WO2018040905A1 - 聚合物复合膜及其制备方法以及包括其的锂离子电池 - Google Patents
聚合物复合膜及其制备方法以及包括其的锂离子电池 Download PDFInfo
- Publication number
- WO2018040905A1 WO2018040905A1 PCT/CN2017/097406 CN2017097406W WO2018040905A1 WO 2018040905 A1 WO2018040905 A1 WO 2018040905A1 CN 2017097406 W CN2017097406 W CN 2017097406W WO 2018040905 A1 WO2018040905 A1 WO 2018040905A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- polymer
- acrylate
- self
- segment
- Prior art date
Abstract
Description
Claims (41)
- 一种聚合物复合膜,包括聚合物基膜,所述聚合物基膜包括相对设置的第一表面和第二表面,所述聚合物复合膜还包括在所述聚合物基膜的所述第一表面上由内至外依次形成的第一陶瓷层、第一耐热纤维层、以及第一粘结层;其中,所述第一耐热纤维层的材料中同时含有第一高分子材料和第二高分子材料;所述第一高分子材料为熔点在180℃以上的耐热高分子材料;所述第二高分子材料的熔点低于所述第一高分子材料、且所述第二高分子材料在25℃的电解液中的吸液率在40%以上,误差为±5%。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一高分子材料在25℃的电解液中的吸液率低于5%,误差为±5%。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一高分子材料的玻璃化转变温度在100℃以上。
- 根据权利要求1所述的聚合物复合膜,其中,所述第二高分子材料的熔点为100至150℃;可选地,所述第二高分子材料的玻璃化转变温度在25℃以下。
- 根据权利要求1所述的聚合物复合膜,其中,所述第二高分子材料的25℃吸液率为40至100%,误差为±5%。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一耐热纤维层的材料为所述第一高分子材料和所述第二高分子材料的共混物。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一耐热纤维层中第一高分子材料和第二高分子材料的重量比为0.5至10:1,可选为为1至5:1,可选为为1至3:1。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一高分子材料选自聚醚酰亚胺、聚醚醚酮、聚醚砜、聚酰胺酰亚胺、聚酰胺酸和聚乙烯吡咯烷酮中的一种或者几种;所述第二高分子材料选自改性聚偏氟乙烯、聚丙烯酸酯、聚苯乙烯和聚氧化乙烯中的一种或者几种;可选地,所述改性聚偏氟乙烯为聚偏氟乙烯-六氟丙烯;可选地,所述聚丙烯酸酯为聚丙烯酸甲酯、聚丙烯酸乙酯、聚甲基丙烯酸甲酯中的一种或几种。
- 根据权利要求8所述的聚合物复合膜,其中,所述第一高分子材料为聚醚酰亚胺,所述第二高分子材料为聚偏氟乙烯-六氟丙烯;可选地所述第一耐热纤维层的材料为聚醚酰亚胺和聚偏氟乙烯-六氟丙烯的共混物。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一耐热纤维层中的纤维直径为100至2000nm,所述第一耐热纤维层的厚度为0.5至30μm。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一耐热纤维层的孔隙率为75%至93%,面密度为0.2至15g/m2。