WO2018012906A1 - 코코넛 섬유를 함유한 바닥재용 조성물 및 이를 이용한 바닥재의 제조 방법 - Google Patents

코코넛 섬유를 함유한 바닥재용 조성물 및 이를 이용한 바닥재의 제조 방법 Download PDF

Info

Publication number
WO2018012906A1
WO2018012906A1 PCT/KR2017/007532 KR2017007532W WO2018012906A1 WO 2018012906 A1 WO2018012906 A1 WO 2018012906A1 KR 2017007532 W KR2017007532 W KR 2017007532W WO 2018012906 A1 WO2018012906 A1 WO 2018012906A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
parts
flooring
emulsifier
acrylonitrile
Prior art date
Application number
PCT/KR2017/007532
Other languages
English (en)
French (fr)
Inventor
정대호
Original Assignee
정대호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020160088731A external-priority patent/KR101674358B1/ko
Application filed by 정대호 filed Critical 정대호
Priority to US16/313,827 priority Critical patent/US10703868B2/en
Publication of WO2018012906A1 publication Critical patent/WO2018012906A1/ko

Abstract

본 발명에 따른 코코넛 섬유를 포함한 바닥재용 조성물은 (A) 아크릴로니트릴 20 내지 60 중량부, 부타디엔 40 내지 80 중량부, 제1 유화제 1 내지 3 중량부, 및 아크릴 모노머 4 내지 7 중량부로 이루어지는 아크로니트릴-부타디엔 라텍스 100 중량부; (B) 황, EZ, MZ, 제2 유화제가 3:1:1:0.1 의 비율로 혼합된 가황처리제 3 내지 6 중량부; (C) 산화아연 2 내지 3 중량부; (D) 산화방지제 2 내지 5 중량부; 및 (E) 탄산칼슘 20 내지 40 중량부를 포함하여 이루어지는 것을 특징으로 한다.

Description

코코넛 섬유를 함유한 바닥재용 조성물 및 이를 이용한 바닥재의 제조 방법
본 발명은 바닥재용 조성물에 관한 것이다. 보다 구체적으로 본 발명은 코코넛 섬유를 이용하여 바닥재를 제조함으로써 인장 강도, 내구성, 내후성 등이 우수하고, 중금속이나 유해 물질이 발생되지 않아 친환경적인 바닥재용 조성물 및 그 제조 방법에 관한 것이다.
일반적으로 어린이 놀이터, 운동장의 트랙, 조깅 및 자전거 주행을 위한 노면에는 지면에 전달되는 충격을 줄이고, 일정한 쿠션감을 주어 운동하는 사람의 피로도를 줄이며 부상 등을 방지하는 역할을 하기 위해 바닥재를 시공하고 있다. 이러한 바닥재는 주로 PVC, 폐타이어, 고무 등을 분쇄하여 칩 형태로 만든 다음, 접착제 및 경화제와 함께 일정한 비율로 혼합하여 교반한 것을 압축성형하는 방식으로 제조하고 있다.
이러한 종래의 방식에 의하면 탄성 흡수력 및 복원력에서 한계가 있기 때문에 수년간 사용하면 강도와 내구성이 크게 저하된다. 따라서, 다양한 첨가제를 사용하거나 바닥재의 구조를 변형하여 이를 보완하는 기술이 제시되고 있다.
예를 들어, 대한민국 특허공개 제10-2012-0027763호에서는 우레탄 바인더의 성능을 보강하여 위 문제점을 해결하고자 하고 있다. 한편, 대한민국 특허공개 제10-2013-0128222호에서는 폴리우레탄수지, EPDM(Ethylene Propylene Diene Monomer) 칩에 폐타이어 칩이나 재생고무 칩 등으로 이루어진 복합재료를 이용하여 표면을 전체적으로 탄성 포장재를 시공하는 기술에 대하여 개시하고 있다.
