WO2018079498A1 - 高周波で用いる扁平粉末および磁性シート - Google Patents
高周波で用いる扁平粉末および磁性シート Download PDFInfo
- Publication number
- WO2018079498A1 WO2018079498A1 PCT/JP2017/038218 JP2017038218W WO2018079498A1 WO 2018079498 A1 WO2018079498 A1 WO 2018079498A1 JP 2017038218 W JP2017038218 W JP 2017038218W WO 2018079498 A1 WO2018079498 A1 WO 2018079498A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- less
- flat powder
- saturation magnetization
- magnetic
- magnetic sheet
- Prior art date
Abstract
質量%で、C:1.5~3.0%、Cr:10~20%、N:0.03~0.30%を含み、残部Feおよび不可避的不純物からなり、平均粒径が200μm以下、平均厚さが5μm以下、平均アスペクト比が5以上、飽和磁化が1.0T超、tanδが0.1となる周波数(FR)が200MHz以上である、高周波で用いる扁平粉末が提供される。この扁平粉末によれば、従来にない、1.0Tを超える飽和磁化を有し、かつ、200MHz以上の高いFRを兼備する金属磁性扁平粉末およびこれを用いた磁性シートが提供される。
Description
本発明は、各種の電子デバイスなどに用いられる、高周波においても優れた磁気特性を有する扁平粉末および磁性シートに関する。
従来、スマートフォン、携帯電話、ノート型パーソナルコンピューター、タブレット型パーソナルコンピューターなど、各種の電子機器が普及し、その小型化による電磁干渉が問題となっている。また、通信の高速化による高周波化が進むことによって、より高周波で優れた磁気特性を示す磁性シートの要求が高まっている。このような電子機器に用いられる磁性シートとして、特開2012-009797号公報(特許文献1)に、1GHz以上の高周波数帯域で電磁波吸収周波数を任意に調整でき、かつ薄肉で、優れた電磁波吸収性を得ることができる軟磁性樹脂組成物および電磁波吸収体が提案されている。
また、特開2007-266031号公報(特許文献2)に、RFID(Radio Frequency Identification)技術を用いた非接触ICタグ等に好適に用いられるアンテナ用磁芯部材が提案されている。また、特開2011-22661号公報(特許文献3)に、デジタイザ用シートに関して、電磁誘導式デジタイザの位置検出性能を向上させる技術が提案されている。さらには、特開2016-39222号公報(特許文献4)に、インダクタ用部材として、磁芯とコイルを備えたインダクタおよびその製造方法が提案されている。これらに、Fe-Si-Al合金やFe-Si-Cr合金などの軟磁性扁平粉末を、ゴムや樹脂と混練し、シート状にしたものが広く用いられている。
このような磁性シートにおいて、要求される磁気特性は、高い飽和磁化の他に、実透磁率(μ’)と虚透磁率(μ”)があり、μ”は低周波ではほとんど検出されず、特定の周波数を超えると急激に増加する。そのため、μ”が急激に増加する周波数が高いほど高周波まで対応できることになり、とくに高周波で用いる場合は、μ’とμ”の比であるtanδ(μ”/μ’)が、より高い周波数まで低く維持されることが重要となる。ここで、tanδが0.1となる周波数を、以下、「FR」とする。
上述したような特許文献では、Fe-Si-Al合金の扁平粉末は飽和磁化が1.0Tであり、FR(周波数)は20MHz以下程度である。また、一般的にFe-Si-Cr合金の扁平粉末は飽和磁化が1.2T程度と高いもののFRは50MHz以下程度である。このように、従来の扁平粉末においては、FR(周波数)が200MHzを超えるような高周波帯域に対応できるものはなく、また、1.0Tを超える飽和磁化を兼備するものもないのが実情であった。
