the wood fiber comprises: breaking the raw material wood into a filament having a diameter of 0.05 to 0.15 mm, spraying a sodium hydroxide aqueous solution having a mass concentration of 10% into the filamentous raw material, spraying uniformly, drying, and grinding. Up to 300 to 1200 mesh.
所述小麦纤维的制备方法为，将小麦清洗干净后加工，取麸皮，麸皮烘干后粉磨至300～1200目。 The wheat fiber is prepared by washing and cleaning the wheat, taking the bran, and drying the bran to 300-1200 mesh.

Claims (5)

  1. 一种防冻玻璃清洗剂，其特征在于：每百份中三聚磷酸钠10-15份、柠檬酸钠5-10份、烷基醚磷酸酯5-10份、丁氧基乙醇5-10份、抗氧化剂0.5-2份、消泡剂1-2份、植物纤维5-10份、余量为去离子水，上述份数为质量份数，所述消泡剂为甘油三羟基聚醚或高碳醇；所述抗氧化剂为亚硫酸钠、焦亚硫酸钠、二丁基苯酚或亚硫酸氢钠中得一种；所述植物纤维为木质纤维、丝瓜纤维、荷纤维、小麦纤维中的两种的组合物。Antifreeze glass cleaning agent characterized by: 10-15 parts of sodium tripolyphosphate, 5-10 parts of sodium citrate, 5-10 parts of alkyl ether phosphate, 5-10 parts of butoxyethanol per hundred parts , antioxidants 0.5-2 parts, antifoaming agent 1-2 parts, plant fibers 5-10 parts, the balance is deionized water, the above parts are parts by mass, the antifoaming agent is glycerol trihydroxy polyether or a high carbon alcohol; the antioxidant is one of sodium sulfite, sodium metabisulfite, dibutyl phenol or sodium hydrogen sulfite; the plant fiber is a combination of two of wood fiber, loofah fiber, fiber, and wheat fiber. Things.
  2. 根据权利要求1所述的防冻玻璃清洗剂，其特征在于：所述木质纤维的制备方法为，将原料木破碎成直径为0.05～0.15mm粗的丝状，向丝状原料中喷洒质量浓度为10％的氢氧化钠水溶液，喷洒均匀后烘干、粉磨至300～1200目。The antifreeze glass cleaning agent according to claim 1, wherein the wood fiber is prepared by crushing the raw material wood into a filament having a diameter of 0.05 to 0.15 mm, and spraying the mass concentration into the filamentous material. 10% aqueous sodium hydroxide solution, sprayed evenly, dried and ground to 300-1200 mesh.
  3. 根据权利要求1所述的防冻玻璃清洗剂，其特征在于：所述丝瓜纤维的制备方法为，将成熟的丝瓜晒干后，除去果肉和种子部分，只保留丝瓜网，将丝瓜网粉碎之后烘干、粉磨至300～1200目。The antifreeze glass cleaning agent according to claim 1, wherein the loofah fiber is prepared by drying the mature loofah, removing the pulp and the seed portion, leaving only the loofah net, and pulverizing the loofah net and then baking. Dry and grind to 300 to 1200 mesh.
  4. 根据权利要求1所述的防冻玻璃清洗剂，其特征在于：所述荷纤维的制备方法为，将荷花杆烘干后破碎成直径为0.05～0.15mm粗的丝状，向丝状原料中喷洒质量浓度为10％的氢氧化钠水溶液，喷洒均匀后二次烘干、粉磨至300～1200目。The anti-freeze glass cleaning agent according to claim 1, wherein the charged fiber is prepared by drying the lotus rod and breaking into a filament having a diameter of 0.05 to 0.15 mm, and spraying the filamentous material. The aqueous solution of sodium hydroxide having a mass concentration of 10% is uniformly sprayed, then dried twice, and ground to 300 to 1200 mesh.
  5. 根据权利要求1所述的防冻玻璃清洗剂，其特征在于：所述小麦纤维的制备方法为，将小麦清洗干净后加工，取麸皮，麸皮烘干后粉磨至300～1200目。 The anti-freeze glass cleaning agent according to claim 1, wherein the wheat fiber is prepared by washing and cleaning the wheat, taking the bran, and drying the bran to 300 to 1200 mesh.
PCT/CN2016/111849 2016-12-23 2016-12-23 Antifreeze glass cleaning agent WO2018112939A1 (en)