WO2018108239A1 - Ltps layer qualification on display substrates by inline sem using a multi perspective detector and method for inspecting a large area substrate - Google Patents
Ltps layer qualification on display substrates by inline sem using a multi perspective detector and method for inspecting a large area substrate Download PDFInfo
- Publication number
- WO2018108239A1 WO2018108239A1 PCT/EP2016/080662 EP2016080662W WO2018108239A1 WO 2018108239 A1 WO2018108239 A1 WO 2018108239A1 EP 2016080662 W EP2016080662 W EP 2016080662W WO 2018108239 A1 WO2018108239 A1 WO 2018108239A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- charged particle
- particle beam
- images
- grain structure
- Prior art date
Links
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01J—ELECTRIC DISCHARGE TUBES OR DISCHARGE LAMPS
- H01J37/00—Discharge tubes with provision for introducing objects or material to be exposed to the discharge, e.g. for the purpose of examination or processing thereof
- H01J37/02—Details
- H01J37/22—Optical or photographic arrangements associated with the tube
- H01J37/222—Image processing arrangements associated with the tube
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01J—ELECTRIC DISCHARGE TUBES OR DISCHARGE LAMPS
- H01J37/00—Discharge tubes with provision for introducing objects or material to be exposed to the discharge, e.g. for the purpose of examination or processing thereof
- H01J37/26—Electron or ion microscopes; Electron or ion diffraction tubes
- H01J37/28—Electron or ion microscopes; Electron or ion diffraction tubes with scanning beams
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01J—ELECTRIC DISCHARGE TUBES OR DISCHARGE LAMPS
- H01J2237/00—Discharge tubes exposing object to beam, e.g. for analysis treatment, etching, imaging
- H01J2237/22—Treatment of data
- H01J2237/221—Image processing
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01J—ELECTRIC DISCHARGE TUBES OR DISCHARGE LAMPS
- H01J2237/00—Discharge tubes exposing object to beam, e.g. for analysis treatment, etching, imaging
- H01J2237/22—Treatment of data
- H01J2237/226—Image reconstruction
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01J—ELECTRIC DISCHARGE TUBES OR DISCHARGE LAMPS
- H01J2237/00—Discharge tubes exposing object to beam, e.g. for analysis treatment, etching, imaging
- H01J2237/244—Detection characterized by the detecting means
- H01J2237/2446—Position sensitive detectors
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01J—ELECTRIC DISCHARGE TUBES OR DISCHARGE LAMPS
- H01J2237/00—Discharge tubes exposing object to beam, e.g. for analysis treatment, etching, imaging
- H01J2237/26—Electron or ion microscopes
- H01J2237/2611—Stereoscopic measurements and/or imaging
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01J—ELECTRIC DISCHARGE TUBES OR DISCHARGE LAMPS
- H01J2237/00—Discharge tubes exposing object to beam, e.g. for analysis treatment, etching, imaging
- H01J2237/26—Electron or ion microscopes
- H01J2237/28—Scanning microscopes
- H01J2237/2809—Scanning microscopes characterised by the imaging problems involved
- H01J2237/2811—Large objects
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01J—ELECTRIC DISCHARGE TUBES OR DISCHARGE LAMPS
- H01J2237/00—Discharge tubes exposing object to beam, e.g. for analysis treatment, etching, imaging
- H01J2237/26—Electron or ion microscopes
- H01J2237/28—Scanning microscopes
- H01J2237/2813—Scanning microscopes characterised by the application
- H01J2237/2814—Measurement of surface topography
Definitions
- the present disclosure relates to LTPS layer qualification and a method for inspecting a substrate. More particularly, embodiments described herein relate to a method for inspecting substrates for display manufacturing, still more particularly a large area substrate for display manufacturing.
- a substrate e.g. on a glass substrate
- the substrates are coated in different chambers of a coating apparatus.
- the substrates are coated in a vacuum using a vapor deposition technique.
- electronic devices and particularly opto-electronic devices have reduced significantly in price.
- the pixel density in displays is continuously increased.
- TFT displays a high density TFT integration is desired.
- the yield is attempted to be increased and the manufacturing costs are attempted to be reduced in spite of the increased number of thin-film transistors (TFT) within a device.
- TFT thin-film transistors
- LTPS Low Temperature Poly Silicon
- the gate electrode can be used as a mask for doping of the contact area of the active layer to the source and the drain of the transistor.
- the quality of this self-aligned doping can determine the yield of the manufacturing process. Accordingly, it is a desire to improve and control this process.