したがって、本発明の目的は、従来にない、1.0Tを超える飽和磁化を有し、かつ、200MHz以上の高いFRを兼備する金属磁性扁平粉末およびこれを用いた磁性シートを提供することにある。
本発明の一態様によれば、質量%で、C:1.5~3.0%、Cr:10~20%、N:0.03~0.30%を含み、残部Feおよび不可避的不純物からなり、平均粒径が200μm以下、平均厚さが5μm以下、平均アスペクト比が5以上、飽和磁化が1.0T超、tanδが0.1となる周波数(FR)が200MHz以上である、高周波で用いる扁平粉末が提供される。
本発明の他の一態様によれば、前記扁平粉末を含有する、磁性シートが提供される。
扁平粉末
以下、成分組成の限定理由について説明する。なお、この説明において、組成の成分量は質量%での値である。
以下、成分組成の限定理由について説明する。なお、この説明において、組成の成分量は質量%での値である。
本発明の扁平粉末において、C:1.5~3.0%とする。Cは、FRを上昇させるための必須元素である。Cを多く含むFe基合金を粉砕、扁平加工すると、Cおよび転位を多量に含有するマルテンサイト相が誘起され、この相を多く含む粉末のFRが極めて高いことを見出した。1.5%未満ではFRが低く、3.0%を超えると飽和磁化が低下する。C量は、好ましくは1.8%を超え2.7%未満、より好ましくは2.0%を超え2.4%未満である。
本発明の扁平粉末は、Cr:10~20%である。Crは、マルテンサイト変態開始温度(以下、Ms点と示す)を低下し、原料粉末に残留オーステナイト相を生成させるための必須元素である。本発明のような高濃度のCを含むFe合金のマルテンサイト相は、著しく高硬度であるため、扁平化処理の際に、原料粉末の延性が乏しく、扁平状に加工されずに、粉砕のみされてしまう。したがって、原料粉末に比較的軟質な残留オーステナイト相を生成し、より高いアスペクト比の扁平粉末を得るためにCrは必須である。また、Crは耐食性改善およびNの固溶量増大にも大きく寄与する重要な元素である。しかし、10%未満では扁平加工の際に高いアスペクト比が得られず、20%を超えると飽和磁化が低下する。Cr量は、好ましくは12%を超え19%未満、より好ましくは16%を超え18%未満である。
本発明の扁平粉末は、N:0.03~0.30%である。Nは、Crと同様に、原料粉末に残留オーステナイト相を生成させるための必須元素であり、特にCrよりも飽和磁化の低下が小さく抑えられつつ、この効果が得られるため、重要な元素である。さらに、Cと同様にFRを上昇させる効果も著しく高い。しかし、0.03%未満ではこれら効果が得られず、0.30%を超えると飽和磁化が低下する。好ましくは0.04%を超え0.20%未満、より好ましくは0.05%を超え0.15%未満である。
本発明の扁平粉末は、その平均粒径が200μm以下、平均厚さが5μm以下、平均アスペクト比が5以上である。磁性シートのμ’は、これに用いる扁平粉末のアスペクト比(扁平粉末の長手方向の長さ/扁平粉末の厚さ)が大きいほど高くなることが一般に知られている。したがって、平均粒径が大きく、厚さが小さいものが良い。しかしながら、平均粒径が大きいと磁性シートの表面の滑らかさが劣化する傾向がある。この観点から、200μmを超える場合、磁性シートの表面の凹凸が顕著であり、平均粒径は、好ましくは70μm未満、より好ましくは25μm未満である。一方、扁平粉末の平均厚さが5μmを超える場合、アスペクト比が小さくなりμ’が劣化する。平均厚さは、好ましくは3μm未満、より好ましくは1μm未満である。また、平均アスペクト比が5未満ではμ’が低くなる。平均アスペクト比は、好ましくは10を超え、より好ましくは20を超える。