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一陶瓷层含有陶瓷颗粒和粘结剂,且所述第一陶瓷层在1μm厚度下的面密度ρ满足1.8mg/cm2<ρ≤2.7mg/cm2;可选地满足1.85mg/cm2≤ρ≤2.65mg/cm2,可选地满足1.9mg/cm2≤ρ≤2.6mg/cm2;可选地,所述陶瓷颗粒选自Al2O3、SiO2、BaSO4、BaO、TiO2、CuO、MgO、Mg(OH)2、LiAlO2、ZrO2、CNT、BN、SiC、Si3N4、WC、BC、AlN、Fe2O3、BaTiO3、MoS2、α-V2O5、PbTiO3、TiB2、CaSiO3、分子筛、粘土、勃姆石和高岭土中的一种或几种,可选地,所述陶瓷颗粒的平均粒径为200至800nm;可选地,所述粘结剂为玻璃化温度满足-40℃至0℃的聚丙烯酸酯;可选地,所述第一陶瓷层的单面厚度为1-5μm。
- 根据权利要求12所述的聚合物复合膜,其中,在所述第一陶瓷层中,相对于100重量份的所述陶瓷颗粒,所述粘结剂的含量为2至8重量份;可选地,在所述第一陶瓷层中,相对于100重量份的所述陶瓷颗粒,还包括0.3至1重量份的分散剂、0.5至1.8重量份的增稠剂、以及0至1.5重量份的表面处理剂,且所述分散剂的数均分子量在5万以下;可选地,在所述第一陶瓷层中,相对于100重量份的所述陶瓷颗粒,所述粘结剂的含量为4-6重量份,所述分散剂的含量为0.4-0.8重量份,所述增稠剂的含量为0.7-1.5重量份, 所述表面处理剂的含量为0.5-1.2重量份;可选地,所述分散剂为聚丙烯酸盐、脂肪族聚乙二醇醚、硅酸盐类、磷酸盐类和古尔胶中的至少一种;可选地,所述增稠剂为聚丙烯酸盐、聚丙烯酸盐共聚物、聚乙烯吡咯烷酮、纤维素类衍生物和聚丙烯酰胺中的至少一种;可选地,所述表面处理剂为3-缩水甘油基丙基三甲氧基硅烷和/或3-缩水甘油基丙基三乙氧基硅烷。
- 根据权利要求1所述的聚合物复合膜,其中,所述第一粘结层含有丙烯酸酯类交联聚合物以及苯乙烯-丙烯酸酯类交联共聚物和/或偏氟乙烯-六氟丙烯共聚物,且所述粘结层的孔隙率为40至65%;可选地,所述丙烯酸酯类交联聚合物的玻璃化转变温度为-20℃至60℃,所述苯乙烯-丙烯酸酯类交联共聚物的玻璃化转变温度为-30℃至50℃,所述偏氟乙烯-六氟丙烯共聚物的玻璃化转变温度为-65℃至-40℃。
- 根据权利要求14所述的聚合物复合膜,其中,所述第一粘结层含有所述丙烯酸酯类交联聚合物和所述苯乙烯-丙烯酸酯类交联共聚物且不含有所述偏氟乙烯-六氟丙烯共聚物,所述丙烯酸酯类交联聚合物与所述苯乙烯-丙烯酸酯类交联共聚物的重量比为1:(0.05至2);或者,所述第一粘结层含有所述丙烯酸酯类交联聚合物和所述偏氟乙烯-六氟丙烯共聚物且不含有所述苯乙烯-丙烯酸酯类交联共聚物,所述丙烯酸酯类交联聚合物与所述偏氟乙烯-六氟丙烯共聚物的重量比为1:(0.3至25);或者,所述第一粘结层含有所述丙烯酸酯类交联聚合物、所述苯乙烯-丙烯酸酯类交联共聚物和所述偏氟乙烯-六氟丙烯共聚物,所述丙烯酸酯类交联聚合物、所述苯乙烯-丙烯酸酯类交联共聚物与所述偏氟乙烯-六氟丙烯共聚物的重量比为1:(0.01至2):(0.3至5)。
- 根据权利要求14所述的聚合物复合膜,其中,所述丙烯酸酯类交联聚合物为第一丙烯酸酯类交联聚合物与第二丙烯酸酯类交联聚合物和/或第三丙烯酸酯类交联聚合物的混合物,或为第二丙烯酸酯类交联聚合物,或为第三丙烯酸酯类交联聚合物;所述第一丙烯酸酯类交联聚合物含有70至80重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、10至20重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙 