WO2017092013A1 - Method for preparing dentiform shaped ceramics - Google Patents
Method for preparing dentiform shaped ceramics Download PDFInfo
- Publication number
- WO2017092013A1 WO2017092013A1 PCT/CN2015/096354 CN2015096354W WO2017092013A1 WO 2017092013 A1 WO2017092013 A1 WO 2017092013A1 CN 2015096354 W CN2015096354 W CN 2015096354W WO 2017092013 A1 WO2017092013 A1 WO 2017092013A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- slurry
- shaped
- ceramic
- preparing
- tooth
- Prior art date
Abstract
Description
Claims (10)
- 一种齿状异形陶瓷的制备方法,其特征在于,包括以下步骤: A method for preparing a tooth shaped shaped ceramic, comprising the steps of:S1制备浆料:按以下质量百分比称取各组分并混合均匀,20-75%的陶瓷粉体,10-70%的预混液,0.1-5%的光引发剂,0.1-5%的分散剂,0.1-5%的表面改性剂,得到浆料;S1 preparation of slurry: weigh each component and mix well according to the following mass percentage, 20-75% ceramic powder, 10-70% premix, 0.1-5% photoinitiator, 0.1-5% dispersion a 0.1-5% surface modifier to obtain a slurry;所述预混液由有机溶质与溶剂组成,所述溶剂的质量为预混液的质量的20-85%;所述有机溶质为丙烯酰胺、二甲基丙烯酸酯、甲基丙烯酰胺、甲基丙烯酸2-羟基乙酯和N–N’亚甲基双丙烯酰胺中的至少一种;The premix liquid is composed of an organic solute and a solvent, the mass of the solvent being 20-85% of the mass of the premix liquid; the organic solute is acrylamide, dimethacrylate, methacrylamide, methacrylic acid 2 At least one of -hydroxyethyl ester and N-N'methylenebisacrylamide;S2成型:将浆料置于光固化成型设备中,通过光固化成型法按所设计的陶瓷形状绘制出坯体;S2 molding: the slurry is placed in a photocuring molding apparatus, and the green body is drawn by the photocuring molding method according to the designed ceramic shape;然后,坯体依次经过干燥步骤、脱脂步骤和烧结步骤的加工,制得齿状异形陶瓷。 Then, the green body is sequentially subjected to a drying step, a degreasing step, and a sintering step to obtain a tooth-shaped shaped ceramic.
- 根据权利要求1所述一种齿状异形陶瓷的制备方法,其特征在于,所述成型步骤中,光固化成型设备的扫描速度为800-3500mm/s,扫描方式为XYSTA,扫描间距为0.2-0.7mm。The method for preparing a tooth-shaped shaped ceramic according to claim 1, wherein in the forming step, the scanning speed of the photo-curing device is 800-3500 mm/s, the scanning mode is XYSTA, and the scanning pitch is 0.2- 0.7mm.
- 根据权利要求1所述一种齿状异形陶瓷的制备方法,其特征在于,所述干燥步骤是:将坯体置于液态干燥剂中干燥5-36h或坯体用微波干燥5-36h;干燥温度为25-60℃。The method for preparing a tooth-shaped shaped ceramic according to claim 1, wherein the drying step comprises: drying the blank in a liquid desiccant for 5-36 hours or drying the body with microwave for 5-36 hours; drying The temperature is 25-60 ° C.
- 根据权利要求1所述一种齿状异形陶瓷的制备方法,其特征在于,所述脱脂步骤是:先对坯体进行真空脱脂或气氛保护脱脂处理,再对坯体进行空气脱脂处理。The method for preparing a tooth-shaped shaped ceramic according to claim 1, wherein the degreasing step is: first performing vacuum degreasing or atmosphere protection degreasing treatment on the green body, and then performing air degreasing treatment on the green body.