하지만, 상기 선행기술에서와 같이 복합재료를 이용하여 제작되는 탄성 포장재는 바닥에 충분한 탄성이 부여되도록 하여 보행자의 보행 감이 좋도록 함은 물론, 충격을 완화시켜 주어 안전사고의 발생을 예방하는 효과가 있으나, 종래 탄성 포장재는 자원의 재활용 차원에서 폐타이어 칩이나 재생고무 칩 등의 재생자재나 EPDM 칩으로부터 인체에 해로운 휘발성 유기화합물(VOCs) 등과 같은 유해물질의 방출되어 인체에 유해하였으며, 특히 기온이 높으면 그 방출량이 증가하는 등의 문제점이 있다. 더욱이, 폴리우레탄수지, EPDM 칩, 폐타이어 칩, 재생고무 칩 등 서로 다른 성질을 갖는 복합재료들을 상호 접착하여 이루어지는 종래의 탄성 바닥재는 상호 접착성이 낮아 바닥에 포장되어 사용시 외부의 충격에 쉽게 부서지거나 파손되어 사용이 곤란한 문제점이 있었다.
이에 본 발명자는 상술한 문제점을 해결하기 위하여 폐고무나 폐타이어와 같은 재료를 사용하지 않고 친환경적인 코코넛 섬유를 응용하여 탄성 바닥재를 제조하기 위한 조성물 및 이를 이용하여 제조된 바닥재를 제안하고자 한다.
본 발명의 목적은 유해 물질이 방출되지 않아 보다 친환경적인 코코넛 섬유를 이용한 바닥재용 조성물 및 이를 이용하여 제조된 바닥재를 제공하는 것이다.
본 발명의 또 다른 목적은 인장 강도, 내구성, 내후성 등이 우수한 바닥재용 조성물 및 이를 이용하여 제조된 바닥재를 제공하는 것이다.
본 발명의 상기 목적 및 기타 내재되어 있는 목적은 아래 설명하는 본 발명에 의하여 모두 용이하게 달성될 수 있다.
본 발명에 따른 코코넛 섬유를 포함한 바닥재용 조성물은
(A) 아크릴로니트릴 20 내지 60 중량부, 부타디엔 40 내지 80 중량부, 제1 유화제 1 내지 3 중량부, 및 아크릴 모노머 4 내지 7 중량부로 이루어지는 아크로니트릴-부타디엔 라텍스 100 중량부;
(B) 황, EZ, MZ, 제2 유화제가 3:1:1:0.1 의 비율로 혼합된 가황처리제 3 내지 6 중량부;
(C) 산화아연 2 내지 3 중량부;
(D) 산화방지제 2 내지 5 중량부; 및
(E) 탄산칼슘 20 내지 40 중량부;
를 포함하여 이루어지는 것을 특징으로 한다.
본 발명에서, 선택적으로 (F)로디닉산을 5 중량부 이내로 더 포함하여도 좋다.
본 발명에서, 상기 제1 유화제는 모노에탄올아민(MEA), 다이에탄올아민(DEA), 트리에탄올아민(TEA), 다이글리콜아민(DGA), 다이클로로헥실아민(DCHA), 올레인산 아민염, 톨오일(Tall oil) 아민염, 숙신산 아민염, 지방산, 폴리옥시에틸렌글리콜 지방산-에스테르, 폴리옥시에틸렌트리데실 에테르, 소르비탄올레이트 및 소듐설포네이트로 이루어진 군에서 선택된 1 종 이상의 유화제인 것이 바람직하다.
본 발명에서, 상기 제2 유화제는 메틸알코올, 에틸알코올, 프로필알코올, 및 디메틸 폴리실록산(dimethylpolysiloxane)으로 이루어진 군에서 선택된 하나 또는 그 이상의 혼합물인 것이 바람직하다.
본 발명에 따른 코코넛 섬유를 함유한 바닥재의 제조 방법은
상술한 본 발명에 따른 바닥재용 조성물을 코코넛 섬유에 도포하고;
도포된 코코넛 섬유를 압축하는;
단계를 포함하는 것을 특징으로 한다.
