WO2017191774A1 - 異方性導電フィルム - Google Patents
異方性導電フィルム Download PDFInfo
- Publication number
- WO2017191774A1 WO2017191774A1 PCT/JP2017/016245 JP2017016245W WO2017191774A1 WO 2017191774 A1 WO2017191774 A1 WO 2017191774A1 JP 2017016245 W JP2017016245 W JP 2017016245W WO 2017191774 A1 WO2017191774 A1 WO 2017191774A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- anisotropic conductive
- conductive film
- conductive particles
- region
- film
- Prior art date
Abstract
Description
異方性導電フィルムとして、該規格配置領域内に、導電粒子が連続して所定数以上抜けている箇所が存在しない規格内領域が、異方性導電フィルムの短手方向の所定幅で異方性導電フィルムの長手方向に所定長で形成されている異方性導電フィルムを使用し、
該規格内領域を電子部品の端子列にアライメントする接続構造体の製造方法を提供する。
隣り合う規格領域の間の領域を、端子列と端子列の間の領域にアライメントすることが好ましい。
(異方性導電フィルムの全体構成)
本発明の異方性導電フィルムは、絶縁性樹脂バインダに導電粒子が規則的に配置されている領域(規則配置領域)を有するものであり、好ましくは、平面視において導電粒子が互いに離間し、規則的(例えば格子状)に配置されているものである。ここで、異方性導電フィルムの全面に1つの規則配置領域が広がっていてもよく、全面に複数の導電粒子群がそれぞれ規則配置領域として互いに離隔して配置されていてもよい。
導電粒子の規則的な配置としては、例えば、図1に示す異方性導電フィルム1Aのように、正方格子配列をあげることができる。この他、導電粒子の規則的な配置としては、長方格子、斜方格子、六方格子等の格子配列をあげることができる。導電粒子が所定間隔で直線状に並んだ粒子列を所定の間隔で並列させたものでもよい。また、図2に示す異方性導電フィルム1Bのように、正多角形を隙間無く並べた場合の正多角形(本実施例では正6角形)の頂点のうちの複数個を導電粒子2が占め、導電粒子2の配置として、導電粒子2a、2b、2c、2dからなる台形の繰り返しユニット5が観念できるようにしてもよい。なお、台形の繰り返しユニットは導電粒子の規則的な配置の一例であり、離隔したものであってもよく、また複数個の繰り返しユニットの集合が、離隔した導電粒子規則配置領域であってもよい。ここで、繰り返しユニット5は、最近接する導電粒子2の中心を順次結んで形成される導電粒子の配置の繰り返し単位であって、所定の規則性の繰り返しにより繰り返しユニット5が異方性導電フィルムの一面に及ぶものである。繰り返しユニット5自体における導電粒子の配置形状に特に制限はないが、繰り返しユニット5において導電粒子2が正多角形の一部を占めるように配置されていると、導電粒子の配置を把握しやすいので、所定の配置に対する導電粒子の抜けの有無を容易に判断することができる。なお、導電粒子の配置が把握し易いと、異方性導電フィルムの製造時や、異方性導電フィルムを用いて電子部品を接続した後の圧痕検査等の製品検査においてもそれぞれの作業が容易となり、時間を短縮することができ、工数削減を図ることができる。
導電粒子2としては、公知の異方性導電フィルムにおいて使用されているものを適宜選択して使用することができる。例えば、ニッケル、銅、銀、金、パラジウムなどの金属粒子、ポリアミド、ポリベンゾグアナミン等の樹脂粒子の表面をニッケルなどの金属で被覆した金属被覆樹脂粒子等を挙げることができる。配置される導電粒子の大きさは、好ましくは1μm以上30μm以下、より好ましくは1μm以上10μm以下、さらに好ましくは2μm以上6μm以下である。
