WO2017050768A1 - Plaque isolante et procédé de production d'une plaque isolante - Google Patents
Plaque isolante et procédé de production d'une plaque isolante Download PDFInfo
- Publication number
- WO2017050768A1 WO2017050768A1 PCT/EP2016/072310 EP2016072310W WO2017050768A1 WO 2017050768 A1 WO2017050768 A1 WO 2017050768A1 EP 2016072310 W EP2016072310 W EP 2016072310W WO 2017050768 A1 WO2017050768 A1 WO 2017050768A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer foam
- foam particles
- insulation
- insulating
- insulating board
- Prior art date
Abstract
L'invention concerne une plaque isolante (1) constituée d'un matériau matrice (2) à base d'hydrate de silicate de calcium, des particules (3) de mousse de polymère étant incorporées dans le matériau matrice (2), et la conductivité thermique λP des particules (3) de mousse de polymère étant inférieure à la conductivité thermique λM du matériau matrice (2). L'invention concerne en outre un procédé de fabrication d'une telle plaque isolante (1).
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102015218288.6A DE102015218288A1 (de) | 2015-09-23 | 2015-09-23 | Dämmstoffplatte und Verfahren zur Herstellung einer Dämmstoffplatte |
DE102015218288.6 | 2015-09-23 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2017050768A1 true WO2017050768A1 (fr) | 2017-03-30 |
Family
ID=57113263
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2016/072310 WO2017050768A1 (fr) | 2015-09-23 | 2016-09-20 | Plaque isolante et procédé de production d'une plaque isolante |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE102015218288A1 (fr) |
WO (1) | WO2017050768A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20180354862A1 (en) * | 2015-09-06 | 2018-12-13 | Goertek Inc. | Sound absorption material preparation method, sound absorption material and filling method thereof |
CN114105524A (zh) * | 2021-11-29 | 2022-03-01 | 张家港市华孚实业有限公司 | 一种建筑用保温型膨胀珍珠岩复合材料制备工艺 |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP4105190A4 (fr) * | 2020-02-10 | 2023-08-23 | Shanghai Shengkui Products Co., Ltd | Matériau d'isolation thermique et ignifuge et procédé de préparation associé |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE2655515A1 (de) * | 1976-12-08 | 1978-06-15 | Krupp Gmbh | Verfahren zur herstellung von leichtkalksandsteinen |
EP0570012A1 (fr) * | 1992-05-15 | 1993-11-18 | Rainer Haug | Isolation thermique pour bâtiments |
DE19923493A1 (de) * | 1998-06-15 | 2000-04-06 | Stefan Wisser | Verfahren zur Herstellung eines Leichtwerkstoffes |
WO2010100230A1 (fr) * | 2009-03-06 | 2010-09-10 | Basf Se | Composition de revêtement pour des particules de mousse |
EP2371783A1 (fr) * | 2010-04-01 | 2011-10-05 | Xella Technologie- und Forschungsgesellschaft mbH | Corps de formage en béton poreux et son procédé de fabrication |
-
2015
- 2015-09-23 DE DE102015218288.6A patent/DE102015218288A1/de not_active Ceased
-
2016
- 2016-09-20 WO PCT/EP2016/072310 patent/WO2017050768A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE2655515A1 (de) * | 1976-12-08 | 1978-06-15 | Krupp Gmbh | Verfahren zur herstellung von leichtkalksandsteinen |
EP0570012A1 (fr) * | 1992-05-15 | 1993-11-18 | Rainer Haug | Isolation thermique pour bâtiments |
DE19923493A1 (de) * | 1998-06-15 | 2000-04-06 | Stefan Wisser | Verfahren zur Herstellung eines Leichtwerkstoffes |
WO2010100230A1 (fr) * | 2009-03-06 | 2010-09-10 | Basf Se | Composition de revêtement pour des particules de mousse |
EP2371783A1 (fr) * | 2010-04-01 | 2011-10-05 | Xella Technologie- und Forschungsgesellschaft mbH | Corps de formage en béton poreux et son procédé de fabrication |
