WO2017068446A1 - Poussière de four électrique à arc comme matériau d'enrobage de boulettes de minerai de fer pour une utilisation dans des processus de réduction directe - Google Patents

Poussière de four électrique à arc comme matériau d'enrobage de boulettes de minerai de fer pour une utilisation dans des processus de réduction directe Download PDF

Info

Publication number
WO2017068446A1
WO2017068446A1 PCT/IB2016/055784 IB2016055784W WO2017068446A1 WO 2017068446 A1 WO2017068446 A1 WO 2017068446A1 IB 2016055784 W IB2016055784 W IB 2016055784W WO 2017068446 A1 WO2017068446 A1 WO 2017068446A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
iron ore
pellets
iron
electric arc
Prior art date
Application number
PCT/IB2016/055784
Other languages
English (en)
Inventor
Hamad S. AL-TASSAN
Mohamed Bahgat SADDIK
Sayed Niaz AHSAN
Hesham A. HANAFY
Original Assignee
Sabic Global Technologies B.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sabic Global Technologies B.V. filed Critical Sabic Global Technologies B.V.
Priority to EP16794043.6A priority Critical patent/EP3365470A1/fr
Priority to CN201680075796.4A priority patent/CN108474060A/zh
Priority to US15/768,422 priority patent/US20180320246A1/en
Publication of WO2017068446A1 publication Critical patent/WO2017068446A1/fr

Abstract

L'invention concerne des compositions d'enrobage, et des procédés pour leur utilisation, comprenant 90 % en poids de poussière de four électrique à arc sur la base du poids sec total de la composition d'enrobage. La poussière de four électrique à arc comprend au moins 40 % en poids de Fe2O3 et au moins 30 % en poids de CaO et CaCO3 combinés, sur la base du poids sec total de la poussière de four électrique à arc.
PCT/IB2016/055784 2015-10-23 2016-09-27 Poussière de four électrique à arc comme matériau d'enrobage de boulettes de minerai de fer pour une utilisation dans des processus de réduction directe WO2017068446A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
EP16794043.6A EP3365470A1 (fr) 2015-10-23 2016-09-27 Poussière de four électrique à arc comme matériau d'enrobage de boulettes de minerai de fer pour une utilisation dans des processus de réduction directe
CN201680075796.4A CN108474060A (zh) 2015-10-23 2016-09-27 电弧炉粉尘作为铁矿石球团的涂层材料用于直接还原工艺
US15/768,422 US20180320246A1 (en) 2015-10-23 2016-09-27 Electric arc furnace dust as coating material for iron ore pellets for use in direct reduction processes

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201562245760P 2015-10-23 2015-10-23
US201562245759P 2015-10-23 2015-10-23
US62/245,759 2015-10-23
US62/245,760 2015-10-23

Publications (1)

Publication Number Publication Date
WO2017068446A1 true WO2017068446A1 (fr) 2017-04-27

Family

ID=57249842

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/IB2016/055783 WO2017068445A1 (fr) 2015-10-23 2016-09-27 Procédés de détermination de caractéristiques d'adhérence de matériaux de revêtement pour boulettes de minerai de fer pour une utilisation dans des processus de réduction directe
PCT/IB2016/055784 WO2017068446A1 (fr) 2015-10-23 2016-09-27 Poussière de four électrique à arc comme matériau d'enrobage de boulettes de minerai de fer pour une utilisation dans des processus de réduction directe

Family Applications Before (1)

Application Number Title Priority Date Filing Date
PCT/IB2016/055783 WO2017068445A1 (fr) 2015-10-23 2016-09-27 Procédés de détermination de caractéristiques d'adhérence de matériaux de revêtement pour boulettes de minerai de fer pour une utilisation dans des processus de réduction directe

Country Status (4)

Country Link
US (1) US20180320246A1 (fr)
EP (1) EP3365470A1 (fr)
CN (1) CN108474060A (fr)
WO (2) WO2017068445A1 (fr)

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108026607B (zh) * 2015-07-07 2020-09-11 沙特基础全球技术有限公司 涂覆的铁矿石球团及其制备和还原以形成还原铁球团的方法
CN109482611A (zh) * 2018-11-14 2019-03-19 铜陵有色金属集团股份有限公司 含砷硫化渣的无公害处理方法
BR102019023195B1 (pt) * 2019-11-05 2021-01-19 Vale S.A. processo de produção de aglomerado de finos de minério de ferroe o produto aglomerado
WO2022264549A1 (fr) * 2021-06-18 2022-12-22 Ｊｆｅスチール株式会社 Procédé d'évaluation de minerai aggloméré et minerai aggloméré
JP7111284B1 (ja) * 2021-06-18 2022-08-02 Ｊｆｅスチール株式会社 塊成鉱の評価方法および塊成鉱
CN115232962B (zh) * 2022-07-29 2024-02-02 安徽工业大学 一种含碳粉尘的双层球团制备方法

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5470375A (en) * 1993-06-30 1995-11-28 Bechtel Group, Inc. Method of processing waste material containing non ferrous metal oxides