導電粒子の最短粒子間距離は、導電粒子の平均粒子径の0.5倍以上が好ましい。この距離が短すぎると導電粒子相互の接触によりショートが起こりやすくなる。隣接する導電粒子の距離の上限は、バンプ形状やバンプピッチに応じて定めることができる。一例として、導電粒子を10個以上捕捉させるとすれば、平均粒径の50倍未満であればよく、40倍未満であれば好ましく。30倍未満であればより好ましい。
導電粒子の個数密度は、異方性導電フィルムの製造コストを抑制する点から、50000個/mm2以下が好ましく、35000個/mm2以下がより好ましく、30000個/mm2以下がさらに好ましい。一方、導電粒子の個数密度は、少なすぎると端子で導電粒子が十分に捕捉されないことによる導通不良が懸念されることから、30個/mm2以上あればよく、300個/mm2以上が好ましく、500個/mm2以上がより好ましく、800個/mm2以上がさらに好ましい。
絶縁性樹脂バインダ3としては、公知の異方性導電フィルムにおいて絶縁性樹脂バインダとして使用されている熱重合性組成物、光重合性組成物、光熱併用重合性組成物等を適宜選択して使用することができる。このうち熱重合性組成物としては、アクリレート化合物と熱ラジカル重合開始剤とを含む熱ラジカル重合性樹脂組成物、エポキシ化合物と熱カチオン重合開始剤とを含む熱カチオン重合性樹脂組成物、エポキシ化合物と熱アニオン重合開始剤とを含む熱アニオン重合性樹脂組成物等を挙げることができ、光重合性組成物としては、アクリレート化合物と光ラジカル重合開始剤とを含む光ラジカル重合性樹脂組成物等を挙げることができる。特に問題が生じないのであれば、複数種の重合性組成物を併用してもよい。併用例としては、熱カチオン重合性組成物と熱ラジカル重合性組成物の併用などが挙げられる。
絶縁性樹脂バインダ3の最低溶融粘度は、異方性導電フィルムの製造方法等に応じて適宜定めることができる。例えば、異方性導電フィルムの製造方法として、導電粒子を絶縁性樹脂バインダの表面に所定の配置で保持させ、その導電粒子を絶縁性樹脂バインダに押し込む方法を採用した場合、絶縁性樹脂バインダ3の最低溶融粘度は、フィルム成形性の観点から好ましくは1100Pa・s以上である。特に40~80℃でフィルム成形を可能とする点から、絶縁性樹脂バインダ3の60℃粘度は好ましくは3000~20000Pa・sである。また、後述するように、図5又は図6に示すように絶縁性樹脂バインダ3に押し込んだ導電粒子2の露出部分の周りに凹み3bを形成したり、図7に示すように絶縁性樹脂バインダ3に押し込んだ導電粒子2の直上に凹み3cを形成したりする点から、絶縁性樹脂バインダ3の最低溶融粘度は、1500Pa・s以上であればよく、好ましくは2000Pa・s以上、より好ましくは3000~15000Pa・s、さらに好ましくは3000~10000Pa・sである。この最低溶融粘度は、一例として回転式レオメータ(TA instruments社製)を用い、昇温速度が10℃/分、測定圧力が5gで一定に保持し、直径8mmの測定プレートを使用して求めることができる。また、40~80℃で絶縁性樹脂バインダ3に対して導電粒子2を押し込む工程を行う場合に、上述と同様に凹み3b又は3cの形成の点から、絶縁性樹脂バインダ3の60℃における粘度は、好ましくは3000~20000Pa・sである。この測定は最低溶融粘度と同様の測定方法で行い、温度が60℃の値を抽出して求めることができる。