본 발명은 유해 물질이 방출되지 않아 친환경적이고 내구성, 탄성 복원력, 내마모성, 내후성 등의 물성이 우수한 바닥재용 조성물을 제공하는 발명의 효과를 갖는다.
본 발명에 따른 코코넛 섬유를 포함한 바닥재용 조성물은
(A) 아크릴로니트릴 20 내지 60 중량부, 부타디엔 40 내지 80 중량부, 제1 유화제 1 내지 3 중량부, 및 아크릴 모노머 4 내지 7 중량부로 이루어지는 아크로니트릴-부타디엔 라텍스 100 중량부;
(B) 황, EZ, MZ, 제2 유화제가 3:1:1:0.1 의 비율로 혼합된 가황처리제 3 내지 6 중량부;
(C) 산화아연 2 내지 3 중량부;
(D) 산화방지제 2 내지 5 중량부; 및
(E) 탄산칼슘 20 내지 40 중량부;
를 포함하여 이루어지는 것을 특징으로 한다.
본 발명의 바닥재용 조성물은 코코넛 섬유의 표면에 물과 50:50 또는 45:55 의 비율로 혼합한 용액으로 도포하여 코코넛 섬유의 물성을 개선하는데 사용한다. 이렇게 개선된 코코넛 섬유를 이용하여 바닥재를 제조한다.
본 발명의 아크로니트릴-부타디엔 라텍스(A)는 고형분의 고무 라텍스로써, 코코넛 섬유에 탄성력을 부여하며, 상기 코코넛 섬유 표면을 개질하는 매트릭스로서의 역할을 수행한다. 여기서 사용되는 라텍스는 수용성으로서, 종래의 폴리우레탄 바인더와 같은 유기 화합물의 사용이 불필요하고, 나아가 내후성이 양호하여 바닥 포장용으로 사용하기에 적합하다. 본 발명에 따른 바닥재용 조성물에서는 아크로니트릴-부타디엔 라텍스(A) 100 중량부를 기준으로 하여 다른 성분들을 혼합하여 사용한다.
본 발명의 제1 유화제는 모노에탄올아민(MEA), 다이에탄올아민(DEA), 트리에탄올아민(TEA), 다이글리콜아민(DGA), 다이클로로헥실아민(DCHA), 올레인산 아민염, 톨오일(Tall oil) 아민염, 숙신산 아민염, 지방산, 폴리옥시에틸렌글리콜 지방산-에스테르, 폴리옥시에틸렌트리데실 에테르, 소르비탄올레이트 및 소듐설포네이트 중에서 선택된 1 종 이상의 유화제를 사용할 수 있다.
본 발명의 아크릴 모노머는 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 프로필(메타)아크릴레이트, 이소프로필(메타)아크릴레이트, 부틸(메타)아크릴레이트, 이소부틸(메타)아크릴레이트, 펜틸(메타)아크릴레이트, 헥실(메타)아크릴레이트, 헵틸(메타)아크릴레이트, 옥틸(메타)아크릴레이트, 이소옥틸(메타)아크릴레이트, 2-에틸헥실(메타)아크릴레이트, 노닐(메타)아크릴레이트, 이소노닐(메타)아크릴레이트, 데실(메타)아크릴레이트, 운데실(메타)아크릴레이트, 도데실(메타)아크릴레이트, 트리데실(메타)아크릴레이트, 테트라데실(메타)아크릴레이트, 시클로펜틸(메타)아크릴레이트, 시클로헥실(메타)아크릴레이트 등으로부터 얻은 모노머를 사용할 수 있다.
본 발명의 아크로니트릴-부타디엔 라텍스(A)는 아크릴로니트릴 20 내지 60 중량부, 부타디엔 40 내지 80 중량부, 제1 유화제 1 내지 3 중량부, 및 아크릴 모노머 4 내지 7 중량부의 범위로 혼합하여, 혼합된 라텍스를 100 중량부를 기준으로 하고 다른 성분을 아래 각각 설명하는 비율로 적용한다.