本発明の扁平粉末は、その飽和磁化が1.0T超である。磁性シートの薄肉化および直流重畳特性の観点から、1.0Tを超える高い飽和磁化が必要である。高い飽和磁化は、印加される外部磁場に対し、磁性シートが許容できる最大の磁束密度が高くなるため、磁性シートを薄くできたり、いわゆる直流重畳特性を改善できるなどのメリットがある。飽和磁化は、好ましくは1.10Tを超え、より好ましくは1.25Tを超えるものである。また、他の磁気特性として、扁平粉末の長手方向に磁場を印加して測定した保磁力はFRを高める効果があり、2400A/mを超えるものが好ましい。なお、保磁力には結晶磁気異方定数や転位密度の影響が複雑に影響すると考えられる。ここで、扁平粉末が2400A/mを超える保磁力を有し得ることから、従来の「軟磁性」という表記ではなく、単に「磁性」との表記を用いているが、ここでいう「磁性」は「軟磁性」を含む。
本発明の扁平粉末は、好ましくはSi:1.0%以下、Mn:1.0%以下である。Si、Mnは、原料粉末のMs点調整や硬さ調整のために必要に応じて適宜添加でき、扁平加工により得られるアスペクト比を高くできる効果がある。1.0%を超えると飽和磁化が低下する。Si及びMn量は、より好ましくは各々0.10%を超え0.70%未満、さらに好ましくは各々0.20%を超え0.50%未満である。
本発明の扁平粉末は、好ましくはMo:1.0%以下、V:7.5%以下である。Mo,Vは、FRを上昇させる効果とともに、原料粉末の硬さ調整のために必要に応じて適宜添加できる。Moは、1.0%を超えると飽和磁化を低下させる。Mo量は、より好ましくは0.1%を超え0.7%未満、さらに好ましくは0.3%を超え0.5%未満である。一方、Vは、7.5%を超えると飽和磁化を低下させる。V量は、より好ましくは0.1%を超え7.0%未満、さらに好ましくは4.0%を超え6.0%未満である。
扁平粉末の製造方法
原料粉末の製造方法としては、水アトマイズ法、ガスアトマイズ法、ディスクアトマイズ法のような各種アトマイズ法が好ましい。アトマイズ法のような急冷法により作製された原料粉末にはマルテンサイト相が多く生成する。
原料粉末の製造方法としては、水アトマイズ法、ガスアトマイズ法、ディスクアトマイズ法のような各種アトマイズ法が好ましい。アトマイズ法のような急冷法により作製された原料粉末にはマルテンサイト相が多く生成する。
また、扁平加工前の原料粉末への第1熱処理は、原料粉末の硬さを調節することで、扁平加工により得られるアスペクト比を高くできる。1200℃を超えると原料粉末が焼結してしまうため、第1熱処理の温度は1200℃以下が好ましく、より好ましくは300℃を超え1100℃未満、さらに好ましくは750℃を超え1000℃未満である。
扁平加工後の扁平粉末への第2熱処理は、残留オーステナイト相の低減による飽和磁化増加と、いわゆる2次時効硬化に相当する変態にともなうFRの上昇に効果的である。900℃を超えるとマルテンサイト相がフェライト相に変態し、FRが低下してしまうため、第2熱処理の温度は900℃以下が好ましく、より好ましくは300℃を超え850℃未満、さらに好ましくは500℃を超え800℃未満である。
磁性シート
本発明の磁性シートは、上記扁平粉末を含有する。磁性シートの構成としては、従来提案されている一般的な構成が適用可能であり、磁性シート作製も従来提案されている一般的な方法で可能である。また、磁性シートの他、磁性フイルム、磁性コンパウンド、磁性塗料など、各種の磁性樹脂組成物としても、従来提案されている一般的な方法で製造し、用いることができる。本発明における扁平粉末を用いた磁性シートは、μ”が急激に増加する周波数が100MHz以上(FRは200MHz以上)であり、使用できる周波数としては、100MHz(もしくはそれ以上)対応品と言える。
本発明の磁性シートは、上記扁平粉末を含有する。磁性シートの構成としては、従来提案されている一般的な構成が適用可能であり、磁性シート作製も従来提案されている一般的な方法で可能である。また、磁性シートの他、磁性フイルム、磁性コンパウンド、磁性塗料など、各種の磁性樹脂組成物としても、従来提案されている一般的な方法で製造し、用いることができる。本発明における扁平粉末を用いた磁性シートは、μ”が急激に増加する周波数が100MHz以上(FRは200MHz以上)であり、使用できる周波数としては、100MHz(もしくはそれ以上)対応品と言える。