- 根据权利要求4所述一种齿状异形陶瓷的制备方法,其特征在于,所述真空脱脂或气氛保护脱脂的条件是:将坯体置于负压的排胶炉内或惰性气体/N2保护的排胶炉内,以0.1-5℃/min的速率升温至300-1000℃并保温2-6h,且升温过程中每隔50-150℃保温0-60min;接着,坯体在负压的排胶炉内或惰性气体/N2保护的排胶炉内冷却至室温。The method for preparing a toothed shaped ceramic according to claim 4, wherein the condition of the vacuum degreasing or atmosphere protection degreasing is: placing the blank in a vacuum oven or inert gas/N2 protection In the rubberizing furnace, the temperature is raised to 300-1000 ° C at a rate of 0.1-5 ° C / min and kept for 2-6 h, and the temperature is maintained at 50-150 ° C for 0-60 min during the heating process; then, the blank is under negative pressure. Cool to room temperature in a degreaser or in an inert gas/N2 protected degreaser.
- 根据权利要求4所述一种齿状异形陶瓷的制备方法,其特征在于,所述空气脱脂的条件是:将坯体置于空气气氛的排胶炉中,以5-8℃/min的速率升温至300-1000℃并保温2-3h;然后坯体随炉冷却至室温。The method for preparing a tooth-shaped shaped ceramic according to claim 4, wherein the air degreasing condition is: placing the blank in a debinding furnace in an air atmosphere at a rate of 5-8 ° C / min The temperature was raised to 300-1000 ° C and held for 2-3 h; then the body was cooled to room temperature with the furnace.
- 根据权利要求1所述一种齿状异形陶瓷的制备方法,其特征在于,所述烧结步骤的条件是:将坯体置于烧结炉中,以10-15℃/min的速率升温至1350-1550℃并保温1-4h,然后随炉冷却,制得齿状异形陶瓷。The method for preparing a toothed shaped ceramic according to claim 1, wherein the sintering step is carried out by placing the body in a sintering furnace and raising the temperature to 1350 at a rate of 10-15 ° C/min. The toothed shaped ceramic was prepared by heating at 1550 ° C for 1-4 h and then cooling with the furnace.
- 根据权利要求1所述一种齿状异形陶瓷的制备方法,其特征在于,所述制备浆料步骤中:首先将陶瓷粉体和部分分散剂与乙醇混合均匀,形成陶瓷粉体分散液,备用;The method for preparing a toothed shaped ceramic according to claim 1, wherein in the step of preparing the slurry, firstly, the ceramic powder and a part of the dispersing agent are uniformly mixed with ethanol to form a ceramic powder dispersion, and the mixture is prepared. ;将有机溶质与溶剂混合均匀,形成预混液,然后向预混液中加入陶瓷粉体分散液、表面改性剂及剩余的分散剂,球磨3-24h,得到初浆料;将初浆料置于负压环境下并搅拌初浆料20-120min以除去气泡,再向初浆料中加入光引发剂并混合均匀,制得浆料。The organic solute and the solvent are uniformly mixed to form a premixed liquid, and then the ceramic powder dispersion liquid, the surface modifier and the remaining dispersing agent are added to the premixed liquid, and ball milled for 3-24 hours to obtain a primary slurry; Under the negative pressure environment, the initial slurry was stirred for 20-120 min to remove the bubbles, and then the photoinitiator was added to the primary slurry and uniformly mixed to prepare a slurry.
- 根据权利要求1所述一种齿状异形陶瓷的制备方法,其特征在于,所述陶瓷粉体为氧化锆粉末、氧化铝粉末和莫来石粉末中的至少一种。The method of producing a toothed shaped ceramic according to claim 1, wherein the ceramic powder is at least one of zirconia powder, alumina powder, and mullite powder.
- 根据权利要求1所述一种齿状异形陶瓷的制备方法,其特征在于,所述陶瓷粉体的粒径为0.1-5μm。The method of producing a toothed shaped ceramic according to claim 1, wherein the ceramic powder has a particle diameter of 0.1 to 5 μm.