絶縁性樹脂バインダ3の厚みLaは、好ましくは1μm以上60μm以下、より好ましくは1μm以上30μm以下、さらに好ましくは2μm以上15μm以下である。また、絶縁性樹脂バインダ3の厚みLaは、導電粒子2の平均粒子径Dとの関係では、それらの比(La/D)が0.6~10が好ましい。絶縁性樹脂バインダ3の厚みLaが大き過ぎると異方性導電接続時に導電粒子が位置ズレしやすくなり、端子における導電粒子の捕捉性が低下する。この傾向はLa/Dが10を超えると顕著である。そこでLa/Dは8以下がより好ましく、6以下が更により好ましい。反対に絶縁性樹脂バインダ3の厚みLaが小さすぎてLa/Dが0.6未満となると、導電粒子を絶縁性樹脂バインダ3によって所定の粒子分散状態あるいは所定の配列に維持することが困難となる。特に、接続する端子が高密度COGの場合、絶縁性接着層4の層厚Laと導電粒子2の粒子径Dとの比(La/D)は、好ましくは0.8~2である。
絶縁性樹脂バインダ3における導電粒子2の埋込状態については特に制限がないが、異方性導電フィルムを対向する部品の間で挟持し、加熱加圧することにより異方性導電接続を行う場合、図5、図6に示すように、導電粒子2を絶縁性樹脂バインダ3から部分的に露出させ、隣接する導電粒子2間の中央部における絶縁性樹脂バインダの表面3aの接平面3pに対して導電粒子2の露出部分の周りに凹み3bが形成されているか、又は図7に示すように、絶縁性樹脂バインダ3内に押し込まれた導電粒子2の直上の絶縁性樹脂バインダ部分に、前記と同様の接平面3pに対して凹み3cが形成され、導電粒子2の直上の絶縁性樹脂バインダ3の表面にうねりが存在するようにすることが好ましい。導電粒子2が対向する電子部品の電極間で挟持されて加熱加圧される際に生じる導電粒子2の扁平化に対し、図5に示した凹み3bがあることより、導電粒子2が絶縁性樹脂バインダ3から受ける抵抗が、凹み3bが無い場合に比して低減する。このため、対向する電極間において導電粒子2が挟持され易くなり、導通性能も向上する。また、絶縁性樹脂バインダ3を構成する樹脂のうち、導電粒子2の直上の樹脂の表面に凹み3c(図7)が形成されていることにより、凹み3cが無い場合に比して加熱加圧時の圧力が導電粒子2に集中し易くなり、電極において導電粒子2が挟持され易くなり、導通性能が向上する。
上述の凹み3bの効果を得やすくする点から、接平面3pからの導電粒子2の最深部の距離(以下、埋込量という)Lbと、導電粒子2の平均粒径Dとの比(Lb/D)(以下、埋込率という)は60%以上105%以下であることが好ましい。
本発明の異方性導電フィルムでは、導電粒子2を配置させている絶縁性樹脂バインダ3上に絶縁性接着層4が積層されていてもよい。
絶縁性接着層4と絶縁性樹脂バインダ3を挟んで反対側に第3の絶縁性樹脂層が設けられていてもよい。例えば、第3の絶縁性樹脂層をタック層として機能させることができる。絶縁性接着層4と同様に、電子部品の電極やバンプによって形成される空間を充填させるために設けてもよい。
(製造方法の概要)
本発明では、まず、絶縁性バインダに導電粒子が規則的に配置されている異方性導電フィルムの広幅の原反を入手し、もしくは作製し、次に、その異方性導電フィルムの原反における導電粒子の規則的な配置に対する抜けを調べ、規則的な配置に対して導電粒子が連続して所定数以上抜けている規格外の箇所が、接続を担う領域として使用されないようにするため、規格外の箇所を含む領域を除外するように広幅の原反を所定幅の異方性導電フィルムに裁断する(第1の態様)。あるいは、規格外の箇所がフィルムの短手方向の意図した位置になるように、広幅の原反を所定幅で長さ方向に裁断する(第2の態様)。また、第1の態様において規格外の箇所を除去した後の異方性導電フィルム(即ち、残余の異方性導電フィルム同士、あるいは規格外の箇所を除去したあとの別個の異方性導電フィルム同士)を繋ぎ合わせ、長さ5m以上の異方性導電フィルムを製造してもよい。
これらの転写型は機械加工、フォトリソグラフィ、印刷法等の公知の技術を用いて製造することができる。
また、導電粒子を所定の配列に配置する方法としては、転写側を用いる方法に代えて、二軸延伸フィルムを用いる方法等を使用してもよい。