본 발명의 가황 처리제(B)는 유기 가황촉진제로, 가황속도를 증진시켜 가황시간을 단축시키는 역할을 하며, 가황온도를 저하시키면서 품질을 향상시키는 역할을 한다. 본 발명에 사용되는 유기 가황촉진제는 티아졸계(thiazole) MBT(2-Mercapto benzo thiazole)를 함유한 Zn-MBT(MZ)와, 디티오 카보메이트계(dithio carbamate)인 ZnEDC(zinc dimetyl dithiocarbamate)(EZ)를 병용하여 사용하되, 제2 유화제를 함께 사용한다.
본 발명의 가황 처리제(B)에 적용되는 제2 유화제는 친유성 계면활성제 및 친수성 유화안정제 및 친유성 유화안정제 중에서 선택된 하나 이상이 사용될 수 있다. 또한, 제2 유화제로 알코올(메틸알코올, 에틸알코올 및 프로필알코올 등) 및 디메틸 폴리실록산(dimethylpolysiloxane)으로 이루어진 군중에서 선택된 하나 또는 그 이상의 혼합을 사용하여도 좋다.
본 발명의 가황 처리제(B)의 구성 비율은 황, EZ, MZ, 제2 유화제가 3:1:1:0.1 의 비율을 갖도록 적용한다.
본 발명에서 가황 처리제(B)는 아크로니트릴-부타디엔 라텍스(A) 100 중량부에 대하여 3 내지 6 중량부를 사용한다.
본 발명의 산화아연(C)은 가황 촉진제의 역할을 수행하는데, 가벼운 백색 분말의 형태로 사용한다. 물에는 거의 녹지 않는 성질을 가지나 묽은 산 및 진한 알칼리에도 녹는 양쪽성 산화물이다. 본 발명에서 산화아연(C)은 아크로니트릴-부타디엔 라텍스(A) 100 중량부에 대하여 2 내지 3 중량부를 사용한다.
본 발명에서 산화방지제(D)는 방향족아민류나 하이드로퀴논, 아미노산류 등을 사용할 수 있다. 그 구체적인 예로, N-(1,3-디메틸부틸)-N'-페닐-p-페닐렌디아민 (6PPD); 2-메르캅토벤즈이미다졸 화합물; 2-벤즈이미다졸티올; 디알킬화된 디페닐아민; 옥틸화된 디페닐아민; 니켈 디부틸디티오카르바메이트; N-이소프로필-N'-페닐-p-페닐렌디아민; 4'-디페닐-이소프로필-디아닐린; 2,2'-메틸렌비스(6-tert-부틸-4-메틸페놀); 파라핀 왁스 중에서 선택된 1 종 이상을 적용하여도 좋다. 본 발명에서 산화방지제(D)는 아크로니트릴-부타디엔 라텍스(A) 100 중량부에 대하여 2 내지 5 중량부를 사용한다.
탄산칼슘(E)은 석회석을 분쇄하여 가루를 만들어 체로 쳐서 가르거나 공기 중에서 고체입자가 자유침강할 때 속도의 차이를 이용하여 입자를 크기 또는 비중에 따라 나누는 조작에 의하여 얻는다. 또한, 석회유에 이산화탄소를 불어넣어 생기는 침전물을 여과·건조·미세분쇄하여 제조하기도 한다. 본 발명에서 탄산칼슘(E)은 보강제로서 배합되며, 본 발명에서 탄산칼슘(E)은 아크로니트릴-부타디엔 라텍스(A) 100 중량부에 대하여 20 내지 40 중량부를 사용한다.
본 발명은 로디닉산(F)을 선택적으로 함유할 수 있다. 본 발명의 로디닉산(rhodinic acid)은 자연계로부터 추출되는 물질 중의 하나로, 천연물이면서 식품 등의 첨가물이나 보존제로 사용되는 성분 중의 하나이다. 로디닉산의 분자량은 170.25 이고, 선형 분자식은 (CH3)2C=CHCH2CH2CH(CH3)CH2CO2H이다. 본 발명에서 로디닉산은 바닥재 조성물에 친환경성을 더욱 부여하는 것으로 판단된다. 즉, 로디닉산은 바닥 포장재에서 발생하는 VOC 배출량을 낮추는 효과를 가지는 것으로 판단된다. 본 발명에서 로디닉산(F)는 아크로니트릴-부타디엔 라텍스(A) 100 중량부에 대하여 0 내지 5 중량부로 사용한다.