Non-Patent Citations (2)
Title |
---|
STEPHAN GÜNTHER: "Calciumsilikat - Dämmung mit Platten aus Kieselsäure | Energieheld GmbH", ENERGIEHELD, 20 November 2014 (2014-11-20), pages 1 - 2, XP055323187, Retrieved from the Internet <URL:http://www.energieheld.de/daemmung/daemmstoffe/calciumsilikat> [retrieved on 20161125] * |
STEPHAN GÜNTHER: "Styropor / EPS -Der Klassiker der Dämmung", ENERGIEHELD, 17 December 2015 (2015-12-17), pages 1 - 2, XP055323189, Retrieved from the Internet <URL:http://www.energieheld.de/daemmung/daemmstoffe/styropor-eps> [retrieved on 20161125] * |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20180354862A1 (en) * | 2015-09-06 | 2018-12-13 | Goertek Inc. | Sound absorption material preparation method, sound absorption material and filling method thereof |
US10889525B2 (en) * | 2015-09-06 | 2021-01-12 | Goertek Inc. | Sound absorption material preparation method, sound absorption material and filling method thereof |
CN114105524A (zh) * | 2021-11-29 | 2022-03-01 | 张家港市华孚实业有限公司 | 一种建筑用保温型膨胀珍珠岩复合材料制备工艺 |
Also Published As
Publication number | Publication date |
---|---|
DE102015218288A1 (de) | 2017-03-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE10341255B4 (de) | Wärmeleitplatten aus expandiertem Graphit sowie Verfahren zu ihrer Herstellung | |
DE102007040938B4 (de) | Wandaufbau und Wärmedämmplatte | |
EP3084091B1 (fr) | Panneau d'isolation thermique | |
DE102014101704A1 (de) | Wärmedämmputz | |
WO2017050768A1 (fr) | Plaque isolante et procédé de production d'une plaque isolante | |
WO2018130699A1 (fr) | Mélange de matériaux de construction pour protéger du rayonnement électromagnétique | |
EP3532681A1 (fr) | Structure de plafond multifonctionnelle | |
EP2426096B1 (fr) | Mortier sec composé d'un mortier sec à l'argile et d'une matière supplémentaire comprenant un graphite naturel, un graphite et/ou de la rouille expansés | |
DE202009008493U1 (de) | Wandaufbau und Wärmedämmplatte | |
EP2257506B1 (fr) | Procédé de fabrication d'un élément de construction en forme de plaque ou de profilé et élément de construction en forme de plaque ou de profilé | |
EP3455427A1 (fr) | Système d'absorption acoustique et pièce insonorisée | |
WO2009067727A1 (fr) | Brique moulée et procédé de réalisation d'une brique moulée | |
DE102013208284A1 (de) | Wärmedämmplatte und Verfahren zur Montage von Leitungen | |
EP3289266B1 (fr) | Manchette coupe-feu | |
EP2519699B1 (fr) | Élément de plafond ou de cloison | |
DE102009033367A1 (de) | Aerogel-Aerogel Verbundwerkstoff | |
DE29616127U1 (de) | Halbzeug, nämlich Dämmplatte, insbesondere für einen Fußboden-, Decken- oder Wandaufbau | |
EP2386697A2 (fr) | Panneaux d'isolation thermique, systèmes d'isolation thermique comprenant ces panneaux d'isolation thermique et procédé de fabrication de tels panneaux d'isolation thermique | |
DE102011018171A1 (de) | Graduelle Hydrophilisierung von Aerogelteilchen | |
DE202016002375U1 (de) | Vorrichtung von Bauelemente, insbesondere einer Hauswand in Form einer Holz-Brettschichtwand | |
EP3260289B2 (fr) | Élément composite | |
EP3805459B1 (fr) | Composant de protection acoustique en béton de texture caverneuse | |
EP3543414A1 (fr) | Isolation à base de fibre naturelle, partie de bâtiment pourvue d'isolation à base de fibre naturelle et l'utilisation d'isolation à base de fibre naturelle | |
DE102012110225A1 (de) | Wärmedämmelement | |
EP2440716A2 (fr) | Élément de construction |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 16778235 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 16778235 Country of ref document: EP Kind code of ref document: A1 |