烯酸链段,所述第二丙烯酸酯类交联聚合物含有30至40重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、50至60重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述第三丙烯酸酯类交联聚合物含有50至80重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、15至40重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段;所述第一丙烯酸酯类交联聚合物的玻璃化转变温度为50℃至60℃,所述第二丙烯酸酯类交联聚合物的玻璃化转变温度为-20℃至-5℃,所述第三丙烯酸酯类交联聚合物的玻璃化转变温度为30℃至50℃;所述苯乙烯-丙烯酸酯类交联共聚物含有40至50重量%的聚苯乙烯链段、5至15重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、30至40重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段;所述苯乙烯-丙烯酸酯类交联共聚物的玻璃化转变温度为15至30℃;所述偏氟乙烯-六氟丙烯共聚物含有80至98重量%的聚偏氟乙烯链段和2至20重量%的聚六氟丙烯链段;所述偏氟乙烯-六氟丙烯共聚物的玻璃化转变温度为-60℃至-40℃。
- 根据权利要求14所述的聚合物复合膜,其中,所述第一粘结层含有第一丙烯酸酯类交联聚合物、第二丙烯酸酯类交联聚合物和所述苯乙烯-丙烯酸酯类交联共聚物且不含有所述偏氟乙烯-六氟丙烯共聚物,且所述第一丙烯酸酯类交联聚合物、所述第二丙烯酸酯类交联聚合物与所述苯乙烯-丙烯酸酯类交联共聚物的重量比为(5至10):1:(10至13);或者,所述第一粘结层含有所述第一丙烯酸酯类交联聚合物、所述第二丙烯酸酯类交联聚合物和所述偏氟乙烯-六氟丙烯共聚物且不含有所述苯乙烯-丙烯酸酯类交联共聚物,所述第一丙烯酸酯类交联聚合物、所述第二丙烯酸酯类交联聚合物与所述偏氟乙烯-六氟丙烯共聚物的重量比为(5至15):1:(5至12);或者,所述第一粘结层含有所述第二丙烯酸酯类交联聚合物和所述偏氟乙烯-六氟丙烯共聚物且不含有所述苯乙烯-丙烯酸酯类交联共聚物,所述第二丙烯酸酯类交联聚合物与所述偏氟乙烯-六氟丙烯共聚物的重量比为1:(5至20);或者,所述第一粘结层含有所述第二丙烯酸酯类交联聚合物、所述苯乙烯-丙烯酸酯类交联共聚物和所述偏氟乙烯-六氟丙烯共聚物,所述第二丙烯酸酯类交联聚合物、所述苯乙烯-丙烯酸酯类交联共聚物与所述偏氟乙烯-六氟丙烯共聚物的重量比为1:(0.5至2):(1至5);或者,所述第一粘结层含有第三丙烯酸酯类交联聚合物、所述苯乙烯-丙烯酸酯类交联共聚物 和所述偏氟乙烯-六氟丙烯共聚物,所述所述第三丙烯酸酯类交联聚合物、所述苯乙烯-丙烯酸酯类交联共聚物与所述偏氟乙烯-六氟丙烯共聚物的重量比为1:(0.5至2):(1至5);或者,所述第一粘结层含有所述第一丙烯酸酯类交联聚合物、所述第二丙烯酸酯类交联聚合物、所述苯乙烯-丙烯酸酯类交联共聚物和所述偏氟乙烯-六氟丙烯共聚物,所述第一丙烯酸酯类交联聚合物、所述第二丙烯酸酯类交联聚合物、所述苯乙烯-丙烯酸酯类交联共聚物与所述偏氟乙烯-六氟丙烯共聚物的重量比为(10至15):1:(0.5至2):(5至10);其中,所述第一丙烯酸酯类交联聚合物含有70至80重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、10至20重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述第二丙烯酸酯类交联聚合物含有30至40重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、50至60重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述第三丙烯酸酯类交联聚合