- other self-aligned doping applications i.e. other than manufacturing of a LTPS-TFT, can benefit from an improved process.
- LTPS Low Temperature Poly Silicon
- the inspection of the substrate can, for example, be carried out by an optical system.
- the LTPS grain structure, grain sizes and topography of the grains at the grain edges are particularly difficult to review using optical systems, since the grain size may be below the optical resolution, making the grains invisible for the optical system.
- An inspection of small portions of substrates has also been carried out using charged particle beam devices, combined with surface etching.
- the surface etching may enhance the contrast of e.g. the grain boundaries but involves breaking the glass substrate, so that small pieces of the substrate are inspected instead of the substrate as a whole. Accordingly, it is impossible to continue processing the substrate, e.g. to check the impact of the grain structure on the final product, after inspection of the substrate.
- a method for inspecting a substrate includes providing the substrate being a large area substrate in a vacuum chamber, wherein the substrate has a thin-film with a grain structure deposited on the substrate; generating a primary charged particle beam with an imaging charged particle beam microscope, wherein the primary charged particle beam impinges on the substrate in the vacuum chamber; and generating one or more images from signal particles released from the substrate upon impingement of the primary charged particle beam, wherein the one or more images are topographic images.
- inventive methods described herein may be embodied in a computer readable medium
- the computer readable medium has instructions stored thereon that, when executed, cause a charged particle beam microscope to perform a method for inspecting a substrate accordance with any of the methods described herein.
- FIG. 1 shows a side view of an imaging charged particle beam microscope used for embodiments described herein;
- FIG.2 shows a detection arrangement including a segmented scintillator used for embodiments described herein;
- FIG. 3 A shows topographic images according to embodiments of the present disclosure
- FIG. 3B shows a combined image, which is combined of topographic images according to the present disclosure
- FIG. 4 shows an image of a prior art air SEM measurement, wherein am etched sample surface is measured
- FIG. 5 shows a flow chart illustrating a method according to embodiments described herein, particularly a method for inspecting a large area substrate
- FIG. 6 shows a flow chart illustrating further methods according to embodiments described herein, particularly methods for calibrating and inspecting a large area substrate, e.g. for display manufacturing.
- substrate as used herein embraces both inflexible substrates, e.g., a glass substrate, or a glass plate, and flexible substrates, such as a web or a foil.
- the substrate may be a coated substrate, wherein one or more thin layers of materials are coated or deposited on the substrate, for example by a physical vapor deposition (PVD) process or a chemical vapor deposition process (CVD).
- PVD physical vapor deposition
- CVD chemical vapor deposition
- Embodiments described herein relate to large area substrates, in particular large area substrates for the display market.
- large area substrates or respective substrate supports may have a size of at least 1 m 2 .
- the size may be from about 1.375 rri (1100 mm x 1250 mm- Gen 5) to about 9 m 2 , more specifically from about 2 m 2 to about 9 m 2 or even up to 12 m 2 .
- the substrates or substrate receiving areas, for which the structures, apparatuses, and methods according to embodiments described herein are provided, can be large area substrates as described herein.
- a large area substrate or carrier can be GEN 5, which corresponds to about 1.375 m 2 substrates (1.1 m x 1.25 m), GEN 7.5, which corresponds to about 4.39 m 2 substrates (1.95 m x 2.25 m), GEN 8.5, which corresponds to about 5.7m 2 substrates (2.2 m x 2.5 m), or even GEN 10, which corresponds to about 9 m 2 substrates (2.88 m x 3130 m). Even larger generations such as GEN 11 and GEN 12 and corresponding substrate areas can similarly be implemented. [0022] Without limiting the scope of protection of the present application, in the following the charged particle beam device, e.g.
- a charged particle beam microscope or components thereof will exemplarily be referred to as a charged particle beam device including the detection of secondary or backscattered particles, such as electrons.
- embodiments can still be applied for apparatuses and components detecting corpuscles, such as secondary and/or backscattered charged particles in the form of electrons or ions, photons, X-rays or other signals in order to obtain a specimen image.
- corpuscles the corpuscles are to be understood as light signals in which the corpuscles are photons as well as particles, in which the corpuscles are ions, atoms, electrons or other particles.
- discussions and descriptions relating to the detection are exemplarily described with respect to electrons in scanning electron microscopes.
- Other types of charged particles e.g. positive ions, could be utilized by the device in a variety of different instruments.
- a signal (charged particle) beam, or a signal (charged particle) beamlet is referred to as a beam of secondary and/or backscattered particles.
