WO2017169164A1 - アルカリ二次電池用の負極、この負極を含むアルカリ二次電池及びこの負極の製造方法 - Google Patents
アルカリ二次電池用の負極、この負極を含むアルカリ二次電池及びこの負極の製造方法 Download PDFInfo
- Publication number
- WO2017169164A1 WO2017169164A1 PCT/JP2017/004794 JP2017004794W WO2017169164A1 WO 2017169164 A1 WO2017169164 A1 WO 2017169164A1 JP 2017004794 W JP2017004794 W JP 2017004794W WO 2017169164 A1 WO2017169164 A1 WO 2017169164A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- negative electrode
- powder
- mass
- secondary battery
- hydrogen storage
- Prior art date
Abstract
ニッケル水素二次電池2は、セパレータ28、正極24及び負極26からなる電極群22を備え、負極26は、負極芯体と、この負極芯体に保持されている負極合剤と、を備え、この負極合剤は、水素吸蔵合金の粒子からなる水素吸蔵合金粉末、導電剤の粉末及び負極添加剤の粉末を含んでおり、この導電剤は、一次粒子が中空シェル状の構造を持つ中空カーボンブラックであり、この負極添加剤は、フッ素系アニオン性界面活性剤である。
Description
本発明は、アルカリ二次電池用の負極、この負極を含むアルカリ二次電池及びこの負極の製造方法に関する。
アルカリ二次電池の一種としてニッケル水素二次電池が知られている。このニッケル水素二次電池は、ニッケルカドミウム二次電池に比べて高容量で、且つ、環境安全性にも優れているという点から、各種のポータブル機器やハイブリッド電気自動車等の各種機器に使用されるようになっており、用途が拡大している。このように用途が拡大していることから、ニッケル水素二次電池には、より高性能化が望まれている。
ニッケル水素二次電池に求められる高度化すべき性能の一つとして、低温放電特性がある。ここで、低温放電特性とは、低温環境下でどの程度放電できるかの度合いであり、低温放電特性に優れる電池とは、低温環境下であっても高容量の放電が可能な電池を指す。
ニッケル水素二次電池においては、低温放電特性を改善するために多くの研究がなされている。低温放電特性が改善された電池としては、例えば、特許文献1に示されるようなニッケル水素二次電池が知られている。このニッケル水素二次電池は、水素吸蔵合金の表面を改質することにより、低温放電特性の改善が図られている。
ところで、上記したような各種機器においては用途の拡大にともない、使用条件もより過酷となっており、それにともない、それら機器に搭載されるニッケル水素二次電池には、低温放電特性の更なる改善が求められている。
特許文献1に代表されるような従来のニッケル水素二次電池では、低温放電特性が改善されてはいるものの、近年の過酷な使用条件に十分に対応できていないのが現状である。つまり、ニッケル水素二次電池の低温放電特性は、未だ十分なものとはなっていない。
本発明は、上記の事情に基づいてなされたものであり、その目的とするところは、低温放電特性の更なる向上を図ることができるアルカリ二次電池用の負極、この負極を含むアルカリ二次電池及びこの負極の製造方法を提供することにある。
本発明によれば、負極芯体と、前記負極芯体に保持されている負極合剤と、を備え、前記負極合剤は、水素吸蔵合金の粒子からなる水素吸蔵合金粉末、導電剤の粉末及び負極添加剤の粉末を含んでおり、前記導電剤は、一次粒子が中空シェル状の構造を持つ中空カーボンブラックであり、前記負極添加剤は、フッ素系アニオン性界面活性剤である、アルカリ二次電池用の負極が提供される。
前記中空カーボンブラックからなる前記導電剤の粉末は、前記水素吸蔵合金粉末100質量部に対し、0.25質量部以上、0.5質量部以下添加されている構成とすることが好ましい。
前記フッ素系アニオン性界面活性剤からなる前記負極添加剤の粉末は、前記水素吸蔵合金粉末100質量部に対し、0.01質量部以上、0.05質量部以下添加されている構成とすることが好ましい。
前記フッ素系アニオン性界面活性剤は、パーフルオロブタンスルホン酸塩である構成とすることが好ましい。
また、本発明によれば、容器と、前記容器内にアルカリ電解液とともに収容された電極群とを備え、前記電極群は、セパレータを介して重ね合わされた正極及び負極からなり、前記負極は、上記した何れかの構成のアルカリ二次電池用の負極である、アルカリ二次電が提供される。