物含有50至80重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、15至40重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述苯乙烯-丙烯酸酯类交联共聚物含有40至50重量%的聚苯乙烯链段、5至15重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、30至40重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述偏氟乙烯-六氟丙烯共聚物含有80至98重量%的聚偏氟乙烯链段和2至20重量%的聚六氟丙烯链段;所述第一丙烯酸酯类交联聚合物的玻璃化转变温度为50℃至60℃,所述第二丙烯酸酯类交联聚合物的玻璃化转变温度为-20℃至-5℃,所述第三丙烯酸酯类交联聚合物的玻璃化转变温度为30℃至50℃,所述苯乙烯-丙烯酸酯类交联共聚物的玻璃化转变温度为15至30℃,所述偏氟乙烯-六氟丙烯共聚物的玻璃化转变温度为-60℃至-40℃。
- 根据权利要求14所述的聚合物复合膜,其中,所述第一粘结层中还含有丙烯腈-丙烯酸酯共聚物、氯丙共聚物和丁苯共聚物中的至少一种;可选地,当所述第一粘结层中还含有所述丙烯腈-丙烯酸酯共聚物时,所述丙烯腈-丙烯酸酯共聚物与所述丙烯酸酯类交联聚合物的重量比为0.05至2:1;可选地,当所述第一粘结层中还含有所述氯丙共聚物时,所述氯丙共聚物与所述丙烯酸酯类交联聚合物的重量比为0.15至7:1;可选地,当所述第一粘结层中还含有所述丁苯共聚物时,所述丁苯共聚物与所述丙烯酸酯类交联聚合物的重量比为0.05至2:1。
- 根据权利要求14所述的聚合物复合膜,其中,所述第一粘结层的单面面密度为0.05至0.9mg/cm2;所述第一粘结层的单面厚度为0.1至1μm。
- 根据权利要求1所述的聚合物复合膜,其中,所述聚合物复合膜由依次层叠设置的所述聚合物基膜、所述第一陶瓷层、所述第一耐热纤维层、以及所述第一粘结层组成。
- 根据权利要求1所述的聚合物复合膜,其中,所述聚合物复合膜还包括在所述聚合物基膜的所述第二表面上由内至外依次设置的第二陶瓷层和第二粘结层,所述第二陶瓷层与所述第一陶瓷层相同或不同,所述第二粘结层与所述第一粘结层相同或不同;可选地,所述聚合物复合膜由依次层叠设置的所述第二粘结层、所述第二陶瓷层、所述聚合物基膜、所述第一陶瓷层、所述第一耐热纤维层和所述第一粘结层组成。
- 根据权利要求1所述的聚合物复合膜,其中,所述聚合物复合膜还包括在所述聚合物基膜的所述第二表面上由内至外依次设置的第二陶瓷层、第二耐热纤维层和第二粘结层,所述第二陶瓷层与所述第一陶瓷层相同或不同,所述第二耐热纤维层与所述第一耐热纤维层相同或不同,所述第二粘结层与所述第一粘结层相同或不同;可选地,所述聚合物复合膜由依次层叠设置的所述第二粘结层、所述第二耐热纤维层、所述第二陶瓷层、所述聚合物基膜、所述第一陶瓷层、所述第一耐热纤维层和所述第一粘结层组成。
- 一种聚合物复合膜的制备方法,包括如下步骤:S1、提供聚合物基膜,所述聚合物基膜包括相对设置的第一表面和第二表面;S2、在所述聚合物基膜的第一表面上形成第一陶瓷层;S3、配制含有第一高分子材料和第二高分子材料的纺丝溶液,将所述纺丝溶液通过静电纺丝在所述第一陶瓷层的表面上形成第一耐热纤维层;S4、在所述第一耐热纤维层的表面上形成第一粘结层;所述第一高分子材料为熔点在180℃以上的耐热高分子材料;所述第二高分子材料的熔点低于所述第一高分子材料、且所述第二高分子材料在25℃的电解液中的吸液率在40%以上,误差为±5%;可选地,所述第一高分子材料在25℃的电解液中的吸液率为零低于5%,误差为±5%;可选地,所述第一高分子材料的玻璃化转变温度在100℃以上;可选地,所述第二高分子材料的熔点为100至150℃;可选地,所述第二高分子材料的玻璃化转变温度在25℃以下;可选地,所述第二高分子材料的25℃吸液率为40至100%,误差为±5%。