- the signal beam or secondary beam is generated by the impingement of the primary beam or primary beamlet on a specimen.
- a primary charged particle beam or a primary charged particle beamlet is generated by a particle beam source and is guided and deflected on a specimen to be inspected or imaged.
- Fig. 1 shows a charged particle beam device or a charged particle beam microscope 100.
- An electron beam (not shown) may be generated by the electron beam source 112.
- further beam shaping means like a suppressor, an extractor, and/or an anode may be provided.
- the beam may be aligned to a beam limiting aperture, which is dimensioned to shape the beam, i.e. blocks a portion of the beam.
- the electron beam source cab include a TFE emitter.
- the gun chamber may be evacuated to a pressure
- a condenser lens can be provided in a further vacuum chamber 120 of the column of the charged particle beam microscope 100 .
- the condenser lens can include a pole piece 122 and the coil 124.
- Further electron optical elements 126 can be provided in the further vacuum chamber.
- the further electron optical elements 126 can be selected from the group consisting of: a stigmator, correction elements for chromatic and/or spherical aberrations, and alignment deflectors for aligning the primary charged particle beam to an optical axis of the objective lens 140.
- the primary electron beam can be focused on the substrate 10 by the objective lens 140.
- the substrate 10 is positioned on a substrate position on the substrate support 150.
- signal electrons for example, secondary and/or backscattered electrons, and/or x-rays, are released from the substrate 10, which can be detected by a detector 139.
- a condenser lens 123 is provided.
- a two-stage deflection system (not shown) can be provided between the condenser lens and e.g. a beam limiting aperture, e.g. a beam shaping aperture, for alignment of the beam to the aperture.
- the objective lens 140 has a magnetic lens component having pole pieces 142 and 146, and having a coil 144. The objective lens focuses the primary electron beam on the substrate 10. Further, an upper electrode 152 and a lower electrode 154 form an electrostatic lens component of the objective lens 140.
- a scanning deflector assembly 170 can be provided.
- the scanning deflector assembly 170 can, for example, be a magnetic, but preferably an electrostatic scanning deflector assembly, which is configured for high pixel rates.
- the scanning deflector assembly 170 may be a single stage assembly, as shown in FIG. 1. Alternatively, also a two-stage or even a three-stage deflector assembly can be provided for scanning. Each stage is provided at a different position along the optical axis.
- the lower electrode 154 is connected to a voltage supply (not shown).
- the lower electrode being the deceleration electrode of the immersion lens component, i.e. a retarding field lens component, of the objective lens is typically at a potential to provide a landing energy of the charged particles on the substrate of 2 keV or below, e.g. 500 V or 1 keV.
- the substrate support 150 can according to some embodiments be set to ground potential.
- the lower electrode 154 can have a positive voltage of about 200 V to 1 kV, e.g. to generate landing energy of 200 eV to 1 keV.
- the deceleration of the primary charged particle beam can be provided in the vicinity of the substrate 10, for example in or behind the objective lens, or a combination thereof.
- a deceleration can be provided by the lower electrode 154, i.e. a retarding field lens, respectively.
- a deceleration can e.g. be provided by an electrostatic lens component of the objective lens.
- a retarding bias voltage can be applied to the substrate lOand/or the substrate support in order to provide a retarding field lens component according to embodiments described herein.
- the objective lens can be an electrostatic-magnetic compound lens having e.g. an axial gap or a radial gap, or the objective lens can be an electrostatic retarding field lens.
- the distance between the lower portion or edge of the objective lens, for example the lower electrode 154 and the substrate, or the substrate support can be 1 mm to 3 mm, such as 1 point 5 mm.
- the resolution is mainly delimited by the size of the substrate support for the large area substrates and vibrations and movements resulting from the size of the substrate support.
- An advantage of having a landing energy of 2keV or below, particularly a landing energy of 1 keV or below, is that the primary electron beam impinging onto the substrate generates a stronger signal compared to high-energy electron beams. Since layers, e.g. LTPS layers, deposited on the substrate are thin and since high-energy electrons penetrate deeply into the substrate, i.e. below the layer, only a few electrons may generate a detector signal that contains information about the deposited layer. In contrast, low-energy electrons, such as electrons having a landing energy of 2keV or below, penetrate into a shallow region of the substrate only and thus provide more information about the deposited layer. Accordingly, an improved image of e.g.