更に、本発明によれば、水素吸蔵合金粉末、導電剤の粉末、負極添加剤の粉末及び水をそれぞれ所定量だけ準備する準備工程と、準備された前記水素吸蔵合金粉末、前記導電剤の粉末、前記負極添加剤の粉末及び前記水を混練して負極合剤のペーストを製造するペースト製造工程と、前記ペースト製造工程で得られた負極合剤のペーストを負極芯体に塗着させるペースト塗着工程と、負極芯体に塗着されている負極合剤のペーストを乾燥させる乾燥工程と、を備えており、前記導電剤は、一次粒子が中空シェル状の構造を持つ中空カーボンブラックであり、前記負極添加剤は、フッ素系アニオン性界面活性剤である、アルカリ二次電池用の負極の製造方法が提供される。
本発明のアルカリ二次電池用の負極は、負極合剤に、水素吸蔵合金の粒子からなる水素吸蔵合金粉末、導電剤の粉末及び負極添加剤の粉末を含んでおり、この導電剤は、一次粒子が中空シェル状の構造を持つ中空カーボンブラックであり、負極添加剤は、フッ素系アニオン性界面活性剤である。この構成により、負極全体としての電極反応面積が従来よりも増加され、それにともない、低温環境下においても電気化学反応をより活発化させることができる。このため、本発明の負極を含むアルカリ二次電池は、低温放電特性の更なる向上を図ることができる。
また、本発明のアルカリ二次電池用の負極の製造方法は、水素吸蔵合金粉末、一次粒子が中空シェル状の構造を持つ中空カーボンブラックからなる導電剤の粉末、フッ素系アニオン性界面活性剤からなる負極添加剤の粉末及び水を混練して負極合剤のペーストを製造するペースト製造工程を含んでおり、この工程により、中空カーボンブラックが均一に分散されるとともに極めて微細な気泡が多数発生し、得られる負極の電極反応面積の増加に貢献する。このため、本発明のアルカリ二次電池用の負極の製造方法によれば、低温放電特性に優れるアルカリ二次電池用の負極を容易に製造することができる。
以下、本発明に係るニッケル水素二次電池(以下、単に電池と称する。)2を、図面を参照して説明する。
本発明が適用される電池2としては特に限定されないが、例えば、図1に示すAAサイズの円筒型の電池2に本発明を適用した場合を例に説明する。
図1に示すように、電池2は、上端が開口した有底円筒形状をなす外装缶10を備えている。外装缶10は導電性を有し、その底壁35は負極端子として機能する。外装缶10の開口には、封口体11が固定されている。この封口体11は、蓋板14及び正極端子20を含み、外装缶10を封口するとともに正極端子20を提供する。蓋板14は、導電性を有する円板形状の部材である。外装缶10の開口内には、蓋板14及びこの蓋板14を囲むリング形状の絶縁パッキン12が配置され、絶縁パッキン12は外装缶10の開口縁37をかしめ加工することにより外装缶10の開口縁37に固定されている。すなわち、蓋板14及び絶縁パッキン12は互いに協働して外装缶10の開口を気密に閉塞している。
ここで、蓋板14は中央に中央貫通孔16を有し、そして、蓋板14の外面上には中央貫通孔16を塞ぐゴム製の弁体18が配置されている。更に、蓋板14の外面上には、弁体18を覆うようにしてフランジ付き円筒形状をなす金属製の正極端子20が電気的に接続されている。この正極端子20は弁体18を蓋板14に向けて押圧している。なお、正極端子20には、図示しないガス抜き孔が開口されている。
通常時、中央貫通孔16は弁体18によって気密に閉じられている。一方、外装缶10内にガスが発生し、その内圧が高まれば、弁体18は内圧によって圧縮され、中央貫通孔16を開き、その結果、外装缶10内から中央貫通孔16及び正極端子20のガス抜き孔(図示せず)を介して外部にガスが放出される。つまり、中央貫通孔16、弁体18及び正極端子20は電池のための安全弁を形成している。
外装缶10には、電極群22が収容されている。この電極群22は、それぞれ帯状の正極24、負極26及びセパレータ28からなり、これらは正極24と負極26との間にセパレータ28が挟み込まれた状態で渦巻状に巻回されている。すなわち、セパレータ28を介して正極24及び負極26が互いに重ね合わされている。電極群22の最外周は負極26の一部(最外周部)により形成され、外装缶10の内周壁と接触している。すなわち、負極26と外装缶10とは互いに電気的に接続されている。
そして、外装缶10内には、電極群22の一端と蓋板14との間に正極リード30が配置されている。詳しくは、正極リード30は、その一端が正極24に接続され、その他端が蓋板14に接続されている。従って、正極端子20と正極24とは、正極リード30及び蓋板14を介して互いに電気的に接続されている。なお、蓋板14と電極群22との間には円形の上部絶縁部材32が配置され、正極リード30は上部絶縁部材32に設けられたスリット39の中を通されて延びている。また、電極群22と外装缶10の底部との間にも円形の下部絶縁部材34が配置されている。
更に、外装缶10内には、所定量のアルカリ電解液(図示せず)が注入されている。このアルカリ電解液は、電極群22に含浸され、正極24と負極26との間での充放電の際の電気化学反応(充放電反応)を進行させる。このアルカリ電解液としては、KOH、NaOH及びLiOHのうちの少なくとも一種を溶質として含むアルカリ電解液を用いることが好ましい。