- 根据权利要求23所述的制备方法,其中,第一高分子材料和第二高分子材料的重量比为(0.5至10):1,可选为(1至5):1,可选为(1至3):1。
- 根据权利要求23所述的制备方法,其中,所述第一高分子材料选自聚醚酰亚胺、聚醚醚酮、聚醚砜、聚酰胺酰亚胺、聚酰胺酸和聚乙烯吡咯烷酮中的一种或几种;所述第二高分子材料选自改性聚偏氟乙烯、聚丙烯酸酯、聚苯乙烯和聚氧化乙烯中的一种或几种,可选地,所述改性聚偏氟乙烯为聚偏氟乙烯-六氟丙烯;可选地,所述聚丙烯酸酯为聚丙烯酸甲酯、聚丙烯乙酯、聚甲基丙烯酸甲酯中的一种或多种。
- 根据权利要求23所述的制备方法,其中,所述步骤S3包括:S301、分别独立地配制含有所述第一高分子材料的纺丝溶液A和含有所述第二高分子材料的纺丝溶液B;S302、采用所述纺丝溶液A和所述纺丝溶液B同时进行静电纺丝形成所述第一耐热纤维层。
- 根据权利要求23所述的制备方法,其中,所述步骤S3包括:S311、将所述第一高分子材料和所述第二高分子材料共混,形成共混物;再配制含有所述共混物的纺丝溶液;S312、采用所述纺丝溶液进行静电纺丝形成所述第一耐热纤维层。
- 根据权利要求23所述的制备方法,还包括在完成静电纺丝后,在50至120℃、0.5至10MPa的压力下进行压膜。
- 根据权利要求23所述的制备方法,其中,所述步骤S2中第一陶瓷层的制备方法包括:将陶瓷颗粒、粘结剂、分散剂和增稠剂按照重量比100:(2至8):(0.3至1):(0.5至1.8)混合搅拌得到第一陶瓷层浆料,并将所述第一陶瓷层浆液涂覆于所述聚合物基膜的 所述第一表面上,烘干得到所述第一陶瓷层;其中所述分散剂的数均分子量为5万以下;可选地,所述步骤S2中,所述搅拌的转速为3000至10000rpm,可选为3000-9000rpm;所述搅拌的时间为30至120min;可选地,所述步骤S2中,将陶瓷颗粒、粘结剂、分散剂和增稠剂按照重量比100:(4至6):(0.4至0.8):(0.7至15)的比例搅拌混合。
- 根据权利要求29所述的制备方法,其中,所述陶瓷颗粒选自Al2O3、SiO2、BaSO4、BaO、TiO2、CuO、MgO、Mg(OH)2、LiAlO2、ZrO2、CNT、BN、SiC、Si3N4、WC、BC、AlN、Fe2O3、BaTiO3、MoS2、α–V2O5、PbTiO3、TiB2、CaSiO3、分子筛、粘土、勃姆石和高岭土中的至少一种,可选地,所述陶瓷颗粒的平均粒径为200至800nm,可选为300至600nm;所述粘结剂为玻璃化温度满足-40℃至0℃的聚丙烯酸酯;所述分散剂为聚丙烯酸盐、脂肪族聚乙二醇醚、硅酸盐类、磷酸盐类和古尔胶中的至少一种;所述增稠剂为聚丙烯酸盐、聚丙烯酸盐共聚物、聚乙烯吡咯烷酮、纤维素类衍生物和聚丙烯酰胺中的至少一种。
- 根据权利要求29所述的制备方法,其中,所述步骤S2中混合得到的所述第一陶瓷层浆液中还含有表面处理剂,所述表面处理剂为3-缩水甘油基丙基三甲氧基硅烷和/或3-缩水甘油基丙基三乙氧基硅烷;可选地,相对于100重量份的所述陶瓷颗粒,所述表面处理剂的用量为1.5重量份以下,可选为0.5-1.2重量份。
- 根据权利要求23所述的制备方法,其中,所述步骤S4包括:将含有自交联型纯丙乳液以及自交联型苯丙乳液和/或偏氟乙烯和六氟丙烯的共聚乳液的浆料附着在所述第一耐热纤维层的表面上,接着进行干燥,以在所述第一耐热纤维层的表面上形成孔隙率为40至65%的第一粘结层;可选地,所述自交联型纯丙乳液中的丙烯酸酯类交联聚合物的玻璃化转变温度为-20℃至60℃,所述自交联型苯丙乳液中的苯乙烯-丙烯酸酯类交联共聚物的玻璃化转变温度为-30℃至50℃,所述偏氟乙烯和六氟丙烯的共聚乳液中的偏氟乙烯-六氟丙烯共聚物的玻璃化转变温度为-65℃至-40℃。