- embodiments described herein provide electron microscope images under vacuum condition on large area substrates, i.e. substrate having an area of 1 m 2 or larger. Providing electron microscope images under vacuum allows for having low landing energies of, for example, 2 keV or below such as 1 keV or below. [0033] For high resolution applications it is beneficial to provide a landing energy of e.g. 2 keV or below, such as 1 keV or below, and have a high charged particle beam energy in the column, for example a beam energy of 10 keV or above, such as 30 keV or above.
- Embodiments may include a deceleration before the substrate 10, e.g. within the objective lens and/or between the objective lens and the substrate lOof a factor of 5 or more, such as a factor of 10 or more.
- a low landing energy of 2 keV or below may also be provided without a deceleration, e.g. in the event the beam energy within the column is not above 2 keV.
- an electron microscope image of a thin film having grains is provided.
- a scanning electron microscope image of a portion of a thin film deposited on a large area substrate is provided.
- the image is provided under vacuum conditions allowing for low energy imaging, wherein the landing energy of an electron beam on the thin film is 2 keV or below, for example about 1 keV.
- ⁇ 7keV high-energy electron beam imaging
- embodiments of the present disclosure which refer to low energy imaging, provide a nondestructive imaging.
- an electron beam review can be provided during manufacturing of an optoelectronic device, for example a display manufactured on the large area substrate.
- the charged particle beam microscope 100 shown in fig. 1 includes a detector 139 in a detection vacuum area 130.
- the detector 139 which is also shown in fig. 2 includes a scintillator arrangement 136.
- the scintillator arrangement 136 has an opening 201, for example an opening in the center of the scintillator arrangement.
- the opening 201 serves for having the primary charged particle beam path through the detector 139.
- the scintillator arrangement 136 is segmented to have two or more scintillator segments 236. According to some embodiments, which can be combined with other embodiments described herein, for scintillator segments can be provided, i.e. a Quad- detector is provided.
- the four segments allow for topographic images of the substrate plane in 2 dimensions x and y. Respective images are shown in FIGS. 3 A.
- a light guide 134 is connected to each of the scintillator segments 236. Further, a photo multiplier or another signal detection element 132 can be provided for each of the light guides. Accordingly, some embodiments, which can be combined with other embodiments described herein include an Everhart-Thornley detector arrangement as a detector 139. Some embodiments may also utilize an avalanche photodiode as a signal detection element or a microchannel plate.
- the scintillation arrangement can be manufactured from a low noise scintillator with a lower bandwidth, which results in a better signal-to-noise ratio, which may further be enhanced by averaging over segments of the scintillator arrangement 136.
- the scintillator may have a decay time of 50 ns to 100 ns, e.g. about 60 ns.
- Measurements according to embodiments of the present disclosure may have a pixel rate of 3 MHz to 10 MHz, such as about 5 MHz.
- the primary charged particle beam can be tilted to impinge on the substrate under a predetermined tilted beam landing angle.
- a tilted primary charged particle beam can have a tilt angle (relative to a normal on the substrate), i.e. an angle of incidence larger than 5° such as for example 10° to 20°, such as about 15°.
- a non-tilted primary charged particle beam can have an angle of incident smaller than 3°.
- an imaging charged particle beam microscope as described herein may be utilized for imaging with one or more tilted beams. Accordingly, 3D imaging, imaging of steps, and imaging of other height structures can be improved.
- a beam tilt with a tilt angle can be generated by a pre- lens deflection unit, which may include two deflection coils to deflect the beam away from the optical axis.
- the pre-lens deflection unit can be arranged between the charged particle source and the objective lens.
- An in-lens deflection unit can be provided inside the field of the objective lens such that the respective fields overlap.
- the in-lens deflection unit can be a two- stage unit comprising two deflection coils.
- the in-lens deflection unit can redirect the beam so that the beam crosses the center of the objective lens, i.e. the center of the focusing action, at the optical axis.
- the redirection is such that the charged particle beam hits the surface of the substrate from a direction, which is substantially opposite to the direction without the beam crossing the optical axis.
- the combined action of the in-lens deflection unit and the objective lens directs the primary charged particle beam back to the optical axis such that the primary charged particle beam hits the sample under the predetermined tilted beam landing angle.
- a beam tilt can be generated by a deflection unit that includes two deflectors to deflect the beam away from the optical axis. In light of the two stages, the beam can be deflected to seemingly emerge from a point coincident with the apparent position of the charged particle beam source.
- the pre-lens deflection unit can be arranged between the charged particle source and the objective lens.
- a Wien filter can be disposed which generates crossed electric and magnetic fields. The off-axis path of the charged particle beam trough the objective lens causes a first chromatic aberration.