セパレータ28の材料としては、例えば、ポリアミド繊維製不織布、ポリエチレンやポリプロピレンなどのポリオレフィン繊維製不織布に親水性官能基を付与したものを用いることができる。
正極24は、多孔質構造を有する導電性の正極基材と、この正極基材の空孔内に保持された正極合剤とからなる。
このような正極基材としては、例えば、ニッケル発泡体(ニッケルフォーム)のシートを用いることができる。
正極合剤は、正極活物質粒子と、結着剤とを含む。なお、正極合剤には、必要に応じて正極補助添加剤を添加しても構わない。この結着剤は、正極活物質粒子を互いに結着させるとともに、正極活物質粒子を正極基材に結着させる働きをなす。ここで、結着剤としては、例えば、カルボキシメチルセルロース、メチルセルロース、PTFE(ポリテトラフルオロエチレン)ディスパージョン、HPC(ヒドロキシプロピルセルロース)ディスパージョンなどを用いることができる。
正極活物質粒子としては、ニッケル水素二次電池用として一般的に用いられている水酸化ニッケル粒子が用いられる。この水酸化ニッケル粒子は、高次化されている水酸化ニッケル粒子を採用することが好ましい。
また、上記した水酸化ニッケル粒子は、Coを固溶しているものを用いることが好ましい。この固溶成分としてのCoは、正極活物質粒子間の導電性の向上に寄与し、充電受け入れ性を改善する。ここで、水酸化ニッケル粒子中に固溶されているCoの含有量は、少ないと充電受け入れ性を改善する効果が小さく、逆に多すぎると水酸化ニッケル粒子の粒成長を阻害するようになる。このため、水酸化ニッケル粒子は、固溶成分としてのCoを0.5質量%以上5.0質量%以下含んでいる態様のものを用いることが好ましい。
なお、上記した水酸化ニッケル粒子には、更に、Znを固溶させることが好ましい。ここで、Znは、充放電サイクルの進行に伴う正極の膨化を抑制し、電池のサイクル寿命特性の向上に寄与する。
水酸化ニッケル粒子に固溶されるZnの含有量は、水酸化ニッケルに対して、2.0質量%以上、5.0質量%以下とすることが好ましい。
また、上記した水酸化ニッケル粒子は、表面をコバルト化合物からなる表面層で覆うことが好ましい。表面層としては、3価以上に高次化されたコバルト化合物からなる高次コバルト化合物層を採用することが好ましい。
上記した高次コバルト化合物層は、導電性に優れており、導電性ネットワークを形成する。この高次コバルト化合物層としては、3価以上に高次化されたオキシ水酸化コバルト(CoOOH)などのコバルト化合物からなる層を採用することが好ましい。
上記したような正極活物質粒子は、ニッケル水素二次電池用として一般的に用いられている製造方法により製造される。
ついで、正極24は、例えば、以下のようにして製造することができる。
まず、正極活物質粒子、水及び結着剤を含む正極合剤スラリーを調製する。調製された正極合剤スラリーは、例えば、発泡ニッケルシートに充填され、乾燥させられる。乾燥後、水酸化ニッケル粒子等が充填された発泡ニッケルシートは、ロール圧延されてから裁断され、正極24が作製される。
まず、正極活物質粒子、水及び結着剤を含む正極合剤スラリーを調製する。調製された正極合剤スラリーは、例えば、発泡ニッケルシートに充填され、乾燥させられる。乾燥後、水酸化ニッケル粒子等が充填された発泡ニッケルシートは、ロール圧延されてから裁断され、正極24が作製される。
次に、負極26について説明する。
負極26は、帯状をなす導電性の負極芯体を有し、この負極芯体に負極合剤が保持されている。
負極26は、帯状をなす導電性の負極芯体を有し、この負極芯体に負極合剤が保持されている。
負極芯体は、貫通孔が分布されたシート状の金属材からなり、例えば、パンチングメタルシートを用いることができる。負極合剤は、負極芯体の貫通孔内に充填されるばかりでなく、負極芯体の両面上にも層状にして保持されている。
負極合剤は、負極活物質としての水素を吸蔵及び放出可能な水素吸蔵合金粒子、導電剤、結着剤及び負極添加剤を含む。また、負極合剤には、必要に応じて負極補助添加剤を添加しても構わない。
上記した結着剤は水素吸蔵合金粒子、導電剤等を互いに結着させると同時に水素吸蔵合金粒子、導電剤等を負極芯体に結着させる働きをなす。ここで、結着剤としては、特に限定されるものではなく、例えば、親水性若しくは疎水性のポリマー等ニッケル水素二次電池用として一般的に用いられている結着剤を用いることができる。
水素吸蔵合金粒子における水素吸蔵合金としては、特に限定されるものではなく、ニッケル水素二次電池用として一般的に用いられている水素吸蔵合金を採用することができる。ここで、好ましい水素吸蔵合金としては、希土類元素、Mg及びNiを含む希土類-Mg-Ni系水素吸蔵合金が用いられる。