本発明の異方性導電フィルムの製造方法の第1の態様では、個々のバンプ面積が比較的小さい接続構造体(COGなど、接続する端子配列が離隔して存在する一例でもある)に使用する異方性導電フィルムであっても個々のバンプ面積が比較的大きい接続構造体(FOGなど、接続する有効面積の長辺がフィルム幅と同一となる、端子配列が離隔して存在していないものの一例)に使用する異方性導電フィルムであっても、導電粒子が平面視にて規則的に配置されているもの、好ましくは、平面視にて導電粒子が互いに離間し、かつ規則的に配置されているものにおいて、導電粒子が規則的に配置されている領域(規則配置領域)から、導電粒子が抜けている箇所が所定数連続している規格外の箇所を除去する。言い換えると、抜けている箇所が接続後の導通安定性に問題を生じさせない範囲が点在しているに過ぎない領域は規格内領域とし、除去の対象としない。この問題を生じさせない範囲は、接続対象物により異なるが、一例として異方性導電フィルムをFOGに使用する場合、導電粒子が連続して1~20個、場合により1~209個抜けていても導通安定性に問題は生じ難い。ここで、導電粒子の連続抜け個数である209個という数字には、次に説明するような意味がある。即ち、異方性導電フィルムの幅が2mmで接続すべき端子幅が200μmという一般的に接続面積が広めとされるFOGの異方性導電接続条件(接続面積0.4μm2)において、15個×15個の四方格子で導電粒子を配置しようとした場合には、理想的には225個の導電粒子が接続面積0.4μm2中に存在することになるが、仮に209個の導電粒子が抜けたとしても、接続面積0.4μm2中に最低捕捉数として16個の導電粒子が端子内領域に存在することを意味する。ここで、捕捉される導電粒子数の16は、後述する捕捉される好ましい数値の下限である11個および20個の中間の値として設定している。そのため、導通の安定性が確保されやすくなる条件を見出すのに適した数値であると考える。このように、格子配列軸上の導電粒子個数(上記のように、この場合の格子配列軸の導電粒子個数は15個)よりも、捕捉される導電粒子が多くなる(この場合は16個)ということは、一つの端子において捕捉される導電粒子の個数が、ある方向の格子軸の全数よりも多いということになるので、捕捉された導電粒子は少なくとも2つの同一方向の配列軸に存在することになる。このように、少なくとも2つの格子軸に配置された導電粒子が捕捉されているということは、端子に捕捉された導電粒子の位置はある程度は離間していることが予想されるので、押圧のバランスを比較することができる。即ち、接続時の導電粒子の押し込みの良否を判定する条件が整う。なお、COGに使用する場合、連続して抜けている個数が1~20個であれば導通安定性に問題が生じ難く、15個以下、特に10個以下であれば更に問題が生じ難い。
本発明の異方性導電フィルムの製造方法では、異方性導電フィルムの生産性を高めるため、ある程度広い幅で異方性導電フィルムの長尺体を作成し、その後に前述した検査方法で導電粒子の抜けを確認し、好ましくは凝集などの不良部位も確認し、それらが所定幅の異方性導電フィルムに含まれないように裁断するか、あるいは、抜けのある箇所や凝集などの不良部位を異方性導電フィルム内に含めたまま、それらの位置が異方性導電フィルムの短手方向の意図した位置になるように所定幅の異方性導電フィルムに裁断することにより、実質的に抜けが問題とならない異方性導電フィルムを製造する。この異方性導電フィルムの製造工程では、不良箇所を記録するためにマーキングしてもよい。
本発明の異方性導電フィルムの製造方法では、所定の抜け部分を含む領域を切除した後の残りの異方性導電フィルムをつなぎ合わせ、抜けが含まれていても実用上抜けが問題にならない異方性導電フィルムとして提供することもできる。
本発明の異方性導電フィルムは、FPC、ICチップ、ICモジュールなどの第1電子部品と、FPC、リジッド基板、セラミック基板、ガラス基板、プラスチック基板などの第2電子部品とを熱又は光により異方性導電接続する際に好ましく適用することができる。また、ICチップやICモジュールをスタックして第1電子部品同士を異方性導電接続することもできる。このようにして得られる接続構造体も本発明の一部である。
限定されるものではない。