- the energy dispersive effect of the Wien filter introduces a second chromatic aberration of the same kind as the first chromatic aberration.
- the second chromatic aberration can be adjusted to have the same magnitude but opposite direction as the first chromatic aberration.
- the second chromatic aberration substantially compensates the first chromatic aberration in the plane of the substrate surface.
- the primary charged particle beam is tilted by travelling off-axis through the objective lens and the focusing action of the objective lens.
- a beam tilt may also be introduced by mechanically tilting the column, i.e. the optical axis with respect substrate. Tilting the charged particle beam by providing a tilted beam path within the column provides for faster switching between beam angles and reduces the introduction of vibration as compared to a mechanical movement.
- an apparatus for inspecting a substrate particularly a substrate for display manufacturing.
- the apparatus includes a vacuum chamber as described herein.
- the apparatus further includes a substrate support arranged in the vacuum chamber, as described herein.
- the apparatus further includes a first imaging charged particle beam microscope and optionally a second imaging charged particle beam microscope, as described herein.
- the second imaging charged particle beam microscope is distanced from the first imaging charged particle beam microscope by a distance of at least 5 cm to 60 cm, such as about 25 cm to 35 cm.
- the images shown in FGS. 3 A are images of 4 segments of a detector 139 of the grain structure of low temperature polysilicon.
- the techniques for manufacturing TFT on the glass substrate include the amorphous silicon (a-Si) process and the low temp polysilicon (LTPS) process.
- the major differences between the a-Si process and the LTPS process are the electrical characteristics of the devices and the complexity of the processes.
- the LTPS TFT possesses higher mobility but the process for fabricating the LTPS TFT is more complicated.
- the a-Si TFT possesses lower mobility, the process for fabricating the a-Si TFT is simple. According to embodiments described herein, the LTPS TFT process can be improved and control of the process is beneficial.
- the LTPS TFT process is one example for which embodiments described herein can be beneficially utilized.
- a deposited layer is locally melted due to laser radiation.
- the laser radiation can be provided in a width of about 60 cm.
- a distance between charged particle beam microscopes of about 30 cm may be sufficient to provide an analysis of the process in this region.
- a method for inspecting a substrate includes generating of the primary charged particle beam within the vacuum chamber and generating one or more images from signal particles, wherein the one or more images are topographic images.
- FIG. 3A for example for topographic images can be provided by imaging a portion of a thin film having a grain structure with a segmented detector, for example a Quad detector having four segments.
- the topographic images of FIGS. 3 A can be combined to a combined-perspective secondary electron image shown in FIG. 3B.
- the images described herein may be compared with optical images having two or more, e.g. four, illumination angles of a light source, wherein from the shadows of the illumination angles values of the imaged grains structure can be obtained. This is different as compared to measurements with a tilted beam, which would correspond to a stereoscopic optical image.
- FIG. 3B an algorithm has been provided to highlight the boundaries of the grains of the LTPS thin film.
- the topographic images shown in FIGS. 3 A or the combined image shown in FIG. 3B can be used to qualify LTPS layers, for example in the display industry, or other layers of the thin-film with a grain structure.
- the electron beam reviewed according to methods as described herein is capable to image the thin films having the grain structure, for example LTPS layers with multiple perspective. Improved topographical information can be provided. This allows for more precise evaluation of the grain structure.
- FIG. 4 shows an image of a destructive measurement, wherein an LTPS layer has been etched and imaged with in high energy electron beam.
- the great of lines 42 can be provided on the image surface and peaks corresponding to dots 44 can be identified.
- the one or more images shown in FIGS. 3 A or the combined image shown in FIG. 3B provides improved topographical information and make, thus, be utilized for better evaluation of the grain structure.
- the images obtained as shown in FIGS. 3 A and FIG. 3B are nondestructive. Accordingly, a thin film imaged as shown in FIGS. 3 A and FIG. 3B or a corresponding substrate can be further processed according to embodiments described herein.
- a grain structure can be described by the size of the grains, the shape of the grains, the distribution of the grains, the area of the grains, and the like. These parameters can be evaluated with statistical analysis methods with respect to one or more of the parameters. For example, a characteristic of grains of the grain structure can be determined as an arithmetic mean value, as a quadratic mean value, as a weighted mean value, and/or as a median value.
- the topographical information can be used by an software algorithm, e.g. to detect and analyze the grain structure, for example in LTPS grain structure.
- a calculation of grain structure characteristics may also include a watershed algorithm.