導電剤としては、一次粒子が中空シェル状の構造を持つ中空カーボンブラックが用いられる。ここで、カーボンブラックとは、直径が3~500nm程度の炭素の微粒子のことをいう。一般的なカーボンブラックは、一次粒子の内部は稠密である。しかしながら、本発明で用いる中空カーボンブラックは、一次粒子が内部に空隙を有している。つまり、この空隙を除いたカーボンの部分が殻のような形状をなしている。よって、本発明においては、このように、カーボンが殻のような形状をなし内部に空隙を有する構造を中空シェル状の構造ということとする。
上記した中空カーボンブラックとしては、空隙率が、55%以上であるものを用いることが好ましく、より好ましくは、60%以上、80%以下のものを用いる。また、この中空カーボンブラックとしては、BET法で求めた比表面積が、700m2/g以上、3000m2/g以下のものを用いることが好ましく、より好ましくは、800m2/g以上、1500m2/g以下のものを用いる。
このような中空シェル状の構造を持つ中空カーボンブラックを導電剤として用いると、負極全体としての比表面積を増加させることができ、それにともない、電極反応面積を増加させることができる。このため、斯かる導電剤を用いるとニッケル水素二次電池の低温放電特性の向上に貢献する。
この中空カーボンブラックからなる導電剤の粉末は、上記した水素吸蔵合金粒子からなる水素吸蔵合金粉末100質量部に対し、0.25質量部以上、0.50質量部以下添加されていることが好ましい。中空カーボンブラックからなる導電剤の粉末の添加量が、0.25質量部未満になると、導電性が不十分となり低温放電特性が低下する。一方、中空カーボンブラックからなる導電剤の粉末の添加量が、0.50質量部を超えると、低温放電特性の向上の効果は飽和し、しかも、中空カーボンブラックの嵩密度の低さから、得られる負極板の厚みが増し、外装缶内への収納が困難となる。
次に、負極添加剤としては、フッ素系アニオン性界面活性剤が用いられる。このフッ素系アニオン性界面活性剤は、負極を製造する過程で負極合剤ペースト内において、上記した導電剤の粉末を均一に分散させるとともに、μmオーダーの極めて微細な気泡を形成する。斯かる極めて微細な気泡は、負極合剤が乾燥された後にも微細な空隙として残存し、負極内の電極反応面積の増加に寄与する。
このフッ素系アニオン性界面活性剤は、炭化水素鎖の界面活性剤に比べて耐アルカリ性に優れており、電池内で分解して電池反応に悪影響を及ぼさないので好適である。
このようなフッ素系アニオン性界面活性剤としては、パーフルオロブタンスルホン酸塩を用いることが好ましい。そして、このパーフルオロブタンスルホン酸塩としては、パーフルオロブタンスルホン酸カリウム、パーフルオロブタンスルホン酸ナトリウム、パーフルオロブタンスルホン酸リチウム、パーフルオロブタンスルホン酸セシウム、パーフルオロブタンスルホン酸ルビジウム等を用いることが好ましい。
このフッ素系アニオン性界面活性剤からなる負極添加剤の粉末は、上記した水素吸蔵合金粒子からなる水素吸蔵合金粉末100質量部に対し、0.01質量部以上、0.05質量部以下添加されていることが好ましい。フッ素系アニオン性界面活性剤からなる負極添加剤の粉末の添加量が、0.01質量部未満になると、上記した導電剤の粉末を分散させる能力、すなわち分散性が不十分となる。一方、フッ素系アニオン性界面活性剤からなる負極添加剤の粉末の添加量が、0.05質量部を超えると、負極を製造する過程で負極合剤ペースト内において、mmオーダーの比較的大きな気泡を形成してしまう。斯かる比較的大きな気泡は、負極合剤が乾燥された後にも残存し、負極表面に大きな凹凸を形成してしまう。このような凹凸は、電池の内部短絡の原因となるおそれがある。また、フッ素系アニオン性界面活性剤は、導電性が無く、その添加量が増えると負極の放電反応を阻害する。よって、フッ素系アニオン性界面活性剤からなる負極添加剤の粉末の添加量は、0.05質量部以下とすることが好ましい。
負極26は、例えば、以下のようにして製造することができる。
まず、水素吸蔵合金粒子からなる水素吸蔵合金粉末、一次粒子が中空シェル状の構造を持つ中空カーボンブラックからなる導電剤の粉末、フッ素系アニオン性界面活性剤からなる負極添加剤の粉末及び水をそれぞれ所定量だけ準備する(準備工程)。
まず、水素吸蔵合金粒子からなる水素吸蔵合金粉末、一次粒子が中空シェル状の構造を持つ中空カーボンブラックからなる導電剤の粉末、フッ素系アニオン性界面活性剤からなる負極添加剤の粉末及び水をそれぞれ所定量だけ準備する(準備工程)。
次いで、準備された水素吸蔵合金粉末、導電剤の粉末、結着剤及び水を混練して負極合剤ペーストを製造する(ペースト製造工程)。このペースト製造工程における混練作業により、負極添加剤の作用により、負極合剤ペースト中に導電剤の粉末が均一に分散させられるとともに、極めて微細な気泡が発生する。
得られた負極合剤ペーストは負極芯体に塗着され(ペースト塗着工程)、その後、乾燥させられる(乾燥工程)。