まず、実施例で使用する原盤を以下のとおり作成した。即ち、厚さ2mmのニッケルプレートを用意し、その50cm四方の領域に、六方格子パターンで円柱状の凸部(外径4μm、高さ4μm、中心間距離6μm)を形成し、凸部の面密度が32000個/mm2となる転写体原盤とした。
次に、50cm幅で50μm厚のポリエチレンテレフタレート基材フィルムを用意し、その基材フィルムに、アクリレート樹脂(M208、東亞合成(株))100質量部と光重合開始剤(IRGACURE184、BASFジャパン(株))2質量部とを含有する光硬化性樹脂組成物を、膜厚が30μmとなるように塗布した。
(フィルム状原盤への導電粒子の充填)
COG用に適した樹脂配合を決定するために、表1に示す配合の樹脂組成物を混合し、剥離処理したPETフィルムに塗布し、乾燥することにより、絶縁性バインダA1~A4から絶縁性樹脂層用フィルム(厚み4μm)及び絶縁性バインダBから第2絶縁性樹脂層用フィルム(厚み14μm)を20×30cmのサイズでそれぞれ作成した。
導電粒子が所定の条件で充填された裁断したフィルム状原盤の上に、上述の絶縁性樹脂層用フィルムを長手方向の長さを一致するようにし、幅方向はフィルム状原盤の中央部付近を含むように位置合わせして被せ、60℃、0.5MPaで押圧することにより導電粒子を転写させた。そして、フィルム状原盤から絶縁性樹脂層用フィルムを剥離し、絶縁性樹脂層用フィルム上の導電粒子を、加圧(押圧条件:60~70℃、0.5Mpa)することで絶縁性樹脂層用フィルムに押し込み、更に、第2絶縁性樹脂層用フィルムを導電粒子転写面にかぶせ積層し、これを裁断したフィルム状原盤5点で行うことにより、導電粒子が図8に示す状態で埋め込まれた異方性導電フィルム(ACF1~ACF4)を作製した。この場合、導電粒子の埋め込みは、押し込み条件でコントロールした。このように作成した、長手方向に30cmに裁断したフィルム状原盤5点を一セットとして導電粒子の埋め込み状態を観察したところ、埋め込まれた導電粒子の露出部分の周り又は埋め込まれた導電粒子の直上には表2に示すように凹みが、一セットで全て観察された。また、ACF4は、導電粒子の押し込みを行うとフィルム形状を維持できないものであった。従って、COG用には、ACF1~3を適用できることが分かった。なお、導電粒子の埋込状態は絶縁性バインダBを積層する前に確認した。また、ACF1~3について、CCDイメージセンサーで取得した画像を画像解析ソフト(WinROOF、三谷商事(株))を用いて導電粒子の抜けを観察し確認した。その結果、フィルムの長さ方向の抜けが連続した5個以下(粒子間距離の最大長33μm以内、後述するバンプ幅とバンプ間ギャップの合計38μmより小さい)、幅方向で7個以下(粒子間距離の最大長45μm以内)が組み合わさった抜けが複数存在していた。このフィルム長さ方向33μm×フィルム幅方向38μmの矩形領域を許容できる抜けと見なすことができる。従って、これよりも各寸法が小さいものは許容できる抜けであると認められる。なお、幅方向の抜けはバンプ長さ50μm以上に離間して存在していた。
次に、表3に示した実施例1~4及び比較例1の「導電粒子抜け状態(図4、10参照:LQ[μm]、LR[μm]、LQ/W[%]、LR/W[%])が反映されるように、1.8mm幅でスリットした。なお、得られなかった場合は、導電粒子の散布量等を調整することにより、各実施例及び比較例毎にACF1~ACF3の作製操作を繰り返すことで、それぞれ3種の異方性導電フィルムを作製した。各実施例及び比較例の異方性導電フィルムについて、LR(規格外の箇所(導電粒子が存在しない領域)の幅)の位置がフィルムの中央となるように、1.8mm幅にスリットした。ここで、規格外の箇所は、フィルム長さ方向33μmでフィルム幅方向38μmの大きさの許容できる抜けの矩形領域に対し、何れか一方の辺が大きく、導電粒子が存在しない矩形領域を含み、あるいは上記許容できる抜けの矩形領域が幅方向に50μm未満で接近している領域を含んでいる。