- a calculation based upon one or more images, i.e. topographic images or a combined image of topographic images, can provide at least one characteristic of grains of the grain structure selected from: an area of grains of the grain structure, a circumference of grains of the grain structure, a minimum size of grains of the grain structure, maximum size of grains of the grain structure, a size of grains of the grain structure along a predetermined direction, and the height of peaks of a boundary of grains of the grain structure.
- a two or more channel detector such as a four channel detector is used to image LTPS topography from two or more, e.g. four different perspectives respectively quasi illumination sources in a top down SEM image.
- These two or more, e.g. four perspectives give surface information to detect and evaluate the size, uniformity, local distribution and all statistics for the parameters describing the thin film with the grain structure, i.e. an LTPS layer.
- characteristics of the grain structure and/or statistics of the parameters of the grain structure can be used to verify process parameters of a manufacturing method of the deposited thin film.
- a feedback to the manufacturing process of the thin film having the grain structure can be provided.
- an LTPS TFT process can be controlled by electron beam review (EBR) according to embodiments described herein.
- the area of grains in the grain structure, the circumference of grains in the grain structure, one or more sizes grains in the grain structure can be measured.
- the grains having a size of about 100 nm to 500 nm can be measured.
- the field of view which can be measured by scanning the primary electron beam over the substrate, can have a size of up to 10 ⁇ .
- the grains are typically surrounded by a boundary having peaks, which may have a height of 50 nm or below.
- normal operation of the charged particle beam microscope is with a non-tilted beam, i.e. a beam with an incident angle on the substrate of 3° or below.
- the height of the peaks can be determined by the length of the shadow in one or more of the topographic images.
- the length of the shadow can be calibrated to a measured height of the peaks.
- the primary charged particle beam can be tilted to an angle of 5° or larger, for example to about 15°.
- a height of the height profile i.e.
- a boundary of the grain can be measured with a tilted beam image or with two or more tilted beam images.
- the tilted beam image or the two or more tilted beam images can be obtained on a thin film with a grain structure, for example an LTPS layer, or on a substrate with artificial calibrating features.
- the height of the boundary of the grain structure or the artificial calibrating feature can be measured in absolute values.
- topographic images can be measured and the lengths of a shadow can be calibrated to the previously measured height.
- the apparatus for inspecting large area substrates for display manufacturing can be an in-line apparatus, i.e. the apparatus, potentially including a load lock for loading and unloading the substrate in the vacuum chamber for imaging with the imaging charged particle beam microscope, e.g. an SEM, can be provided in line with another, previous testing or processing procedure and in line with a yet further, subsequent testing or processing procedure. Due to the low energies of the charged particle beam of 2 keV or below on the substrate for imaging, the structures provided on the substrate are not destroyed. Accordingly, the substrate can be provided for further processing in the display manufacturing fab. As understood herein, the number of substrates to be tested can be 10% to 100% of the entire amount of substrates in the fab for display manufacturing. Accordingly, even though the apparatus for inspecting and including a imaging charged particle beam microscope can be provided as an in-line tool without necessarily testing 100% of the substrates in the production line.
- the imaging charged particle beam microscope e.g. an SEM
- the vacuum chamber may include one or more valves, which may connect the vacuum chamber to another chamber, in particular if the apparatus is an inline apparatus. After a substrate has been guided into the vacuum chamber, the one or more valves can be closed. Accordingly, the atmosphere in the vacuum chamber can be controlled by generating a technical vacuum, for example, with one or more vacuum pumps.
- An advantage of inspecting a substrate in a vacuum chamber, compared to e.g. atmospheric pressure, is that the vacuum conditions facilitate using a low-energy charged particle beam for inspecting the substrate.
- low-energy charged particle beams can have a landing energy of 2 keV or below, particularly of 1 keV or below, such as 100 eV to 800 eV. Compared to high-energy beams, low energy beams do not penetrate deeply in the substrate and may therefore provide superior information about e.g. coated layers on the substrate.
- Fig. 5 shows a flowchart illustrating methods of inspecting a substrate, for example for display manufacturing.
- a large area substrate is provided in the vacuum chamber, wherein the large area substrate has thin-film with a grain structure deposited on the substrate.
- the substrate can be measured as part of a regular manufacturing process, i.e. no sample preparation like etching is required. Further, measurement steps illustrated below are non-destructive and the substrate can be further processed after the electron beam review.
- a primary charged particle beam is generated as indicated by block 504 and impinges on the thin film on the large area substrate under vacuum conditions. The vacuum conditions allow for low energy landing energies on the substrate.