以下、本発明について実施例によって具体的に説明する。なお、以下、実施例によって本発明の効果が明らかにされるが、この実施例の記載に基づいて本発明が限定的に解釈されるべきではない。
No.1~122
(1)扁平粉末の作製
水アトマイズ法、ガスアトマイズ法、ディスクアトマイズ法または溶融による合金化後の粉砕法(鋳造粉砕法)のいずれかにより所定の成分の粉末を作製し150μm以下に分級した。各種アトマイズは従来提案されている一般的な方法で可能であり、アルミナ製坩堝を溶解に用い、坩堝下の直径2mmのノズルから合金溶湯を出湯し、これに高圧水を噴霧し溶湯を分断、高圧ガス(アルゴンまたは窒素)を噴霧し溶湯を分断、または回転ディスクにより遠心力で溶湯を分断することで実施した。
(1)扁平粉末の作製
水アトマイズ法、ガスアトマイズ法、ディスクアトマイズ法または溶融による合金化後の粉砕法(鋳造粉砕法)のいずれかにより所定の成分の粉末を作製し150μm以下に分級した。各種アトマイズは従来提案されている一般的な方法で可能であり、アルミナ製坩堝を溶解に用い、坩堝下の直径2mmのノズルから合金溶湯を出湯し、これに高圧水を噴霧し溶湯を分断、高圧ガス(アルゴンまたは窒素)を噴霧し溶湯を分断、または回転ディスクにより遠心力で溶湯を分断することで実施した。
なお、N量は高濃度のNを含む原料を選定すること、もしくは/および、アトマイズに高圧窒素ガスを選定することで調製可能である。これら粉末の一部には、次に続く扁平加工の前に熱処理を施した。これらを原料粉末として、扁平加工を実施した。扁平加工は従来提案されている一般的な方法で可能であり、アトライタ加工を用い、SUJ2製の直径4.8mmのボールを使用し、原料粉末と工業エタノールとともに攪拌容器に投入し、羽根の回転数を300rpmとして実施した。
工業エタノールの添加量は、原料粉末100質量部に対し、100質量部とした。扁平化加工時間とともにタップ密度は低下していくが、扁平化加工中に少量の粉末をサンプリングし、所定のタップ密度が得られた時点で扁平加工を完了とした。扁平加工後に攪拌容器から取り出した扁平粉末と工業エタノールをステンレス製の皿に移し、80℃で24時間乾燥させた。このようにして得た扁平粉末の一部は真空中、アルゴン中または窒素中で熱処理し、各種の評価に用いた。
(2)扁平粉末の評価
得られた扁平粉末の平均粒径、タップ密度、飽和磁化、透磁率を評価した。平均粒径はレーザ回折法、タップ密度は、約20gの扁平粉末を、容積100cm3のシリンダーに充填し、落下高さ10mmタップ回数200回の時の充填密度、飽和磁化はVSM装置で評価した。
得られた扁平粉末の平均粒径、タップ密度、飽和磁化、透磁率を評価した。平均粒径はレーザ回折法、タップ密度は、約20gの扁平粉末を、容積100cm3のシリンダーに充填し、落下高さ10mmタップ回数200回の時の充填密度、飽和磁化はVSM装置で評価した。
(3)磁性シートの作製および評価
得られた扁平粉末を用いて、以下の手順で磁性シートを作製した。まず、トルエンに塩素化ポリエチレンを溶解し、これに得られた扁平粉末を混合、分散した。この分散液をポリエステル樹脂に厚さ100μm程度となるように塗布し、常温常湿で乾燥させた。その後、130℃、15MPaの圧力でプレス加工し、磁性シートを得た。磁性シートのサイズは150mm×150mmで厚さは50μmであった。なお、磁性シート中の扁平粉末の体積充填率はいずれも約50%であった。
得られた扁平粉末を用いて、以下の手順で磁性シートを作製した。まず、トルエンに塩素化ポリエチレンを溶解し、これに得られた扁平粉末を混合、分散した。この分散液をポリエステル樹脂に厚さ100μm程度となるように塗布し、常温常湿で乾燥させた。その後、130℃、15MPaの圧力でプレス加工し、磁性シートを得た。磁性シートのサイズは150mm×150mmで厚さは50μmであった。なお、磁性シート中の扁平粉末の体積充填率はいずれも約50%であった。
