WO2017125839A1 - Nano- ou micro-catalyseurs de céramique fondue ayant une superficie élevée - Google Patents
Nano- ou micro-catalyseurs de céramique fondue ayant une superficie élevée Download PDFInfo
- Publication number
- WO2017125839A1 WO2017125839A1 PCT/IB2017/050192 IB2017050192W WO2017125839A1 WO 2017125839 A1 WO2017125839 A1 WO 2017125839A1 IB 2017050192 W IB2017050192 W IB 2017050192W WO 2017125839 A1 WO2017125839 A1 WO 2017125839A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- micromaterial
- catalytic
- nano
- hollow
- ceramic
- Prior art date
Abstract
La présente invention concerne un nano- ou micro-matériau catalytique creux broyable, des procédés de fabrication du nano- ou micro-matériau catalytique creux broyable et des utilisations de celui-ci. Le nano- ou micro-matériau catalytique creux broyable peut comprendre une enveloppe de céramique définissant un espace creux fermé. L'enveloppe de céramique peut comprendre un métal catalytique dispersé dans l'ensemble de l'enveloppe. Le nano- ou micro-matériau catalytique creux broyable, lorsqu'il est broyé, présente une surface d'au moins 5 m2/g.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201662280385P | 2016-01-19 | 2016-01-19 | |
US62/280,385 | 2016-01-19 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2017125839A1 true WO2017125839A1 (fr) | 2017-07-27 |
Family
ID=59362188
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/IB2017/050192 WO2017125839A1 (fr) | 2016-01-19 | 2017-01-13 | Nano- ou micro-catalyseurs de céramique fondue ayant une superficie élevée |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2017125839A1 (fr) |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20030181535A1 (en) * | 2000-07-24 | 2003-09-25 | Van Hardeveld Robert Martija | Shell metal catalyst and a precursor thereof, a process for their preparation and the use of the catalyst |
US20100204342A1 (en) * | 2007-06-26 | 2010-08-12 | Denki Kagaku Kogyo Kabushiki Kaisha | Spherical organic polymer-silicon compound composite particles, hollow particles and their production methods |
US20140178262A1 (en) * | 2012-12-20 | 2014-06-26 | Basf Corporation | Hollow Microsphere Catalyst Support and Methods of Making Same |
-
2017
- 2017-01-13 WO PCT/IB2017/050192 patent/WO2017125839A1/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20030181535A1 (en) * | 2000-07-24 | 2003-09-25 | Van Hardeveld Robert Martija | Shell metal catalyst and a precursor thereof, a process for their preparation and the use of the catalyst |
US20100204342A1 (en) * | 2007-06-26 | 2010-08-12 | Denki Kagaku Kogyo Kabushiki Kaisha | Spherical organic polymer-silicon compound composite particles, hollow particles and their production methods |
US20140178262A1 (en) * | 2012-12-20 | 2014-06-26 | Basf Corporation | Hollow Microsphere Catalyst Support and Methods of Making Same |
Non-Patent Citations (2)
Title |
---|
GUO ET AL.: "Synthesis and characterization of carbon sphere-silica core-shell structure and hollow silica spheres", COLLOIDS AND SURFACES A: PHYSICOCHEMICAL AND ENGINEERING ASPECTS, vol. 345, 2009, pages 141 - 146, XP026196123 * |
YANG ET AL.: "Templated synthesis of inorganic hollow spheres with a tunable cavity size onto core-shell gel particles", ANGEWANDTE CHEMIE, vol. 115, no. 17, 2003, pages 1987 - 1989, XP055401992 * |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Debecker et al. | Aerosol processing: a wind of innovation in the field of advanced heterogeneous catalysts | |
Noval et al. | Fe 3 O 4-TiO 2 and Fe 3 O 4-SiO 2 core-shell powders synthesized from industrially processed magnetite (Fe 3 O 4) microparticles | |
Lee et al. | Functionalization of hollow nanoparticles for nanoreactor applications | |
Ying et al. | Research needs assessment on nanostructured catalysts | |
KR101197837B1 (ko) | 복합 입자 담지물, 그 복합 입자 담지물의 제조 방법, 및 그 복합 입자 담지물을 화학 합성용 촉매로서 이용한 화합물의 제조 방법 | |
Yue et al. | Thermal-stable Pd@ mesoporous silica core-shell nanocatalysts for dry reforming of methane with good coke-resistant performance | |
Blanford et al. | Gems of chemistry and physics: Macroporous metal oxides with 3D order | |
Xu et al. | Core/shell-structured TS-1@ mesoporous silica-supported Au nanoparticles for selective epoxidation of propylene with H 2 and O 2 | |
Barhoum et al. | Sol-gel hot injection synthesis of ZnO nanoparticles into a porous silica matrix and reaction mechanism | |
Yan et al. | High catalytic activity for CO oxidation of Co 3 O 4 nanoparticles in SiO 2 nanocapsules | |
Tai et al. | Oxidation of carbon monoxide on Au nanoparticles in titania and titania-coated silica aerogels | |
Motl et al. | Aerosol-assisted synthesis and assembly of nanoscale building blocks | |
EP1657219A2 (fr) | Substance nanostructurée | |
WO2012035637A1 (fr) | Matière à base de silice, son procédé de fabrication, matière portant un métal noble et procédé de fabrication d'un acide carboxylique à l'aide de celle-ci comme catalyseur | |
WO2017062226A1 (fr) | Catalyseurs de type cœur/coquille et hochet/coquille et leur procédé de fabrication | |
WO2014070116A1 (fr) | Nanoparticules encapsulées | |
US20100056360A1 (en) | Magnetic mesoporous material as chemical catalyst | |
JP5837620B2 (ja) | 触媒 | |
Lv et al. | One-pot synthesis of stable Pd@ mSiO 2 core–shell nanospheres with controlled pore structure and their application to the hydrogenation reaction | |
JP2010221081A (ja) | 複合粒子担持物及びその製造方法並びにカルボン酸エステルの製造方法 | |
Wang et al. | Metal-nanoparticles supported on solid as heterogeneous catalysts | |
Du et al. | Synthesis of a hollow structured core–shell Au@ CeO 2–ZrO 2 nanocatalyst and its excellent catalytic performance | |
Szczęśniak et al. | Recent advances in mechanochemical synthesis of mesoporous metal oxides | |
Karandikar et al. | Co3O4@ Mesoporous Silica for Fischer–Tropsch Synthesis: Core–Shell Catalysts with Multiple Core Assembly and Different Pore Diameters of Shell | |
Ming et al. | A new strategy for finely controlling the metal (oxide) coating on colloidal particles with tunable catalytic properties |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 17741153 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 17741153 Country of ref document: EP Kind code of ref document: A1 |