- Block 506 in fig. 5 refers to generation of one or more topographic images.
- topographic images are generated with non-tilted beam.
- a non-tilted beam is beneficial for ease of control of the electron beam microscope and, thus, throughput.
- Topographic images can be provided by a segmented detector, such that for a non-tilted beam for viewing angles can be obtained with one measurement.
- the topographic images can be used for determining one or more characteristics or parameters of the grain structure, for example grains in an LTPS layer.
- Fig. 6 shows a flowchart illustrating yet a further method of inspecting a substrate.
- the primary charged particle beam can be tilted to an angle of incidence of 5° or above, such as 10° to 20°. This is indicated in block 602.
- one or more images of an area with a tilted beam are generated.
- the height of a structure or feature is measured as indicated by block 606.
- the same area and/or at the same structure a feature is measured with a non-tilted beam in block 608, wherein one or more topographic images, e.g. test images, are generated.
- the height measured in absolute values as indicated by block 606 is calibrated to a length of a shadow of the image measured in block 608.
- a test image is measured with a non-tilted beam such that the length of the shadow can be calibrated to the measured heights in absolute values.
- This calibration is indicated by block 610.
- the calibration is used to measure the height of a peak of the grain boundary of the grain structure with the calibration and based upon a shadow length. According to embodiments described herein, the process indicated by block 612 can be repeated a plurality of times based on the calibration generated by block 602 to 610. Accordingly, the calibration can be provided once or on a regular basis at a predetermined time interval.
- a measurement during review of substrates in the manufacturing process can be conducted with a non-tilted beam.
- the calibration can be used to determine the height of boundaries of the grain structure based upon the previously done calibration. This is beneficial for increasing the measurements speed and, thus, the throughput.
- the calibration needs to be conducted a single time, and may be checked for example once a week, or even once a month, or on even longer timescales, wherein measurements are conducted all the time.
Landscapes
- Chemical & Material Sciences (AREA)
- Analytical Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Computer Vision & Pattern Recognition (AREA)
- Analysing Materials By The Use Of Radiation (AREA)
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020197011597A KR102260984B1 (ko) | 2016-12-12 | 2016-12-12 | 기판을 검사하기 위한 방법 및 명령들이 저장된 컴퓨터 판독가능 매체 |
PCT/EP2016/080662 WO2018108239A1 (en) | 2016-12-12 | 2016-12-12 | Ltps layer qualification on display substrates by inline sem using a multi perspective detector and method for inspecting a large area substrate |
CN201680090320.8A CN109863573B (zh) | 2016-12-12 | 2016-12-12 | 检查基板的方法和具有指令存储于其上的计算机可读介质 |
TW106143405A TWI734875B (zh) | 2016-12-12 | 2017-12-11 | 檢查基板的方法和具有複數個指令儲存於其上的電腦可讀取媒體 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/EP2016/080662 WO2018108239A1 (en) | 2016-12-12 | 2016-12-12 | Ltps layer qualification on display substrates by inline sem using a multi perspective detector and method for inspecting a large area substrate |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2018108239A1 true WO2018108239A1 (en) | 2018-06-21 |
Family
ID=57588995
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2016/080662 WO2018108239A1 (en) | 2016-12-12 | 2016-12-12 | Ltps layer qualification on display substrates by inline sem using a multi perspective detector and method for inspecting a large area substrate |
Country Status (4)
Country | Link |
---|---|
KR (1) | KR102260984B1 (zh) |
CN (1) | CN109863573B (zh) |
TW (1) | TWI734875B (zh) |
WO (1) | WO2018108239A1 (zh) |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2020011580A1 (en) * | 2018-07-13 | 2020-01-16 | Asml Netherlands B.V. | Sem image enhancement methods and systems |