次に、この磁性シートを、外径7mm、内径3mmのドーナツ状に切り出し、インピーダンス測定器により、室温でインピーダンス特性の周波数特性を測定し、その結果から透磁率(μ’およびμ”)を算出した。ここで、μ’の評価として1~5MHzの平均値、高周波特性の評価としてFRを用いた。さらに、得られた磁性シートの厚さ方向が観察できる樹脂埋め研磨試料を作製し、SEM観察により無作為に選んだ50粉末について、画像解析から平均厚さと平均アスペクト比を算出した。なお、アスペクト比は、「扁平粉末の長手方向長さ/扁平粉末の厚さ」である。
このようにして作製した扁平粉末と磁性シートについての原料粉末組成や評価結果を、表1~3に示す。No.1~100は本発明例であり、No.101~122は比較例である。なお、表1~3において、FRを単に「周波数」と示している。
比較例No.101は、C含有量が高いために、飽和磁化が低下し、実透磁率(μ’)が低下した。比較例No.102は、C含有量が低いために、周波数(FR)が低い。比較例No.103は、Cr含有量が高いために、飽和磁化が低い。比較例No.104は、Cr含有量が低く、かつ平均アスペクト比が低いために、実透磁率(μ’)が低下すると共に、周波数(FR)が低い。比較例No.105は、N含有量が高いために、飽和磁化が低い。比較例No.106は、N含有量が低く、平均アスペクト比が低いために、実透磁率(μ’)が低下した。
比較例No.107は、C含有量が高いために、飽和磁化が低下し、実透磁率(μ’)が低下した。比較例No.108は、C含有量が低いために、周波数(FR)が低い。比較例No.109は、Cr含有量が高いために、飽和磁化が低い。比較例No.110は、Cr含有量が低いために、実透磁率(μ’)が低下し、かつ周波数(FR)が低い。比較例No.111は、N含有量が高いために、飽和磁化が低い。
比較例No.112は、N含有量が低く、かつ平均アスペクト比が低いために、実透磁率(μ’)が低く、かつ周波数(FR)が低い。比較例No.113は、Si含有量が高く、かつ飽和磁化が低いために、周波数(FR)が低い。比較例No.114は、Mn含有量が高いために、飽和磁化が低い。比較例No.115は、Mo含有量が高いために、飽和磁化が低い。比較例No.116は、V含有量が高いために、飽和磁化が低い。比較例No.117は、平均粒径が大きいために、シート表面の凹凸が激しく発生した。
比較例No.118は、平均厚さが大きく、かつ平均アスペクト比が低いために、実透磁率(μ’)が低下した。比較例No.119は、平均アスペクト比が低いために、実透磁率(μ’)が低下した。比較例No.120は、飽和磁化が低いために、実透磁率(μ’)が低下した。比較例No.121は、第1の熱処理が高いために、製造不可能となった。比較例No.122は、第2の熱処理温度が高いために、周波数(FR)が低い。これに対して、本発明例No.1~100は、いずれも本発明の条件を満足し、保磁力メータにより測定した実施例扁平粉末の長手方向の保磁力は、いずれも2400A/m超で、測定上限範囲以上であった。したがって、目的とするいずれの効果をも十分達成していることが分かる。
以上述べたように、高Cのマルテンサイト相とN添加により、高保磁力を実現し、高CrによるMs点低下で、扁平加工前の状態に軟質な残留オーステナイト相を生成し、扁平化で高いアスペクト比を実現した高周波で用いる扁平粉末および磁性シートが提供される。
Claims (3)
- 質量%で、C:1.5~3.0%、Cr:10~20%、N:0.03~0.30%を含み、残部Feおよび不可避的不純物からなり、平均粒径が200μm以下、平均厚さが5μm以下、平均アスペクト比が5以上、飽和磁化が1.0T超、tanδが0.1となる周波数(FR)が200MHz以上である、高周波で用いる扁平粉末。
- 請求項1に記載の扁平粉末において、質量%で、Si:1.0%以下、Mn:1.0%以下、Mo:1.0%以下、V:7.5%以下のいずれか1種もしくは2種以上を更に含む高周波で用いる扁平粉末。
- 請求項1または2に記載の扁平粉末を含有する、磁性シート。