実施例1~4及び比較例1のぞれぞれで作製した3種の異方性導電フィルムを用いてCOG接続して得た接続構造体の導通特性(初期導通性並びに導通信頼性)を以下のように試験・評価した。
COG接続する電子部品として次の評価用IC(図10参照)とガラス基板を使用し、評価対象の異方性導電フィルムを、これらの評価用ICとガラス基板との間に挟み、加熱加圧(180℃、60MPa、5秒)して各評価用接続物を得た。この場合、異方性導電フィルムの長手方向とバンプの短手方向を合わせるとともに、異方性導電フィルムの一対の規格内領域がICチップの短手方向の両端部に位置するように接合した。得られた接続構造体の導通抵抗をデジタルマルチメータ(34401A、アジレント・テクノロジー(株))を用いて、4端子法(JIS K7194)で測定した。実用上、2Ω以下であることが望まれる。
(導通信頼性)
初期導通抵抗の測定に供した接続構造体を、85℃、湿度85%の恒温槽に500時間投入した後に再度導通抵抗を測定した。実用上、5Ω以下であることが望まれる。
IC外形:1.6mm(幅)×30.0mm(長さ)×0.2mm(厚さ)
金バンプ:15μm(高)×20μm(幅)×100μm(長)
(バンプ間ギャップ18μm、金バンプはIC外形幅方向の端部に、それぞれIC外形長手方向に沿って、1000個配列している。金バンプ配列間の距離は1000μmとなる。)
ガラス材質 コーニング社製1737F
外形 30mm×50mm
厚み 0.5mm
端子 ITO配線
測定に供した接続構造体について、全ての端子で初期導通抵抗が2Ω以下であり且つ導通信頼性試験後の導通抵抗が5Ω以下である場合を「良好」と評価し、それ以外(一つでも上記範囲を外れるバンプがある場合)を「不良」と評価した。得られた結果を表3に示す。
表1の絶縁性樹脂バインダに代えて表4のバインダを使用し、且つ導電粒子が所定の抜けの状態になるような条件を選択すること以外、COG対応の異方性導電フィルムの作成操作を繰り返すことにより、FOG用転写体原盤、FOG用フィルム状原盤、更に導電粒子が図8に示す状態で埋め込まれた異方性導電フィルム(ACF5~ACF8(表5参照))を作製した。この場合、導電粒子の埋め込み状態は、押し込み条件でコントロールした。その結果、埋め込まれた導電粒子の露出部分の周り又は埋め込まれた導電粒子の直上には表5に示すように凹みが観察された。これは、絶縁性バインダDを積層する前に確認した。なお、ACF8は、導電粒子の押し込みを行うとフィルム形状を維持できないものであった。従って、FOG用には、ACF5~7を適用できることが分かった。
次に、20×30cmに裁断された5枚1セットの異方性導電フィルム(ACF5~7)について、それぞれを幅2mmにスリットした。これらから、任意に5箇所(5枚で合計25箇所)抜き取ったフィルム20mmの領域で、フィルム長手方向200μm(端子の幅方向)において10個以上導電粒子が必ず存在したものを実施例5の異方性導電フィルムとして用意した。また、導電粒子が1又は2個の領域を有するようにする以外は同様の操作を繰り返することにより比較例2の異方性導電フィルムとして用意した。
実施例5及び比較例2のそれぞれで作製した3種の異方性導電フィルムを用いてFOG接続して得た接続構造体の導通特性(初期導通性並びに導通信頼性)を以下のように試験・評価した。
FOG接続する電子部品として次の評価用FPCとガラス基板を使用し、評価対象の異方性導電フィルムを、先に任意抜き取った25箇所がこれらの評価用FPCとガラス基板との間にくるようにそれぞれを裁断して挟み、加熱加圧(180℃、4.5MPa、5秒)して各評価用接続物を得た。この場合、異方性導電フィルムの長手方向とバンプの短手方向を合わせるように接合した。得られた接続構造体の導通抵抗をデジタルマルチメータ(34401A、アジレント・テクノロジー(株))を用いて、4端子法(JIS K7194)で測定した。実用上、2Ω以下であることが望まれる。
(導通信頼性)
初期導通抵抗の測定に供した接続構造体を、85℃、湿度85%の恒温槽に500時間投入した後に再度導通抵抗を測定した。実用上、5Ω以下であることが望まれる。