負極合剤ペーストが乾燥した後、水素吸蔵合金粒子等を含む負極合剤が付着した負極芯体はロール圧延及び裁断が施され、これにより負極26が作製される。
以上のようにして作製された正極24及び負極26は、セパレータ28を介在させた状態で、渦巻き状に巻回され、これにより電極群22が形成される。
このようにして得られた電極群22は、外装缶10内に収容される。引き続き、当該外装缶10内には所定量のアルカリ電解液が注入される。その後、電極群22及びアルカリ電解液を収容した外装缶10は、正極端子20を備えた封口体11により封口され、本発明に係る電池2が得られる。得られた電池2は、初期活性化処理が施され、使用可能状態とされる。
[実施例]
1.電池の製造
(実施例1)
1.電池の製造
(実施例1)
(1)正極の作製
Niに対してZnが2.5質量%、Coが1.0質量%となるように、硫酸ニッケル、硫酸亜鉛及び硫酸コバルトを計量し、これらを、アンモニウムイオンを含む1Nの水酸化ナトリウム水溶液に加え、混合水溶液を調製した。得られた混合水溶液を攪拌しながら、この混合水溶液に10Nの水酸化ナトリウム水溶液を徐々に添加して反応させ、ここでの反応中のpHを13~14に安定させて、水酸化ニッケルを主体とし、Zn及びCoを固溶した水酸化ニッケル粒子からなるベース粒子を生成させた。
Niに対してZnが2.5質量%、Coが1.0質量%となるように、硫酸ニッケル、硫酸亜鉛及び硫酸コバルトを計量し、これらを、アンモニウムイオンを含む1Nの水酸化ナトリウム水溶液に加え、混合水溶液を調製した。得られた混合水溶液を攪拌しながら、この混合水溶液に10Nの水酸化ナトリウム水溶液を徐々に添加して反応させ、ここでの反応中のpHを13~14に安定させて、水酸化ニッケルを主体とし、Zn及びCoを固溶した水酸化ニッケル粒子からなるベース粒子を生成させた。
得られたベース粒子を10倍の量の純水で3回洗浄した後、脱水及び乾燥処理を行った。なお、得られたベース粒子につき、レーザー回折・散乱式粒径分布測定装置を用いて粒径を測定した結果、斯かるベース粒子の体積平均粒径(MV)は8μmであった。
次に、得られたベース粒子を硫酸コバルト水溶液中に投入し、この硫酸コバルト水溶液を撹拌しながら、1mol/lの水酸化ナトリウム水溶液を徐々に滴下して反応させ、ここでの反応中のpHを11に維持しながら沈殿物を生成させた。ついで、生成した沈殿物を濾別して、純水で洗浄したのち、真空乾燥させた。これにより、ベース粒子38を核として、この核の表面に5質量%の水酸化コバルトの層を備えた中間生成物粒子を得た。なお、水酸化コバルトの層の厚さは約0.1μmであった。
ついで、この中間生成物粒子を、25質量%の水酸化ナトリウム水溶液中に投入した。ここで、中間生成物粒子からなる粉末の質量をPとし、水酸化ナトリウム水溶液の質量をQとした場合、これらの質量比が、P:Q=1:10となるように設定した。そして、この中間生成物粒子の粉末が加えられた水酸化ナトリウム水溶液を撹拌しながら温度が85℃で一定のまま8時間保持する加熱処理を施した。
上記した加熱処理を経た中間生成物粒子からなる粉末を純水で洗浄し、65℃の温風を当てて乾燥させた。これにより、Zn及びCoが固溶した水酸化ニッケル粒子からなるベース粒子の表面に高次化されたコバルト酸化物からなる表面層を有した正極活物質粒子からなる正極活物質粉末を得た。
上記した加熱処理を経た中間生成物粒子からなる粉末を純水で洗浄し、65℃の温風を当てて乾燥させた。これにより、Zn及びCoが固溶した水酸化ニッケル粒子からなるベース粒子の表面に高次化されたコバルト酸化物からなる表面層を有した正極活物質粒子からなる正極活物質粉末を得た。
次に、上記したように作製した水酸化ニッケル粒子からなる正極活物質粉末95質量部に、酸化亜鉛の粉末3.0質量部と、水酸化コバルトの粉末2.0質量部と、結着剤としてのヒドロキシプロピルセルロースの粉末を0.2質量%含む水50.0質量部とを添加して混練して正極合剤スラリーを調製した。
ついで、この正極合剤スラリーを正極基材としてのシート状のニッケル発泡体(ニッケルフォーム)に充填した。ここで、ニッケル発泡体としては、面密度(目付)が約600g/m2、多孔度が95%、厚みが約2mmであるものを用いた。
正極合剤のスラリーが充填されたニッケル発泡体を乾燥後、正極合剤が充填されたニッケル発泡体を、以下の式(1)で計算される正極活物質の充填密度が2.9g/cm3となるように調整して圧延した後、所定の寸法に切断して、非焼結式ニッケル極からなるAAサイズ用の正極24を得た。
正極活物質の充填密度[g/cm3]=正極合剤質量[g]÷(電極高さ[cm]×電極長さ[cm]×電極厚み[cm]-ニッケル発泡体の質量[g]÷ニッケルの比重[g/cm3])・・・(1)
(2)負極の作製
La、Sm、Mg、Ni、Alの各金属材料を所定のモル比となるように混合した後、誘導溶解炉に投入して溶解させ、これを冷却してインゴットを作製した。