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2061346C3 (de) * 1970-12-12 1974-10-10 Huettenwerk Oberhausen Ag, 4200 Oberhausen Verfahren zur Vorbereitung von Eisenerzpellets zur Direktreduktion im Fest- und Wanderbett
CN1168837C (zh) * 1999-06-11 2004-09-29 酒泉钢铁(集团)有限责任公司 采用熔剂分加技术生产酸性球团烧结矿的方法
US7226495B1 (en) * 2000-05-15 2007-06-05 Companhia Vale Do Rio Doce Method to increase the adherence of coating materials on ferrous materials
SE0201453D0 (sv) * 2002-05-10 2002-05-10 Luossavaara Kiirunavaara Ab Method to improve iron production rate in a blast furnace
CN100342041C (zh) * 2006-01-10 2007-10-10 许贵宾 熔剂性铁矿粉复合球团的生产方法
DE102010022692A1 (de) * 2010-03-17 2011-09-22 Sms Siemag Ag Brikett zur Erzeugung eines Schaumschlacke-Effekts bei der EAF-Technologie der Edelstahlherstellung
US8287619B2 (en) * 2010-06-08 2012-10-16 C.V.G. Ferrominera Orinoco C.A. Process and equipment for the production of direct reduced iron and/or pig iron from iron ores having a high-phosphorus content
CA2937648C (fr) * 2014-01-31 2023-05-09 Saudi Basic Industries Corporation Boulettes de fer composites

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5470375A (en) * 1993-06-30 1995-11-28 Bechtel Group, Inc. Method of processing waste material containing non ferrous metal oxides

Non-Patent Citations (8)

* Cited by examiner, † Cited by third party
Title
BASDAG ET AL: "Coating of iron oxide pellets for direct reduction", SCANDINAVIAN JOURNAL OF METALLURGY,, vol. 31, 1 January 2002 (2002-01-01), pages 229 - 233, XP002762648 *
CANO JAM; WENDLING F, MINING ENG, vol. 45, 1993, pages 633 - 636
CASTRO P A ET AL: "Effect of different coatings on the adherence of direct reduction pellets", IRONMAKING CONFERENCE PROCEEDINGS, XX, XX, vol. 4, 11 November 2003 (2003-11-11), pages 195 - 202, XP009122851 *
J. FEINMAN AND D. R. MAC RAE: "Direct reduced iron: Technology and Economics of Production and Use", 1999, ISS, WARRENDALE, PA
JERKER STERNELAND; PAR G. JONSSON, ISIJ INTERNATIONAL, vol. 43, no. 1, 2003, pages 26 - 35
JIANHUA SHAO; ZHANCHENG GUO; HUIQING TANG, STEEL RESEARCH INT., vol. 84, no. 2, 2013, pages 111 - 118
L. G. HENDERICKSON; J. A. SANDOVAL, IRON STEEL SOC. AIME, 1980, pages 35 - 48
WONG PLM; KIM MJ; KIM HS; CHOI CH, IRONMAKING STEELMAKING, vol. 26, 1999, pages 53 - 57

Also Published As

Publication number Publication date
US20180320246A1 (en) 2018-11-08
CN108474060A (zh) 2018-08-31
EP3365470A1 (fr) 2018-08-29
WO2017068445A1 (fr) 2017-04-27

Similar Documents

Publication Publication Date Title
US20180320246A1 (en) Electric arc furnace dust as coating material for iron ore pellets for use in direct reduction processes
Zheng et al. Preparation of monodispersed micaceous iron oxide pigment from pyrite cinders
JP5287127B2 (ja) 焼結用配合鉄鉱石の評価方法
Sivrikaya et al. The bonding/strengthening mechanism of colemanite added organic binders in iron ore pelletization
Mombelli et al. Experimental analysis on the use of BF-sludge for the reduction of BOF-powders to direct reduced iron (DRI) production
US8016935B2 (en) Anti-corrosion pigments coming from dust of an electric arc furnace and containing sacrificial calcium
CA3027025A1 (fr) Method for manufacturing briquettes containing a calcium-magnesium compound and an iron-based compound, and briquettes thus obtained
Wang et al. Co-utilization of converter sludge-containing dedust wastewater in iron ore sintering to save fresh water, enhance quality and reduce pollution
Wan et al. Efficient improvement for the direct reduction of high-iron red mud by co-reduction with high-manganese iron ore
JP5565481B2 (ja) 焼結用配合鉄鉱石の評価方法
Zhang et al. Effect of MgO and basicity on microstructure and metallurgical properties of iron ore sinter
CN108026607B (zh) 涂覆的铁矿石球团及其制备和还原以形成还原铁球团的方法
EP1504128B1 (fr) Procede destine a ameliorer le taux de production de fer dans un haut fourneau
Loncnar et al. Comparison of the mineralogy and microstructure of EAF stainless steel slags with reference to the cooling path
Rao et al. Mineralogy, liberation and leaching characteristics of iron oxide phases in an Indian diaspore sample
Kim et al. Effects of K2CO3 addition on the physicochemical properties of goethite composite pellets with different basicities (CaO/SiO2)
Nie et al. Innovative application of two-stage sulfuric acid leaching for efficient recovery of Ti from titanium-bearing electric furnace slag
Robinson Studies in low temperature self-reduction of by-products from integrated iron and steelmaking
Mou et al. Sinter plant operations: raw materials
EP3628753B1 (fr) Procédé pour préparer des pastilles contenant du fer et du chrome
Tastanova et al. Processing and production of pellets from poor-grade manganesecontaining raw materials
Longbottom et al. Characterisation of steelplant by-products to realise the value of Fe and Zn
AU2019203137A1 (en) Ironmaking Feedstock
Andersson Recycling of Blast Furnace Sludge within the Integrated Steel Plant
Ferreira et al. Reduction by Hydrogen of the Waste Rock Minerals Constituents of a Vanadium Ore

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16794043

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 15768422

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2016794043

Country of ref document: EP