이상의 성분으로 이루어지는 바닥재용 조성물은 물과 혼합하여 코코넛 섬유의 표면에 분사하여 사용한다. 이 때, 바닥재용 조성물 45 내지 50 중량%와 물 50 내지 55 중량%를 혼합하여 사용한다.
실시예 1 내지 5
아크로니트릴 50 중량부, 부타디엔 40 중량부, 제1 유화제로 제이켐상사에서 구입한 모노에탄올아민(MEA) 3 중량부, 및 아크릴 모노머로 메틸(메타)아크릴레이트 모노머 7 중량부를 시중에서 구입하여, 반응기에 투입하고 공중합시켜 아크로니트릴-부타디엔 라텍스 100 중량부(A)를 준비하였다. 이를 기준으로 하여 아래 표 1에서와 같이 다른 성분들을 혼합하여 실시예 1 내지 5에 따른 바닥재용 조성물을 제조하였다. 로디닉산(F)의 경우 실시예 5에서만 사용하였으며, 로디닉산 고형분(Sigma-Aldrich사, 제품번호 364428)을 다른 성분과 함께 추가하였다.
Figure PCTKR2017007532-appb-T000001
실시예 1 내지 5에서 제조된 바닥재용 조성물을 코코넛 섬유에 적용하기 위해 코코넛 섬유를 준비하였다. 준비된 코코넛 섬유를 한 가닥씩 노즐로 배출하면서 두 가닥을 서로 엮어 롤(roll) 형태로 만들어 놓고, 이 롤을 건조기에 넣어 120 내지 200 도로 30 분간 열처리를 하였다. 열처리된 코코넛 섬유 롤을 엮어진 방향의 반대 방향으로 회전하는 통에 일정 간격으로 컷팅하여 공급하였다. 회전하는 통 안에는 고압의 공기를 주입하여 컷팅된 섬유를 분해하였다. 분해된 코코넛 섬유는 컨베이어 벨트 위에 놓여진 상태로 이송시키되, 컨베이어 벨트의 상부에 분사 노즐을 설치하여 실시예 1 내지 5에서 제조된 바닥재용 조성물을 물과 1:1의 비율로 희석하여 컨베이어 벨트 위의 코코넛 섬유의 표면에 분사하여 코코넛 섬유의 표면에 물에 희석된 실시예 1 내지 5에 따른 바닥재용 조성물을 도포하였다.
이렇게 준비된 코코넛 섬유를 두 개의 압력 롤 사이에 투입하여 일정한 치수의 판재 모양으로 5 장의 코코넛 매트를 제조하였다. 제조된 매트를 각종 시험을 위해 가로, 세로, 두께를 100 x 200 x 10 mm 의 크기로 다섯 개의 시험편을 제작하였다.
제작된 시험편을 가지고 다음의 시험 항목에 대해 각종 물성에 대한 평가를 한국건설생활환경시험연구원에 의뢰하여 그 결과를 얻을 수 있었다.
(1) 인장강도(길이) : KS K 0743:2009 C.R.E, (단위: N) [(20.0 ± 2.0) ℃, (50 ± 10) % R.H.]
(2) 인장신도(길이) : KS K 0743:2009 C.R.E , (단위: %) [(20.0 ± 2.0) ℃, (50 ± 10) % R.H.]
(3) 미끄럼 저항성(습윤시) : KS F 2375:2001 (단위: BPN)
(4) 유해물질 용출 : 국민안전처고시 제2015-143호(2015. 12. 24) (단위: mg/kg)
(5) 촉진노출시험 : GR M 6004:2008 (제논 램프에 250 시간 노출 후 변퇴색 검사(Grey Scale)), (단위: 급) [(25.0 ± 2.0) ℃, (50 ± 10) % R.H.]