La、Sm、Mg、Ni、Alの各金属材料を所定のモル比となるように混合した後、誘導溶解炉に投入して溶解させ、これを冷却してインゴットを作製した。
ついで、このインゴットに対し、温度1000℃のアルゴンガス雰囲気下にて10時間加熱する熱処理を施して均質化した後、アルゴンガス雰囲気下で機械的に粉砕して、希土類-Mg-Ni系水素吸蔵合金粉末を得た。得られた希土類-Mg-Ni系水素吸蔵合金粉末について、レーザー回折・散乱式粒径分布測定装置(装置名:Microtrac社製SRA-150)により粒径分布を測定した。その結果、質量基準による積算が50%にあたる平均粒径は65μmであった。
この水素吸蔵合金粉末の組成を高周波プラズマ分光分析法(ICP)によって分析したところ、組成は、La0.30Sm0.70Mg0.10Ni3.33Al0.17であった。また、この水素吸蔵合金粉末についてX線回折測定(XRD測定)を行ったところ、結晶構造は、いわゆる超格子構造のCe2Ni7型であった。
得られた水素吸蔵合金の粉末100質量部に対し、一次粒子が中空シェル状の構造を持つ中空カーボンブラックからなる導電剤の粉末0.50質量部、パーフルオロブタンスルホン酸カリウムの粉末0.01質量部、スチレンブタジエンゴムの粉末1.0質量部、ポリアクリル酸ナトリウムの粉末0.25質量部、カルボキシメチルセルロースの粉末0.05質量部及び水20質量部を添加して25℃の環境下において混練し、負極合剤ペーストを調製した。
ここで、上記した中空カーボンブラックとしては、ライオンスペシャリティケミカルズ社製のケッチェンブラック(登録商標)を用いた。この中空カーボンブラックの物性値としては、BET法による比表面積が1270m2/g、空隙率が80%、一次粒子径が34.0nmである。
この負極合剤ペーストを負極基板としてのパンチングメタルシートの両面に均等、且つ、厚さが一定となるように塗布した。また、貫通孔内にも負極合剤ペーストは充填されている。なお、このパンチングメタルシートは、貫通孔が多数あけられた鉄製の帯状体であり、厚さが60μmであり、その表面にはニッケルめっきが施されている。
負極合剤ペーストの乾燥後、負極合剤を保持したパンチングメタルシートを、以下の式(2)で計算される水素吸蔵合金の充填密度(以下、水素吸蔵合金充填密度という)が5.5g/cm3となるように調整して圧延した後、所定の寸法に切断してAAサイズ用の負極26を得た。
水素吸蔵合金充填密度[g/cm3]=水素吸蔵合金質量[g]÷(電極高さ[cm]×電極長さ[cm]×電極厚み[cm]-パンチングメタルシートの質量[g]÷鉄の比重[g/cm3])・・・(2)
(3)ニッケル水素二次電池の組み立て
得られた正極24及び負極26をこれらの間にセパレータ28を挟んだ状態で渦巻状に巻回し、電極群22を作製した。ここでの電極群22の作製に使用したセパレータ28はスルホン化処理が施されたポリプロピレン繊維製不織布から成り、その厚みは0.1mm(目付量40g/m2)であった。
得られた正極24及び負極26をこれらの間にセパレータ28を挟んだ状態で渦巻状に巻回し、電極群22を作製した。ここでの電極群22の作製に使用したセパレータ28はスルホン化処理が施されたポリプロピレン繊維製不織布から成り、その厚みは0.1mm(目付量40g/m2)であった。
一方、KOH、NaOH及びLiOHを溶質として含む水溶液からなるアルカリ電解液を準備した。このアルカリ電解液は、KOH、NaOH及びLiOHの質量混合比が、KOH:NaOH:LiOH=15:2:1であり、比重が1.30である。
ついで、有底円筒形状の外装缶10内に上記した電極群22を収容するとともに、準備したアルカリ電解液を2.4g注入した。その後、封口体11で外装缶10の開口を塞ぎ、公称容量1500mAhのAAサイズのニッケル水素二次電池2を組み立てた。
(4)初期活性化処理
得られた電池2に対し、温度25℃の環境下にて、1.0Itで16時間の充電を行った後、1.0Itで電池電圧が1.0Vになるまで放電させる充放電作業を1サイクルとする充放電サイクルを3回繰り返した。このようにして初期活性化処理を行い、電池2を使用可能状態とした。
得られた電池2に対し、温度25℃の環境下にて、1.0Itで16時間の充電を行った後、1.0Itで電池電圧が1.0Vになるまで放電させる充放電作業を1サイクルとする充放電サイクルを3回繰り返した。このようにして初期活性化処理を行い、電池2を使用可能状態とした。
(実施例2)
パーフルオロブタンスルホン酸カリウムの粉末の添加量を0.02質量部としたこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
パーフルオロブタンスルホン酸カリウムの粉末の添加量を0.02質量部としたこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
(実施例3)
パーフルオロブタンスルホン酸カリウムの粉末の添加量を0.05質量部としたこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