WO2023155078A1 (en) * | 2022-02-16 | 2023-08-24 | Applied Materials, Inc. | Method of in-line inspection of a substrate, scanning electron microscope, and computer-readable medium |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5993938A (en) * | 1996-04-19 | 1999-11-30 | Toray Industries, Inc. | Aromatic polyamide film, method of manufacturing the same and magnetic recording medium using the same film |
US20080283747A1 (en) * | 2007-05-14 | 2008-11-20 | Hitachi High-Technologies Corporation | Scanning Electron Microscope and Three-Dimensional Shape Measuring Device That Used It |
US20080294236A1 (en) * | 2007-05-23 | 2008-11-27 | Boston Scientific Scimed, Inc. | Endoprosthesis with Select Ceramic and Polymer Coatings |
US20140092230A1 (en) * | 2012-09-28 | 2014-04-03 | Carl Zeiss Microscopy Gmbh | Method for avoiding artefacts during serial block face imaging |
WO2016101978A1 (en) * | 2014-12-22 | 2016-06-30 | Applied Materials, Inc. | Apparatus for inspecting a substrate, method for inspecting a substrate, large area substrate inspection apparatus and method of operating thereof |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2007067296A2 (en) * | 2005-12-02 | 2007-06-14 | Alis Corporation | Ion sources, systems and methods |
US7981150B2 (en) * | 2006-11-09 | 2011-07-19 | Boston Scientific Scimed, Inc. | Endoprosthesis with coatings |
TWI449898B (zh) * | 2007-02-28 | 2014-08-21 | 尼康股份有限公司 | Observation device, inspection device and inspection method |
JP5444053B2 (ja) * | 2010-03-15 | 2014-03-19 | 株式会社日立ハイテクノロジーズ | 多結晶シリコン薄膜検査方法及びその装置 |
JP6084888B2 (ja) * | 2013-04-17 | 2017-02-22 | 株式会社アドバンテスト | 欠陥検査装置及び欠陥検査方法 |
KR20160024542A (ko) * | 2014-08-26 | 2016-03-07 | 현대제철 주식회사 | 강재의 탄화물 분석방법 |
-
2016
- 2016-12-12 CN CN201680090320.8A patent/CN109863573B/zh active Active
- 2016-12-12 WO PCT/EP2016/080662 patent/WO2018108239A1/en active Application Filing
- 2016-12-12 KR KR1020197011597A patent/KR102260984B1/ko active IP Right Grant
-
2017
- 2017-12-11 TW TW106143405A patent/TWI734875B/zh active
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5993938A (en) * | 1996-04-19 | 1999-11-30 | Toray Industries, Inc. | Aromatic polyamide film, method of manufacturing the same and magnetic recording medium using the same film |
US20080283747A1 (en) * | 2007-05-14 | 2008-11-20 | Hitachi High-Technologies Corporation | Scanning Electron Microscope and Three-Dimensional Shape Measuring Device That Used It |
US20080294236A1 (en) * | 2007-05-23 | 2008-11-27 | Boston Scientific Scimed, Inc. | Endoprosthesis with Select Ceramic and Polymer Coatings |
US20140092230A1 (en) * | 2012-09-28 | 2014-04-03 | Carl Zeiss Microscopy Gmbh | Method for avoiding artefacts during serial block face imaging |
WO2016101978A1 (en) * | 2014-12-22 | 2016-06-30 | Applied Materials, Inc. | Apparatus for inspecting a substrate, method for inspecting a substrate, large area substrate inspection apparatus and method of operating thereof |
Also Published As
Publication number | Publication date |
---|---|
KR102260984B1 (ko) | 2021-06-03 |
KR20190052121A (ko) | 2019-05-15 |
CN109863573B (zh) | 2021-10-15 |
CN109863573A (zh) | 2019-06-07 |
TW201837865A (zh) | 2018-10-16 |
TWI734875B (zh) | 2021-08-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US9966227B2 (en) | Specimen observation method and device using secondary emission electron and mirror electron detection | |
JP6255047B2 (ja) | 異物付着防止機能を備えた電子線検査装置及び方法 | |
TWI691717B (zh) | 用以檢查一樣本之方法及設備 | |
US10249472B2 (en) | Charged particle beam device, charged particle beam influencing device, and method of operating a charged particle beam device | |
WO2016101978A1 (en) | Apparatus for inspecting a substrate, method for inspecting a substrate, large area substrate inspection apparatus and method of operating thereof | |
US10345250B2 (en) | Method of inspecting a sample with a charged particle beam device, and charged particle beam device | |
JP2021119565A (ja) | ディスプレイ製造用基板上での自動限界寸法測定方法、ディスプレイ製造用大面積基板の検査方法、ディスプレイ製造用大面積基板の検査装置及びその操作方法 | |
US7282711B2 (en) | Multiple electron beam device | |
TWI734875B (zh) | 檢查基板的方法和具有複數個指令儲存於其上的電腦可讀取媒體 | |
WO2023155078A1 (en) | Method of in-line inspection of a substrate, scanning electron microscope, and computer-readable medium |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 16815784 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 20197011597 Country of ref document: KR Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 16815784 Country of ref document: EP Kind code of ref document: A1 |