(6) 치수변화율 : KS I 3403:2014 (단위: %) (70.0 ± 1) ℃, 48 h
(7) 한계하강높이 : 안전인증기준부속서 2 (어린이 놀이기구) [산업통상자원부고시 제2015-0107호(2015. 06. 04)]
이상의 시험 항목에 따라 실시예 1 내지 5의 물성을 평가한 결과를 아래 표 2 및 표 3에 나타내었다.
Figure PCTKR2017007532-appb-T000002
Figure PCTKR2017007532-appb-T000003
위 표 1 및 표 2에서 알 수 있는 바와 같이, 본 발명에 따른 바닥재용 조성물을 코코넛 섬유에 도포하여 제조된 바닥재는 친환경적이고 필요한 각종 물성을 만족하므로 어린이용 놀이터 바닥, 운동장 트랙 등의 바닥재나 토목 또는 건설공사 등에 적용하는 고무 또는 우레탄 매트 등을 대체하기에 적합함을 알 수 있다.
이상에서와 같은 발명의 설명은 본 발명의 이해를 위하여 예를 들어 설명한 것에 불과할 뿐, 본 발명의 범위를 정하고자 하는 것이 아님을 주의하여야 한다. 본 발명의 범위는 아래 첨부된 청구범위에 의하여 정하여지며, 이 범위 내에서 본 발명의 단순한 변형이나 변경은 모두 본 발명의 범위 내에 속하는 것으로 이해되어야 한다.

Claims (5)

  1. (A) 아크릴로니트릴 20 내지 60 중량부, 부타디엔 40 내지 80 중량부, 제1 유화제 1 내지 3 중량부, 및 아크릴 모노머 4 내지 7 중량부로 이루어지는 아크로니트릴-부타디엔 라텍스 100 중량부;
    (B) 황, EZ, MZ, 제2 유화제가 3:1:1:0.1 의 비율로 혼합된 가황처리제 3 내지 6 중량부;
    (C) 산화아연 2 내지 3 중량부;
    (D) 산화방지제 2 내지 5 중량부; 및
    (E) 탄산칼슘 20 내지 40 중량부;
    를 포함하여 이루어지는 것을 특징으로 하는 바닥재용 조성물.
  2. 제1항에 있어서, (F)로디닉산을 5 중량부 이내로 더 포함하는 것을 특징으로 하는 바닥재용 조성물.
  3. 제1항 또는 제2항에 있어서, 상기 제1 유화제는 모노에탄올아민(MEA), 다이에탄올아민(DEA), 트리에탄올아민(TEA), 다이글리콜아민(DGA), 다이클로로헥실아민(DCHA), 올레인산 아민염, 톨오일(Tall oil) 아민염, 숙신산 아민염, 지방산, 폴리옥시에틸렌글리콜 지방산-에스테르, 폴리옥시에틸렌트리데실 에테르, 소르비탄올레이트 및 소듐설포네이트로 이루어진 군에서 선택된 1 종 이상의 유화제인 것을 특징으로 하는 바닥재용 조성물.
  4. 제1항 또는 제2항에 있어서, 상기 제2 유화제는 메틸알코올, 에틸알코올, 프로필알코올, 및 디메틸 폴리실록산(dimethylpolysiloxane)으로 이루어진 군에서 선택된 하나 또는 그 이상의 혼합물인 것을 특징으로 하는 바닥재용 조성물.
  5. 제1항 또는 제2항에 따른 바닥재용 조성물을 코코넛 섬유에 도포하고;
    도포된 코코넛 섬유를 압축하는;
    단계를 포함하는 것을 특징으로 하는 코코넛 섬유를 함유한 바닥재의 제조 방법.
PCT/KR2017/007532 2016-07-13 2017-07-13 코코넛 섬유를 함유한 바닥재용 조성물 및 이를 이용한 바닥재의 제조 방법 WO2018012906A1 (ko)