パーフルオロブタンスルホン酸カリウムの粉末の添加量を0.05質量部としたこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
(比較例1)
中空カーボンブラックからなる導電剤の粉末及びパーフルオロブタンスルホン酸カリウムの粉末を添加しなかったこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
中空カーボンブラックからなる導電剤の粉末及びパーフルオロブタンスルホン酸カリウムの粉末を添加しなかったこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
(比較例2)
パーフルオロブタンスルホン酸カリウムの粉末を添加しなかったこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
パーフルオロブタンスルホン酸カリウムの粉末を添加しなかったこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
(比較例3)
中空カーボンブラックからなる導電剤の粉末を0.25質量部添加したこと及びパーフルオロブタンスルホン酸カリウムの粉末を添加しなかったこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
中空カーボンブラックからなる導電剤の粉末を0.25質量部添加したこと及びパーフルオロブタンスルホン酸カリウムの粉末を添加しなかったこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
(比較例4)
中空カーボンブラックからなる導電剤の粉末を1.00質量部添加したこと及びパーフルオロブタンスルホン酸カリウムの粉末を添加しなかったこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
中空カーボンブラックからなる導電剤の粉末を1.00質量部添加したこと及びパーフルオロブタンスルホン酸カリウムの粉末を添加しなかったこと以外は、実施例1と同様にしてニッケル水素二次電池を作製した。
2.ニッケル水素二次電池の評価
(1)低温放電特性試験
作製された実施例1~3、比較例1~4の電池に対し、25℃の環境下にて、1.0Itで、電池電圧が最大値に達した後、10mV低下するまで充電し、その後、-10℃の環境下にて、3時間放置した。
(1)低温放電特性試験
作製された実施例1~3、比較例1~4の電池に対し、25℃の環境下にて、1.0Itで、電池電圧が最大値に達した後、10mV低下するまで充電し、その後、-10℃の環境下にて、3時間放置した。
ついで、3時間放置した後の電池に対し、-10℃の環境下にて、1.0Itで、電池電圧が1.0Vになるまで放電し、このときの放電容量を求めた。
ここで、比較例1の放電容量の値を100として、各電池の放電容量の値との比を求め、その結果を低温放電特性比として、表1に示した。
なお、この低温放電特性比の値が大きいほど低温放電特性に優れていることを示している。
(2)考察
(i)中空カーボンブラック及びパーフルオロブタンスルホン酸カリウムのどちらも含んでいない負極を用いた比較例1の電池は、低温放電特性比が100である。これに対し、中空カーボンブラックを含み、パーフルオロブタンスルホン酸カリウムは含んでいない負極を用いた比較例2~4の電池は、低温放電特性比が107~108であり、低温放電特性が比較例1の電池に比べて改善されていることがわかる。このことから、中空カーボンブラックを添加すると低温放電特性の改善に効果があると言える。
(i)中空カーボンブラック及びパーフルオロブタンスルホン酸カリウムのどちらも含んでいない負極を用いた比較例1の電池は、低温放電特性比が100である。これに対し、中空カーボンブラックを含み、パーフルオロブタンスルホン酸カリウムは含んでいない負極を用いた比較例2~4の電池は、低温放電特性比が107~108であり、低温放電特性が比較例1の電池に比べて改善されていることがわかる。このことから、中空カーボンブラックを添加すると低温放電特性の改善に効果があると言える。
(ii)一方、比較例同士を比べると、比較例3では、中空カーボンブラックの添加量は0.25質量部であり、低温放電特性比が107である。これに対し、比較例2は、この比較例3の2倍の量の0.50質量部の中空カーボンブラックが添加されているが、低温放電特性比は107で同じである。更に、比較例4は、比較例3の4倍の量の1.00質量部の中空カーボンブラックが添加されているが、低温放電特性比は108であり、僅かに改善されている程度である。これらのことから、中空カーボンブラックを添加すると低温放電特性比は改善されるものの、0.50質量部以上添加しても低温放電特性比の改善効果は飽和してしまうと言える。また、そのときの低温放電特性比は108が限界であり、近年の使用条件に十分に対応できるものとはなっていない。