38μm厚のポリイミド基板にスズメッキされた8μm厚の400μmピッチのCu配線(L/S=200/200)が形成されたもの
ガラス材質 コーニング社製1737F
外形 30mm×50mm
厚み 0.5mm
端子 ITO配線
測定に供した接続構造体について、初期導通抵抗が2Ω以下であり且つ導通信頼性試験後の導通抵抗が5Ω以下である場合を「良好」と評価し、それ以外を「不良」と評価した。その結果、実施例5の3種の異方性導電フィルムを用いて作製した接続構造体の導通特性は良好であったが、一方、比較例2の異方性導電フィルムを用いて作製した接続構造体は、規則配置領域内に規格外領域が実施例5に比べて存在していたため、導通特性が不良という評価であった。
1P 異方性導電フィルムの短手方向の幅の端部
2、2a、2b、2c、2d 導電粒子
2t 導電粒子の頂部
2X 導電粒子の抜け
2Y 抜けが連続している部分
3 絶縁性樹脂バインダ
3a 隣接する導電粒子間の中央部における絶縁性樹脂バインダの表面
3b、3c 凹み
3p 接平面
4 絶縁性接着層
5 繰り返しユニット
10 バンプ、端子
11 端子列
12 電子部品
D 導電粒子の平均粒子径
L1 格子軸
La 絶縁性樹脂バインダの厚み
Q 規格内領域
R 規格外の箇所を含む領域
S 任意の領域
Claims (10)
- 絶縁性樹脂バインダに導電粒子が規則的に配置されている規則配置領域を有する、長さが5m以上の異方性導電フィルムであって、該規則配置領域内に、導電粒子が連続して所定数以上抜けている箇所が存在しない規格内領域が、異方性導電フィルムの短手方向の所定幅で、異方性導電フィルムの長手方向に所定長以上で存在する異方性導電フィルム。
- 該規則配置領域と該規格内領域とが一致している請求項1記載の異方性導電フィルム。
- 導電粒子が連続して所定数以上抜けている箇所である規格外の箇所が存在する請求項1記載の異方性導電フィルム。
- 異方性導電フィルムの全幅で長手方向200μmの任意に選択した領域において、導電粒子が10個以上存在する請求項1~3のいずれかに記載の異方性導電フィルム。
- 異方性導電フィルムの短手方向の少なくとも端部領域に沿って規格内領域を有する請求項1~4のいずれかに記載の異方性導電フィルム。
- 異方性導電フィルムがリールに巻かれた巻装体である請求項1~5のいずれかに記載の異方性導電フィルム。
- 絶縁性樹脂バインダに導電粒子が規則的に配置されている異方性導電フィルムの広幅原反を、規則的な配置に対して導電粒子が連続して所定数以上抜けている規格外の箇所が含まれないように、もしくは規格外の箇所がフィルムの短手方向の意図した位置になるように、長さ方向に裁断し、長さ5m以上の異方性導電フィルムとする異方性導電フィルムの製造方法。
- 絶縁性樹脂バインダに導電粒子が規則的に配置されている規格配置領域を有する異方性導電フィルムから、導電粒子が連続して所定数以上抜けている規格外の箇所を除去し、除去後の異方性導電フィルムをつなぎ合わせ、長さ5m以上の異方性導電フィルムとする異方性導電フィルムの製造方法。
- 端子列を有する第1電子部品と端子列を有する第2電子部品とを、絶縁性樹脂バインダに導電粒子が規則的に配置されている規格配置領域を有する異方性導電フィルムを介して熱圧着することにより第1の電子部品と第2の電子部品の端子列同士を異方性導電接続する接続構造体の製造方法であって、
異方性導電フィルムとして、該規格配置領域内に、導電粒子が連続して所定数以上抜けている箇所が存在しない規格内領域が、異方性導電フィルムの短手方向の所定幅で異方性導電フィルムの長手方向に所定長で形成されている異方性導電フィルムを使用し、
該規格内領域を電子部品の端子列にアライメントする接続構造体の製造方法。 - 第1電子部品及び第2電子部品がそれぞれ複数の端子列を有し、異方性導電フィルムに規格内領域が並列して形成されている場合に、
隣り合う規格領域の間の領域を、端子列と端子列の間の領域にアライメントする請求項9記載の接続構造体の製造方法。