- 根据权利要求32所述的方法,其中,所述浆料含有所述自交联型纯丙乳液与所述自交联型苯丙乳液且不含有所述偏氟乙烯和六氟丙烯的共聚乳液,所述自交联型纯丙乳液与所述自交联型苯丙乳液的固含量的重量比为1:(0.05至2);或者,所述浆料含有所述自交联型纯丙乳液与所述偏氟乙烯和六氟丙烯的共聚乳液且不含有所述自交联型苯丙乳液,所述自交联型纯丙乳液与所述偏氟乙烯和六氟丙烯的共聚乳液的固含量的重量比为1:(0.3至25);或者,所述浆料含有所述自交联型纯丙乳液、所述自交联型苯丙乳液、所述偏氟乙烯和六氟丙烯的共聚乳液,所述自交联型纯丙乳液、所述自交联型苯丙乳液、所述偏氟乙烯和六氟丙烯的共聚乳液的固含量的重量比为1:(0.01至2):(0.3至5)。
- 根据权利要求32所述的方法,其中,所述自交联型纯丙乳液为第一自交联型纯丙乳液与第二自交联型纯丙乳液和/或第三自交联型纯丙乳液的混合物,或为第二自交联型纯丙乳液,或为第三自交联型纯丙乳液;所述第一自交联型纯丙乳液中的丙烯酸酯类交联聚合物含有70至80重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、10至20重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述第二自交联型纯丙乳液中的丙烯酸酯类交联聚合物含有30至40重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、50至60重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述第三自交联型纯丙乳液中的丙烯酸酯类交联聚合物含有50至80重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、15至40重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段;所述第一自交联型纯丙乳液中的丙烯酸酯类交联聚合物的玻璃化转变温度为50℃至60℃,所述第二自交联型纯丙乳液中的丙烯酸酯类交联聚合物的玻璃化转变温度为-20℃至-5℃,所述第三自交联型纯丙乳液中的丙烯酸酯类交联聚合物的玻璃化转变温度为30℃至50℃;所述自交联型苯丙乳液中的苯乙烯-丙烯酸酯类交联共聚物含有40至50重量%的聚苯乙烯链段、5至15重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、30至40重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段;所述苯乙烯-丙烯酸酯类交联共聚物的玻璃化转变温度为15至30℃;所述偏氟乙烯和六氟丙烯的共聚乳液中的偏氟乙烯-六氟丙烯共聚物含有80至98重量%的聚偏氟乙烯链段和2至20重量%的聚六氟丙烯链段;所述偏氟乙烯-六氟丙烯共聚物 的玻璃化转变温度为-60℃至-40℃。
- 根据权利要求32所述的方法,其中,所述步骤S4中,所述浆料含有第一自交联型纯丙乳液、第二自交联型纯丙乳液和所述自交联型苯丙乳液且不含有所述偏氟乙烯和六氟丙烯的共聚乳液,所述第一自交联型纯丙乳液、所述第二自交联型纯丙乳液与所述自交联型苯丙乳液的固含量的重量比为(5至10):1:(10至13);或者,所述浆料含有所述第一自交联型纯丙乳液、所述第二自交联型纯丙乳液以及所述偏氟乙烯和六氟丙烯的共聚乳液且不含有所述自交联型苯丙乳液,所述第一自交联型纯丙乳液、所述第二自交联型纯丙乳液与所述偏氟乙烯和六氟丙烯的共聚乳液的固含量的重量比为5至15:1:5至12;或者,所述浆料含有所述第二自交联型纯丙乳液以及所述偏氟乙烯和六氟丙烯的共聚乳液且不含有所述自交联型苯丙乳液,所述第二自交联型纯丙乳液与所述偏氟乙烯和六氟丙烯的共聚乳液的固含量的重量比为1:5至20;或者,所述浆料含有所述第二自交联型纯丙乳液、所述自交联型苯丙乳液以及所述偏氟乙烯和六氟丙烯的共聚乳液,所述所述第二自交联型纯丙乳液、所述自交联型苯丙乳液与所述偏氟乙烯和六氟丙烯