(iii)中空カーボンブラック及びパーフルオロブタンスルホン酸カリウムのどちらも含んでいる負極を用いた実施例1~3の電池は、パーフルオロブタンスルホン酸カリウムを含んでいない負極を用いた比較例2~4に比べ、低温放電特性が更に向上していることがわかる。
これは、パーフルオロブタンスルホン酸カリウムにより、導電剤である中空カーボンブラックがより均一に分散されたとともに、極めて微細な気泡が形成され、その気泡が負極内の空隙となったため、負極全体における電極反応面積が増加し、それにより、低温でも電池反応が活発化され、低温放電特性比がより改善されたものと考えられる。
ここで、パーフルオロブタンスルホン酸カリウムの添加量については、実施例2における0.02質量部の場合に低温放電特性比が122となっており、実施例2が最良の態様であると言える。この実施例2の態様の場合、中空カーボンブラックの分散性は十分に高く、電極反応面積の増加効果も十分発揮されていると考えられる。
パーフルオロブタンスルホン酸カリウムの添加量が、0.01質量部である実施例1の場合、低温放電特性比は114であり、比較例1~4よりも優れているが、実施例2よりも低い。これは、パーフルオロブタンスルホン酸カリウムの添加量が十分ではなく、中空カーボンブラックの分散性及び電極反応面積の増加効果が実施例2ほどは発揮されていないためと考えられる。
パーフルオロブタンスルホン酸カリウムの添加量が、0.05質量部である実施例3の場合、低温放電特性比は113であり、比較例1~4よりも優れているが、実施例2よりも低い。これは、導電性が無いパーフルオロブタンスルホン酸カリウムの添加量が実施例2よりも増え、それにより、放電反応が阻害されたためと考えられる。
以上より、中空カーボンブラックにパーフルオロブタンスルホン酸カリウムを組み合わせると、これらの相乗効果により、低温放電特性比が従来よりも大幅に改善され、電池の低温放電特性の向上を図ることができると言える。
ここで、本実施形態においては、パーフルオロブタンスルホン酸カリウムについてのみ記載したが、他のパーフルオロブタンスルホン酸塩、すなわち、パーフルオロブタンスルホン酸ナトリウム、パーフルオロブタンスルホン酸リチウム、パーフルオロブタンスルホン酸セシウム、パーフルオロブタンスルホン酸ルビジウム等を用いても同様の効果が得られる。
なお、本発明は、上記した実施形態及び実施例に限定されるものではなく、種々の変形が可能である。本発明が適用される電池は、アルカリ二次電池であればよく、ニッケル水素二次電池の他に、例えば、ニッケル亜鉛二次電池等を挙げることができる。また、電池の構造は格別限定されることはなく、円形電池の他、角形電池であってもよい。
2 ニッケル水素二次電池
22 電極群
24 正極
26 負極
28 セパレータ
22 電極群
24 正極
26 負極
28 セパレータ
Claims (6)
- 負極芯体と、
前記負極芯体に保持されている負極合剤と、を備え、
前記負極合剤は、水素吸蔵合金の粒子からなる水素吸蔵合金粉末、導電剤の粉末及び負極添加剤の粉末を含んでおり、
前記導電剤は、一次粒子が中空シェル状の構造を持つ中空カーボンブラックであり、
前記負極添加剤は、フッ素系アニオン性界面活性剤である、
アルカリ二次電池用の負極。 - 前記中空カーボンブラックからなる前記導電剤の粉末は、前記水素吸蔵合金粉末100質量部に対し、0.25質量部以上、0.5質量部以下添加されている、請求項1に記載のアルカリ二次電池用の負極。
- 前記フッ素系アニオン性界面活性剤からなる前記負極添加剤の粉末は、前記水素吸蔵合金粉末100質量部に対し、0.01質量部以上、0.05質量部以下添加されている、請求項1又は2に記載のアルカリ二次電池用の負極。
- 前記フッ素系アニオン性界面活性剤は、パーフルオロブタンスルホン酸塩である、請求項1~3の何れかに記載のアルカリ二次電池用の負極。
- 容器と、前記容器内にアルカリ電解液とともに収容された電極群とを備え、
前記電極群は、セパレータを介して重ね合わされた正極及び負極からなり、
前記負極は、請求項1~4の何れかに記載されたアルカリ二次電池用の負極である、アルカリ二次電池。 - 水素吸蔵合金粉末、導電剤の粉末、負極添加剤の粉末及び水をそれぞれ所定量だけ準備する準備工程と、
準備された前記水素吸蔵合金粉末、前記導電剤の粉末、前記負極添加剤の粉末及び前記水を混練して負極合剤のペーストを製造するペースト製造工程と、
前記ペースト製造工程で得られた負極合剤のペーストを負極芯体に塗着させるペースト塗着工程と、
負極芯体に塗着されている負極合剤のペーストを乾燥させる乾燥工程と、
を備えており、
前記導電剤は、一次粒子が中空シェル状の構造を持つ中空カーボンブラックであり、
前記負極添加剤は、フッ素系アニオン性界面活性剤である、
アルカリ二次電池用の負極の製造方法。