的共聚乳液的固含量的重量比为1:(0.5至2):(1至5);或者,所述浆料含有第三自交联型纯丙乳液、所述自交联型苯丙乳液以及所述偏氟乙烯和六氟丙烯的共聚乳液,所述第三自交联型纯丙乳液、所述自交联型苯丙乳液与所述偏氟乙烯和六氟丙烯的共聚乳液的固含量的重量比为1:(0.5至2):(1至5);或者,所述浆料含有所述第一自交联型纯丙乳液、所述第二自交联型纯丙乳液、所述自交联型苯丙乳液以及所述偏氟乙烯和六氟丙烯的共聚乳液,所述第一自交联型纯丙乳液、所述第二自交联型纯丙乳液、所述自交联型苯丙乳液与所述偏氟乙烯和六氟丙烯的共聚乳液的固含量的重量比为(10至15):1:(0.5至2):(5至10);所述第一自交联型纯丙乳液中的丙烯酸酯类交联聚合物含有70至80重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、10至20重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述第二自交联型纯丙乳液中的丙烯酸酯类交联聚合物含有30至40重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、50至60重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述第三自交联型纯丙乳液中的丙烯酸酯类交联聚合物含有50至80重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、15至40重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段, 所述自交联型苯丙乳液中的苯乙烯-丙烯酸酯类交联共聚物含有40至50重量%的聚苯乙烯链段、5至15重量%的聚甲基丙烯酸甲酯链段、2至10重量%的聚丙烯酸乙酯链段、30至40重量%的聚丙烯酸丁酯链段和2至10重量%的聚丙烯酸链段,所述偏氟乙烯和六氟丙烯的共聚乳液中的偏氟乙烯-六氟丙烯共聚物含有80至98重量%的聚偏氟乙烯链段和2至20重量%的聚六氟丙烯链段;所述第一自交联型纯丙乳液中的丙烯酸酯类交联聚合物的玻璃化转变温度为50℃至60℃,所述第二自交联型纯丙乳液中的丙烯酸酯类交联聚合物的玻璃化转变温度为-20℃至-5℃,所述第三自交联型纯丙乳液中的丙烯酸酯类交联聚合物的玻璃化转变温度为30℃至50℃,所述苯乙烯-丙烯酸酯类交联共聚物的玻璃化转变温度为15至30℃,所述偏氟乙烯-六氟丙烯共聚物的玻璃化转变温度为-60℃至-40℃。
- 根据权利要求32所述的方法,其中,所述步骤S4中,所述浆料中还含有丙烯腈和丙烯酸酯的共聚乳液、氯丙乳液和丁苯胶乳中的至少一种;可选地,当所述浆料中还含有所述丙烯腈和丙烯酸酯的共聚乳液时,所述丙烯腈和丙烯酸酯的共聚乳液与所述自交联型纯丙乳液的固含量的重量比为0.05至2:1;可选地,当所述浆料中还含有所述氯丙乳液时,所述氯丙乳液与所述自交联型纯丙乳液的固含量的重量比为0.15至7:1;可选地,当所述浆料中还含有所述丁苯胶乳时,所述丁苯胶乳与所述自交联型纯丙乳液的固含量的重量比为0.05至2:1。
- 根据权利要求32所述的方法,其中,所述附着的方法为喷涂法和/或丝网印刷法;所述喷涂法和丝网印刷法的操作温度各自独立地为30至80℃;所述干燥的温度为30至80℃。
- 根据权利要求23所述的方法,还包括:在所述聚合物基膜的第二表面上形成第二陶瓷层;在所述第二陶瓷层的表面上形成第二粘结层。
- 根据权利要求23所述的方法,还包括:在所述聚合物基膜的第二表面上形成第二陶瓷层;在所述第二陶瓷层的表面上形成第二耐热纤维层;在所述第二耐热纤维层的表面上形成第二粘结层。
- 由权利要求23至39中任一项所述的方法制备得到的聚合物复合膜。
- 一种锂离子电池,包括正极、负极和位于所述正极和负极之间的电池隔膜,所述电池隔膜为权利要求1至22以及40中任一项所述的聚合物复合膜。